Patent Application
20210079042
This relates to anionic peptides and peptide hydrogels that can undergo multiple gel-to-solution (gel-sol) and solution-to-gel (sol-gel) phase transitions, and their use, such as for controlled delivery of proteins and cells to a subject, and for culturing mammalian cells.
The use of injectable hydrogels allows the local delivery of encapsulated protein therapeutics directly to tissue, limiting systemic distribution of the protein therapeutic and any associated toxicity. However, current strategies for hydrogel mediated protein delivery still have challenges that must be overcome before becoming clinically viable Limitations include engineering hydrogels that have minimal biocompatibility complications and will predictably control the rate of protein release to neighboring tissue over a desired period of time for optimal therapeutic outcome. Currently, hydrogel characteristics (mesh size, etc.) are relied upon to control the release profile of the encapsulated protein. Thus, for every distinct protein therapeutic, a corresponding hydrogel must be engineered (one protein-one gel); this represents a tremendous research and regulatory burden.
Several attempts have been made to use synthetic hydrogels for cell encapsulation and 3D culturing. However, the adhesion and proliferation of encapsulated cells in injectable hydrogels was not possible, limiting the utility of such systems for delivery of cell-based therapeutics.
This disclose provides novel anionic amphiphilic β-hairpin peptides that self-assemble under appropriate conditions to form a reversible gel-sol hydrogel that can be used to readily deliver protein therapeutics and cells by injection to a target location in a subject. Unlike prior peptide hydrogels, the disclosed embodiments are shown to provide tunable protein release in vivo, and further to provide 3D cell culture matrices that avoid the use of non-human media components, promote growth and proliferation of cells in vitro, and continue to encapsulate the cells to retain them in the target location following injection into a target location in a subject.
In some embodiments, an isolated peptide is provided, comprising or consisting of an amino acid sequence set forth as: XBXZXZXBX-[DPP, DPG, or NG]-XBXZXBXBX, wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; and the peptide is no more than 50 amino acids in length. In several such embodiments, the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In a non-limiting example, the peptide is the AcVES3 peptide:
The disclosed peptides form an amphiphilic β-hairpin conformation in an aqueous solution comprising 150 mM NaCl and a pH of 7.4 at 25-37° C., and can be used to produce a peptide hydrogel. For example, an aqueous solution containing 2% w/v of a disclosed peptide and 150 mM NaCl and a pH of 7.4 forms a peptide hydrogel comprising a fibrillar network of a plurality of the peptide when incubated at 25-37° C. in a container. The peptide hydrogel undergoes a gel-sol phase transition upon application of shear stress, and a sol-gel phase transition upon removal of the shear stress.
In additional embodiments, a peptide hydrogel formed with a disclosed isolated peptide is provided, such as a peptide hydrogel formed with the AcVES3 peptide. In some embodiments, the peptide hydrogel further comprises a heterologous protein (such as IL-7) dispersed within the peptide hydrogel. In additional embodiments, the peptide hydrogel further comprises a heterologous protein dispersed within the peptide hydrogel, wherein the heterologous protein is fused to a peptide tag having a net positive charge that increases retention of the heterologous protein in the hydrogel.
In some embodiments, an isolated peptide is provided, comprising or consisting of an amino acid sequence set forth as: XBXZXZXBX-[DPP, DPG, or NG]-XBXZXBXBX, wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; and the peptide is no more than 50 amino acids in length, and the peptide further comprises an amino acid sequence of an integrin binding peptide. In several such embodiments, the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In a non-limiting example, the peptide is the AcVES3-RGDV peptide:
The disclosed peptides comprising the amino acid sequence of the integrin binding peptide form an amphiphilic β-hairpin conformation in an aqueous solution comprising 150 mM NaCl and a pH of 7.4 at 25-37° C., and can be used to produce a peptide hydrogel. For example, an aqueous solution containing 2% w/v of a disclosed peptide comprising the amino acid sequence of the integrin binding peptide and 150 mM NaCl and a pH of 7.4 forms a peptide hydrogel comprising a fibrillar network of a plurality of the peptide comprising the amino acid sequence of the integrin binding peptide when incubated at 25-37° C. in a container. The peptide hydrogel undergoes a gel-sol phase transition upon application of shear stress, and a sol-gel phase transition upon removal of the shear stress.
In some embodiments, a peptide hydrogel formed with a disclosed isolated peptide comprising the amino acid sequence of the integrin binding peptide is provided, such as a peptide hydrogel formed with the AcVES3-RGDV peptide. In some embodiments, the peptide hydrogel further comprises mammalian cells (such as CAR T cells) dispersed within the peptide hydrogel, wherein the mammalian cells comprise a cell surface comprising one or more integrin proteins that bind to the integrin binding peptide.
The disclosed peptide hydrogels are cytocompatibile and biocompatible, and can be used in methods of administering mammalian cells (such as CAR T cells) or a heterologous protein (such as IL-7) to a subject, for example, by injecting the hydrogel comprising the heterologous protein or mammalian cells to a target location in the subject.
In some embodiments, a syringe containing a disclosed peptide hydrogel is provided.
Further provided is a method of culturing mammalian cells in a three-dimensional matrix, comprising, mixing a disclosed peptide comprising the amino acid sequence of the integrin binding peptide and mammalian cells under conditions sufficient to form a peptide hydrogel encapsulating the mammalian cells, wherein the mammalian cells comprise a cell surface comprising one or more integrin proteins that bind to the integrin binding peptide fused to the AcVES3 peptide, and incubating the mammalian cells under conditions sufficient for cell growth and proliferation.
The foregoing and other features and advantages of this disclosure will become more apparent from the following detailed description of several embodiments which proceeds with reference to the accompanying figures.
The nucleic and amino acid sequences listed in the accompanying sequence listing are shown using standard letter abbreviations for nucleotide bases, and three letter code for amino acids, as defined in 37 C.F.R. 1.822. Only one strand of each nucleic acid sequence is shown, but the complementary strand is understood as included by any reference to the displayed strand. The Sequence Listing is submitted as an ASCII text file in the form of the file named “99301_sequence_listing_ST25.txt” (˜16 kb), which was created on Dec. 15, 2017 which is incorporated by reference herein.
Hydrogels formed from peptides disclosed herein are remarkably cytocompatible even in the absence of serum. This is surprising because prior peptide-based hydrogels typically require serum to be present to ensure cytocompatibility; proteins from the serum coat the matrix of these hydrogels, which provides a protective layer between the peptide matrix and the cells. Because of this, the prior peptide-based hydrogels are not chemically defined in that the composition of the serum protein coatings is not known, and therefore, such peptide hydrogels may not be preferred for in vivo implantation of cell-based therapeutics. In contrast, the unique charge state and hydrophilicity of the fibrils formed by the disclosed peptides (such as Ac-VES3 and AcVES3-RGDV) are believed to provide the cytocompatible properties of corresponding hydrogel. No serum proteins are needed to coat and passivate the surface of the hydrogels formed by the disclosed peptides (such as Ac-VES3 and AcVES3-RGDV), and thus the hydrogel is chemically defined.
Further, when implanted in vivo, hydrogels formed from peptides disclosed herein (such as Ac-VES3 and AcVES3-RGDV) do not elicit a lymphocytic inflammatory response, demonstrating that such hydrogels are remarkably biocompatible. In contrast, most other peptide hydrogels elicit a lymphocytic response. In light of the minimal immune background of hydrogels formed from peptides disclosed herein (such as Ac-VES3 and AcVES3-RGDV), these hydrogels are ideal materials for delivery of therapeutic proteins (such as cytokines, for example, IL-7) that modulate lymphocytic behavior.
In addition to providing superior cytocompatibility and biocompatibility, hydrogels formed from peptides disclosed herein (such as Ac-VES3 and AcVES3-RGDV) displays shear-thin/recovery mechanical properties, which allows the hydrogels and any therapeutic dispersed within the hydrogels to be delivered locally to tissue by simple syringe injection. Taken together, the cytocompatible, biocompatible, and mechanical properties of the disclosed hydrogels make them ideal for both cell and protein delivery.
Unless otherwise noted, technical terms are used according to conventional usage. As used herein, the singular forms “a,” “an,” and “the,” refer to both the singular as well as plural, unless the context clearly indicates otherwise. For example, the term “a peptide” includes single or plural peptides and can be considered equivalent to the phrase “at least one peptide.” As used herein, the term “comprises” means “includes.” Thus, “comprising a peptide” means “including a peptide” without excluding other elements. It is further to be understood that any and all base sizes or amino acid sizes, and all molecular weight or molecular mass values, given for nucleic acids or polypeptides are approximate, and are provided for descriptive purposes, unless otherwise indicated. Although many methods and materials similar or equivalent to those described herein can be used, particular suitable methods and materials are described below. In case of conflict, the present specification, including explanations of terms, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting. To facilitate review of the various embodiments, the following explanations of terms are provided:
About: Unless context indicated otherwise, “about” refers to plus or minus 5% of a reference value. For example, “about” 100 refers to 95 to 105.
Administration: The introduction of a composition into a subject by a chosen route. Administration can be local or systemic. Exemplary routes of administration include, but are not limited to, oral, injection (such as subcutaneous, intramuscular, intradermal, intraperitoneal, and intravenous), sublingual, rectal, transdermal, intranasal, and vaginal routes.
Amphiphilic β-hairpin conformation: A structural conformation of a peptide or protein. The β-hairpin conformation includes two β-strands linked by a β-turn to form a “hairpin”-like shape. The structure is amphiphilic; thus, one face of the hairpin is primarily hydrophobic, and the other is primarily hydrophilic. A limited number of the side chains of hydrophobic amino acids can exist on the hydrophilic face of the hairpin and vice versa, but not so many as to change the overall amphiphilicity of the folded structure. A non-limiting example of a peptide that can fold into an amphiphilic β-hairpin conformation is provided herein as AcVES3.
