The semiconductor integrated circuit (IC) industry has experienced exponential growth. Technological advances in IC materials and design have produced generations of ICs where each generation has smaller and more complex circuits than the previous generation. In the course of IC evolution, functional density (i.e., the number of interconnected devices per chip area) has generally increased while geometry size (i.e., the smallest component (or line) that can be created using a fabrication process) has decreased. This scaling down process generally provides benefits by increasing production efficiency and lowering associated costs. Such scaling down has also increased the complexity of processing and manufacturing ICs.
Aspects of the present disclosure are best understood from the following detailed description when read with the accompanying figures. It is noted that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.
The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.
Further, spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.
The gate all around (GAA) transistor structures described below may be patterned by any suitable method. For example, the structures may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers may then be used to pattern the GAA structure.
For advanced technology of semiconductor devices, multiple threshold voltages (Vts) for device function flexibility become more and more important. However, multiple patterning gates (MPGs) to enable multiple Vts face difficulties because of shrinkage of device dimension and cell heights. Multiple Vts are arranged one next to another in various regions of a semiconductor device and may be referred to as mixed Vts. When a wet over-etching is applied to ensure complete removal of the gate material in one region, the gate material in another neighboring region may suffer loss and a patterning boundary is thereby varied. There are challenges in fabrication of MPGs having mixed Vts, especially in advanced semiconductor devices such as Fin Field Effect Transistor (FinFET) devices with nanowires or nanosheets for GAA structures at technology nodes of 3 nm (N3) and below.
Embodiments disclosed herein relate generally to fabricating semiconductor devices with mixed threshold voltages (Vts) boundary isolation of multiple patterning gates and structures formed thereby. The embodiments of the disclosure provide an etching back process to produce mixed Vts boundary isolation of multiple patterning gates. The etching back process uses a sacrificial layer to allow removing a first-type work function layer (e.g., an n-type work function layer) from a neighboring p-type device region without metal gate material loss in the n-type device region. The embodiments of the disclosure can avoid metal gate material loss and prevent from metal gate retreat along the N/P boundary. Therefore, the embodiments of the disclosure can achieve high Vt in both n-type and p-type device regions, better Vt control in terms of Vt level and uniformity for semiconductor devices such as FinFET devices with nanowires or nanosheets for multiple GAA structures having mixed Vts at technology nodes of N3 and below. Moreover, cell height budget of the semiconductor devices can be saved due to minimized lateral material loss of metal gate.
The foregoing broadly outlines some aspects of the embodiments described herein. Some embodiments described herein are described in the context of FinFET devices, and more particularly, in the context of forming mixed Vts boundary isolation of multiple patterning gates for FinFET devices with GAA structures. The GAA structures in the p-type and n-type device regions are formed using the etching back process of a sacrificial layer. Some variations of the exemplary methods and structures are described. A person having ordinary skill in the art will readily understand other modifications may be made that are contemplated within the scope of other embodiments. Implementations of some aspects of the present disclosure may be used in other processes and/or in other devices. Throughout the various views and illustrative embodiments, like reference numbers are used to designate like elements. Although embodiments of the method may be described in a particular order, various other embodiments of the method may be performed in any logical order and may include fewer or more steps than what is described herein.
Referring to
The substrate 202 can be any suitable substrate, and can be processed with various features. In some embodiments, the substrate 202 may be a semiconductor substrate such as a silicon substrate. In some embodiments, the substrate 202 includes various layers, including conductive or insulating layers formed on a semiconductor substrate. The substrate 202 may include various doping configurations. For example, different doping profiles (e.g., n wells, p wells) may be formed on the substrate 202 in regions designed for different device types (e.g., n-type FETs, p-type FETs). The suitable doping may include ion implantation of dopants and/or diffusion processes. The substrate 202 typically has isolation features (e.g., shallow trench isolation (STI) features) interposing the regions providing different device types. The substrate 202 includes other semiconductors such as germanium or diamond. Alternatively, the substrate 202 includes a compound semiconductor such as silicon carbide (SiC), gallium arsenic, gallium phosphide, indium phosphide, indium arsenide, indium antimonide; an alloy semiconductor, such as SiGe, GaAsP, AlInAs, AlGaAs, GaInAs, GaInP, GaInAsP, and/or other suitable materials. Further, the substrate 202 may optionally include an epitaxial layer, may be strained for performance enhancement, may include a silicon-on-insulator structure, and/or have other suitable enhancement features.
The epitaxial stack 204 includes first epitaxial layers 206 of a first composition interposed by second epitaxial layers 208 of a second composition. The materials of the first and second epitaxial layers 206 and 208 may be chosen based on providing differing etch selectivity properties. In some embodiments, the first composition and the second composition are different. In some embodiments, the second epitaxial layers 208 include the same material as the substrate 202. In some embodiments, the first and second epitaxial layers 206 and 208 include a different material than the substrate 202. In some examples, the first epitaxial layer 206 includes SiGe and the second epitaxial layer 208 includes Si. Alternatively, in some embodiments, either of the first and second epitaxial layers 206 and 208 include other materials such as germanium, a compound semiconductor such as SiC, gallium arsenide, gallium phosphide, indium phosphide, indium arsenide, and/or indium antimonide, an alloy semiconductor such as SiGe, GaAsP, AlInAs, AlGaAs, InGaAs, GanP, and/or GaInAsP, or combinations thereof. In various embodiments, the first and second epitaxial layers 206 and 208 are substantially dopant-free (i.e., having an extrinsic dopant concentration less than about 1×1017 cm−3).
As described in more detail below, in an example, channel nanostructures of a transistor are respectively formed using the second epitaxial layers 208. The thickness of the second epitaxial layers 208 is thus chosen based on, for example, manufacturing considerations, transistor performance considerations, and the like. In an example, the thickness of the first epitaxial layers 206 is used to define a space between adjacent channel nanostructures, and the respective thickness of the first epitaxial layers 206 is chosen based on, for example, manufacturing considerations, transistor performance considerations, and the like. In some embodiments, the first and second epitaxial layers 206 and 208 have different thicknesses. Further, the first epitaxial layers 206 may have different thicknesses from one layer to another layer, and the second epitaxial layers 208 may have different thicknesses from one layer to another layer. In some embodiments, the thickness of each of the first and second epitaxial layers 206 and 208 ranges from several nanometers to tens of nanometers. In some embodiments, each of the first epitaxial layers 206 has a thickness ranging from about 10 nm to about 20 nm. In some embodiments, each of the second epitaxial layers 208 has a thickness ranging from about 5 nm to 12 nm.
