Information
-
Patent Grant
-
6177149
-
Patent Number
6,177,149
-
Date Filed
Monday, December 21, 199825 years ago
-
Date Issued
Tuesday, January 23, 200123 years ago
-
Inventors
-
Original Assignees
-
Examiners
Agents
- Smith, Gambrell & Russell, LLP
-
CPC
-
US Classifications
Field of Search
US
- 427 576
- 427 575
- 427 569
- 427 253
- 427 255394
- 427 573
- 438 648
- 438 656
- 438 674
- 438 680
- 438 653
- 438 685
- 438 627
-
International Classifications
-
Abstract
A Ti film is formed by CVD in holes formed in an insulating film formed on a Si substrate or on a Si film formed on a Si substrate by a method comprising the steps of: loading a Si substrate into a film forming chamber; evacuating the chamber at a predetermined vacuum; supplying TiCl4 gas, H2 gas, Ar gas and SiH4 gas into the film forming chamber; and producing a plasma in the film forming chamber to deposit a Ti film in the holes formed in the insulating film. The Si substrate is heated at 550° C. or above during the deposition of the Ti film, and the flow rates of the processing gases are regulated so that Si-to-insulator selectivity is not less than one. This method enables formation of a Ti film on a Si base at positions of holes in an insulating layer, with a good morphology of the interface between the Si base and the Ti film and with a good step coverage.
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a method of forming a titanium (Ti) film to be used as a contact metal film or an adhesion layer for a semiconductor device by a chemical vapor deposition (CVD) process.
2. Description of the Related Art
Recently, most semiconductor integrated circuits are fabricated in a circuit configuration of a multilevel structure to cope with market demand for high-density and large-scale integration. Accordingly, techniques for filling contact holes for the electrical connection of semiconductor devices formed in a lower layer to wiring lines formed in upper wiring layers, and via holes for the electrical connection of wiring lines in different wiring layers have become important.
Generally, aluminum (Al), tungsten (W), aluminum-base alloys and tungsten-base alloys are used for filing contact holes and via holes. If a contact hole (or a via hole) is filled with such a metal or an alloy, which is in direct contact with an Al wiring line or a silicon (Si) substrate in a lower layer, it is possible that an alloy of silicon and aluminum is produced in the boundary owing to the diffusion of Al and Si. Such an alloy has a high resistivity and is undesirable in view of need to reduce the power consumption and to increase the operating speed of integrated circuits If W or a W-base alloy is used for filling a contact hole, WF
6
gas as a source gas for depositing W or the W-base alloy tends to deteriorate the electrical properties of the Si substrate.
To avoid such problems, a barrier layer is formed on surfaces defining contact holes or via holes before filling the contact holes and the via holes with the filing metal. Generally, a two-layer barrier layer consisting of a Ti film and a TiN (titanium nitride) film is used as the barrier layer. It has been the usual way to form such a barrier layer by a physical vapor deposition (PVD) process. However, a PVD film has a poor coverage and is incapable of meeting the requirements of tight design rule, the reduction of the width of lines and diameter of openings and the increase of aspect ratio to meet the recent demand for the enhancement of the level of integration and the miniaturization of IC chips.
Recently, Ti films and TiN films have been formed by a CVD process capable of forming such films in a better film quality than the PVD process. The Ti film serving as a contact metal film is formed by a plasma CVD process. Usually, the plasma CVD process for forming a Ti film uses TiCl
4
gas as a source gas, H
2
gas and Ar gas. During the plasma CVD process, Si forming the substrate and Ti contained in the source gas interact and Si diffuses in the Ti layer, deteriorating the morphology of a TiSi
X
(typically, TiSi
2
) interfacial layer formed between the Si substrate and the Ti layer. The diffusion of Si into the Ti layer is liable to cause junction leakage when the Ti layer is used for filling a contact hole and affects adversely to electrical connection when the same is used for filling a via hole.
The aspect ratio of contact holes and via holes formed in SiO
2
insulating films has increased with the progressive miniaturization of IC chips. Therefore, the Ti film is required to be formed in a satisfactory step coverage.