Cell culture: The process by which either prokaryotic or eukaryotic cells are grown under controlled conditions. In practice the term “cell culture” has come to refer to the culturing of cells derived from multicellular eukaryotes, especially animal cells, such as mammalian cells. Mammalian cells are grown and maintained at an appropriate temperature and gas mixture (typically, 37° C., 5% CO2) in a cell incubator. Culture conditions vary widely for each cell type, and variation of conditions for a particular cell type can result in different phenotypes being expressed. Aside from temperature and gas mixture, the most commonly varied factor in culture systems is the growth medium. Recipes for growth media can vary in pH, glucose concentration, growth factors, and the presence of other nutrient components. The growth factors used to supplement media are often derived from animal blood, such as calf serum.
Chimeric Antigen Receptor (CAR): An engineered T cell receptor having an extracellular antibody-derived targeting domain (such as an scFv) joined to one or more intracellular signaling domains of a T cell receptor. A “chimeric antigen receptor T cell” or “CAR T cell” is a T cell expressing a CAR, and has antigen specificity determined by the antibody-derived targeting domain of the CAR. Methods of making CARs (e.g., for treatment of cancer) are available (see, e.g., Park et al., Trends Biotechnol., 29:550-557, 2011; Grupp et al., N Engl J Med., 368:1509-1518, 2013; Han et al., J. Hematol Oncol., 6:47, 2013; Haso et al., (2013) Blood, 121, 1165-1174; PCT Pubs. WO2012/079000, WO2013/059593; and U.S. Pub. 2012/0213783, each of which is incorporated by reference herein in its entirety.)
Consists Of: With regard to a polypeptide, a polypeptide that consists of a specified amino acid sequence does not include any additional amino acid residues, nor does it include additional non-peptide components, such as lipids, sugars or labels.
Cytokine: A generic name for a diverse group of soluble proteins and peptides which act as humoral regulators at nano- to picomolar concentrations and which, either under normal or pathological conditions, modulate the functional activities of individual cells and tissues. These proteins also mediate interactions between cells directly and regulate processes taking place in the extracellular environment. Many cytokines act as cellular survival factors by preventing programmed cell death. Non-limiting examples of cytokines include IL-2, IL-7, and IL-15.
Disperse: Distribute throughout a medium, such as a disclosed peptide hydrogel. In particular examples, cells or proteins that are dispersed in a medium are distributed evenly throughout the medium. However, dispersal of cells or proteins in a medium does not require absolute even distribution.
Fusion Protein: A single polypeptide chain including the sequence of two or more heterologous proteins, often linked by a peptide linker.
Heterologous: A heterologous peptide refers to a peptide derived from a different source or species.
Integrin Binding Peptide: A peptide having an amino acid sequence that binds to one or more integrin proteins on the surface of cells. In a non-limiting example, an integrin binding peptide is set forth as RGDV (SEQ ID NO: 5).
Isolated: An “isolated” biological molecule (such as a nucleic acid molecule, or peptide) that has been substantially separated or purified away from other biological components in the tissue or cell of the organism in which the component naturally occurs, or from contaminants or other by-products generated when a nucleic acid molecule or peptide is generate synthetically. In some embodiments, nucleic acids and peptides that have been “isolated” include nucleic acids and peptides purified by standard purification methods. The term embraces nucleic acids and peptides prepared by recombinant expression in a host cell as well as chemically synthesized nucleic acids and peptides.
Peptide: A chain of amino acids, typically less than 75 amino acids in length, such as 20-50 amino acids in length. The residues in a peptide can include post-translational or secondary modifications, such as glycosylation, sulfation or phosphorylation, as well as chemical modifications. “Peptide” applies to naturally occurring amino acid polymers and non-naturally occurring amino acid polymers, including amino acid polymers in which one or more amino acid residues are non-natural amino acids. A “residue” refers to an amino acid or amino acid mimetic incorporated in a peptide by an amide bond or amide bond mimetic. A peptide has an amino terminal (N-terminal) end and a carboxy terminal (C-terminal) end.
Typically, the amino acids making up a peptide are numbered in order, starting at the amino terminus and increasing in the direction toward the carboxy terminus of the peptide. Thus, when one amino acid is said to “follow” another, that amino acid is positioned closer to the carboxy terminal end of the peptide than the preceding amino acid.
Peptide hydrogel: A colloid gel including an internal phase and a dispersion medium, in which an aqueous solution is the dispersion medium and a self-assembled network of peptides is the internal phase. The peptides in the hydrogel are self-assembled and are folded into an amphiphilic β-hairpin conformation in the fibrillar network that forms the internal phase of the hydrogel. The peptide hydrogels disclosed herein are made using peptides that form an amphiphilic β-hairpin conformation in an aqueous solution comprising 150 mM NaCl and a pH of 7.4 at 25-37° C. Thus, an aqueous solution containing 2% w/v of a disclosed peptide and 150 mM NaCl and a pH of 7.4 forms a peptide hydrogel comprising a fibrillar network of a plurality of the peptide when incubated at 25-37° C. in a container. Peptide hydrogels include a sufficient elastic modulus or stiffness that allows them to maintain shape. In several embodiments, the peptide hydrogel has an elastic modulus of 40 Pascal or greater. Peptide hydrogels formed from the disclosed self-assembled peptides in an amphiphilic β-hairpin conformation can be characterized by shear-thin/recovery rheological properties. The hydrogel undergoes a gel-sol phase transition upon application of shear stress, and a sol-gel phase transition upon removal of the shear stress. Thus, application of shear stress converts the solid-like gel into a viscous gel capable of flow, and cessation of the shear results in gel recovery. General information concerning peptide hydrogels having shear-thin/recovery rheological properties and methods of making same is provided, for example, in Sathaye, et al. Biomacromolecules, 2014, 15(11):3891-3900; Hule et al., 2008, Faraday Discuss, 139:251-420. In several embodiments, the peptide hydrogel can be a sterile hydrogel prepared with physiological and non-toxic dispersion medium for use to deliver a therapeutic protein or cells to a subject.
Peptide Linker: A peptide of 20 or fewer amino acids that is used to fuse two heterologous polypeptides into one contiguous polypeptide chain. Non-limiting examples of peptide linkers include glycine linkers, serine linkers, and glycine-serine linkers, such as a 10 amino acid glycine-serine linker Unless context indicates otherwise, reference to “linking” or “fusing” a first polypeptide and a second polypeptide (or to two polypeptides “linked” or “fused” together) by peptide linker refers to covalent linkage of the first and second polypeptides to the N- and C-termini of the peptide linker to form a single polypeptide chain.
Peptide tag: A peptide sequence that is attached (for instance through genetic engineering) to another peptide or a protein, to provide a function to the resultant fusion. Peptide tags are usually relatively short in comparison to a protein to which they are fused. Usually a peptide tag will be no more than about 20 amino acids in length. Peptide tags confer one or more different functions to a fusion protein (thereby “functionalizing” that protein). In several embodiments described herein, a peptide tag having a net positive charge is fused to a protein having a net negative charge to delay release of the protein from a negatively charged peptide hydrogel as described herein.
Protein: Any chain of amino acids, regardless of length or post-translational modification (e.g., glycosylation or phosphorylation). “Protein” applies to amino acid polymers including naturally occurring amino acid polymers and non-naturally occurring amino acid polymer as well as in which one or more amino acid residue is a non-natural amino acid, for example an artificial chemical mimetic of a corresponding naturally occurring amino acid. A “residue” refers to an amino acid or amino acid mimetic incorporated in a polypeptide by an amide bond or amide bond mimetic. A protein has an amino terminal (N-terminal) end and a carboxy terminal (C-terminal) end.
Polypeptide and peptide modifications: The present disclosure includes synthetic peptides, as well as derivatives (chemically functionalized polypeptide molecules obtained starting with the disclosed polypeptide sequences) and variants (homologs) of peptides described herein. The peptides disclosed herein include a sequence of amino acids that can include L- and/or D-amino acids, naturally occurring and otherwise.
Peptides can be modified by a variety of chemical techniques to produce derivatives having essentially the same activity as the unmodified polypeptides, and optionally having other desirable properties. For example, carboxylic acid groups of the protein, whether carboxyl-terminal or side chain, may be provided in the form of a salt of a pharmaceutically-acceptable cation or esterified to form a C1-C16 ester, or converted to an amide of formula NR1R2 wherein R1 and R2 are each independently H or C1-C16 alkyl, or combined to form a heterocyclic ring, such as a 5- or 6-membered ring Amino groups of the polypeptide, whether amino-terminal or side chain, may be in the form of a pharmaceutically-acceptable acid addition salt, such as the HCl, HBr, acetic, benzoic, toluene sulfonic, maleic, tartaric and other organic salts, or may be modified to C1-C16 alkyl or dialkyl amino or further converted to an amide.
Hydroxyl groups of the polypeptide side chains can be converted to C1-C16 alkoxy or to a C1-C16 ester using well-recognized techniques. Phenyl and phenolic rings of the polypeptide side chains can be substituted with one or more halogen atoms, such as F, Cl, Br or I, or with C1-C16 alkyl, C1-C16 alkoxy, carboxylic acids and esters thereof, or amides of such carboxylic acids. Methylene groups of the polypeptide side chains can be extended to homologous C2-C4 alkylenes. Thiols can be protected with any one of a number of well-recognized protecting groups, such as acetamide groups. Those skilled in the art will also recognize methods for introducing cyclic structures into the polypeptides of this disclosure to select and provide conformational constraints to the structure that result in enhanced stability. For example, a C- or N-terminal cysteine can be added to the polypeptide, so that when oxidized the polypeptide will contain a disulfide bond, generating a cyclic polypeptide. Other polypeptide cyclizing methods include the formation of thioethers and carboxyl- and amino-terminal amides and esters.
Subject: Living multi-cellular vertebrate organisms, a category that includes human and non-human mammals. In one example, a subject is a human.
Therapeutic protein: A protein capable of inducing a desired therapeutic or prophylactic effect when properly administered to a subject, alone or in combination with another therapeutic agent(s) or pharmaceutically acceptable carriers. Non-limiting examples of therapeutic proteins include, but are not limited to, antibodies, cytokines (for example, IL-7, IL-2, IL-15), blood factors (for example, Factor VIII and Factor IX), and hormones (for example, insulin, glucagon, growth hormone, gonadotropins).