The number of epitaxial layers depends on the desired number of channel nanostructures for the semiconductor device 200. In some embodiments, the number of second epitaxial layers 208 is from 2 to 10, for example, to form a stack of 2 to 10 channel nanostructures. In some embodiments and as illustrated in
In some embodiments, the first and second epitaxial layers 206 and 208 are epitaxially grown layer-by-layer from a top surface of the substrate 202. In an example, each of the first and second epitaxial layers 206 and 208 are grown by a molecular beam epitaxy (MBE) process, a chemical vapor deposition (CVD) process such as a metal organic CVD (MOCVD) process, and/or other suitable epitaxial growth processes. The epitaxial growth results in the first and second epitaxial layers 206 and 208 having the same crystal orientation as the substrate 202.
As also shown in the example of
Referring to
In some embodiments, the device fins include a first device fin 210A disposed in a first region of the semiconductor device 200 and a second device fin 210B disposed in a second region of the semiconductor device 200. In some embodiments, the first region is a first-type device region such as an n-type metal-oxide-semiconductor (NMOS) region 200A, and the second region is a second-type device region such as a p-type metal-oxide-semiconductor (PMOS) region 200B. It should be noted that although a single first device fin 210A is illustrated in the NMOS region 200A and a single second device fin 210B is illustrated in the PMOS region 200B, any number of the device fins can be formed in each of the NMOS region 200A and the PMOS region 200B. It should also be noted that although the first-type device region is illustrated as an NMOS region and the second-type device region is illustrated as a PMOS region, the first-type device region can also be a PMOS region and the second-type device region can also be an NMOS region.
The device fins 210A and 210B protrude upwards from the substrate 202 in z-direction. In various embodiments, each of the device fins 210A and 210B includes a fin base 202F and a fin stack 204F on the fin base 202F. The fin base 202F is formed from the substrate 202, while the fin stack 204F is formed from the epitaxial stack 204. The fin stack 204F includes portions of the first epitaxial layers 206 and the second epitaxial layers 208. As shown in
In some embodiments, the device fins 210A and 210B are fabricated using suitable processes including photolithography and etch processes. During a photolithography process, a photoresist layer is first applied to the hard mask layer 209 by, for example, spin coating. Then, the photoresist layer is exposed according to a mask of patterns, and is developed to form the patterns in the photoresist layer. The photoresist layer with the patterns can be used as an etch mask to pattern other layers. In some embodiments, patterning the photoresist layer is performed using an extreme ultraviolet light lithography process. The patterned photoresist layer is then used to protect regions of the substrate 202 and layers 206, 208 formed thereupon, while an etching process forms trenches 214 in unprotected regions through the hard mask layer 209, through the epitaxial stack 204, and into the substrate 202, thereby leaving the device fins 210A and 210B. In some examples, the trenches 214 are formed using a dry etch such as reactive ion etching (RIE), a wet etch, or a combination thereof.
In various other embodiments, the device fins 210A and 210B may be formed by any suitable method. For example, the device fins 210A and 210B may be patterned using one or more photolithography processes, including double-patterning or multi-patterning processes. Generally, double-patterning or multi-patterning processes combine photolithography and self-aligned processes, allowing patterns to be created that have, for example, pitches smaller than what is otherwise obtainable using a single, direct photolithography process. For example, in one embodiment, a sacrificial layer is formed over a substrate and patterned using a photolithography process. Spacers are formed alongside the patterned sacrificial layer using a self-aligned process. The sacrificial layer is then removed, and the remaining spacers, or mandrels, may then be used to pattern the epitaxial stack 204 to provide the device fins 210A and 210B.
Referring to
The isolation structures 216 may include one or more dielectric materials. Examples of dielectric materials for formation of the isolation structures 216 include, but are not limited to, silicon oxide, silicon nitride, silicon oxynitride, fluoride-doped silicate glass (FSG), a low dielectric constant (low-k) dielectric material, and/or other suitable dielectric materials. The dielectric material may be deposited by any suitable technique such as CVD, flowable CVD (FCVD), or spin coating to fill the trenches 214. After the deposition process, a planarization process such as a chemical mechanical polishing (CMP) process is performed on the deposited dielectric material to remove the dielectric material from the top surface of the hard mask layer 209 so that isolation structures 216 may be coplanar with the hard mask layer 209.
Referring
Unlike the device fins 210A and 210B configured to provide active regions, the dielectric fin 218 is inactive and not configured to form an active region. The dielectric fin 218 is formed within the isolation structure 216 between the first and the second device fins 210A and 210B for preventing the epitaxial source/drain bridging of an n-type FET formed in the NMOS region 200A and a p-type FET formed in the PMOS region 200B subsequently formed. In some embodiments, the dielectric fin 218 is placed in the middle of the first device fin 210A and the second device fin 210B, for example, with distances S1 and S2 having a difference smaller than about 20% or smaller than about 10% percent of either of distances S1 and S2. With the dielectric fin 218 being in the middle of the first device fin 210A and the second device fin 210B, both S1 and S2 may be kept minimal while still leaving adequate spacing between the p-type and n-type FETs, and hence the density of the resulting FETs may be maximized.
To form dielectric fin 218, in some embodiments, a trench is first formed in the corresponding isolation structure 216 between the first and the second device fins 210A and 210B using photolithography and etching processes. The bottom surface of the trench may be higher than or level with the bottom surfaces of the isolation structure 216 between the first and the second device fins 210A and 210B. The trench is then filled with one or more dielectric materials such as silicon carbide nitride (SiCN), silicon oxycarbide (SiOC), silicon oxycarbon nitride (SiOCN), a metal oxide, such as hafnium oxide, zirconium oxide, and aluminum oxide, and/or other suitable dielectric materials using a deposition process, such as CVD, FCVD, PVD, or ALD. Following the deposition, a planarization process such as a CMP process may be performed to remove the excess dielectric material. After the planarization process, the isolation structures 216, the dielectric fin 218, and the hard mask layer 209 may have coplanar top surfaces.
