Self-aligned elevated transistor

Abstract

A method of forming a a self-aligned elevated transistor using selective epitaxial growth is described. An oxide layer is provided overlying a semiconductor substrate. The oxide layer is etched through to the semiconductor substrate to form a trench having a lower portion contacting the substrate and an upper portion having a width larger than the width of the lower portion. A silicon layer is grown within the trench using selective epitaxial growth wherein the silicon layer fills the lower portion and partially fills the upper portion. Nitride spacers are formed on the sidewalls of the trench. A polysilicon layer is deposited overlying the oxide layer and within the trench and etched back to form a gate electrode within the trench between the nitride spacers. The nitride spacers are etched away where they are not covered by the gate electrode leaving thin nitride spacers on sidewalls of the gate electrode. Ions are implanted into the silicon layer exposed at the edges of the trench whereby source and drain pockets are formed within the silicon layer wherein the junction depth is determined by the thickness of the silicon layer. A dielectric layer is deposited overlying the oxide layer and the gate electrode and source/drain pockets within the trench to complete formation of the self-aligned elevated transistor in the fabrication of an integrated circuit.

Description

BACKGROUND OF THE INVENTION

[0001] (1) Field of the Invention

[0002] The invention relates to the fabrication of integrated circuit devices, and more particularly, to a method of forming a self-aligned elevated transistor using the technique of silicon epitaxial growth in the manufacture of integrated circuits.

[0003] (2) Description of the Prior Art

[0004] Shallow trench isolation (STI) will be employed widely in current and future integrated circuit technologies to provide sufficient isolation between neighboring devices. However, there are a number of problematic issues in STI processes including “hump effects” and chemical mechanical polishing (CMP) induced dishing over wide trenches that must be resolved prior to its further and wider applications. The STI corner represents an abrupt transition from the transistor active area to isolation. The gate polysilicon wraparound of a sharp trench corner causes a separate conduction characteristic of the corner resulting in a “double hump” in the transistor drain current-gate voltage characteristics. It is desired to void the problem of the

[0005] Another object of the present invention is to provide a method of forming a self-aligned elevated transistor using selective epitaxial growth in the fabrication of an integrated circuit.

[0006] Yet another object of the present invention is to provide a method of forming a self-aligned elevated transistor wherein there is absolute control over junction depth.

[0007] A further object of the invention is to provide a method of forming a self-aligned elevated transistor using selective epitaxial growth wherein there is absolute control over junction depth.

[0008] A still further object of the invention is to provide a method of forming a self-aligned elevated transistor wherein the packing density of integrated circuits is not limited by the dimension of isolation trenches.

[0009] Yet another object of the present invention is to provide a method of forming a self-aligned elevated transistor without the use of shallow trench isolation.

[0010] A still further object of the invention is to provide a method of forming a self-aligned elevated transistor using selective epitaxial growth wherein the packing density of integrated circuits is not limited by the dimension of isolation trenches.

[0011] In accordance with the objects of this invention the method of forming a a self-aligned elevated transistor using selective epitaxial growth wherein the packing density of integrated circuits is not limited by the dimension of isolation trenches is achieved. An oxide layer is provided overlying a semiconductor substrate. The oxide layer is etched through to the semiconductor substrate to form a trench having a lower portion contacting the substrate and an upper portion having a width larger than the width of the lower portion. A silicon layer is grown within the trench using selective epitaxial growth wherein the silicon layer fills the lower portion and partially fills the upper portion wherein the thickness of the silicon layer partially filling the upper portion is controlled. A liner oxide layer is deposited overlying the oxide layer and the silicon layer within the trench. Nitride spacers are formed on the sidewalls of the trench over the liner oxide layer. The liner oxide is removed where it is not covered by the nitride spacers overlying the silicon layer. A gate oxide layer is grown overlying the silicon layer within the trench. A polysilicon layer is deposited overlying the oxide layer and within the trench and etched back to form a gate electrode within the trench between the nitride spacers. The nitride spacers are etched away where they are not covered by the gate electrode leaving thin nitride spacers on sidewalls of the gate electrode and exposing the liner oxide overlying the silicon layer at edges of the trench. The exposed liner oxide is etched away. Ions are implanted into the silicon layer at the edges of the trench whereby source and drain pockets are formed within the silicon layer and wherein the controlled thickness of the silicon layer partially filling the upper portion of the trench corresponds to a desired junction depth of the source/drain pockets. The gate electrode and source/drain pockets are silicided. A dielectric layer is deposited overlying the oxide layer and silicided source/drain pockets and silicided gate electrode within the trench wherein the gate electrode and the source/drain pockets form the self-aligned elevated transistor in the fabrication of an integrated circuit.