This disclosure provides peptides that, under appropriate conditions (e.g., 2.0% w/v peptide in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C.), can fold into an amphiphilic β-hairpin conformation comprising a β-turn, two β-strands, a hydrophobic face, and a hydrophilic face. Under the appropriate conditions, the folded peptides self-assemble into a fibrillar network and cause a solution containing the network to undergo a sol-gel phase transition to form a hydrogel.
The resultant hydrogel is mechanically rigid and displays shear-thinning/recovery behavior. This characteristic provides a free flowing suspension during the application of shear and complete reformation of the gel network (self-healing) after cessation of the shear. This combination of shear thinning and self-healing allows material formation in a spatially resolved manner. For example, in some embodiments, one of ordinary skill in the art can inject (shear thin) a pre-formed hydrogel containing a heterologous therapeutic protein (such as IL-7) or a heterologous cell (such as a CAR T-cell) into a target location in a subject where it self heals and reforms the hydrogel containing the heterologous therapeutic protein or a heterologous cell. The shear stress converts the gel to a lower viscosity, flowable fluid. The shear stress is relieved when the fluid exits the syringe and the gel quickly self-heals, recovering its original mechanical rigidity. This shear-thinning/recovery mechanism allows the hydrogel to be easily delivered by syringe to the target location in the subject.
As illustrated in
Self-assembly of monomeric hairpins is facilitated facially by hydrophobic association of the hydrophobic faces of folded hairpins and laterally via H-bond formation and hydrophobic van der Waals contacts between neighboring hairpins. Detailed knowledge of these parameters allows control the self-assembly process and thus the ultimate hydrogel material properties. For example, under folding conditions peptides may adopt a desired secondary structure (e.g., may adopt an amphiphilic β-hairpin structure where one face of each β-strand in the hairpin is lined with hydrophobic residues and the other face is lined with hydrophilic residues). For example, intramolecular folding is dictated by the alleviation of charge density on the hydrophilic face upon folding, the formation of intramolecular hydrophobic van der Waals interactions, the formation of intramolecular hydrogen bonds between β-strands within the hairpin, and the turn propensity of the β-turn sequence included in the peptide, see, e.g.,
Thus, peptides for use in the disclosed hydrogels can be constructed to have desired characteristics by varying one or more of at least the following parameters: 1) electrostatics, for example, by varying the charge within the peptide intramolecular folding and self-assembly rates can be varied; 2) van der Waals interactions, for example, constructing peptides having varying a) lateral and facial intermolecular hydrophobic interactions and/or b) intramolecular hydrophobic interactions, allows varying the folding and self-assembly of the peptides as well as the material properties of the hydrogel; 3) hydrogen bonding, for example peptides may be constructed with varying a) intramolecular and/or b) intermolecular hydrogen bond formation to vary the folding, self-assembly and final material properties; and 4) turn sequence, for example, the turn region of peptides of the invention may be designed to control folding and thus trigger self-assembly.
In several embodiments, the disclosed peptide includes high β-sheet propensity residues flanking an intermittent four residue turn sequence. Polar and apolar residues may be arranged sequentially in the strand regions to afford amphiphilic surfaces when the peptide is folded in a β-hairpin conformation. For the four residue turn sequence, the peptide typically includes four residues (termed i, i+1, i+2, and i+3) that form a type II′ β-turn. In the disclosed AcVES3 peptide, these four residues are VDPPT, and the type II′ β-turn is defined by the dihedral angles (Phi and Psi) adopted by the DPP portion of the turn sequence, where ‘D’ denotes D-stereochemistry of the first proline residue. The preferred Phi and Psi dihedral angles (degrees) that define a type II′ turn are: residue i+1 (60,−120); residue i+2 (−80,0). However, these values can vary by +/−20 degrees and the peptide can still form the appropriate β-turn structure
In one particular embodiment, AcVES3, a 20-residue peptide is composed of high β-sheet propensity valine, glutamate, and serine residues flanking an intermittent tetrapeptide-VDPPT-designed to adopt type-IF β-turn structure. In addition to incorporating local design elements to stabilize hairpin structure, nonlocal effects were also considered by arranging the polar and apolar residues flanking the β-turn in an alternating fashion to favor β-hairpin formation in the self-assembled state. In addition, a β-branched residue was placed at the i-position of the turn to enforce a trans prolyl amide bond geometry at the i+1 position. This design element ensures that under folding conditions, intramolecular folding of monomeric hairpins is favored prior to self-assembly. A cis prolyl bond, which is designed against, could result in the presentation of individual β-strands within each monomer in an extended conformation. Peptides capable of adopting both cis and trans conformers could undergo indiscriminant self-association of extended and correctly folded monomers and may be actively designed against.
In some embodiments, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (1), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. For example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (1a), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. For example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (1b), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (1c), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (1d), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated.
In some embodiments, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (2a), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. For example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (2b), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; the DP is a proline that is a D amino acid; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (2c), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (2d), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated.
In some embodiments, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; each Z is independently selected from any one of D, E, Q, N, T, K, R, and S; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (3a), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. For example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; each B is independently selected from any one of D, E, and S; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (3b), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein each X is independently selected from any one of L, I, T, and V; the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (3c), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated. In another example, the peptide comprises or consists of an amino acid sequence set forth as:
wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some embodiments of peptide (3d), the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated.
In some embodiments, the peptide is set forth as any one of:
wherein each X, if present, is independently selected from any one of L, I, T, and V; each B, if present, is independently selected from any one of D, E, and S; each Z, if present, is independently selected from any one of D, E, Q, N, T, K, R, and S; the DP is a proline that is a D amino acid; and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C.
In a preferred embodiment, the peptide is set forth as:
In several embodiments, any of the amphiphilic β-hairpin peptides disclosed herein can be fused to an integrin binding peptide for production of peptide hydrogels that provide a matrix for cell growth and proliferation, and which can be used to administer cells to a subject. The presence of the integrin binding peptide in the hydrogel increases cell binding to the hydrogel matrix, which increases retention of the cells in the matrix. Trigger-dependent gelation of the peptide allows homogeneous cell encapsulation and its integrin-binding activity provides proliferation of encapsulated anchorage-dependent cells, though the system also may be applicable to anchorage-independent cells. The expanded cells can be directly delivered with the hydrogel to the target tissue site by syringe injection due to the shear-thinning recovery property of the hydrogel, and the delivered cells can be retained in the target tissue over an extended period of time.
In some embodiments, the peptide comprises or consists of an amino acid sequence set forth as Peptide (1) described above fused to the integrin binding peptide (such as one of RGDV (SEQ ID NO: 5), KQAGDV (SEQ ID NO: 6), RLD, KRLDGS (SEQ ID NO: 7), LDV, IDS, LET, IET, YYDLR (SEQ ID NO: 8), or FYFDLR (SEQ ID NO: 9), wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. For example, the peptide comprises an amino acid sequence set forth as Peptide (1a), Peptide (1b), peptide (1c), peptide (1d), Peptide (2a), Peptide (2b), peptide (2c), peptide (2d), Peptide (3a), Peptide (3b), peptide (3c), peptide (3d), described above fused to the integrin binding peptide (such as one of RGDV (SEQ ID NO: 5), KQAGDV (SEQ ID NO: 6), RLD, KRLDGS (SEQ ID NO: 7), LDV, IDS, LET, IET, YYDLR (SEQ ID NO: 8), or FYFDLR (SEQ ID NO: 9), wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. In some such embodiments, the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated.
In some embodiments, the peptide comprises or consists of an amino acid sequence set forth as Peptide (1) described above fused to the integrin binding peptide (such as one of RGDV (SEQ ID NO: 5), KQAGDV (SEQ ID NO: 6), RLD, KRLDGS (SEQ ID NO: 7), LDV, IDS, LET, IET, YYDLR (SEQ ID NO: 8), or FYFDLR (SEQ ID NO: 9) by a peptide linker, wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. For example, the peptide comprises an amino acid sequence set forth as Peptide (1a), Peptide (1b), peptide (1c), peptide (1d), Peptide (2a), Peptide (2b), peptide (2c), peptide (2d), Peptide (3a), Peptide (3b), peptide (3c), peptide (3d), described above fused to the integrin binding peptide (such as one of RGDV (SEQ ID NO: 5), KQAGDV (SEQ ID NO: 6), RLD, KRLDGS (SEQ ID NO: 7), LDV, IDS, LET, IET, YYDLR (SEQ ID NO: 8), or FYFDLR (SEQ ID NO: 9) by the peptide linker, wherein the C-terminus of the peptide is amidated or free carboxylic acid; the N-terminus of the peptide is acetylated or free amine; the peptide is no more than 50 amino acids in length, and the peptide is in an amphiphilic β-hairpin conformation when dissolved at 2.0% w/v in 50 mM Bis Tris Propane, pH 7.4, 150 mM NaCl, at 25° C. The peptide linker can be, for example, a glycine linker (such as GGGG, SEQ ID NO: 10), a serine linker, or a glycine-serine linker. In some such embodiments, the C-terminus of the peptide is amidated and the N-terminus of the peptide is acetylated.
In a preferred embodiment, the peptide fused to the integrin binding peptide is set forth as:
Peptides for use in the disclosed embodiments can be peptides from about 20 to about 75 residues (e.g., from about 20 to about 50 residues, from about 20 to about 40 residues, from about 20 to about 30 residues, from about 20 to about 25 residues, from about 20 to about 50 residues, from about 20 to about 40 residues, from about 20 to about 30 residues, or from about 20 to about 25 residues (“about” refers to plus or minus 2 residues). In some embodiments, the peptides for use in the disclosed embodiments can be from 20 to 75 residues (e.g., from 20 to 50 residues, from 20 to 40 residues, from 20 to 30 residues, from 20 to 25 residues, from 20 to 50 residues, from 20 to 40 residues, from 20 to 30 residues, or from 20 to 25 residues). In some embodiments, the peptide can be no more than 50 residues, such as no more than 30 residues or no more than 20 residues. In additional embodiments, the peptide can be 20, 25, 30, 35, 40, 45, or 50, residues in length. In some embodiments, the peptide can be 20 amino acids in length.
