The present invention relates to an on-line coating adhesion determination apparatus of a galvannealed steel sheet, and a galvannealed steel sheet manufacturing line.
A galvannealed steel sheet has been used worldwide as a steel sheet for vehicles. The quality characteristics required for the galvannealed steel sheet include corrosion resistance, coating properties, weldability, powdering resistance during press forming, and Hacking resistance during press forming, and the like. Fe—Zn phases constituting the coating layer of the galvannealed steel sheet include a ζ phase, a δ1 phase, and a Γ·Γ1 phase. Among the above-described characteristics, press formability particularly represented by powdering resistance and flaking resistance is dependent on the amounts of the ζ phase and the Γ·Γ1 phase. The powdering resistance is enhanced as the Γ·Γ1 phase is reduced, and the flaking resistance is enhanced as the ζ phase is reduced. Therefore, in order to obtain good press formability, a coating layer mainly containing the δ1 phase is required.
In order to form the coating layer mainly containing the δ1 phase, the coating bath composition (Al concentration in a bath), the bath temperature of a coating bath, and heating and cooling conditions for alloying need to be optimized depending on the steel components. Typically, the Al concentration in a bath and the bath temperature are maintained in constant ranges, and moreover, a heating and cooling pattern that is considered to be optimal is determined depending on an alloying rate of the steel for the operation. However, in practice, due to operational conditions in an upstream process (a process before coating) such as hot rolling, the alloying rate may vary in coils even in same type of steel and in parts even in same coil depending on actual operational conditions. Therefore, each time, an operator finely adjusts the heating and cooling conditions while visually checking the degree of alloying. As a result, which alloy phase is obtained and whether or not powdering resistance and flaking resistance are good are checked by off-line testing and analysis on the representative parts (typically a front portion and/or a tale portion) of a coil after production.
However, in the method of checking coating quality through the off-line testing and analysis, quick feedback of the operational condition may not be achieved. Therefore, for example, in a case where an alloying rate is changed due to a change in steel type, there is a risk of a reduction in yield. In addition, for example, depending on coiling conditions during hot rolling or the like, there may be cases where alloying of the front portion of a coil is slower than alloying of the middle portion. In this case, when the operation is performed to meet the alloying condition of the front portion, the middle portion is excessively alloyed, and powdering of most of parts of the coil may become apparent.
In order to prevent the problems beforehand, on-line measurement with high accuracy over the entire length of the coil is effective. A technique employed for this purpose is an on-line X-ray diffraction method. An X-ray diffraction method is a method for qualitative and quantitative measurement of crystal phases in a coating layer using the diffraction phenomenon which occurs when crystals are irradiated with X-rays. In a case where this method is used for the on-line measurement, selecting diffracted X-rays having a good correlation between the diffracted X-ray intensity and the crystal phase thickness is necessary. Furthermore, in order to obtain high measurement accuracy, selecting diffracted X-rays having a high intensity from a practical diffraction angle range is necessary.
In Patent Documents 1 and 2, as a practical diffraction angle (2θ) range, 2θ>80° (in a case where Cr is used as an X-ray target, a crystal lattice spacing is d<1.78 Å) is disclosed as a range in which effects of flapping of a steel sheet, the thermal effect of the steel sheet, and a change in incident X-ray intensity are small. As the crystal lattice spacing which satisfies the above conditions, those that are widely used in the past are, for example, as described in Patent Documents 2 to 5, d=1.26 Å (2θ=130° when the target is Cr) for a ζ phase, d=1.28 Å (2θ=127° when the target is Cr) for a δ1 phase, and d=1.22 Å (2θ=139° when the target is Cr) for a Γ·Γ1 phase.
However, it cannot be said that the on-line X-ray diffraction method according to the related art is sufficient to perform on-line measurement over the entire coil length with high accuracy, to quickly feed the results back to operational conditions, and to prevent excessive alloying or non-alloying beforehand. The biggest reason is that the three X-ray diffraction peaks respectively indicated by the ζ phase, the δ1 phase, and the Γ·Γ1 phase, which have been used in the past, are adjacent to each other and are present in a region with a background that is high and is not flat. In the related art, a constraint condition of 2θ>80° which is a range in which the effects of the flapping of a steel sheet, the thermal effect from the steel sheet, and a change in incident X-ray intensity are small, and a condition of simultaneous measurement caused by the fact that the X-ray diffraction peaks of the three phases (the ζ phase, the δ1 phase, and the Γ·Γ1 phase) are adjacent, are considered to be important. As a result, the technique is extremely insufficient for achieving the original object to measure the thickness of each phase with good accuracy.
