Patent Grant
9454077
The disclosures of all patents and publications referenced in this application are hereby incorporated by reference into this application in their entireties in order to more fully describe the state of the art as known to those skilled therein as of the date of the invention described and claimed herein.
The disclosure of this patent document contains material, which is subject to copyright protection. The copyright owner has no objection to the facsimile reproduction by anyone of the patent document or the patent disclosure, as it appears in the Patent and Trademark Office patent file or records, but otherwise reserves all copyright rights whatsoever.
In many applications, control of the surface properties is important. For example, controlling the dewetting properties of thin polymer films on an organic or inorganic substrate are important in numerous applications such as sensors, coatings, adhesives, resist layers, lubricating surfaces, and microelectronics. A smooth surface is thought to be wetted by an adsorbed species when van der Waals interactions at the substrate-liquid, liquid-air, and substrate-air interfaces allow the liquid to spread on the surface such that the contact angle is zero or very close to zero. When a thin film is cast on a nonwettable surface for which the interfacial tensions do not favor wetting, dewetting can occur, a process in which the film retracts from the surface, typically forming holes.
Currently, thin amorphous polymer films, such as polystyrene films, are applied to a surface and vitrified to stabilize the film. However, such glassy films are metastable and can spontaneously dewet when exposed to a solvent vapor or heated above the glass transition temperature. Such dewetting of films after exposure to solvent vapor is a current problem in developing sensors to detect nerve agents.
Control of surface properties can also enable new fields of study. For example, glycomics (a field that explores the information content of carbohydrates) has emerged recently. Patterning a surface with carbohydrate microarrays can allow investigation of carbohydrate interactions with viruses, enzymes, cells, antibodies, proteins and the like. However, most current methods for generating carbohydrate microarrays involve either a noncovalent immobilization that becomes less stable as the molecular weight of the carbohydrate decreases, or synthetic methods in which each carbohydrate to be spotted must first be chemically modified.
Accordingly, improved control of surface properties is currently needed to improve various applications, such as sensors, coatings, adhesives, resist layers, lubricating surfaces, microelectronics, etc., and to enable new applications.
In some aspects, the invention provides photoactive compounds of formula (I):
wherein each of the rings A-D can independently be substituted with one or more R1 groups and n can be any integer from 1 to 1000 (e.g., 1 to 10, such as 2). In formula (I), R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, a substituted or unsubstituted straight- or branched-chain alkyl containing, for example, 1 to 6 carbons, a substituted or unsubstituted alkene containing, for example, 2 to 4 carbons, —C(O)R3, —CO2R3, —OC(O)R3, —OR3, or —OC(O)R5. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Y can independently be —CH2—, —C(O)—, —OC(O)—, —C(O)O—, —C(O)NR3—, or —NR3C(O)—.
In other aspects, the invention provides photoactive compounds of formula (II):
wherein each of the rings E and F can independently be substituted with one or more R1 groups and n can be any integer from 1 to 1000 (e.g., 1 to 10, such as 2). In formula (II), R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, a substituted or unsubstituted straight- or branched-chain alkyl containing, for example, 1 to 6 carbons, a substituted or unsubstituted alkene containing, for example, 2 to 4 carbons, —C(O)R3, —CO2R3, —OC(O)R3, —OR3, or —OC(O)R5. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne.
In other aspects, the invention provides photoactive compounds of formula (IV):
wherein ring I can be substituted with one or more R1 groups and n can be any suitable integer from 1 to 100 (e.g., 1 to 20, such as 11). In formula (IV), X can be R2, —CO2R3, —C(O)NR3R3, —SR4, —CN, —OR3, a halogen, a β-diketone, a silane, a phosphate, a phosphonate, a polymer, or block copolymer. In some embodiments, X can be bound to a surface. R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, —R2, —C(O)R3, —CO2R3, —OC(O)R3, or —OR3. Each R2 can independently be hydrogen, a substituted or unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, a substituted or unsubstituted alkene which contains 2-4 carbons, a substituted or unsubstituted alkyne which contains 2-4 carbons, or —OC(O)R5, wherein R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R4 can independently be hydrogen, —S-pyridyl, —SR3, —SO2R3, or —SR8, wherein the —SR8 and the rest of formula (IV) can combine to form a bis-disulfide.
In one aspect, the invention provides methods for forming a non-dewetting cross-linked polymer film on a surface. Methods of the invention can include adding to a polymer film on a surface a compound of formula (I) or formula (II), and irradiating the compound to form a cross-linked polymer film. Alternatively, the method can include coating a surface with a composition that includes a compound of formula (I) or (II), and irradiating the composition to form a cross-linked polymer film. The cross-linked polymer film can be resistant to dewetting from the surface even after heating above the glass transition temperature or melting temperature of the polymer, or even after exposure to solvents. In some embodiments, irradiation of the polymer film may be through a photomask, resulting in a patterned array of cross-links.
In another aspect, the invention provides methods for immobilizing molecules on a surface. The method can include immobilizing a compound of formula (IV) on a surface; applying a molecule to be immobilized; and irradiating the compound. A photochemical reaction between the molecule and the compound can result in covalent links between the molecule and the compound and the compound can be immobilized on the surface. In some embodiments, the irradiation of the compound may be through a photomask. In other embodiments, the molecule may be a carbohydrate or a polymer. In some other embodiments, the invention also provides carbohydrate microarrays formed by the methods of the invention.
In yet another aspect, the invention provides arrays on a surface that includes a compound of formula (IV) immobilized on the surface and at least one molecule covalently attached to the compound of formula (IV). In some embodiments, the molecule covalently attached to the compound can be a carbohydrate, a polymer, a DNA, an RNA, a protein, a peptide, and the like.
The patent or application file contains at least one drawing executed in color. Copies of this patent or patent application publication with color drawings will be provided by the Office upon request and payment of the necessary fee.
For the purposes of promoting an understanding of the principles of the invention, reference will now be made to specific embodiments. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended. Alteration and further modifications of the invention, and further applications of the principles of the invention as illustrated herein, as would normally occur to one skilled in the art to which the invention relates, are also within the scope of the invention.
At the outset, certain terms described in this application are defined below.
The term “alkyl” as used herein refers to a substituted or unsubstituted aliphatic hydrocarbon chain and includes, but is not limited to, straight and branched chains containing from 1 to 12 carbon atoms, or in some instances, from 1 to 6 carbon atoms, unless explicitly specified otherwise. For example, methyl, ethyl, propyl, isopropyl, butyl, i-butyl and t-butyl are encompassed by the term “alkyl.” Specifically included within the definition of “alkyl” are those aliphatic hydrocarbon chains that are optionally substituted.
The term “amide” refers to)(—CONR9R10, wherein R9 and R10 are independently hydrogen or alkyl.
The term “aryl” as used herein refers to an aromatic hydrocarbon or heterocycle. The aromatic hydrocarbon or heterocycle can contain from 3 to 10 atoms in certain embodiments. For example, an aromatic hydrocarbon encompasses phenyl or naphthyl, and an aromatic heterocycle encompasses pyridyl, pyrrole, thiophene, furan, diazoles, thiazoles, oxazoles, and imidazoles.
The term “carbonyl” refers to —C(O)—.
The term “β-diketone” refers to —COCH2C(O)R7 wherein R7 is alkyl.
The term “ether” refers to —OR6, wherein R6 is a straight- or branched-chain alkyl containing from 1 to 6 carbons or a substituted or unsubstituted aryl.
The term “ester” refers to —C(O)OR7 wherein R7 is alkyl.
The term “halogen” refers to bromine, chlorine, fluorine, and iodine.
The term “phosphate” refers to —PO4Hm and its salts, wherein m is 0-3, having a charge of 0, −1, or −2.
The term “phosphonate” refers to —P(OR3)3, where R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene.
The term “silane” refers to a group comprising silicon to which at least one hydrolyzable group is bonded, such as —Si(OCH3)3, —Si(OCH2CH3)3, —Si(Cl)3, -silylimidazoles, -silylamines, and the like.
The term “carbohydrate” refers to a natural or synthetic monosaccharide, oligosaccharide, polysaccharide, or a glycoside thereof.
The term “glycoside” refers to a —O—, —N—, or —S— glycoside.
The term “oligosaccharide” refers to 1-20 monosaccharides covalently bonded together forming linear or branched structures, or structures which are a combination of both. Such structures include natural and synthetic disaccharides and branched- or straight-chain tri-, tetra-, penta-, hexa-, hepta-, octa-, nona-, and decasaccharides.
The term “mixed monolayer” refers to a monolayer or a multilayer containing at least two different types of molecules, such as phthalimides and amines.
The term “SAM” refers to a self-assembled monolayer.
Certain embodiments of the invention are directed to photoactive compounds that are capable of forming covalent bonds with nearby molecules after irradiation. In some embodiments, the invention provides photoactive compounds that may or may not be surface bound and that are capable of linking two molecules, such as polymers or small molecules.
