The present invention relates to the fabrication of active and passive polymer-based, optoelectronic components. The technical task at hand is to devise a method directed to the fabrication of passive and active optoelectronic components having a high level of integration and high packing density. The fabrication process should make it possible to influence the parameters and properties of the optoelectronic component to be produced, in particular, to selectively influence the refractive index, nonlinear optical property, polarizability, double refraction and amplification properties during the fabrication process.
As described in
Also known is a process for fabricating waveguide circuits from polymeric waveguides using mask-assisted exposure processes, as described in source 6.] by L-H. Lösch, P. Kersten and W. Wischmann in “Optical Waveguide Materials” (M. M. Broer, G. H. Sigel Jr., R. Th. Kersten, H. Kawazoe ed) Mat. Res. Soc. 244, Pittsburg, Pa. 1992, pp. 253–262.
Substantial differences in refractive indices can be produced by implanting ions at high energies and high doses in PMMA. Processes of this kind are described in source 11.] by R. Kallweit, J. P-Biersack in “Ion Beam Induced Changes of the Refractive Index of PMMA”, Radiation Effects and Defects in Solids, 1991, vol. 116, pp. 29–36, and in source 12.] by R. Kallweit, U. Roll, J. Kuppe, H. Strack “Long-Term Studies on the Optical Performance of Ion Implanted PMMA Under the Influence of Different Media”, Mat. Res. Soc. Symp. Proc. Vol. 338 (1994) 619–624. In this context, differences in the refractive indices in solid PMMA material of up to 20% are obtained. However, masking processes must be used for patterning. Due to the high ion energy and the required absorber layer thickness in the mask, the resolution is limited by the edge roughness that is attainable using mask fabrication technologies. Electrically switchable regions incorporated in waveguides can be produced by diffusing poled, nonlinearly optical materials in polymers. In this manner, one can achieve a link to electrical adjustability of optical paths, or to the influencing of optical processes.
Free configurability of the pattern is achieved if, using the new process of additive lithography, three-dimensional patterns and periodic arrangements are constructed on any desired, inexpensive substrates, and if the refractive index of the deposited material is adapted to the task, by properly selecting the precursor material, as well as the sources listed below, are named as sources for the aforementioned subject area.
It is, thus, possible to construct narrow-band, geometrical and permanently adjustable filters and highly reflective mirrors on a miniaturized scale from photon crystals. If the photon crystals produced using deposition techniques are combined with nonlinear, optical materials in the interstices of the deposited materials, it is possible to obtain miniaturized, adjustable optical components [source 21.]
Present-day surface-imaging processes make it possible, using optical phase masks and steppers and, with the use of dry etching processes, to achieve the resolution and height ratios required for optical gratings and other optical elements. This can be achieved using the lithography and process equipment of the manufacturers of electronic storage devices having a
1 G-bit size, and corresponding resolution. High-throughput production processes are used in corpuscular-beam optical miniaturization techniques, as explained in the following sources:
A further known miniaturization technique is based on techniques using small mask templates as described in the following sources:
Miniaturization can also be achieved through the use of electron-beam-induced deposition in projectors.
At the present time, one does not know of integrated optical patterns, where the process of refractive index modulation is employed by diffusing nonlinear optical, high-refractive-index or liquid-crystal monomers into existing polymers, in conjunction with free-standing polymer patterns, where the refractive index difference with respect to the vacuum is used as the essential step for the refractive index increases.
The process according to the present invention for fabricating active and passive optical components is based on the generally known processes of surface imaging, to produce an oxygen-resistant etching mask in unexposed regions, and of diffusing molecules into patterned polymer layers.
According to the present invention, at least one patterned, highly sensitive polymer resist layer is deposited on an optoelectronic component, made of glass and conductor path, or of substrate. Defined regions of the polymer resist layer are subsequently exposed, producing an etching mask. High-grade anisotropic deep etching is performed on the unprotected regions to transfer the etching mask to the polymer resist layer located underneath the etching mask. The exposed regions of the polymer resist layer are ablated in the vertical direction, uncovering the unexposed side surfaces of the regions protected by the etching mask.
In the ensuing gas-phase or liquid-phase diffusion process, the unexposed polymer resist layer is filled with monomers, from its surface, through the mask of the surface masking and, from its side surfaces uncovered by the oxygen deep etching, with the application of heat. In the process, monomers are used, which are suited for breaking up the already existing pattern of the polymer, and for repatterning it, so that the optical properties of the optoelectronic component can be selectively changed as a function of the type of monomers used, and also as a function of the temperature and application time. In the diffusion process, the polymer then swells on all sides and, therefore, the previously lost edge region can be compensated selectively by the swollen material and, in a controlled manner, by the diffusion time and temperature. In addition, because of the acting surface tension, the surfaces produced by the swelling are very smooth, i.e. peak-to-valley heights in the 2 nm range are obtained. The obtained refractive index profile is assured in the long term by UV hardening and by deep crosslinking of the diffused molecules carried out after the diffusion.
