Non-planar sputter targets having crystallographic orientations promoting uniform deposition

Abstract

A non-planar sputter target having differing crystallographic orientations in portions of the sputter target surface (25) that promote more desirable deposition and density patterns of material sputtered from the target surface onto a substrate is disclosed. A closed dome (22) end of the sputter target (20) is comprised of a first crystallographic orientation and sidewalls (24) of the sputter target are comprised of a crystallographic orientation different from that of the dome. The sputter target is formed, preferably by hydroforming or other metal working techniques, in the absence of annealing. The hydroforming manipulations result in the different crystallographic orientations while minimizing, or ideally omitting, the application of heat. Quick and cost effective non-planar sputter targets that are easily repeatably producable are achievable as a result. There are vectors (α, β1, β2) in the target.

Description

BACKGROUND OF THE INVENTION

1. Field of Invention

This invention relates to non-planar sputter targets having crystallographic orientations promoting uniform deposition of sputtered material onto a substrate and methods of making the same.

2. Description of Related Art

Cathodic sputtering is widely used for depositing thin layers or films of materials from sputter targets onto substrates. Basically, a cathode assembly including the sputter target is placed together with an anode in a chamber filled with an inert gas, preferably argon. A substrate is positioned in the chamber near the anode with a receiving surface oriented normal to a path between the cathode assembly and the anode. A high voltage electric field is applied across the cathode assembly and the anode causing electrons to eject from the cathode assembly and ionize the inert gas. The positively charged ions of the inert gas are then propelled against a sputtering surface of the sputter target due to the electric field. The ion bombardment against the sputtering surface of the target causes portions of the material of the sputtering surface to dislodge from the sputter target surface and deposit as a thin film or layer on the receiving surface of the substrate at an opposite end of the chamber.

Recently, non-planar sputter targets have been developed to provide improved sputtering and deposition uniformity. For example, open-ended cup-shaped hollow cathode magnetron (HCM) sputter targets have been developed, as disclosed in U.S. Pat. No. 6,419,806 of common assignment herewith, the disclosure of which is incorporated herein by reference. These cup or pot shaped targets are generally comprised of a high purity metallic material as the target surface and are typically formed from well-known metal-working operations such as hydroforming. The closed end of the cup-shaped target comprises a dome. Sidewalls extend from the dome to an open end of the target The application of heat and other manipulations that may be used to form the cup-shaped targets often cause changes in the microstructure or crystallographic orientation of the materials comprising the sputter target surface. Such changes may adversely affect the deposition of sputtered materials onto the substrate.

A need in the art exists for methods of making sputter targets of desired crystallographic orientation and for targets made by such methods wherein the targets, upon sputtering, result in improved coating uniformity.

SUMMARY OF THE INVENTION

This invention provides a non-planar sputter target having crystallographic orientations in the sputter target surface that promote more desirable deposition and density patterns of material sputtered from the target surface onto a substrate. An exemplary embodiment of this invention more specifically provides a pot or bowl-shaped sputter target of the type shown in U.S. Pat. No. 6,419,806 and having a substantially planar end wall, or dome, at a closed end of the target Sidewalls are connected to the dome and extend from the dome to an open end of the target. An inner surface of the dome and sidewalls form the sputter surface of the target, wherein the dome portion has a first crystallographic orientation and the sidewalls have a second crystallographic orientation different than the first.

According to one exemplary embodiment of the invention, a flat blank of a target surface material is provided and manipulated into a desired target shape by hydroforming. The flat target surface material is preferably comprised of a high purity metal selected from the group consisting of titanium, copper, tantalum and alloys thereof. The use of a single layer blank of material requires less material than prior plural layer targets have required, and requires less processing time to shape the single blank into the desired shape. Thus, a more reliable and cost-effective non-planar sputter target is produced in less time according to the invention.

Alternatively, a plurality of layers of materials may be used to form the target, provided the desired crystallographic orientations of the sputter target surface and target shape are achieved. Various embodiments of the invention provide a flat blank of backing plate material adjacent the target surface material. The adjacent layers of materials are similarly manipulated by hydroforming to achieve the desired target shape and target surface orientations. Still other embodiments of the invention may comprise interlayers between the backing plate and target surface layers. In any event, the backing plate material is preferably a malleable, low purity metal selected from the group consisting of aluminum, copper, steel, titanium and alloys thereof.

