Patent Grant
8866027
This application is the U.S. National Phase under 35 U.S.C. §371 of International Application No. PCT/JP2008/050434, filed on Jan. 16, 2008, which in turn claims the benefit of Japanese Application No. 2007-010416, filed on Jan. 19, 2007 and Japanese Application No. 2007-047609, filed on Feb. 27, 2007, the disclosures of which Applications are incorporated by reference herein.
The present invention relates to a printed wiring board used as a substrate for a magnetic head suspension in a hard disk drive, and to a method for manufacturing the printed wiring board.
In recent years, as the density of electronic devices is increased and as the sizes electronic devices are reduced, printed wiring boards have been applied to a variety of uses. For example, in a hard disk drive, in which high-speed transfer of data is required, a printed wiring board is used as a substrate for a magnetic head suspension on which a magnetic head is mounted.
Patent Document 1 discloses such a printed wiring board having an insulating layer in which through hole is formed, conductive paste filling the through hole, and a conductive layer formed on either side of the insulating layer. Each conductive layer is formed of copper foil and has a predetermined wiring pattern. Since conductive paste generally has good conductivity, it is widely used for a wide variety of electronic devices. In the printed wiring board, a conductive paste in which conductive filler such as metal powder is dispersed in a binder resin such as epoxy resin is used. The conductive layers formed on both sides of the insulating layer are electrically connected to each other with the conductive paste.
Patent Document 2 discloses a printed wiring board having an insulating layer and a conductive layer formed on either side of the insulating layer. The conductive layers are electrically connected to each other with solder paste. The printed wiring board includes an insulating layer in which through hole is formed, solder paste caused to fill the through hole by reflow soldering, a conductive layer formed either side of the insulating layer. Each conductive layer has a predetermined wiring pattern. In the printed wiring board, the conductive layers formed on both sides of the insulating layer are electrically connected to each other with solder paste.
Patent Document 3 discloses a printed wiring board that is used as a substrate for a magnetic head suspension in the above described hard disk drive. The printed wiring board includes a metallic substrate made, for example, of stainless steel (SUS), an insulating layer laminated on the metallic substrate, and a conductive layer laminated on the insulating layer. The conductive layer is made of copper foil and is formed into a predetermined wiring pattern. Each layer of the printed circuit board is etched to have a predetermined shape.
Although the above described conductive paste is effective as means for electrically connecting conductive layers made of copper foils to each other, it can hardly be used as means for electrically connecting a metallic substrate and a conductive layer in a printed wiring board for a magnetic head suspension. That is, insulating oxide film is easily formed on the surface of a metallic substrate formed, for example, of stainless steel. Also, organic matter easily collects on the surface. Thus, when electrically connecting a metallic substrate with a conductive layer using conductive paste, insulating layer is likely to be formed at the interface between the conductive paste and the metallic substrate. As a result, since the resistance is increased at the interface between the conductive paste and the metallic substrate, the connection reliability between the metallic substrate and the conductive layer is decreased.
A metallic substrate and a conductive layer may be electrically connected to each other with solder paste. In this case, to remove insulating oxide film on the surface of the metallic substrate, flux needs to be added to the solder paste. However, the use of flux causes insulation deterioration such as migration.
Accordingly, it is an objective of the present invention to provide a printed wiring board that uses conductive paste, thereby achieving a superior connection reliability.
To achieve the foregoing objective and in accordance with a first aspect of the present invention, a printed wiring board including a metallic substrate, an insulating layer, a conductive layer, a bottomed via hole or through hoe, and a conductive paste is provided. The insulating layer is provided on a surface of the metallic substrate. The conductive layer is provided on a surface of the insulating layer, and is electrically connected to the metallic substrate. The via hole is formed in the insulating layer and the conductive layer. The via hole has a bottom in the metallic substrate, and has a wall surface in the insulating layer and in the conductive layer. The through hole extends through the insulating layer, the conductive layer, and the metallic substrate. The conductive paste fills the bottomed via hole or the through hole to electrically connect the metallic substrate and the conductive layer to each other. The printed wiring board is subjected to a process in which current is applied to the interface between the metallic substrate and the conductive paste.
In this configuration, since insulating oxide film and organic matter on the surface of the metallic substrate are destroyed and removed, formation of insulating layer at the interface between the conductive paste and the metallic substrate is effectively inhibited. Therefore, the resistance at the interface between the conductive paste and the metallic substrate is reduced, so that the metallic substance and the conductive layer are reliably connected to each other with the conductive paste. As a result, the connection reliability of the metallic substrate and the conductive layer is improved. Also, since the need for flux when connecting the metallic substrate and the conductive layer to each other is eliminated, insulation deterioration such as migration caused by flux is prevented.
