This application claims the benefit of Korean Patent Application No. 10-2011-0076559, filed on Aug. 1, 2011, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference.
1. Field of the Invention
The present invention relates to a power device manufacturing method, and more particularly, to a power device manufacturing method that manufactures a vertically-structured power device that is capable of operating a normally-OFF operation.
2. Description of the Related Art
A semiconductor light emitting device (LED) is a semiconductor device that generates various colored lights based on the re-bonding of an electron and a hole at a P-N junction when a current is applied. Demand for the semiconductor LED has been continuously increased since the semiconductor LED has many advantages, for example, a long lifespan, a low power consumption, a fast start-up, a high vibration resistance, and the like, when compared to a filament-based LED. Particularly, a nitride semiconductor that emits a blue light, in a short wavelength range, has drawn attention.
As information communication technologies have been considerably developed globally, communication technologies for high-speed and large-capacity signal communication have also been rapidly developed. Particularly, as demand for a personal cellular phone, a satellite communication, a military radar, a broadcasting communication, a communication relay, and the like in wireless communication technology has increased, the demands for a high-speed, a high-power electronic device required for a high-speed information communication system of a microwave band and a millimeter-wave band have increased. Also, research on a power device used for a high-power have been actively conducted to reduce energy loss.
Particularly, since the nitride semiconductor has advantageous properties, such as a high energy gap, a high heat stability, a high chemical stability, a high electronic saturation velocity of about 3×107 centimeters per second (cm/sec), the nitride semiconductor may be readily utilized as an optical element, and a high frequency and high power electronic device. Accordingly, research on the nitride semiconductor is being actively conducted the world over. An electronic device based on the nitride semiconductor may have varied advantages, such as, a high breakdown field of about 3×106 volts per centimeter (V/cm), a maximum current density, a stable high temperature operation, a high heat conductivity, and the like.
A heterostructure field effect transistor (HFET) generated based on a heterojunction of compound semiconductors has a high band-discontinuity at a junction interface, a high-electron density may be freed in the interface and thus, an electron mobility may increase. However, in an aluminum gallium nitride (AlGaN)/gallium nitride (GaN) HFET structure having a high electron mobility, a current flows even in a state where a signal is not applied and thus, power is consumed.
Since a power device may require a high current density, power loss in a normally-ON device may be a great drawback. Accordingly, a normally-OFF device that embodies a metal-oxide semiconductor (MOS) HFET by removing an AlGaN layer from a gate portion has been developed.
However, it is difficult to control the AlGaN layer to have a thickness less than or equal to 30 nanometers (nm). Also, the power device may operate vertically and thus, to increase a current density, increasing an area of the AlGaN layer may be needed. Recently, a vertically structured field-effect transistor (FET) device using a SiC substrate has been developed. However, the vertically structured FET device needs an implantation device to implant a carrier, and a process, for example, a heat treatment and the like, to activate a carrier.
An aspect of the present invention provides a power device manufacturing method that manufactures a vertically structured power device that is capable of performing a normally-OFF operation.
According to an aspect of the present invention, there is provided a power device manufacturing method, the method including forming a first drift region on a substrate, forming a trench by patterning the first drift region, forming a second drift region by growing n-gallium nitride (GaN) in the trench, and alternately disposing the first drift region and the second drift region, forming a source electrode contact layer on the second drift region, forming a source electrode and a gate electrode on the source electrode contact layer, and forming a drain electrode on one side of the substrate which is an opposite side of the first drift region.
The forming of the second drift region may be performed in a temperature range from about 1000° C. to about 1200° C.
The power device manufacturing method may further include forming an n-GaN layer on the second drift region, and a doping concentration of an n-type dopant doped on the n-GaN layer may be higher than the second drift region.
The doping concentration of the n-type dopant doped on the n-GaN layer may be in a range from about 1.0×1017/cm3 to about 1.0×1020/cm3.
The first drift region may include at least one of p-GaN and aluminum gallium nitride (AlGaN).
The source electrode contact layer may include at least one of an n+-GaN layer and a heterojunction of AlGaN and GaN.
The substrate may be selected from n+-GaN, n+-silicon carbide (SiC), sapphire, and silicon (Si).
