Patent Grant
7252712
The present invention refers to processes for obtaining a gallium-containing nitride crystal by an ammonobasic method as well as the gallium-containing nitride crystal itself. Furthermore, an apparatus for conducting the various methods is disclosed.
Optoelectronic devices based on nitrides are usually manufactured on sapphire or silicon carbide substrates that differ from the deposited nitride layers (so-called heteroepitaxy). In the most often used Metallo-Organic Chemical Vapor Deposition (MOCVD) method, the deposition of GaN is performed from ammonia and organometallic compounds in the gas phase and the growth rates achieved make it impossible to provide a bulk layer. The application of a buffer layer reduces the dislocation density, but not more than to approx. 108/cm2. Another method has also been proposed for obtaining bulk monocrystalline gallium nitride. This method consists of an epitaxial deposition employing halides in a vapor phase and is called Halide Vapor Phase Epitaxy (HVPE) [“Optical patterning of GaN films” M. K. Kelly, O. Ambacher, Appl. Phys. Lett. 69 (12) (1996) and “Fabrication of thin-film InGaN light-emitting diode membranes” W. S. Wrong, T. Sands, Appl. Phys. Lett. 75 (10) (1999)]. This method allows for the preparation of GaN substrates having a 2-inch (5 cm) diameter.
However, their quality is not sufficient for laser diodes, because the dislocation density continues to be approx. 107 to approx. 109/cm2. Recently, the method of Epitaxial Lateral OverGrowth (ELOG) has been used for reducing the dislocation density. In this method the GaN layer is first grown on a sapphire substrate and then a layer with SiO2 is deposited on it in the form of strips or a lattice. On the thus prepared substrate, in turn, the lateral growth of GaN may be carried out leading to a dislocation density of approx. 107/cm2.
The growth of bulk crystals of gallium nitride and other metals of group XIII (IUPAC, 1989) is extremely difficult. Standard methods of crystallization from melt and sublimation methods are not applicable because of the decomposition of the nitrides into metals and N2. In the High Nitrogen Pressure (HNP) method [“Prospects for high-pressure crystal growth of III–V nitrides” S. Porowski et al., Inst. Phys. Conf. Series, 137, 369 (1998)] this decomposition is inhibited by the use of nitrogen under the high pressure. The growth of crystals is carried out in molten gallium, i.e. in the liquid phase, resulting in the production of GaN platelets about 10 mm in size. Sufficient solubility of nitrogen in gallium requires temperatures of about 1500° C. and nitrogen pressures in the order of 15 kbar.
The use of supercritical ammonia has been proposed to lower the temperature and decrease the pressure during the growth process of nitrides. Peters has described the ammonothermal synthesis of aluminium nitride [J. Cryst. Growth 104, 411–418 (1990)]. R. Dwilinski et al. have shown, in particular, that it is possible to obtain a fine-crystalline gallium nitride by a synthesis from gallium and ammonia, provided that the latter contains alkali metal amides (KNH2 or LiNH2). The processes were conducted at temperatures of up to 550° C. and under a pressure of 5 kbar, yielding crystals about 5 μm in size [“AMMONO method of BN, AlN, and GaN synthesis and crystal growth”, Proc. EGW-3, Warsaw, Jun. 22–24, 1998, MRS Internet Journal of Nitride Semiconductor Research, http://nsr.mij.mrs.org/3/25]. Another supercritical ammonia method, where a fine-crystalline GaN is used as a feedstock together with a mineralizer consisting of an amide (KNH2) and a halide (KI) also provided for recrystallization of gallium nitride [“Crystal growth of gallium nitride in supercritical ammonia” J. W. Kolis et al., J. Cryst. Growth 222, 431–434 (2001)]. The recrystallization process conducted at 400° C. and 3.4 kbar resulted in GaN crystals about 0.5 mm in size. A similar method has also been described in Mat. Res. Soc. Symp. Proc. Vol. 495, 367–372 (1998) by J. W. Kolis et al. However, using these supercritical ammonia processes, no production of bulk monocrystalline was achieved because no chemical transport processes were observed in the supercritical solution, in particular no growth on seeds was conducted.
Therefore, there was a need for an improved method of preparing a gallium-containing nitride crystal.
The lifetime of optical semiconductor devices depends primarily on the crystalline quality of the optically active layers, and especially on the surface dislocation density. In case of GaN based laser diodes, it is beneficial to lower the dislocation density in the GaN substrate layer to less than 106/cm2, and this has been extremely difficult to achieve using the methods known so far. Therefore, there was a need for gallium-containing nitride crystals having a quality suitable for use as substrates for optoelectronics.
The subject matter of the present invention is recited in the appended claims. In particular, in one embodiment the present invention refers to a process for obtaining a gallium-containing nitride crystal, comprising the steps of:
In a second embodiment a process for preparing a gallium-containing nitride crystal is described which comprises the steps of:
A gallium-containing nitride crystal obtainable by one of these processes is also described. Further subject matter of the invention are a gallium-containing nitride crystal having a surface area of more than 2 cm2 and having a dislocation density of less than 106/cm2 and a gallium-containing nitride crystal having a thickness of at least 200 μm and a full width at half maximum (FWHM) of X-ray rocking curve from (0002) plane of 50 arcsec or less.
The invention also provides an apparatus for obtaining a gallium-containing nitride crystal comprising an autoclave 1 having an internal space and comprising at least one device 4, 5 for heating the autoclave to at least two zones having different temperatures, wherein the autoclave comprises a device which separates the internal space into a dissolution zone 13 and a crystallization zone 14.