The present invention has been made in view of the above and it is therefore an object of the present invention to provide a method of forming a Ti film by CVD, capable of forming a Ti film in minute holes formed in an insulating film in a satisfactory step coverage without deteriorating the morphology of a TiSi
X
interfacial layer formed between the Ti film and a Si base.
SUMMARY OF THE INVENTION
According to the present invention, there is provided a method of forming a titanium film (by CVD) in holes formed in an insulating film formed on a silicon base, comprising the steps of loading a silicon base formed with holes into a film forming chamber, evacuating the chamber at a predetermined vacuum, supplying processing gases including TiCl
4
gas, a reduction gas, Ar gas and SiH
4
gas into the film forming chamber, and producing a plasma in the film forming chamber to deposit a titanium film in the holes formed in the insulating film, in which the silicon base is heated at 550° C. or above during the deposition of the titanium film, and the flow rates of the processing gases are regulated so that a silicon-to-insulating film selectivity is not less than one.
The flow rates of the processing gases may be selected so that the silicon -to-insulating film selectivity is three or more. SiH
4
may have a flow rate which is from about 10 to about 50% of the flow rate of TiCl
4
. Furthermore, SiH
4
may have a flow rate which is from about 0.05 to about 0.25% of the flow rate of all of the processing gases. The temperature of the silicon base during the film formation is preferably from 580 to 630° C. H
2
gas is used most advantageously as the reduction gas.
The inventors of the present invention made studies to form a Ti film by CVD in a satisfactory step coverage without deteriorating the morphology of the TiSi
X
layer and found that such a Ti film can be formed when the temperature of the substrate is 550° C. or above, SiH4 gas is used in addition to TiCl
4
gas, H
2
gas and Ar gas, and the respective flow rates of those processing gases are adjusted properly.
The deterioration of the morphology of the TiSi
X
interfacial layer formed between the Ti film and the Si base is caused by the interaction of Si and Ti, and the irregular diffusion of Si into the Ti film during the formation of the Ti film. SiH
4
gas suppresses the irregular diffusion of Si into the Ti film to prevent the deterioration of the morphology of the TiSi
X
layer. However, since SiH
4
gas is a reducing gas, TiSi
X
is produced by the interaction of SiH
4
gas and TiCl
4
gas and such a reaction deteriorates the step coverage.
To utilize the function of SiH
4
to avoid deteriorating the morphology of the TiSi
X
layer without deteriorating the step coverage of the CVD-Ti film, it is effective to increase the silicon-to-insulating film selectivity by heating the substrate at 550° C. or above during the film forming process, and to adjust the flow rates of the processing gases, particularly, the flow rate of SiH
4
gas, so that the silicon-to-insulating film selectivity is not less than one. The present invention has been made on the basis of such knowledge.
The above and other objects, features and advantages of the present invention will become more apparent from the following description taken in connection with the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1
is a sectional view of a film forming system for carrying out a method of forming a Ti film by CVD in a preferred embodiment of the present invention;
FIGS. 2A and 2B
are fragmentary sectional views of Si substrates to which the present invention is applied;
FIG. 3
is a graph showing the dependence of step coverage on the flow rate of SiH
4
gas;
FIG. 4
is a graph showing the dependence of the thickness of a Ti film formed on Si on the temperature of the Si substrate for SiH
4
flow rates of 0 sccm, 1 sccm and 5 sccm;
FIG. 5
is a graph showing the dependence of the thickness of a Ti film formed on SiO
2
on the temperature of the Si substrate for SiH
4
flow rates of 0 sccm, 1 sccm and 5 sccm;
FIG. 6
is an electron micrograph of a Ti film formed in a contact hole with the substrate heated at 620° C. and SiH
4
supplied at 1 sccm; and
FIG. 7
is an electron micrograph of a TiSi
X
interfacial layer formed between a Si base and a Ti film formed on the Si base.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
Referring to
FIG. 1
, a film forming system for carrying out a method of forming a titanium (Ti) film by CVD in a preferred embodiment of the present invention has a substantially cylindrical vessel
1
defining an airtight film forming chamber, a susceptor
2
for supporting a silicon (Si) wafer or substrate W, i.e., an object to be processed, in a horizontal attitude thereon, and a cylindrical support member
3
supporting the susceptor
2
for vertical movement. A heating element
4
is embedded in the susceptor
2
. Power is supplied by a power source, not shown, to the heating element
4
to heat a silicon (Si) wafer W supported on the susceptor
2
at a predetermined temperature.
