Patent Application
20070091288
The present disclosure relates generally to lenses for photolithography systems and, more particularly, to an objective lens for use in a liquid immersion lithography process.
The semiconductor integrated circuit (IC) industry has experienced rapid growth. Technological advances in IC materials and design have produced generations of ICs where each generation has more complex circuits than the previous generation. However, these advances have increased the complexity of processing and manufacturing ICs and, for these advances to be realized, similar developments in IC processing and manufacturing have been needed.
The growth of the semiconductor IC industry is driven by Moore's law: “The complexity of minimum component cost has increased at a rate of roughly a factor of two per year”. In the course of integrated circuit evolution, functional density (i.e., the number of interconnected devices per chip area) has generally increased while feature size (i.e., the smallest component or line that can be created using a fabrication process) has decreased. This scaling down process generally provides benefits by increasing production efficiency and lowering associated costs.
One of the factors enabling the continued minimization of feature size is improvement in photolithography and its ability to print smaller features. The minimum feature size in an optical lithography system may be determined in part by diffraction, which is related to the wavelength of light and the medium through which the light shines. Accordingly, one approach to reducing feature size and improving resolution is to use light with a shorter wavelength. Another approach is to use a medium between the lens and the substrate other than air. Since the index of refraction of a medium (referred to as ‘n’) is larger than one, the wavelength in the medium is reduced by the factor of n. This may improve resolution.
One such method of enhancing resolution using a non-air medium is referred to as immersion lithography. Depending on the inserted medium, immersion lithography may be classified as solid immersion lithography or liquid immersion lithography. However, in liquid immersion lithography, there may be chemical reaction and physical damage between an optical lens used during lithography and the liquid used for immersion. Such a chemical reaction or other mechanism may damage the optical system and degrade the system's resolution.
Accordingly, what is needed is an improved optical lens and method of manufacturing such a lens.
The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.
The present disclosure relates generally to lenses for photolithography systems and, more particularly, to an objective lens for use in a liquid immersion lithography process. It is understood, however, that the following disclosure provides many different embodiments, or examples, for implementing different features of the invention. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.
Referring to
The light source 110 may be any suitable light source. For example, the light source 110 may be a mercury lamp having a wavelength of 436 nm (G-line) or 365 nm (I-line); a Krypton Fluoride (KrF) excimer laser with wavelength of 248 nm; an Argon Fluoride (ArF) excimer laser with a wavelength of 193 nm; a Fluoride (F2) excimer laser with a wavelength of 157 nm; or other light sources having a wavelength below approximately 100 nm.
In lithography systems with wavelengths below approximately 157 nm, various system components may demonstrate a high level of absorption. This may be solved by some extent with the use of reflective optics, but these optics may introduce other challenges. Immersion lithography may be used to reduce feature sizes in lithography while addressing some of the concerns with wavelengths below 157 nm. It is understood that in the above description of light sources, each light source may have a certain wavelength distribution, or line width, rather than an exact single wavelength. For example, the I-line (e.g., 365 nm) wavelength of the mercury lamp may not be exactly 365 nm, but may be centered at approximately 365 nm with a range of varying wavelengths extending above and below 365 nm. This range may be used to determine a minimum possible line width during photolithography, with less variation from the desired 365 nm wavelength resulting in a thinner line width.
The illumination system (e.g., the condenser) 120 may comprise a single lens or may comprise a lens system having multiple lenses and/or other lens components. For example, the illumination system may comprise microlens arrays, shadow masks, or other structures designed to aid in directing light from the light source 110 onto the photomask 130.
The photomask 130 may comprise a transparent substrate and an absorption layer. The transparent substrate may use fused silica (SiO2) relatively free of defects, such as borosilicate glass and soda-lime glass. The absorption layer may be formed using a number of different processes and materials, such as depositing a metal film made with chromium (Cr) oxide and iron oxide, or an inorganic film made with MoSi, ZrSiO, SiN, and/or TiN. The absorption layer may be patterned to have one or more openings through which light may travel without being absorbed by the absorption layer.
The objective lens 140 may comprise a single lens or a plurality of lens elements illustrated as 170, 172, 174. As will be described later in greater detail, each lens element may include a transparent substrate and may have an anti-reflection coating (ARC) on at least one surface of each lens element. The transparent substrate may be a conventional objective lens, and may be made of fused silica (SiO2), calcium-fluoride (CaF2), lithium fluoride (LiF), or barium fluoride (BaF2). The materials used for each lens element may be chosen based on the wavelength of light used in the lithography process to lessen absorption and scattering.
At least one lens element may also have a protective coating (PC) to minimize or prevent corrosion (e.g., a chemical reaction between the lens 140 and the immersion liquid 150), erosion (e.g., a physical or mechanical bubble of liquid at the lens), dissolution of the lens and liquid, or other of the objective lens 140 by the immersion liquid 150. If the immersion liquid 150 is corrosive, the lens element 170 may have an asymmetric coating. For example, the lens element 170 may have an ARC on one surface and a protective coating on the surface that is proximate to or in contact with the immersion liquid 150. In the present example, the lens element 170 of the objective lens 140 may be in direct contact with the immersion liquid 150. The immersion liquid 150 may be selected both for optical qualities and for compatibility with the semiconductor substrate 160. For example, the immersion liquid 150 may be selected to minimize chemical reactions, scattering, and light absorption, as well as to be relatively bubble-free and thermally stable during lithography. Water may be used, as may other liquids.
Due to the possible high index of the immersion liquid 150, such as with an organic fluid or a non-water containing fluid, the friction between the immersion liquid 150 and one or more of the lens elements could be relatively high. Moreover, lens cleaning may be necessary by using various solvents to remove the residue of fluid, e.g., a by-product from the photoresist and/or other particles from the process. A protective coating layer can be used for lens protection from any mechanical and/or chemical interaction with the immersion liquid 150 or other material.