In a yet another embodiment, a process for preparing a bulk monocrystalline gallium-containing nitride in an autoclave is disclosed, which comprises the steps of providing a supercritical ammonia solution containing gallium-containing nitride with ions of alkali metals, and recrystallizing said gallium-containing nitride selectively on a crystallization seed from said supercritical ammonia solution by means of the negative temperature coefficient of solubility and/or by means of the positive pressure coefficient of solubility.
A process for controlling recrystallization of a gallium-containing nitride in a supercritical ammonia solution which comprises steps of providing a supercritical ammonia solution containing a gallium-containing nitride as a gallium complex with ions of alkali metal and NH3 solvent in an autoclave and decreasing the solubility of said gallium-containing nitride in the supercritical ammonia solution at a temperature less than that of dissolving gallium-containing nitride crystal and/or at a pressure higher than that of dissolving gallium-containing nitride crystal is also disclosed.
In the present invention the following definitions apply:
Gallium-containing nitride means a nitride of gallium and optionally other element(s) of group XII (according to IUPAC, 1989). It includes, but is not restricted to, the binary compound GaN, ternary compounds such as AlGaN, InGaN and also AlInGaN (The mentioned formulas are only intended to give the components of the nitrides. It is not intended to indicate their relative amounts).
Bulk monocrystalline gallium-containing nitride means a monocrystalline substrate made of gallium-containing nitride from which e.g. optoelectronic devices such as LED or LD can be formed by epitaxial methods such as MOCVD and HVPE.
Supercritical solvent means a fluid in a supercritical state. It can also contain other components in addition to the solvent itself as long as these components do not substantially influence or disturb the function of the supercritical solvent. In particular, the solvent can contain ions of alkali metals.
Supercritical solution is used when referring to the supercritical solvent when it contains gallium in a soluble form originating from the dissolution of gallium-containing feedstock.
Dissolution of gallium-containing feedstock means a process (either reversible or irreversible) in which said feedstock is taken up into the supercritical solvent as gallium in a soluble form, possibly as gallium complex compounds.
Gallium complex compounds are complex compounds, in which a gallium atom is a coordination center surrounded by ligands, such as NH3 molecules or its derivatives, like NH2−, NH2−, etc.
Negative temperature coefficient of solubility means that the solubility of a respective compound is a monotonically decreasing function of temperature if all other parameters are kept constant. Similarly, positive pressure coefficient of solubility means that, if all other parameters are kept constant, the solubility is a monotonically increasing function of pressure. In our research we showed that the solubility of gallium-containing nitride in supercritical nitrogen-containing solvents, such as ammonia possesses a negative temperature coefficient and a positive pressure coefficient in temperatures ranging at least from 300 to 600° C. and pressures from 1 to 5.5 kbar.
Over-saturation of supercritical solution with respect to gallium-containing nitride means that the concentration of gallium in a soluble form in said solution is higher than that in equilibrium (i.e. it is higher than solubility). In the case of dissolution of gallium-containing nitride in a closed system, such an over-saturation can be achieved by either increasing the temperature and/or decreasing the pressure.
Spontaneous crystallization means an undesired process where nucleation and growth of the gallium-containing nitride from over-saturated supercritical solution take place at any site within an autoclave except at the surface of a crystallization seed where the growth is desired. Spontaneous crystallization also comprises nucleation and disoriented growth on the surface of crystallization seed.
Selective crystallization on a seed means a process of crystallization on a seed carried out without spontaneous crystallization.
Autoclave means a closed container which has a reaction chamber where the ammonobasic process according to the present invention is carried out.
The present invention can provide a gallium-containing nitride monocrystal having a large size and a high quality. Such gallium-containing nitride crystals can have a surface area of more than 2 cm2 and a dislocation density of less than 106/cm2. Gallium-containing nitride crystals having a thickness of at least 200 μm (preferably at least 500 μm) and a FWHM of 50 arcsec or less can also be obtained. Depending on the crystallization conditions, it possible to obtain gallium-containing nitride crystals having a volume of more than 0.05 cm3, preferably more than 0.1 cm3 using the processes of the invention.
As was explained above, the gallium-containing nitride crystal is a crystal of nitride of gallium and optionally other element(s) of Group XIII (the numbering of the groups is given according to the IUPAC convention of 1989 throughout this application). These compounds can be represented by the formula AlxGa1-x-yInyN, wherein 0≦x<1, 0≦y<1, 0≦x+y<1 (preferably 0≦x<0.5 and 0≦y<0.5). Although in a preferred embodiment, the gallium-containing nitride is gallium nitride, in a farther preferred embodiment part (e.g. up to 50 mol.-%) of the gallium atoms can be replaced by one or more other elements of Group XIII (especially Al and/or In).
The gallium-containing nitride may additionally include at least one donor and/or at least one acceptor and/or at least one magnetic dopant e.g. to alter the optical, electrical and magnetic properties of the substrate. Donor dopants, acceptor dopants and magnetic dopants are well-known in the art and can be selected according to the desired properties of the substrate. Preferably the donor dopants are selected from the group consisting of Si and O. As acceptor donors Mg and Zn are preferred. Any known magnetic dopant can be included into the substrates of the present invention. A preferred magnetic dopant is Mn and possibly also Ni and Cr. The concentrations of the dopants are well-known in the art and depend on the desired end application of the nitride. Typically the concentrations of these dopants range from 1017 to 1021/cm3. Instead of adding dopants as part of the feedstock into the autoclave, dopants can also be included into the gallium-containing nitride crystal from trace amounts of the autoclave material which dissolve during the process of the invention. For example, if the autoclave comprises a nickel alloy then nickel can be included into the gallium-containing nitride crystal.