The disclosed peptides, and modified versions thereof can be synthesized using any appropriate technique, such as automated solid phase procedures. The disclosed peptides may incorporate one or more modified amino acid residues (e.g., D-amino acids, homologs of naturally occurring amino acids, amino acids with modified side chains, etc.). Exemplary techniques and procedures for solid phase synthesis are described in Solid Phase Peptide Synthesis: A Practical Approach, by E. Atherton and R. C. Sheppard, published by IRL, Oxford University Press, 1989. Alternatively, apelin-36 (42-57) peptides may be prepared by way of segment condensation, as described, for example, in Liu et al., Tetrahedron Lett. 37:933-936, 1996; Baca et al., J. Am. Chem. Soc. 117:1881-1887, 1995; Tam et al., Int. J. Peptide Protein Res. 45:209-216, 1995; Schnolzer and Kent, Science 256:221-225, 1992; Liu and Tam, J. Am. Chem. Soc. 116:4149-4153, 1994; Liu and Tam, Proc. Natl. Acad. Sci. USA 91:6584-6588, 1994; and Yamashiro and Li, Int. J. Peptide Protein Res. 31:322-334, 1988). Other methods useful for synthesizing the apelin-36 (42-57) peptides of the disclosure are described in Nakagawa et al., J. Am. Chem. Soc. 107:7087-7092, 1985.
Additional exemplary techniques for peptide synthesis are taught by Bodanszky, M. and Bodanszky, A., The Practice of Peptide Synthesis, Springer Verlag, New York, 1994; and by Jones, J., Amino Acid and Peptide Synthesis, 2nd ed., Oxford University Press, 2002. The Bodanszky and Jones references detail the parameters and techniques for activating and coupling amino acids and amino acid derivatives. Moreover, the references teach how to select, use and remove various useful functional and protecting groups. Peptides of the disclosure can also be readily purchased from commercial suppliers of synthetic peptides once the supplied is provided with the sequence of the peptide. Such suppliers include, for example, Advanced ChemTech (Louisville, Ky.), Applied Biosystems (Foster City, Calif.), Anaspec (San Jose, Calif.), and Cell Essentials (Boston, Mass.).
Following synthesis, exemplary techniques for peptide purification include reverse phase chromatography, high performance liquid chromatography, ion exchange chromatography, size exclusion chromatography, affinity chromatography, and gel electrophoresis. The actual conditions used to purify a particular peptide, or a modified form thereof, will depend, in part, on synthesis strategy and on factors such as net charge, hydrophobicity, hydrophilicity, and the like.
As discussed above, the disclosed amphiphilic β-hairpin peptides can be used to make a peptide hydrogel. The resultant hydrogel is mechanically rigid and displays shear-thinning/recovery behavior. This characteristic provides a free flowing suspension during the application of shear and complete reformation of the gel network (self-healing) after cessation of the shear. This combination of shear thinning and self-healing allows material formation in a spatially resolved manner. For example, in some embodiments, one of ordinary skill in the art can inject (shear thin) a pre-formed hydrogel containing a heterologous therapeutic protein (such as IL-7) or a heterologous cell (such as a CAR T-cell) into a target location in a subject where it self heals and reforms the hydrogel containing the heterologous therapeutic protein or a heterologous cell. The shear stress converts the gel to a lower viscosity, flowable fluid. The shear stress is relieved when the fluid exits the syringe and the gel quickly self-heals, recovering its original mechanical rigidity. This shear-thinning/recovery mechanism allows the hydrogel to be easily delivered by syringe to the target location in the subject.
Peptide hydrogels based on a disclosed peptide can readily be made by preparing an aqueous solution comprising one or more amphiphilic β-hairpin peptides as disclosed herein and altering one or more characteristics of the solution, wherein a hydrogel is formed. The characteristic altered may be any characteristic that results in formation of a hydrogel upon its alteration. Suitable examples include, but are not limited to, ionic strength, temperature, concentration of a specific ion, and pH. In particular embodiments, the character altered may be the pH of the solution. The disclosed peptides form a hydrogel at a pH of about 7 or higher. Increasing pH and increasing ionic strength both encourage hydrogel formation, and the two effects are roughly additive. Thus, the lower the pH, the higher the salt concentration necessary for hydrogel formation. In some embodiments, the hydrogel can be formed in a container (such as a syringe), for example a closed container.
In some embodiments, altering one or more characteristic of the solution results in a salt concentration of from about 10 mM to about 400 mM, such as about 50 to about 300 mM, about 100 to about 200 mM, or about 150 mM. Any salt may be used, for example, KCl, NaCl, MgCl2, KF, MgSO4, etc. In one embodiment, the salt may be NaCl. In some embodiments, the solution may have a desired pH, for example, a pH of from about 7 to about 9, a pH of from about 7.5 to about 8.5, a pH of from about 7.0 to about 8.0, or a pH of about 7.4, which may stay the same or be changed upon formation of the hydrogel.
In one non-limiting example, the hydrogel is formed in 50 mM Bis Tris Propane (BTP), 150 mM NaCl, pH 7.4. Any buffer system can be used except phosphate based buffer systems, as phosphate buffers are known to precipitate β-hairpin peptides. Accordingly, peptide hydrogels including the disclosed peptides can simply be formed by, for example, adding buffer of appropriate ionic strength to an aqueous solution of unfolded peptide; drawing the resulting solution into a syringe; and allowing it to gel at 25° C. directly in the syringe.
The disclosed hydrogels are well hydrated solid materials and have a stiffness greater than 40 Pascal (Pa), as measured by the storage modulus G′ at a strain of 0.2%. Above approximately 40 Pa the material is a self-supporting solid gel material. The stiffness can reach greater than 10,000 Pa at higher peptide concentration. The hydrogels typically contain at least 0.5 wt % peptide in an aqueous medium. For example, the disclosed hydrogel may have varying amounts of solid (peptide) material. For example, hydrogels may be formed comprising a percent by weight of peptide of from about 0.25% w/v to about 4.0% w/v, from about 0.25% w/v to about 3.0% w/v, from about 0.25% w/v to about 2.0% w/v, from about 0.25% w/v to about 1.0% w/v, from about 0.5% w/v to about 4.0% w/v, from about 0.5% w/v to about 3.0% w/v, from about 0.5% w/v to about 2.0% w/v, from about 0.5% w/v to about 1.0% w/v, from about 1.0% w/v to about 4.0% w/v, from about 1.0% w/v to about 3.0% w/v, from about 1.0% w/v to about 2.0% w/v, from about 2.0% w/v to about 4.0% w/v, or from about 2.0% w/v to about 3.0% w/v.
In one aspect, the amount by weight of peptide and the kinetics of gelation may be varied to produce a hydrogel having a desired modulus (stiffness). Hydrogels of the invention may have a modulus from about 40 Pascal (Pa) to about 50,000 Pa, from about 40 Pa to about 25,000 Pa, from about 40 Pa to about 10,000 Pa, from about 40 Pa to about 5,000 Pa, from about 40 Pa to about 1,000 Pa, from about 40 Pa to about 500 Pa, from about 40 Pa to about 100 Pa, from about 100 Pa to about 50,000 Pa, from about 100 Pa to about 25,000 Pa, from about 100 Pa to about 10,000 Pa, from about 100 Pa to about 5,000 Pa, from about 100 Pa to about 2,000 Pa, from about 100 Pa to about 1,000 Pa, from about 100 Pa to about 500 Pa, or from about 100 Pa to about 250 Pa.
In some embodiments, the disclosed peptide hydrogel includes one or more heterologous proteins (such as one or more therapeutic proteins) dispersed within the hydrogel. Non-limiting examples of therapeutic proteins that can be included in the peptide hydrogel include antibodies, cytokines (for example, IL-7, IL-2, IL-15), blood factors (for example, Factor VIII and Factor IX), and hormones (for example, insulin, glucagon, growth hormone, gonadotropins).
In a preferred embodiment, the peptide hydrogel (such as an AcVES3 peptide hydrogel) includes IL-7 dispersed within the hydrogel. Full human IL-7 sequence is set forth in Genbank NP_000871.1 (incorporated by reference herein), and as:
Typically, the human IL-7 protein included in the peptide hydrogel is the mature human IL-7 sequence, not including the signal peptide, which is set forth as:
The human IL-7 protein included in the peptide hydrogel can be glycosylated, or not glycosylated. For example, unglycosylated IL-7 protein produced in bacteria can be included in the hydrogel.
Any appropriate amount of protein (e.g., unglycosylated mature human IL-7) can be included in the hydrogel. For example, the hydrogel includes from 0.001 to 10 mg/mL heterologous protein dispersed within the hydrogel, such as from 0.001 to 10 mg/mL, from 0.01 to 10 mg/mL, from 0.1 to 10 mg/mL, from 1.0 to 10 mg/mL, from 0.001 to 5 mg/mL, from 0.01 to 5 mg/mL, from 0.1 to 5 mg/mL, from 1.0 to 5 mg/mL, from 0.001 to 1 mg/mL, from 0.01 to 1 mg/mL, or from 0.1 to 1 mg/mL heterologous protein dispersed within the hydrogel. In some embodiments, the hydrogel includes up to 10 mg/mL heterologous protein dispersed within the hydrogel, such as up to 5 mg/mL, up to 1 mg/mL, up to 0.1 mg/mL, or up to 0.01 mg/mL heterologous protein dispersed within the hydrogel.
The amphiphilic β-hairpin peptides disclosed herein are anionic. Accordingly, in typical embodiments involving a heterologous protein encapsulated within the peptide hydrogel, the heterologous protein has a net negative charge to prevent binding to the hydrogel matrix and protein denaturation. Depending on the heterologous protein, the net negative charge may lead to a relatively short retention time in the peptide hydrogel. In some embodiments, the heterologous protein included in the peptide hydrogel is fused to a peptide tag having a net positive charge to increase retention of the heterologous protein in the anionic hydrogel. For example, the peptide tag comprises from 2-10 arginine or lysine residues or a mixture thereof. Non-limiting examples of such peptide tags include the RH1 (G(RH)1R), SEQ ID NO: 12), RH2 (G(RH)2R), SEQ ID NO: 13), RH3 (G(RH)3R), SEQ ID NO: 14), RH4 (G(RH)4R), SEQ ID NO: 15), RH5 (G(RH)5R), SEQ ID NO: 16), and RH6 (G(RH)6R), SEQ ID NO: 17) tags disclosed herein. In other embodiments, the heterologous protein is fused to a peptide tag having a net negative charge that decreases retention of the heterologous protein in the anionic hydrogel. For example, the peptide tag comprises from 2-10 aspartic acid or glutamic acid residues or a mixture thereof.