The above printed wiring board is preferably configured such that the metallic substrate is made of at least one selected from the group consisting of stainless steel, aluminum, iron, copper, nickel, titanium, molybdenum, chromium, and zinc. According to this configuration, even in a case where a metallic substrate made, for example, of stainless steel, on which insulating oxide film is easily formed and organic matter easily collects, is used, the resistance at the interface between the conductive paste and the metallic substrate is effectively reduced. As a result, for example, even in a case where a metallic substrate made of stainless steel having superior heat radiating property, spring characteristic, and corrosion resistance is used, the connection reliability between the metallic substance and the conductive layer is improved.
To achieve the foregoing objective and in accordance with a second aspect of the present invention, a printed wiring board including a metallic substrate, an insulating layer, a conductive layer, a bottomed via hole or through hoe, and a conductive paste is provided. The insulating layer is provided on a surface of the metallic substrate. The conductive layer is provided on a surface of the insulating layer, and is electrically connected to the metallic substrate. The via hole is formed in the insulating layer and the conductive layer. The via hole has a bottom in the metallic substrate, and has a wall surface in the insulating layer and in the conductive layer. The through hole extends through the insulating layer, the conductive layer, and the metallic substrate. The conductive paste fills the bottomed via hole or the through hole to electrically connect the metallic substrate and the conductive layer to each other. In the printed wiring board, the metallic substrate is made of stainless steel, and the contact resistance at an interface between the metallic substrate and the conductive paste is 0.03 Ω·mm2 or less.
Since the contact resistance at the interface between the conductive paste and the metallic substrate is less than or equal to 0.03 Ω·mm2, the metallic substance and the conductive layer are reliably connected to each other with the conductive paste. As a result, the connection reliability of the metallic substrate and the conductive layer is improved. Also, since the need for flux when connecting the metallic substrate and the conductive layer to each other is eliminated, insulation deterioration such as migration caused by flux is prevented. Further, the use of stainless steel as the material of the metallic substrate provides a printed wiring board having a metallic substrate with superior heat radiating property, spring characteristic, and corrosion resistance.
Further, since the contact resistance at the interface between the conductive paste and the metallic substrate is less than or equal to 0.03 Ω·mm2, and the connection reliability between the metallic substrate and the conductive layer is improved, this configuration is suitable for a printed wiring board used as a substrate of a suspension in a hard disk drive.
To achieve the foregoing objective and in accordance with a third aspect of the present invention, a printed wiring board including a metallic substrate, an insulating layer, a conductive layer, a bottomed via hole or through hoe, and a conductive paste is provided. The insulating layer is provided on a surface of the metallic substrate. The conductive layer is provided on a surface of the insulating layer, and is electrically connected to the metallic substrate. The via hole is formed in the insulating layer and the conductive layer. The via hole has a bottom in the metallic substrate, and has a wall surface in the insulating layer and in the conductive layer. The through hole extends through the insulating layer, the conductive layer, and the metallic substrate. The conductive paste contains metallic particles and fills the bottomed via hole or the through hole to electrically connect the metallic substrate and the conductive layer to each other. In the printed wiring board, the metallic particles of the conductive paste are anchored to the metallic substrate at an interface between the metallic substrate and the conductive paste.
Since metallic particles in the conductive paste are anchored to the metallic substrate at the interface between the metallic substrate and the conductive paste, the resistance at the interface between the conductive paste and the metallic substrate is reduced. Thus, the metallic substrate and the conductive layer are reliably connected to each other with the conductive paste. As a result, the connection reliability of the metallic substrate and the conductive layer is improved. Also, since the need for flux when connecting the metallic substrate and the conductive layer to each other is eliminated, insulation deterioration such as migration caused by flux is prevented. The “anchorage” refers to a state in which, when a connected part is observed with a cross-sectional scanning microscope, no gap is seen and contacting part is not in points but linearly extends.
In the printed wiring board, it is preferable that the length of a part at which the metallic particles are anchored to the metallic substrate be 0.1 μm or longer.
Since the length of the part at which the metallic particles in the conductive paste and the metallic substrate are anchored to each other is longer than or equal to 0.1 μm, the area through which current flows is large. As a result, the resistance at the interface between the conductive paste and the metallic substrate is further effectively reduced.
The above printed wiring board is preferably configured such that the metallic substrate is made of at least one selected from the group consisting of stainless steel, aluminum, iron, copper, nickel, titanium, molybdenum, chromium, and zinc.
According to this configuration, even in a case where a metallic substrate made, for example, of stainless steel, on which insulating oxide film is easily formed and organic matter easily collects, is used, the resistance at the interface between the conductive paste and the metallic substrate is effectively reduced. As a result, the connection reliability of the metallic substrate and the conductive layer is improved. Particularly, for example, even in a case where a metallic substrate made of stainless steel having superior heat radiating property, spring characteristic, and corrosion resistance is used, the connection reliability between the metallic substance and the conductive layer is improved.