The source electrode may include a material selected from a group consisting of chromium (Cr), aluminum (Al), tantalum (Ta), molybdenum (Mo), tungsten (W), titanium (Ti), and gold (Au).
Additional aspects, features, and/or advantages of the invention will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the invention.
These and/or other aspects, features, and advantages of the invention will become apparent and more readily appreciated from the following description of embodiments, taken in conjunction with the accompanying drawings of which:
Reference will now be made in detail to embodiments of the present invention, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to the like elements throughout. Embodiments are described below to explain the present invention by referring to the figures.
Throughout the specifications, when it is described that each of a layer, a side, a chip, and the like is formed “on” or “under” a layer, a side, a chip, and the like, the term “on” may include “directly on” and “indirectly on,” and the term “under” may include “directly under” and “indirectly under.” A standard for “on” or “under” of each element may be determined based on a corresponding drawing.
A size of each element in drawings may be exaggerated for ease of description, and does not indicate a real size.
Referring to
As shown in
The first drift region 200 may be formed by growing p-GaN or aluminum gallium nitride (AlGaN) on the substrate 100. The p-GaN or the AlGaN may be grown based on various schemes, for example, a metal-organic chemical vapor deposition (MOCVD) scheme, a molecular beam epitaxy (MBE) scheme, a hydride vapor phase epitaxy (HVPE) scheme, and the like, so that the first drift region 200 may be formed, however, the examples may not be limited thereto. The first drift region 200 may operate as a p-type conductive column in a super-junction structure.
Subsequently, as shown in
When a portion of the passivation layer 300 is removed, the first drift region 200 may be exposed, and the exposed first drift region 200 may be patterned so as to form a trench. In this example, a plurality of trenches may be formed, and a portion where the second drift region 400 is to be formed may be defined.
The plurality of trenches may be formed in the patterned first drift region 200. That is, the first drift region 200 and the plurality of trenches may be alternately disposed.
The second drift region 400 may be formed by growing n-GaN in the plurality of trenches. The second drift region 400 may be formed by growing n-GaN from the exposed substrate 100 at a lower portion of the plurality of trenches, based on the MOCVD scheme. While n-GaN is grown, a doping concentration of an n-type dopant may be adjusted in the second drift region 400. Since n-GaN is grown in the plurality of trenches, the second drift region 400 and the first drift region 200 may be alternately disposed. Thus, a super-junction structure may be formed.
A power device manufactured according to an embodiment of the present invention may have a relatively high withstand voltage since a depletion layer is formed near a p-n junction surface due to the super-junction structure during a p-n junction. During the p-n junction, a potential difference is locally created as a free electron and a hole are diffused to each other, and the power device is in a state of equilibrium, and thus, the depletion layer that does not contain a carrier may be formed near the p-n junction surface and the withstand voltage may increase.
The forming of the second drift region 400 by growing n-GaN may be performed in a temperature range from about 1000° C. to about 1200° C. Here, n-GaN may be regrown at a high temperature and thus, a crystal may not be damaged and a reliability may be secured. Also, an ion-implantation device and the like may not be additionally used and thus, a process may be simplified and a cost may be reduced.
As shown in
The source electrode contact layer 700 that may reduce an ohmic resistance occurring when the source electrode contact layer is in a contact with the source electrode 920, may be formed on the n-GaN layer 500 having a higher doping concentration of the n-type dopant than the second drift region 400. The source electrode contact layer 700 may include at least one of n+-GaN and a heterojunction of AlGaN and GaN. That is, an ON-resistance may be reduced by forming the source electrode contact layer 700 from n+-GaN having a high doping concentration of an n-type dopant and thus, a current density may increase.
A p-GaN layer 600 may be additionally formed between the source electrode contact layer 700 and the n-GaN layer 500 having a higher doping concentration of the n-type dopant than the second drift region 400. The p-GaN layer 600 may reduce a resistance occurring when the p-GaN layer 600 is in contact with the source electrode contact layer 700, and may increase a current density.