In addition, in recent years, for the enhancement in the productivity of a manufacturing line or competitiveness, the manufacturing line of the galvannealed steel sheet has been increased in speed. In order to determine the coating adhesion of the galvannealed steel sheet in a high-speed manufacturing line on-line, an analysis time for the determination of the coating adhesion needs to be reduced. In order to significantly determine the difference between a steel sheet having good coating adhesion and a steel sheet having poor coating adhesion, a significant difference of three times (3σ) or more of measurement variation needs to be provided between the measurement values of the two.
As the analysis time for the determination is increased, the length of the steel sheet that has passed from the start to the end of the determination is increased. When the manufacturing line is increased in speed, the necessary steel sheet length for the determination is further increased. When the length is excessively increased, quality assurance on the entire length of the coil becomes difficult, and rapid feedback to the operational conditions becomes difficult. In order to enable measurement within a shorter time, the improvement in the signal intensity and the S/N ratio is necessary. In addition, steel sheet vibrations are increased due to an increase in speed, and there is a greater need for reducing the effect of the steel sheet vibrations on signals than in the related art.
Patent Document 6 discloses a technique for reducing an effect of steel sheet vibrations. In Patent Document 6, an incident X-ray beam is incident on a multi-layer film mirror to be collimated. As a result, diffracted X-rays generated by irradiating the coating layer of a steel sheet surface with the incident X-ray beam are collimated. Therefore, even in a case where the distance between the diffraction position of the X-rays and a detection system is changed due to vibrations of the steel sheet, there is an advantage in that the detected intensity of the diffracted X-rays is stabilized.
The effect of the multi-layer film mirror is also described in Non-Patent Document 1. An example, in which a multi-layer film mirror and a parallel slit are used in order to efficiently collimate divergent beams emitted from an X-ray source in a laboratory, is disclosed.
The present invention has been made taking the foregoing problems into consideration, and an object thereof is to provide an on-line coating adhesion determination apparatus of a galvannealed steel sheet, which can follow a further increase in the speed of a manufacturing line, and a galvannealed steel sheet manufacturing line.
The present inventors had intensively and repeatedly conducted research focusing on the fact that a background intensity is low and flat (is approximately horizontal) in a range in which a diffraction angle 2θ is on a low angle side. As a result, it was found that on a low angle side corresponding to a crystal lattice spacing d of 1.5 Å or higher, a plurality of X-ray diffraction peaks for a single phase are present. The inventors had repeatedly examined the quantitativeness of the peak intensities, and as a result, identified a peak for each phase, which has excellent quantitativeness and has low background intensity. Moreover, it was found that, by using a value obtained by subtracting a background intensity from the intensity of X-ray diffraction peak corresponding to a crystal lattice spacing d of 1.914 Å, the thickness of a Γ·Γ1 phase, which affects the coating adhesion of a galvannealed steel sheet, can be measured with good accuracy.
Subsequently, the present inventors proceeded to examine the realization of the technique. In order to apply the technique to a manufacturing line having high sheet threading speed for the steel sheet, problems of steel sheet vibrations during sheet threading need to be solved. Under the thought that a parallel beam optical system has to be used as an optical system in order to reduce the effect of steel sheet vibrations, a method of detecting a Fe—Zn phase low angle peak corresponding to a crystal lattice spacing d of 1.5 Å or higher, in the parallel beam optical system with high sensitivity was intensively and repeatedly examined. As a result, first, regarding the specifications of an X-ray tube, selection of an output, a focal size, an extraction angle, and an extraction method is important for sensitivity enhancement. Next, the specifications of an optical system for irradiating a sample with a beam emitted from the X-ray tube and efficiently guiding the beam to a detector were examined. As a result, it was found that the detection efficiency particularly in an incidence optical system can be enhanced by appropriately setting a capture angle and reflectance. Here, the present inventors repeatedly conducted a systematic experiment by changing such parameters, and as a result, found that on the premise of a parallel beam optical system, a desired diffraction peak can be detected with good sensitivity by designing a X-ray tube and the optical system so as to allow two parameters including “emitted beam luminance” and “width-direction gain” to be higher than specific lower limits. Therefore, the present inventors produced an on-line X-ray diffraction apparatus which satisfied the above conditions and installed the apparatus at a position at which the sum of a sheet thickness change and steel sheet vibrations was within ±3 mm between an alloying furnace and coiling in a continuous galvanizing line. The present inventors found that on-line adhesion determination of a galvannealed sheet can be actually performed with good accuracy within a short period of time and completed the present invention.
The present invention has been made on the basis of the findings, and the gist is as follows:
(1) That is, according to an aspect of the present invention, an on-line coating adhesion determination apparatus of a galvannealed steel sheet, includes: an X-ray tube which irradiates a galvannealed steel sheet that travels on a transportation line, with X-rays; an optical system which allows the X-rays emitted from the X-ray tube to irradiate the galvannealed steel sheet as a parallel beam and be diffracted; and a detector which measures an intensity of the diffracted X-rays and is installed at a position at which the X-ray diffraction peak corresponding to a crystal lattice spacing d of 1.5 Å or higher is detected, in which an emitted beam luminance of the X-rays is 20 W/mm2 or higher, and the width-direction gain of the X-rays in the optical system is 0.15 or higher.