In a particularly preferred exemplary embodiment of the invention, the material comprising the target surface is tantalum. Manipulation of the target surface material, preferably by hydroforming, into a desired shape alters the crystallographic orientation of the target surface. In the case of a tantalum target surface having a pot or bowl shape, the dome portion of the target surface has a predominate {111} orientation, whereas the sidewalls have a mixture of {112}<110> and {110}<110> orientations, for example. The differing orientations in the dome and sidewalls of the target surface have been found to emit sputtered materials at different angles from the respective dome and sidewall portions of the target surface. The differing angles of emissions affect the uniformity and density of depositions of the sputtered material on the substrate.

The two-part orientation representation {hkl}<hkl>, is standard “sheet texture” notation, and has the following meaning. The first part, {hkl}, represents the miller indices of the crystallographic planes parallel with the sputter surface of the target. The second part, <hkl>, represents the indices for the crystallographic direction parallel with the material flow direction during forming. For the example of a 3D target with cylindrical sidewall geometry, a {112}<110> sidewall orientation means the following. The {112} planes are parallel with the inside surface of the cylinder and the <110> direction is parallel with the cylindrical axis. The shorthand notation “{112}/{110}” is used in this manuscript to represent a mixed {112}<110> and {110}<110> texture.

As used herein, the term “predominate”, when used to describe the texture of the sputter surface of the dome or end wall of the target means that the proportion of the specific {h,k,l} orientation to the total of all crystalline orientations is at least 120/N % in various random portions of the dome sputter surface. Here, N refers to the number of orientations included in the x-ray diffraction analysis. For example, with BCC tantalum, six orientations (N=6) are measured ({110}, {200}, {211}, {310}, {222}, and {321}). The measured {200} and {222} diffraction intensities represent the {100} and {111} orientations, respectively. For tantalum, a predominate {111} texture indicates an orientation percentage greater than 20%. When the term “major” is used to describe the preferred texture of the sputter side walls of the target, this means that the proportion of combined {112} and {110} orientations to the total of all crystalline orientations is at least 200/N %, or 33%. Within this major {112}/{110} texture, the {112}<110> orientation is usually present in a slightly greater amount than the {110}<110> orientation. Measurement of all of these orientations can be made in accordance with conventional X-ray diffraction protocols such as those reported in U.S. Pat. No. 5,456,815.

After shaping by hydroforming, for example, the dome of the preferred tantalum target is comprised of predominate {111} orientations and the sidewalls are comprised of major {112}/{110} orientations. Tantalum has the BCC crystal structure for which <111> is the preferred emission direction. Thus, emissions from the dome tend to occur predominantly directly normal to the dome surface, whereas emissions from the sidewalls tend to occur at various non-normal angles from the side walls forming an annular atomic pattern across the barrel of the HCM. The sidewall emissions may occur at approximately 19.5 degree angles relative to the target surface normal due to the {112}<110> tantalum portions of the sidewall and at approximately 35.3 degree angles relative to normal due to the {110}<110> tantalum portions of the sidewall. As a result of the above-identified orientations, material sputtered from the cup-shaped target forms a more evenly distributed pattern when deposited on the substrate. The {112}/{110} texture provides sidewall emission which avoids the axial center of the HCM, giving rise to the beneficial annular atomic density pattern. Other textures can be conceived which would, achieve the same result. For example, a tantalum {100}<100> orientation would be a good candidate. For other materials of different crystal structure, such as FCC aluminum and copper, or HCP titanium, different orientations can be chosen to avoid sidewall emission intercepting the cylindrical axis of the HCM.

According to the various exemplary embodiments of the invention, the target surface material, or adjacent materials where applicable, is manipulated into a desired non-planar shape, preferably by hydroforming, or other metal working techniques. In the preferred embodiment of the invention, the desired target shape is a pot or bowl shape, although the artisan should appreciate that other shapes can be used, particularly as hydroforming is conducive to forming even complex shapes. Little or no heat is required during or after shaping material so as to minimize the recrystallization of the sputter surface into undesirable orientations. Post-shaping annealing is therefore preferably not performed.

In practice, according to a preferred method of forming a target according to the invention, a blank of material is placed over an annular platen of a hydroforming press. A tank having a bladder filled with hydraulic fluid is positioned in a housing above the blank. The bladder thus faces an upper surface of the blank. A mandrel or punch shaped to form the blank is positioned below the platen. The housing is lowered to contact the bladder with the upper surface of the blank. Thereafter, the mandrel is urged upwards through the opening in the annular platen and against a lower surface of the blank. As the mandrel continues to press upwards against the blank, the upper surface of the blank is urged against the bladder. At the same time, the pressure in the bladder increases up to as much as about 10,000 psi. Thus, as the mandrel urges the blank upwards, the pressurized bladder provides resistance until the blank is made to conform to the shape of the mandrel. Thereafter, the mandrel and bladder are retracted, and the target removed from the mandrel. No annealing is performed.

