The present invention relates to magnetic random access memory, and more specifically, to materials optimized for spin-torque memory having a seed layer and free magnetic layer for perpendicular anisotropy.
A spin torque magnetic random access memory (MRAM) device uses a two terminal spin-torque based memory element including a pinned layer, a tunnel barrier layer and a free layer in a magnetic tunnel junction (MTJ) stack as shown in
The present invention provides magnetic tunnel junction (MTJ) stacks of optimal material choices which have perpendicular magnetic anisotropy (PMA) and provide high magnetoresistance (MR) with a tunnel barrier layer of the MTJ stack and can be grown at room temperature.
According to an embodiment of the present invention a magnetic layer is provided. The magnetic layer includes a seed layer comprising at least tantalum and a free magnetic layer comprising at least iron. The free magnetic layer is grown on top of the seed layer and the free magnetic layer is perpendicularly magnetized.
According to one embodiment of the present invention, a MTJ stack is provided. The MTJ stack includes a seed layer comprising at least tantalum and a free magnetic layer comprising at least iron. The free magnetic layer is grown on top of the seed layer and the free magnetic layer is perpendicularly magnetized.
According to another embodiment of the present invention, a spin-torque based magnetic random access memory (MRAM) device is provided. The spin-torque based MRAM device includes a MTJ stack including a seed layer comprising tantalum and a free magnetic layer comprising at least iron. The free magnetic layer is grown on top of the seed layer and the free magnetic layer is perpendicularly magnetized.
According to yet another embodiment of the present invention, a spin-torque MRAM device is provided. The spin-torque based MRAM includes a multi-layer MTJ stack that includes a plurality of seed layers each comprising tantalum and a plurality of free magnetic layers comprising at least iron wherein each free magnetic layer of the plurality of free magnetic layers is grown on top of each seed layer of the plurality of seed layers in a stacked manner and each free magnetic layer of the plurality of free magnetic layers is perpendicularly magnetized.
Additional features and advantages are realized through the techniques of the present invention. Other embodiments and aspects of the invention are described in detail herein and are considered a part of the claimed invention. For a better understanding of the invention with the advantages and the features, refer to the description and to the drawings.
The subject matter which is regarded as the invention is particularly pointed out and distinctly claimed in the claims at the conclusion of the specification. The forgoing and other features, and advantages of the invention are apparent from the following detailed description taken in conjunction with the accompanying drawings in which:
With reference now to
According to an embodiment of the present invention, the free magnetic layer 104 may further include at least one of cobalt (Co) and boron (B). Therefore, the free magnetic layer may include CoFeB, for example. The CoFeB may be of a variety of compositions. For example, the CoFeB composition may include 60% of Co, 20% of Fe and 20% of B. According to an embodiment of the present invention, Co is less than approximately 90% of the composition of the free magnetic layer 104. The composition range of the Fe is between 10% and 100%; and the B is less than approximately 40% of the composition of the free magnetic layer 104. The present invention is not limited to the use of CoFeB; other suitable elements may be utilized. According to an embodiment of the present invention, a predetermined thickness of the free magnetic layer 104 ranges from approximately 0.5 nanometers (nm) to approximately 1.5 nanometers (nm).
The present invention discloses examples of optimal MTJ stack material choices that provide switching characteristics required for integrated memory applications of a spin-torque switched MTJ. For example, according to one embodiment of the present invention, the free magnetic layer 104 has a high magnetoresistance (MR). According to another embodiment of the present invention, the free magnetic layer 104 is in a body-centered cubic (BCC) structure. According to another embodiment of the present invention, the free magnetic layer 104 is not in the L10 crystal structure (i.e., phase).
According to an embodiment of the present invention, a tunnel barrier layer is formed on top of the free magnetic layer 104 and will now be described with reference to
Further, according to the current embodiment of the present invention, an interface layer may be grown between the seed layer 102 and the free magnetic layer 104 as shown in
As shown in
According to an embodiment of the present invention, a multilayer MTJ stack may be implemented within embodiments of the present invention when a thicker perpendicular magnetic layer is desired as discussed below with reference to
The MTJ stack materials of embodiments of the present invention have perpendicular magnetic anisotropy (PMA) and provide high magnetoresistance (MR) with a tunnel barrier layer of the MTJ stack and can be grown at room temperature. For example, the MTJ stack materials include a seed layer including tantalum and a free magnetic layer comprising at least iron.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one ore more other features, integers, steps, operations, element components, and/or groups thereof.