In several embodiments, the peptide tag is fused to the amphiphilic β-hairpin peptide by a peptide linker, such as a glycine linker, and serine linker, or a glycine-serine linker (for example, GGSGSGGSGS, SEQ ID NO: 18).
Peptide hydrogels including a heterologous protein can be readily produced by preparing an aqueous solution comprising the heterologous protein (such as IL-7) and the amphiphilic β-hairpin peptides as disclosed herein (such as AcVES3) and altering one or more characteristics of the solution, wherein a hydrogel is formed. As discussed above, the characteristic altered may be any characteristic that results in formation of a hydrogel upon its alteration, such as ionic strength, temperature, concentration of a specific ion, and pH. In some embodiments, the hydrogel including the heterologous protein can be formed in a container (such as a syringe), for example a closed container.
The peptide hydrogel including an encapsulated protein can be used for any suitable purpose. For example, peptide hydrogels with an encapsulated therapeutic protein can be administered to a subject in need thereof (for example, by injection to a target location in the subject). T cells are essential for the immune response to opportunistic infections, yet are deficient in subjects with HIV/AIDs, sepsis, and also in chemotherapy and bone marrow transplantation patients. Administration of Interleukin-7 (IL-7) is used to maintain and increase the number and function of endogenous T cells, as well as to enhance and promote the transfer of T cells, such as in CAR T cell therapy for cancer. Thus, the peptide hydrogel comprising dispersed IL-7 protein can be administered to a subject to provide IL-7 to maintain and promote endogenous T cell function, for example to treat or inhibit opportunistic infections, HIV/AIDs, and/or sepsis, as well as to enhance and promote T cell transfer procedures.
In additional embodiments, the disclosed peptide hydrogel includes heterologous cells dispersed within the hydrogel, such as T cells, CAR T cells, and/or fibroblasts dispersed within the hydrogel. Peptide hydrogels for culture and delivery of cells are based on the amphiphilic β-hairpin peptides fused to an integrin binding peptide as disclosed herein.
Any appropriate amount of cells (e.g., CAR T cells) can be included in the hydrogel. For example, the hydrogel includes from 102 to 106 cells/mL dispersed within the hydrogel, such as from 103 to 106 cells/mL, from 104 to 106 cells/mL, from 105 to 106 cells/mL, from 102 to 105 cells/mL, from 102 to 104 cells/mL, from 102 to 103 cells/mL, from 103 to 105 cells/mL, from 103 to 104 cells/mL, or from 104 to 105 cells/mL dispersed within the hydrogel. In some embodiments, the hydrogel includes up to 106 cells/mL dispersed within the hydrogel, such as up to 105 cells/mL, up to 104 cells/mL, or up to 103 cells/mL dispersed within the hydrogel.
Peptide hydrogels including a heterologous cell can be readily produced by preparing an aqueous solution comprising the heterologous cell and the amphiphilic β-hairpin peptides as disclosed herein (such as AcVES3-RGDV) and altering one or more characteristics of the solution, wherein a hydrogel is formed. As discussed above, the characteristic altered may be any characteristic that results in formation of a hydrogel upon its alteration, such as ionic strength, temperature, concentration of a specific ion, and pH. In some embodiments, the hydrogel including the heterologous cell can be formed in a container (such as a syringe), for example a closed container.
The peptide hydrogel including an encapsulated cell can be used for any suitable purpose. For example, peptide hydrogels with an encapsulated therapeutic cell can be administered to a subject in need thereof (for example, by injection to a target location in the subject). In the situation of cell delivery into humans, it is preferable to use chemically defined media devoid of any foreign animal-derived materials such as fetal bovine serum (FBS). Accordingly, for a peptide hydrogel preparation containing dispersed cells intended for administration to a human, the peptide hydrogel and cells are typically incubated in media devoid of any foreign animal-derived materials such as FBS, for example, the culture media can be Essential 8 Medium. In some embodiments, the at least 10% of the mammalian cells dispersed within a peptide hydrogel administered to a target location in a subject remain at the target location for at least 30 days after administration.
The following examples are provided to illustrate particular features of certain embodiments, but the scope of the claims should not be limited to those features exemplified.
Development of three-dimensional (3D) cell culture matrices for tissue engineering is an important issue. Use of an injectable material is desirable for the 3D cell culture systems particularly for cell transplantation.
This example illustrated design, production, and assessment of a novel β-hairpin peptide hydrogel system to support 3D cell culture and in vivo cell delivery. An integrin-binding β-hairpin peptide is disclosed, AcVES3-RGDV, which forms a clear and rigid peptide hydrogel under physiological conditions. Two-dimensional (2D) and three-dimensional (3D) cell culture experiments using the peptide hydrogel were performed to evaluate its cyto-compatibility and cell proliferation. Moreover, in vivo cell delivery was performed using the peptide hydrogel and retention of the cells was monitored over a month.
The results demonstrate that the combination of a newly designed anionic self-assembling peptide hydrogel with an integrin-binding sequence motif creates a potent biomaterial for 2D and 3D cell culture and subsequent in vivo cell delivery. Trigger-dependent gelation of the peptide allows homogeneous cell encapsulation and its integrin-binding activity provides proliferation of encapsulated anchorage-dependent cells, though the system also may be applicable to anchorage-independent cells. The expanded cells can be directly delivered with the hydrogel to the target tissue site by syringe injection due to the shear-thinning recovery property of the hydrogel, and the delivered cells can be retained in the target tissue over an extended period of time. In summary, the 3D cell culture and cell delivery system using the integrin-binding peptide hydrogel have the potential for clinical use.
A series of anionic peptides was developed that minimize potential electrostatic interactions between the hydrogel and cells, but allow the cells to bind specifically to the hydrogel matrix for proliferation (
One of the peptides, AcVES3 was used as a starting template to develop an integrin binding peptide for 3D cell growth (
The nanoscale structure was assessed using TEM analysis (
The mechanical properties of the three peptide hydrogels were further ascertained using rheology (
Transparency of 3D cell culture matrices needs to be considered from the aspect of optical observation (Tam et al. Transparent Porous Polysaccharide Cryogels Provide Biochemically Defined, Biomimetic Matrices for Tunable 3D Cell Culture. Chemistry of Materials 28, 3762-3770 (2016)). As shown in
To evaluate cell adhesiveness of the peptide gels in 2D cell culture, HDFs (human dermal fibroblasts) were seeded onto surfaces of gels and cultured with either Essential 8 Medium or serum-free DMEM (
3D Cell Encapsulation Culture in Peptide Gels with Serum-Free Growth Media
HDFs were encapsulated and cultured in hydrogels with Essential 8 Medium to assess their performance in 3D culturing. In the AcVES3-RGDV gels, these cells proliferated well with minimal cell death even after one week of culturing (
Murine animal experiments were performed to evaluate in vivo effects of peptide gels for cell delivery. Red fluorescent protein (RFP)-expressing fibroblasts were utilized to detect and follow delivered cells by fluorescence imaging. When the cell suspension control was injected into mice, these cells disappeared after one week, which may be a consequence of either cell dispersion and/or apoptosis (
In light of the above, hydrogels formed from the AcVES-RGDV peptide are cytocompatible even in the absence of serum. This is surprising because prior peptide-based hydrogels typically require serum to be present to ensure cytocompatibility; proteins from the serum coat the matrix of these gels, which provides a protective layer between the peptide matrix and the cells. Because of this, the prior peptide-based hydrogels are not chemically defined in that the composition of the serum protein coatings is not known, and therefore, such peptide hydrogels may not be preferred for in vivo implantation of cell-based therapeutics. In contrast, the unique charge state and hydrophilicity of the fibrils formed by the AcVES3-RGDV peptide is believed to provide the cytocompatible properties of corresponding hydrogel. No serum proteins are needed to coat and passivate the surface of the hydrogels formed by the disclosed peptides (such as Ac-VES3 and AcVES3-RGDV), and thus the gel is chemically defined. In addition to providing superior cytocompatibility, hydrogels formed from AcVES3-RGDV were biocompatible, display shear-thin/recovery mechanical properties (allowing the gel to be delivered locally by simple syringe injection) and retain dispersed cells even after injection to a target location in an animal. Taken together, the cytocompatible, biocompatible, and mechanical properties of the disclosed hydrogels make them ideal for therapeutic cell delivery.
Peptide synthesis and purification. Peptides were synthesized on PL-rink resin (Agilent Technologies) using an automated ABI 433A peptide synthesizer (Applied Biosystems). Syntheses were performed via solid-phase Fmoc-based chemistry with 1H-benzotriazolium-1-[bis(dimethylamino)methylene]-5-chloro-hexafluorophosphate-(1-),3-oxide (HCTU, Peptide International) activation. Fmoc-protected amino acids were purchased from Novabiochem. Dried resin-bound peptides were cleaved from the resin and side-chain deprotected with a TFA/thioanisole/ethanedithiol/anisole (90:5:3:2) cocktail for 2 h under an argon atmosphere. Crude peptides were precipitated with cold ethyl ether and lyophilized. Peptides were purified by reversed phase-high performance liquid chromatography (RP-HPLC) with a Phenomenex PolymerX column employing a linear gradient from 0-80% acetonitrile with 20 mM ammonium bicarbonate, peptide peaks fractionated, and finally lyophilized. Peptides were converted to sodium salts by the addition of 20 mM ammonium bicarbonate at 1 mg mL−1 and a NaOH solution added and subsequently lyophilized until use. Analytical HPLC and electron spray ionization (negative mode) mass spectrometry confirmed the purity and composition of the peptides.
Circular dichroism (CD). CD spectroscopy of the peptides was measured on an Aviv 410 spectropolarimeter (Aviv Biomedical). A 300 μM solution of peptide was prepared and an equal volume of buffer (50 mM HEPES containing 300 mM NaCl, pH 7.4) was added. A peptide solution was quickly transferred to 1 mm path length cell previously equilibrated at 5° C. Then, CD wavelength spectra were collected from 200-260 nm at 37° C. CD spectra were also collected as a function of temperature to follow β-sheet formation at 216 nm (2-52° C. with a 5° C. increment and a 10 min equilibration time for each temperature point. The mean residue ellipticity [θ] was calculated from [θ]=(θobs/10lcr), where θobs is the measured ellipticity in millidegree, l is the cell path length in centimeters, c is the concentration in molar, and r is the number of residues of peptide sequence.