In one or more aspects, the invention provides photoactive compounds of formula (I):
wherein each of the rings A-D can independently be substituted with one or more R1 groups and n can be any integer from 1 to 1000 (e.g., 1 to 10, such as 2). In formula (I), R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, a substituted or unsubstituted straight- or branched-chain alkyl containing, for example, 1 to 6 carbons, a substituted or unsubstituted alkene containing, for example, 2 to 4 carbons, —C(O)R3, —CO2R3, —OC(O)R3, —OR3, or —OC(O)R5. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Y can independently be —CH2—, —C(O)—, —OC(O)—, —C(O)O—, —C(O)NR3—, or —NR3C(O)—. In one embodiment, one or more R1 groups are at the meta and/or para positions of each of the rings A-D. Examples of compounds of formula (I) can include Compound 1 shown below and derivatives thereof:
In other aspects, the invention provides photoactive compounds of formula (II):
wherein each of the rings E and F can independently be substituted with one or more R1 groups and n can be any integer from 1 to 1000 (e.g., 1 to 10, such as 2). In formula (II), R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, a substituted or unsubstituted straight- or branched-chain alkyl containing, for example, 1 to 6 carbons, a substituted or unsubstituted alkene containing, for example, 2 to 4 carbons, —C(O)R3, —CO2R3, —OC(O)R3, —OR3, or —OC(O)R5. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Examples of compounds of formula (II) can include Compound 2 shown below and derivatives thereof:
In some other aspects, the invention provides photoactive compounds of formula (III):
wherein each of the rings G and H can independently be substituted with one or more R1 groups and n can be any suitable integer from 1 to 1000 (e.g., 1 to 100, 1 to 20, such as 11). In formula (III), X can be R2, —CO2R3, —C(O)NR3R3, —SR4, —CN, —OR3, a halogen, a β-diketone, a silane, a phosphate, a phosphonate, a polymer, or block copolymer. In some embodiments, X can be bound to a surface. R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, —R2, —C(O)R3, —CO2R3, —OC(O)R3, or —OR3. Each R2 can independently be hydrogen, a substituted or unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, a substituted or unsubstituted alkene which contains 2-4 carbons, a substituted or unsubstituted alkyne which contains 2-4 carbons, or —OC(O)R5, wherein R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R4 can independently be a hydrogen, —S-pyridyl, —SR3, —SO2R3, or —SR8, wherein the —SR8 and the rest of formula (III) can combine to form a bis-disulfide. Y can independently be —CH2—, —C(O)—, —OC(O)—, —C(O)O—, —C(O)NR3—, or —NR3C(O)—. Examples of a compound of formula (III) can include Compound 3 shown below and derivatives thereof:
In other aspects, the invention provides photoactive compounds of formula (IV):
wherein ring I can be substituted with one or more R1 groups and n can be any suitable integer from 1 to 1000 (e.g., 1 to 100, 1 to 20, such as 11). In formula (IV), X can be R2, —CO2R3, —C(O)NR3R3, —SR4, —CN, —OR3, a halogen, a β-diketone, a silane, a phosphate, a phosphonate, a polymer, or block copolymer. In some embodiments, X can be bound to a surface. R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, —R2, —C(O)R3, —CO2R3, —OC(O)R3, or —OR3. Each R2 can independently be hydrogen, a substituted or unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, a substituted or unsubstituted alkene which contains 2-4 carbons, a substituted or unsubstituted alkyne which contains 2-4 carbons, or —OC(O)R5, wherein R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R4 can independently be a hydrogen, —S-pyridyl, —SR3, —SO2R3, or —SR8, wherein the —SR8 and the rest of formula (IV) can combine to form a bis-disulfide. Examples of a compound of formula (IV) can include Compound 4 shown below and derivatives thereof:
In some embodiments, the photoactive compounds of the invention can include compounds that can form radicals that lead to the formation of covalent bonds. For example, exposure to UV light can allow the photoactive compound to undergo photochemical hydrogen abstraction reactions (e.g., abstracting a hydrogen atom from a nearby molecule). The resulting radicals can then recombine, forming a covalent bond. In some embodiments, the photoactive compounds of the invention can include compounds that can form radicals near a carbonyl group. Moreover, the photoactive compounds of the invention can include aromatic carbonyl functional groups that can react with hydrogen atom donors (e.g., C—H groups, Si—H groups, S—H groups, and the like) upon absorption of a photo to form covalent bonds. As an example,
Alternatively, the photoactive compounds of the invention can abstract electrons from molecules that have suitable electron donating groups, such as amines and sulfides. Electron transfer to the photoactive compound can be followed by proton transfer and can result in covalent bond formation between the photoactive compound and the molecule having a suitable electron donating group in a manner similar to hydrogen abstraction described above.
The specific choice of photoactive compound for use in the invention will depend on characteristics of the desired application. For example, self quenching ability, quenching by a particular polymer, miscibility in various polymers, and whether there are chromophores in the surrounding that are affected by various wavelengths of light can all be factors to consider in choosing the desired photoactive compounds of the invention.
The invention also provides compounds of Formula (V):
wherein X can be —R2, —CO2R3, —C(O)NR3R3, —SR4, —CN, —OR3, a halogen, a β-diketone, a silane, a phosphate, a phosphonate, a polymer, or block copolymer; Z can be —NR3R3, —OH, —SH, —C(O)NR3R3, —CO2R3, a carboxylate, an ammonium, or a salt thereof; and n can be an integer from 1 to 1000, such as 1 to 100, 1 to 30, 1 to 20, 1 to 15, 1 to 10, 5 to 20, 5 to 15, 5 to 10, or 15 to 30, or n is 8, 9, 10, 11, 12, or 13. Each R2 can independently be hydrogen, a substituted or unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, a substituted or unsubstituted alkene which contains 2-4 carbons, a substituted or unsubstituted alkyne which contains 2-4 carbons, or —OC(O)R5, wherein R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R4 can independently be a hydrogen, —S-pyridyl, —SR3, —SO2R3, or SR8, wherein the —SR8 and the rest of formula (V) can combine to form a bis-disulfide. In one embodiment, Z can be a polar group or a group that has a charge, such as a positive or negative charge. Examples of a compound of formula (V) can include Compound 5 shown below and derivatives thereof:
In some embodiments, compounds of Formula (III), (IV), and (V) can be immobilized on a surface as a mixture containing at least two of the compounds. For example, the compounds of Formula (V) can be mixed together with a compound of Formula (III) or (IV), or both, prior to or concurrently with addition to the surface. The compound of Formula (V) may be able to improve the biomolecular compatibility and/or binding affinity for molecules to be immobilized, such as a carbohydrate, to surfaces having the compounds of Formula (III) and/or (IV).
In some embodiments, the ratio of compound of Formula (V) to compound of Formula (III) and/or (IV) may be from about 100:1 to about 1:1. For example, the ratio of compound of Formula (V) to compound of Formula (III) and/or (IV) may be from about 100:1, 80:1, 60:1, 50:1, 30:1, 20:1, 10:1, 5:1, 2:1, and the like to about 1:1.
Therefore, the compounds of the invention have a number of significant advantages over those of the conventional art. For example, a protecting group is not needed which can facilitate in the synthesis of the compounds. Moreover, additional reagents are not needed to react with the compounds as the radicals that form upon irradiation can readily form covalent bonds with nearby molecules.
It should be noted that other photoactive compounds having a similar structure to that shown for compounds of Formula (I) through (IV) described above are within the scope of the invention. For example, the phthalimide or benzophenone portion of compounds of Formula (I) through (IV) can be replaced with acetone, xanthone, and other aromatic hydrocarbons having carbonyl groups. For example, compounds of Formula (VI) are within the scope of the invention,
wherein each of the rings A-D can independently be substituted with one or more R1 groups and n can be any integer from 1 to 1000 (e.g., 1 to 10, such as 2). In formula (VI), R1 can independently be a hydrogen, a halogen, a hydroxyl, an aryl, an amide, a cyano, a substituted or unsubstituted straight- or branched-chain alkyl containing, for example, 1 to 6 carbons, a substituted or unsubstituted alkene containing, for example, 2 to 4 carbons, —C(O)R3, —CO2R3, —OC(O)R3, —OR3, or —OC(O)R5. Each R3 can independently be a hydrogen, a substituted or unsubstituted C1-C10 straight-chain or branched-chain alkyl, or a substituted or unsubstituted alkene. Each R5 can independently be a hydrogen, an unsubstituted straight- or branched-chain alkyl which contains 1-6 carbons, or a straight- or branched-chain alkyl which contains 1-6 carbons and is substituted by an alkyne. Y can independently be —CH2—, —C(O)—, —OC(O)—, —C(O)O—, —C(O)NR3—, or —NR3C(O)—. In one embodiment, one or more R1 groups can be at the meta and/or para positions of each of the rings A-D. Other exemplary compounds described above will be readily apparent to one of ordinary skill in the art.
The invention relates to methods for controlling surface properties of materials. In certain embodiments, methods for controlling the dewetting properties of layers on surfaces are described. In other embodiments, methods for providing a desired architecture on a surface are provided by controlling the dewetting properties of layers on surfaces. In yet other embodiments, methods for controlling the affinity for certain materials on the surface are provided.
In the following embodiments, compounds of formula (I), compounds of formula (II), compounds of formula (III), and/or compounds of formula (IV) can be utilized as a photoactive compound. For example, mono-benzophenone, bis-benzophenone, mono-phthalimide, bis-phthalimide, or derivative compounds thereof can be utilized. The amount of compound added will depend on the desired amount for each application, as can be readily determined by one skilled in the art. For example, the photoactive compound can be utilized as a 1% solution.
In certain embodiments, irradiation can be carried out with ultraviolet light. In some embodiments, light of wavelengths from 290-350 nm, (e.g., 290-300 nm and/or 330-350 nm) can be used in the invention. In one embodiment, the polymer film can be irradiated for a period of time suitable to form the desired amount of cross-links. For example, the polymer film can be irradiated for about an hour. The extent of reaction may be monitored with techniques known to the skilled artisan, such as optical microscopy and atomic force microscopy to look at the degree of dewetting, and infrared spectroscopy to look at the disappearance of the carbonyl peak.
The surface can be the surface of an inorganic material, an organic material, a polymer, and the like. For example, the surface can be the surface of silicon, titania, glass, gold, polycarbonate, polystyrene, poly(vinyl alcohol), poly(tert-butyl acrylate), poly(methyl methacrylate), paper, fingernail, and the like.
In certain embodiments, the surface can be the surface of a device, such as a chip, an optical lens, a plate, a sensor, a biomedical device, a circuit, a substrate for electroplating, or a combination thereof.
Controlling Dewetting Properties of Polymers
In certain embodiments, the invention relates to methods for stabilizing layers from dewetting from a surface. Methods of the invention can include (1) adding a photoactive compound (e.g. Compound 1 shown in
In yet other embodiments, methods of the invention can include (1) coating a surface with a composition that include a polymer and a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation, and (2) irradiating the composition to form a cross-linked polymer.
The cross-linked polymer described above can be formed as a coating on a surface, and at various thicknesses. For example, the cross-linked polymer can form a coating with a thickness of less than 5 nm, 10 nm, 20 nm, 50 nm, 100 nm, 500 nm, 1 micron, 10 micron, 50 micron, 100 micron, 200 micron, 300 micron, 500 micron and the like. If a monolayer of polymer is formed on the surface, the thickness can depend on the molecular weight of the polymer. In some embodiments, the polymer may be applied to the surface by spin coating, spray coating, or any other conventional techniques known in the art to obtain a uniform coating.
In some embodiments, the photoactive compound can further include a desired functional group. Some examples of desired functional group include functional groups that have specific affinity to other molecules, such as peptides or small molecules. In other embodiments, one or more additional compounds that are capable of providing a desired functionality can be added to a polymer on a surface. Some examples of one or more additional compounds can include one or more of a peptide, growth factor, antibody, small molecule drug, carbohydrate, lipid, antibiotic, antimicrobial, and the like. In some embodiments, the desired functionality may be at least some resistance to antigens, nerve agents, and the like.
Any polymer can be used in the invention. Some exemplary polymers can include polymers that contain a tertiary hydrogen and electron donating or withdrawing groups that can form resonance structures with the resulting radical after hydrogen abstraction occurs on the polymer chain, such as polystyrenes, polyethers, polyesters, polyamides, polyvinyls, polysaccharides, and the like.
The invention also provides methods for forming a non-dewetting, patterned array of cross-linked polymer. In certain embodiments, a robotic spotter can be utilized to pattern areas containing a photoactive compound and polymer, and the patterned array can be irradiated. Alternatively, a mask containing the desired pattern or image can be placed over a surface coated with a photoactive compound and polymer, and the coating can be irradiated though the mask. Other suitable methods to form a patterned array of cross-linked polymer will be readily apparent to one of ordinary skill in the art. The patterned array of cross-linked polymer can become resistant to dewetting.
The cross-linked polymer films of the invention have applications in thin film device fabrication, particularly in microelectronics, sensors, and coating compositions. For example, a polymer surface applied to a surface acoustic wave sensor can serve as an artificial nose or sniffer system. Generally, thin polymer films are coated onto quartz, and an aromatic ketone group on the surface reacts in the presence of light, where adsorption causes a change in the wave sensor. The invention can provide polymer films that can be utilized to form stable surfaces that that normally would not be stable and improve the performance of these devices.
