The invention relates to a method for making a microcircuit card comprising a support card and a module carrying the microcircuit, the module being installed in an open cavity in said support card. A more particular object of the invention is to combat a type of fraud consisting of demounting a module of this kind without affecting its functions, in order to transplant it into another support card.
The development of microcircuit cards in all fields is constantly calling into question security criteria. One of these criteria is the fact that any attempt to extract the module from the support card must lead to failure, i.e. to destruction of the microcircuit and/or its connections. The need to make progress in this field is keenly felt, especially since producing microcircuit identity cards has been envisaged.
The module that is installed in the cavity in the support card comprises a support film forming a printed circuit and carrying the microcircuit on one side. In most of the technologies currently used it is possible to demount the module without destroying it. This is because the module is often stuck to a peripheral flat defined between the open side and the bottom of the cavity, the microcircuit, which is often coated, being housed in the cavity itself. It is relative easy to insert a tool between the edge of the cavity and that of the module, to detach the latter. If this is done carefully, separation does not lead to the destruction of the microcircuit and/or its connections. Adding a drop of adhesive to connect the bottom of the cavity to the coating of the microcircuit has been proposed. However, demounting remains possible if a tool can be inserted between the resin of the coating and the adhesive. Another technique, proposed by the applicant, consists in depositing the resin protecting the microcircuit into the cavity itself and coating the microcircuit with this resin before the resin is polymerized. This technique makes the module more difficult to demount but the results are difficult to control since they depend greatly on the adherence of the resin to the walls of the cavity and in particular to its bottom. The invention aims to improve this technique.
The invention relates more particularly to a method of making a microcircuit card comprising a card body and a module comprising a support film forming a printed circuit carrying said microcircuit on one of its faces, wherein said module is fixed into a cavity in said card body by means of a resin at least partly filling said cavity and surrounding said Microcircuit, characterized in that the adherence of the resin to the wall of the cavity is increased so that it is significantly greater than its adherence to the support film of said module.
The adherence of the resin may be modified by appropriate surface treatment of the walls of the cavity and more particularly of its bottom. This surface treatment, which is reflected in an increase in the roughness and/or in a chemical modification of the treated surface, very significantly increases the adherence of the resin to the treated surface and in particular makes it very much stronger than the adherence of the same resin to the support film of the module. This being so, in the event of a fraudulent attempt to demount the module by inserting a tool between the edge of the cavity and that of the module the force applied results at best in unsticking the support film from the resin, the microcircuit and its connecting wires remaining embedded in the resin attached to the cavity. Consequently, the module demounted in this way becomes unusable.
The success of this type of surface treatment depends in particular on controlling the settings of the surface treatment means.
Paradoxically, in the context of developing the invention, it has been possible to show that it is preferable to make the card body from a plastic material having a low surface energy (typically less than 45 mN/m), i.e. one having an intrinsically weak adherence to the resin usually employed for the coating in the bottom of the cavity, and even to the adhesive for fixing the module to the periphery of the cavity. This is because, starting from a material of this kind with an intrinsically low surface energy, a better correlation is obtained between the setting parameters of the surface treatment means and the adherence obtained after surface treatment. Moreover, as explained later, materials known for their low surface energy, and relatively little used until now in the field of microcircuit cards for this reason, also have the best mechanical strength and thermal characteristics, which offers the prospect of a longer service life of the microcircuit card.
By way of nonlimiting example, the card body can be made so that at least the bottom of the cavity consists of polyethylene terephthalate (PET), polycarbonate or polybutylene terephthalate (PBT). It is not necessary for the whole of the card body to be made from a material of this kind. For example, if the card body is made by laminating a plurality of layers of plastic materials, possibly different materials, it will suffice for the layer at the depth of the bottom of the cavity to be of a plastic material with a low surface energy, for example one of the materials mentioned above. In the case of PET, polyethylene terephthalate film (PETF) in particular may be used.
If the card body is made in this way, i.e. by laminating a plurality of films, the cavity can be produced after lamination, by machining into the thickness of said card body, taking care that this operation is effected to the correct depth to expose the low surface energy plastic material, so that the latter forms the bottom of the cavity. Of course, the machining may be carried out on a one-piece card body, i.e. one made from a solid block of low surface energy plastic material. Another possibility is to mold the card body, in which case the cavity may be formed during molding. The plastic material used for the molding process is chosen for its low surface energy and is one of the materials indicated above, for example.
The surface treatment may comprise laser beam treatment generating mechanical and/or chemical modifications of the treated surface. Good results are obtained with a YAG laser beam generator or a CO2 laser beam generator.
The treatment may consist in chemical modification of the bottom surface by exposure to ultraviolet rays, for example by means of a lamp, possibly associated with laser treatment using an excimer laser beam generator emitting in the ultraviolet band. Excimer lasers, in particular argon-fluorine and xenon-chlorine lasers, may be used for this purpose.
The surface state of the cavity may also be modified by plasma treatment using a specific gas or in the open air (corona treatment). This type of treatment is reflected in chemical modification of the surface.
Laser treatment has the advantage of combining chemical modifications with the creation of microcavities which encourage increased adherence of the resin.
The operating parameters of the treatment means indicated above may be adjusted precisely to control the modification of the surface state of a plastic material and more particularly of a low surface energy plastic material.
After the operation of adjusting the surface state referred to above, the method is completed in a manner that is known in the art by depositing a required quantity of resin onto the bottom of the cavity treated in this way and placing the module in the cavity so that its microcircuit is surrounded by the liquid resin. The resin is then polymerized. Depending on the type of resin used, polymerization may be obtained by heat treatment or by ultraviolet irradiation followed by heat treatment after mounting the module. The adhesive used to fix the module to the peripheral flat of the cavity may be a cold adhesive or a heat-activated adhesive. After polymerization, resin adheres both to the interior surface of the module and to that of the treated cavity. However, the adherence of the resin to the module is much lower than the adherence of the same resin to the bottom of the cavity. This results in destruction of the module in the event of an attempt to extract it.
The invention will be better understood and its other advantages will become more clearly apparent in the light of the following description of one embodiment of the method conforming to the invention, which is given by way of example only and with reference to the appended drawings, in which:
a shows a variant of the
The method of the invention comprises the successive operations shown in FIGS. 1 to 5. In
Number | Date | Country | Kind |
---|---|---|---|
01/16483 | Dec 2001 | FR | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/FR02/04426 | 12/18/2002 | WO | 1/31/2005 |