Also, since the metallic particles in the conductive paste and the metallic substrate are anchored to each other at the interface between the metallic substrate and the conductive paste, so that the connection reliability between the metallic substrate and the conductive layer is improved, this configuration is suitable for a printed wiring board used as a substrate of a suspension in a hard disk drive.
To achieve the foregoing object and in accordance with a fourth aspect of the present invention, a method for manufacturing a printed wiring board is provided. The manufacturing method includes at least the steps of: preparing a base fabricated by laminating a metallic substrate, an insulating layer, and a conductive layer; selectively removing the insulating layer, thereby forming a bottomed via hole or a through hole, wherein the via hole has a bottom in the metallic substrate, and has a wall surface in the insulating layer and in the conductive layer, and wherein the through hole extends through the insulating layer, the conductive layer, and the metallic substrate; applying conductive paste to the base thereby filling the through hole with the conducive paste, such that the surface of the metallic substrate that is the bottom of the bottomed via hole or the surface of the metallic substrate in which the through opens is continuous with the surface of the conducive layer that is the wall surface of the through hole; and applying electric current to the interface between the metallic substrate and the conductive paste.
In this configuration, since insulating oxide film and organic matter on the surface of the metallic substrate are destroyed and removed, formation of insulating layer at the interface between the conductive paste and the metallic substrate is effectively inhibited. Therefore, the resistance at the interface between the conductive paste and the metallic substrate is reduced. Thus, the metallic substrate and the conductive layer are reliably connected to each other with the conductive paste. As a result, the connection reliability of the metallic substrate and the conductive layer is improved. Also, since the need for flux when connecting the metallic substrate and the conductive layer to each other is eliminated, insulation deterioration such as migration caused by flux is prevented.
In the method for manufacturing a printed wiring board, it is preferable that the density of the current applied to the interface between the metallic substrate and the conductive paste be 0.1 A/mm2 to 1000 A/mm2. In this configuration, since insulating oxide film and organic matter on the surface of the metallic substrate are destroyed and removed without altering the resin of the conductive paste or melting the metallic substrate due to the heat of current.
In the method for manufacturing a printed board, it is preferable that the period during which the current is applied be 1×10−6 seconds to 100 seconds. In this configuration, insulating oxide film and organic matter on the surface of the metallic substrate are effectively destroyed and removed without reducing the productivity of the printed wiring board.
a) to 2(h) are cross-sectional views for explaining a method for manufacturing the printed wiring board according to the embodiment of the present invention;
a) to 3(f) are cross-sectional views for explaining a method for manufacturing the printed wiring board according to the embodiment of the present invention, showing steps subsequent to those of
A preferred embodiment of the present invention will now be described. A printed wiring board 1 of the present invention is used, for example, as a substrate for a magnetic head suspension on which a magnetic head is mounted in a hard disk drive.
As shown in
The metallic substrate 2 is made, for example, of stainless steel, aluminum, iron, copper, nickel, titanium, molybdenum, chromium, or zinc. Among these, the metal foil is preferably made of stainless steel because of its superior heat radiating property, spring characteristic, and corrosion resistance. The thickness of the metallic substrate 2 is preferably 1 μm to 100 μm.
The insulating layer 3 is made of a resin material having a superior flexibility. As the resin, polyester, which has versatility, is used for the printed wiring board. Particularly, it is preferable to use a resin that has a high heat resistance in addition to flexibility. As such resin film, for example, polyamide-based resin and polyimide-based resin such as polyimide and polyamide-imide are preferable. The thickness of the insulating layer 3 is preferably 5 μm to 200 μm.
The conductive layer 4 is formed on the surface of the insulating layer 3. The conductive layer 4 includes a conductive film 8 forming a base and a plating layer 12 formed on the surface of the conductive film 8. Taking the conductivity and durability into consideration, the conductive film 8 is preferably made, for example, of copper or a copper-based alloy. For example, copper film or a chromium film is used. The plating layer 12 is formed, for example, of copper, aluminum, nickel, gold, solder, or an alloy of these. In view of improving the conductivity, copper is particularly preferable. The thickness of the conductive layer 4 is preferably 2 μm to 50 μm.
To improve the reliability related to the ground connection between the conductive layer 4 and a grounding terminal (not shown), the surface of the conductive layer 4 is coated with a plating layer 5. In consideration of the environment, a lead-free plating layer 5 is preferably used. To prevent the connection reliability between the conductive layer 4 and the terminal from being degraded, a gold plating layer may be used as the lead-free the plating layer 5. Plating to the surface of the conductive layer 4 is performed by electroless plating or electrolytic plating. When forming gold plating layer, nickel plating layer as diffusion preventing layer is first formed on the surface of the exposed conductive layer 4. Gold plating layer is formed on the surface of the nickel plating layer.