[0012] Also, according to the objects of the invention, a new self-aligned elevated transistor is achieved. An oxide layer overlies a semiconductor substrate. A silicon layer fills a lower portion of a trench through the oxide layer and partially fills an upper portion of the trench wherein the lower portion of the trench contacts the semiconductor substrate and has a width smaller than a width of the upper portion of the trench. A polysilicon gate electrode overlies a center portion of the silicon layer having a gate oxide layer therebetween. Source/drain pockets lie within the silicon layer at edge portions of the silicon layer not covered by the polysilicon gate electrode. A dielectric layer overlies the oxide layer and the gate electrode and source/drain pockets within the trench to complete elevated transistor in an integrated circuit device.

BRIEF DESCRIPTION OF THE DRAWINGS

[0013] In the accompanying drawings forming a material part of this description, there is shown:

[0014] FIGS. 1 through 14 schematically illustrate in cross-sectional representation a preferred embodiment of the present invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0015] Referring now to FIG. 1, there is illustrated a portion of a partially completed integrated circuit in which there is a monocrystalline silicon semiconductor substrate 10. An oxide layer 14 is deposited by chemical vapor deposition (CVD) or thermally grown over the surface of the substrate. This layer 14 may comprise undoped silicon oxide and has a thickness of between about 4000 and 6000 Angstroms.

[0016] The oxide layer is patterned using conventional photolithographic and etching techniques to form an opening to the substrate as shown in FIG. 2. The opening consists of a wide trench 15 through an upper portion of the oxide layer 14 and a narrow via 17 within the trench continuing through to the substrate surface. For example, the trench 15 has a width of between about 12,500 and 15,000 Angstroms and a depth of between about 3000 and 5000 Angstroms or about ¾ of the thickness of the oxide layer 14. The via 17 has a width of between about 5000 and 10,000 Angstroms and a depth of between about 300 and 500 Angstroms or about ¼ of the thickness of the oxide layer 14. The wide trench 15 can be about 1.0 to 1.25 microns wide or as narrow as about 0.9 microns.

[0017] Referring now to FIG. 3, the substrate 10 exposed within the via opening 17 is subjected to selective epitaxial growth (SEG). Silicon 18 grows to fill the via to leave spacers 24 on the inside sidewalls of the trench as shown in FIG. 6.

[0018] Now, a threshold voltage implant 28 is made through the gate oxide into the silicon 18. For example, for an NMOS device, BF2 ions are implanted at between about 1E12 to 1E13 atoms/cm2 at 40 to 50 KeV. For a PMOS device, phosphorus or arsenic ions are implanted at 1E12 to 1E13 atoms/cm2 at between about 40 and 50 KeV.

[0019] Referring now to FIG. 7, the liner oxide within the trench not covered by the spacers 24 is removed, preferably using a wet etch to minimize silicon damage.

[0020] Gate oxide 26 is regrown on the exposed silicon 18 within the trench to a thickness of between about 35 and 50 Angstroms, as shown in FIG. 8.

[0021] Now, a layer of polysilicon is deposited over the substrate and filling the trench. The polysilicon layer is doped, as is conventional, then etched back to leave a polysilicon gate 30 recessed within the trench, as seen in FIG. 9.

[0022] Referring now to FIG. 10, a self-aligned nitride etch is performed with high selectivity to silicon nitride over oxide, polysilicon, and silicon. For example, any of the following chemistries may be used: Co/C4F8/Ar/O2, SF6/O2/Ar,He, NF3/O2/Ar,He. That is, the silicon nitride spacers 24 are removed where they are not covered by the polysilicon gate 30, leaving very thin nitride spacers 32. An intentionally prolonged nitride overetch will etch into the underlying oxide 20 and 14, leaving behind about 100 to 200 Angstroms of oxide 20.

[0023] A self-aligned oxide strip removes the liner oxide 20 where it is not covered by the nitride spacers 32, as shown in FIG. 11. For example, the liner oxide may be removed by diluted hydrofluoric acid (DHF) (100:1) at about 24° C. for 60 to 80 seconds. The silicon layer 18 is now exposed adjacent to the gate 30.

[0024] Referring now to FIG. 12, a self-aligned source/drain implant 35 forms source and drain regions 38 within the silicon 18 adjacent to the gate electrode 30. The source/drain regions or pockets 38 have a junction depth determined by the thickness of the SEG layer 18 and are not determined by thermal drive-in.

