Methods of forming a capacitor comprising ferroelectric material and including current leakage paths having different total resistances

Information

  • Patent Grant
  • 10680057
  • Patent Number
    10,680,057
  • Date Filed
    Wednesday, July 31, 2019
    5 years ago
  • Date Issued
    Tuesday, June 9, 2020
    4 years ago
Abstract
A memory cell comprises a capacitor having a first conductive capacitor electrode having laterally-spaced walls that individually have a top surface. A second conductive capacitor electrode is laterally between the walls of the first capacitor electrode, and comprises a portion above the first capacitor electrode. Ferroelectric material is laterally between the walls of the first capacitor electrode and laterally between the second capacitor electrode and the first capacitor electrode. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. A parallel current leakage path is between an elevationally-inner surface of the portion of the second capacitor electrode that is above the first capacitor electrode and at least one of the individual top surfaces of the laterally-spaced walls of the first capacitor electrode. The parallel current leakage path is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path. Other aspects, including methods, are disclosed.
Description
TECHNICAL FIELD

Embodiments disclosed herein pertain to memory cells and to methods of forming a capacitor.


BACKGROUND

Memory is one type of integrated circuitry, and is used in computer systems for storing data. Memory may be fabricated in one or more arrays of individual memory cells. Memory cells may be written to, or read from, using digit lines (which may also be referred to as bit lines, data lines, sense lines, select lines, or data/sense lines) and access lines (which may also be referred to as word lines). The digit lines may conductively interconnect memory cells along columns of the array, and the access lines may conductively interconnect memory cells along rows of the array. Each memory cell may be uniquely addressed through the combination of a digit line and an access line.


Memory cells may be volatile or non-volatile. Non-volatile memory cells can store data for extended periods of time including when the computer is turned off. Volatile memory dissipates and therefore requires being refreshed/rewritten, in many instances multiple times per second. Regardless, memory cells are configured to retain or store memory in at least two different selectable states. In a binary system, the states are considered as either a “0” or a “1”. In other systems, at least some individual memory cells may be configured to store more than two levels or states of information.


A capacitor is one type of electronic component that may be used in a memory cell. A capacitor has two electrical conductors separated by electrically insulating material. Energy as an electric field may be electrostatically stored within such material. One type of capacitor is a ferroelectric capacitor which has ferroelectric material as at least part of the insulating material. Ferroelectric materials are characterized by having two stable polarized states. Polarization state of the ferroelectric material can be changed by application of suitable programming voltages, and remains after removal of the programming voltage (at least for a time). Each polarization state has a different charge-stored capacitance from the other, and which ideally can be used to write (i.e., store) and read a memory state without reversing the polarization state until such is desired to be reversed. Less desirable, in some memory having ferroelectric capacitors the act of reading the memory state can reverse the polarization. Accordingly, upon determining the polarization state, a re-write of the memory cell is conducted to put the memory cell into the pre-read state immediately after its determination. Regardless, a memory cell incorporating a ferroelectric capacitor ideally is non-volatile due to the bi-stable characteristics of the ferroelectric material that forms a part of the capacitor.


One type of memory cell has a select device electrically coupled in series with a ferroelectric capacitor. Current typically leaks through the select device to adjacent substrate material even when the select device is idle (i.e., when inactive or “off”). This leads to voltage drop at the adjacent electrode of the ferroelectric capacitor, thus creating a voltage differential between the two capacitor electrodes. This results in an electric field being applied across the ferroelectric material when the memory cell is idle. Even if small, such an electric field may start to flip individual dipoles in the ferroelectric material and continue until all are flipped, thus erasing a programmed state of the memory cell. This can occur over a small amount of time, thereby destroying or preventing non-volatility in the memory cell.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is a schematic-like diagrammatic view of a memory cell accordance with an embodiment of the invention.



FIG. 2 is a diagrammatic sectional view of a memory cell in accordance with an embodiment of the invention.



FIG. 3 is an enlarged cross-sectional view taken through line 3-3 in FIG. 2.



FIG. 4 is an enlarged cross-sectional view taken through line 4-4 in FIG. 2.



FIG. 5 is an enlarged cross-sectional view taken within box 5 in FIG. 2.



FIG. 6 is a diagrammatic cross-sectional view of a memory cell in accordance with an embodiment of the invention.



FIG. 7 is a diagrammatic cross-sectional view of a substrate construction in process in accordance with an embodiment of the invention.



FIG. 8 is a view of the FIG. 7 construction at a processing step subsequent to that shown by FIG. 7.



FIG. 9 is a view of the FIG. 8 construction at a processing step subsequent to that shown by FIG. 8.



FIG. 10 is a view of the FIG. 9 construction at a processing step subsequent to that shown by FIG. 9.



FIG. 11 is a view of the FIG. 10 construction at a processing step subsequent to that shown by FIG. 10.



FIG. 12 is a view of the FIG. 11 construction at a processing step subsequent to that shown by FIG. 11.



FIG. 13 is a view of the FIG. 12 construction at a processing step subsequent to that shown by FIG. 12.



FIG. 14 is a view of the FIG. 13 construction at a processing step subsequent to that shown by FIG. 13.



FIG. 15 is a view of the FIG. 14 construction at a processing step subsequent to that shown by FIG. 14.



FIG. 16 is a view of the FIG. 15 construction at a processing step subsequent to that shown by FIG. 15.