By diffusing heavy metal oxide-containing, nonlinearly optical or liquid-crystal monomers or also molecules containing “rare earths” into the uncovered, deep polymer patterns, it is possible, in addition to passive materials, also to produce nonlinearly optical, active materials in selected regions. It is, therefore, possible to produce diffused refractive index profiles in regions defined by optical and corpuscular beam lithography.
The drawing illustrates a diagram for fabricating according to the present invention refractive index profile patterns, with the aid of chemical diffusion, in the expanded silylation process.
A highly sensitive, patternable polymer layer is deposited on the substrate composed of glass and conductor path. In the exemplary embodiment, Novolak is used. The etching mask is produced by the exposure of defined regions of the polymer resist layer, corresponding to the later component, in conjunction with a process of silylating the unexposed regions. By combining the silylation process used for high-resolution pattern definition with the dry etching of the cross-linked polymers to produce the great height-to-width ratios of the patterns, it is ensured that the non-cross-linked/unexposed material is available for further chemical diffusion of monomers for the various desired effects. This part of the material is normally removed in the development process when the negative working novolak is exposed. It is retained after dry etching as a result of the silylation. If the silylation process is begun with a short isotropic process attacking the silicon oxide of the silylation mask, the pattern broadens, but the rough edge structure of the silylated region, obtained by the shot noise of the electron exposure in the edge region of the mask, is smoothed.
Thus, in the following anisotropic dry etching process, which employs an etchant that attacks the silicon oxide of the etching mask, it is possible to use directional oxygen ions to achieve smooth side walls of the polymer. This solves the shot-noise edge roughness problem inevitably encountered in corpuscular beam optics. The scattering losses to be expected at the rough surfaces are also minimized.
In the subsequent diffusion process, the polymer then swells on all sides, with the result that the edge region that had been previously lost can be compensated for in a controlled manner by the swollen material, and by the diffusion time and temperature. By diffusing heavy metal oxide-containing, nonlinearly optical compounds or other similar compounds, or molecules contained in “rare earths”, into the uncovered deep polymer patterns, nonlinearly optical active materials can also be produced, in addition to passive materials, in selected regions. Thus, diffused refractive index profiles can be produced in regions defined by optical and corpuscular beam lithography. Such diffusion can take place, as in a conventional manner, into unetched polymer layers, resulting in refractive index differences of up to 10%. If diffusion is carried out in polymer layers already patterned using wet chemical development or by dry etching, then refractive index differences of between 1.5 and 3 can be achieved.
Using this process, one can increase the refractive index difference of 10-3 to 10-4 to 0.06, in the case of UV-and electron-exposed plexiglass, as the difference in the refractive index between silylated and unsilylated novolak. The refractive index differences attained can be further increased by dissolving resist regions, negatively polymerized by the exposure process, out of the optically active and passive pattern, using high-resolution oxygen dry etching, resulting in refractive index differences with respect to vacuum of n=1. In the case of the free-standing, silylated region, the refractive index difference increases to 1.57, while it is 1.63 for the unsilylated material. Consequently, the finished component is made of chemically inert, saturated materials of glass-like composition and good durability. The diffused regions can be cross-linked with long-term stability by UV deep cross-linking, rendering possible a long service life for the components. Electrical and integrated optical components can be easily combined in the layers of the component, because the process involves processes that have been used for a number of years in lithography. Fabrication is accelerated, because the novolak resist systems are characterized by approx. 20 times higher sensitivity in comparison with PMMA (plexiglass). The oxygen etching process additionally tempers the regions diffused with chemicals and, thus, ensures the durability of the components.
The process according to the invention present makes it possible to produce high-quality and highly effective diffractive patterns having few grating planes or lines and, thus, to fabricate integrated optical components, such as couplers, gratings, selectors and reflectors having few grating periods. By employing such high refractive index differences in the optical patterns and gratings, one can achieve the same optical quality using much shorter components, than is possible using polymer-plexiglass techniques. This greatly increases the packing density of the integrated optical elements in miniaturized integrated optics. The following are possibilities for implementing the optical components according to the present invention on a large scale:
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP97/03558 | 7/5/1997 | WO | 00 | 3/29/2000 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO99/03021 | 1/21/1999 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
4704347 | Vollenbroek et al. | Nov 1987 | A |
4751170 | Mimura et al. | Jun 1988 | A |
4824522 | Baker et al. | Apr 1989 | A |
5102776 | Hammer et al. | Apr 1992 | A |
5116461 | Lebby et al. | May 1992 | A |
5265185 | Ashley | Nov 1993 | A |
5943464 | Khodja | Aug 1999 | A |
Number | Date | Country |
---|---|---|
24 60 716 | May 1976 | DE |
24 60 715 | Jun 1976 | DE |
24 46 789 | Sep 1976 | DE |
25 15 550 | Oct 1976 | DE |
196 16 324 | Oct 1997 | DE |
0 614 126 | Sep 1994 | EP |
63 249837 | Oct 1988 | JP |
402140749 | May 1990 | JP |
Number | Date | Country | |
---|---|---|---|
20030052081 A1 | Mar 2003 | US |