[0025] For example, a large angle tilt implant is made with four-way rotation. For a N+ implant, arsenic ions are implanted at about 1E15 atoms/cm2 at 50 to 60 KeV. For a P+ implant, phosphorus ions are implanted at about 1E15 atoms/cm2 at 30 to 40 KeV. A N2 anneal at 800-900° C. for 15 to 20 seconds is preferred to get lateral diffusion of dopants to form NLDD or PLDD regions.

[0026] The gate and source/drain pockets are silicided 40, as shown in FIG. 13. For example, the wafer surface is cleaned, such as by DHF and NH4OH/H2O2/H2O. Titanium is deposited to a thickness of between about 200 to 300 Angstroms. Silicon is implanted through the titanium layer at a dosage of about 1E13 atoms/cm2 at 40 to 50 KeV. A rapid thermal process (RTP) forms the salicide layer 40 on the silicon and polysilicon surfaces, as shown.

[0027] FIG. 14 shows dielectric layer 44 isolating the elevated transistor 30 of the invention. Dielectric layer may be, for example, tetraethoxysilane (TEOS) oxide, phosphosilicate glass (PSG), borosilicate glass (BSG), HSQ, or high density plasma (HDP) fluorosilicate glass (FSG).

[0028] Processing continues as is conventional in the art to form electrical contacts to the source/drain and gate areas outside of the cross-section shown in the figures, as is understood in the art.

[0029] The new self-aligned elevated transistor of the invention will now be described with reference to FIG. 14. An oxide layer 14 overlies a semiconductor substrate 10. A silicon layer 18 fills a lower portion of a trench through the oxide layer and partially fills an upper portion of the trench wherein the lower portion of the trench contacts the semiconductor substrate and has a width smaller than a width of the upper portion of the trench. A polysilicon gate electrode 30 overlies a center portion of the silicon layer having a gate oxide layer 26 therebetween. Source/drain pockets 38 lie within the silicon layer at edge portions of the silicon layer not covered by the polysilicon gate electrode 30. A dielectric layer 44 overlies the oxide layer and the gate electrode and source/drain pockets within the trench to complete elevated transistor in an integrated circuit device.

[0030] The process of the present invention provides an effective and very manufacturable method for fabricating an elevated transistor. This is a simpler process than SIMOX (separation by implantation of oxygen) or SOI (silicon on insulator) processes. For example, the inventive process requires no oxygen implantation and no annealing treatment, which reduces the thermal budget. The process of the invention results in a new structure that is midway between a partially depleted SOI and a fully depleted SOI. Partially depleted SOI's pose long-term unstable I-V characteristics while fully depleted SOI's do not allow SEG implementation. This invention provides the advantages of a fully depleted SOI while allowing SEG implementation and also allowing back gate biasing. The process of the invention allows absolute control over some device parameters, most significantly the junction depth of the source/drain regions which is controlled by the thickness of the selective epitaxial growth.

[0031] The process of the invention has a number of advantages over current STI structures. A lower leakage current is achieved by the invention because leakage currents are confined to one direction; that is, laterally from the source/drain structures into the channel area. Conventional buried source/drain regions have leakage currents in all directions into the substrate. Since the transistor is formed in a self-aligned process within a trench and having isolation therearound, there is an increase in packing density over STI processes. No excessive etching of the substrate is required to form a trench. No hump effects or CMP-induced dishing occur.

[0032] Other advantages include the ability to control the orientation of the SEG growth because of the presence of the oxide 14 “frame.” The process is totally self-aligned, thereby eliminating masking steps and allowing smaller feature sizes. A more planar overall topology results as well.

[0033] While the invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of the invention.

Claims

1. A method of forming an elevated transistor in the fabrication of an integrated circuit comprising: providing an oxide layer overlying a semiconductor substrate; etching through said oxide layer to said semiconductor substrate to form a trench having a lower portion contacting said substrate and an upper portion having a width larger than the width of said lower portion; growing a silicon layer within said trench filling said lower portion and partially filling said upper portion; forming nitride spacers on the sidewalls of said trench; depositing a polysilicon layer overlying said oxide layer and within said trench and etching back said polysilicon layer to form a gate electrode within said trench between said nitride spacers; etching away said nitride spacers not covered by said gate electrode leaving thin nitride spacers on sidewalls of said gate electrode and exposing said silicon layer at edges of said trench; implanting ions into said silicon layer at said edges of said trench whereby source and drain pockets are formed within said silicon layer; and depositing a dielectric layer overlying said oxide layer and said source/drain pockets and said gate electrode within said trench wherein said gate electrode and said source/drain pockets form said elevated transistor in the fabrication of said integrated circuit.

2. The method according to claim 1 wherein said oxide layer comprises thermal oxide and has a thickness of between about 4000 and 6000 Angstroms.