DETAILED DESCRIPTION OF EXAMPLE EMBODIMENTS

A memory cell 9 in accordance with an embodiment of the invention is shown and initially described with reference to a schematic-like FIG. 1. Integrated circuitry (not shown) having memory cell 9 would likely have thousands or millions of such memory cells fabricated relative to a memory array or sub-array, and are not particularly material to the disclosure herein. Such arrays or sub-arrays would likely have a plurality of access lines and digit lines having individual memory cells 9 there-between where such cross. Individual memory cells may be considered as comprising the portions of an individual access line and a crossing individual digit line.


Memory cell 9 comprises a select device 12 and a capacitor 14 electrically coupled in series (i.e., circuit) with select device 12, for example by a conductive (i.e., electrically) path 16 as shown. Capacitor 14 in the depicted diagram may be considered as comprising two conductive capacitor electrodes 18 and 20 having ferroelectric material 19 there-between. Physically, path 16 may simply be a single electrode shared by capacitor 14 and select device 12. Capacitor 14 comprises an intrinsic current (i.e., electrical) leakage path from one of capacitor electrodes 18 or 20 to the other through ferroelectric material 19. Such intrinsic path is diagrammatically shown as a dashed line in a path 22 going around ferroelectric material 19 for clarity in FIG. 1. However in reality, path 22 would intrinsically/inherently be through ferroelectric material 19 to and between each of capacitor electrodes 18 and 20. Intrinsic path 22 will have some comparatively rather high overall/total resistance (i.e., electrical) which is diagrammatically indicated as a resistor 24 as device 14 in operation functions as a capacitor. Total resistance of resistor 24 will depend upon composition of ferroelectric material 19, thickness of ferroelectric material 19, and dipole orientation within ferroelectric material 19. Resistor 24 may inherently be a non-linear/variable resistor whereby its resistance is voltage dependent.


Memory cell 9 comprises a parallel (i.e., circuit-parallel) current leakage path 26 from one capacitor electrode 18 or 20 to the other. In one embodiment, parallel path 26 has a dominant band gap of 0.4 eV to 5.0 eV, and in one embodiment that is less than that of ferroelectric material 19. Such may be greater than dominant band gap of ferroelectric material 19 if parallel path 26 is sufficiently shorter in length than path 22. Regardless, in one embodiment parallel path 26 has some total resistance (e.g., shown as a resistor 28) that is lower than the total resistance of intrinsic path 22. By way of examples only, total resistance through intrinsic leakage path 22 may be 1×1011-1×1018 ohms and total resistance through parallel leakage path 26 may be 1×1011-1×1017 ohms. In one embodiment, the parallel current leakage path is configured so that current there-through when the memory cell is idle is no more than one nanoampere.


Select device 12 may be any existing or yet-to-be-developed select device, including multiple devices. Examples include diodes, field effect transistors, and bipolar transistors. In operation, select device 12 will exhibit current leakage when the memory cell is idle (i.e., when the integrated circuitry associated with memory cell 9 is operationally “on”, but no “read” or “write” operation of memory cell 9 is occurring). A select device current leakage path 30 exists, and is diagrammatically shown as a dashed line around select device 12, although such would be intrinsically/inherently through select device 12 or to underlying substrate (e.g., held at ground or other potential). Leakage path 30 is shown as having some total resistance 32. In one embodiment, parallel path 26 is configured so that current there-through when memory cell 9 is idle is greater than or equal to current leakage through path 30 when memory cell 9 is idle. Such will be dependent upon the construction and materials of select device 12, capacitor 14, parallel path 26, and upon voltages at various points within memory cell 9 in normal operation. Ideally and regardless, such enables voltage at electrodes 18 and 20 to be equal or at least very close to one another (e.g., within 50 millivolts) when idle whereby no or negligible electric field is created within ferroelectric material 19 when memory cell 9 is idle. For example and further, any voltage differential across the capacitor when idle ideally is such that any electric field in ferroelectric material 19 is at least 20 times lower than the intrinsic coercive field of ferroelectric material 19. Such may preclude unintended dipole direction change within ferroelectric material 19. Alternately as examples, such may at least reduce risk of or increase time until unintended dipole direction change within ferroelectric material 19.


In one embodiment, resistor 28 in parallel path 26 is a non-linear resistor between capacitor electrodes 18 and 20 exhibiting overall higher resistance at higher voltages (e.g., between 1 to 5 Volts) than at lower voltages (e.g., less than 250 millivolts). Ideally, such a non-linear resistor is formed towards providing a greater magnitude of reduction of current leakage in parallel path 26 during higher voltage “read” and “write” operations as compared to when idle at lower voltage.


An access line and a digit line (neither being shown) would likely be associated with memory cell 9. For example, select device 12 may be a simple two terminal diode or other two terminal device. A cross point-like array construction may then be used whereby a conductive path 11 as part of first capacitor electrode 18 connects with or is part of an access or digit line (not shown) and a conductive path 13 as part of select device 12 connects with or is part of the other of an access or digit line (not shown). As an alternate example, select device 12 may be a field effect transistor. Then, as an example, conductive path 11 may be part of a capacitor cell electrode 18 that is common to multiple capacitors 14 (not shown) within a memory array or sub-array, component 16 may be one source/drain region of the transistor, and component 13 may be the other. The gate (not shown) of the transistor may be a portion of an access line (not shown), and source/drain component 13 may connect with or be part of a sense line (not shown). Other architectures and constructions could alternately of course be used.