A shower head
10
is disposed on the upper wall of the vessel
1
so as to face a Si wafer W supported on the susceptor
2
. The shower head
10
has a lower wall provided with a plurality of gas discharge holes
10
a
and facing a Si wafer W supported on the susceptor
2
, a space
11
, a perforated diffusing wall
12
formed in the space
11
, and an upper wall provided with a gas supply port
13
. A gas supply pipe
15
is connected to the gas supply port
13
.
The gas supply pipe
15
is connected to hydrogen (H) gas source
16
, an argon (Ar) gas source
17
, a titanium tetrachloride (TiCl
4
) gas source
18
and a silane (SiH
4
) gas source
19
through mass flow controllers
21
and valves
20
. The processing gases are supplied from the gas sources
16
,
17
,
18
and
19
through the gas supply pipe
15
and the shower head
10
into the film forming chamber defined by the vessel
1
, whereby a titanium (Ti) film is formed on the silicon wafer.
A radio frequency power source
23
is connected through a matching circuit
22
to the shower head
10
to apply a radio frequency voltage to the shower head
10
. The processing gases are ionized in the vessel
1
by radio frequency power supplied to the shower head
10
to produce a plasma of the source gas in the vessel
1
. The shower head
10
is electrically isolated from the vessel
1
by an insulating member
14
, and the vessel
1
is grounded.
The bottom wall of the vessel
1
is provided with an exhaust port
8
. An exhaust system
9
for evacuating the vessel
1
is connected to the exhaust port
8
. The vessel
1
has a side wall provided in its lower part with an opening
24
. A gate valve
25
is disposed in the opening
24
to open and close the opening
24
. The gate valve
25
is opened and the susceptor
2
is lowered to its lower position when carrying a wafer W into and carrying the same out of the vessel
1
through the opening
24
.
When forming a Ti film by the film forming system, the gate valve
25
is opened, a Si wafer W is loaded into the vessel
1
and is mounted on the susceptor
2
, the Si wafer W is heated by the heating element
4
, the vessel is evacuated to a high vacuum by a vacuum pump included in the exhaust system
9
, TiCl
4
gas, H
2
gas, Ar gas and SiH
4
gas are supplied into the vessel
1
, and a radio frequency voltage is applied to the shower head
10
by the radio frequency power source
23
to produce a plasma in the shower head
10
.
The Si wafer W on which a Ti film is to be formed is, for example, a Si substrate
41
provided with an insulating film
42
of SiO
2
and contact holes
43
(only one of them is shown) formed in the insulating film
42
as shown in
FIG. 2A
, or a Si substrate
41
provided with a polysilicon film
47
formed on the Si substrate
41
, an insulating film
45
of SiO
2
formed on the polysilicon film
47
, and via holes
46
(only one of them is shown) as shown in FIG.
2
B. An insulating layer may be formed between the Si substrate
41
and the polysilicon film
47
. The Si substrate
41
and the insulating film
45
of SiO
2
will generally be referred to as “silicon base”.
