1. Field of the Invention
The invention relates to a method of forming a resist pattern, which improves an OPE characteristic generated by the difference between sparse and dense mask patterns and has high fidelity to the design of the pattern, and a method of manufacturing a semiconductor device using the method of forming the resist pattern.
2. Description of the Background Art
With high integration of semiconductor devices, a method of manufacturing a semiconductor that is suitable for a micro process has been studied and developed.
However, deterioration of fidelity to the design of the pattern based on the optical proximity effect (referred to as “OPE” below) by adjacent patterns has been a problem, and the OPE characteristic is an important parameter in miniaturization.
In photolithography, it is known that multiple interferences of light occur in a resist film, and the dimensional width of the resist pattern changes along with changes in the resist film thickness. The multiple interferences of light occur as a result of irradiated light that is incident on the resist film formed on the substrate interfering with the reflected light from the substrate, and the amount of optical energy absorbed in the thickness direction of the photoresist film differs.
As described in Japanese Patent Laying-Open No. 08-015859, a method of forming an anti-reflective film on the substrate as a means of reducing multiple interfering actions of light in the resist film is conventionally known. The conventional method of forming a resist pattern in which the anti-reflective film is formed on the substrate is shown in
In order to prevent in-film multi-reflection inside the resist or to prevent the deactivation of an acid of a chemical amplification type resist due to amine in air, as described in Japanese Patent Laying-Open No. 07-295228, a method of forming an upper layer film of a water-soluble polymer on the resist is known. In the chemical amplification type resist, there is an acid catalyst type resist in which an acid is generated in the exposed part as a catalyst, and it is a resist with high sensitivity and high resolution because the catalyst is used. However, after exposure and before baking is performed, the acid catalyst generated in the exposed part becomes inactive due to the influence of a small amount of amine which exists in air, and the line width and resolution of the resist change. It is considered that the formation of the upper layer film is effective in preventing such a PED (Post Exposure Delay) phenomenon.
The conventional method of forming a resist pattern in which an upper layer film is formed is shown in
The relationship between the optical intensity of the mask pattern obtained through a mask and the OPE is shown in
Further, in the conventional method of forming a resist pattern in which the upper layer film is not formed, because the generated acid catalyst H+ is deactivated by amine existing in air after exposure, and while the baking process is performed as shown in
On the other hand, in the conventional method of forming a resist pattern in which the upper layer film is formed, as shown in
The mechanism of deterioration of the OPE characteristic accompanied by deterioration of the shape of the resist is shown in
The objective of the present invention is to provide a method of forming a resist pattern, which improves a dissolution contrast, improves the OPE characteristic generated by the difference between sparse and dense mask patterns, and has high fidelity to the design of the pattern by coating the resist with an acid polymer dissolved in an alcohol based solvent as an upper layer film and forming a mixing layer on the resist. Further, it is to provide a method of manufacturing a semiconductor device using the method of forming the resist pattern.
The present invention is a method of forming a resist pattern by photolithography, and consists of a step of forming a resist having an acid dissociative dissolution suppression group on a substrate, a step of coating the resist with an acid polymer dissolved in an alcohol based solvent and forming an upper layer film, a step of exposing through a mask, a step of performing a baking process, and a step of processing with an alkali developer; and in which in the step of performing a baking process, a mixing layer is formed on the resist by the upper layer film and a thicker mixing layer is formed in the non-exposed part of the region where the pattern density of the mask pattern is high compared to the region where the pattern density is low.
Further, the method of manufacturing a semiconductor device in the present invention consists of a step of forming a resist pattern on an underlying film that is formed on a semiconductor substrate or in the semiconductor substrate using the above-described method of forming a resist pattern, and a step of patterning the semiconductor substrate or the underlying film using the resist pattern as a mask.