(2) In the on-line coating adhesion determination apparatus of a galvannealed steel sheet described in (1), the detector may be installed at a position of a diffraction angle at which the X-ray diffraction peak corresponding to a crystal lattice spacing d of 1.914 Å is detected.
(3) In the on-line coating adhesion determination apparatus of a galvannealed steel sheet described in (1) or (2), as the X-ray tube, an X-ray tube in which an energy of the X-rays incident on the galvannealed steel sheet is lower than an excitation energy of Fe-Ku fluorescence X-rays, may be used.
(4) According to another aspect of the present invention, a galvannealed steel sheet manufacturing line includes: installing the on-line coating adhesion determination apparatus described in any one of (1) to (3), at a position at which the sum of the sheet thickness change and steel sheet vibrations is within ±3 mm between an alloying furnace and coiling.
By applying the on-line coating adhesion determination apparatus of a galvannealed steel sheet of the present invention, determination of good adhesion and poor adhesion can be achieved within a short period time. Therefore, even when the sheet threading speed of a steel sheet in a manufacturing line is further increased, on-line measurement can be performed over the entire length of a coil with good accuracy. In addition, by quickly feeding the results back to operational conditions, excessive alloying or non-alloying can be prevented beforehand. As a result, this significantly contributes to improvement of yield and quality assurance even during high-speed sheet threading. Therefore, a galvannealed steel sheet with excellent coating quality can be stably supplied to customers at low cost.
Hereinafter, an on-line coating adhesion determination apparatus of a galvannealed steel sheet according to an embodiment of the present invention (hereinafter, sometimes simply referred to as a determination apparatus according to this embodiment), and a galvannealed steel sheet manufacturing line in which the apparatus according to the embodiment of the present invention is installed and a high-speed operation is enabled (hereinafter, sometimes simply referred to as a manufacturing line according to this embodiment) will be described in detail with reference to the drawings.
The determination apparatus according to this embodiment is a measurement apparatus which measures the thickness of a predetermined phase contained in an Fe—Zn alloy phase of the galvannealed steel sheet, and includes an X-ray tube which irradiates the galvannealed steel sheet with X-rays, an optical system from the X-ray tube to a detector, and the detector which measures the intensity of diffracted X-rays obtained through the X-ray irradiation. Using a parallel beam optical system as the optical system, X-rays are allowed to be incident on the galvannealed steel sheet and be diffracted. In addition, the detector is installed at a position corresponding to a diffraction angle at which X-rays diffraction peak corresponding to a crystal lattice spacing d of 1.5 Å or higher are detected. In addition, the emitted beam luminance of the X-rays is 20 W/mm2 or higher, and the width-direction gain of the X-rays in the optical system is 0.15 or higher.
Hereinafter, an X-ray diffraction method applied to the determination apparatus according to this embodiment will be described. The X-ray diffraction method applied to the determination apparatus according to this embodiment includes irradiating a polycrystalline sample with characteristic X-rays and measuring the reflection intensity at a specific diffraction angle and is classified into the Debye-Scherrer method. In addition, an X-ray diffraction apparatus which can be applied to the determination apparatus according to this embodiment is constituted by an X-ray tube which generates an X-ray beam, various slits for restricting the divergence of the X-ray beam, a detector, a light-receiving slit, a count recording device, and the like.
The X-ray tube which can be used in this embodiment generates thermal electrons by allowing current to flow through a filament, generates X-rays by allowing the thermal electrons to accelerate at a high voltage of tens of kilo voltages and strike a metal target, and extract the generated X-rays through a beryllium window. The metal target of the X-ray tube is selected in consideration of absorption of X-rays by a specimen and measurement accuracy, and Cu, Cr, Fe, Co, Mo, W and the like are used. Among these, Cu, Cr, and Co are particularly preferable due to excellent versatility. The generated X-rays include, as well as Kα rays as an object, Kβ rays and white X-ray components and thus need to be converted into monochromic light by removing such components. Conversion of the X-ray beam into monochromic light is performed by inserting a Kβ filter made of a metallic foil in front of the light-receiving slit or by using a monochromator. Further, a pulse height analyzer may also be combined or a collimation system using an X-ray collimator may also be employed.
As the slit for restricting the divergence of the X-ray beam, a solar slit for restricting the divergence of the X-ray beam in a vertical direction and a divergence slit for restricting the angle of divergence of a sample in a horizontal plane is preferably used. Diffracted X-rays generated by irradiating a material surface with the X-ray beam are collected via the light-receiving slit, and are detected by the X-ray detector further via the solar slit and a scattering slit such that the intensity thereof is measured.