Due to the preparation process the gallium-containing nitride crystal can also contain alkali elements, usually in an amount of more than about 0.1 ppm. Generally it is desired to keep the alkali elements content lower than 10 ppm, although it is difficult to specify what concentration of alkali metals in gallium-containing nitride has a disadvantageous influence on its properties.
It is also possible that halogens are present in the gallium-containing nitride. The halogens can be introduced either intentionally (as a component of the mineralizer) or unintentionally (from impurities of the mineralizer or the feedstock). It is usually desired to keep the halogen content of the gallium-containing nitride crystal in the range of about 0.1 ppm or less.
The process of the invention is a supercritical crystallization process, which includes at least two steps: a dissolution step at a first temperature and at a first pressure and a crystallization step at a second temperature and at a second pressure. Since generally high pressures and/or high temperatures are involved, the process according to the invention is preferably conducted in an autoclave. The two steps (i.e. the dissolution step and the crystallization step) can either be conducted separately or can be conducted at least partially simultaneously in the same reactor.
For conducting the two steps separately, the process can be conducted in one single reactor but the dissolution step is conducted before the crystallization step. In this embodiment the reactor can have the conventional construction of a single chamber. The process of the invention in the two-step embodiment can be conducted using constant pressure and two different temperatures or using constant temperature and two different pressures. It is also possible to use two different pressures and two different temperatures. The exact values of pressure and temperature should be selected depending on the feedstock, the specific nitride to be prepared and the solvent. Generally the pressure is in the range of 1 to 10 kbar, preferably 1 to 5.5 kbar and more preferably 1.5 to 3 kbar. The temperature is usually in the range of 100° C. to 800° C., preferably 300° C. to 600° C., more preferably 400° C. to 550° C. If two different pressures are employed, the difference in pressure should be from 0.1 kbar to 9 kbar, preferably from 0.2 kbar to 3 kbar. However, if the dissolution and crystallization are controlled by the temperature, the difference in temperature should be at least 1° C., and preferably from 5° C. to 150° C.
In a preferred embodiment, the dissolution step and the crystallization step are conducted at least partially simultaneously in the same container. For such an embodiment the pressure is practically uniform within the container, while the temperature difference between the dissolution zone and crystallization zone should be at least 1° C., and preferably is from 5° C. to 150° C. Furthermore, the temperature difference between the dissolution zone and crystallization zone should be controlled so as to ensure chemical transport in the supercritical solution, which takes place through convection.
A possible construction of a preferred container is given in
In a preferred embodiment of the invention, the process can be conducted in an apparatus comprising an autoclave 1 having an internal space and comprising at least one device 4, 5 for heating the autoclave to at least two zones having different temperatures, wherein the autoclave comprises a device which separates the internal space into a dissolution zone 13 and a crystallization zone 14 (hereinafter also referred to as “separating device” or “installation”). These two zones having different temperatures should preferably coincide with the dissolution zone 13 and the crystallization zone 14. The device which separates the internal space of the autoclave can be, for example, at least one baffle 12 having at least one opening 2. Examples are baffles having a central opening, circumferential openings or a combination thereof. The size of the opening(s) 2 should be large enough to allow transport between the zones but should be sufficiently small to maintain a temperature gradient in the reactor. The appropriate size of the opening(s) depends on the size and the construction of the reactor and can be easily determined by a person skilled in the art.
In one embodiment, two different heating devices can be employed, the position of which preferably corresponds to the dissolution zone 13 and the crystallization zone 14. However, it has been observed that transport of gallium in a soluble form from the dissolution zone 13 to the crystallization zone 14 can be further improved if a cooling means 6 is present between the first and the second heating devices and is located at approximately the position of the separating device. The cooling means 6 can be realized by liquid (e.g. water) cooling or preferably by fan cooling. The heating devices can be powered electrically, by either inductive or, preferably, by resistive heating means. Use of a heating-cooling-heating configuration gives wider possibilities in forming the desired temperature distribution within the autoclave. For example, it enables to obtain a low temperature gradients with in most of the crystallization zone 14 and a low temperature gradient within most of the dissolution zone 13, while achieving a high temperature gradient in the region of the baffle 12.
When the process of the present, invention is conducted a gallium-containing feedstock, an alkali metal-containing component, at least one crystallization seed and a nitrogen-containing solvent are provided in at least one container. In the preferred apparatus described above, the gallium-containing feedstock 16 is placed in the dissolution zone 13 and the at least one crystallization seed 17 is placed in the crystallization zone 14. The alkali metal-containing component is also preferably placed in the dissolution zone. Then the nitrogen-containing solvent is added to the container, which is then closed. Subsequently the nitrogen-containing solvent is brought into a supercritical state, e.g. by increasing pressure and/or heat.
In the present invention any materials containing gallium, which are soluble in the supercritical solvent under the conditions of the present invention, can be used as a gallium-containing feedstock. Typically the gallium-containing feedstock will be a substance or mixture of substances, which contains at least gallium, and optionally alkali metals, other Group XIII elements, nitrogen, and/or hydrogen, such as metallic Ga, alloys and inter-metallic compounds, hydrides, amides, imides, amido-imides, azides. Suitable gallium-containing feedstocks can be selected from the group consisting of gallium nitride GaN, azides such as Ga(N3)3, imides such as Ga2(NH)3, amido-imides such as Ga(NH)NH2, amides such as Ga(NH2)3, hydrides such as GaH3, gallium-containing alloys, metallic gallium and mixtures thereof. Preferred feedstocks are metallic gallium and gallium nitride and mixtures thereof. Most preferably, the feedstock is metallic gallium and gallium nitride. If elements of Group XIII other than gallium are to be present in the gallium-containing nitride crystal, corresponding compounds or mixed compounds including Ga and the other Group XIII element can be used. If the substrate is to contain dopants or other additives, precursors thereof can be added to the feedstock.