In this embodiment, SiH
4
gas is used and process conditions are determined so that Si-to-SiO
2
selectivity is not less than one to deposit a Ti film
44
on the bottoms of the contact holes
43
or the bottoms of the via holes
46
in a high step coverage, maintaining an interfacial layer formed between the Si base
41
and the Ti film
44
in a satisfactory morphology (conditions of the surface and section of the interfacial layer). That is, process conditions are determined so that Ti is deposited on portions of the surface of the Si wafer
41
forming the bottom surfaces of the contact holes
43
or on portions of the polysilicon film
44
forming the bottom surfaces of the via holes
46
, at a deposition rate higher than that at which Ti is deposited on the surface of the insulating film
42
of SiO
2
or the insulating film
45
of SiO
2
. More concretely, the Si substrate
41
is heated at 550° C. or above to increase the Ti deposition rate on the Si substrate
41
, and the flow rates of the processing gases, particularly, the flow rate of SiH
4
gas is controlled as described later so that Si-to-SiO
2
selectivity is one or above. Thus, the Ti film can be formed in high step coverage in the contact hole
43
or the via hole
46
; that is, the thickness of the Ti film at the top of the contact hole
43
or the via hole
46
is not great. When Si-to-SiO
2
selectivity is three or above, the Ti film can be formed in a more satisfactory step coverage. The step coverage is expressed as A/B where A is the thickness of a Ti film formed on the Si substrate
41
in
FIG. 2A and B
is the thickness of a Ti film formed on the SiO
2
layer
42
.
To form an interfacial layer of a satisfactory morphology and securing a high Si-to-SiO
2
selectivity, a preferable SiH
4
flow rate is in the range of 1 to 5 sccm, more preferably, in the range of 1 to 3 sccm. If SiH
4
flow rate is less than 1 sccm, the effect of SiH
4
on the improvement of the morphology of the interfacial layer is insignificant. If SiH
4
flow rate is greater than 5 sccm, it is difficult to adjust the Si-to-SiO
2
selectivity to a desired value.
Preferable flow rates of TiCl
4
gas, H
2
gas and Ar gas are in the range of 5 to 15 sccm, in the range of 0.5 to 3.5 slm and in the range of 0.5 to 2 slm, respectively. It is preferable that the output capacity of the radio frequency power source is in the range of 200 to 800 W, and the pressure in the vessel
1
is in the range of 0.5 to 3.0 torr.
Experiments were conducted to verify the effects of the present invention, in which Ti films were formed on a SiO
2
film provided with contact holes. In the experiments, the vessel
1
was evacuated to 1.0 torr, the output power of the radio frequency power source
23
(13.56 MHz) was 200 W, H
2
gas flow rate was 1 slm, Ar gas flow rate was 1 slm, TiCl
4
gas flow rate was 10 sccm, and SiH
4
gas flow rate was varied in the range of 1 to 5 sccm.
FIG. 3
is a graph showing the relationship of the step coverage with the flow rate of SiH
4
gas when the Si wafer was heated at 620° C. The diameter of the hole is about 0.6 micronmeter, and the aspect ratio is about 4. As is obvious from
FIG. 3
, the step coverage decreases with the increase of the SiH
4
flow rate.
FIG. 4
is a graph showing the relationship of the thickness of a Ti film formed on a Si substrate with the temperature of the Si substrate, for SiH
4
flow rates of 0 sccm, 1 sccm and 5 sccm determined on the basis of experiments, in which the temperature of the Si substrate was varied up to 620° C. It will be noted that the Ti film thickness begins to increase when the temperature exceeds 550° C. Particularly when the temperature exceeds 580° C., the film thickness increases sharply.
FIG. 5
is a graph showing the relationship of the thickness of a Ti film formed on SiO
2
with the temperature of the Si substrate, for SiH
4
flow rates of 0 sccm, 1 sccm and 5 sccm determined on the basis of experiments, in which the temperature of the Si substrate was varied up to 620° C. It is observed that the Ti film thickness does not change substantially with the temperature change. As is obvious from
FIGS. 4 and 5
, the Si-to-SiO
2
selectivity increases with the increase of the temperature of the Si substrate beyond 550° C. and is very high when the temperature of the Si substrate is 580° C. or above. The Si-to-SiO
2
selectivity is greater than one even if SiH
4
flow rate is as much as 5 sccm when the temperature of the Si substrate is 620° C. It is known from
FIGS. 4 and 5
that the Si-to-SiO
2
selectivity is equal to or greater than one at SiH
4
flow rate in the range of 1 to 5 sccm if the temperature of the Si substrate is 550° C. or above. This range of the flow rate (1-5 sccm) of SiH
4
corresponds to about 0.05% to about 0.25% of the flow rate of all the processing gases and about 10% to about 50% of the flow rate of the TiCl
4
gas. The step coverage improves if the Si-to-SiO
2
selectivity increases, and an allowable step coverage can be achieved when the Si-to-SiO
2
selectivity is one or above.