Next, this embodiment will be described in more detail.
First, the X-ray tube used in the on-line coating adhesion determination apparatus of the galvannealed steel sheet according to this embodiment will be described. As the X-ray tube, a sealed-type X-ray tube is preferably used. As the X-ray source, as well as the X-ray tube, there is a rotating anticathode-type X-ray generating device, which is advantageous in terms of high output. However, in a case of being used in the galvannealed steel sheet manufacturing line, maintenance and management of a vacuum system and the like are complex. Therefore, the X-ray tube is appropriate. As the sealed-type X-ray tube, any of a fluorescence X-ray tube and a diffracted X-ray tube may be used. However, the diffracted X-ray tube which has a small focal size and high luminance is more appropriate. Examples of the sealed-type X-ray tube are shown in Table 1. The fluorescence X-ray tube has a relatively greater focal size than that of the diffracted X-ray tube, and tubes of Nos. 1 to 3 in Table 1 correspond to the fluorescence X-ray tube. Tubes of Nos. 4 to 15 in Table 1 correspond to the diffracted X-ray tube. In addition, a focal point luminance in Table 1 is a value obtained by dividing an output (W) by the area (mm2) of a focal point.
Regarding the specifications of the X-ray tube according to this embodiment, in addition to an output, selection of a focal size, an extraction angle, and an extraction method is important for sensitivity enhancement.
Regarding the inclination direction of the extraction angles m1 and m2, as shown in
In a case where the size (expressed as width×length, the same is applied hereinafter) of the focal point 12 in a plan view is a (mm)×b (mm), when the point extraction is employed, as shown in
Next, the optical system in the determination apparatus according to this embodiment will be described. In the determination apparatus according to this embodiment, a parallel beam optical system which is less likely to be affected by steel sheet vibrations during on-line measurement is used.
As the X-ray source 21 shown in
An emission side solar slit 23a is disposed in the emission optical system 23. In addition, in the solar slit 23a, an inlet side opening 23a1, which restricts the incidence expansion width of the X-rays incident to the solar slit 23a, and an outlet side opening 23a2, which restricts the emission expansion width of the X-rays emitted from the solar slit 23a, are provided. In
A view of the arrangement of the incidence optical system 22 is shown in
In this embodiment, by calculating the width (sample irradiation width) and length (sample irradiation length) of the X-rays irradiating the sample 25 and obtaining the emitted beam luminance on the sample 25, the specifications of the X-ray source 21 and the optical system are designed. First, a method of calculating the sample irradiation width and the sample irradiation length in a case where only the solar slit 22c is used as the optical element of the incidence optical system 22 and X-rays subjected to the point extraction are incident thereon will be described with reference to
Sc=(Bc+L·tan αc)/sin θ (1)
The emitted beam width Bc is a value determined by the design of the optical element, and is approximately 1 mm. In
The capture angle is an effective capture angle of a portion captured by the optical element from the X-rays that diverge in all directions from the focal point 12. As the capture angle is increased, the amount of X-rays captured by the optical element is increased. The capture angle width direction αc is a capture angle when the optical system is viewed from the side. In the case where the solar slit 22c is used, the capture angle width direction αc is an expansion angle of the X-ray beam passing through the solar slit 22c, and αc is in a range of approximately 0.1° to 0.6°. The X-ray incident angle θ with respect to the sample 25 is typically set to about the half of the diffraction angle.
Next, as shown in (b) in
SL=XL+R·tan αL (2)
The actual focal length XL is sectional lengths of the actual focal points 13 and 14 after the extraction shown in
Next,
A method of calculating the sample irradiation width and the sample irradiation length in a case where the multi-layer film parabolic mirror 22b in addition to the solar slit 22c are used as the optical element and X-rays subjected to the line extraction are incident thereon will be described with reference to
Sc=(Bc+L·tan β)/sin θ (3)
In Expression (3), β is an expansion angle of the emitted beam until the beam reaches the sample after being emitted from the solar slit 22c, and is a value determined by the design of the multi-layer film parabolic mirror 22b. In Examples of Table 3, 0.05° was used as a general value. Bc is a value determined by the design of the optical element, and is approximately 1 mm. In
The sample irradiation length SL is calculated from a slit outlet focal length XLo, the sample distance L, and the capture angle longitudinal direction αL, by the following Expression (4).
SL=XLo+L·tan αL (4)
The slit outlet focal length XLo becomes equal to the slit length of the restriction slit 22d in the case of the figure. The sample distance L and the capture angle longitudinal direction αL are as described above.