The form of the feedstock is not particularly limited and it can be in the form of one or more pieces or in the form of a powder. If the feedstock is in the form of a powder, care should be taken that individual powder particles are not transported from the dissolution zone to the crystallization zone, where they can cause irregular crystallization. It is preferable that the feedstock is in one or more pieces and that the surface area of the feedstock is larger than that of the crystallization seed.
The nitrogen-containing solvent employed in the present invention must be able to form a supercritical fluid, in which gallium can be dissolved in the presence of alkali metal ions. Preferably the solvent is ammonia, a derivative thereof or mixtures thereof. An example of a suitable ammonia derivative is hydrazine. Most preferably the solvent is ammonia. To reduce corrosion of the reactor and to avoid side-reactions, halogens e.g. in the form of halides are preferably not intentionally added into the container. Although traces of halogens may be introduced into the system in the form of unavoidable impurities of the starting materials, care should be taken to keep the amount of halogen as low as possible. Due to the use of a nitrogen-containing solvent such as ammonia it is not necessary to include nitride compounds into the feedstock. Metallic gallium (or aluminium or indium) can be employed as the feedstock while the solvent provides the nitrogen required for the nitride formation.
It has been observed that the solubility of gallium-containing feedstock, such as gallium and corresponding elements of Group XIII and/or their compounds, can be significantly improved by the presence of at least one type of alkali metal-containing component as a solubilization aid (“mineralizer”). Lithium, sodium and potassium are preferred as alkali metals, wherein sodium and potassium are more preferred. The mineralizer can be added to the supercritical solvent in elemental form or preferably in the form of its compound (such as a salt). Generally the choice of the mineralizer depends on the solvent employed in the process. According to our investigations, alkali metal having a smaller ion radius can provide lower solubility of gallium-containing nitride in the supercritical solvent than that obtained with alkali metals having a larger ion radius. For example, if the mineralizer is in the form of a compound such as a salt, it is preferably in the form of an alkali metal hydride such as MH, an alkali metal nitride such as M3N, an alkali metal amide such as MNH2, an alkali metal imide such as M2NH or an alkali metal azide such as MN3 (wherein M is an alkali metal). The concentration of the mineralizer is not particularly restricted and is selected so as to ensure adequate levels of solubility of both feedstock (the starting material) and gallium-containing nitride (the resulting product). It is usually in the range of 1:200 to 1:2, in the terms of the mols of the metal ion based on the mols of the solvent (molar ratio). In a preferred embodiment the concentration is from 1:100 to 1:5, more preferably 1:20 to 1:8 mols of the metal ion based on the mols of the solvent.
The presence of the alkali metal ions in the process can lead to alkali metal in the thus prepared substrates. It is possible that the amount of alkali metal is more than about 0.1 ppm, even more than 10 ppm. However, in these amounts the alkali metals do not detrimentally effect the properties of the substrates. It has been found that even at an alkali metal content of 500 ppm, the operational parameters of the substrate according to the invention are still satisfactory.
The dissolved feedstock crystallizes in the crystallization step under the low solubility conditions on the crystallization seed(s) which are provided in the container. The process of the invention allows bulk growth of monocrystalline gallium-containing nitride on the crystallization seed(s) and in particular leads to the formation of stoichiometric gallium-containing nitride in the form of a bulk monocrystalline layer on the crystallization seed(s).
Various crystals can be used as crystallization seeds in the present invention. however, it is preferred that the chemical and crystallographic constitution of the crystallization seeds is similar to those of the desired layer of bulk monocrystalline gallium-containing nitride. Therefore, the crystallization seed preferably comprises a crystalline layer of gallium-containing nitride. To facilitate crystallization of the dissolved feedstock, the dislocation density of the crystallization seed is preferably less than 106/cm2. Suitable crystallization seeds generally have a surface area of 8×8 mm2 or more and thickness of 100 μm or more, and can be obtained e.g. by HVPE.
After the starting materials have been introduced into the container and the nitrogen-containing solvent has been brought into its supercritical state, the gallium-containing feedstock is at least partially dissolved at a first temperature and a first pressure, e.g. in the dissolution zone of an autoclave. Gallium-containing nitride crystallizes on the crystallization seed (e.g. in the crystallization zone of an autoclave) at a second temperature and at a second pressure while the nitrogen-containing solvent is in the supercritical state, wherein the second temperature is higher than the first temperature and/or the second pressure is lower than the first pressure. If the dissolution and the crystallization steps take place simultaneously in the same container, the second pressure is essentially equal to the first pressure.
This is possible since the solubility of gallium-containing nitride under the conditions of the present invention shows a negative temperature coefficient and a positive pressure coefficient in the presence of alkali metal ions. Without wishing to be bound by theory, it is postulated that the following processes occur. In the dissolution zone, the temperature and pressure are selected such that the gallium-containing feedstock is dissolved and the nitrogen-containing solution is undersaturated with respect to gallium-containing nitride. In the crystallization zone, the temperature and pressure are selected such that the solution, although it contains approximately the same concentration of gallium as in the dissolution zone, is over-saturated with respect to gallium-containing nitride. Therefore, crystallization of gallium-containing nitride on the crystallization seed occurs. This is illustrated in
This theory is equally applicable for all gallium-containing nitrides, such as AlGaN. InGaN and AlInGaN as well as GaN (The mentioned formulas are only intended to give the components of the nitrides. It is not intended to indicate their relative amounts). In the case of nitrides other than gallium nitride aluminum and/or indium in a soluble form also have to be present in the supercritical solution.