FIGS. 2-5 diagrammatically show an example physical construction of a portion of a memory cell 9 comprising capacitor 14 and parallel current leakage path 26 in accordance with an embodiment of the invention. Like numerals from the above-described embodiments have been used where appropriate, with some differences being indicated with different numerals. FIGS. 2-5 depict a portion of a fragment or construction 10 comprising a base substrate 50 that may include any one or more of conductive/conductor/conducting (i.e., electrically herein), semiconductive, or insulative/insulator/insulating (i.e., electrically herein) materials. Various materials are shown above base substrate 50. Materials may be aside, elevationally inward, or elevationally outward of the depicted FIGS. 2-5 materials. For example, other partially or wholly fabricated components of integrated circuitry may be provided somewhere above, about, or within substrate 50 (e.g., memory cell 9 including capacitor 14 being shown), and are not particularly germane to the inventions disclosed herein. Select device 12 may be electrically coupled to either one of capacitor electrodes 18 or 20, with such shown being schematically connected to electrode 18 through a conductor 56. Regardless, unless otherwise indicated, any of the materials, regions, and structures described herein may be homogenous or non-homogenous, and regardless may be continuous or discontinuous over any material which such overlie. Further, unless otherwise stated, each material may be formed using any suitable existing or yet-to-be-developed technique, with atomic layer deposition, chemical vapor deposition, physical vapor deposition, epitaxial growth, diffusion doping, and ion implanting being examples.


An insulative-comprising material 52 is shown as being above base substrate 50. By way of example only, such is shown as comprising material 53 above base substrate 50, material 54 above material 53, and material 55 above material 54. In this document, unless otherwise indicated, “elevational(ly)”, “higher”, “upper”, “lower”, “top”, “atop”, “bottom”, “above, “below”, “under”, “beneath”, “up”, and “down” are generally with reference to the vertical direction. Further, “vertical” and “horizontal” as used herein are directions that are perpendicular or within 10 degrees of perpendicular relative one another independent of orientation of the substrate in three-dimensional space. “Horizontal” refers to a general direction (i.e., within 10 degrees) along a primary substrate surface and may be relative to which the substrate is processed during fabrication. Also, “extend(ing) elevationally” and “elevationally-extending” in this document encompasses a range from vertical to no more than 45° from vertical. An example material 53 is silicon nitride above silicon dioxide. An example material 54 is doped silicon dioxide, and an example material 55 is silicon nitride. Example thicknesses for materials 53, 54, and 55 are 250 to 500 Angstroms, 0.4 micron to 1.0 micron, and 250 to 500 Angstroms, respectively.


In this document, “thickness” by itself (no preceding directional adjective) is defined as the mean straight-line distance through a given material or region perpendicularly from a closest surface of an immediately adjacent material of different composition or of an immediately adjacent region. Additionally, the various materials or regions described herein may be of substantially constant thickness or of variable thicknesses. If of variable thickness, thickness refers to average thickness unless otherwise indicated, and such material or region will have some minimum thickness and some maximum thickness due to the thickness being variable. As used herein, “different composition” only requires those portions of two stated materials or regions that may be directly against one another to be chemically and/or physically different, for example if such materials or regions are not homogenous. If the two stated materials or regions are not directly against one another, “different composition” only requires that those portions of the two stated materials or regions that are closest to one another be chemically and/or physically different if such materials or regions are not homogenous. In this document, a material, region, or structure is “directly against” another when there is at least some physical touching contact of the stated materials, regions, or structures relative one another. In contrast, “over”, “on”, “adjacent”, “along”, and “against” not preceded by “directly” encompass “directly against” as well as construction where intervening material(s), region(s), or structure(s) result(s) in no physical touching contact of the stated materials, regions, or structures relative one another.


Example construction 10 comprises lower conductor 56 which, for example, may be a conductive line running into and out of the plane of the page upon which FIG. 2 lies, for example an access line or a digit line, or be electrically coupled (in one embodiment, directly electrically coupled) to or part of a select device 12. In this document, regions/materials/components are “electrically coupled” relative one another if in normal operation electric current is capable of continuously flowing from one to the other, and does so predominately by movement of subatomic positive and/or negative charges when such are sufficiently generated. Another electronic component may be between and electrically coupled to the regions/materials/components. In contrast, when regions/materials/components are referred to as being “directly electrically coupled”, no intervening electronic component (e.g., no diode, transistor, resistor, transducer, switch, fuse, etc.) is between the directly electrically coupled regions/materials/components. Example conductive materials for conductor 56, and for any conductive material herein, include one or more of elemental metal, a mixture or alloy of two or more elemental metals, conductive metal compounds, and conductively doped semiconductive materials, with TiN being one specific example for conductor 56.