The diffraction angle used in the determination apparatus according to this embodiment is an angle corresponding to a crystal lattice spacing d of 1.5 Å or higher. This is shown in Table 2. In addition, in this embodiment, the diffraction angle corresponding to the crystal lattice spacing d means that a range finely adjusted within ±0.5° is included. Particularly, in this embodiment, diffraction angles corresponding to the crystal lattice spacings d of Nos. 5, 7, 9, 10, 12, 13, and 15 are preferably employed. The diffraction angle is a preferable diffraction angle which enables a relatively high coefficient of correlation between the refraction intensity at each diffraction angle and the thickness of the alloy phase including the ζ phase, the δ1 phase, and the Γ·Γ1 phase and accurate measurement of adhesion of the coating layer.
Next, the light-receiving optical system 23 will be described. An example of the arrangement of the light-receiving optical system is shown in
Next, as the X-ray detector that can be used in the determination apparatus according to this embodiment, for example, there are a proportional counter (PC) which achieves ionization by X-rays using gas, a scintillation counter (SC) which achieves ionization using a solid light-emitting action, a solid state detector (SSD) which is operated using a semiconductor element, and the like. As the proportional counter, a gas flow type acounter, in which operation is performed while allowing gas to flow, and a sealed type sealed in a metal container can be used. As the solid state detector, an Si (Li) type detector which is used while being cooled by liquid nitrogen, a silicon drift detector which does not use liquid nitrogen due to electron cooling, and the like. The proportional counter rather than the scintillation counter, and the solid state detector rather than these counters has an excellent ability to discriminate (energy resolution) of X-ray incident on the detector. However, the solid state detector is expensive and it is difficult to manufacture a large element with this. Therefore, not many solid state detectors having a large effective area are on the market. The scintillation counter and the proportional counter are relatively cheap and can be relatively easily manufactured to have an appropriate size for diffracted X-ray analysis, which is appropriate even in this embodiment.
In a case where the sample is a galvanized steel sheet, when the energy of incident X-rays is higher than the excitation energy of Fe-Kα fluorescence X-rays of the steel sheet, the X-rays incident on the detector 24 include both the diffracted rays of the incident X-rays and fluorescence X-rays of iron. The fluorescence X-rays of iron are treated as noise components in the diffracted rays and reduce the accuracy of the obtained information regarding the X-rays. Here, when rays having a lower excitation energy than that of the Fe-Kα fluorescence X-rays, for example, Co-Kα rays are selected as the energy of X-rays, the generation of fluorescence X-rays of iron can be limited. As a result, the accuracy of the obtained X-ray information can be increased, which is appropriately for use as the determination apparatus according to this embodiment. However, in this case, Zn-Kα fluorescence X-rays are not excited, and thus are not compatible with an X-ray source of a Zn coating weight meter.
The determination apparatus according to this embodiment includes the X-ray tube and the optical system designed to allow the two parameters “emitted beam luminance” and “width-direction gain” to be higher than specific lower limits on the premise of the parallel beam optical system, and can detect a desired diffraction peak with good sensitivity. First, the “emitted beam luminance” will be described.
The “emitted beam luminance” is the luminance of X-rays per sample irradiation area. The calculation order is as follows.
1) An effective focal point luminance is obtained.
2) Capture correction and reflectance correction are performed.
3) The emitted beam luminance is obtained from the correction and the sample irradiation area.
The effective focal point luminance is a value obtained by dividing the X-ray output by the actual focal area. The actual focal area is obtained as follows from the actual focal size shown in
a) In case of point extraction: ½ (actual focal width)×½ (actual focal length)×π (5)
b) In case of line extraction: actual focal width×actual focal length (6)
A value that approaches an actual measurement value is obtained through calculation using elliptic approximation of the actual focal point in the case of the point extraction and using rectangular approximation in the case of the line extraction.
Next, capture correction is performed in consideration that the amount of the X-ray output per actual focal point unit area captured in the width direction and in the longitudinal direction, and reflectance correction is performed in consideration of the degree of reflection of the mirror being used. The correction expressions are as follows.
Capture correction=effective focal point luminance×capture angle width direction×capture angle longitudinal direction (7)
Reflectance correction=capture correction×reflectance width direction×reflectance longitudinal direction (8)
The capture correction is to correct the degree of the effective focal point luminance (the intensity of all X-rays that diverge from the X-ray source) being used (the product of width and length). The reflectance correction is the product of the reflectances of the optical element in the width direction and in the longitudinal direction.
(8) A value obtained by dividing the corrected values obtained in Expression (8) by the sample irradiation area is the “emitted beam luminance”. The sample irradiation area is the product of the sample irradiation width Sc and the sample irradiation length SL shown in
Next, the “width-direction gain” will be described. The width-direction gain is calculated by the following expression.
Width-direction gain=capture angle width direction×reflectance width direction (9)
The width-direction gain is an index that, when the optical element such as the mirror is viewed from the X-ray source, indicates the degree of visibility of the element in the width direction and the degree of reflectance being used. An increase in the width-direction gain means effective use of the optical element, and the X-rays from the ray source are effectively captured, collimated, and reflected to be guided to irradiate the sample.