Other examples include use of the polymer films as adhesives, such as self-adhesives, hot-melt adhesives, or as UV-curable binding agents in coating compositions, such as protective materials for coating mineral surfaces or as paints. The methods of the invention are particularly suitable for the production of coatings and protective films, such as coatings for clothing, cosmetics, and personal care products.
The cross-linked polymer film of the invention can also be applied as a removable layer in many applications. For example, a polymer can be applied to the skin of a burn patient, cross-linked to form a protective surface layer, and the cross-linked polymer can be peeled off later. A cross-linked polymer of the invention can also be used as a tough surface layer for inorganic substrates, such as hydrogels or monolayers.
The addition of a desired functionality to the non-dewetting cross-linked polymer film can be particularly desirable for some thin film applications. For example, the methods of the invention can be suitable for linking biological molecules such as peptides, growth factors, antibodies, small molecule drugs, carbohydrates, lipids, antibiotics and antimicrobials to non-dewetting polymer films. For wound healing applications, polymer films can be fabricated to deliver biological molecules such as growth factors or antigen-resistant drugs to the site of injury.
The methods of the invention are also applicable to the development of protective coatings for use against biological weapons. For example, a desired functionality such as nerve agent or antigen resistance can be provided to a polymer, and the polymer applied as a protective coating to clothing worn by military personnel.
Forming Three-Dimensional Structures on Surfaces
The invention also provides methods for forming three-dimensional structural features. Methods of the invention can include (1) adding a photoactive compound to a polymer on a surface, where the photoactive compound is capable of forming covalent bonds with nearby molecules upon irradiation, (2) placing a mask which contains a desired pattern, (3) irradiating the photoactive compound through the mask to form a pattern of cross-linked and uncrosslinked polymer, and (4) heating the pattern to a temperature that is near or above the glass transition temperature or the melting temperature of the polymer. Upon heating the surface, at least some of the uncrosslinked polymer can migrate toward the interface between the crosslinked and uncrosslinked regions to form a vertical structure.
In other embodiments, methods of the invention can include (1) coating a surface with a composition that includes a polymer and a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation, (2) placing a mask which contains a desired pattern, (3) irradiating the photoactive compound through the mask to form a pattern of cross-linked and uncrosslinked polymer, and (4) heating the pattern to a temperature that is near or above the glass transition temperature or the melting temperature of the polymer. Upon heating the surface, at least some of the uncrosslinked polymer can migrate toward the interface between the crosslinked and uncrosslinked regions to form a vertical structure.
In yet other embodiments, methods of the invention can include (1) coating a surface with a polymer (2) forming on the polymer a pattern of photoactive compound capable of forming covalent bonds with nearby molecules after irradiation, (3) irradiating the photoactive compound to form a pattern of cross-linked and uncrosslinked polymer, and (4) heating the pattern to a temperature that is near or above the glass transition temperature or the melting temperature of the polymer. Upon heating the pattern, at least some of the uncrosslinked polymer can migrate toward the interface between the crosslinked and uncrosslinked regions to form a vertical structure.
In some embodiments, the polymer may be applied to the surface by spin coating, spray coating, or any other conventional techniques known in the art to obtain a uniform coating.
The polymer described above can be formed as a coating on a surface, and at various thicknesses. For example, the polymer may be formed as a coating with a thickness of greater than 1 nm, 5 nm, 10 nm, 20 nm, 50 nm, 100 nm, 500 nm, 1 micron, 10 micron, 50 micron, 100 micron, 200 micron, 300 micron, 500 micron and the like. If a monolayer of polymer is formed on the surface, the thickness can depend on the molecular weight of the polymer.
The pattern described above can be formed at various widths. For example, the uncrosslinked or crosslinked regions can be formed have a width that is greater than 20 nm, 50 nm, 100 nm, 500 nm, 1 micron, 10 micron, 50 micron, 100 micron, 200 micron, 300 micron, 500 micron, 1 mm, and the like.
The height of the vertical structure that builds up near the interface of the crosslinked and uncrosslinked regions can be dependent on the thickness of the polymer film and/or the width of the uncrosslinked regions. Greater thickness and width of the uncrosslinked regions may lead to greater height of the vertical structure near the interface. The height of the material that builds up near the interface can be greater than 5 nm, 10 nm, 20 nm, 50 nm, 100 nm, 200 nm, 300 nm, 500 nm, 1000 nm, and the like.
In some embodiments, the photoactive compound can further include a desired functional group. Some examples of desired functional group can include functional groups that have specific affinity to other molecules, such as peptides or small molecules. In other embodiments, a second compound that is capable of providing a desired functionality can be added to a polymer on a surface. Some examples of the second compound include one or more of a peptide, growth factor, antibody, small molecule drug, carbohydrate, lipid, antibiotic, antimicrobial, and the like. In some embodiments, the desired functionality may be at least some resistance to antigens, nerve agents, and the like.
Any suitable polymer can be used in the invention. Some exemplary polymers can include polymers that contain a tertiary hydrogen and electron donating or withdrawing groups that can form resonance structures with the resulting radical after hydrogen abstraction occurs on the polymer chain, such as polystyrenes, polyethers, polyesters, polyamides, polyvinyls, polysaccharides, and the like.
The patterned three-dimensional structures can be utilized in a number of different applications, such as for microreactors carrying out microscopic amounts of reaction near the surface. The patterned three-dimensional structures may be utilized as assays to determine which reactions are successful by placing suitable markers after reaction. For example, to test for successful synthesis of a particular carbohydrate, various different reagents can be utilized in each microreactor. After the surface has been subjected to a suitable reaction condition, a marker can be deposited into the microreactors, where the marker fluoresces only when it binds to the carbohydrates that form after a completed reaction. The detection of the fluorescence signal in various microreactors can be utilized to determine which reagents are suitable for a successful reaction.
Immobilizing Molecules on a Surface
Other embodiments of the invention also relate to methods for immobilizing molecules on a surface. Methods of the invention can include (1) immobilizing on a surface a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation; (2) applying a molecule to the photoactive compound; and (3) irradiating the photoactive compound, wherein a photochemical reaction between the photoactive compound and the molecule results in covalent links between the molecule and the photoactive compound to immobilize the molecule near the surface. In certain embodiments, the photoactive compound can be immobilized on the surface as a self-assembled monolayer (see
In other some embodiments, methods of the invention can include (1) immobilizing on a surface a composition that includes a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation and a second compound that can increase the affinity of desired molecules to the composition; (2) applying a molecule to the composition; and (3) irradiating the composition, wherein a photochemical reaction between the photoactive compound and the molecule results in covalent links between the molecule and the photoactive compound to immobilize the molecule near the surface. In certain embodiments, the composition can be immobilized on the surface as a self-assembled monolayer. In other embodiments, the photoactive compound can be immobilized on the surface as a multilayer.
In some embodiments, the molecule that forms covalent links with the photoactive compound can be a carbohydrate.
The invention also provides methods for immobilizing a patterned array of molecules on a surface. A mask containing the desired pattern or image can be placed over the coated surface and irradiated through the mask. Alternatively, a robotic spotter can be utilized to pattern areas containing a photoactive compound and a molecule, and the patterned array can be irradiated. Other suitable methods to form a patterned array of immobilized carbohydrates will be readily apparent to one of ordinary skill in the art.
The photoactive compound and/or the immobilized molecule can be formed as a coating on a surface, and at various thicknesses. For example, the molecule may form a coating with a thickness of less than 1 nm, 2 nm, 5 nm, 10 nm, 20 nm, 50 nm, 100 nm and the like. For example, if a monolayer of immobilized molecule is formed on the surface, the thickness can depend on the molecular weight of the molecule. In some embodiments, the molecule may be applied to the surface by spin coating, spray coating, or any other conventional techniques known in the art to obtain a uniform coating.
In some embodiments, the photoactive compound can further include a functional group capable of being immobilized on a surface. Some examples of functional group capable of being immobilized on a surface include a carboxylic acid, thiol, β-diketone, silane, phosphate, phosphonate, alkane, alkene, or alkyne, polymer, block copolymer, and the like. In some other embodiments, the photoactive compound can be incorporated into polymers and/or hydrogels to modify the molecule-surface interfacial tension or to modify steric constraints that may make the photoactive portion of the molecule inaccessible.
Any suitable molecules can be utilized. Carbohydrates, polymers, lipids, proteins, and the like can be utilized. For example, carbohydrates, such as monosaccharides, disaccharides, trisaccharides, tetrasaccharides, oligosaccharides, polysaccharides, glycosides thereof, and the like, can be utilized in the invention. In some embodiments, the carbohydrate can be a simple carbohydrate, such as glucose or sucrose. In other embodiments, a 2000 kDA dextran can be utilized. In some other embodiments, the carbohydrates can be underivatized carbohydrates, without chemical modification. As another example, suitable polymers can include polyacrylic acid, polystyrene, polyvinyl alcohol, and the like. Other exemplary molecules that can be immobilized on a surface will be readily apparent to one of ordinary skill in the art.
The invention does not require the chemical modification of each molecule prior to deposition and it is not dependent on the molecular weight of the deposited molecule. Moreover, the invention can utilize bonds, such as C—H bonds, S—H bonds, Si—H bonds, and the like, which is present in many molecules (e.g., C—H bonds are readily found in carbohydrates). Moreover, the invention requires no reagents and generates no byproducts.
The invention has applications in a wide number of applications. For example, the invention can be utilized in tissue engineering, sensor fabrication, glycome sequencing, and in microarray construction for high-throughput characterization of carbohydrate enzyme activity and carbohydrate interactions with cells, antibodies, proteins and microorganisms.
Moreover, the surfaces may be used as biological sensors for identifying biological warfare agents. The invention also provides a platform for screening antibody activity towards various viruses, photopatterning any kind of polymer, biological or synthetic, that contains a C—H bond, and glycomic and proteomic studies aimed at the discovery of new drugs and the understanding of cellular processes.
The invention can also be utilized as immobilized coatings that impart desired functionality to a surface. For example, hydrophilic molecules can be immobilized on the surface of an optically transparent substrate to provide an anti-fogging substrate. An another example, hydrophobic molecules can be immobilized on the surface of a substrate to provide a surface that strongly repels water (e.g., to coat automobile windshield to repel rain water).
In some embodiments, arrays having the photoactive compounds of the invention immobilized on a surface can be utilized to covalently attach numerous molecules, such as DNA, RNA, proteins, polymers, carbohydrates, and the like to the photoactive compounds for applications described herein.
In addition, a patterned array of molecules can be utilized as a template for carrying out further reactions selectively in desired areas of the patterned surface.