Referring to
The STI structures 216P surrounds the dielectric fin 218 and the fin bases 202F. In some embodiments, the recessing process includes a dry etching process, a wet etching process, or a combination thereof. In some embodiments, the recessing depth is controlled (e.g., by controlling an etching time) so as to result in a desired height of the exposed upper portions of the first and second device fins 210A and 210B. In some embodiments, after recessing, the top surfaces of the STI structures 216P may be lower than or level with the top surfaces of the fin bases 202F so that the recessing exposes each of the first and second epitaxial layers 206 and 208 of the fin stack 204F.
The hard mask layer 209 may also be removed before, during, and/or after recessing of the isolation structures 216. In some embodiments, the hard mask layer 209 is removed by a CMP process performed prior to the recessing of the isolation structures 216. In some embodiments, the hard mask layer 209 is removed by an etchant used to recess the isolation structures 216.
The recessing of the isolation structures 216 also forms trenches 219 that separate the device fin 210A or 210B from the dielectric fin 218. In some embodiments, the device fins 210A, 210B may have a width W1 ranging from about 20 nm to about 100 nm, the dielectric fin 218 may have a width W2 ranging from about 5 nm to about 12 nm. A ratio of the width W1 of the device fins 210A and 210B over the width W2 of the dielectric fin 218 is set to be from about 4:1 to about 7:1. If the ratio is too great, the dielectric fin 218 may be too thin for enough mechanical strength. If the ratio is too small, the dielectric fin 218 may be too wide which increases fin pitch and enlarges circuit area. The width W3 of the trenches 219 is set to minimize the fin pitch while functioning as an end cap for the first and second device fins 210A and 210B. In some embodiments, the trenches 219 may have a width W3 less than about 12 nm.
Referring to
The sacrificial gate structure 220 is formed over the device fins 210A and 210B and the dielectric fin 218. In some embodiments, the sacrificial gate structure 220 is disposed along the sidewalls and over the top surfaces of the device fins 210A and 210B and the dielectric fin 218. In some embodiments, the sacrificial gate structure 220 includes a sacrificial gate stack (222, 224) and gate spacers 226 formed along the sidewalls of the sacrificial gate stack (222, 224). According to embodiments of the present disclosure, the sacrificial gate stack (222, 224) will be replaced with replacement gate stacks in a gate-last process to form GAA structures without metal gate material loss and having excellent mixed Vts boundary isolation for meal gates in the respective NMOS region 200A and PMOS region 200B.
The sacrificial gate stack (222, 224) defines the channel region of a GAA device in each of the NMOS region 200A and the PMOS region 200B. In some embodiments, the sacrificial gate stack (222, 224) includes a sacrificial gate dielectric 222 and a sacrificial gate electrode 224 over the sacrificial gate dielectric 222. In some embodiments, the sacrificial gate dielectric 222 may further include a sacrificial gate cap on top of the sacrificial gate electrode 224.
In some embodiments, the sacrificial gate dielectric 222 may be made of silicon oxide, silicon nitride, or silicon oxynitride. The sacrificial gate electrode 224 may be made of silicon such as polycrystalline silicon or amorphous silicon. In some embodiments, the sacrificial gate stack (222, 224) is formed by first blanketly depositing a sacrificial gate dielectric layer over the device fins 210A and 210B, the dielectric fin 218 and the STI structures 216P. A sacrificial gate electrode layer is then blanketly deposited on the sacrificial gate dielectric layer such that the device fins 210A and 210B and the dielectric fin 218 are fully embedded in the sacrificial gate electrode layer. In some embodiments, the thickness of the sacrificial gate dielectric layer is in a range from about 1 nm to about 5 nm in some embodiments. The thickness of the sacrificial gate electrode layer is in a range from about 100 nm to about 200 nm in some embodiments. In some embodiments, the sacrificial gate electrode layer is subjected to a planarization operation. The sacrificial gate dielectric layer and the sacrificial gate electrode layer may be deposited using CVD including LPCVD and PECVD, PVD, ALD, or other suitable process. Subsequently, the sacrificial gate dielectric layer and the sacrificial gate electrode layer are patterned using photolithography and etching processes. For example, a photoresist layer (not shown) is applied over the sacrificial electrode layer and lithographically patterned by lithographic exposure and development. The pattern in the photoresist layer is sequentially transferred into the sacrificial electrode layer and the sacrificial dielectric layer by at least one anisotropic etch, thereby forming the sacrificial gate stack (222, 224). The anisotropic etch may be a dry etch, for example RIE, a wet etch, or a combination thereof. If not completely consumed, the remaining photoresist layer after formation of the sacrificial gate stacks (222, 224) is removed by, for example, ashing. By patterning the sacrificial gate stack (222, 224), the fin stack 204F of the first and second epitaxial layers 206 and 208 are partially exposed on opposite sides of the sacrificial gate stack (222, 224), thereby defining source/drain regions. In this disclosure, a source and a drain are interchangeably used and the structures thereof are substantially the same.
In some embodiments, the gate spacers 226 include a dielectric material such as, for example, an oxide, a nitride, an oxynitride, or combinations thereof. In some embodiments, the gate spacers 226 are made of silicon nitride. In some embodiments, the gate spacers 226 are formed by first depositing a conformal gate spacer material layer on exposed surfaces of the sacrificial gate stack (222, 224), the device fins 210A and 210B, the dielectric fin 218, and the STI structures 216P and then etching the gate spacer material layer to remove horizontal portions of the gate spacer material layer. In some embodiments, the gate spacer material layer is deposited, for example, by CVD, PECVD, or ALD. In some embodiments, the gate spacer material layer is etched by dry etch such as, for example, ME. Vertical portions of the gate spacer material layer present on the sidewalls of sacrificial gate stack (222, 224) constitute the gate spacers 226.
Referring to
The recesses 230 expose the substrate 202 where the source/drain structures will be formed. The recesses 230 may be formed using an anisotropic etching process such as plasma etching, RIE or other suitable dry etching processes. Alternatively, the anisotropic etching process may be a wet etching process that uses an etchant solution such as ammonium hydroxide-peroxide water mixture (APM), tetramethylammonium hydroxide (TMAH), ammonium hydroxide (NH4OH), or another etchant. In some embodiments, the substrate 202 is also partially etched. Accordingly, the bottom surfaces of the recesses 230 may be leveled with the top surface of the fin base 202F or lower than the top surface of the fin base 202F.