The corresponding structures, materials, acts, and equivalents of all means or step plus function elements in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the present invention has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the invention in the form disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the invention. The embodiment was chosen and described in order to best explain the principles of the invention and the practical application, and to enable others of ordinary skill in the art to understand the invention for various embodiments with various modifications as are suited to the particular use contemplated
The flow diagrams depicted herein are just one example. There may be many variations to this diagram or the steps (or operations) described therein without departing from the spirit of the invention. For instance, the steps may be performed in a differing order or steps may be added, deleted or modified. All of these variations are considered a part of the claimed invention.
While the preferred embodiment to the invention had been described, it will be understood that those skilled in the art, both now and in the future, may make various improvements and enhancements which fall within the scope of the claims which follow. These claims should be construed to maintain the proper protection for the invention first described.
This application is a continuation of U.S. application Ser. No. 12/815,923 filed on Jun. 15, 2010 entitled SEED LAYER AND FREE MAGNETIC LAYER FOR PERPENDICULAR ANISOTROPY IN A SPIN-TORQUE MAGNETIC RANDOM ACCESS MEMORY, the entire contents of which are incorporated herein by reference.
Number | Name | Date | Kind |
---|---|---|---|
7313013 | Sun et al. | Dec 2007 | B2 |
7457064 | Nemoto et al. | Nov 2008 | B2 |
7489541 | Pakala et al. | Feb 2009 | B2 |
20040247942 | Wu et al. | Dec 2004 | A1 |
20050041456 | Saito | Feb 2005 | A1 |
20050185455 | Huai | Aug 2005 | A1 |
20070096229 | Yoshikawa et al. | May 2007 | A1 |
20070137028 | Carey et al. | Jun 2007 | A1 |
20080094886 | Ranjan et al. | Apr 2008 | A1 |
20080253174 | Yoshikawa et al. | Oct 2008 | A1 |
20090027948 | Ruehrig | Jan 2009 | A1 |
20090079018 | Nagase et al. | Mar 2009 | A1 |
20090116137 | Takekuma et al. | May 2009 | A1 |
20090218645 | Ranjan et al. | Sep 2009 | A1 |
20090243008 | Kitagawa et al. | Oct 2009 | A1 |
20100020592 | Hosotani et al. | Jan 2010 | A1 |
20100078763 | Hosotani et al. | Apr 2010 | A1 |
20100096716 | Ranjan et al. | Apr 2010 | A1 |
20110169111 | Hu et al. | Jul 2011 | A1 |
Entry |
---|
Ikeda et al., “Tunnel magnetoresistance of 604% at 300 K by suppression of Ta diffusion in CoFeB/MgO/CoFeB pseudo-spin-valves annealed at high temperature,” Applied Physics Letter, 2008, 3 pgs. vol. 93, American Institute of Physics. |
Jung et al., “Strong perpendicular magnetic anisotropy in thick CoFeB films sandwiched by Pd and MgO layers,” Applied Physics Letters, 2010, 3 pgs, vol. 96, American Institute of Physics. |
Mizunuma et al., “MgO barrier-perpendicular magnetic tunnel junctions with CoFe/Pd multilayers and ferromagnetic insertion layers,” Applied Physics Letters, 2009, 3 pgs., vol. 95, American Institute of Physics. |
International Search Report; International Application No. PCT/US11/36910; International Filing Date: May 18, 2011; Date of Mailing: Aug. 26, 2011. |
International Search Report—Written Opinion; International Application No. PCT/US11/36910; International Filing Date: May 18, 2011; Date of Mailing: Aug. 26, 2011. |
Office Action—Non-Final for U.S. Appl. No. 12/815,923, filed Jun. 15, 2010; First Named Inventor: Daniel C. Worledge; Mail Date: Nov. 14, 2011. |
Office Action—Non-Final for U.S. Appl. No. 12/684,372, filed Jan. 8, 2010; First named Inventor: Guohan Hu; Mail Date: Dec. 16, 2011. |
Number | Date | Country | |
---|---|---|---|
20120299137 A1 | Nov 2012 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 12815923 | Jun 2010 | US |
Child | 13570375 | US |