The preferred hydroforming process according to the invention takes approximately 1.5 minutes, is performed at room temperature, and is readily repeatable to form a plurality of consistently shaped targets as desired. Because the process is performed at room temperature, heat induced crystallographic orientation changes are minimized, or ideally eliminated. Significantly, because no annealing step is performed once the blank is formed into the desired shape, recrystallization or other orientation changes to the sputter surface are minimized, or ideally eliminated.

These and other features and advantages of this invention are described in, or are apparent from, the following detailed description of various exemplary embodiments of the systems and methods according to this invention.

BRIEF DESCRIPTION OF THE DRAWINGS

Various exemplary embodiments of the systems and methods of this invention will be described in detail with reference to the following figures, wherein:

FIG. 1 illustrates an exemplary non-planar sputter target comprised of a single metallic material;

FIG. 1A illustrates a diagrammatic cross-sectional view of vector emissions from sidewalls of a target according to the invention;

FIG. 2 illustrates an exemplary non-planar sputter target comprised of a plurality of metallic layers; and

FIG. 3 illustrates a schematic diagram of a hyrdroforming press.

DETAILED DESCRIPTION OF EXEMPLARY EMBODIMENTS

FIGS. 1 and 1A illustrate an exemplary non-planar sputter target 20 according to the invention. FIG. 1, more specifically, shows a cup-shaped sputter target 20 having a substantially planar end wall, or dome 22, at a closed end of the target Sidewalls 24 are connected to the dome 22 and extend from the dome 22 to an open end of the target. An inner surface of the dome 22 and sidewalls 24 form the sputter surface 25 of the target, wherein the dome portion has a first crystallographic orientation and the sidewalls have a second crystallographic orientation different than the first. The differing crystallographic orientations in the sputter target surface promote more desirable deposition and density patterns of material sputtered from the target surface onto a substrate, wherein material sputtered from the dome is emitted perpendicularly therefrom as shown by vector α, and material sputtered from the sidewalls are emitted non-perpendicularly from the sidewalls as shown by vectors β₁, β₂ in FIG. 1A such that the emissions form an annular pattern spaced from the central axis Z of the target. Based on preliminary observations, the cloud of atomic material for sputtering thus exists in a predominantly annular pattern with the annulus located proximate the sidewalls, spaced from the central axis of the cup.

According to one exemplary embodiment of the invention, a flat blank of a target surface material is provided having an original, unaltered crystallographic orientation and is manipulated into a desired target shape by hydroforming, for example, or other metal working techniques. The flat target surface material is preferably comprised of a high purity metal selected from the group consisting of titanium, copper, tantalum and alloys thereof. Ta is most preferred. Alternatively, a plurality of layers of materials may be used to form the target, provided the desired crystallographic orientations over portions of the sputter target surface and target shape are achieved.

Various embodiments of the invention provide a flat blank of backing plate material adjacent the target surface material. FIG. 2 illustrates an exemplary embodiment of the sputter target according to the invention wherein at least two materials comprise the inner sputtering surface and outer shell of the target assembly. As shown in FIG. 2 using like reference numerals, the adjacent layers of materials are similarly manipulated or worked, preferably by hydroforming or other metal working techniques, to achieve the desired target shape and target surface orientations. Still other embodiments of the invention may comprise interlayers between the backing plate and target surface layers. In any event, the backing plate material is preferably a malleable, low purity metal selected from the group consisting of aluminum, copper, steel, titanium and alloys thereof.

In a particularly preferred exemplary embodiment of the invention, the flat target surface blank is comprised of tantalum. Working of the blank and the target surface material, preferably by hydroforming into a desired shape alters the crystallographic orientation of portions of the target surface. In the case of a {111}/{100} tantalum blank used to form a target surface having a pot or bowl shape in accordance with the invention, referring again to FIG. 1, the dome portion 22 of the target surface 25 tends to maintain its original predominate {111}/{100} orientations, whereas the sidewalls 24 may have a mixture of {112}/{110} orientations, for example. The proportion of the {112}/{110} orientations in the sidewalls is preferably at least 33% of the total of all crystalline orientations in the sidewall, thus constituting a major texture as defined herein.