A via hole 6 is formed in the printed wiring board 1 to connect the conductive layer 4 to the metallic substrate 2. The via hole 6 is filled with conductive paste 7. The metallic substrate 2 and the conductive layer 4 are electrically connected to each other with the conductive paste 7. Although not illustrated, the via hole 6 may be replaced by a through hole that extends through the insulating layer 3, the conductive layer 4, and the metallic substrate 2. In this case, the metallic substrate 2 and the conductive paste 7 contact each other on the wall surface of the through hole.
The through hole 6 opens on the surface of the metallic substrate 2 and extend through the insulating layer 3 and the conductive layer 4. The diameter of the through hole 6 is preferably 30 to 400 μm, and more preferably 50 to 200 μm. This is because if the diameter is less than 30 μm, the contact area at the through hole 6 is too small, and thus the connection resistance will be excessive when the metallic substrate 2 and the conductive layer 4 are electrically connected to each other. If the diameter is greater than 400 μm, the through hole 6 will be large compared to the width of the traces of the wiring pattern formed on the conductive layer 4, which makes high-density packaging difficult. The cross-sectional shape of the through hole 6 may be other than circular. The cross-sectional shape may be, for example, elliptic or polygonal. When the cross-sectional shape is other than circular, the longest axis of the opening will be referred to as the diameter of the through hole.
As the conductive paste 7, a paste that contains a conductive filler such as metallic powder dispersed in a binder resin is used. As the metallic powder, for example, silver, platinum, gold, copper, nickel, or palladium is used. Among these, because of the superior conductivity, silver powder and silver-coated copper powder are preferable. As the binder resin, for example, epoxy resin, phenol resin, polyester resin, polyurethane resin, acrylic resin, melamine resin, polyimide resin, or polyamide-imide resin is used. Among these, in view of improving the heat resistance of the conductive paste, thermosetting resin is preferably used. In the present embodiment, it is preferable to use epoxy resin.
The type of the epoxy resin is not particularly limited. For example, an epoxy resin of bisphenol A, F, S, or AD type, an epoxy resin of copolymerized bisphenol A type and bisphenol F type, a naphthalene type epoxy resin, a novolac-type epoxy resin, a biphenyl type resin, or a dicyclopentadiene type resin is used. Also, a phenoxy resin, which is a high-molecular weight, may be used.
The binder resin may be dissolved in solvent before use. As the solvent, for example, organic solvent such as ester solvent, ether solvent, ketone solvent, ether ester solvent, alcohol solvent, hydrocarbon solvent, and amine solvent may be used. Since the through hole 6 is filled with the conductive paste 7 by screen printing, it is preferable to use a high-boiling-point solvent that has a superior print performance. More specifically, carbitol acetate or butyl carbitol acetate is preferable. These solvents may be used in combination. These components are mixed with a triple roll mill or rotational agitator-defoamer, such that they are dispersed evenly to obtain the conductive paste.
In the printed wiring board 1, an additional insulating layer 15 is formed on the surface of a part of the conductive layer 4 and on the surface of the conductive paste 7. The additional insulating layer 15 covers a part of the conductive layer 4 and the conductive paste 7. The same material of the insulating layer 3 is used for the additional insulating layer 15.
A procedure for manufacturing the printed wiring board will now be described with reference to the drawings.
First, the metallic substrate 2 is prepared as shown in
Subsequently, after a predetermined pattern is formed on the insulating layer 3 using resist, the conductive layer 4 is formed on the surface of the insulating layer 3 by semi-additive process, in which traces are formed by plating. Specifically, the conductive film 8, which is the base of the conductive layer 4, is first formed on the surface of the insulating layer 3 as shown in
Then, as shown in
As shown in
As show in
Then, as shown in
Then, as shown in
As shown in
Then, as shown in
Then, as shown in
Next, as shown in
The present embodiment is characterized in that, in the state of
The printed wiring board 1 is provided, in which the metallic substrate 2 and the conductive layer 4 are connected to each other with the metallic particles contained in the conductive paste 7 anchored to the metallic substrate 2 at the interface between the metallic substrate 2 and the conductive paste 7. Therefore, the printed wiring board 1 is provided, which has a superior connection reliability between the metallic substrate 2 and the conductive layer 4 and is particularly suitable as a substrate used for a suspension in a hard disk drive.
In view of increasing the size of a part through which current flows thereby reducing the resistance value, the length of the part at which the metallic particles of the conductive paste 7 are anchored to the metallic substrate 2 is preferably longer than or equal to 0.1 μm.