In the determination apparatus of this embodiment, the emitted beam luminance is preferably 20 W/mm2 or higher, more preferably 50 W/mm2 or higher, and even more preferably 80 W/mm2 or higher. When the emitted beam luminance is 20 W/mm2 or higher, the diffraction intensity can be increased, and thus time for determination can be significantly reduced.
In addition, the width-direction gain is preferably 0.15 or higher, more preferably 0.25 or higher, and even more preferably 0.35 or higher. When the width-direction gain is 0.15 or higher, the utility of the X-rays can be increased. Accordingly, the diffraction intensity can be increased, and thus time for determination can be significantly reduced.
When the determination apparatus according to this embodiment is installed in the galvannealed steel sheet manufacturing line, the range of the installation position is in a range from the completion of alloying to coiling. In addition, a change in sheet thickness and the effect of steel sheet vibrations need to be considered. Although described later in Examples, in terms of apparatus performance, there is no problem in measurement sensitivity as long as a change from the reference position of the sample is within ±3 mm. Typically, it is thought that the range of the change in the sheet thickness is about 3 mm. Therefore, it is preferable that the determination apparatus is installed at a location in which the range of the steel sheet vibrations is controlled to be within 3 mm. As a method of controlling vibrations, well-known methods such as supporting using a touch roll, coiling around a roll, and installation of an anti-vibration device may be applied.
In this embodiment, the optical element that can be used in the optical system is exemplified by the solar slit and the multi-layer film parabolic mirror. However, the present invention is not limited thereto, and well-known optical elements such as a flat plate-type multi-layer film mirror having a flat reflective surface, and an analyzing crystal such as LiF, pyrographite, Si, or Ge may be applied. In addition, as in Example B, in a case where the analyzing crystal is used in the incidence optical system and the solar slit is also used thereafter, the sample irradiation width is obtained by using Expression (1), and the sample irradiation length is obtained by using Expression (4).
Hereinafter, a specific example of the determination apparatus according to this embodiment will be described with reference to
As a representative example of an on-line measurement apparatus, the specific configuration of an apparatus for detecting a Γ·Γ1 phase among Fe—Zn alloy phases will be described with reference to
By using the above-described diffracted X-ray intensity, the amount of the Γ·Γ1 phase can be measured. Regarding the quantification of the Γ·Γ1 phase, a value obtained by subtracting the background intensity from the diffracted X-ray intensity may be configured into the amount of the phase on the basis of a calibration curve created in advance.
For comparison, the configuration of a high-angle-side Fe—Zn phase peak measurement apparatus according to the related art is shown in
A determination apparatus shown in
As described above, according to the determination apparatus of this embodiment, the optical system which irradiates the galvannealed steel sheet with a parallel beam of the X-rays is provided as the optical system. Therefore, even when the galvannealed steel sheet which travels in a transportation line vibrates, the incident angle of the X-rays becomes constant in the beam, and thus the X-ray diffraction angle can be allowed to be constant, thereby enhancing the detection sensitivity of the diffracted X-rays. In addition, since the emitted beam luminance is 20 W/mm2 or higher and the width-direction gain is 0.15 or higher, the X-ray diffraction intensity can be increased, and thus time for determination can be significantly reduced.
In addition, according to the determination apparatus of this embodiment, since the detector 24 is installed at a position of the diffraction angle at which the X-ray diffraction peak corresponding to a crystal lattice spacing d of 1.914 Å is detected, the thickness of the Γ·Γ1 phase can be measured with good accuracy, and thus the adhesion of the coating layer can be determined with good accuracy.
Furthermore, according to the determination apparatus of this embodiment, since the X-ray tube in which the energy of the X-rays incident on the galvannealed steel sheet is lower than the excitation energy of Fe-Kα fluorescence X-rays is used as the X-ray tube, the detection sensitivity of the three phases of the Γ·Γ1 phase, the δ1 phase, and the ζ phase contained in the Fe—Zn alloy phases can be enhanced.
In addition, according to the manufacturing line of this embodiment, since the determination apparatus having shortened determination time is installed at a position at which the sum of a sheet thickness change and steel sheet vibrations is within ±3 mm between an alloying furnace and coiling. Therefore, even in a case where the sheet threading speed of the galvannealed steel sheet is increased, a necessary steel sheet length for adhesion determination can be reduced. Therefore, quality assurance on the entire length of the coil becomes possible, and rapid feedback to the operational conditions is facilitated.
Next, the present invention will be described using Examples.