FIG. 6
is an electron micrograph of a Ti film formed in a contact hole with the substrate heated at 620° C. and SiH
4
supplied at 1 sccm. The Ti film is formed in the contact hole in a high step coverage.
FIG. 7
is an electron micrograph of a TiSi
X
interfacial layer formed between a Si base and a Ti film formed on the Si base by the diffusion of Si into the Ti film. The electron microphotograph as taken after removing the TiSi
X
film with dilute hydrofluoric acid.
FIG. 7
proves that SiH
4
is effective in improving the morphology of the interfacial layer.
The experiments proved that both the morphology of the interfacial layer between the Si base and the Ti film and step coverage are satisfactory when SiH
4
gas is used in addition to TiCl
4
gas, H
2
gas and Ar gas, the Si substrate is heated at 550° C. or above, and the flow rates of the processing gases, particularly, the flow rate of SiH
4
gas is controlled properly.
As described above, a process gas with a higher SiH
4
concentration provides TiSi
X
interfacial layer with a better morphology, whereas a process gas with a lower SiH
4
concentration provides a better step coverage. Therefore, in an early stage of a Ti deposition, the SiH
4
concentration may be from 20% to 50% of the TiCl
4
gas, or from 0.1% to 0.25% of the total gas. Following that stage, the SiH
4
concentration may be changed to less than 0.1% of the total gas, or less than 20% of the TiCl
4
gas. This process can provide the interfacial layer with a better morphology and a titanium film with a better step coverage.
The Si substrate provided with the Ti film thus formed is placed in a chamber, TiCl
4
gas, Ar gas, NH
3
gas and MMH (monomethyl hydrazine) gas is supplied into the chamber to construct a two-layer barrier layer by forming a TiN film over the Ti film, and then a wiring metal film, such as an aluminum film, is formed over the two-layer barrier layer.
The present invention is not limited in its practical application to the embodiments specifically described herein. For example, other gasses may be used in addition to TiCl
4
gas, H
2
gas and Ar gas and SiH
4
gas, and process conditions are not limited to those described above.
Although the invention has been described in its preferred embodiments with a certain degree of particularity, it is to be understood that the embodiments are illustrative and not restrictive and many changes and variations may be made therein without departing from the scope and spirit of the invention.
Claims
- 1. A method of forming a titanium film by chemical vapor deposition in holes formed in an insulating film provided on a silicon base, said method comprising the steps of:loading a silicon base having thereon an insulating film formed with holes into a film forming chamber; evacuating the chamber at a predetermined vacuum; supplying processing gases including TiCl4 gas, a reduction gas, Ar gas and SiH4 gas into the film forming chamber; and producing a plasma in the film forming chamber to deposit a titanium film in the holes formed in the insulating film, while said silicon base is heated at a temperature of from 550 to 630° C., and while said TiCl4 gas and said SiH4 gas are supplied with a flow rate of the SiH4 gas being from 10 to 50% of a flow rate of the TiCl4 gas, to thereby obtain a silicon-to-insulating film selectivity of not less than one.
- 2. The method of forming a titanium film by chemical vapor deposition according to claim 1, wherein theSiH4 gas has a flow rate which is from about 0.05 to about 0.25% of the flow rate of all of the processing gases.
- 3. The method of forming a titanium film by chemical vapor deposition according to claim 1, wherein the reduction gas is H2.
- 4. The method of forming a titanium film by chemical vapor deposition according to claim 1, wherein said silicon base is heated at a temperature from 580 to 630° C.
- 5. The method of forming a titanium film by chemical vapor deposition according to claim 1, wherein said TiCl4 gas, H2 gas, Ar gas and SiH4 gas have flow rates of 5 to 15 sccm, 0.5 to 3.5 slm, 0.5 to 2 slm and 1 to 5 sccm, respectively.