Also, the printed wiring board 1 is provided, in which stainless steel is used as the material of the metallic substrate 2, the contact resistance at the interface between the conductive paste 7 and the metallic substrate 2 is 0.03 Ω·mm2 or less, and the connection reliably between the metallic substrate 2 and the conductive layer 4 is improved. Particularly, the printed wiring board 1 that is suitable as a substrate for a suspension used in a hard disk drive is provided.
The current density of the current applied to the surface of the metallic substrate 2 in which the through hole 6 is opened (that is, the interface between the conductive paste 7 and the metallic substrate 2) is preferably 0.1 A/mm2 to 1000 A/mm2. This is because if the current density is less than 0.1 A/mm2, the insulating oxide film and organic matter on the surface of the metallic substrate 2 will not be easily destroyed and removed. Also, if the current density is greater than 1000 A/mm2, the heat caused by the current can alter the resin forming the conductive paste 7 or melt and exfoliate the metallic substrate 2.
As the current applied to the interface between the conductive paste 7 and the metallic substrate 2, a direct current, an alternating current, or a pulse current may be used. These types of currents may used in combination. When applying a current of 0.1 A/mm2 to 1000 A/mm2, time during which the current is applied (application period) is preferably 1×10−6 seconds to 100 seconds. This is because if the application period is shorter than 1×10−6 seconds, the insulating oxide film and organic matter on the surface of the metallic substrate 2 will not be easily destroyed and removed. If the application period is longer than 100 seconds, time required for fabricating the printed wiring board 1 will be too long, and the productivity of the printed wiring board 1 will be lowered.
Then, as shown in
The present embodiment has the advantages described below.
(1) The printed wiring board 1 includes the metallic substrate 2, the insulating layer 3 provided on the surface of the metallic substrate 2, and the conductive layer 4 formed on the surface of the insulating layer 3. The conductive layer 4 is electrically connected to the metallic substrate 2. The through hole 6 is formed in the insulating layer 3 and the conductive layer 4 so as to extend through the insulating layer 3 and the conductive layer 4, and open in the metallic substrate 2. The through hole 6 is filled with the conductive paste 7 for electrically connecting the metallic substrate 2 and the conductive layer 4 to each other. The printed wiring board 1 is subjected to a process in which current is applied to the interface between the metallic substrate 2 and the conductive paste 7. This destroys and removes insulating oxide film and organic matter on the surface of the metallic substrate 2, and reduces the resistance at the interface between the conductive paste 7 and the metallic substrate 2. As a result, the use of the conductive paste 7 having a superior conductivity improves the connection reliability between the metallic substrate 2 and the conductive layer 4. Also, since the need for flux is eliminated, insulation deterioration such as migration caused by flux is prevented.
(2) The printed wiring board 1 includes the metallic substrate 2, the insulating layer 3 provided on the surface of the metallic substrate 2, and the conductive layer 4 formed on the surface of the insulating layer 3. The conductive layer 4 is electrically connected to the metallic substrate 2. The through hole 6 is formed in the insulating layer 3 and the conductive layer 4 so as to open in the metallic substrate 2 and extend through the insulating layer 3 and the conductive layer 4. The through hole 6 is filled with the conductive paste 7 for electrically connecting the metallic substrate 2 and the conductive layer 4 to each other. Further, in the printed wiring board 1, the metallic substrate 2 is made of stainless steel, and the contact resistance at the interface between the conductive paste 7 and the metallic substrate 2 is 0.03 Ω·mm2 or less. Therefore, the use of the conductive paste 7 having a superior conductivity improves the connection reliability between the stainless steel metallic substrate 2 and the conductive layer 4. Also, since the need for flux is eliminated, insulation deterioration such as migration caused by flux is prevented. Further, the use of stainless steel as the material of the metallic substrate 2 provides a printed wiring board 1 having a metallic substrate with superior heat radiating property, spring characteristic, and corrosion resistance.
(3) Since the contact resistance at the interface between the conductive paste 7 and the metallic substrate 2 is less than or equal to 0.03 Ω·mm2, and the connection reliability between the metallic substrate 2 and the conductive layer 4 is improved, the printed wiring board 1 is particularly suitable for a printed wiring board used as a substrate of a suspension in a hard disk drive.