The OPE characteristic generated by the difference between sparse and dense mask patterns can be improved, and fidelity to the design of the pattern can be promoted. Further, the method of forming the resist pattern is useful in a method of manufacturing the entire semiconductor device with 90 nm to 32 nm design rules and semiconductor devices with design rules thereafter.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
The method of forming a resist pattern in the present invention consists of a step of forming a resist having an acid dissociative dissolution suppression group on a substrate, a step of coating the resist with an acid polymer dissolved in an alcohol based solvent and forming an upper layer film, a step of exposing through a mask, a step of performing a baking process, and a step of processing with an alkali developer; and in which in the step of performing a baking process, a mixing layer is formed on the resist by the upper layer film. A thicker mixing layer can be formed in an unexposed part of the region where the pattern density of the mask pattern is high compared to the region where the pattern density is low.
Because the exposure amount becomes large in a region where the pattern density of the mask pattern is high due to diffraction, etc., penetration of the solvent to the resist in the upper layer film becomes large. Therefore, a thick mixing layer is formed, and in a region where the pattern density is low, a thin mixing layer is formed. Because the thicker the mixing layer is formed, the lower the solubility in the developing step becomes, and the solubility can be decreased more greatly in a region where the pattern density is high compared to a region where the pattern density is low. By controlling the solubility in such a manner, the OPE characteristic due to the difference between sparse and dense mask patterns can be improved, and fidelity to the design of the pattern can be promoted. Therefore, such method of forming a resist pattern is applied to a method of manufacturing a semiconductor device, and by forming a resist pattern on a semiconductor substrate or on an underlying film formed on the semiconductor substrate and then by patterning the semiconductor substrate or the underlying film using the resist pattern as a mask, scattering due to the difference between sparse and dense patterns can be reduced and the pattern can be formed per the designed dimension with good accuracy.
The variations of dissolution contrast due to the sparse and dense patterns is shown in
The mixing layer is a layer formed by an acid polymer and a solvent in the upper layer film penetrating into the resist by diffusing and mixing, and is a layer in which a water-soluble film forming component and/or an alkali-soluble film forming component of the upper layer film composition are/is included in a base polymer having an acid dissociative dissolution suppression group in the resist composition. The acid dissociative dissolution suppression group in the resist has an alkali dissolution suppression property that makes the entire resin component alkali-insoluble before exposure, and the entire resin component can be changed to alkali-soluble when the acid dissociative dissolution suppression group is separated due to an acid generated by an acid generator included in the resist as baking is performed at exposure and after exposure (Post Exposure Bake) (may be referred to as “PEB” below). However, the ratio of the acid dissociative dissolution suppression group separating increases corresponding to the exposure amount radiating on the resist, and as a result, because a water-soluble film forming material, an alkali-soluble film forming component, and a solvent in the upper layer film penetrate easily as the exposure amount increases, the mixing layer becomes thick. The thickness of the mixing layer in the exposed part is about 10 nm to 100 nm, and 0 to 30 nm in the non-exposed part. Further, because the amount of diffracting light changes with the mask pattern density, when the pattern density increases, the amount of diffracting light increases and the mixing layer in the exposed part and in the non-exposed part becomes thick.
An ArF resist, which is a resist that is sensitive to an ArF excimer laser beam, etc. can be used as the resist applied on the substrate. On the other hand, in the respect of the quality of material, a resist consisting of at least a base polymer having an acid dissociative dissolution suppression group, an acid generator, and a solvent can be used as a positive resist composition, two kinds or more of the base polymer may be mixed and used, and furthermore other conventionally known resins for a photo resist composition can be mixed and used. Furthermore, in order to improve the shape of the resist pattern, stability over the passage of time, etc., a quencher, and if desired, miscible additives such as an additional resin to improve the performance of the resist film, a surfactant to improve the coating property, a dissolution suppressant, a plasticizer, a stabilizer, a colorant, and an antihalation agent can be included appropriately.