Transmission electron microscopy (TEM) analysis. The hydrogel nanostructure of the peptide gels was observed using a Hitachi H-7650 transmission electron microscope at a voltage of 80 kV. A 1 wt % solution of peptide and an equal volume of buffer (50 mM HEPES containing 300 mM NaCl, pH 7.4) was mixed and incubated overnight at 37° C. to allow for gelation. The next day, samples for TEM analysis were prepared by suspending 5 μL of the resulting peptide gel in 195 μL of water to yield a 40-fold dilution. Small amounts (5 μL) of each diluted gel solution were applied to separate carbon coated copper grids. After 1 min, the grid was washed with water. Then, a 1 w/v % uranyl acetate aqueous solution was placed on each grid for negative staining. Excess staining solution was blotted away, left to air dry, and the grids were imaged immediately.
Oscillatory rheology. Rheology experiments were performed on an AR-G2 rheometer (TA Instruments) equipped with a 25-mm stainless steel parallel plate geometry with a 0.5 mm gap height. To mimic syringe delivery, a shear-thinning recovery procedure was used. A 1 wt % peptide solution in water was prepared on ice and an equal volume of buffer (50 mM HEPES containing 300 mM NaCl, pH 7.4) was added to initiate gelation. For the gelation by DMEM, a 1 wt % peptide in 285 mM sucrose was prepared and an equal volume of HEPES-supplemented DMEM was added. A 300 μL of the solution was immediately transferred to the rheometer plate equilibrated at 5° C. Oil was placed around the sample and on the plate to prevent evaporation. After the temperature was ramped to 37° C. (0.5° C. s−1), a 1-hour dynamic time sweep was performed to monitor the storage (G′) and loss (G″) modulus of the resulting hydrogel. An angular frequency of 6 rad s−1 and 0.2% strain was applied. After which, a 1000% strain was applied for 30 s to disrupt the material. Subsequently, the ability of the hydrogel to reheal itself was monitored by measuring the recovery of G′ at 6 rad s−1 and 0.2% strain for additional 1 hour. Bovine type I collagen gels (0.3 wt %, Thermo Fisher Scientific) were prepared following manufacturer's instructions.
Rheology measurements of cell-encapsulating gels after 4 days of 3D cell culturing were performed using 8-mm stainless steel parallel plate geometry with a 0.5 mm gap height. A cell-encapsulating gel (100 μL) in a transwell insert (for 24 well plates, Corning) was transferred to the rheometer plate previously equilibrated at 37° C. and oil was placed around the sample. Dynamic time sweep was performed with 6 rad s−1 angular frequency and 0.2% strain, the gel was shear-thinned at 1000% strain for 30 s every 10 min, and allowed to recover by reducing the strain to 0.2%.
Optical transmittance measurements. Optical transmittance measurements were performed using Agilent 8453 UV-visible Spectroscopy System. A 1 wt % aqueous solution of peptide was prepared and an equal volume of buffer (50 mM HEPES containing 300 mM NaCl, pH 7.4) was added to initiate gelation. A 150 μL of the solution was immediately transferred to a 10 mm path length quartz cell and incubated for 1 hour at 37° C. to complete gelation. A 0.3 wt % collagen gel was also prepared following manufacturer's instructions. The transmittance of the gels was measured in the wavelength range of 380-780 nm.
Cell culture. Human neonatal dermal fibroblasts (HDFs) and red fluorescent protein (RFP)-expressing human neonatal dermal fibroblasts (RFP-HDFs) were purchased from Cell Applications and ANGIO-PROTEOMIE™, respectively. Cells were maintained in Dulbecco's Modified Eagle Medium (DMEM, low glucose, Thermo Fisher Scientific) containing 10% FBS, 100 U/mL penicillin, and 100 μg/mL streptomycin.
2D cell culture on peptide gels. Peptides were initially dissolved in water at 1 wt % on ice and mixed with an equal volume of ice-cold 2×HEPES buffer (50 mM HEPES, 300 mM NaCl, pH 7.4). The peptide solution (50 μL per well) was transferred to a non-tissue culture treated 96-well plates and incubated at 37° C. to initiate gelation. After 1 hour, HDFs (2×104 cells per 200 μL, per well) in serum-free DMEM, 10% FBS supplemented DMEM, or Essential 8 Medium (Thermo Fisher Scientific) were seeded on the peptide gels and cultured for 4 days. Bovine type I collagen gels (0.3 wt %, 50 μL per well) were prepared in 96-well plates following manufacturer's instructions.
3D cell culture in peptide gels. Peptides were initially dissolved in 285 mM sucrose at 1 wt % on ice and mixed with an equal volume of cell suspension in serum-free HEPES-supplemented DMEM (2×106 cells mL−1). The cell-peptide suspension (5×104 cells per 50 μL per insert) was transferred to a Falcon cell culture insert (for 24-well plates, 8 μm pore size, Corning) and incubated at 37° C. for 30 min for gelation. These inserts were previously coated with the empty hydrogel (30 μL per insert) to avoid cell adhesion to the bottom surface of the inserts. After gelation of cell-peptide solution, 500 μL of Essential 8 Medium were added to the top and bottom of the gels. Type I collagen gels were prepared following manufacturer's instructions. Briefly, a 0.4 wt % collagen solution was prepared on ice and mixed with cell suspension in serum-free DMEM (4×106 cells mL−1) at a ratio of 3:1 (0.3 wt % collagen, 1×106 cells mL−1).
Cell viability assay. Cell viability was evaluated by live and dead cell staining after 2D and 3D cell culture. Serum-free DMEM containing 1 μM calcein-AM and 2 μM ethidium homodimer-1 was added to the cells (200 μL per well for 2D culture and 500 μL each to the top and bottom of the gels for 3D culture). After incubation at 37° C. for 30 min, live and dead cells were visualized using EVOS FL Auto Cell Imaging System (Thermo Fisher Scientific). For the pseudo-colored composite image of varying heights of encapsulated cells, images of the live-stained cells were captured every 5 μm of height. Then Z-stack images for each 100 μm were flattened using the EVOS software, and the flattened images were pseudo-colored and merged using ImageJ.
Cell proliferation assay. A cell proliferation assay was performed using Cell Counting Kit-8 (CCK-8, Dojindo Molecular Technologies) for 2D and 3D cell culture. Serum-free DMEM containing 10% CCK-8 was added to the gels (200 μL per well for 2D culture; 500 μL to the top of the gels for 3D culture) and incubated for 2 hours at 37° C. Subsequently, media were transferred to 96-well plates (150 μL per well) and their absorbance measured at 450 nm relative to control viabilities from day 0 for 2D cell culture and day 1 for 3D cell culture. Experiments were performed in triplicate.
Cytoskeleton staining. For 2D cell culture, the peptide and collagen gels (70 μL) were prepared as described above on the glass bottom of 35 mm dishes (7 mm glass diameter, MatTek). HDFs in Essential 8 Medium (1.5×105 cells per 3 mL) were added to the dishes and incubated at 37° C. for 24 hours. Cells were fixed and permeabilized with 4% paraformaldehyde and 0.1% Triton X-100 in PBS for 15 min, and then blocked with 1% BSA in PBS. Cells were incubated with anti-vinculin antibody (hVIN-1, Sigma) for 1 hour at room temperature. Then, a goat anti-mouse IgG (H+L) cross-adsorbed secondary antibody, Rhodamine Red-X (2 μg mL−1, Thermo Fisher Scientific), Alexa Fluor 488 phalloidin (5 units mL−1, Thermo Fisher Scientific), and Hoechst 33342 (5 μg mL−1, Invitrogen) in PBS were added to the dishes and incubated for 1 hour at room temperature. After washing, cells were visualized using an EVOS FL Auto Cell Imaging System.
For 3D cell culture, HDF-encapsulating gels were prepared in the Falcon cell culture inserts (5×104 cells per 50 μL gel per insert) as described above. Next, cells were cultured in Essential 8 Medium for 4 days. Cells were then fixed, permeabilized, and stained simultaneously with 4% paraformaldehyde, 0.1% Triton X-100, and Alexa Fluor 488 phalloidin (5 units mL−1) in PBS (500 μL to the top and bottom of the gels) for 1 hour at room temperature. After washing with PBS (15 min for 3 times), Hoechst 33342 (5 μg mL−1, 500 μL to the top and bottom of the gels) was added for 30 min at room temperature. Cells were washed with PBS and visualized using an EVOS FL Auto Cell Imaging System.
In vivo studies. Six- to eight-week-old non-tumor bearing female athymic nude mice were used for this experiment (n=3). Animal care was in accordance with the procedures outlined in the Guide for Care and Use of Laboratory Animals (National Research Council, 1996; National Academy Press, Washington, D.C.) and animal protocols were approved by the Frederick National Laboratory for Cancer Research (FNLCR) Institutional Animal Care and Use Committee.
Hydrogel-based in vivo cell transplantation. RFP-HDFs were encapsulated in 0.5 wt % AcVES3-RGDV at 107 cells mL−1 as described in the 3D cell culture section. After gelation, the cell-peptide gel (106 cells per 100 μL) was injected into the left dorsal region of the mouse and as a control, RFP-HDF suspension in serum-free DMEM (106 cells per 100 μL) was injected into the right dorsal region of the mouse.