- 6. A method of forming a titanium film in holes formed in an insulating film provided on a silicon base, said method comprising the steps of:loading a silicon base having thereon an insulating film formed with holes into a film forming chamber; evacuating the chamber at a predetermined vacuum; supplying processing gases including TiCl4 gas, a reduction gas, Ar gas and SiH4 gas into the film forming chamber; producing a plasma in the film forming chamber to deposit a titanium film in the holes formed in the insulating film, while said silicon base is heated at a temperature of from 550 to 630° C., and while said TiCl4 gas and said SiH4 gas are supplied with a flow rate of the SiH4 gas being from 10 to 50% of a flow rate of the TiCl4 gas, to thereby obtain a silicon-to-insulating film selectivity of not less than one; and depositing a titanium nitride film on the titanium film.
- 7. The method of forming a titanium film by chemical vapor deposition according to claim 6, wherein the SiH4 gas has a flow rate which is from about 0.05 to about 0.25% of the flow rate of all of the processing gases.
- 8. The method of forming a titanium film by chemical vapor deposition according to claim 6, wherein the reduction gas is H2.
- 9. The method of forming a titanium film by chemical vapor deposition according to claim 6, wherein said silicon base is heated at a temperature from 580 to 630° C.
- 10. The method of forming a titanium film by chemical vapor deposition according to claim 6, wherein said TiCl4 gas, H2 gas, Ar gas and SiH4 gas have flow rates of 5 to 15 sccm, 0.5 to 3.5 slm, 0.5 to 2 slm and 1 to 5 sccm, respectively.
- 11. A method of forming a titanium film by chemical vapor deposition in holes formed in an insulating film provided on a silicon base, said method comprising the steps of:loading a silicon base having thereon an insulating film formed with holes into a film forming chamber; evacuating the chamber at a predetermined vacuum; supplying processing gases including TiCl4 gas, a reduction gas, Ar gas and SiH4 gas into the film forming chamber; and depositing a titanium film in the holes formed in the insulating film by producing a plasma in the film forming chamber, while said silicon base is heated at a temperature of from 550 to 630° C., and while said TiCl4 gas and said SiH4 gas are supplied with a flow rate of the SiH4 gas being from 10 to 50% of a flow rate of the TiCl4, to thereby obtain a silicon-to-insulating film selectivity of not less than one; wherein said SiH4 gas is supplied with a first concentration at an early stage of the step of depositing the titanium film, and with a second concentration smaller than the first concentration at a later stage of the step of depositing the titanium film.
- 12. The method of forming a titanium film by chemical vapor deposition according to claim 11, wherein said first concentration of the SiH4 gas is from 0.10 to 0.25% of the total gases; and said second concentration of the SiH4 gas is less than 0.10% of the total gases.
- 13. The method of forming a titanium film by chemical vapor deposition according to claim 11, wherein said first concentration of the SiH4 gas is from 20 to 50% of the TiCl4 gas; and said second concentration of the SiH4 gas is less than 20% of the TiCl4 gas.
- 14. A method of forming a titanium film by chemical vapor deposition in holes formed in an insulating film provided on a silicon base, said method comprising the steps of:loading a silicon base having thereon an insulating film formed with holes into a film forming chamber; evacuating the chamber at a predetermined vacuum; supplying the processing gases including TiCl4 gas, a reducing gas, Ar gas and SiH4 gas into the film forming chamber; and producing a plasma in the film forming chamber to deposit a titanium film in the holes formed in the insulating film, while said silicon base is heated at a temperature of from 550 to 630° C., and while said TiCl4 gas and said SiH4 gas are supplied with a flow rate of the SiH4 gas being from about 0.05 to about 0.25% of the flow rate of all of the processing gases, to thereby obtain a silicon-to-insulating film selectivity of not less than one.
- 15. The method of forming a titanium film by chemical vapor deposition according to claim 14, wherein the flow rate of the SiH4 gas is from 10 to 50% of the flow rate of the TiCl4 gas.
Priority Claims (1)
Number |
Date |
Country |
Kind |
9-366066 |
Dec 1997 |
JP |
|
US Referenced Citations (6)
Foreign Referenced Citations (1)
Number |
Date |
Country |
8283944 |
Oct 1996 |
JP |