Subsequently, as shown in
As shown in
The source electrodes 920 may be formed on positions corresponding to the source electrode contact layer 700, and may include a material selected from chromium (Cr), aluminum (Al), tantalum (Ta), molybdenum (Mo), tungsten (W), titanium (Ti), and gold (Au). The gate electrode 910 may be formed on a position corresponding to the gate insulating layer 800, and may be formed between the source electrodes 920. The gate electrode 910 may include a material selected from nickel (Ni), Al, Ti, titanium nitride (TiN), platinum (Pt), Au, ruthenium oxide (RuO2), vanadium (V), W, tungsten nitride (WN), hafnium (Hf), hafnium nitride (FIN), Mo, nickel silicide (NiSi), cobalt silicide (CoSi2), tungsten silicide (WSi2), platinum silicide (PtSi), iridium (Ir), zirconium (Zr), Ta, tantalum nitride (TaN), copper (Cu), ruthenium (Ru), cobalt (Co), and combinations thereof.
The drain electrode 930 may be formed on one side of the substrate 100, that is, on an opposite side of the first drift region 200. The drain electrode 930 may include a material selected from Cr, Al, Ta, Mo, W, Ti, and Au. The drain electrode 930 may be formed to face the source electrodes 920 and thus, a vertically structured power device may be formed.
A process of forming the drain electrode 930 may be different for a type of the substrate 100. Hereinafter, various processes of forming the drain electrode 930 based on the type of the substrate 100 will be described.
When the substrate 100 is a conductive substrate, the drain electrode 930 may be directly formed on the substrate 100 without removing the substrate 100. When the substrate 100 is a sapphire substrate, an n+-GaN layer may be formed on the substrate 100, the sapphire substrate may be removed through a laser lift off process, and the drain electrode 930 may be formed. When the substrate 100 is a Si substrate, an n+-GaN layer may be formed on the substrate 100, the Si substrate may be removed through a wet etching process with a potassium hydroxide (KOH) solution, and the drain electrode 930 may be formed.
A power device manufactured based on an embodiment of the present invention may grow n-GaN to form a second drift region and thus, a crystal may not be damaged and a reliability may be secured. Also, an ion-implantation device and the like may not be additionally used and thus, a process may be simplified and a cost may be reduced. A first drift region and the second drift region are alternately disposed to form a super-junction structure and thus, a withstand voltage may increase since a depletion layer is formed near a p-n junction surface during a p-n junction. Also, an ON-resistance may be reduced in a source electrode contact layer. An n-GaN layer having a higher doping concentration of an n-type dopant than the second drift region may be formed on the second drift region and thus, the power device may be capable of performing a normally-OFF operation and thus, a power consumption may be reduced.
According to embodiments of the present invention, a power device manufacturing method may form a second drift region by growing n-GaN and thus, a crystal may not be damaged and a reliability may be secured. Also, an ion-implantation device and the like may not be additionally used and thus, a process may be simplified and a cost may be reduced.
In addition, a first drift region and the second drift region are alternately disposed so as to form a super-junction structure of n-GaN and p-GaN and thus, a withstand voltage may increase since a depletion layer is formed between n-GaN and p-GaN when a reverse voltage is applied.
Further, a current density may increase by reducing an ON-resistance in a source electrode contact layer. An n-GaN layer having a higher doping concentration of an n-type dopant than the second drift region may be formed on the second drift region, and the power device may be capable of performing a normally-OFF operation and thus, power consumption may be reduced.
Although a few embodiments of the present invention have been shown and described, the present invention is not limited to the described embodiments. Instead, it would be appreciated by those skilled in the art that changes may be made to these embodiments without departing from the principles and spirit of the invention, the scope of which is defined by the claims and their equivalents.
Number | Date | Country | Kind |
---|---|---|---|
10-2011-0076559 | Aug 2011 | KR | national |
Number | Name | Date | Kind |
---|---|---|---|
20070018243 | Ono et al. | Jan 2007 | A1 |
20080079009 | Yaegashi | Apr 2008 | A1 |
20090134456 | Sugimoto et al. | May 2009 | A1 |
20090315037 | Kikkawa | Dec 2009 | A1 |
20100044718 | Hanser et al. | Feb 2010 | A1 |
20100117119 | Uesugi et al. | May 2010 | A1 |
20110204381 | Okada et al. | Aug 2011 | A1 |
Number | Date | Country |
---|---|---|
2002-076339 | Mar 2002 | JP |
10-2009-0060280 | Jun 2009 | KR |
Number | Date | Country | |
---|---|---|---|
20130034939 A1 | Feb 2013 | US |