Capacitor 14 comprises a first conductive capacitor electrode 18 that in one embodiment has laterally-spaced walls 58, 59 that individually have a top surface 60. In one embodiment, first capacitor electrode 18 has a bottom 62 extending laterally to and between laterally-spaced walls 58, 59. Alternately and by way of example only, first capacitor electrode 18 may comprise an upwardly and downwardly-open (not shown) conductive material cylinder (e.g., little or no bottom 62 extending between walls 58, 59). Capacitor 14 includes a second conductive capacitor electrode 20 which in the depicted embodiment is laterally between walls 58, 59 of first capacitor electrode 18. Second capacitor electrode 20 is shown as comprising a conductive material 64 (e.g., TiN), a conductive material 66 (e.g., W), and a conductive material 68 (e.g., TiN). For purposes of the continuing discussion, second capacitor electrode 20 may be considered as comprising a portion 70 that is above first capacitor electrode 18. Portion 70 comprises an elevationally-inner surface 71 that is above first capacitor electrode 18, and in one embodiment of which is an elevationally-innermost surface of portion 70 that is above first capacitor electrode 18. Example thicknesses for constructions/materials 18, 64, 66, 68, and 70 are 30 to 50 Angstroms, 30 to 50 Angstroms, 200 to 400 Angstroms, 300 to 500 Angstroms, and 500 to 900 Angstroms.


Ferroelectric material 19 is laterally between walls 58, 59 of first capacitor electrode 18 and laterally-between second capacitor electrode 20 and first capacitor electrode 18. Example ferroelectric materials include ferroelectrics that have one or more of transition metal oxide, zirconium, zirconium oxide, niobium, niobium oxide, hafnium, hafnium oxide, lead zirconium titanate, and barium strontium titanate, and may have dopant therein which comprises one or more of silicon, aluminum, lanthanum, yttrium, erbium, calcium, magnesium, strontium, and a rare-earth element. An example thickness for ferroelectric material 19 is 15 to 200 Angstroms. As asserted above with respect to FIG. 1, capacitor 14 in FIGS. 2-5 comprises an intrinsic current leakage path 22 from one of the first and second capacitor electrodes to the other through the ferroelectric material.


Parallel path 26 is shown as being encompassed by or within a material 34. Parallel path 26 is shown as extending between a) elevationaily inner surface 71 of portion 70 of second capacitor electrode 20 that is above first capacitor electrode 18, and b) at least one of individual top surfaces 60 (in one embodiment and as shown both top surfaces 60) of laterally-spaced walls 58, 59 of first capacitor electrode 18. As shown, parallel current leakage path 26 is circuit-parallel intrinsic current leakage path 22, and is of lower total resistance than the intrinsic current leakage path. Example materials 34 includes one or more of amorphous silicon, polycrystalline silicon, germanium, chalcogenide (e.g., metal dichalcogenides), silicon-rich silicon nitride, silicon-rich silicon oxide, and intrinsically dielectric material suitably doped with conductivity increasing dopants (e.g., SiO2 and/or Si3N4 doped with one or more of Ti, Ta, Nb, Mo, Sr, Y, Cr, Hf, Zr, W, and lanthanide series ions). Material 34, and thereby parallel path 26, may predominantly (i.e., more than 50 atomic %) comprise such material(s). Any of these materials may be doped or undoped to provide desired total resistance for current leakage flow there-through when memory cell 9 is idle.


In one embodiment, material 34 is homogenous whereby parallel path 26 between capacitor electrodes 18 and 20 is homogenous. In one embodiment, material 34 is non-homogenous whereby parallel path 26 between capacitor electrodes 18 and 20 is non-homogenous. In an embodiment where material 34 and thereby parallel path 26 are non-homogenous, parallel path 26 may have multiple band gaps due to different composition materials therein having different band gaps. Yet, parallel path 26 may have a dominant (meaning controlling) band gap of 0.4 eV to 5.0 eV likely dependent on the respective volumes of the individual different materials within parallel path 26. Accordingly, and regardless, “dominant” is used and applies herein regardless of homogeneity of the particular path/material. In one embodiment, dominant band gap of ferroelectric material 19 may be lower than that of parallel path 26. In one embodiment, minimum length of parallel path 26 is made longer than minimum thickness of ferroelectric material 19. As one example, such a length relationship may be used when density of states in the parallel path is equal to or greater than that in the ferroelectric material when dominant band gaps of the ferroelectric material and parallel path are about the same. As another example, such a length relationship may be used when density of states in the parallel path is equal to or greater than that in the ferroelectric material when dominant band gap of the ferroelectric material is less than that of the parallel path.


In one embodiment and as shown in FIGS. 2-5, material 34 and thereby parallel path 26 are directly against ferroelectric material 19. FIG. 6 depicts an alternate embodiment memory cell 9a wherein parallel path 26 is not directly against ferroelectric material 19. Like numerals from the above-described embodiments have been used where appropriate, with some construction differences being indicated with the suffix “a” or with different numerals. Capacitor 14a is shown as comprising some material 35 (e.g., dielectric material such as silicon dioxide and/or silicon nitride) spaced between materials 34 and 19 whereby parallel path 26 is not directly against ferroelectric material 19. Any other attribute(s) or aspect(s) as described herein and/or shown may be used.


In one embodiment, memory cell 9 comprises a select device, for example a select device 12 schematically shown as electrically coupling (in one embodiment directly electrically coupling) with first capacitor electrode 18 through conductor 56 in FIG. 2. In one such embodiment, in operation, the select device exhibits currents leakage when the memory cell is idle, with the parallel path being configured so that current there-through when the memory cell is idle is greater than or equal to said current leakage of the select device when the memory cell is idle.