In vivo fluorescence imaging. Multispectral fluorescence imaging was performed daily (Monday-Friday) for 42 days using a Maestro Flex imager (PerkinElmer). Briefly, mice were anesthetized for 3-4 minutes in an induction chamber with 3% isoflurane with filtered air (0.2 μm filter) used as a carrier at a flow rate of 1 liter per minute. After isoflurane induction, the mice were transferred to an imaging chamber, where isoflurane was reduced to 2% and O2 was used as a carrier. The imaging platform was kept at 37° C. to maintain the mouse's internal temperature. Image acquisition (Maestro software, ver. 2.10.0) of the RFP fluorescence signal utilized a 533±26 nm excitation filter (placed in front of the 300 W xenon excitation source), a 580 nm long-pass filter (placed in front of the CCD) and implementing a multispectral imaging acquisition of 550-720 nm range, 10 nm increment, auto exposure (typically 0.5-5 seconds per emission wavelength), with a 2×2 pixel binning, resulting in a stack of images (image cube). RFP signal was distinguished from the tissue autofluorescence by employing vendor specified unmixing protocol. Quantitative analysis was performed by drawing a standard circular region of interest (ROI) over the injection site of the unmixed RFP component image. The total RFP signal (scaled counts second−1) within each ROI was measured and plotted as a function of time.
Collection of RFP-HDFs from the tissue graft. After in vivo imaging on day 42, mice were euthanized using CO2 and ex vivo images (Maestro Software) were acquired by exposing the cell-peptide gel injection site. Image acquisition and processing were performed with the same parameters as performed for in vivo imaging as stated above. Utilizing the unmixed RFP image to guide resecting the RFP-positive tissue, the RFP positive cells were resected and then homogenized by squeezing them through a cell strainer. The collected cells were then cultured on a tissue culture plate with FBS-supplemented DMEM for 10 days and observed using an EVOS FL Auto Cell Imaging System.
This example provides general and specific strategies for delivery of a protein of interest that can reliably control the rate of release from a peptide hydrogel using a designed electrostatic interaction between a peptide tag fused to the protein of interest and the hydrogel. The results illustrate a new strategy to control protein release from a peptide hydrogel. By altering the charge of the peptide tag incorporated onto the protein encapsulated in the hydrogel, mainly by changing the arginine content, a range of release profiles that were previously unattainable without alterations to the hydrogel material itself has been obtained. Furthermore, using the curves generated from different peptide tag lengths, the release profile of a linear combination of two tags to achieve a finely-tuned release timeline was could predicted and validated. The presence of heterologous protein (EGFP) and corresponding peptide tag did not alter the material properties of the hydrogel, as protein loaded AcVES3 hydrogel had identical stiffness and shear-thin recovery capabilities as the empty gel. It is anticipated that the approach provided herein will streamline protein delivery.
Protein therapeutics have become a significant source of new drugs in recent years due to high affinity and selectivity towards specific biological targets. However, proteins cannot be delivered orally and the need for constant IV injections can complicate treatment regimens and reduce patient compliance. Various delivery platforms have been investigated for improved protein delivery, but challenges remain. For many materials, the formulation process of encapsulating protein lacks precise control over the amount of drug loaded, and undesirable interactions between proteins and organic cosolvents, crosslinking agents, or the materials themselves can lead to denaturation (see, Ma, G. Journal of Controlled Release 2014, 193, 324-340). Additionally, it has been difficult to design and achieve sustained release of proteins over weeks or months (see, e.g., Vaishya et al., Expert Opinion on Drug Delivery, 12, 415-440, 2015).
Hydrogels, materials made from either synthetic or natural polymers, have received significant attention towards improving protein delivery. This is due to the fact that the soft, highly aqueous environment is compatible with protein encapsulation and many gels can be directly injected in to a site of interest. Unfortunately, there is currently no universal approach that can fine tune the release timeline of a specific protein other than altering the hydrogel itself (See Vulic et al., Biomacromolecules, 15: 3867-3880, 2014; Martino et al., PNAS, 110: 4563-4568, 2013; Vulic & Shoichet, J American Chemical Society, 134: 882-885, 2012; Battig et al., J American Chemical Society, 134: 12410-12413, 2012; Bertz et al., J Biotechnology, 163, 243-249, 2013; Freeman et al., Biomaterials, 29: 3260-3268, 2008; Young et al., J Controlled Release, 109: 256-274, 2005). Such alterations can drastically affect the material properties (i.e. rigidity and reheating), and the long regulatory process to approve different materials can be burdensome. What is needed is a simple method that can predictably control the rate of protein release, be genetically incorporated, and be readily translatable to different types of proteins without having to redesign the hydrogel for each delivery application.
Over the last decade, a variety of hydrogels based on self-assembling β-hairpin peptides have been developed. The triggering mechanism for gelation is dependent on the specific peptide, but the folding and self-assembling process results in fiber-containing nanostructures as observed by electron microscopy. The hydrogels also have self-healing properties, as they can respond to shear forces and rapidly recover their rigidity.
Initial protein delivery from peptide hydrogels was limited to rapid or very slow release by pairing a protein with a hydrogel of either the same or opposite charge, respectively (see Branco et al., Biomaterials, 31, 9527-9534, 2010; Nagy-Smith et al., J Materials Chemistry B, 4, 1999-2007, 2016). To access a more diverse range of release timelines, a new system was devised in which a genetically incorporated peptide tag on a protein of interest was engineered to interact with the hydrogel matrix (
Initially, the fluorescent protein EGFP and the hydrogelating peptide AcVES3 were selected, both having a net negative charge, and a cationic fusion tag was installed at the N-terminus of EGFP. AcVES3 was chosen because it forms strong gels at low weight percentages and is highly cytocompatible. EGFP is a good model because its high extinction coefficient allows for the detection of low protein concentrations by UV, while its folding and activity can be easily assessed by comparing the fluorescence properties of the protein before encapsulation and after release from the gel. After preliminary validation by comparing the release of EGFP and its N-terminal His-6 tagged precursor (NH6), a small library of proteins with cationic fusions of different lengths was designed and generated (see the following table). To sufficiently separate the fusion domain from the main chain of EGFP, a 10 amino acid peptide linker consisting of glycine and serine was also incorporated.
The net charge of AcVES3 is −5. The amino acid sequence of the EGFP protein used in these assays is as follows:
After encapsulation of the proteins in 0.5 wt % AcVES3 hydrogels, UV absorbance readings of the gel supernatants at various time points were used to determine the extent of protein release (
Combinations of different fusions were sought to access additional time regimes and achieve further control over protein release. To assist in the formulation process, the release data for individual EGFP analogs (
Further, the rheological properties of AcVES3 hydrogels were examined to determine whether protein encapsulation affected the shear-thin properties of the gel (
In addition, the release of multiple proteins from the AcVES3 gel was assessed (
General. All reagents and kits were purchased from commercial vendors. Experiments utilizing kits or the transformation of vectors into competent cells were performed following the protocols from their respective manufacturers, which are noted below for each. LC buffers consisted of 20 mM NH4HCO3 (Std C) and 20 mM NH4HCO3 in 80% acetonitrile (Std D). HEPES buffered saline (HBS) was used for gel experiments and UV/fluorescence measurements with 1×HBS=25 mM HEPES, 150 mM NaCl, pH 7.4.
Peptide Synthesis and Purification. AcVES3 was synthesized using standard Fmoc chemistry on an ABI 433A automated peptide synthesizer, using PL-Rink resin (0.25 mmol scale). Fmoc deprotection was performed using a cocktail of 1.0% DBU, 19% piperidine in NMP and monitored to completion by conductivity. Activation of 4 eq. of amino acid was achieved with 3.6 eq. HCTU and 10 eq DIEA in NMP, and the coupling proceeded for 30 min with constant vortexing. The peptide was cleaved from resin using 95% TFA, 2.5% TIPS, and 2.5% water for 3 hr, after which the resin was filtered and the collected filtrate was concentrated. Following ether precipitation, the crude solid was dried under vacuum. AcVES3 was purified by prep-HPLC. The crude peptide was dissolved at 2 mg/mL in Std C and 5 mL per run was injected into a Waters 600 system, equipped with a Waters 2489 UV Detector and a Phenomenex PolymerX RP-1 column (250×21.2 mm, 10 μm, heated to 40° C.). A gradient of 1% Std D per min was used for 25 min, followed by 0.5% Std D per min for 150 min. The UV trace at 220 nm was monitored and fractions containing the major peptide peak were combined and lyophilized. Purity was assessed by LCMS (Shimadzu LCMS 2020) and analytical HPLC (Agilent 1200 series, PolymerX RP-1 column, 250×4.6 mm, 10 μm) using gradients of 1% Std D per min. Purified AcVES3 was converted to the sodium salt by dissolving at 1 mg/mL Std C and adding 1 eq NaOH per glutamate residue (5 eq NaOH per 1 eq peptide) using a 0.1 M NaOH stock. The solution was then frozen and lyophilized.
Plasmid Generation of EGFP Analogs. Primers (IDT) encoding genes of interest, including N-terminal cleavage sites, underwent overlapextension PCR using the Qiagen Fast Cycling PCR kit and an EGFP containing plasmid as the template. PCR products were purified using the QIAquick PCR purification kit, then subjected to Gateway BP cloning (Invitrogen) using the pDonr253 donor vector, transformed into DH5α subcloning efficiency cells (Invitrogen), and plated on LB agar plates containing 50 μg/mL spectinomycin. The plates were grown overnight at 37° C. Single colonies were picked and grown overnight in 10 mL LB media with 50 μg/mL spectinomycin at 37° C., 250 RPM. Minipreps (Qiagen) were performed to isolate amplified entry vectors. Once the sequences were validated (Macrogen), the vectors were subjected to Gateway LR cloning (Invitrogen) using the pDest527 vector, transformed into DH5α subcloning efficiency cells, and plated on LB agar plates containing 100 μg/mL ampicillin. The plates were grown overnight at 37° C. Single colonies were picked and grown overnight in 10 mL LB media with 100 μg/mL ampicillin at 37° C., 250 RPM. Minipreps were performed to isolate amplified expression vectors and the sequences were validated prior to expression. When not in use, vectors were stored at −20 C.
Expression of EGFP Analogs. Expression vectors were transformed in to Rosetta 2 DE3 pLyss competent cells (Millipore) and plated on LB Agar containing 100 μg/mL carbenecillin and 34 μg/mL chloramphenicol. The plates were grown overnight at 37° C. Single colonies were picked and grown overnight in 20 mL LB media containing 100 μg/mL carbenecillin and 34 μg/mL chloramphenicol at 37° C., 250 RPM. 5 mL of overnight culture was used to seed 500 mL of LB (100 μg/mL carbenecillin and 34 μg/mL chloramphenicol), and the culture was shaken at 37° C., 250 RPM. OD600 was monitored until reaching a value of 0.6-0.8, usually around 2-2.5 hr. At this point, the incubator temperature was reduced to 17° C. and the flasks were cooled for 15 min. To induce expression, IPTG was added to a final concentration of 0.5 mM and the flasks were shaken at 17° C., 250 RPM for 20 h. Each flask was split into 2×250 mL centrifuge bottles and spun down for 20 min at 7000 g. The supernatant was removed and the pellets were stored at −80° C. until purification.