As a result of the predominate and major orientations in the dome and sidewalls, respectively, emissions from the dome tend to occur predominantly directly normal (vector α) to the dome surface. At the same time, emissions from the sidewalls tend to occur at approximately 19.5 degree angles (vector β₁) relative to the target surface normal at the sidewalls due to the {112}<110> tantalum portions of the sidewall, and at approximately 35.3 degree angles (vector β₂) relative to normal due to the {110}<110> tantalum portions of the sidewall.

According to the invention, the target surface material, or adjacent materials where applicable, are manipulated, using a hydroforming press, into a desired non-planar shape. In the preferred embodiment of the invention, the desired target shape is a pot or bowl shape, although the artisan should appreciate that other shapes are equally possible as hydroforming is particularly conducive to forming even complex shapes. Little or no heat is required when shaping material in a hydroforming process. As a result, planar portions (or unworked portions) of the target surface material tend to maintain their original crystallographic orientations. On the other hand, non-planar portions (or worked portions) of the target surface tend to deviate from their original crystallographic orientations. The minimization, or absence, of heat when forming the non-planar sputter targets according to the invention differs from prior art sputter targets that rely on heating at different stages of the process to achieve the desired shape or crystallographic orientations of the sputter target surface.

As shown in FIG. 3, a blank 30 of material is placed over an annular platen 110 of a hydroforming press 100. A bladder 120 filled with hydraulic fluid is positioned in a housing above the blank. The bladder thus faces an upper surface of the blank. A mandrel or punch 130 shaped to form the desired target contour is positioned below the platen. In practice, the housing is lowered to contact the bladder with the upper surface of the blank. Thereafter, the mandrel is urged upwards through the opening in the annular platen and against a lower surface of the blank. As the mandrel continues to press upwards against the blank, the upper surface of the blank is urged against the bladder. At the same time, the pressure in the bladder increases up to as much as about 10,000 psi. Thus, as the mandrel urges the blank upwards, the pressurized bladder provides resistance until the blank is made to conform to the shape of the mandrel. The mandrel and bladder are retracted and the target is removed from the hydroforming press, for example. Measurement of the crystallographic orientations in different sections of the sputter surface of the target may be made by X-ray diffraction.

The entire hydroforming process according to the invention takes approximately 1.5 minutes and is performed at room temperature. Because the process is performed at room temperature, heat induced crystallographic orientation changes are minimized, or ideally eliminated. Significantly, no additional annealing step is required once the blank is formed into the desired shape according to the invention. Thus, further crystallographic orientation changes are also minimized or ideally avoided. Although the mandrel shown complies with a pot or bowl-shaped sputter target, the artisan will appreciate that many other shapes may be used as well by altering the mandrel accordingly, to produce non-planar sputter targets according to the invention.

Processes for producing cup or bowl shaped targets with the desired texture can be summarized as involving several steps. The first step is to produce at starting plate with {111}{100} mixed fiber texture; more preferably with a {111} percentage greater than 20%. A recrystallized equiaxed microstructure is preferred with a grain size <100 μm. The second step is to form the plate into the bowl shape using spin-forming, hydroforming or deep drawing. This work must be done cold or at a temperature to prevent dynamic recrystallization. The amount of work needed to achieve the desired texture in the sidewall of the bowl is 35% deformation (preferably >50%). A stress relieving anneal can be included as the final step. The temperature must be low enough to prevent recrystallization and the evolution of a {1111} texture component in the sidewall.

Grain Structure: The micro structure of the tantalum will have an equiax, fully recrystallized grain structure at the dome and a cold worked structure along the sidewalls. The planar blanks going into forming the NNS (near net shape) blanks are fully annealed prior to forming and not annealed post forming.

Grain Size: The average grain size will be <150 microns at the sidewall and <100 microns at the dome [ASTM E112, Table 4, Mean Intercept]

While this invention has been described in conjunction with the exemplary embodiments described above, it is evident that many alternatives, modifications and variations will be apparent to those skilled in the art. Accordingly, the exemplary embodiments of the invention, as set forth above, are intended to be illustrative and not limiting. Various changes may be made without departing from the spirit and scope of the invention.

Claims

1. A sputter target comprising: a substantially cylindrical side wall connected to an end wall, said side wall and said end wall having inner and outer surfaces wherein said inner surfaces are comprised of a high purity metal or alloy thereof for sputtering thereof during physical vapor deposition, said inner surfaces of said side wall having a texture which provides emission which avoids the central axis of the HCM, and said inner surface of said end wall having a texture which may provide emission normal to the surface.