The base polymer of the resist composition includes a polymer consisting of a (meth)acrylic acid ester unit, a polymer having a configuration unit including an acid anhydride of dicarboxylic acid, a polymer having a configuration unit including a phenolic hydroxyl group, a silsesquioxane resin, a polymer having an α-(hydroxyalkyl)acrylic acid unit, and a polymer having a dicarboxylic acid monoester unit. Further, a polymer having an alkali soluble configuration unit including an aliphatic cyclic group having both (i) a fluorine atom or a fluorinated alkyl group and (ii) an alcohol hydroxyl group or an alkyloxy group can be used.
The acid dissociative dissolution suppression group includes an acid dissociative dissolution suppression group including an aliphatic polycyclic group, and examples of the polycyclic group include a group in which one hydrogen atom is removed from bicycloalkane, tricycloalkane, or tetracycloalkane which is substituted or unsubstituted with a fluorine atom or a fluorinated alkyl group. A specific example includes a group in which one hydrogen atom is removed from polycycloalkane such as adamantane, norbornane, isobornane, tricyclodecane, and tetracyclododecane. The polycyclic group can be used by being selected appropriately from many resists proposed as an ArF resist. However, an adamantane group, a norbornyl group, and a tetracyclododecanyl group are preferable industrially.
The acid generator include an onium salt such as diphenyliodonium trifluoromethanesulfonate, (4-methoxyphenyl)phenyliodonium trifluoromethanesulfonate, bis(p-tert-butylphenyl)iodonium trifluoromethanesulfonate, triphenylsulfonium trifluoromethanesulfonate, (4-methoxyphenyl)diphenylsulfonium trifluoromethane sulfonate, (4-methylphenyl)diphenylsulfonium trifluoromethane sulfonate, (4-methylphenyl)diphenylsulfonium nonafluorobutanesulfonate, (p-tert-butylphenyl)diphenylsulfonium trifluoromethanesulfonate, diphenyliodonium nonafluorobutanesulfonate, bis(p-tert-butylphenyl)iodonium nonafluorobutanesulfonate, triphenylsulfonium nonafluorobutanesulfonate, (4-trifluoromethylphenyl)diphenylsulfonium trifluoromethanesulfonate, (4-trifluoromethylphenyl)diphenylsulfonium nonafluorobutanesulfonate, and tri(p-tert-butylphenyl)sulfonium trifluoromethanesulfonate. Among the onium salts, the triphenylsulfonium salts can be used preferably because they are difficult to decompose and are difficult to generate organic gas. The amount of the triphenylsulfonium salt is preferably 50 mol % to 100 mol % to the total amount of the acid generator, more preferably 70 mol % to 100 mol %, and the most preferably 100 mol %.
The solvent of the resist that can be used is appropriately selected from one kind or two kinds or more of any known kinds. Examples include ketones such as acetone, methylethylketone, cyclohexanone, methylisoamineketone, and 2-heptanone, polyhydric alcohols such as monomethyl ethers of ethylene glycol, ethylene glycol monoacetate, diethylene glycol, diethylene glycol monoacetate, propylene glycol, propylene glycol monoacetate, dipropylene glycol, or dipropylene glycol monoacetate, monoethyl ether, monopropyl ether, monobutyl ether, and monophenyl ether, and their derivatives, cyclic ethers such as dioxane, and esters such as methyl lactate, ethyl lactate, methyl acetate, ethyl acetate, butyl acetate, methyl pyruvate, ethyl pyruvate, methyl methoxypropionate, and ethyl etoxypropionate. These organic solvents may be used individually and may be used as a mixed solvent of two kinds or more.