(4) The printed wiring board 1 includes the metallic substrate 2, the insulating layer 3 provided on the surface of the metallic substrate 2, and the conductive layer 4 formed on the surface of the insulating layer 3. The conductive layer 4 is electrically connected to the metallic substrate 2. The through hole 6 is formed in the insulating layer 3 and the conductive layer 4 so as to extend through the insulating layer 3 and the conductive layer 4, and opens in the metallic substrate 2. The through hole 6 is filled with the conductive paste 7 that contains metallic particles and electrically connects the metallic substrate 2 and the conductive layer 4 to each other. The metallic particles contained in the conductive paste 7 are anchored to the metallic substrate 2 at the interface between the metallic substrate 2 and the conductive paste 7. Therefore, the resistance at the interface between the conductive paste 7 and the metallic substrate 2 is reduced, so that the metallic substance 2 and the conductive layer 7 are reliably connected to each other with the conductive paste 7. As a result, the connection reliability of the metallic substrate 2 and the conductive layer 4 is improved. Also, since the need for flux when connecting the metallic substrate 2 and the conductive layer 4 to each other is eliminated, insulation deterioration such as migration caused by flux is prevented.
(5) The length of the part at which the metallic particles of the conductive paste 7 are anchored to the metallic substrate 2 is longer than or equal to 0.1 μm. Therefore, the resistance at the interface between the conductive paste 7 and the metallic substrate 2 is further effectively reduced.
(6) Since the metallic particles in the conductive paste 7 are anchored to the metallic substrate 2 at the interface between the metallic substrate 2 and the conductive paste 7, so that the connection reliability between the metallic substrate 2 and the conductive layer 4 is improved, this configuration is suitable for a printed wiring board used as a substrate of a suspension in a hard disk drive.
(7) The metallic substrate 2 is made of at least one selected from the group consisting of stainless steel, aluminum, iron, copper, nickel, titanium, molybdenum, chromium, and zinc. Therefore, even in a case where a metallic substrate 2 made, for example, of stainless steel, on which insulating oxide film is easily formed and organic matter easily collects, is used, the resistance at the interface between the conductive paste 7 and the metallic substrate 2 is effectively reduced. As a result, for example, even in a case where a metallic substrate 2 made of stainless steel having superior heat radiating property, spring characteristic, and corrosion resistance is used, the connection reliability between the metallic substance 2 and the conductive layer 4 is improved.
(8) The method for manufacturing the printed wiring board 1 includes: preparing a base fabricated by laminating the metallic substrate 2, the insulating layer 3, and the conductive layer 4; selectively removing the insulating layer 3, thereby forming the through hole 6 extending through the insulating layer 3 and the conductive layer 4, the through hole 6 opening in the metallic substrate 2; and applying the conductive paste 7, such that the surface of the metallic substrate 2, in which the through hole 6 opens, and the surface of the conductive layer 4, which is the wall surface of the through hole 6, are continuous, thereby filling the through hole 6 with the conductive paste 7. The method for manufacturing the printed wiring board 1 according to the present embodiment further includes applying current to the interface between the metallic substrate 2 and the conductive paste 7. This destroys and removes insulating oxide film and organic matter on the surface of the metallic substrate 2, and reduces the resistance at the interface between the conductive paste 7 and the metallic substrate 2. As a result, the use of the conductive paste 7 having a superior conductivity improves the connection reliability between the metallic substrate 2 and the conductive layer 4. Also, since the need for flux is eliminated, insulation deterioration such as migration caused by flux is prevented.
(9) The current density of the current applied to the interface between the metallic substrate 2 and the conductive paste 7 is 0.1 A/mm2 to 1000 A/mm2. Accordingly, since insulating oxide film and organic matter on the surface of the metallic substrate 2 are destroyed and removed without altering the resin of the conductive paste 7 or melting the metallic substrate 2 due to the heat of current.
(10) A current of which the density is 0.1 A/mm2 to 1000 A/mm2 is applied for 1×10−6 to 100 seconds. Accordingly, insulating oxide film and organic matter on the surface of the metallic substrate 2 are effectively destroyed and removed without reducing the productivity of the printed wiring board 1.
The present invention is not limited to the foregoing embodiment, but may be modified as follows without departing from the scope of the invention.
For example, latent hardener may be added to the conductive paste 7, in which conductive filler is dispersed in binder resin. In this case, for example, if a polyester resin is used as the binder resin, isocyanate compound may be used. If an epoxy resin is used, amine compound or imidazole compound may be used.
In the above embodiment, polyimide cover coat ink is applied by screen printing and dried to form the film-like insulating layer 3 made of a polyimide resin on the surface of the metallic substrate 2. However, an adhesive layer (not shown) may be formed on one side of the insulating layer 3, which is a resin film, and the metallic substrate 2 and the insulating layer 3 may be bonded to each other with means of the adhesive layer.
The present invention will now be described based on Examples and Comparative Examples. The present invention is not limited to these Examples. The Examples may be changed or modified based on the spirit of the present invention, and the changes and modifications are not excluded from the scope of the present invention.