Referring to
The cavities 232 are formed between the second epitaxial layers 208 beneath the sacrificial gate structure 220. In some embodiments, a wet etching process is performed to selectively remove the portions of the first epitaxial layers 206 that underlie the gate spacers 226, thereby forming the cavities 232. In some embodiments, the amount of the first epitaxial layers 206 etched is controlled so that the lateral etching distance is no greater than the width of the gate spacers 226. Depending on the materials forming the first and the second epitaxial layers 206, 208, the wet etching process may use an etchant such as, but not limited to, ammonium hydroxide (NH4OH), tetramethylammonium hydroxide (TMAH), ethylenediamine pyrocatechol (EDP), or potassium hydroxide (KOH) solutions. Alternatively, operation 116 may first selectively oxidize lateral ends of the first epitaxial layers 206 that are exposed in the recesses 230 to increase the etching selectivity between the first epitaxial layers 206 and the second epitaxial layer 208. In some examples, the oxidation process may be performed by exposing the semiconductor device 200 to a wet oxidation process, a dry oxidation process, or a combination thereof.
Referring to
In an example, the inner spacer layer 234 is a conformal dielectric layer formed on the lateral ends of the first and second epitaxial layers 206 and 208. In some embodiments, the inner spacer layer 234 wraps around the gate spacers 226 and fills the cavities 232. The inner spacer layer 234 may include silicon oxides, silicon nitrides, silicon carbides, silicon carbide nitride, silicon oxide carbide, silicon carbide oxynitride, and/or other suitable dielectric materials. The inner spacer layer 234 can be formed by ALD or any other suitable methods. By conformally forming the inner spacer layer 234, the size of cavity 232 is reduced or completely filled.
Referring to
The inner spacers 236 fill the cavities 232, contacting end surfaces of the first epitaxial layers 206. An etching process is performed to remove the portions of the inner spacer layer 234 from the sidewalls of the second epitaxial layer 208. Portions of the inner spacer layer 234 remaining in the cavities 232 constitute the inner spacers 236. In some embodiments, a wet etching process is performed using an etchant such as, for example, buffered hydrofluoric acid (BHF), hydrofluoric acid (HF), hydrofluoric nitric acid (HNA), phosphoric acid, HF diluted by ethylene glycol (HFEG), hydrochloric acid (HCl), or any combination thereof.
Referring to
In the NMOS region 200A, the first source/drain structures 242 are on opposite sides of the sacrificial gate structure 220, in contact with the second epitaxial layers 208 and separated from the first epitaxial layers 206 by the inner spacers 236. In the PMOS region 200B, the second source/drain structures 244 are on opposite sides of the sacrificial gate structure 220, in contact with the second epitaxial layers 208 and separated from the first epitaxial layers 206 by the inner spacers 236.
In some embodiments, the first source/drain structures 242 in the NMOS region 200A include an n-doped semiconductor material for an n-type FET and the second source/drain structures 244 in the PMOS region 200B include a p-doped semiconductor material for a p-type FET. The first source/drain structures 242 in the NMOS region 200A and the second source/drain structures 244 in the PMOS region 200B may include the same or different semiconductor materials. Exemplary semiconductor materials include, but are not limited to, silicon germanium (SiGe), silicon carbide (SiC), silicon phosphorus, germanium, an III-V compound semiconductor, and an II-VI compound semiconductor. The materials of an III-V compound semiconductor may include InAs, AlAs, GaAs, InP, GaN, InGaAs, InAlAs, GaSb, AlSb, AlP or GaP. In some examples, the first source/drain structures 242 in the NMOS region 200A are made of n-doped SiC, and the second source/drain structures 244 in the PMOS region 200B are made of p-doped SiGe. Exemplary n-type dopants include, but are not limited to, P, As, and Sb. Exemplary p-type dopants include, but are not limited to, B, Al, Ga, and In.
The first source/drain structures 242 in the NMOS region 200A and the second source/drain structures 244 in the PMOS region 200B may be independently formed by metal-organic CVD (MOCVD), molecular beam epitaxy (MBE), liquid phase epitaxy (LPE), vapor phase epitaxy (VPE), selective epitaxial growth (SEG), or a combination thereof. The source/drain structures 242 and 244 may have several facets. In addition, the first source/drain structures 242 and the second source/drain structures 244 may be independently doped by in-situ doping during the epitaxial growth and/or by implantation after the epitaxial growth. In some instances, the top surfaces of the source/drain structures 242 and 244 may be higher than or at the same level with a top surface of a topmost second epitaxial layer 208 in the fin stack 204F.
Referring to
In some embodiments, the ILD layer 250 includes a low-k dielectric material, such as tetraethylorthosilicate (TEOS), un-doped silicate glass, or doped silicon oxide such as borophosphosilicate glass (BPSG), fused silica glass (FSG), phosphosilicate glass (PSG), boron doped silicon glass (BSG), other suitable dielectric materials, or combinations thereof. The ILD layer 250 may include a multi-layer structure having multiple dielectric materials and may be formed by a deposition process such as, for example, CVD, flowable CVD (FCVD), spin-on coating, other suitable methods, or combinations thereof. In some embodiments, forming the ILD layer 250 further includes performing a CMP process to planarize a top surface of the ILD layer 250, such that the top surface of the sacrificial gate structure 220 is exposed.
Referring to
The gate trench 254 exposes portions of the device fins 210A and 210B in the channel regions. The ILD layer 250 protects the source/drain structures 242 and 244 during the removal of the sacrificial gate dielectric 222 and the sacrificial gate electrode 224. The sacrificial gate dielectric 222 and the sacrificial gate electrode 224 may be removed using one or more selective etching processes. Each etching process can be a dry etch, a wet etch, or a combination thereof. In instances where the sacrificial gate electrode 224 is polysilicon and the ILD layer 250 is silicon oxide, a wet etchant such as a TMAH solution can be used to selectively remove the sacrificial gate electrode 224. The sacrificial gate dielectric 222 is thereafter removed using plasma dry etching and/or wet etching.