Depositing Metals on a Surface
Other embodiments of the invention also relate to methods for depositing metals on a surface. Methods of the invention can include (1) immobilizing on a surface a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation; (2) applying a molecule to the photoactive compound; (3) irradiating the photoactive compound, wherein a photochemical reaction between the photoactive compound and the molecule results in covalent links between the molecules and the photoactive compound to immobilize the molecule near the surface; (4) contacting the surface having immobilized molecules with a catalyst for forming a metal, where the catalyst has a selective affinity for the immobilized molecules; and (5) carrying out a metal reducing reaction to deposit metal near the immobilized molecules. In certain embodiments, the photoactive compound can be immobilized on the surface as a self-assembled monolayer. In other embodiments, the photoactive compound can be immobilized on the surface as a multilayer.
In some other embodiments, methods of the invention can include (1) immobilizing on a surface a composition that includes a photoactive compound capable of forming covalent bonds with nearby molecules after irradiation and a second compound that can increase the affinity of desired molecules to the composition; (2) applying a molecule to the composition; (3) irradiating the composition, wherein a photochemical reaction between the photoactive compound and the molecule results in covalent links between the molecule and the photoactive compound to immobilize the molecule near the surface; (4) contacting the surface having immobilized molecules with a catalyst for forming a metal, where the catalyst has a selective affinity for the immobilized molecules; and (5) carrying out a metal reducing reaction to deposit metal near the immobilized molecules. In certain embodiments, the photoactive compound can be immobilized on the surface as a self-assembled monolayer. In other embodiments, the photoactive compound can be immobilized on the surface as a multilayer.
In some embodiments, a mask containing the desired pattern or image can be placed over the surface and irradiated though the mask. Alternatively, a robotic spotter can be utilized to pattern areas containing a photoactive compound and a molecule, and the patterned array can be irradiated. Other suitable methods to form a patterned array of immobilized carbohydrates will be readily apparent to one of ordinary skill in the art.
The photoactive compound and/or the immobilized molecule can be formed as a coating on a surface, and at various thicknesses. For example, the molecule may form a coating with a thickness of less than 1 nm, 2 nm, 5 nm, 10 nm, 20 nm, 50 nm, 100 nm and the like. For example, if a monolayer of immobilized molecule is formed on the surface, the thickness can depend on the molecular weight of the molecule. In some embodiments, the molecule may be applied to the surface by spin coating, spray coating, or any other conventional techniques known in the art to obtain a uniform coating.
In some embodiments, the photoactive compound can further include a functional group capable of being immobilized on a surface. Some examples of functional group capable of being immobilized on a surface include a carboxylic acid, thiol, β-diketone, silane, phosphate, phosphonate, alkane, alkene, or alkyne, polymer, block copolymer, and the like. In some other embodiments, the photoactive compound can be incorporated into polymers and/or hydrogels to modify the carbohydrate-surface interfacial tension or to modify steric constraints that may make the photoactive portion of the molecule inaccessible.
Any suitable molecules can be utilized. Carbohydrates, polymers, lipids, proteins, and the like can be utilized. Suitable polymers can include polyacrylic acid, polystyrene, polyvinyl alcohol, and the like. Other exemplary molecules than can be immobilized on a surface will be readily apparent to one of ordinary skill in the art.
Any suitable metals can be deposited on the surface with the use of appropriate catalysts. For example, nickel, copper, gold, silver, titanium, aluminum, silicon, and the like can be deposited. The invention has significant advantages over conventional techniques, such as electroplating, as expensive and potentially dangerous reaction conditions can be avoided.
Although the invention was described in reference to deposition of metals, other non-metals, such as insulator, semiconductors, organic molecules, polymers, and the like can be deposited, as will be readily apparent to one of ordinary skill in the art.
The invention will be further described with reference to the following examples; however, it is to be understood that the invention is not limited to such examples. Rather, in view of the present disclosure that describes the current best mode for practicing the invention, many modifications and variations would present themselves to those of skill in the art without departing from the scope and spirit of this invention. All changes, modifications, and variations coming within the meaning and range of equivalency of the claims are to be considered within their scope.
To a solution of 6.7 g (0.03 mol) of 3-benzoylbenzoic acid (Aldrich) in 250 ml of methylene chloride and 50 ml of ether in a 500 ml three necked round bottom flask which was equipped with a reflux condenser and sealed with argon was added 0.4 g (0.003 mol) of 4-pyrrolidinopyridine (Aldrich), and 6.1 g (0.03 mol) of DCC (Acros). The solution was stirred for 5 min. 0.93 g (0.015 mol) of ethylene glycol was added. The reaction mixture was stirred overnight and then refluxed for 5 hours to complete the esterification. After cooling to room temperature, the N, N-dicyclohexyl urea was removed by filtration. The filtrate was washed with water (3×100 ml), 5% acetic acid solution (3×100 ml), water (2×100 ml), and NaCl saturated water (100 ml). The solution was dried with anhydrous Na2SO4. After removing the solvent on a rotoevaporator, the product was chromatographed on silica gel with ethyl acetate/hexane (v/v=1/3). 6.5 g of Compound 1 was obtained (90% yield).
Halogenation.
Addition of a halogen with a Lewis acid allows for halogenation of the aromatic rings in the meta positions. The halogen can then be replaced by a molecule bearing a nucleophile.
Alkylation Using an Alkene.
Addition of an alkene with a Bronsted or Lewis acid results in substitution in the meta positions.
Alkylation Using an Alcohol.
Addition of an alcohol with a Bronsted or Lewis acid results in substitution in the meta positions.
Additionally, benzophenone derivatives bearing substituents that are amenable to derivatization (methoxy, alcohol, etc.) can be used to make the derivative compound of Compound 1.
150 ml of DMF was added to a flask containing 1.056 g of potassium phthalimides. 0.7145 g of dibromohexane was added. The solution was stirred overnight at 20° C. 75 ml of chloroform were added to the solution followed by 50 ml H2O. The organic layer was separated and extracted with 50 ml of chloroform two times. The combined organic layers were rinsed with 75 ml of H2O four times. Chloroform was removed under reduced pressure. A clear liquid removed. White needles of Compound 2 precipitated from the liquid after 12 hours. The product of was collected by filtration and washed with ether.
9.8 mmol of 11-bromoundecanetrimethoxysilane (Gelest) was added to a solution of an equimolar amount of potassium phthalimides (Aldrich) in 40 ml of anhydrous DMF (Aldrich) (see also
Polymer films were prepared on Silicon wafers (Wafer World) by spin-coating toluene solutions containing varying amounts of polystyrene (PS) and Compound 1 (see
The films were placed in sealed glass vials and purged with argon for 10 minutes. The films were irradiated for 1 hour with a Rayonet Photochemical Reactor equipped with lamps that emit at 350 nm.
The irradiated PS films were examined by infrared (IR) spectroscopy and gel permeation chromatography (GPC). Hydrogen abstraction is expected to occur at the aromatic ketone as schematically illustrate in
To further verify that PS can be photochemically cross-linked by photoexcitation of Compound 1 in a PS matrix, samples containing Compound 1 and PS (Mn=2600) were analyzed by GPC. It should be noted that GPC can qualitatively demonstrate the occurrence of cross-linking Analysis of the GPC curves shown in
To examine the effect of crosslinking on the dewetting behavior of PS, samples having 29:1 ratio of Compound 1:PS and without any Compound 1 were heated to about 170° C. (Tg is about 100° C.).
Additional films were cast containing intermediate concentrations of Compound 1 relative to the 29:1 and 0:1 Compound 1:PS samples described above.
Additionally, the dosage of UV light was adjusted.
Additionally, 25 nm films having ratios of 3:1 and 0:1 Compound 1:PS were spun cast on silicon wafers, irradiated for 1 hour, and annealed at 170° C. overnight.
7 nm films having 17:1 and 0:1 ratios of Compound 1:PS were also spun cast on silicon wafers, irradiated for 1 hour, and annealed at 170° C. overnight.
Dewetting Upon Exposure to Solvent Vapors
Dewetting of polymer films upon exposure to solvent vapors were also studied. The 7 nm and 25 nm PS films with and without Compound 1 were placed in a flask of saturated toluene vapor at room temperature. The resulting OM images are shown in
For the 25 nm films, the inhibition of dewetting is more pronounced.
Dewetting-Resistant PS Films on Other Surfaces
Films of PMMA were prepared on silicon, followed by deposition of a PS film containing Compound 1 (1:17 ratio of PS:Compound 1) on top of the PMMA film.
100 nm gold film was also formed on silicon, followed by deposition of a PS film containing Compound 1 in the sample on top of the gold film.
Irradiation Through a Photomask
Additionally, irradiation was carried out using a photomask. As shown in the OM images of
In order to pattern PS dewetting morphologies on a surface, a 30 nm thick PS film containing Compound 1 was irradiated through a photomask having Columbia University's crown logo. The film was then heated in a vacuum oven at 170° C. for 5 hours. The resulting pattern is shown in
Another feature of interest is the preference for droplet formation on the larger masked areas. Both the base of the crown and the middle bar show a more regular presentation of droplets as opposed to the thinner regions of the pattern.
Microchannels of varying widths were also patterned. Irradiating and heating this sample as above resulted in the pattern shown in
Another feature of interest is the height of the matter that collects at the wall of the channel. The effect of the channel width on the height of the channel walls is illustrated in the graph in
An interesting characteristic of thin polymer films is the change in properties with a change in size. For example, it has been suggested that the mechanism by which dewetting occurs is dependent on the thickness of the film. For films of less than 10 nm, spinodal dewetting has been attributed to the rupture of the film whereas films greater than 10 nm are said to dewet by nucleation onto defect sites. The effect of film thickness on the confined dewetting behavior was examined.
In order to visualize the edge of the pattern we obtained AFM images of the surface.
The crosslinked polymer can act as a microvessel/microvial that confines the uncrosslinked polymer to a defined space. Heating such a system above Tg results in the formation of smaller patterns within the larger pattern. The structures of the smaller patterns can be controlled by changing the size of the larger pattern.
In order to create a novel surface suitable for immobilizing carbohydrates, Compound 4 was self-assembled on, glass (Arraylt), silicon (Wafer World) and quartz (SPI) in anhydrous toluene to produce SAM 4 as follows (see
The self-assembly of Compound 4 on the surface was verified by the UV/Vis spectroscopy.
In order to test the ability of surface bound phthalimides to photochemically immobilize sugars, FITC-conjugated polysaccharide films were spin-coated onto SAM 4 and irradiated with a medium pressure mercury lamp in an inert environment (dashed line). The fluorescein isothiocyanate (FITC)-conjugated α(1,6)dextrans weighing 20 kD or 2000 kD (Dextran-FITC) (Sigma) were spin-coated from a 10 mg/ml aqueous solution at 3000 RPM for 90 seconds and placed in argon purged quartz tubes. Irradiation was carried out with a Rayonet Photochemical Reactor equipped with lamps that emit at 300 nm. For ellipsometry and fluorescence experiments, the surface was rinsed by placing in H2O for 12 hours followed by rinsing with methanol. Substrates were blown dry with argon.