FPLC Purification of EGFP Analogs. Pellets (from ˜250 mL culture) were resuspended in 20 mL lysis buffer (50 mM sodium phosphate pH 8.0, 100 mM NaCl, 10 mM imidazole, 1× Bug Buster, and 1 EDTA-free protease inhibitor tablet) and subjected to sonication (1 amp, 1 s on, 1 s off, 1.5 min total on). The lysate was then centrifuged at 4° C., 7000 g for 20 min and the supernatant was syringe filtered (0.45 um). Using a GE P-960 sample pump, the lysate was injected into a GE ATKA FPLC system equipped with a 5 mL Talon resin column. Purification was carried out using a step gradient of 0/20/60/100% B (Buffer A: 50 mM sodium phosphate pH 8.0, 100 mM NaCl, 10 mM imidazole; Buffer B: 50 mM sodium phosphate pH 8.0, 100 mM NaCl, 100 mM imidazole). Fractions were monitored for absorbance at 280/488 nm, typically eluting at 60 and/or 100% B. Purity was confirmed by SDS PAGE gel, with the pure fractions combined and subjected to several rounds of buffer exchanges in to 50 mM sodium phosphate pH 8.0, 100 mM NaCl using Amicon Ultra-15 centrifugal filters (MWCO 10 kDa) to achieve sub-micromolar imidazole concentrations. The concentrated protein was diluted to 1.5 mL, and the concentration was determined by UV (ε=56000 M−1cm−1 at 488 nM). Typical yields were 20-60 mg per L culture.
FXa or TEV Protease Cleavage of EGFP Analogs. To remove the N-terminal His-6 tag encoded in the pDest527 expression vector, either FXa or TEV proteases were employed to cleave at the respective sites installed onto the fusions. For the generation of native EGFP, FXa cleavage was used to create the typical Met-containing N-terminus. The protocol followed that of the Millipore FXa cleavage/capture kit. A typical experiment would use 5 mg of NH6(pDest527)-FXa-EGFP in 10 mL of 1× cleavage capture buffer and 100 μg of FXa (protein:enzyme weight ratio of ˜50:1). The reaction was monitored by SDS PAGE gel and was typically completed within 7 hr. The reaction solution was added to prewashed p-aminobenzamidine functionalized resin to bind FXa, allowed to rock at RT for 30 min, and then the resin was filtered using an empty polypropylene column. EGFP was exchanged in to Milli-Q water using Amicon Ultra-15 filters (MWCO 10 kDa) and typically achieved near quantitative yields (˜4.5 mg from 5 mg NH6 fusion). The unstructured nature of the poly-Arg containing fusions made them susceptible to non-specific cleavage by FXa, and a TEV cleavage site was installed to circumvent this. The protocol for cleavage by Halo-TEV protease (Promega) followed that of the manufacturer. A typical experiment would use 3 mg of His-6 EGFP fusion in 3 mL buffer (50 mM phosphate, pH 8.0, 100 mM NaCl), 1 mM DTT, and 10 μL HaloTEV protease. The reaction would be monitored by SDS PAGE gel and was typically completed between 3-7 hr. The completed reaction solution was added to prewashed HaloLink resin to bind HaloTEV, allowed to rock at RT for 30 min, and then the resin was filtered using an empty polypropylene column. The RH #analogs were exchanged into buffer (50 mM phosphate, pH 8.0, 100 mM NaCl) using Amicon Ultra-15 filters to reduce DTT concentration to sub-micromolar levels. Greater than 90% yields were typically achieved (˜2.5 mg).
Prior to all gel experiments, the proteins were dialyzed into 2×HBS buffer (50 mM HEPES, 300 mM NaCl, pH 7.4).
UV Absorbance and Fluorescence Measurements. Protein stock concentrations in 2×HBS were determined by UV absorbance (ε=56000 M−1 cm−1 at 488 nM) using an Agilent 8453 UV-Vis spectrometer with a 1 cm cell, then diluted to a concentration of 60 μM in 2×HBS for gel experiments. All proteins exhibited typical UV spectra for EGFP, with 488/280 nm ratios of ˜2.0. Baseline fluorescence spectra were obtained using a Photon Technology International SpectroFluorometer and a 3×3 mm cell. Samples were diluted to 30 nM to prevent detector oversaturation. All proteins exhibited similar fluorescence properties, with maxima around 507 nm and corrected fluorescence intensities of ˜30,000 units.
Gel Release Experiments. AcVES3 was dissolved in cold Milli-Q water at 1 wt %. The peptide solution was vortexed for 30 s, chilled on ice for 10 min, and this process was repeated 2 more times to ensure complete dissolution of the peptide. 50 μL of peptide solution was added to a pre-chilled glass vial, followed by the addition of 50 μL pre-chilled protein (60 μM in 2×HBS)—3 vials were prepared for each protein. The vial was capped and the hydrogel was set for 1 hr at 37° C., with a final gel composition of 0.5 wt % AcVES, 30 μM protein in 1×HBS (25 mM HEPES, 150 mM NaCl, pH 7.4). After setting for 1 hr, 1 mL of 1×HBS was added to the top of the gel and the samples were incubated at 37° C. At specified time points, the supernatant was removed and replaced with 1 mL fresh 1×HBS. The UV spectrum for each supernatant was taken to determine protein concentration, which was used to quantify the number of moles per time point. The cumulatively released protein amount was compared to the initial protein loading in the gel (#mol cumulatively released protein/3.0×10−9 mol loaded protein). Each protein supernatant was diluted to 30 nM for fluorescence measurements and the obtained spectra were normalized to that of the corresponding protein before hydrogel encapsulation.
Oscillatory Rheology. Rheological assessment was conducted on a Texas Instruments AR-G2 rheometer using a 25 mm stainless steel parallel geometry. A representative set of proteins was used to determine whether the fusion domain affected the material properties of the AcVES3 hydrogels. The 0.5 wt % gels were prepared as described in the previous section, with 150 μL of chilled AcVES3 solution mixed with 150 μL pre-chilled 2×HBS solution (with 60 μM of protein, or just buffer for empty gel). This solution was immediately applied to the center of the plate and the upper geometry was lowered to a gap height of 0.5 cm. The temperature was increased from 5° C. to 37° C. over 100 s at a constant angular frequency of 6 rad s−1 and 0.2% strain. The storage and loss moduli were monitored for 60 min at a constant angular frequency of 6 rad s−1 and 0.2% strain at 37° C. After the time sweep, dynamic frequency sweeps (0.1-100 rad s−1 at constant 0.2% strain) and strain sweeps (0.1-1000% strain at constant 6 rad s−1) were performed to ensure that time sweep data were collected in the linear viscoelastic regime. Subsequent shear thinning experiments were carried out in duplicate. Fresh samples were applied to the plate, the geometry was lowered, and the temperature was increased from 5° C. to 37° C. The moduli were monitored for 60 min (6 rad s−1, 0.2% strain, 37° C.), followed by the application of 1000% strain for 30 s to shear the gel, after which the strain was reduced to 0.2% and the gel was allowed to recover for 60 min (6 rad s−1, 0.2% strain).
Data Fitting and Linear Combination of EGFP Analogs. Cumulative release data was fitted to the Korsmeyer-Peppas equation:
when
is the amount of protein released at time t, k is the release constant, and n is the release exponent. Excel Solver was utilized to obtain k and n of each analog by method of least squares. The predicted release was generated by summing calculated release of the analogs, scaled by the amount added as a fraction of the total concentration.
This example describes use of the AcVES3 hydrogel to provide controlled release of IL-7 protein in vitro and in vivo. As discussed below, the AcVES3 hydrogel loaded with IL-7 shows superior in vitro and in vivo activity compared to soluble IL-7.
T cells are essential for the immune response to opportunistic infections, yet are deficient in subjects with HIV/AIDs, sepsis, and also in chemotherapy and bone marrow transplantation patients. Administration of IL-7 is used to maintain and increase the number and function of endogenous T cells, as well as to enhance and promote the transfer of T cells, such as in CAR T cell therapy for cancer.
For a controlled, sustained release, IL-7 was incorporated into an anionic hydrogel (AcVES3). In in vitro studies, an IL-7-dependent T cell line proliferated for greater than 18 days with a single IL-7/hydrogel insert in the culture media, comparable to a control without the IL-7/hydrogel insert where soluble IL-7 was added to the culture media every 3 days. Thus, the IL-7/AcVES3 hydrogel is significantly more efficient than soluble IL-7 for cell culture.
In in vivo murine experiments, AcVES3 hydrogel with and without 200 μg dispersed IL-7 was injected into mice, splenocytes were isolated 9 days following injection, and relevant spleen immune cell count assessed using flow cytometry. For comparison, purified IL-7 was injected at 20 μg daily or once at day 0. There were 2-3 mice in each group. The experimental protocol is depicted in
Further, the IL-7/hydrogel greatly enhanced expansion of heterologous T cells transferred to T cell deficient mice in a model of T cell adoptive transfer (
AcVES3 hydrogel biocompatibility was assessed with histology assays (
In light of the above, hydrogels formed from Ac-VES3 did not elicit a lymphocytic inflammatory response when implanted in vivo, demonstrating that such hydrogels are remarkably biocompatible. In contrast, prior peptide hydrogels (e.g., formed from cationic peptides) elicit a lymphocytic response. In light of the minimal immune background of the AcVES3 hydrogel, these gels are ideal materials for delivery of therapeutic proteins (such as cytokines, for example, IL-7) that modulate lymphocytic behavior.
It will be apparent that the precise details of the methods or compositions described may be varied or modified without departing from the spirit of the described embodiments. We claim all such modifications and variations that fall within the scope and spirit of the claims below.