Referring to
The first epitaxial layers 206 may be removed or etched using an etchant that can selectively etch the first epitaxial layers 206 against the second epitaxial layers 208. In some embodiments, the selective removal process includes oxidizing the first epitaxial layers 206 using a suitable oxidizer, such as ozone. Thereafter, the oxidized first epitaxial layers 206 may be selectively removed from the gate trench 254. In some other embodiments, the selective removal process includes a dry etching process. In some embodiments, when the second epitaxial layers 208 include silicon and the first epitaxial layers 206 include silicon germanium, the first epitaxial layer 206 may be selectively removed by applying an HCl gas at a temperature of about 500° C. to about 700° C., or applying a gas mixture of CF4, SF6, and CHF3. The inner spacers 236 serve as etch stop layers to protect the source/drain structures 242 and 244 during removal of the first epitaxial layers 206 in the gate trench 254. As a result, the remaining second epitaxial layers 208 form the first channel nanostructures 256A in the NMOS region 200A and the second channel nanostructures 256B in the PMOS region 200B. The channel nanostructures 256A and 256B may be nanowires or nanosheets.
The removal of the first epitaxial layers 206 also forms multiple spaces 258 between the channel nanostructures 256A and 256B. The spaces 258 define spacing (ss) between adjacent channel nanostructures 256A and 256B. In some embodiments, the spacing (ss) between the adjacent channel nanostructures 256A and 256B is less than about 12 nm.
Referring to
In some embodiments, the gate dielectric layer (260, 262) includes multiple layers. In an example, the gate dielectric layer (260, 262) includes an interfacial layer 260 and a high-k dielectric layer 262. In some embodiments, the interfacial layer 260 wraps around each of channel nanostructures 256A in the NMOS region 200A and each of channel nanostructures 256B in the PMOS region 200B. The high-k dielectric layer 262 wraps around the respective interfacial layers 260. Note that the spaces 258 between the respective first and second channel nanostructures 256A and 256B are reduced.
In some embodiments, the interfacial layer 260 includes a dielectric material such as silicon oxide. In some embodiments, the interfacial layer 260 is formed by chemical oxidation or thermal oxidation of surface portions of the channel nanostructures 256A and 256B and substrate 202. Alternatively, in some embodiments, the interfacial layer 260 is formed by deposition of a dielectric material using ALD, CVD, and/or other suitable methods. Accordingly, the interfacial layer 260 is also deposited on a portion of the dielectric fin 218 that is exposed by the gate trench 254. In some embodiments, the interfacial layer 260 is formed to have a thickness ranging from about 0.5 nm to about 1.5 nm.
In some embodiments, the high-k dielectric layer 262 includes a high-k dielectric material having a dielectric constant greater than silicon oxide. Examples of high-k dielectric materials include, but are not limited to, hafnium oxide (HfO2), hafnium silicon oxide (HfSiO), hafnium silicon oxynitride (HfSiON), hafnium tantalum oxide (HMO), hafnium titanium oxide (HMO), hafnium zirconium (HfZrO), zirconium oxide (ZrO2), aluminum oxide (Al2O3), titanium oxide (TiO2), and hafnium oxide-alumina (HfO2—Al2O3) alloy. The high-k dielectric layer 262 may be formed by CVD, ALD or other suitable methods. In some embodiments, the high-k dielectric layer 262 is formed using a conformal deposition process such as ALD in order to ensure the high-k dielectric layer 262 having a uniform thickness around each channel nanostructure 256A, 256B. In some embodiments, the high-k dielectric layer 262 is formed to have a thickness ranging from about 1 nm to about 1.5 nm.
Referring to
The sacrificial layer 264 is formed to fully fill the trenches 219 and the spaces 258 in both the NMOS region 200A and the PMOS region 200B. The sacrificial layer 264 thus merges the dielectric fin 218 and the channel nanostructures 256A and 256B as well as adjacent channel nanostructures 256A and 256B. In some embodiments, the sacrificial layer 264 has a thickness ranging from about 2 nm to about 6 nm. The sacrificial layer 264 may include a material that can be selectively etched relative to the high-k dielectric layer 262. In some embodiments, the sacrificial layer 264 includes an oxide such as silicon oxide, aluminum oxide, or zirconium oxide or a nitride such as silicon nitride or titanium nitride. In some embodiments, the sacrificial layer 264 is deposited by deposition process such as, for example, CVD, PECVD, PVD, or ALD.
Referring to
In some embodiments, an isotropic etch such as a wet etch is performed to recess the sacrificial layer 264. After recessing, the top surface of the sacrificial layer 264 may be lower or leveled with the top surface of the topmost first channel nanostructure 256A in the NMOS region 200A and the top surface of the topmost second channel nanostructure 256B in the PMOS region 200B. The top surface of the sacrificial layer 264 may also be lower than the top surface of the dielectric fin 218. In some embodiments, the top surface of the sacrificial layer 264 is below the top surface of the dielectric fin 218 in a range from about from 3 nm to about 5 nm.
In the present disclosure, because the portion of the high-k dielectric layer 262 on the top surface of each of the topmost first channel nanostructure 256A in the NMOS region 200A and the topmost second channel nanostructure 256B in the PMOS region 200B not covered by the sacrificial layer 264 is exposed to the etchant during the recessing of the sacrificial layer 264, the thickness of the portion of the high-k dielectric layer 262 on the top surface of each of the topmost first and second channel nanostructures 256A and 256B is reduced compared to portions of the high-k dielectric layer 262 on sidewall and bottom surfaces of the topmost first and second channel nanostructures 256A, 256B, as well as on the underlying first and second channel nanostructures 256A and 256B that remain covered by the sacrificial layer 264.
Referring to
The hard mask layer 266 may include a material that can be selectively removed relative to the sacrificial layer 264 and the high-k dielectric layer 262. In some embodiments, the etching selectivity between the hard mask layer 266 and the sacrificial layer 264 is greater than 300, and the etching selectivity between the hard mask layer 266 and the high-k dielectric layer 262 is greater than 500. In some embodiments, the hard mask layer 266 includes silicon oxide, aluminum oxide, zirconium oxide, silicon nitride, or titanium nitride. The hard mask layer 266 may be deposited by a conformal deposition process such as CVD or ALD. In some embodiments, the hard mask layer 266 is formed to have a thickness ranging from about 1 nm to about 5 nm. If the thickness of the hard mask layer 266 is too small, it cannot function as an etching mask during the subsequent etching process, in some instances. If the thickness of the hard mask layer 266 is too great, production costs are increased as a result of unnecessary consumption of material and increased processing time to pattern the hard mask layer 266, in some instances.