In one embodiment, a memory cell comprises a capacitor comprising a first conductive capacitor electrode (e.g., 18, and regardless of whether having laterally-spaced walls). The capacitor comprises a second conductive capacitor electrode (e.g., 20) comprising a portion (e.g., 70) above first capacitor electrode 18. Ferroelectric material (e.g., 19) is between second capacitor electrode 20 and first capacitor electrode 18. The capacitor comprises an intrinsic current leakage path (e.g., 22) from one of the first and second capacitor electrodes to the other through the ferroelectric material. A parallel current leakage path (e.g., 26) is between the second capacitor electrode and the first capacitor electrode. The parallel current leakage path is circuit-parallel the intrinsic path, is of lower total resistance than the intrinsic current leakage path, and comprises an annulus 90 (FIGS. 4-6). In one embodiment, the first capacitor electrode 18 comprises an annulus 91 (FIGS. 3, 5, 6). In one such embodiment, the annulus of the first capacitor electrode is directly against material (e.g., 34) of the parallel current leakage path that is in the shape of the annulus of the parallel current leakage path. In such one embodiment, a longitudinal end 92 of annulus 91 of first capacitor electrode 18 and a longitudinal end 93 of annulus 90 of the material of the parallel current leakage path are directly against one another (FIGS. 5 and 6). In one embodiment, the ferroelectric material comprises an annulus 94 (FIGS. 3-6) laterally inside the first electrode. Any other attribute(s) or aspect(s) as described herein and/or shown may be used.


In one embodiment, a memory cell comprises a capacitor comprising a first conductive capacitor electrode (e.g., 18, and independent of whether having laterally-spaced walls). The capacitor comprises a second conductive capacitor electrode (e.g., 20, and independent of whether comprising a portion above the first capacitor electrode). Ferroelectric material (e.g., 19) is between the second capacitor electrode and the first capacitor electrode. The capacitor comprises an intrinsic current leakage path (e.g., 22) from one of the first and second capacitor electrodes to the other through the ferroelectric material. A circuit-parallel current leakage path (e.g., 26) between the second capacitor electrode and the first capacitor electrode. The circuit-parallel current leakage path is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path. The circuit-parallel current leakage path is physically-parallel and alongside the ferroelectric material from a bottom surface 93 to a top surface 95 (FIGS. 5 and 6) of material (e.g., 34) of the current leakage path. In one embodiment, the circuit-parallel current leakage path is directly against the ferroelectric material. In one such embodiment, the circuit-parallel current leakage path is directly against the ferroelectric material from the bottom surface to the top surface of the material of the current leakage path. Any other attribute(s) or aspect(s) as described herein and/or shown may be used.


Embodiments of the invention encompass methods of forming a capacitor and as well memory cells as identified above independent of method of manufacture. Example such embodiments are described with reference to FIGS. 7-16. Like numerals from above-described embodiments have been used for predecessor materials/constructions that result in a finished construction as shown, for example, in FIGS. 2-5.


Referring to FIG. 7, a capacitor opening 15 has been formed in insulative-comprising material 52. Capacitor opening 15 may be of any one or more shapes in horizontal cross section, for example circular, ellipsoidal, 4-sided (e.g., square or rectangular), 6-sided, a combination of straight and curved sides, etc. Capacitor opening 15 is shown as having straight vertical sidewalls, although such may be non-vertical and/or not straight. An example maximum open dimension for capacitor opening 15 is 300 to 600 Angstroms. Likely several capacitor openings 15 would be formed for forming several capacitors simultaneously. An example technique for forming capacitor opening 15 includes photolithographic patterning and etch with or without pitch multiplication.


Referring to FIG. 8, a conductive lining 18 has been formed in capacitor opening 15 to comprise a first conductive capacitor electrode of a capacitor being formed in capacitor opening 15. In one embodiment and as shown, material of conductive lining 18 extends outwardly of capacitor opening 15 and over an uppermost surface 17 of insulative-comprising material 52.


Referring to FIG. 9, and in one embodiment, capacitor opening 15 with conductive lining 18 therein has been plugged with photoresist 80.


Referring to FIG. 10, photoresist 80 and material of conductive lining 18 that extend outwardly of capacitor opening 15 over uppermost surface 17 have been removed back at least to uppermost surface 17.


Referring to FIG. 11, conductive lining 18 has been elevationaily recessed in capacitor opening 15 relative to uppermost surface 17 of insulative-comprising material 52 thus, for example, completing fabrication of example first capacitor electrode 18. In one embodiment, first capacitor electrode 18 has laterally-opposing walls 58 and 59, and in one embodiment a bottom 62 extending laterally to and between laterally-spaced walls 58 and 59. Such acts of removing can be conducted by any suitable isotropic and/or anisotropic etching chemistry that etches material of lining/first capacitor electrode 18 selectively relative to material 55. In this document, a selective etch or removal is an etch or removal where one material is removed relative to another stated material at a rate of at least 2.0:1. Photoresist 80 is shown remaining within capacitor opening 15 during such removal/recessing, with material 80 also being removed back as shown. FIG. 12 shows subsequent removal of all remaining photoresist 80 (not shown) from capacitor opening 15. Such provides but one example embodiment of forming conductive lining 18 within capacitor opening 15 to have an uppermost surface 60 therein that is below an uppermost surface 17 of insulative-comprising material 52 immediately laterally adjacent capacitor opening 15. Alternate existing or yet-to-be-developed techniques may be used.