Two controls were also prepared similarly as described above. In the first, polysaccharides were spin-coated onto SAM 4 and left in the dark (dotted line). In the second, polysaccharides were spin-coated onto an underivatized silicon wafer (straight line). All three samples were placed in water filled vials for twelve hours. After removing the samples and rinsing with water and methanol followed by blow-drying with argon, the fluorescence spectra of each sample were obtained as shown in
The film thicknesses of the three samples were measured using a Beaglehole ellipsometer in variable angle mode. A refractive index value of 1.5 was used for the organic layer. As shown in Table 1, the irradiated sample retains 7.1±0.3 nm of material after the rinse. The thickness of the material on the SAM kept in the dark was 0.7±0.3 nm and the thickness on the underivatized silicon wafer was 0.4±0.3 nm. The reported thicknesses do not include the thickness of the SAM (1.2 nm). The surfaces were further investigated with water contact angle measurements. The hydrophilic nature of the sugars reduced the water contact angle from 65±1° to 28±1° on the irradiated SAM. Inefficient immobilization on the dark control is evident from a post-rinse contact angle of 62±1°. The higher retention of material on the irradiated SAM demonstrates that self-assembled phthalimide monolayers are capable of photochemically bonding to an overlayer carbohydrate film despite any spatial restrictions on the chromophore as a result of placement in a constrained environment. We speculate that the nature of the bonding is covalent and results from radical-radical combination following hydrogen abstraction.
The above experiments were also performed on self-assembled monolayers having benzophenone chromophores, another class of aromatic carbonyls that can photochemically abstract hydrogen from C—H groups and have been shown to graft polymers to surfaces. The resulting carbohydrate film thickness and fluorescence intensity were lower and the contact angle was higher than the films on SAM 4. Without wishing to be bound by theory, the lower performance may be due to the radical center in the benzophenone SAM occurring further from the surface than in the phthalimides, self-quenching of the excited state or a higher interfacial tension between the more hydrophobic benzophenone monolayer and the carbohydrate film in comparison to the phthalimide-carbohydrate interaction. Benzophenone SAMs have more hydrophobic character than SAM 4 (phthalimide SAM) as evidenced by a higher water contact angle of about 85°. Preliminary experiments with a microarray spotter have shown that hydrophilic surfaces are more easily spotted than hydrophobic surfaces. In any case, other photoactive carbonyl groups capable of abstracting hydrogen atoms can be substituted and may enhance or retard the reaction due to the efficiency of self-assembly, steric and energetic constraints.
In addition to covalently attaching underivatized sugars to a surface, patterns of grafted sugars were also generated, which is schematically shown in
Patterns were visualized by condensing water onto the pattern and imaging with a Nikon Eclipse optical microscope equipped with an INSIGHT digital camera. Two methods were used to condense water onto the surface. In the first, the surface was exposed to an extended breath. In the second, the surface was held over boiling water.
As described above, other studies suggested that the immobilization efficiency decreases with the decreasing molecular weight of the carbohydrate. In order to show the versatility of the invention, glucose and sucrose, two simple sugars at the extreme of low molecular weight containing both six and five member carbohydrate moieties, were tested. The resulting water condensation images are presented in
As shown, the invention requires no chemical modification of the sugars prior to deposition. Further, because covalent attachment is involved, sugars of all molecular weights can be immobilized, whereas sugars of lower molecular weights were more prone to be washed away in the conventional art. The photochemical nature of the technique allows simple arrays to be created without a robot and makes the method adaptable to the full potential of photolithography, which is currently used in industry for the high-throughput fabrication of computer chips and nanoscale patterning. Multiple carbohydrate patterns can be immobilized by repeating the reaction with a different carbohydrate in a previously masked region. In conjunction with a microarray spotter, large libraries of carbohydrates can be immobilized on surfaces. The versatility and ease of the method provides an opportunity for biologists, chemists and engineers to investigate and create new biological materials.
Instrumental Measurements
UV-vis spectra were obtained using a Shimadzu (UV-2401PC) UV-vis recording spectrophotometer. Contact angle measurements were performed with a Rame-Hart 100-00 contact angle goniometer using Millipore Milli-Q water. At least three droplets were measured on each sample and averaged. Thicknesses were measured with a Beaglehole ellipsometer in variable angle mode. A refractive index of 1.5 was used for all samples. Measurements were performed three times in different locations on the surface and averaged. Fluorescence spectra were obtained using a Jobin Yvon Fluorolog 3 spectrofluorimeter in front face mode. The surface was placed at an angle of 20° to a line parallel to the plane of the detector.
As schematically shown in
Microarrays were robotically prepared as follows. Antigen preparations were dissolved in saline (0.9% NaCl) at a given concentration and were spotted as triplet replicate spots in parallel. The initial amount of antigen spotted was 0.35 ng per spot and diluted by serial dilutions of 1:5 thereafter (See also microarray images inserted in
After microarray spotting, the SAM 4A slides were air-dried and placed in a quartz tube. The sealed tube was subsequently purged with argon or nitrogen before irradiation. UV irradiation was conducted by placing the quartz tube under a desktop lamp containing a 300 nm Rayonet bulb for one hour. Precaution was made to avoid skin and eye contact with the radiation during the irradiation process.
Then, the printed microarrays were rinsed and washed with PBS (PH 7.4) and with 0.05% Tween 25 times with five minutes of incubation in each washing step. They were then “blocked” by incubating the slides in 1% BSA in PBS containing 0.05% NaN3 at room temperature (RT) for 30 minutes. Antibody staining was conducted at RT for one hour at given dilutions in 1% BSA PBS containing 0.05% NaN3 and 0.05% Tween 20. Determination of immobilized polysaccharides on the surface after irradiation and extensive washing was performed by staining the arrays using a biotinylated anti-α(1,6)dextran monoclonal antibody, 16.4.12E. This antibody is specific for the terminal non-reducing end epitopes displayed by all three dextran-conjugates immobilized on the surface. Since a biotinylated anti-dextran antibody (mAb 16. 4.12E) was applied in this study, streptavidin-Cy3 conjugate (Amersham Pharmasia) with wavelengths of excitation and emission at 552 and 570 nm, respectively, was applied to reveal the bound anti-dextran antibodies. The stained slides were rinsed five times with PBS and with 0.05% Tween 20 after each staining step. A ScanArray 5000A Standard Biochip Scanning System (PerkinElmer, Torrance, Calif.) equipped with multiple lasers, emission filters and ScanArray Acquisition Software was used to scan the microarray. Fluorescence intensity values for each array spot and its background were calculated using ScanArray Express (PerkinElmer, Torrance, Calif.). A nitrocellulose substrate (FAST), an established platform, was similarly treated to provide a comparative data.
The results illustrated in
A panel of mono- and oligosaccharide arrays on SAM 4A and FAST slides were also studied. The spotted arrays were probed with a biotinylated lectin ConA (see
Mixed monolayers were formed from a solution containing a 20:1 ratio of aminopropyltrimethoxy silane to Compound 4 (SAM 4B). The 20:1 ratio of aminopropyltrimethoxy silane to Compound 4 was mixed in a vial containing anhydrous toluene. A microscope slide was placed in a vial, sealed, and purged with argon. The prepared solution was added into the sealed vial via a syringe and allowed to react overnight. The slide was then removed and rinsed as described above. As shown in
A FAST slide and a SAM 4B slide were spotted with a panel of carbohydrates (38 total) and protein/peptide (8) preparations, as shown in
As shown in
In addition to immobilization of various carbohydrates, variety of polymers were also immobilized and patterned on a surface. PS, poly(tert-butyl acrylate) (PTBA), and poly(vinyl alcohol) PVA were immobilized and patterned on SAM 4. The OM images of the immobilized PVA, PTBA, and PS patterns are shown in
To test for the robustness of the immobilized films, surfaces with PVA were irradiated for various time periods to obtain different thicknesses. The surfaces immobilized with PVA were rinsed in hot water after irradiation. The immobilized surfaces were placed in a vial of deionized water and heated to 75° C. for 15 minutes and to 90° C. for 2.5 hours. The deionized water was changed and the surface was rinsed with deionized water. Surfaces were then placed back into a heated water (about 95° C.) for additional three hours.
Moreover, electroless deposition of nickel was carried out to selectively deposit nickel on regions immobilized with polyacrylic acid (PAA). A glass surface was coated with SAM 4 and PAA (35 wt % in water) was spin-coated onto SAM 4 as described above. Then, the sample was irradiated through a photomask having lines of varying widths for about 4 to 5 hours. The sample was then rinsed with water and immersed in a aqueous catalyst solution containing 5 mM palladium tetraammonium dichloride for about 30 seconds. The sample was then removed and placed in deionized water for about 30 seconds to rinse off any catalyst that are not on the regions coated with PAA. The sample was then placed in a nickel bath for 15 minutes. The nickel bath contained 4 g of nickel sulfate, 2 g sodium citrate, 1 g of lactic acid, 0.2 g of dimethyl amine borane, and 100 mL of deionized water. The pH of the nickel bath was adjusted to 6.8±0.2 using ammonium hydroxide.
As various changes can be made without departing from the scope and spirit of the invention as described, it is intended that all subject matter contained in the above description, shown in the accompanying drawings, or defined in the appended claims be interpreted as illustrative, and not in a limiting sense.
The present application is a divisional of U.S. patent application Ser. No. 13/416,968, filed Mar. 9, 2012, as a continuation of U.S. patent application Ser. No. 11/595,292, filed Nov. 9, 2006 and issued as U.S. Pat. No. 8,158,832, which claims the benefit of the filing dates of U.S. Provisional Application No. 60/735,402, filed on Nov. 9, 2005, and U.S. Provisional Application No. 60/776,096, filed on Feb. 23, 2006, both of which are incorporated by reference herein in their entireties.