In a preferred embodiment of the invention, the gallium-containing feedstock is dissolved in at least two steps. In this embodiment, the gallium-containing feedstock generally comprises two kinds of starting materials which differ in solubility. The difference in solubility can be achieved chemically (e.g. by selecting two different chemical compounds) or physically (e.g. by selecting two forms of the same compound having for example different surface areas, like microcrystalline powder and large crystals). In a preferred embodiment, the gallium-containing feedstock comprises two different chemical compounds such as metallic gallium and gallium nitride which dissolve at different rates. In a first dissolution step, the first component of the gallium-containing feedstock is substantially completely dissolved at a dissolution temperature and at a dissolution pressure in the dissolution zone. The dissolution temperature and the dissolution pressure, which can be set only in the dissolution zone or preferably in the whole container, are selected so that the second component of the gallium-containing feedstock and the crystallization seed(s) remain substantially undissolved. This first dissolution step results in an undersaturated or at most saturated solution (preferably undersaturated solution) with respect to gallium-containing nitride. For example, the dissolution temperature can be 100° C. to 350° C., preferably from 150° C. to 300° C. The dissolution pressure can be 0.1 kbar to 5 kbar, preferably from 0.1 kbar to 3 kbar.
Subsequently the conditions in the crystallization zone are set at a second temperature and at a second pressure so that over-saturation with respect to gallium-containing nitride is obtained and crystallization of gallium-containing nitride occurs on the at least one crystallization seed. Simultaneously the conditions in the dissolution zone are set at a first temperature and at a first pressure (preferably equal to the second pressure) so that the second component of the gallium-containing feedstock is now dissolved (second dissolution step). As explained above the second temperature is higher than the first temperature and/or the second pressure is lower than the first pressure so that the crystallization can take advantage of the negative temperature coefficient of solubility and/or of the positive pressure coefficient of solubility. Preferably the first temperature is higher than the dissolution temperature. During the second dissolution step and the crystallization step, the system should be in a stationary state so that the concentration of gallium in the supercritical solution remains substantially constant, i.e. approximately the same amount of gallium should be dissolved per unit of time as is crystallized in the same unit of time. This allows for the growth of gallium-containing nitride crystals of especially high quality and large size.
Typical pressures for the crystallization step and the second dissolution step are in the range of 1 to 10 kbar, preferably 1 to 5.5 kbar and more preferably 1.5 to 3 kbar. The temperature is generally in the range of 100 to 800° C., preferably 300 to 600° C., more preferably 400 to 550° C. The difference in temperature should be at least 1° C., and is preferably from 5° C. to 150° C. As explained above, the temperature difference between the dissolution zone and crystallization zone should be controlled so as to ensure chemical transport in the supercritical solution, which takes place through convection.
In the process of the invention, the crystallization should take place selectively on the crystallization seed and not on a wall of the container. Therefore, the over-saturation extent with respect to the gallium-containing nitride in the supercritical solution in the crystallization zone should be controlled so as to be below the spontaneous crystallization level where crystallization takes place on a wall of the autoclave and/or disoriented growth occurs on the seed, i.e. the level at which spontaneous crystallization occurs. This can be achieved by adjusting the chemical transport rate and/or the crystallization temperature and/or crystallization pressure. The chemical transport is related on the speed of a convective flow from the dissolution zone to the crystallization zone, which can be controlled by the temperature difference between the dissolution zone and the crystallization zone, the size of the opening(s) of baffle(s) between the dissolution zone and the crystallization zone etc.
The performed tests showed that the best bulk monocrystalline gallium nitride obtained had a dislocation density close to 104/cm2 and simultaneously a FWHM of X-ray rocking curve from (0002) plane below 60 arcsec. These crystals possess an appropriate quality and durability for optical semiconductor devices. The gallium-containing nitride of the present invention typically has a wurzite structure.
Feedstock material for use in the present invention can also be prepared using a method similar to those described above. The method involves the steps of:
In this embodiment the comments given above with respect to the individual components, process parameters, etc. also apply. Preferably during the crystallization step in this embodiment the conditions in the whole container are set at the second temperature and the second pressure.
Gallium-containing nitride exhibits good solubility in a supercritical nitrogen-containing solvent (e.g. ammonia), provided alkali metals or their compounds, such as KNH2, are introduced into it.
ΔSm≈(∂Sm/∂T)|p,xΔT+(∂Sm/∂p)|T,xΔp+(∂Sm/∂x)|T,pΔx,
where the partial differentials (e.g. (∂Sm/∂T)|p,x) determine the behavior of Sm with variation of its parameters (e.g. T). In this specification the partial differentials are called “coefficients” (e.g. (∂Sm/∂T)|p,x is a “temperature coefficient of solubility” or “temperature coefficient”).