Referring to FIG. 13, a current leakage lining 34 has been formed atop recessed conductive lining 18 within capacitor opening 15. In one embodiment and as shown, material of current leakage lining 34 extends outwardly of capacitor opening 15 and over uppermost surface 17 of insulative-comprising material 52. In one embodiment and as shown, current leakage lining 34 has been formed directly against conductive lining 18. In one embodiment, the forming of current leakage lining 34 may be conducted by PVD (physical vapor deposition) that forms material of current leakage lining 34 in an uppermost portion of capacitor opening 15 and not in a lowest portion of capacitor opening 15. Material of current leakage lining 34 may bulge laterally (not shown) toward a radial center of capacitor opening 15 (sometimes commonly known as a “bread-loafing” effect) and is not shown for simplicity in the drawings.


Referring to FIG. 14, ferroelectric material 19 has been formed aside conductive lining 18 and current leakage lining 34 in capacitor opening 15, and which will comprise capacitor insulator material of the capacitor being formed. In one embodiment and as shown, ferroelectric material 19 extends outwardly of capacitor opening 15 and over an uppermost surface 82 of material of current leakage lining 34 laterally outward of capacitor opening 15. In one embodiment and as shown, ferroelectric material 19 is formed directly against current leakage lining 34 in capacitor opening 15. Conductive material 64 has been formed in capacitor opening 15 to comprise a second electrode of capacitor 14 being formed. In one embodiment and as shown, conductive material 64 extends outwardly of capacitor opening 15 over an uppermost surface 84 of ferroelectric material 19 that extends outwardly of capacitor opening 15.


Referring to FIG. 15, material of current leakage lining 34, ferroelectric material 19, and conductive material 64 that are laterally outward of capacitor opening 15 have been removed back at least to elevationally outermost surface 17 of insulative-comprising material 52.


Referring to FIG. 16, conductive material 66 and 68 are shown as having been subsequently deposited and patterned to produce the FIG. 16 construction (the same as that depicted in FIG. 2, but for the select device). Capacitor 14 comprises an intrinsic current leakage path (e.g., 22) from one of the first and second capacitor electrodes to the other through the ferroelectric material. The current leakage lining forms a parallel current leakage path 26 (FIGS. 2, 3, 5, and 6) that is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path, as described above. Any aspect of the method may encompass any of the features described above with respect to a memory cell construction.


CONCLUSION

In some embodiments, a memory cell comprises a capacitor having a first conductive capacitor electrode having laterally-spaced walls that individually have a top surface. A second conductive capacitor electrode is laterally between the walls of the first capacitor electrode, and comprises a portion above the first capacitor electrode. Ferroelectric material is laterally between the walls of the first capacitor electrode and laterally between the second capacitor electrode and the first capacitor electrode. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. A parallel current leakage path is between an elevationally-inner surface of the portion of the second capacitor electrode that is above the first capacitor electrode and at least one of the individual top surfaces of the laterally-spaced walls of the first capacitor electrode. The parallel current leakage path is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path.


In some embodiments, a memory cell comprises a capacitor comprising a first conductive capacitor electrode and a second conductive capacitor electrode comprising a portion above the first capacitor electrode. Ferroelectric material is between the second capacitor electrode and the first capacitor electrode. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. A parallel current leakage path is between the second capacitor electrode and the first capacitor electrode. The parallel current leakage path is circuit-parallel the intrinsic path, of lower total resistance than the intrinsic current leakage path, and comprises an annulus.


In some embodiments, a memory cell comprises a capacitor having a first conductive capacitor electrode and a second conductive capacitor electrode. Ferroelectric material is between the second capacitor electrode and the first capacitor electrode. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. A circuit-parallel current leakage path is between the second capacitor electrode and the first capacitor electrode. The circuit-parallel current leakage path is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path. The circuit-parallel current leakage path is physically-parallel and alongside the ferroelectric material from a bottom surface to a top surface of material of the current leakage path.


In some embodiments, a method of forming a capacitor comprises forming a conductive lining in a capacitor opening in insulative-comprising material to comprise a first capacitor electrode of a capacitor being formed in the capacitor opening. The conductive lining has an uppermost surface within the capacitor opening that is below an uppermost surface of the insulative-comprising material immediately laterally adjacent the capacitor opening. A current leakage lining is formed atop the conductive lining within the capacitor opening. Ferroelectric material is formed aside the conductive lining and the current leakage lining in the capacitor opening. The ferroelectric material comprises capacitor insulator material of the capacitor. Conductive material is formed in the capacitor opening to comprise a second capacitor electrode of the capacitor. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. The current leakage lining forms a parallel current leakage path that is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path.


In some embodiments, a method of forming a capacitor comprises forming a conductive lining in a capacitor opening in insulative-comprising material to comprise a first capacitor electrode of a capacitor being formed in the capacitor opening. Material of the conductive lining extends outwardly of the capacitor opening and over an uppermost surface of the insulative-comprising material. The capacitor opening with the conductive lining therein is plugged with photoresist. The photoresist and the material of the conductive lining extending outwardly of the capacitor opening over an uppermost surface of the insulative-comprising material are removed back at least to the uppermost surface of the insulative-comprising material. The conductive lining in the capacitor opening is elevationally recessed relative to the uppermost surface of the insulative-comprising material. All remaining of the photoresist is removed from the capacitor opening. After removing the photoresist, a current leakage lining is formed atop the recessed conductive lining within the capacitor opening. Material of the current leakage lining extends outwardly of the capacitor opening and over the uppermost surface of the insulative-comprising material. Ferroelectric material is formed aside the conductive lining and the current leakage lining in the capacitor opening. The ferroelectric material extends outwardly of the capacitor opening and over an uppermost surface of the material of the current leakage lining laterally outward of the capacitor opening. The ferroelectric material comprises capacitor insulator material of the capacitor. Conductive material is formed in the capacitor opening and extends laterally outwardly of the capacitor opening over an uppermost surface of the ferroelectric material laterally outward of the capacitor opening. The conductive material comprises a second capacitor electrode of the capacitor. The material of the current leakage lining, the ferroelectric material, and the conductive material that are laterally outward of the capacitor opening are removed back at least to the elevationally outermost surface of the insulative-comprising material. The capacitor comprises an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material. The current leakage lining forms a parallel current leakage path that is circuit-parallel the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path.