(Fabrication of Printed Wiring Board)
The following description is made with reference to
The conductive paste 7 was prepared by dissolving 100 parts by weight of an epoxy resin of bisphenol A type (epoxy equivalent of 7000 to 8500) in butyl carbitol acetate, adding to the solution 1 part by weight of imidazole latent hardener, and adding silver particles to the solution such that the silver particles accounted for 60 vol % of the total dissolved solid.
The filling conductive paste 7 was heat-treated (180° C., 30 minutes) to be hardened, thereby fabricating a printed wiring board 30 shown in
(Measurement of Initial Resistance and Initial Contact Resistance)
As shown in
In the fabricated printed wiring board 30, current of 1 A (that is, a current density of 8.0 A/mm2) was applied for one second to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a (hereinafter, referred to as resistance after current application) was measured, and the contact resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a (hereinafter, referred to as contact resistance after current application) was measured by four-terminal sensing. The results are shown in Table 1.
In the fabricated printed wiring board 30, current of 2 A (that is, a current density of 15.9 A/mm2) was applied for one second to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 1.
In the fabricated printed wiring board 30, current of 2 A (that is, a current density of 23.9 A/mm2) was applied for one second to the interface between the metallic substrate 3 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 1.
In the fabricated printed wiring board 30, current of 2 A (that is, a current density of 31.8 A/mm2) was applied for one second to the interface between the metallic substrate 4 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 1.
(Fabrication of Printed Wiring Board and Measurement of Initial Resistance and Initial Contact Resistance)
A stainless steel metal foil (SUS304HTA), or the metallic substrate 2, was immersed in hydrochloric acid aqueous solution of 20% for 10 minutes and was washed with water. Thereafter, a printed wiring board 30 was fabricated by the same method as described above, and the initial resistance and the initial contact resistance were measured. The results are shown in Table 2. The contact area at the interface between the metallic substrate 2 and the conductive paste 7 was 0.1256 mm2. Also, due to the limitation of the four-terminal sensing, the contact resistance contained the resistance at the through hole 6a.
In the printed wiring board 30, which was fabricated by using the metallic substrate 2 that had been immersed in a hydrochloric acid aqueous solution of 20%, current of 1 A (that is, a current density of 8.0 A/mm2) was applied for one second to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were again measured by four-terminal sensing. The results are shown in Table 2.
In the printed wiring board 30, which was fabricated by using the metallic substrate 2 that had been immersed in a hydrochloric acid aqueous solution of 20%, current of 2 A (that is, a current density of 15.9 A/mm2) was applied for one second to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 2.
In the printed wiring board 30, which was fabricated by using the metallic substrate 2 that had been immersed in a hydrochloric acid aqueous solution of 20%, current of 2 A (that is, a current density of 23.9 A/mm2) was applied for one second to the interface between the metallic substrate 3 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 2.
In the printed wiring board 30, which was fabricated by using the metallic substrate 2 that had been immersed in a hydrochloric acid aqueous solution of 20%, current of 2 A (that is, a current density of 31.8 A/mm2) was applied for one second to the interface between the metallic substrate 4 and the conductive paste 7, and the resistance of the metallic substrate 2 and the conductive paste 7 at the through hole 6a after the current application and the contact resistance after the current application were measured by four-terminal sensing. The results are shown in Table 2.
(Fabrication of Printed Wiring Board)
The following description is made with reference to
The filling conductive paste 7 was heat-treated (180° C., 30 minutes) to be harden, thereby fabricating a printed wiring board 40 shown in
(Measurement of Initial Resistance and Initial Connection Resistance)
As shown in
In the fabricated printed wiring board 40, current of 10 mA (that is, a current density of 0.5 A/mm2) was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance at the through hole 6a (hereinafter, referred to as resistance after current application) was measured, and the connection resistance at the through hole 6a (hereinafter, referred to connection resistance after current application) was measured by four-terminal sensing. The results are shown in Table 3.
The initial connection resistance and the connection resistance after current application are each considered to be the sum of the contact resistance of the metallic substrate 2 and the conductive paste 7, the contact resistance of the plating layer 5 and the conductive paste 7, and the resistance of the conductive paste 7.
In the fabricated printed wiring board 40, current of 30 mA (that is, a current density of 1.4 A/mm2) was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance at the through hole 6 after the current application and the connection resistance after the current application were measured by four-terminal sensing. The results are shown in Table 3.
In the fabricated printed wiring board 40, current of 100 mA (that is, a current density of 4.7 A/mm2) was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance at the through hole 6 after the current application and the connection resistance after the current application were measured by four-terminal sensing. The results are shown in Table 3.
In the fabricated printed wiring board 40, current of 200 mA (that is, a current density of 9.4 A/mm2) was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance at the through hole 6 after the current application and the connection resistance after the current application were measured by four-terminal sensing. The results are shown in Table 3.