Work described herein may have been supported by, or in part by, U.S. Army Research Laboratory and the U.S. Army Research Office under contract/grant number DA W911NF-04-1-0282 and in part by the National Science Foundation under grant numbers DMR-02-14263, IGERT-02-21589, CHE-04-15516, and RF CUNY #404340001A. The U.S. Government may have certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5120569 | Zupancic et al. | Jun 1992 | A |
| 5370974 | Agostino et al. | Dec 1994 | A |
| 6080589 | Kandil et al. | Jun 2000 | A |
| 6329209 | Wagner et al. | Dec 2001 | B1 |
| 6355491 | Zhou et al. | Mar 2002 | B1 |
| 6368838 | Singhvi et al. | Apr 2002 | B1 |
| 6828110 | Lee et al. | Dec 2004 | B2 |
| 8158832 | Carroll et al. | Apr 2012 | B2 |
| 8957225 | Carroll et al. | Feb 2015 | B2 |
| 20020064556 | Cheng et al. | May 2002 | A1 |
| 20030078314 | Johnson et al. | Apr 2003 | A1 |
| 20030215801 | Pieken et al. | Nov 2003 | A1 |
| 20030228637 | Wang | Dec 2003 | A1 |
| 20040025268 | Porat et al. | Feb 2004 | A1 |
| 20040033546 | Wang | Feb 2004 | A1 |
| 20040106886 | Verdonk et al. | Jun 2004 | A1 |
| 20040249186 | Balzer et al. | Dec 2004 | A1 |
| 20040253634 | Wang | Dec 2004 | A1 |
| 20050011229 | Lisec | Jan 2005 | A1 |
| 20050032081 | Ju et al. | Feb 2005 | A1 |
| 20050080213 | Meyer et al. | Apr 2005 | A1 |
| 20050112292 | Parker et al. | May 2005 | A1 |
| 20070020620 | Finn et al. | Jan 2007 | A1 |
| 20100099580 | Carroll et al. | Apr 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| WO-02064556 | Aug 2002 | WO |
| WO-2004025268 | Mar 2004 | WO |
| WO-2004106886 | Dec 2004 | WO |
| WO-2006064505 | Jun 2006 | WO |
| WO-2008054398 | May 2008 | WO |
| Entry |
|---|
| U.S. Appl. No. 02/064,556, filed Aug. 22, 2002, Dukler et al. |
| Adamo, R. et al., “Synthesis of the β anomer of the spacer-equipped tetrasaccaride side chain of the major glycoprotein of the Bacillus anthracis exoporium,” Carbohydrate Research, vol. 340, pp. 2579-2582 (2005). |
| Adams, E. W. et al., “Oligosaccharide and glycoprotein microarrays as tools in HIV glycobiology: Glycan-dependent gp120/protein interactions,” Chemistry & Biology, vol. 11(6), pp. 875-881 (2004). |
| Allen, C. F. H. et al., “Use of Potassium Phthalimide for Identification of Alkylene Bis Halides and Bis Sulfonates,” Analytical Chemistry, vol. 44, No. 9, Aug. 1972, 1694-1696. |
| Andrew et al., “Photopolymerization via the paterno-Buechi reaction. II. reaction of aromatic diketones with furans,” Journal of polymer Science, Polymer Chemistry Edition, Interscience publishers, New York, NY, vol. 14, pp. 331-341 (1976). |
| Angeloni, S. et al. “Glycoprofiling with micro-arrays of glycoconjugates and lectins.” Glycobiology, 15:31-41. (2005). |
| Baek, S. “Selectivity Studies on Anion-Selective Membrane Electrodes,” Analytical Chemistry, vol. 44, No. 9, Aug. 1972. |
| Becker et al., “Ions derives from dianthrylethane species. How to mode of linking affects the intramolecular electron transfer,” Journal of the American chemical society, vol. 113, pp. 1121-1127 (Feb. 1991). |
| Blawas, A. S. & Reichert, W. M., “Review: Protein patterning,” Biomaterials, vol. 19, pp. 595-609 (1998). |
| Blixt, O. et al. “Printed covalent glycan array for ligand profiling of diverse glycan binding proteins.” PNAS USA, 101(49):17033-17038. (2004). |
| Borman, Stu, “Antibody Could Lead to Anthrax Test.” Chemical & Engineering News. (Aug. 23, 2006). |
| Boydston, et al., “Orientation within the Exoporium and Structural Stability of the Collagen-Like Glycoprotein BcIA of Bacillus anthracis,” J Bacteriol., vol. 187, pp. 5310-5317 (2005). |
| Brun, M. A. et al., “Miniturization of microwave-assisted carbohydratefunctionalization to create oligosaccharide microarrays,” ChemBioChem, vol. 7, pp. 421-424 (2006). |
| Bryan, M. C. et al. “High-throughput identification of fucosyltransferase inhibitors using carbohydrate microarrays.” Bioorg. Med. Chem. Lett., 14:3185-3188. (2004). |
| Calarese, G. T. et al., “Dissection of the carbohydratespecifically of the broadly neutralizing anti-HIV-1 antibody 2G12,” PNAS, vol. 102, pp. 13372-13377 (Sep. 2005). |
| Carroll et al., “Photo-Generation of Carbohydrate MicroArrays, ” in MicroArrays, Preparation, Microfluidics, Detection Methods and Biological Applications, Dill, K. et al, Eds., Springer, New York, Ch. 9, pp. 191-210, (2009). |
| Carroll, Gregory et al. “Photochemical Micropatterning of Carbohydrates on a Surface.” Langmuir, 22:2899-2905. (2006). |
| Carroll, Gregory T. et al. “Photoactive Additives for Cross-Linking Polymer Films: Inhibition of Dewetting in Thin Polymer Films.” Langmuir, 22:7748-7754. (2006). |
| Carroll, Gregory T. et al. “Photochemical Micropatterning of Carbohydrates on a Surface.” Langmuir. (2006). |
| Charych, D. et al., “A ‘litmus test’ for molecular recognition using artificial membranes,” Chemistry & Biology, vol. 3, pp. 113-120 (1996). |
| Charych, D. H. et al., “Direct colorimetric detection of a receptor-ligand interaction by a polymerized bilayer assembly,” Science, vol. 261(5121), pp. 585-588 (1993). |
| Chee, M. et al., “Accessing genetic information with high-density DNA arrays,” Science, vol. 274(5287), pp. 610-614 (1996). |
| Chen, C. S. et al. “Geometric control of cell life and death.” Science, 276:1425-1428. (1997). |
| Choi, “Glycomic researches search for the elusive sweet spot. Carbohydrate array development continues, but sample variety remains limited,” The Scientist, pp. 30-31 (Mar. 28, 2005). |
| Ciccotosto, S. et al., “Synthesis and evaluation of N-acetylneuraminic acid-based affinity matrices for the purification of sialic acid-recognizing proteins,” Glycoconjugate Journal, vol. 15, pp. 663-669 (1998). |
| Cisar, J. et al., “Binding properties of immunogobulin combining sites specific for terminal or nonterminal antigenic determinants in dextran,” J. Exp. Med., vol. 142, pp. 435-459 (1975). |
| Cohen, S. et al., “Attenuated Nontoxinogenic and Nonencapsulated Recombinant Bacillus anthracis Spore Vaccines Protect against Anthrax,” Infect. Immun., vol. 68, pp. 4549-4558 (2000). |
| Constans, Aileen, “High-Carb Science with Sugarcoated Arrays.” The Scientist, p. 33. (Nov. 8, 2004). |
| International Search Report and Written Opinion issued for corresponding International Patent Application No. PCT/US2006/043614. |
| Database Beilstein, Beilstein Institute for Organic Chemistry, Frankfurt, Chemische Berichte, vol. 62, pp. 1410 (1929). |
| Database Beilstein, Beilstein Institute for Organic Chemistry, Chemische Berichte, vol. 122, pp. 2291-2298 (1989). |
| Database Beilstein, Beilstein Institute for organic Chemistry, Frankfurt, JACS, vol. 74, pp. 1621 (1952). |
| Database Beilstein, Beilstein Institute for Organic Chemistry, Journal fur praktische Chemi, vol. 319, pp. 589-600 (1977). |
| Daubenspeck, et al., “Novel Oligosaccharide Side Chains of the Collagen-like Region of BcIA, the Major Glycoprotein of the Bacillus anthracis,” J. Biol. Chem., vol. 279, pp. 30945-30953 (2004). |
| Davaraj, et al., “Chemoselective covalent coupling of oligonucleotide probes to self-assembled monolayers,” J. Am. Chem. Soc., vol. 127, pp. 8600-8601 (Jun. 22, 2005). |
| De Smet et al. “Covalently attached saccharides on silicon surfaces.” J. Am. Chem. Soc., 125:13916-13917. (2003). |
| Disney, Matthew D. and Peter H. Seeberger, “The use of carbohydrate microarrays to study carbohydrate-cell interactions and to detect pathogens.” Chem. Biol., 11:1701-1707. (2004). |
| Extended Search Report mailed on Jul. 26, 2010 for European patent Application No. 06851911.5 filed Nov. 9, 2006. |
| Fang, Y. et al., “Ganglioside microarrays for toxin detection,” Langmuir, vol. 19, pp. 1500-1505 (2003). |
| Fazio, F. et al. “Synthesis of Sugar Arrays in Microtiter Plate.” J. Am. Chem. Soc., 124:14397-14402. (2002). |
| Feizi, T. et al., “Oligosaccharide microarrays to decipher the glyco code,” Nature Reviews, vol. 5, pp. 582-588 (2004). |
| Fodor, S. P. A. et al. “Light-directed, spatially addressable parallel chemical synthesis.” Science, 251:767-773. (1991). |
| Fodor, S. P. A. et al., “Multiplexed biochemical assays with biological chips,” Nature, vol. 264, pp. 555-556 (1993). |
| Fodor, Stephen P. et al. “Light-Directed, Spatially Addressable Parallel Chemical Synthesis.” Science, 251:767-773. (Feb. 15, 1991). |
| Fuerstner et al., High-surface sodium as a reducing agent for TiCI3<′ Synthesis, Georg Thieme Verlag, Stuttgart, pp. 63-68 (Jan. 1995). |
| Fuerstner et al., “Syntheses, structures, and complexation properties of photoresponsive crownophanes,” Liebigs annalen: Organic and Bioorganic Chemistry, VCH Publisher, pp. 655-662 (May 1, 1996). |
| Fuerstner, A. et al., “Carbonyl Coupling Reactions Catalytic in Titanium and the Use of Commercial Titanium Powder for Organic Synthesis,” Journal of the American Chemical Society, vol. 117(16), pp. 4468-4475, (1995). |
| Fukui, S. et al. “Oligosaccharide microarrays for high-throughput detection and specificity assignments of carbohydrate-protein interactions.” Nature Biotechnol., 20:1011-1017. (2002). |
| Fuson, R. C. et al., “1, 6-Reductive coupling of hindered o-vinyl diaryl ketones,” Journal of Organic Chemistry, vol. 26, pp. 1042-1044, (1961). |
| Gan, D. et al., “Thin-Film Morphologies of Random Copolymers as Functions of Thermal History,” Journal of Colloid and Interface Science 239, 272-277 (2001). |
| Giannasca, K. T. et al., “Adherence of Salmonella typhimurium to Caco-2 cells: Identification of a glycoconjugate receptor,” Infection and Immunity, vol. 64(1), pp. 135-145 (1996). |
| Gruetzmacher, H. F. et al., “[3.2] Paracyclophane-10-enes and [3.2.3.2] paracyclophane-10, 27-dienes: a convenient synthesis by the McMurry reaction and dynamic stereochemistry,” Chemische Berichte, vol. 122(12), pp. 2291-2297, (1989). |
