1. Field of the Invention
The invention relates generally to methods for assuring performance of photomasks employed for fabricating microelectronic products. More particularly, the invention relates to methods for assuring performance of phase shift photomasks employed for fabricating microelectronic products.
2. Description of the Related Art
Photolithographic processes and methods are integral to the fabrication of microelectronic products. They are employed for defining patterned photoresist mask layers that are employed within various microelectronic fabrication processes. The microelectronic fabrication processes may include, but are not limited to etch processes, deposition processes and ion implantation processes.
As microelectronic product feature dimensions have decreased, it has become increasingly difficult to form patterned photoresist layers with enhanced resolution while employing conventional photomasks and conventional actinic radiation sources. Phase shift photomask constructions have arisen as a result of the need for forming such patterned photoresist layers with enhanced resolution. Phase shift photomasks differ from conventional photomasks insofar as phase shift photomasks provide for a phase shifting of actinic radiation such as to provide a higher resolution (i.e., sharper) actinic radiation intensity peak transmitted through a phase shift photomask. In turn, this provides a correspondingly enhanced resolution of a patterned photoresist layer formed employing a phase shift photomask.
Various phase shift photomask constructions are known. A particularly common phase shift photomask construction is an attenuated phase shift photomask construction. It employs transparent areas of a transparent substrate that are separated by masked regions of the substrate formed from an incompletely opaque material layer. Typically, the incompletely opaque material layer has a transmittance on the order of several percent. The thickness of the incompletely opaque material layer is selected such as to provide for a phase shift of actinic radiation when employing the attenuated phase shift photomask.
While attenuated phase shift photomasks provide particular advantage when employed within photolithographic methods, they are nonetheless not entirely without problems. In that regard, it is particularly important when employing attenuated phase shift photomasks that a transmittance of an incompletely opaque material layer be within a generally narrow range. At a transmittance level below the narrow range, enhanced resolution of transmitted actinic radiation is not realized. At a transmittance level above the narrow range, a side lobe effect of the transmitted actinic radiation may occur. The side lobe effect yields an undesirable inhomogeneous photoexposure and development of a patterned photoresist layer.
Desirable are methods for assuring optimal performance of attenuated phase shift photomasks. The invention is directed towards the foregoing object.
A first object of the invention is to provide a method for assuring performance of a phase shift photomask.
A second object of the invention is to provide a method in accord with the first object of the invention, wherein the method assures optimal performance of the phase shift photomask.
In accord with the objects of the invention, the invention in a first instance provides a method for inspecting a phase shift photomask. The method provides that an optical property of a phase shift photomask is measured in an active pattern region of the phase shift photomask. The invention is particularly applicable to an attenuated phase shift photomask, where a transmittance of an incompletely opaque material layer is measured within the active pattern region. To provide optimal performance of the method, the active pattern region is designed and measured within the context of specific geometric limitations.
The invention provides a method for assuring optimal performance of a phase shift photomask.
The invention realizes the foregoing object by providing that an optical property of a phase shift photomask is measured in an active pattern region of the phase shift photomask. The optical property is measured in the active pattern region rather than, for example, a non-active pattern border region of the phase shift photomask.
The objects, features and advantages of the invention are understood within the context of the Description of the Preferred Embodiment, as set forth below. The Description of the Preferred Embodiment is understood within the context of the accompanying drawings, which form a material part of this disclosure, wherein:
The invention provides a method for assuring optimal performance of a phase shift photomask.
The invention realizes the foregoing object by providing that an optical property of a phase shift photomask is measured in an active pattern region of the phase shift photomask rather than, for example, a non-active pattern border region of the phase shift photomask.
The preferred embodiment of the invention illustrates the invention within the context of measuring a transmittance of an incompletely opaque material layer within an attenuated phase shift photomask. However, the invention is not intended to be so limited. Rather, in a broad embodiment, the invention may be employed within the context of assuring performance of phase shift photomasks including but not limited to attenuated phase shift photomasks and phase shift photomasks other than attenuated phase shift photomasks. Such other phase shift photomasks may include, but are not limited to alternating phase shift photomasks. Within a broad embodiment of the invention, an optical property measured within an active pattern region of a phase shift photomask to assure performance thereof may include, but is not limited to an optical transmittance, an optical absorbance or an optical phase shift.
The substrate 10 may be formed from any of several materials as are employed when fabricating microelectronic products. The materials may include, but are not limited to conductor materials, semiconductor materials and dielectric materials. Typically, the substrate 10 comprises a semiconductor substrate.
The blanket photoresist layer 12 may be formed of positive photoresist materials or negative photoresist materials. However, the invention provides particular value under circumstances where the blanket photoresist layer 12 is formed of a positive photoresist material.
Finally,
Within
For comparison purposes,
The invention is directed towards providing a method for assuring optimal performance of a phase shift photomask such as to avoid side lobes within an actinic radiation curve. This in turn will provide a patterned photoresist layer with enhanced resolution absent indented tops.
The invention primarily realizes the foregoing object by measuring an optical property of a phase shift photomask within an active pattern region of the phase shift photomask. The optical property is measured within the active pattern region, for example, in comparison with a non-active pattern border region of a phase shift mask where it is not measured. The method further employs the optical property measurement for purposes of disqualifying the phase shift photomask from use, thus assuring optimal performance of the phase shift photomask.
The invention employs a minimum of a 3×3 array of apertures within the attenuated phase shift photomask. The apertures are separated in a horizontal direction and in a vertical direction by an equal distance X. The invention further contemplates definition of a design ratio requirement DR for inspecting an active pattern region of an attenuated phase shift photomask. The design ratio provides that: (1) the separation distance between apertures X; minus (2) 2 times a measurement tooling registration tolerance 2RT; divided by (3) a minimum linewidth phase shift photomask design rule MDR, falls within a specified range (i.e., DR=((X−2RT)/MDR)). The specified range is preferably 1.17 to 1.8. The invention further provides for obtaining a minimum of 5 measurements at a minimum of 5 separated measurement locations within the minimum of 3×3 array. An attenuated phase shift mask is determined to be qualified for use in a photolithographic process if each of the 5 measurements has a transmittance of at least less than 6.3 percent and preferably also greater than 4.0 percent. Absent conformance with the foregoing upper limit requirement, the attenuated phase shift mask is not employed when photoexposing a blanket photoresist layer, since a side-lobing effect is expected.
With respect to definition of measurement locations within a minimum of 3×3 array within an attenuated phase shift mask, they may be defined employing a direct write database, such as a direct write electron beam database. The direct write database preferably derives from data initially employed for direct write electron beam exposure when fabricating the phase shift photomask. Individual measurement locations may be measured while employing an appropriate measurement apparatus. Aerial image measurement systems are commonly available for measurement of transmittance or absorbance. Phase angle measurement apparatus are also available for measurement of phase angles.
The preferred embodiment of the invention is illustrative of the invention rather than limiting of the invention. Revisions and modifications may be made to methods, materials, structures and dimensions in accord with the preferred embodiment of the invention while still providing an embodiment in accord with the invention, further in accord with the accompanying claims.