In Example 1, results of measurement regarding a change in the intensity of an Fe—Zn phase low-angle peak corresponding to a crystal lattice spacing d of 1.5 Å or higher with the specifications of the X-ray tube and the optical system designed to change the “emitted beam luminance” and the “width-direction gain” using the parallel beam optical system in a laboratory are described. In Example 2, results of on-line measurement performed by installing the determination apparatus according to this embodiment in a galvanneal manufacturing line will be described. In addition, the present invention is not limited to the following examples.
A sample of the galvannealed steel sheet manufactured in an actual line as a test steel sheet was prepared. The Zn coating weight was 45 g/m2, and Fe (%) in the coating layer was 9.5% and 10.5%. Regarding determination of coating adhesion performed off-line, 9.5% was evaluated as pass (A grade), and 10.5% was evaluated as fail (C grade) although it was close to the borderline of pass and fail. Using this, measurement of the grades shown in Tables 3A to 3D was performed in the laboratory.
As the X-ray tube, fluorescence and diffraction sealed-type X-ray tubes which had varying output, focal size, and extraction method, and used Cr, Cu, and Co as metal targets were used. All of the extraction angles in the diffraction X-ray tube were 6°. As the fluorescence X-ray tube, an X-ray tube having a focal size on the target of 7 mm×7.5 mm and a target inclination angle of 26° with respect to electron beams from the filament was used. In this case, the effective focal size of the extracted X-rays became 7 mm×7 mm.
As the optical element of the incidence optical system, the following combinations were used. The combinations of the optical element are described along with symbols in Table 3B.
“-” . . . Only solar slit
“A” . . . Solar slit and multi-layer film parabolic mirror
“B” . . . Solar slit and pyrographite
“C” . . . Solar slit and flat type multi-layer film mirror
As the optical element of the light-receiving optical system, the solar slit was used. As the detector, the following was used. The types of detectors are described along with symbols in Table 3B.
“S-PC” . . . Sealed type gas proportional counter
“SDD” . . . Solid state detector
“SC” . . . Scintillation counter
The obtained diffraction signals of the Fe—Zn phase were evaluated from the following viewpoints.
Strength (Cps):
A value obtained by subtracting the background intensity from the peak intensity was obtained as the intensity using a steel sheet in which Fe (%) in the coating layer was 9.5%. The background was set to a straight line connecting both ends of the peak. The measurement time was 0.1 sec.
Determination Time (Sec):
The intensities of the steel sheet in which Fe (%) in the coating layer was 9.5% and a steel sheet in which Fe (%) was 10.5% were compared, and measurement time necessary for allowing the difference therebetween to become three times the measurement errors (theoretical standard deviation) was obtained. In a case of measuring the peak intensity of a Γ phase, the determination time corresponds to measurement time necessary for determination of pass or fail of adhesion.
Vibration Acceptability (Mm):
By using the steel sheet in which Fe (%) in the coating layer was 9.5%, a change in the peak intensity was examined while changing the sample position, and an acceptable degree of displacement due to vibrations was evaluated. An example of results is shown in
The results are shown in Tables 3A to 3D. In Nos. 1 to 28, the specifications of the X-ray tube and the optical system in Invention Examples were designed to increase the emitted beam luminance and the width-direction gain compared to Comparative Examples. The relationship is shown in
Nos. 29 to 31 are measurement examples of the high-angle-side Fe—Zn phase peak according to the related art. Although the signal intensity is high and steel sheet vibrations are acceptable, there is an original problem of peak separation of each phase, and the difference between samples having different Fe (%) in the coating layers cannot be accurately determined
The determination apparatus according to this embodiment was installed in the galvannealed steel sheet manufacturing line. The installation position is a horizontal pass after the completion of alloying and a roll coiling section. The configuration of the apparatus is as shown in
The galvannealed steel sheet was manufactured in the manufacturing line at a line speed of 180 mpm. During the manufacturing of the galvannealed steel sheet, an alloying temperature was intentionally changed from an appropriate alloying temperature to an excessive alloying temperature to cause a good adhesion portion and a defective portion to be present in a single coil. This test was repeatedly conducted on three coils. Samples were obtained from a front portion, a middle portion, and a tail portion in the coils, and an off-line adhesion test was conducted. The grades of adhesion include an A grade (pass), a B grade (pass although the grade is close to the borderline of pass and fail), and a C grade (fail although the grade is close to the borderline of pass and fail). The samples were subjected to a constant potential electrolysis method to peel the coating layers and allow only a Γ phase single layer to remain, and the diffracted ray intensity of the Γ phase was obtained off-line.
On the other hand, during the manufacturing of the coils, by operating the determination apparatus according to this embodiment shown in
It can be seen from
While the preferable embodiments of the present invention have been described in detail with reference to the drawings, the present invention is not limited to the embodiments. It should be noted by those skilled in the art to which the present invention belongs that various changes and modification examples can be made in the scope of the technical spirit described in the appended claims, and these examples naturally belong to the technical range of the present invention.