| Havens, C. B. et al., “Diesters of aliphatic dicarboxylic acids and hydroxybenzophenones for stabilizing haloethylene polymers,” (1960). |
| Heid, Stephen, et al., Self-Assembled Mono- and Multilayers of Terminally Functionalized Organosilyl Comounds on Silicon Subtrates, Langmuir, vol. 12, pp. 2118-2120 (1996). |
| Heidelberger, M. et al., Cross-reactions of the group-specific polysaccariddes of streptococcal groups B and G in anti-pneumococcal sera with especial references to type XXIII and its determinants, J. Immunology, vol. 99, pp. 794-796 (1967). |
| Heidelberger, M., “Cross-reactions of glucose-containing polysaccharides in antipneumococcal sera,” J. Immunology, vol. 91, pp. 735-739 (1963). |
| Heller et al., “DNA microarrat technology: Devices, systems and applications,” Annual Reviews in BioMedical Engineering, vol. 4, pp. 129-153 (2005). |
| Horan, N. et al., “Nonstatistical binding of a protein to clustered carbohydrates,” Proceedings of the National Academy of Sciences of the United States of America, vol. 96(21), pp. 11782-11786 (1999). |
| Houseman, B. T. et al., “Carbohydrate arrays for the evaluation of protein binding and enzymatic modification,” Chemistry & Biology, vol. 9, pp. 443-454 (2002). |
| Houseman, B. T. et al., “Maleimide-functionalized self-assembled monolayers for the preparation of peptide and carbohydrate biochips,” Langmuir, vol. 19(5), pp. 1522-1531 (2003). |
| Huang, et al., “Prostate-specific antigen immunosensing based on mixed self-assembled monolayers, camel antibodies and colloidal gold enhanced sandwich assays,” Biosensors and Bioelectronics, vol. 21, pp. 483-490 (2005). |
| Husemann, M. et al., “Manipulation of Surface Properties by Patterning of Covalently Bound Polymer Brushes.” J. Am. Chem. Soc 122, 1844-1845. (2000). |
| Iqbal, et al., “A review of molecular recognition technologies for detection of biological threat agents,” Biosensors & Bioelectronics, vol. 15, pp. 549-578 (2000). |
| Ito et al., “Photochemistry of bichromophoric aromatic diketones: the effect of methylene chain,” Journal of Organic Chemistry, American Chemical society, Eaton, vol. 54, pp. 506-509 (Jan. 1989). |
| Jelinek, R. and S. Kolusheva, “Carbohydrate Biosensors.” Chem. Rev., 104:5987-6015. (2004). |
| Kanaoka, Y. “Photoreactions of cyclic imides. Examples of synthetic organic photochemistry.” Acc. Chem. Res., 11:407-413. (1978). |
| Kempter, G. et al., “Heterocycles from 2-amino ketones. XXIII. Reaction of o-amino ketones with dicarboxylic acids,” Journal fuer Praktische Chemie (Leipzig), vol. 319(4), pp. 589-600, (1977). |
| Kobayashi, K. et al., “Glycopeptide derived from hen egg ovomucin has the ability to bind enterohemorrahgic Escherichia coli O157:H7,” Journal of Agricultural and Food Chemistry, vol. 52(18), pp. 5740-5746 (2004). |
| Kovac, et al., “Synthesis of Ligands related to the O-Specific antigen of Type 1 Shigella dysenterin. 3. Glycosylation of 4,6-O-Substitute derivatives of Methyl 2-Acetamido-2-deoxy-α-D-glucopyranoside with Glycosyl donors derived from Mono-and Oligosaccharides,” Journal of Organic Chemistry, vol. 57, pp. 2455-2467 (1992). |
| Kovac, P. et al., “Systematic Chemical synthesis and N.M.R. spectra of methyl α-Glycosides of isomalto-oligosaccharides and related compounds,” Carbohydr. Res., vol. 184, pp. 87-112 (1988). |
| Kramer, M. J. et al., “Electron microscopic evidence for a double hair-like nap appearing at low frequency on Bacillus anthracis Sterne spores,” Can. J. Mircobiol., vol. 15, pp. 1247-1248 (1969). |
| Kramer, M. J. et al., “Ultrastructural differences in the exoporium of the Sterne and Vollum strains of Bacillus anthracis,” Can. J. Microbiol., vol. 14, pp. 1297-1299 (1968). |
| Kuziemko, G. M. et al., “Cholera Toxin Binding Affinity and Specificity for Gangliosides Determined by Surface Plasmon Resonance,” Biochemistry, vol. 35, pp. 6375-6384 (1996). |
| Lai, et al., “Proteomic Analysis of the Spore Coats of Bacillus subtilis and Bacillus anthracis,” J. Bateriol, vol. 185, pp. 1443-1454 (2003). |
| Langer, R. and J. P. Vacanti, “Tissue engineering.” Science, 260:920-926. (1993). |
| Lee, K. et al. “Photolithographic Technique for Direct Photochemical Modification and Chemical Micropatterning of Surfaces.” Langmuir, 20, 1812-1818. (2004). |
| Lee, M. et al. “Facile Preparation of Carbohydrate Microarrays by Site-Specific, Covalent Immobilization of Unmodified Carbohydrates on Hydrazide-Coated Glass Slides,” Organic Letters, 2005, vol. 7, No. 19, 4269-4272. |
| Lee, W. et al., “Protein array consisting of sol-gel bioactive platform for detection of E-coli 0157:H7,” Biosensors and Bioelectronics, vol. 20(11), pp. 2292-2299 (2005). |
| Lipshutz, R.J. et al., “High density synthetic oligonucleotide arrays,” Nature Genetics, vol. 21, pp. 20-24 (1999). |
| Liu, G. Y. and N. A. Amro, “Positioning protein molecules on surfaces: a nanoengineering approach to supramolecular chemistry.” Proc. Natl. Acad. Sci. USA, 99(8):5165-5170. (2002). |
| Lopez, G. P. et al. “Imaging of features on surfaces by condensation figures.” Science, 260:647-649. (1993). |
| Love, K. R. et al., “Carbohydrate arrays as tools for glycomics,” Angewandte Chemie International Edition, vol. 41(19), pp. 3583-3586 (2002). |
| Lui, et al., “Micro-patterning of 3-aminopropyltrimethoxy-silance self-assembled monolayers with colloidal gold,” Supramolecular Science, pp. 705-708 (1998). |
| MacBeath, G. et al., “Printing small molecules as microarrays and detecting protein-ligand interactions en masse,” Journal of the American Chemcial Society, vol. 121, pp. 7967-7968 (1999). |
| Mahal, L. K., “Catching bacteria with sugar,” Chemistry & Biology, vol. 11(12), pp. 1602-1604 (2004). |
| Mammen, M. et al., “Polyvalent interactions in biological systems: Implications for design and use of multivalent ligands and inhibitors,” Angewandte Chemie International Edition, vol. 37, pp. 2754-2794 (1998). |
| Mock, M. et al., “Anthrax,” Annu. Rev. Microbiol., vol. 55, pp. 647-671 (2001). |
| Moon, J. H. et al. “Formation of Uniform Aminosilane Thin Layers: An Imine Formation to Measure Relative Surface Density of the Amine Group.” Langmuir, 12:4621-4624. (1996). |
| Morinage, T. et al., “Polyester compositions,” Jpn. Kokai Tokkyo Koho, 5 pp. (1979). |
| Nagai, Y. et al., “UV-curable hot-melt acrylic adhesive compositions useful for adhesive tapes and labels,” Jpn. Kokai Tokkyo Koho, 12 pp., (2001). |
| Newcombe, et al., “Survival of Spacecraft-Associated Microorganisms under Simulated Martian UV Irradiation,” Appl. Environ. Microbiol., vol. 71, pp. 8147-8156 (2005). |
| Ngundi, M. M. et al., “Detection of bacterial toxins with monosaccharide arrays,” Biosensors and Biolelectronics, vol. 21(7), pp. 1195-1120 (2006). |
| Ni, J. H. et al., “Synthesis of malemide-activated carbohydrates as chemoselective tags for sitespecific glycosylation of peptides and proteins,” Bioconjugate Chemistry, vol. 14(1), pp. 232-238 (2003). |
| Nimrichter, L. et al. “Intact cell adhesion to glycan microarrays.” Glycobiology, 14(2):197-203. (2004). |
| Pacifici, J. G. et al., “Photopolymerizable polymeric compositions containing halogen-containing aromatic ketones,” U.S., 7 pp. (1977). |
| Park, S. and I. Shin, “Fabrication of carbohydrate chips for studying protein-carbohydrate interactions.” Angew. Chem. Int. Ed. Engl., 41(17):3180-3182. (2002). |
| Park, S. et al. “Carbohydrate chips for studying high-throughput carbohydrate-protein interactions.” J. Am. Chem. Soc., 126:4812-4819. (2004). |
| Pavliak, et al., “Stereoselective syntheses of a di-, tri-, and tetra-saccharide fragment of Shigella dysenteriae type 1 0-antigen using 3,4,6-tri-O-acetyl-2-deoxy-α-D-glucopyranosyl chloride as a glycosyl donor,” Carbohydrate Research, vol. 229, pp. 103-116 (1992). |
| Peramo, Antonio, et al., “Deposition of Patterned Glycosaminoglycans on Silanized Glass Surfaces,” Langmuir, vol. 22, pp. 3228-3234 (2006). |
| Pirrung, M. C., “How to make a DNA chip.” Angewandte Chemie, International Edition, 41:1276-1289. (2002). |
| Pitts et al., “New Photoactivators for multiphoton excited three-dimensional submicron Cross-linking of proteins: Bovine Serum Albumin and Type 1 Collagen,” Photochemistry and photobiology, vol. 76, pp. 135-144 (2002). |
| Pitts, J. D. et al., “New Photoactivators for Multiphoton Excited Three-dimensional Submicron Cross-linking of Proteins: Bovine Serum Albumin and Type 1 Collegen,” Photochemistry and Photobiology, 2002, 76(2): 135-144. |
| Pope, M. R. et al., “Specific activity of polypyrrole nanoparticulate immunoreagents: Comparison of surface chemistry and immobilization options,” Bioconjugate Chemistry, vol. 7, pp. 436-444 (1996). |
| Prucker, O. et al. “Photochemical Attachment of Polymer Films to Solid Surfaces via Monolayers of Benzophenone Derivatives.” J. Am. Chem. Soc., 121:8766-8770. (1999). |
| Puu, G., “An approach for analysis of protein toxins based on thin films of lipid mixtures in an optical biosensor,” Analytical Chemistry, vol. 73, pp. 72-79 (2001). |
| Ratner, D. M. et al., “Tools for glycomics: Mapping interactions of carbohydrates in biological systems,” ChemBioChem, vol. 5(10), pp. 1375-1383 (2004). |
| Ratner, Daniel et al. “Probing Protein—Carbohydrate Interactions with Microarrays of Synthetic Oligosaccharides.” Chem Bio Chem, 5:379-383. (2004). |
| Redmond, et al., “Identification of proteins in the exosporium of Bacillus anthracis,” Microbiology, vol. 150, pp. 355-363 (2004). |
| Resnick, “New Glycan arrays discover autoimmunogenic activities of SARS-CoV: concern over monkey vaccine,” Medical New Today, Article [retrieved from] <http://www.medicalnewstoday.com/releases/11474.php>, 4 pages (Jul. 31, 2004). |
| Rezania, A. et al., “Bioactivation of metal oxide surfaces. 1. Surface characterization and cell response,” Langmuir, vol. 15, pp. 6931-6939 (1999). |