The diagram shown in
The process according to invention allows the growth of bulk monocrystalline gallium-containing nitride crystals on the crystallization seed and leads in particular to the formation of stoichiometric gallium-containing nitride, obtained in the form of a bulk monocrystalline layer grown on a gallium-containing nitride crystallization seed. Since such a monocrystal is obtained in a supercritical solution that contains ions of alkali metals, it can contain alkali metals in a quantity higher than 0.1 ppm. Because it is desired to maintain a purely basic character of the supercritical solution, mainly in order to avoid corrosion of the apparatus, halides are preferably not intentionally introduced into the solvent. The process of the invention can also provide a bulk monocrystalline gallium-containing nitride crystal in which part of the gallium, e.g. from 5 to 50 mol-% may be substituted by Al and/or In. Moreover, the bulk monocrystalline gallium-containing nitride crystal may be doped with donor and/or acceptor and/or magnetic dopants. These dopants can modify optical, electric and magnetic properties of the gallium-containing nitride crystal. With respect to the other physical properties, the bulk monocrystalline gallium-containing nitride crystal can have a dislocation density below 106/cm2, preferably below 105/cm2; or most preferably below 104/cm2. Besides, the FWHM of the X-ray rocking curve from (0002) plane can be below 600 arcsec, preferably below 300 arcsec, and most preferably below 60 arcsec. The best bulk monocrystalline gallium nitride obtained may have a dislocation density lower than 104/cm2 and simultaneously a FWHM of the X-ray rocking curve from (0002) plane below 60 arcsec.
Due to their good crystalline quality the gallium-containing nitride crystals obtained in the present invention may be used as a substrate material for optoelectronic semiconductor devices based on nitrides, in particular for laser diodes.
The following examples are intended to illustrate the invention and should not be construed as being limiting.
The dislocation density can be measured by th eso-called EPD method (Etch Pit Density) and subsequent evaluation using a microscope
The FWHM of the X-ray rocking curve can be determined by X-ray diffraction analysis.
Since it is not possible to readily measure the temperature in an autoclave while in use under supercritical conditions, the temperature in the autoclave was estimated by the following method. The outside of the autoclave is equipped with thermocouples near the dissolution zone and the crystallization zone. For the calibration, additional thermocouples were introduced into the inside of the empty autoclave in the dissolution zone and the crystallization zone. The empty autoclave was then heated stepwise to various temperatures and the values of the temperature of the thermocouples inside the autoclave and outside the autoclave were measured and tabulated. For example, if the temperature of the crystallization zone is determined to be 500° C. and the temperature of the dissolution zone is 400° C. inside the empty autoclave when the temperature measured by the outside thermocouples are 480° C. and 395° C., respectively. It is assumed that under supercritical conditions the temperatures in the crystallization/dissolution zones will also be 500° C./400° C. when temperatures of 480° C./395° C. are measured by the outside thermocouples. In reality, the temperature difference between the two zones can be lower due to effective heat transfer through the supercritical solution.
Two crucibles were placed into a high-pressure autoclave having a volume of 10.9 cm3. The autoclave was manufactured according to a known design [H. Jacobs, D. Schmidt, Current Topics in Materials Science, vol. 8, ed. E. Kaldis (North-Holland, Amsterdam, 1981); 381]. One of the crucibles contained 0.4 g of gallium nitride in the form of 0.1 mm thick plates produced by the HVPE method as feedstock, while the other contained a gallium nitride seed of a double thickness weighing 0.1 g. The seed was also obtained by the HVPE method. Further, 0.72 g of metallic potassium of 4N purity was placed in the autoclave, the autoclave was filled with 4.81 g of ammonia and then closed. The autoclave was put into a furnace and heated to a temperature of 400° C. The pressure within the autoclave was 2 kbar. After 8 days the temperature was increased to 500° C., while the pressure was maintained at the 2 kbar level and the autoclave was maintained under these conditions for another 8 days.(
Two crucibles were put into the above-mentioned high-pressure autoclave having a volume of 10.9 cm3. One of the crucibles contained 0.44 g of gallium nitride in the form of 0.1 mm thick plates produced by the HVPE method as feedstock, and the other contained a gallium nitride seed of a double thickness weighing 0.1 g, also obtained by the HVPE method. Further, 0.82 g of metallic potassium of 4N purity was placed in the autoclave, the autoclave was filled with 5.43 g of ammonia and then closed. The autoclave was put into a furnace and heated to a temperature of 500° C. The pressure within the autoclave was 3.5 kbar. After 2 days the pressure was lowered to 2 kbar, while the temperature was maintained at the 500° C. level and the autoclave was maintained under these conditions for another 4 days (
Two crucibles were placed into the above-mentioned high-pressure autoclave having a volume of 10.9 cm3. One of the crucibles contained 0.3 g of the feedstock in the form of metallic gallium of 6N purity and the other contained a 0.1 g gallium nitride seed obtained by the HVPE method. Further, 0.6 g of metallic potassium of 4N purity was placed in the autoclave; the autoclave was filled with 4 g of ammonia and then closed. The autoclave was put into a furnace and heated to a temperature of 200° C. After 2 days the temperature was increased to 500° C., while the pressure was maintained at the 2 kbar level and the autoclave was maintained in these conditions for further 4 days (
This is an example of a process, in which the dissolution and crystallization steps take place simultaneously (recrystallization process). In this example and all the following an apparatus is used which is schematically shown in