3. The method according to claim 1 wherein said step of growing said silicon layer comprises selective epitaxial growth.

4. The method according to claim 1 wherein said silicon layer has a controlled thickness corresponding to a desired junction depth of said source/drain pockets.

5. The method according to claim 4 wherein said thickness is between about 1000 and 2000 Angstroms.

6. The method according to claim 1 further comprising depositing a liner oxide layer over said oxide layer and within said trench underlying said nitride spacers.

7. The method according to claim 1 further comprising siliciding said gate electrode and said source/drain pockets before said step of depositing said dielectric layer.

8. A method of forming an elevated transistor in the fabrication of an integrated circuit comprising: providing an oxide layer overlying a semiconductor substrate; etching through said oxide layer to said semiconductor substrate to form an trench having a lower portion contacting said substrate and an upper portion having a width larger than the width of said lower portion; growing a silicon layer within said-trench filling said lower portion and partially filling said upper portion wherein the thickness of said silicon layer partially filling said upper portion is controlled; depositing a liner oxide layer overlying said oxide layer and said silicon layer within said trench; forming nitride spacers on the sidewalls of said trench over said liner oxide layer; removing said liner oxide not covered by said between about 4030 and 6000 Angstroms.

10. The method according to claim 8 wherein said step of growing said silicon layer comprises selective epitaxial growth.

11. The method according to claim 8 wherein said controlled thickness of said silicon layer partially filling said upper portion of said trench corresponds to a desired junction depth of said source/drain pockets.

12. The method according to claim 11 wherein said thickness is between about 1000 and 2000 Angstroms.

13. The method according to claim 8 wherein said liner oxide layer has a thickness of between about 500 and 1000 Angstroms.

14. The method according to claim 8 further comprising siliciding said gate electrode and said source/drain pockets before said step of depositing said dielectric layer.

15. A method of forming an elevated transistor in the fabrication of an integrated circuit comprising: providing an oxide layer overlying a semiconductor substrate; etching through said oxide layer to said semiconductor substrate to form a trench having a lower portion contacting said substrate and an upper portion having a width larger than the width of said lower portion; growing a silicon layer within said trench using selective epitaxial growth wherein said silicon layer fills said lower portion and partially fills said upper portion wherein the thickness of said silicon layer partially filling said upper portion is controlled; depositing a liner oxide layer overlying said oxide layer and said silicon layer within said trench; forming nitride spacers on the sidewalls of said trench over said liner oxide layer; removing said liner oxide not covered by said nitride spacers overlying said silicon layer; growing a gate oxide layer overlying said silicon layer within said trench; depositing a polysilicon layer overlying said oxide layer and within said trench and etching back said polysilicon layer to form a gate electrode within said trench between said nitride spacers; etching away said nitride spacers not covered by said gate electrode leaving thin nitride spacers on sidewalls of said gate electrode and exposing said liner oxide overlying said silicon layer at edges of said trench; etching away said exposed liner oxide; implanting ions into said silicon layer at said edges of said trench whereby source and drain pockets are formed within said silicon layer and wherein said controlled thickness of said silicon layer partially filling said upper portion of said trench corresponds to a desired junction depth of said source/drain pockets; siliciding said gate electrode and said source/drain pockets; and depositing a dielectric layer overlying said oxide layer and said silicided source/drain pockets and said silicided gate electrode within said trench wherein said gate electrode and said source/drain pockets form said elevated transistor in the fabrication of said integrated circuit.

16. The method according to claim 15 wherein said oxide layer comprises thermal oxide and has a thickness of between about 4000 and 6000 Angstroms.

17. The method according to claim 15 wherein said controlled thickness is between about 1000 and 2000 Angstroms.

18. The method according to claim 15 wherein said liner oxide layer has a thickness of between about 500 and 1000 Angstroms.

19. An elevated transistor in an integrated circuit comprising: an oxide layer overlying a semiconductor substrate; a silicon layer filling a lower portion of a trench within said oxide layer and partially filling an upper portion of said trench wherein said lower portion of said trench contacts said semiconductor substrate and has a width smaller than a width of said upper portion of said trench; a polysilicon gate electrode overlying a center portion of said silicon layer having a gate oxide layer therebetween; source/drain pockets within said silicon layer at edge portions of said silicon layer not covered by said polysilicon gate electrode; and a dielectric layer overlying said oxide layer, said gate electrode, and said source/drain pockets to complete said elevated transistor in said integrated circuit device.

20. The elevated transistor according to claim 19 wherein said trench has a width as small as 1.0 to 1.25 microns.