| Rosen, George, “Photopolymerizable compounds and compositions comprising the product of the reaction of a monomeric ester and a polycarboxy-substituted benzophenone,” U.S., 7 pp., Division of U.S. Pat. No. 3,926,641, (1977). |
| Rowe Taitt, C. et al., “Evanescent wave fluorescence biosensors,” Biosensors and Bioelectronics, vol. 20(12), pp. 2470-2487 (2005). |
| Rowe-Taitt, C. A. et al., “A ganglioside-based assay for cholera toxin using an array biosensors,” Analytical Biochemistry, vol. 281(1), pp. 123-133 (2000). |
| Rowe-Taitt, C. A. et al., “Array biosensorfor detection of biohazards,” Biosensors and Bioelectronics, vol. 14(10-11), pp. 785-794 (2000). |
| Rowe-Taitt, C. A. et al., “Simultaneous detection of six biohazardous agents using a planar waveguide array biosensor,” Biosensors and Bioelectronics, vol. 15(11-12), pp. 579-589 (2000). |
| Roy, A. et al., “Structure of the capsular polysaccharide from Streptococcus pneumoniae,” Carbohydrate Research, vol. 126, pp. 271-277 (1984). |
| Rozsnyai, L. F. et al. “Photolithographic immobilization of biopollymers on solid supports.” Angew. Chem., 31(6):759-761. (1992). |
| Saksena, et al., “one-pot preparation of a series of glycoconjugates with predetermined antigen-carrier ratio from oligosaccharides that mimic the O-ps of vibrio cholerae O:1, serotype Ogawa,” Carbohydrate Research, vol. 338, pp. 2591-2603 (2003). |
| Saksena, R. et al., “Studies toward a conjugate vaccine for anthrax. Synthesis and characterization of anthrsoe[4,6-dideoxy-4-(3-hydroxy-3-methylbutanamido)-2-O-methyl-D-glucopyranose] and its methyl glycosides,” Carbohydrate Research, vol. 340, pp. 1591-1600 (2005). |
| Saksena, R. et al., “Synthesis of the tetrasacchride side chain of the major glycoprotein of the Bacillus anthracis exosporium,” Bioorganic and Medicinal Chemistry Letters, vol. 16, pp. 615-617 (2006). |
| Sapsford, K. E. et al., “Detection of Campylobacter and Shigella species in food samples using an array biosensor,” Analytical Chemistry, vol. 76, pp. 433-440 (2004). |
| Schmelmer, U. et al., “Surface-Initiated Polymerization of Self-Assembled Monolayers: Amplification of Patterns on the Micrometer and Nanometer Scale,” Angew. Chem. Int. Ed. 2003, 42, No. 5, pp. 559-563. |
| Schmidt, “Sugar rush,” New Scientist, vol. 176, Issue 2366, p. 34 (Oct. 2002). |
| Seeberger, P. H. et al., “Carbohydrate microarrays as versatile tools for glycobiology,” Glycobiology, vol. 14(11), p. 1073 (2004). |
| Seo, et al., “Photocleavable fluorescent nucleotides for DNA sequencing on a chip contructed by site-specific coupling chemistry,” PNAS USA, vol. 101, pp. 5488-5493 (Apr. 13, 2004). |
| Shin, I., et al. “Carbohydrate microarrays: An advanced technology for functional studies of glycans.” Chem. Eur. J., 11:2894-2901. (2005). |
| Shin, I. J. et al., “Carbohydrate arrays for functional studies of carbohydrates,” Combinatorial Chemistry & High Throughput Screening, vol. 7(6), pp. 565-574 (2004). |
| Shoji, T. et al., “Multilayer stable-modulus films for seld assembly of microstructures, preparation thereof,” and UV-curable compositions therefor, Jpn. Koai Tokkyl Koho, 15 pp. (2004). |
| Song, X. et al., “Direct, ultrasensitive, and selective optical detection of protein toxins using multivalent interactions,” Analytical Chemistry, vol. 71, pp. 2097-2107 (1999). |
| Song, X. et al., “Flow cytometry-based biosensor for detection of multivalent proteins,” Analytical Biochemistry, vol. 284, pp. 35-41 (2000). |
| Steichen, et al., “Identification of the immunodominant Protein and Other Proteins of the Bacillus anthracis Exosporium,” J. Bacteriol, vol. 185, pp. 1903-1910 (2003). |
| Sun, et al., Carbohydrate and protein immobilization onto solid surfaces by sequential Diels-Alder and azide-alkyne cycloadditions, Bioconjub. Chem., vol. 17, pp. 52-57 (Jan.-Feb. 2006). |
| Sylvestre, et al., “A Collagen-like surface glycoprotein is a structural component on the Bacillus anthracis exosporium,” Mol. Microbiol., vol. 45, pp. 169-178 (2002). |
| Takahashi, S. and J. Anzai. “Phenylboronic acid monolayer-modified electrodes sensitive to sugars.” Langmuir, 21:5102-5107. (2005). |
| Tamborrini, et al., “Anti-Carbohydrate Antibodies for the Detection of Anthrax Spores,” Angewandte Chemie International Edition, vol. 45, Issue 39, pp. 6581-6582 (Published Online: Aug. 17, 2006). |
| Tamborrini, et al., “Anti0Carbohydrate antibodies for the detection of anthrax spores,” Angew. Chem. Int. Ed., vol. 45, pp. 1-3 (2006). |
| Tamborrini, Marco et al. “Anti-Carbohydrate Antibodies for the Detection of Anthrax Spores.” Agnew. Chem. Int. Ed., 45:1-3. (2006). |
| Tang, P. W. et al., “Neoglycolipid micro-immunoassays applied to the oligosaccharides of human-milk galactosyltransferase detect blood-group related antigens on both o-linked and n-linked chains,” Carbohydrate Research, vol. 161(1), pp. 133-143 (1987). |
| Tang, P. W. et al., “Novel approach to the study of the antigenicities and receptor functions of carbohydrate chains of glycoproteins,” Biochemical and Biophysical Research Communications, vol. 132(2), pp. 474-480 (1985). |
| Turnbull, P. C. B., “Current status of immunization against anthrax: old vaccines may be here to stay for a while,” Curr. Opin. Infect. Dis., vol. 13, pp. 113-120 (2000). |
| Turro, N. J. “Modern Molecular Photochemistry.” University Science Books, Sausalito, CA. (1991). |
| Wadkins, R. M. et al., “Detection of multiple toxic agents using a planar array immunosensor,” Biosensors and Bioelectronics, vol. 13(3-4), pp. 407-415 (1998). |
| Wang, D. et al. “Carbohydrate microarrays for the recognition of cross-reactive molecular markers of microbes and host cells.” Nature Biotechnol., 20:275-281. (2002). |
| Wang, D. et al., “Glycan arrays lead to the discovery of autoimmunogenic activity of SARS-CoV,” Physiol Genomics, vol. 18, pp. 245-248 (2004). |
| Wang, D., “Carbohydrate antigens,” Encyclopedia of Molecular Cell Biology and Molecular Medicine, vol. II, Chapter, 11, pp. 277-301 (2004). |
| Wang, D., “Carbohydrate microarrays,” Proteomics, vol. 3, pp. 2167-2175 (2003). |
| Wang, et al., “A Carbohydrate-based microarray system for charcterizing AIDS-associated microbial infections,” Preliminary Program, AIDS Vaccine 2001, Philadelphia, 1 page (Sep. 5-8, 2001). |
| Wang, et al., “Photogenerated Glycan arrays identify immunogenic sugar moieties of Bacillus anthracis exosporium,” Proteomics, vol. 7, pp. 180-184 (2007). |
| Wang, R. et al., “A Practical Protocol for Carbohydrate Microarrays,” Methods Mol. Biol., vol. 310, pp. 241-252 (2005). |
| Wang, S. P. et al., “Immunologic relationship between gential TRIC, lymphogranuloma venereum, and related organisms in a new microtiter indirect immunofluoresecence test,” American Journal of Opthalmology, vol. 70(3), pp. 367-374 (1970). |
| Webb, G. F., “A silent bomb: The risk of anthrax as a weapon of mass destruction,” Proc. Natl. Acad. Sci. USA, vol. 100, pp. 4355-4356 (2003). |
| Whitesides, G. M. et al. “Soft lithography in biology and biochemistry.” Annu. Rev. Biomed. Eng., 3:335-373. (2001). |
| Willats, William G. T. et al. “Sugar-coated microarrays: a novel slide surface for the high-throughput analysis of glycans.” Proteomics, 2:1666-1671. (2002). |
| Williams, et al., “Species-Specific Peptide Ligands for the Detection of Bacillus anthracis Spores,” Appl. Environ. Micriobiol., vol. 69, pp. 6288-6293 (2003). |
| Wilson, M. et al., “Synthesis and activity of inhibitors highly specific for the glycolytic enzymes form Trypanosoma brucei,” Molecular and Biochemical Parasitology, vol. 59(2), pp. 201-210, (1993). |
| Wu, Q. et al., “Synthesis of di (4-hydroxyl benzophenone) sebacate and its usage as initiator in the photocrosslinking of polyethylene,” Journal of Applied Polymer Science, vol. 85(7), pp. 1581-1586, (2002). |
| Xiao, S. J. et al., “Covelent attachment of cell-adhesive, (Arg-Gly-Asp)-containing peptides to titanium surfaces,” Langmuir, vol. 14, pp. 5507-5516 (1998). |
| Xiao, S. J. et al., “Immobilization of the cell-adhesive peptide Arg-Gly-Asp-Cys (RGDC) on titanium surfaces by covalent chemical attachment,” Journal of Materials Science: Materials in Medicine, vol. 8, pp. 867-872 (1997). |
| Yeong, W. Y. et al. “Rapid protyping in tissue engineering: challenges and potential.” Trends Biotechnol., 22(12), 643-652. (2004). |
| Zhang, et al., “Carbohydrate-Protein interactions by “Clicked” Carbohydrate Self-Assmebled Monolayers,” Annal. Chem., vol. 78, pp. 2001-2018 (Mar. 15, 2006). |
| Zhang, J. et al., “Synthesis of methyl α-glycosides of some higher oligosaccharide fragments of the O-antigen of Vibrio Cholerae O1, serotype Inaba and Ogawa,” Carbohydrate Research, vol. 300, pp. 329-339 (1997). |
| Zhang, Y. et al., “Studying the interaction of α-Gal carbohydrate antigen and proteins by quartz-crystal microbalance,” Journal of American Chemical Society, vol. 125, pp. 9292-9293 (2003). |
| Zhou, et al., “Oligosaccharide microarray fabricated on aminooxyacetyl functionalized glass surface for characterization of carbohydrate-protein interaction,” Biosensors and Bioelectronics, vol. 21, pp. 1-5 (2005). |
| Zhou, et al., “Oligosaccharide microarrays fabricated on aminooxyacetyl functionalized glass surface for characterization of carbohydrate-protein interaction,” Biosensor and Bioelectronics, vol. 21, pp. 1451-1458 (Feb. 2006). |
| Number | Date | Country | |
|---|---|---|---|
| 20160231649 A1 | Aug 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60776096 | Feb 2006 | US | |
| 60735402 | Nov 2005 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13416968 | Mar 2012 | US |
| Child | 14589306 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11595292 | Nov 2006 | US |
| Child | 13416968 | US |