The semiconductor substrate 160 may be a wafer comprising an elementary semiconductor such as crystal silicon, polycrystalline silicon, amorphous silicon, germanium, and diamond, a compound semiconductor such as silicon carbide and gallium arsenic, an alloy semiconductor such as SiGe, GaAsP, AlInAs, AlGaAs, and GaInP, or any combination thereof.
Referring now to
The PC 220 may be formed either directly on or proximate to (if there are intervening layers) the transparent substrate 210. The material forming the PC 220 may be selected to adhere relatively well to the transparent substrate 210, to be transparent to the light used during lithography, and to be chemically stable with the immersion liquid 150. It is understood that the material may change depending on the particular immersion liquid used during lithography. In the present example, chemically stable indicates that the chemical reaction rate between the PC 220 and the immersion liquid is less than 10−5 per hour, where the chemical reaction rate is defined as the decrease of the relative thickness of the PC 220 per hour. The chemical stability of the PC 220 in the immersion liquid 150 enables the PC to protect the lens element 170 of the objective lens 140 from damage by the immersion liquid or corresponding substances. Accordingly, the resolution of lithography may be maintained while prolonging the lifetime of the objective lens 140.
As one example, SiO2 may be used for the PC 220 when the transparent substrate 210 is formed of CaF2, LiF, or BrF2. SiO2 is compatible with water used as the immersion liquid 150. Other materials that may be used for the PC 220 include indium tin oxide (ITO), polymer, and the non-photo-active resin of a photoresist.
In the present example, the thickness of the PC 220 may be less than 1000 μm, and the surface flatness of the PC 220 may be controlled so that the variation of the surface is less than the half of the wavelength of the light used in lithography. In some embodiments, the thickness of the PC 220 may be increased within a range of up to approximately 1 mm, enabling the PC 220 to perform both protective and anti-reflection functions. The deposition of the PC 220 may be implemented by spin-on coating, chemical vapor deposition (CVD), atomic layer deposition (ALD), physical vapor deposition (PVD) such as sputtering and evaporation, or epitaxy growth.
Referring now to
Referring now to
Referring now to
Referring to
In step 620, a material for an PC (e.g., the PC 220 of
In step 630, the PC is formed on one surface of the lens element 170. The PC may be formed either directly on or proximate to (if there are intervening layers) the transparent substrate. The material forming the PC may be selected to adhere relatively well to the transparent substrate, to be transparent to the light used during lithography, and to be chemically stable with the immersion liquid 150. It is understood that the material may change depending on the particular immersion liquid used during lithography. In the present example, chemically stable indicates that the chemical reaction rate between the PC and the immersion liquid is less than 10−5 per hour, where the chemical reaction rate is defined as the decrease of the relative thickness of the PC 220 per hour.
In the present example, the thickness of the PC may be less than 1000 μm, and the surface flatness of the PC may be controlled so that the variation of the surface is less than the half of the wavelength of the light used in lithography. In some embodiments, the thickness of the PC may be increased within a range of up to approximately 1 mm, enabling the PC to perform anti-corrosion, anti-erosion, anti-dissolution, anti-reflection and other functions. The formed PC may be planarized through processing such as polishing.
In step 640, an ARC (e.g., the ARC 310 of
In step 650, the lens element 170 with its PC and ARC may be assembled with other lens elements into an objective lens. It is understood that such assembly may not be required. For example, the lens element may be used alone or may already be part of an objective lens when one or both of the PC and ARC are formed. Other lens elements used with the lens element 170 may or may not have an PC or an ARC.
Referring to
At step 720, the immersion liquid is dispensed between the substrate to be patterned and the objective lens, with the objective lens positioned with the PC close to or in contact with the immersion liquid. In some embodiments, the objective lens may be at least partly held in position by the surface tension of the immersion liquid.
At step 730, the objective lens is illuminated to perform lithography on the substrate. The illuminating light may include a predetermined wavelength of light in the range between about 100 nm and about 500 nm. For example, the illuminating light may be from a mercury lamp with a wavelength of 436 nm (G-line) or 365 nm (I-line); a Krypton Fluoride (KrF) excimer laser with a wavelength of 248 nm; an Argon Fluoride (ArF) excimer laser with a wavelength of 193 nm; or a Fluoride (F2) excimer laser with a wavelength of 157 nm. Alternatively, a 193 nm ArF excimer laser may be used in liquid immersion lithography to enhance the resolution of the pattern.
Due to the possible high index fluid, e.g., organic fluid or non-water containing fluid may be adopted in future, the friction between the immersion liquid 150 and the lens element 170 can be relatively higher. Moreover, lens cleaning may be necessary by using various solvents to remove the residue of fluid, such as the by-product from PR, the immersion fluid 150 and/or other particles from the lithography process. The protective coating (PC) 220 can be used for lens protection from the mechanical/chemical interaction with fluids and/or other material. In addition or in the alternative, the PC 220 can also be used to prevent corrosion.
The present disclosure has been described relative to a preferred embodiment. Improvements or modifications that become apparent to persons of ordinary skill in the art only after reading this disclosure are deemed within the spirit and scope of the application. It is understood that several modifications, changes and substitutions are intended in the foregoing disclosure and in some instances some features of the invention will be employed without a corresponding use of other features. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the scope of the invention.
The present disclosure is a continuation-in-part of U.S. Ser. No. 10/702,664 filed Nov. 6, 2003, the contents of which are hereby incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10702664 | Nov 2003 | US |
| Child | 11548551 | Oct 2006 | US |