In the present disclosure, because the hard mask layer 266 is only deposited on portions of the high-k dielectric layer 262 that are not covered by the sacrificial layer 264, the portion of the high-k dielectric layer 262 on the top surface of each of the topmost first and second channel nanostructures 256A, 256B may contain elements providing the hard mask layer 266. Accordingly, the portion of the high-k dielectric layer 262 on the top surface of each of the topmost first and second channel nanostructures 256A, 256B may have a different composition from the portions of the high-k dielectric layer 262 on sidewall and bottom surfaces of the topmost first and second channel nanostructures 256A, 256B, as well as on the underlying first and second channel nanostructures 256A and 256B that remain covered by the sacrificial layer 264.
Referring to
The patterned hard mask layer 266P covers a portion of the sacrificial layer 264 in the PMOS region 200B, while exposing another portion of the sacrificial layer 264 in the NMOS region 200A. In some embodiments and as shown in
In some embodiments, prior to etching the hard mask layer 266, a patterned mask layer 270 is formed to cover the PMOS region 200B, while exposing the NMOS region 200A. In an example, the patterned mask layer 270 includes a patterned photoresist layer and is formed by a lithography process. In another example, the patterned mask layer 270 includes a patterned anti-reflective coating (ARC) layer. The patterned ARC layer is formed by depositing an ARC material layer, forming a patterned photoresist layer by a lithography process and etching the ARC material layer through the pattered photoresist layer to form the ARC layer. Subsequently, a portion of the hard mask layer 266 in the NMOS region 200A that is exposed by the patterned mask layer 270 is removed, while leaving the portion of the hard mask layer 266 in the PMOS region 200B intact. In some embodiments, removal of the hard mask layer 266 is performed using an anisotropic etching process which can be a dry etch, a wet etch, or a combination thereof. The remaining portion of the hard mask layer 266 in the PMOS region 200B constitutes the patterned hard mask layer 266P. After formation of the patterned hard mask layer 266P, the patterned mask layer 270 is removed by an etching process such as plasma etch.
The thickness of the portion of the high-k dielectric layer 262 on the top surface of the topmost first channel nanostructure 256A may be reduced by the etching chemistry used to patterning the hard mask layer 266.
Referring to
The removal of the sacrificial layer 264 from the NMOS region 200A re-exposes the portion of the high-k dielectric layer 262 in the NMOS region 200A. In some embodiments, the portion of the sacrificial layer 264 in the NMOS region 200A that is not covered by the patterned hard mask layer 266P is removed by an etching process. The etching process may include an isotropic etch with an adequate etching selectivity with respect to the patterned hard mask layer 266P to minimize loss of sidewalls of the patterned hard mask layer 266P during the etching process. In some embodiments, the etching selectivity between the patterned hard mask layer 266P and the sacrificial layer 264 is greater than 300. As a result, after etching, the boundary between the patterned hard mask layer 266P and the underlying sacrificial layer 264 in the PMOS region 200B is kept. In some embodiments, a wet etch is performed to selectively etching the sacrificial layer 264 without substantially affecting the high-k dielectric layer 262 and the patterned hard mask layer 266P. The remaining portion of the sacrificial layer 264 in the PMOS region 200B herein refers to as a sacrificial layer portion 264P.
Referring to
The removal of the patterned hard mask layer 266P exposes the sacrificial layer portion 264P remaining in the PMOS region 200B. In some embodiments, the patterned hard mask layer 266P is removed by an etching process which can be a dry etch, a wet etch, or a combination thereof. In some embodiments, a dry etch such as RIE is performed to remove the patterned hard mask layer 266P from the structure. In some embodiments, the etching process also etches the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B, thereby reducing the thickness of the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B. The portions of the high-k dielectric layer 262 on the sidewall and bottom surfaces of the topmost first channel nanostructure 256A, as well as on the underlying first channel nanostructures 256A that remain covered by the sacrificial layer 264, are intact.
Referring to
The n-type work function layer 272 is formed as a conformal layer and disposed over the high-k dielectric layer 262, the sacrificial layer portion 264P and the dielectric fin 218. In the NMOS region 200A, the n-type work function layer 272 wraps around the first channel nanostructures 256A. In the PMOS regions 200B, since the sacrificial layer portion 264P seals the gaps between the second channel nanostructures 256B and the dielectric fin 218, the n-type work function layer 272 is only present on top of the sacrificial layer portion 264P and on the portion of the high-k dielectric layer 262 on the topmost second channel nanostructure 256B not covered by the sacrificial layer portion 264P. Accordingly, the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B may contain elements providing the n-type work function layer 272. The thickness of the n-type work function layer 272 is controlled such that in the NMOS region 200A, the n-type work function layer 272 fully fills the spaces 258 between adjacent first channel nanostructures 256A, while the trenches 219 between the first channel nanostructures 256A and the dielectric fin 218 are only partially filled. As a result, the n-type work function layer 272 merges the adjacent first channel nanostructures 256A, but does not merge the first channel nanostructures 256A and the dielectric fin 218. In some embodiments, the n-type work function layer 272 has a thickness ranging from about 1.5 nm to about 5 nm.
The n-type work function layer 272 is adapted to tune the threshold voltage Vt1 for an n-type FET formed in the NMOS region 200A. In some embodiments, the n-type work function layer 272 includes titanium aluminum carbide (TiAlC), titanium aluminum (TiAl), tantalum aluminum carbide (TaAlC), tantalum carbide (TaC), tantalum aluminum silicon carbide (TaAlSiC), or titanium aluminum silicon carbide (TiAlSiC). In various embodiments, the n-type work function layer 272 may be formed by a conformal deposition method such as, for example, ALD or CVD.
Referring to
In some embodiments, prior to the removal of the portion of the n-type work function layer 272 in the PMOS region 200B, a patterned mask layer 280 is formed to cover the NMOS region 200A, while exposing the PMOS region 200B. In an example, the patterned mask layer 280 includes a patterned photoresist layer and is formed by a lithography process. In another example, the patterned mask layer 280 including a patterned ARC layer. The patterned ARC layer is formed by depositing an ARC material layer, forming a patterned photoresist layer by a lithography process and etching the ARC material layer through the pattered photoresist layer to form the patterned ARC layer. The patterned mask layer 280 partially overlaps the dielectric fin 218 between the NMOS region 200A and the PMOS region 200B.