A known amine etc. can be used as a quencher to improve the shape of the resist pattern and the stability over the passage of time, etc. However, a secondary lower aliphatic amine, tertiary lower aliphatic amine, and organic acid such as organic carboxylic acid and oxoacid of phosphorus can be included preferably. The lower aliphatic amine refers to an amine of alkyl or alkyl alcohol having 5 or less carbon atoms, and examples of the secondary and tertiary amines include trimethylamine, diethylamine, triethylamine, di-n-propylamine, tri-n-propylamine, tripentylamine, diethanolamine, and triethanolamine. However, alkanolamine such as triethanolamine is especially preferable. These may be used individually, and two kinds or more of them may be combined and used. These amines are used normally in the range of 0.01% by mass to 2.0% by mass to the resin component. The preferred examples of the organic carboxylic acid include malonic acid, citric acid, malic acid, succinic acid, benzoic acid, and salicylic acid. The oxoacid of phosphorous and its derivatives include phosphoric acids and the derivatives such as their ester, e.g., phosphoric acid, phosphoric acid di-n-butyl ester and phosphoric acid diphenyl ester, phosphonic acids and the derivatives such as their ester, e.g., phosphonic acid, phosphonic acid dimethyl ester, phosphonic acid di-n-butyl ester, phenylphosphonic acid, phosphonic acid diphenyl ester, and phosphonic acid dibenzyl ester, phosphinic acids and the derivatives such as their ester, e.g., phosphinic acid and phenylphosphinic acid, and phosphonic acid is especially preferable among these. The organic acid is used at a ratio of 0.01 parts by mass to 5.0 parts by mass per the resin component 100 parts by mass. These may be used individually, and two kinds or more of them may be combined and used. These organic acids are preferably used at the range of an equimolar amount or less to amine.
The material of the upper layer film includes at least one kind selected from the water-soluble film forming component and the alkali-soluble film forming component, is a composition including at least an acid polymer and a solvent, and can be included with a surfactant, etc. if desired.
Polymers having a refractive index nd of 1.40 to 1.80 can be used as the acid polymer, and for example the polymers that can be used include at least one kind selected from an acid generator and acid compounds, and the acid compound is at least one kind selected from carboxylic acid, sulfonic acid, and sulfonyl compounds having at least a fluorinated hydrocarbon group. Further, the polymers that can be used include a nitrogen compound, and the nitrogen compound is at least one kind selected from quaternary ammonium hydroxide and alkanolamine compounds or the nitrogen compound is as least one kind selected from amino derivatives.
An example of the water-soluble film forming component that can be used is a cellulose based polymer such as hydroxypropylmethyl cellulose phthalate, hydroxypropylmethyl cellulose acetate phthalate, hydroxypropylmethyl cellulose acetate succinate, hydroxypropylmethyl cellulose hexahydrophthalate, hydroxypropylmethyl cellulose, hydroxypropyl cellulose, hydroxyethyl cellulose, cellulose acetate hexahydrophthalate, carboxymethyl cellulose, ethyl cellulose, and methyl cellulose. Further, an acrylic acid based polymer having acrylic acid, etc. as a monomer such as N,N-dimethylacylamido, N,N-dimethylaminopropylmethacrylamido, N,N-dimethylaminopropylacrylamido, N-methylacrylamido, diacetone acrylamido, N,N-dimethylaminoethylmethacrylate, N,N-diethylaminoethylmethacrylate, N,N-dimethylaminoethylacrylate, and acryloylmorpholine may be used. Among these, the acrylic acid based polymer which is a water-soluble polymer not having a hydroxyl group and polyvinylpyrrolidone are preferable. These water-soluble film forming components may be used individually, and two kinds or more of them may be combined and used.
An example of the alkali-soluble film forming component that can be used is a novolac resin obtained by condensing phenols (such as phenol, m-cresol, xylenol, and trimethylphenol), aldehydes (such as formaldehyde, 3-hydroxybenzaldehyde, and 4-hydroxybenxaldehyde) and/or ketones (such as methylethylketone and acetone) under the existence of an acid catalyst. Further, a hydroxyetyrene based resin such as a single polymer of hydroxysteyrene, a copolymer of hydroxysteyrene and other styrene based monomers, a copolymer of hydroxystyrene and acrylic acid, methacrylic acid, or its derivatives can be used. The alkali-soluble film forming components may be used individually, and two kinds or more of them may be combined and used. Between the water-soluble film forming component and the alkali-soluble film component, the water-soluble film forming component is preferable as the component used for a material for forming the upper layer film in the present invention.