In the fabricated printed wiring board 40, current of 500 mA (that is, a current density of 23.4 A/mm2) was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7, and the resistance at the through hole 6 after the current application and the connection resistance after the current application were measured by four-terminal sensing. The results are shown in Table 3.
(Evaluation of Conductive Paste and Metallic Substrate)
The printed wiring board 40 of Example 10, in which a current of 30 mA was applied for two seconds to the interface between the metallic substrate 2 and the conductive paste 7 was cut along the axis of the through hole 6 by using a cross section polisher (SM-09010 manufactured by Japan Electron Optics Laboratory Co.). The interface between the conductive paste 7 and the metallic substrate 2 at the vertical cross-section of the through hole 6 was observed with an SEM (Scanning Electron Microscope, trade name: S-800 manufactured by Hitachi High-Technologies Corporation). The cross-sectional structure of the interface between the conductive paste 7 and the metallic substrate 2 is shown in
As indicated by Table 1, the contact resistance after current application was significantly lower than the initial contact resistance (0.15 Ω·mm2) in any of Examples 1 to 4. Also, as indicated by Table 2, the contact resistance after current application was significantly lower than the initial contact resistance (0.1883 Ω·mm2) in any of Examples 5 to 8. Further, the connection resistance after current application was significantly lower than the initial connection resistance (0.0406 Ω·mm2) in any of Examples 9 to 13. Accordingly, it was confirmed that the application of current to the interface between the metallic substrate 2 and the conductive paste 7 increased the connection reliability between the metallic substrate 2 and the conductive layer 4.
As shown in
The applications of the present invention include a printed wiring board used as a substrate for a magnetic head suspension in a hard disk drive, and a method for manufacturing the printed wiring board.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2007-010416 | Jan 2007 | JP | national |
| 2007-047609 | Feb 2007 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2008/050434 | 1/16/2008 | WO | 00 | 6/9/2009 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2008/087976 | 7/24/2008 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5733467 | Kawakita et al. | Mar 1998 | A |
| 6096411 | Nakatani et al. | Aug 2000 | A |
| 6143116 | Hayashi et al. | Nov 2000 | A |
| 6388201 | Yamato et al. | May 2002 | B2 |
| 6762921 | Asai et al. | Jul 2004 | B1 |
| 6942817 | Yagi et al. | Sep 2005 | B2 |
| 7356916 | Nishii et al. | Apr 2008 | B2 |
| 7760067 | Prusseit et al. | Jul 2010 | B2 |
| 20020007961 | Yamato et al. | Jan 2002 | A1 |
| 20020027127 | Yagi et al. | Mar 2002 | A1 |
| 20020070412 | Mitlehner et al. | Jun 2002 | A1 |
| 20040247978 | Shimamune | Dec 2004 | A1 |
| 20060198081 | Seitz et al. | Sep 2006 | A1 |
| 20070062925 | Park | Mar 2007 | A1 |
| 20070246247 | Ooyabu et al. | Oct 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| 05-206596 | Aug 1993 | JP |
| 05-218605 | Aug 1993 | JP |
| 05-243697 | Sep 1993 | JP |
| 10-178249 | Jun 1998 | JP |
| 10-335526 | Dec 1998 | JP |
| 11-054865 | Feb 1999 | JP |
| 11-251751 | Sep 1999 | JP |
| 2000-068620 | Mar 2000 | JP |
| 2001-352137 | Dec 2001 | JP |
| 2002-25028 | Jan 2002 | JP |
| 2002-025213 | Jan 2002 | JP |
| 2002-076614 | Mar 2002 | JP |
| 2002-094206 | Mar 2002 | JP |
| 2006-202359 | Aug 2006 | JP |
| 2006-245121 | Sep 2006 | JP |
| 2006-245122 | Sep 2006 | JP |
| 2007-294483 | Nov 2007 | JP |
| Entry |
|---|
| English machine translation of previously cited JP2006-202359. |
| English machine translation of previously cited JP11-251751. |
| International Preliminary Report on Patentability and Written Opinion of the International Searching Authority, issued in corresponding International Patent Application No. PCT/JP2008/050434, dated Jul. 21, 2009. |
| Japanese Office Action, with English translation, issued in Japanese Patent Application No. 2007-047609, dated Oct. 18, 2011. |
| Japanese Office Action issued in Japanese Patent Application No. 2007-047609, dated Jan. 10, 2012. |
| Japanese Office Action issued in Japanese Patent Application No. 2007-047609 dated Apr. 24, 2012. |
| Number | Date | Country | |
|---|---|---|---|
| 20100044094 A1 | Feb 2010 | US |