An amount of 3.0 g of gallium nitride produced by the HVPE method was placed in the high-pressure autoclave described above, which was set in the horizontal position. This gallium nitride had the form of plates of about 0.2 mm thickness, and it was distributed (roughly uniformly) in equal portions in the dissolution zone 13 and the crystallization zone 14. The portion placed in the dissolution zone 13 played the role of feedstock, whereas the portion placed in the crystallization zone 14 played the role of crystallization seeds. Metallic potassium of 4N purity was also added in a quantity of 2.4 g. Then the autoclave 1 was filled with 15.9 g of ammonia (5N); closed, put into a set of furnaces 4 and heated to a temperature of 450° C. The pressure inside the autoclave 1 was approx. 2 kbar. During this stage, which lasted one day, partial dissolution of gallium nitride was carried out in both zones. Then the temperature of the crystallization zone 14 was increased to 500° C. while the temperature of the dissolution zone 13 was lowered to 400° C. and the autoclave 1 was kept in these conditions for 6 more days (
The above-mentioned high pressure autoclave 1 having a volume of 35.6 cm3 was charged with feedstock in the form of a 3.0 g pellet of sintered gallium nitride (introduced into the dissolution zone 13), two seeds of gallium nitride obtained by the HVPE method and having the form of plates having a thickness of 0.4 mm and a total weight of 0.1 g (introduced into the crystallization zone 14), as well as with 2.4 g of metallic potassium of 4N purity. Then the autoclave was filled with 15.9 g of ammonia (5N) and closed. The autoclave 1 was then put into a set of furnaces 4 and heated to 450° C. The pressure inside the autoclave was about 2 kbar. After an entire day the temperature of the crystallization zone 14 was raised to 480° C., while the temperature of the dissolution zone 13 was lowered to 420° C. and the autoclave was maintained under these conditions for 6 more days (see
The above-mentioned high pressure autoclave 1 having a volume of 35.6 cm3 (see
The above-mentioned high pressure autoclave 1 having a volume of 35.6 cm3 (see
An amount of 1.0 g of gallium nitride produced by the HVPE method was put into the dissolution zone 13 of the high-pressure autoclave 1 having a volume of 35.6 cm3. In the crystallization zone 14 of the autoclave, a crystallization seed of gallium nitride having a thickness of 100 μm and a surface area of 2.5 cm2, obtained by the HVPE method, was placed. Then the autoclave was charged with 1.2 g of metallic gallium of 6N purity and 2.2 g of metallic potassium of 4N purity. Subsequently, the autoclave 1 was filled with 15.9 g of ammonia (5N), closed, put into a set of furnaces 4 and heated to a temperature of 200° C. After 3 days—during which period metallic gallium was dissolved in the supercritical solution—the temperature was increased to 450° C. which resulted in a pressure of about 2.3 kbar. The next day the crystallization zone temperature was increased to 500° C. while the temperature of the dissolution zone 13 was lowered to 370° C. and the autoclave 1 was kept in these conditions for the next 20 days (see
An amount of 3.0 g of gallium nitride in the form of a sintered gallium nitride pellet was put into the dissolution zone 13 of high-pressure autoclave 1 having a volume of 35.6 cm3 (see
An amount of 0.5 g of gallium nitride plates having an average thickness of about 120 μm, produced by the HVPE method, were put into the dissolution zone 13 of high-pressure autoclave 1 having a volume of 35.6 cm3. In the crystallization zone 14 of the autoclave, three crystallization seeds of gallium nitride obtained by the HVPE method were placed. The crystallization seeds had a thickness of about 120 μm and a total surface area of 1.5 cm2. Then the autoclave was charged with 0.41 g of metallic lithium of 3N purity. Subsequently, the autoclave 1 was filled with 14.4 g of ammonia (5N), closed, put into a set of furnaces 4 and heated so that the temperature of the crystallization zone 14 was increased to 550° C. and the temperature of the dissolution zone 13 was increased to 450° C. The resulting pressure was about 2.6 kbar. The autoclave 1 was kept in these conditions for the next 8 days (see
An amount of 0.5 g of gallium nitride having an average thickness of about 120 μm, produced by the HVPE method, was placed into the dissolution zone 13 of hill-pressure autoclave 1 having a volume of 35.6 cm3. In the crystallization zone 14 of the autoclave, three crystallization seeds of gallium nitride obtained by the HVPE method were placed. The crystallization seeds had a thickness of 120 μm and a total surface area of 1.5 cm2. Then the autoclave was charged with 0.071 g of metallic gallium of 6N purity and 1.4 g of metallic sodium of 3N purity. Subsequently, the autoclave 1 was filled with 14.5 g of ammonia (5N), closed, put into a set of furnaces 4 and heated to a temperature of 200° C. After 1 day—during which period metallic gallium was dissolved in the supercritical solution—the autoclave 1 was heated so that the temperature in the crystallization zone was increased to 500° C., while the temperature in the dissolution zone was increased to 400° C. The resulting pressure was about 2.3 kbar. The autoclave 1 was kept in these conditions for the next 8 days (see
An amount of 0.5 g of gallium nitride having an average thickness of about 120 μm, produced by the HVPE method, was placed into the dissolution zone 13 of the high-pressure autoclave 1 having a volume of 35.6 cm3. In the crystallization zone 14 of the autoclave, three crystallization seeds of gallium nitride obtained by the HVPE method were placed. The crystallization seeds had a thickness of 120 μm and a total surface area of 1.5 cm2. Then the autoclave was charged with 0.20 g of gallium amide and 1.4 g of metallic sodium of 3N purity. Subsequently, the autoclave 1 was filled with 14.6 g of ammonia (5N), closed, put into a set of furnaces 4 and heated to a temperature of 200° C. After 1 day—during which period gallium amide was dissolved in the supercritical solution—the autoclave 1 was heated so that the temperature in the crystallization zone was increased to 500° C., while the temperature in the dissolution zone was increased to 400° C. The resulting pressure was about 2.3 kbar. The autoclave 1 was kept in these conditions for the next 8 days (see also
One crucible was placed into the above-mentioned high-pressure autoclave having a volume of 10.9 cm3. The crucible contained 0.3 g of the feedstock in the form of metallic gallium of 6N purity. Also three gallium-nitride seeds having a thickness of about 0.5 mm and a total mass of 0.2 g, all obtained by the HVPE method, were suspended within the autoclave. Further, 0.5 g of metallic sodium of 3N purity was placed in the autoclave; the autoclave was filled with 5.9 g of ammonia and then closed. The autoclave was put into a furnace and heated to a temperature of 200° C., where the pressure was about 2.5 kbar. After 1 day the temperature was increased to 500° C., while the pressure increased up to 5 kbar and the autoclave was maintained in these conditions for further 2 days (
The monocrystalline gallium nitride layers have a wurzite structure like in all of the other examples.