Known kinds of acid generator used for the amplification type resist can be used as the acid generator in the acid polymer. Specifically, the acid generator includes an onium salt such as diphenyliodonium trifluoromethanesulfonate, (4-methoxyphenyl)phenyliodonium trifluoromethanesulfonate, bis(p-tert-butylphenyl)iodonium trifluoromethanesulfonate, triphenylsulfonium trifluoromethanesulfonate, (4-methoxyphenyl)diphenylsulfonium trifluoromethanesulfonate, (4-methylphenyl)diphenylsulfonium trifluoromethanesulfonate, (4-methylphenyl)diphenylsulfonium nonafluorobutanesulfonate, (p-tert-butylphenyl)diphenylsulfonium trifluoromethanesulfonate, diphenyliodonium nonafluorobutanesulfonate, bis(p-tert-butylphenyl)iodonium nonafluorobutanesulfonate, triphenylsulfonium nonafluorobutanesulfonate, (4-trifluoromethylphenyl)diphenylsulfonium trifluoromethanesulfonate, (4-trifluoromethylphenyl)diphenylsulfonium nonafluorobutanesulfonate, and tri(p-tert-butylphenyl)sulfonium trifluoromethanesulfonate.
Further, the acid compounds include inorganic acids such as hydrochloric acid, sulfuric acid, nitric acid, and phosphoric acid, and organic acids such as formic acid, acetic acid, propionic acid, benzenesulfonic acid, and toluenesulfonic acid. The organic acids may be used individually, and two kinds or more of them may be combined and used.
The kinds of the acid compounds represented with Formulas (1), (2), and (3) are preferable.
R1fCOOH (1)
In Formula (1), R1f is a fluorinated hydrocarbon group in which a part of or a whole hydrogen atom of a saturated or unsaturated hydrocarbon group having 1 to 20 carbon atoms is substituted with a fluorine atom.
R1fSO3H (2)
R2f(SO2R1f)n (3)
In Formula (3), R2f is an amino group or a saturated or unsaturated and fluorine-substituted or unsubstituted hydrocarbon group having 1 to 20 carbon atoms, and n is an integer of 1 to 4.
Here, the fluorine-substituted carboxylic acid represented with Formula (1) includes perfluoroheptanoic acid and perfluorooctanoic acid, and further, the fluorine-substituted sulfonic acid represented with Formula (2) includes perfluoropropylsulfonic acid, perfluorooctylsulfonic acid, and perfluorodecylsulfonic acid. A specific example of perfluoroheptane acid is EF-201 (manufactured by Tohkem Products Corp.) and a specific example of perfluorooctylsulfonic acid is EF-101 (manufactured by Tohkem Products Corp.). Further, the fluorine-substituted sulfonyl compounds represented with Formula (3) include tris(trifluoromethylsulfonyl)methane, bis(trifluoromethylsulfonyl)ammonium, and bis(heptafluoroethylsulfonyl)ammonium.
Examples of the nitrogen compounds include quaternary ammonium hydroxide, alkanolamine compounds, and amino acid derivatives. The quaternary ammonium hydroxide includes a tetramethylammonium hydroxide, a tetraethylammonium hydroxide, a tetrapropylammonium hydroxide, a tetrabutylammonium hydroxide, a methyltripropylammonium hydroxide, and a methyltributylammonium hydroxide. Examples of the alkanolamine compounds include monoethanolamine, diethanolamine, triethanolamine, 2-(2-aminoethoxy)ethanol, N,N-dimethylethanolamine, N,N-diethylethanolamine, N,N-dibutylethanolamine, N-methylethanolamine, N-ethylethanolamine, N-butylethanolamine, N-methyldietheanolamine, monoisopropanolamine, diisopropanolamine, and triisopropanolamine.