2. A target as recited in claim 1 consisting essentially of Ta, which has a side wall with a major {112}/{110} texture and an end wall with a predominate {111} texture.

3-6. (canceled)

7. A sputter target comprising: a sputtering surface having a planar portion and a non-planar portion, the planar portion having a first crystallographic orientation and the non-planar portion having a second crystallographic orientation different than the first crystallographic orientation.

8-9. (canceled)

10. The sputter target of claim 3, wherein the first crystallographic orientation emits materials from the sputtering surface at a first angle and the second crystallographic orientation emits materials from the sputtering surface at a second angle different than the first angle.

11. The sputter target of claim 4, wherein the target and sputtering surface are pot or bowl-shaped, the planar portion comprising a dome and the non-planar portion comprising sidewalls of the pot or bowl-shaped target and sputtering surface.

12. The sputter target of claim 5, wherein the high purity metal is selected from the group consisting of titanium, copper, tantalum and alloys thereof.

13. The sputter target of claim 6, wherein emissions of sputtered material from the dome occur normal to the sputtering surface of the dome, and emissions of sputtered material from the sidewalls occur non-normal to the sputtering surface of the sidewalls and doesn't intercept the cylindrical axis.

14. The sputter target of claim 7, wherein emissions from the non-planar portion are at acute angles from the surface of the non-planar portions.

15. (canceled)

16. The sputter target of claim 8, wherein the non-planar portion comprises a mixture of orientations wherein the mixture of orientations in the non-planar portion is {112}/{110} tantalum.

17. (canceled)

18. A method of making a sputter target having different crystallographic orientations in portions of a sputter surface of the target, the method comprising: a. providing a hydroforming press having an annular platen, a housing holding a bladder filled with hydraulic fluid, and a mandrel; b. placing a blank of material on the annular platen; c. lowering the housing to contact the bladder with an upper surface of the blank; d. raising the mandrel through a central opening in the annular platen to contact a lower surface of the blank; e. raising the mandrel further to urge the blank into the bladder thereby increasing pressure in the bladder; f. forming the blank into the desired shape by the resistance provided from the pressurized bladder and the mandrel urging the blank into said bladder; g. retracting said bladder and mandrel to yield the sputter target; and h. measuring the crystallographic orientations in various portions of the sputtering surface of the target; and wherein no annealing is performed after shaping of the target.

19. The method of claim 10, wherein the pressure in the bladder is up to about 15,000 psi.

20. The method of claim 11, wherein the hydroforming process occurs at room temperature.

21. The method of claim 12, wherein the mandrel is shaped to provide a target having a sputter surface comprised of a planar portion and a non-planar portion, the planar portion having a first crystallographic orientation substantially the same as that of the blank prior to hydroforming, and the non-planar portion having a second crystallographic orientation different than the first crystallographic orientation as a result of the hydroforming process.

22. The method of claim 13, wherein the blank is a high purity metal from among the group consisting of titanium, copper, tantalum and alloys thereof.

23. The method of claim 14, wherein the high purity metal is a mixture of {111}/{100} tantalum, having at least 20% {111} tantalum.

24. The method of claim 15, wherein the non-planar portion is comprised of a mixture of orientations after hydroforming.

25. The method of claim 16, wherein the mixture of orientations in the non-planar portion is {1 12}/{110} tantalum.

26. A method of making a sputter target assembly having first and second sputtering surfaces with said first sputtering surface having a first crystallographic orientation and said second sputtering surface having a second crystallographic orientation, said method comprising. a. providing a blank of a first metal having said first crystallographic orientation; b. forming said blank into a desired shape by deforming a portion of said blank to transform its crystallographic orientation from said first crystallographic orientation to said second crystallographic orientation; c. said method being performed in the absence of heat treatment annealing to prevent recrystallization of said deformed portion of said blank back to said first crystallographic orientation.

27. (canceled)

28. A method as recited in claim 18 wherein said step (b) of forming comprises hydroforming.

29. A method as recited in claim 19 wherein said deformation is from about 35% or greater deformation.

30. (canceled)

31. A method as recited in claim 20 wherein said first metal is Ta and said first crystallographic orientation is chosen from {111} or mixed {111} {100}.

32. A method as recited in claim 21 wherein said Ta has a grain size of less than about 100 μm.

33. A method as recited in claim 22 wherein said first crystallographic orientation is predominantly {111}.

34. A method as recited in claim 23 wherein said second crystallographic orientation is major {112}/{110}.

35. (canceled)