| Number | Date | Country | Kind |
|---|---|---|---|
| 347918 | Jun 2001 | PL | national |
| 350375 | Oct 2001 | PL | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB02/04185 | 5/17/2002 | WO | 00 | 12/5/2003 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO02/101120 | 12/19/2002 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5096860 | Nadkarni | Mar 1992 | A |
| 5456204 | Dimitrov et al. | Oct 1995 | A |
| 5589153 | Garces et al. | Dec 1996 | A |
| 5679965 | Schetzina | Oct 1997 | A |
| 5780876 | Hata | Jul 1998 | A |
| 5868837 | DiSalvo et al. | Feb 1999 | A |
| 5928421 | Yuri et al. | Jul 1999 | A |
| 6046464 | Schetzina | Apr 2000 | A |
| 6067310 | Hashimoto et al. | May 2000 | A |
| 6156581 | Vaudo et al. | Dec 2000 | A |
| 6172382 | Nagahama et al. | Jan 2001 | B1 |
| 6177057 | Purdy | Jan 2001 | B1 |
| 6249534 | Itoh et al. | Jun 2001 | B1 |
| 6252261 | Usui et al. | Jun 2001 | B1 |
| 6329215 | Porowski et al. | Dec 2001 | B1 |
| 6372041 | Cho et al. | Apr 2002 | B1 |
| 6399500 | Porowski et al. | Jun 2002 | B1 |
| 6399966 | Tsuda et al. | Jun 2002 | B1 |
| 6423984 | Kato et al. | Jul 2002 | B1 |
| 6447604 | Flynn et al. | Sep 2002 | B1 |
| 6459712 | Tanaka et al. | Oct 2002 | B2 |
| 6468882 | Motoki et al. | Oct 2002 | B2 |
| 6488767 | Xu et al. | Dec 2002 | B1 |
| 6509651 | Matsubara et al. | Jan 2003 | B1 |
| 6586762 | Kozaki | Jul 2003 | B2 |
| 6593589 | Osinski et al. | Jul 2003 | B1 |
| 6614824 | Tsuda et al. | Sep 2003 | B2 |
| 6677619 | Nagahama et al. | Jan 2004 | B1 |
| 6686608 | Takahira | Feb 2004 | B1 |
| 6711191 | Kozaki et al. | Mar 2004 | B1 |
| 6720586 | Kidoguchi et al. | Apr 2004 | B1 |
| 6858882 | Tsuda et al. | Feb 2005 | B2 |
| 6924512 | Tsuda et al. | Aug 2005 | B2 |
| 20010008656 | Tischler et al. | Jul 2001 | A1 |
| 20010022154 | Cho et al. | Sep 2001 | A1 |
| 20020014631 | Iwata et al. | Feb 2002 | A1 |
| 20020031153 | Niwa et al. | Mar 2002 | A1 |
| 20020047113 | Ohno et al. | Apr 2002 | A1 |
| 20020063258 | Motoki | May 2002 | A1 |
| 20020078881 | Cuomo et al. | Jun 2002 | A1 |
| 20030143771 | Kidoguchi et al. | Jul 2003 | A1 |
| 20040031978 | D'Evelyn et al. | Feb 2004 | A1 |
| 20040139912 | Dwilinski et al. | Jul 2004 | A1 |
| 20040244680 | Dwilinski et al. | Dec 2004 | A1 |
| 20040255840 | Dwilinski et al. | Dec 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| 1289867 | Apr 2001 | CN |
| 1065289 | May 2001 | CN |
| 0 716 457 | Jun 1996 | EP |
| 0 711 853 | Sep 1999 | EP |
| 0 949 731 | Oct 1999 | EP |
| 0 973 207 | Jan 2000 | EP |
| 1 088 914 | Apr 2001 | EP |
| 2 796 657 | Jan 2001 | FR |
| 2 326 160 | Dec 1998 | GB |
| 2 333 521 | Jul 1999 | GB |
| 2-137287 | May 1990 | JP |
| 7-22692 | Mar 1995 | JP |
| 7-165498 | Jun 1995 | JP |
| 7-249830 | Sep 1995 | JP |
| 8-250802 | Sep 1996 | JP |
| 9-134878 | May 1997 | JP |
| 10-7496 | Jan 1998 | JP |
| 10-70079 | Mar 1998 | JP |
| 10-70338 | Mar 1998 | JP |
| 11-54847 | Feb 1999 | JP |
| 11-307813 | Nov 1999 | JP |
| 2000-82863 | Mar 2000 | JP |
| 2000-82867 | Mar 2000 | JP |
| 2000-216494 | Aug 2000 | JP |
| 2000-327495 | Nov 2000 | JP |
| 2001-85737 | Mar 2001 | JP |
| 2001-342100 | Dec 2001 | JP |
| WO 9855671 | Dec 1998 | WO |
| WO 0124284 | Apr 2001 | WO |
| WO 01024921 | Apr 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040139912 A1 | Jul 2004 | US |