In compliance with the statute, the subject matter disclosed herein has been described in language more or less specific as to structural and methodical features. It is to be understood, however, that the claims are not limited to the specific features shown and described, since the means herein disclosed comprise example embodiments. The claims are thus to be afforded full scope as literally worded, and to be appropriately interpreted in accordance with the doctrine of equivalents.

Claims
  • 1. A method comprising: forming a conductive lining in a capacitor opening in insulative-comprising material to comprise a first capacitor electrode of a capacitor being formed in the capacitor opening, the conductive lining having an uppermost surface within the capacitor opening that is below an uppermost surface of the insulative-comprising material immediately laterally adjacent the capacitor opening;forming a current leakage lining atop the conductive lining within the capacitor opening;forming ferroelectric material aside the conductive lining and the current leakage lining in the capacitor opening, the ferroelectric material comprising capacitor insulator material of the capacitor;forming conductive material in the capacitor opening to comprise a second capacitor electrode of the capacitor; andthe capacitor comprising an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material, the current leakage lining forming a parallel current leakage path that is circuit-parallel with the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path.
  • 2. The method of claim 1 comprising forming the current leakage lining directly against the conductive lining.
  • 3. The method of claim 1 comprising forming the conductive lining to comprise a bottom extending laterally to and between laterally-spaced walls of the conductive lining.
  • 4. The method of claim 1 comprising elevationally recessing the conductive lining in the capacitor opening relative to the uppermost surface of the insulative-comprising material immediately laterally adjacent the capacitor opening before forming the current leakage lining.
  • 5. The method of claim 1 comprising: forming material of the conductive lining to extend outwardly of the capacitor opening and over the uppermost surface of the insulative-comprising material;removing the material of the conductive lining that extends over the uppermost surface of the insulative-comprising material back at least to the uppermost surface of the insulative-comprising material; andelevationally recessing the conductive lining in the capacitor opening relative to the uppermost surface of the insulative-comprising material before forming the current leakage lining.
  • 6. The method of claim 1 comprising forming the ferroelectric material directly against the current leakage lining in the capacitor opening.
  • 7. The method of claim 1 comprising forming the parallel current leakage path to have a dominant band gap of 0.4 eV to 5.0 eV and that is less than dominant band gap of the ferroelectric material.
  • 8. The method of claim 1 comprising forming the parallel current leakage path to comprise a non-linear resistor between the first and second capacitor electrodes exhibiting higher resistance at higher voltages than at lower voltages.
  • 9. The method of claim 1 comprising forming the ferroelectric material to have its dominant band gap be equal to or less than that of the parallel current leakage path.
  • 10. The method of claim 1 comprising forming the parallel current leakage path to predominantly comprise one or more of amorphous silicon, polycrystalline silicon, and germanium.
  • 11. The method of claim 1 comprising forming the parallel current leakage path to predominantly comprise one or more chalcogenides.
  • 12. The method of claim 1 comprising forming the parallel current leakage path to predominantly comprise one or more of silicon-rich silicon nitride, silicon-rich silicon oxide, and intrinsically dielectric material doped with conductivity increasing dopants.
  • 13. The method of claim 1 wherein forming the current leakage lining comprises physical vapor deposition that forms material of the current leakage lining in an uppermost portion of the capacitor opening and not in a lowest portion of the capacitor opening.
  • 14. A method comprising: forming a conductive lining in a capacitor opening in insulative-comprising material to comprise a first capacitor electrode of a capacitor being formed in the capacitor opening, material of the conductive lining extending outwardly of the capacitor opening and over an uppermost surface of the insulative-comprising material;plugging the capacitor opening with the conductive lining therein with photoresist;removing the photoresist and the material of the conductive lining extending outwardly of the capacitor opening over an uppermost surface of the insulative-comprising material back at least to the uppermost surface of the insulative-comprising material;elevationally recessing the conductive lining in the capacitor opening relative to the uppermost surface of the insulative-comprising material;removing all remaining of the photoresist from the capacitor opening;after removing the photoresist, forming a current leakage lining atop the recessed conductive lining within the capacitor opening, material of the current leakage lining extending outwardly of the capacitor opening and over the uppermost surface of the insulative-comprising material;forming ferroelectric material aside the conductive lining and the current leakage lining in the capacitor opening, the ferroelectric material extending outwardly of the capacitor opening and over an uppermost surface of the material of the current leakage lining laterally outward of the capacitor opening, the ferroelectric material comprising capacitor insulator material of the capacitor;forming conductive material in the capacitor opening, the conductive material extending laterally outwardly of the capacitor opening over an uppermost surface of the ferroelectric material laterally outward of the capacitor opening, the conductive material comprising a second capacitor electrode of the capacitor;removing the material of the current leakage lining, the ferroelectric material, and the conductive material that are laterally outward of the capacitor opening back at least to an elevationally outermost surface of the insulative-comprising material; andthe capacitor comprising an intrinsic current leakage path from one of the first and second capacitor electrodes to the other through the ferroelectric material, the current leakage lining forming a parallel current leakage path that is circuit-parallel with the intrinsic current leakage path and of lower total resistance than the intrinsic current leakage path.
RELATED PATENT DATA