Subsequently, the portion of the n-type work function layer 272 in the PMOS region 200B that is exposed by the patterned mask layer 280 is removed, while leaving the portion of the n-type work function layer 272 in the NMOS region 200A intact. In some embodiments, the portion of the n-type work function metal layer 272 in the PMOS region 200B is removed using an anisotropic etching process. The anisotropic etch can be a dry etch such as RIE, a wet etch, or a combination thereof. In some embodiments, the anisotropic etching process used to etching the n-type work function layer 272 also etches the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B, thereby reducing the thickness of the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B. In some embodiments, the portion of the high-k dielectric layer 262 on the top surface of the topmost second channel nanostructure 256B is thinner than the portion of the high-k dielectric layer 262 on the top surface of the topmost first channel nanostructure 256A for about 1 Å.
In embodiments of the present disclosure, due to the presence of the sacrificial layer portion 264P that prevents the n-type work function layer 272 from being deposited into the gaps between the second channel nanostructures 256B and the dielectric fin 218 in the PMOS region 200B, strong etching that is required for the complete removal of the n-type work function material from the gaps between the second channel nanostructures 256B and the dielectric fin 218 in the PMOS region 200B but would result in over-etching of the n-type work function material in the NMOS region 200A is no longer needed. As a result, the gate metal loss caused by the over-etching of the work function material in the NMOS region 200A is avoided. The end of the remaining n-type work function layer 272 can be thus kept at the boundary of the NMOS region 200A and the PMOS region 200B. In some embodiments and as shown in
Referring to
As shown in
Referring to
The p-type work function layer 282 is conformally deposited on the high-k dielectric layer 262 in the PMOS region 200B and the n-type work function layer 272 in the NMOS region 200A. In the PMOS region 200B, the p-type work function layer 282 wraps around the high-k dielectric layer 262. The thickness of the p-type work function layer 282 is controlled such that in the PMOS region 200B, the p-type work function layer 282 fully fills the trench 219 between the second channel nanostructures 256B and the dielectric fin 218 as well as the spaces 258 between adjacent second channel nanostructures 256B. As a result, the p-type work function layer 282 merges the second channel nanostructures 256B and the dielectric fin 218 as well as adjacent second channel nanostructures 256B in the PMOS region 200B.
The p-type work function layer 282 is adapted to tune the threshold voltage Vt2 for a p-type FET formed in the PMOS region 200B. In some embodiments, the p-type work function layer 282 includes titanium nitride (TiN), tungsten carbon nitride (WCN), titanium silicon nitride (TiSiN), or tantalum nitride (TaN). In various embodiments, the p-type work function layer 282 may be formed by a conformal deposition method such as, for example, ALD or CVD.
In some embodiments and as shown in
After deposition of the p-type work function layer 282 or the conductive fill material layer, if present, a planarization process such as CMP may be performed to remove the conductive fill material layer, if present, the p-type work function layer 282, the n-type work function layer 272, and the high-k dielectric layer 262 from a top surface of the ILD layer 250. The top surfaces of the ILD layer 250, the high-k dielectric layer 262, the n-type work function layer 272, and the p-type work function layer 282 are thus coplanar with each other.
An n-type FET is thus formed in the NMOS region 200A. The n-type FET includes a plurality of first channel nanostructures 256A spaced apart from each other, a first gate stack (260, 262, 272), and first source/drain structures 242 adjoining the first channel nanostructures 256A. The first gate stack includes a first portion surrounding each of the first channel nanostructures 256A and a second portion over a topmost first channel nanostructure 256A and in a first portion of a gate trench 254 in the NMOS region 200A. The first portion of the first gate stack includes a first portion of a high-k dielectric layer 262 surrounding each of the first channel nanostructures 256A and an n-type work function layer 272 over the high-k dielectric layer 262 and surrounding each of the first channel nanostructures 256A. The second portion of the first gate stack includes a second portion of the high-k dielectric layer 262 on sidewalls and bottom surfaces of the first portion of the gate trench 254, the n-type work function layer 272 on the second portion of the high-k dielectric layer 262, and a first portion of the p-type work function layer 282.
A p-type FET is thus formed in the PMOS region 200B. The p-type FET includes a plurality of second channel nanostructures 256B spaced apart from each other, a second gate stack (260, 262, 282), and second source/drain structures 244 adjoining the second channel nanostructures 256B. The second gate stack includes a first portion surrounding each of the second channel nanostructures 256B and a second portion over a topmost second channel nanostructure 256B and in a second portion of the gate trench 254 in the PMOS region 200B. The first portion of the second gate stack includes a third portion of a high-k dielectric layer 262 surrounding each of the second channel nanostructures 256B and a second portion of the p-type work function layer 282 over the second portion of the high-k dielectric layer 262 and surrounding each of the second channel nanostructures 256A. The second portion of the gate stack includes a fourth portion of the high-k dielectric layer 262 on sidewalls and bottom surfaces of the second portion of the gate trench 254 and a second portion of the p-type work function layer 282.
A dielectric fin 218 is disposed at the boundary of the NMOS region 200A and the PMOS region 200B to separate the n-type FET and the p-type FET from each other. The n-type work function layer 272 has an edge located on top of the dielectric fin 218. The Vt boundary between the n-type FET and the p-type FET thus is kept, which provides a better Vt control.
In the n-type FET, because only the portion of the high-k dielectric layer 262 on the upper portion of the topmost channel nanostructure 256A is exposed to the etchants used to recessing the sacrificial layer 264 and patterning the hard mask layer 266, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256A (also referred to as HK top1) has a thickness less than that of other portions of the high-k dielectric layer 262 on sidewall and bottom surfaces of the topmost channel nanostructure 256A as well as on surfaces of the channel nanostructures 256A beneath the topmost channel nanostructures 256A due to the removal of the high-k dielectric material by the etchants. Additionally, because the hard mask layer 266 is only deposited on the upper portion of the topmost first nanostructure 256A, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256A may contain the elements providing the hard mask layer 266. Accordingly, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256A may have a different composition from the other portions of the high-k dielectric layer 262 on the sidewall and bottom surfaces of the topmost channel nanostructure 256A as well as on the surfaces of the channel nanostructures 256A beneath the topmost channel nanostructures 256A.