According to the present invention, a galvannealed steel sheet with stable quality can be stably supplied at low cost, and thus the spread of vehicles with excellent antirust properties is further accelerated. This is connected to the enhancement in the life-span and safety of vehicles and contributes to the improvement in the global environment from the viewpoint of saving resources. Therefore, industrial utility is extremely high.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2013/079044 | 10/25/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2015/059835 | 4/30/2015 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4064437 | Hirose et al. | Dec 1977 | A |
| 5155751 | Chohata et al. | Oct 1992 | A |
| 5414747 | Ruud et al. | May 1995 | A |
| 20020003858 | Kondo et al. | Jan 2002 | A1 |
| 20020174918 | Fujimura et al. | Nov 2002 | A1 |
| 20060140343 | Gibson et al. | Jun 2006 | A1 |
| 20070058776 | Kataoka et al. | Mar 2007 | A1 |
| 20080117511 | Chen | May 2008 | A1 |
| 20120288058 | Maeyama et al. | Nov 2012 | A1 |
| Number | Date | Country |
|---|---|---|
| 1392956 | Jan 2003 | CN |
| 1800839 | Jul 2006 | CN |
| 201251557 | Jun 2009 | CN |
| 101558454 | Oct 2009 | CN |
| 0 473 154 | Mar 1992 | EP |
| 1 233 265 | Aug 2002 | EP |
| 2 395 128 | Dec 2011 | EP |
| 52-21887 | Feb 1977 | JP |
| 56-94249 | Jul 1981 | JP |
| 58-190747 | Nov 1983 | JP |
| 60-58537 | Apr 1985 | JP |
| 62-59844 | Mar 1987 | JP |
| 1-301155 | Dec 1989 | JP |
| 3-249162 | Nov 1991 | JP |
| 4-42044 | Feb 1992 | JP |
| 4-110644 | Apr 1992 | JP |
| 5-45305 | Feb 1993 | JP |
| 5-264477 | Oct 1993 | JP |
| 6-347247 | Dec 1994 | JP |
| 7-260715 | Oct 1995 | JP |
| 9-33455 | Feb 1997 | JP |
| 2001-272358 | Oct 2001 | JP |
| 2002-168811 | Jun 2002 | JP |
| 3329931 | Sep 2002 | JP |
| 2010-121198 | Jun 2010 | JP |
| 2010-265525 | Nov 2010 | JP |
| 2012-255769 | Dec 2012 | JP |
| 10-1992-0004832 | Mar 1992 | KR |
| 10-2006-0071739 | Jun 2006 | KR |
| 10-2007-0031231 | Mar 2007 | KR |
| 10-2009-0071208 | Jul 2009 | KR |
| Entry |
|---|
| Extended European Search Report dated Apr. 25, 2017, issued in European Patent Application No. 13896032.3. |
| European Search Report for EP 13781069 dated Nov. 4, 2015. |
| Fujinawa et al., “Development of a High-Resolution and High-Accuracy Parallel Beam Powder Diffractometer Using Laboratory X-Ray Sources”, Advances in X-Ray Chemical Analysis, Japan 31, pp. 11-27, issued in 2000 by AGNE Gijutsu Center Inc., total 19 pages. |
| Harada, “New X-ray Source based on Multilayer Mirror”, Structural Object, vol. 10, No. 1, pp. 20-29, issued in 2004 by AGNE Gijutsu Center Inc. |
| International Preliminary Report on patentability for PCT/JP2013/079044 (PCT/IPEA/409) dated Oct. 26, 2015. |
| International Search Report for PCT/JP2013/062170 dated Jun. 25, 2013. |
| International Search Report for PCT/JP2013/079044 dated Jan. 14, 2014. |
| Kawabe et al., “Continuous Measurement of Fe Content in Galvannealed Coating”, Kawasaki Steel Technical Report, 18 (1986) 2, pp. 129-135, total 15 pages. |
| Notice of Allowance for KR 10-2014-7000382 dated Aug. 28, 2015. |
| Office Action for CN 201380002155.2 dated Aug. 5, 2015. |
| Office Action for U.S. Appl. No. 14/380,441 dated Dec. 31, 2015. |
| Taniyama et al., “In-situ Observation of Growth Behavior of Fe-Zn Intermetallic Compounds at Initial Stage of Galvannealing Process”, Materials Transactions, vol. 45, No. 7, Jan. 1, 2004, pp. 2326-2331. |
| Written Opinion of the International Searching Authority for PCT/JP2013/079044 (PCT/ISA/237) dated Jan. 14, 2014. |
| Chinese Office Action dated Dec. 13, 2017, issued in Chinese Application No. 201380080399.2. |
| Number | Date | Country | |
|---|---|---|---|
| 20160252469 A1 | Sep 2016 | US |