This patent resulted from a divisional application of U.S. patent application Ser. No. 15/404,576, filed Jan. 12, 2017, entitled “Memory Cells Comprising Ferroelectric Material And Including Current Leakage Paths Having Different Total Resistances”, naming Muralikrishnan Balakrishnan, Beth R. Cook, and Durai Vishak Nirmal Ramaswamy as inventors, the disclosure of which is incorporated by reference.

US Referenced Citations (42)
Number Name Date Kind
5828092 Tempel Oct 1998 A
6144060 Park et al. Nov 2000 A
6249014 Bailey Jun 2001 B1
6337496 Jung Jan 2002 B2
6611014 Kanaya et al. Aug 2003 B1
6635528 Gilbert et al. Oct 2003 B2
6878021 Martin et al. Apr 2005 B1
7001821 Aggarwal et al. Feb 2006 B2
7304339 Chen Dec 2007 B2
7408212 Luan et al. Aug 2008 B1
8193522 Li Jun 2012 B2
8212256 Chen et al. Jul 2012 B2
9761715 Ramaswamy et al. Sep 2017 B2
10163917 Ramaswamy Dec 2018 B2
20010040249 Jung Nov 2001 A1
20010044205 Gilbert et al. Nov 2001 A1
20040099893 Martin et al. May 2004 A1
20040114428 Morikawa Jun 2004 A1
20040129961 Paz De Araujo et al. Jul 2004 A1
20040228172 Rinerson et al. Nov 2004 A1
20050051822 Manning Mar 2005 A1
20050101034 Aggarwal et al. May 2005 A1
20060151771 Asano et al. Jul 2006 A1
20080266949 He et al. Oct 2008 A1
20080273363 Mouli Nov 2008 A1
20090016094 Rinerson et al. Jan 2009 A1
20090026434 Malhotra et al. Jan 2009 A1
20090078979 Kumura et al. Mar 2009 A1
20090153056 Chen et al. Jun 2009 A1
20100129938 Kumura et al. May 2010 A1
20110188281 Siau et al. Aug 2011 A1
20120051137 Hung et al. Mar 2012 A1
20140095853 Sarangshar Apr 2014 A1
20140254276 Tokuhira et al. Sep 2014 A1
20140332750 Ramaswamy et al. Nov 2014 A1
20140346428 Sills et al. Nov 2014 A1
20150028280 Sciarrillo et al. Jan 2015 A1
20150249113 Takagi et al. Sep 2015 A1
20150349255 Pellizzer et al. Dec 2015 A1
20160020389 Ratnam et al. Jan 2016 A1
20160240545 Karda Aug 2016 A1
20190189357 Chavan et al. Jun 2019 A1
Foreign Referenced Citations (3)
Number Date Country
1505043 Jun 2004 CN
100483542 Apr 2009 CN
103746073 Apr 2014 CN
Non-Patent Literature Citations (10)
Entry
Nigo et al., “Conduction Band Caused by Oxygen Vacancies in Aluminum Oxide for Resistance Random Acess Memory”, Journal of Applied Physics vol. 122, 2012, United States, 6 pages.
WO PCT/US2017/068317 IPRP, dated Jul. 16, 2019, Micron Technology Inc.
Katiyar et al., “Electrical Properties of Amorphous Aluminum Oxide Thin Films”, Acta Materialia vol. 55, Dec. 2005, Netherlands, pp. 2617-1622.
Li et al., “Low-Temperature Magnetron Sputter-Deposition, Hardness, and Electrical Resistivity of Amorphous and Crystalline Alumina Thin Films”, Journal of Vacuum Science & Technology A vol. 18, No. 5, Sep.-Oct. 2000, United States, pp. 2333-2338.
Lv et al., “Transition Metal Dichalcogenides and Beyond: Synthesis, Properties, and Applications of Single- and Few-layer Nanosheets”, American Chemical Society Accounts of Chemical Research vol. 48, Dec. 9, 2014, United States, pp. 56-64.
Podgornyi et al., “Leakage Currents in Thin Ferroelectric Films”, Physics of the Solid State vol. 54, No. 5, Dec. 2012, Germany, pp. 911-914.
Schroeder et al., “Hafnium Oxide Based CMOS Compatible Ferroelectric Materials”, ECS Journal of Solid State Science and Technology vol. 2(4), Jan. 28, 2013, United States, pp. N69-N72.
U.S. Appl. No. 16/507,826, filed Jul. 10, 2019, by Mutch et al.
U.S. Appl. No. 16/255,569, filed Jan. 23, 2019, by Calderoni et al.
Junlabhut et al., “Optical Absorptivity Enhancement of SiO2 Thin Film by Ti and Ag Additive”, Energy Procedia vol. 34, Dec. 2013, United Kingdom, pp. 734-739.
Related Publications (1)
Number Date Country
20190355803 A1 Nov 2019 US
Divisions (1)
Number Date Country
Parent 15404576 Jan 2017 US
Child 16527301 US