In the p-type FET, because only the portion of the high-k dielectric layer 262 on the upper portion of the topmost channel nanostructure 256B is exposed to etchants used to recessing the sacrificial layer 264, removing the patterned hard mask layer 266P and patterning the n-type work function layer 272, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256B (also referred to as HK top2) has a thickness less than that of other portions of the high-k dielectric layer 262 on sidewall and bottom surfaces of the topmost channel nanostructure 256B as well as on surfaces of the channel nanostructures 256B beneath the topmost channel nanostructures 256B due to removal of the high-k dielectric material by the etchants. Additionally, because the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256B is subject to an additional etching process that removes the n-type work function layer 272 from the PMOS region 200B, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256B (HK top2) is even thinner than the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256A (HK top1). In some embodiments, the HK top2 is about 1 Å thinner than HK top1. Further, because the hard mask layer 266 and the n-type work function layer 272 are only deposited on the upper portion of the topmost nanostructure 256B, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256B may contain the elements providing the hard mask layer 266 and the elements providing the n-type work function layer 272. Accordingly, the portion of the high-k dielectric layer 262 on the top surface of the topmost channel nanostructure 256B may also have a different composition from the other portions of the high-k dielectric layer 262 on the sidewall and bottom surfaces of the topmost channel nanostructure 256B as well as on the surfaces of the channel nanostructures 256B beneath the topmost channel nanostructures 256B.
One aspect of this description relates to a semiconductor device. The semiconductor device includes a plurality of first channel nanostructures spaced apart from each other and in a first device region, a plurality of second channel nanostructures spaced apart from each other and in a second device region, a dielectric fin at a boundary between the first device region and the second device region, a high-k dielectric layer surrounding each of the first channel nanostructures and each of the second channel nanostructures and over the dielectric fin, a first work function layer surrounding each of the first channel nanostructures and over the high-k dielectric layer, and a second work function layer surrounding each of the second channel nanostructures and over the high-k dielectric layer and the first work function layer. The first work functional layer fully fills spaces between the plurality of first channel nanostructures and has an edge located above the dielectric fin. The second work functional layer fully fills spaces between the plurality of second channel nanostructures.
Another aspect of this description relates to a semiconductor device. The semiconductor device includes a substrate, first channel nanostructures disposed in a first device region of the substrate and spaced apart from each other by a first space, second channel nanostructures disposed in a second device region of the substrate and spaced apart from each other by a second space, and a dielectric fin disposed at a boundary between the first device region and the second device region. The semiconductor device further includes a high-k dielectric layer surrounding each of the first channel nanostructures and each of the second channel nanostructures and over the dielectric fin. A portion of the high-k dielectric layer over a top surface of a topmost first channel nanostructure has a thickness less than a thickness of a portion of the high-k dielectric layer over sidewalls and a bottom surface of the topmost first channel nanostructure, and a portion of the high-k dielectric layer over a top surface of a topmost second channel nanostructure has a thickness less than a thickness of a portion of the high-k dielectric layer over sidewalls and a bottom surface of the topmost second channel nanostructure. The semiconductor device further includes a first work function layer surrounding each of the first channel nanostructures and over the high-k dielectric layer. The first work function layer has an edge above the dielectric fin. The semiconductor device further includes a second work function layer surrounding each of the second channel nanostructures and over the high-k dielectric layer and the first work function layer.
Still another aspect of this description relates to a method for forming a semiconductor device. The method includes forming a plurality of first channel nanostructures in a first device region of a substrate and a plurality of second channel nanostructures in a second device region of the substrate. The method further includes forming a dielectric fin at a boundary of the first device region and the second device region. The method further includes depositing a high-k dielectric layer to surround each of the first channel nanostructures and each of the second channel nanostructures and over the dielectric fin. The method further includes depositing a sacrificial layer over the high-k dielectric layer. The sacrificial layer fully fills spaces between the first channel nanostructures, spaces between the second channel nanostructures and spaces between the dielectric fin and corresponding first and second channel structures. The method further includes recessing the sacrificial layer to provide a recessed sacrificial layer, thereby exposing a top portion of a topmost first channel nanostructure of the plurality of first channel nanostructures and a top portion of a topmost second channel nanostructure of the plurality of second channel nanostructures. The method further includes removing a portion of the recessed sacrificial layer in the first device region. The method further includes depositing a first work function layer in the first and the second device regions to surround each of the first channel nanostructures and over a remaining portion of the recessed sacrificial layer in the second device region. The first work function layer merges adjacent first channel nanostructures, but does not merge the first channel nanostructures with the dielectric fin. The method further includes removing a portion of the first work function layer in the second device region. The method further includes removing the remaining portion of the recessed sacrificial layer. The method further includes depositing a second work function layer in the first and the second device regions to surround each of the second channel nanostructures, on a remaining portion of the first work function layer in the first device region and over the dielectric fin. The second work function layer merges adjacent second channel nanostructures.
The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure.
This application claims the benefit of U.S. Provisional Patent Application No. 63/169,143, filed Mar. 31, 2021, which is incorporated by reference herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 9236267 | De et al. | Jan 2016 | B2 |
| 9502265 | Jiang et al. | Nov 2016 | B1 |
| 9520466 | Holland et al. | Dec 2016 | B2 |
| 9520482 | Chang et al. | Dec 2016 | B1 |
| 9536738 | Huang et al. | Jan 2017 | B2 |
| 9576814 | Wu et al. | Feb 2017 | B2 |
| 9608116 | Ching et al. | Mar 2017 | B2 |
| 9786774 | Colinge et al. | Oct 2017 | B2 |
| 9853101 | Peng et al. | Dec 2017 | B2 |
| 9881993 | Ching et al. | Jan 2018 | B2 |
| 10381490 | Kim | Aug 2019 | B2 |
| 11710739 | Yang | Jul 2023 | B2 |
| 11735647 | Huang | Aug 2023 | B2 |
| 20200035567 | Chanemougame | Jan 2020 | A1 |
| 20220320090 | Hsu | Oct 2022 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20220320089 A1 | Oct 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| 63169143 | Mar 2021 | US |