Examples of the amino acid derivatives include glycine, alanine, valine, leucine, isoleucine, proline, phenylalanine, tryptophan, methionine, serine, threonine, cysteine, tyrosine, asparagines, glutamine, aspartic acid, glutamic acid, lysine, alginine, histidine, 4-hydroxyproline, desmosine, γ-aminobutyric acid, and β-cyanoalanine.
Any solvent can be used as the solvent that dissolves the acid polymer as long as it does not have a property to dissolve the resist film and it may dissolve the acid polymer. Such a solvent includes an alcohol based solvent, a paraffin based solvent, and a fluorine based solvent. A common alcohol based solvent such as isopropyl alcohol, isobutyl alcohol, 1-hexanol, 2-methyl-1-propanol, and 4-methyl-2-pentanol can be used as the alcohol based solvent, and especially 2-methyl-1-propanol and 4-methyl-2-pentanol are preferable. It is confirmed that n-heptane can be used as the paraffin based solvent and perfluoro-2-butyltetrahydrofuran can be used as the fluorine based solvent. Among these, the alcohol based solvent is preferable in the respect of alkali solubility at development. These may be used individually, and two kinds or more of them may be combined and used.
Besides the above-described compositions, at least one kind selected from anionic surfactants may be included in the material for forming the upper layer film. Specific examples of the anionic surfactants include ammonium alkyldiphenylether sulfonate, tetramethylammonium alkyldiphenylether sulfonate, trimethylethanolammonium alkyldiphenylether sulfonate, triethylammonium alkyldiphenylether sulfonate, ammonium alkyldiphenylether disulfonate, diethanolammonium alkyldiphenylether disulfonate, and tetramethylammonium alkyldiphenylether disulfonate. However, it is not limited to these. Moreover, the alkyl group in the above-described compound has 5 to 18 carbon atoms, and may be substituted with an alkoxy group having 5 to 18 carbon atoms. These anionic surfactants may be used individually, and two kinds or more of them may be combined and used.
The preferred embodiment including affinity with the resist is an embodiment in which the base polymer of the resist composition is a polymer consisting of an acrylic acid ester unit, in which the solvent in the upper layer film is a mixture of an alcohol based solvent and a fluorine based solvent, and in which a hydrophilic surfactant is added as an additive.
In Example 1, a semiconductor device is manufactured using a chemical amplification positive resist, using a method of forming a resist pattern in the present invention, and irradiating with a ArF excimer laser beam (wavelength 193 nm). Its step diagram is shown in
Next, as shown in
The steps from the exposure step to the developing step in the method of forming a resist pattern in the present invention are shown in
In the conventional method of forming a resist pattern, as shown in
The OPE characteristic of the resist pattern of 90 nm spacing formed in the present invention is shown in
In the present invention, the mixing layer is formed on the ArF resist using the acid polymer dissolved in the alcohol based solvent that does not dissolve the underlying resist on the upper layer film. Because the mixing layer is formed thicker as the pattern density of the mask pattern is higher, and is formed thinner when the pattern density is lower, the dissolution contrast can be improved depending on the pattern density when it is developed. The original optical contrast decreases as the pattern density becomes high and becomes a cause of the deterioration of the OPE characteristic. However, because the higher the pattern density is, the thicker the mixing layer in the present invention is formed, the dissolution speed on the non-exposed part where the pattern density is high is suppressed largely, and as a result, the dissolution contrast can be improved, and the difference of the dissolution contrast due to the difference between sparse and dense patterns can be improved.
A semiconductor device is obtained in the same manner as Example 1, except that TILC-019 manufactured by Tokyo Ohka Kogyo Co. Ltd. is used as the upper layer film. A material in which the acid polymer is dissolved in the alcohol based solvent such as isobutyl alcohol is used as a material for the upper layer film. The method of forming a resist pattern from the exposure step to the developing step in the present invention is shown in
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
2006-023110 (P) | Jan 2006 | JP | national |
Number | Date | Country | |
---|---|---|---|
Parent | 11700131 | Jan 2007 | US |
Child | 12767258 | US |