Information
-
Patent Grant
-
6215187
-
Patent Number
6,215,187
-
Date Filed
Tuesday, September 21, 199924 years ago
-
Date Issued
Tuesday, April 10, 200123 years ago
-
Inventors
-
Original Assignees
-
Examiners
- Whitehead, Jr.; Carl
- Potter; Roy
Agents
-
CPC
-
US Classifications
Field of Search
US
- 257 758
- 257 774
- 257 701
- 257 778
- 257 516
- 438 118
- 438 622
- 438 210
- 438 329
-
International Classifications
-
Abstract
A semiconductor device and manufacturing method thereof attaining higher capacitor capacitance and lower power consumption are provided. On an interlayer oxide film which is a BPTEOS film containing an impurity, an interlayer oxide film which is a TEOS film not containing any impurity is formed. Openings of approximately inverted frusto-conical shape of approximately the same size are formed in interlayer oxide films, respectively, providing a contact hole of such a shape that includes two inverted frusto-cones continued in the vertical direction as a whole is provided. Along the inner wall surface of the contact hole, a storage electrode, a dielectric film and a cell plate electrode constituting a capacitor are formed successively.
Description
BACKGROUND OF THE INVENTION
1. Field of the Invention
The present invention relates to a semiconductor device and manufacturing method thereof. More specifically, the present invention relates to a semiconductor device having a capacitor and a contact plug in an MOSFET (Metal Oxide Semiconductor Field Effect Transistor), a DRAM (Dynamic Random Access Memory) or the like, and to a manufacturing method thereof.
2. Description of the Background Art
As the technique of manufacturing semiconductors and especially the technique of miniature processing have been developed, degree of integration and capacity of DRAMs for MOS transistors have been increased. As the degree of integration increases, the area occupied by a semiconductor element per 1 bit has been decreased. Therefore, the area of a capacitor storing information (charges) decreases, and hence charges stored therein decreases. As a result, the capacitor has come to be very sensitive to slight electrical influence, so that there have been problems of erroneous calling of information where charges are erroneously injected to the capacitor or charges are erroneously ejected from the capacitor, as well as the problem of soft error in which the contents of the memory is destroyed by α ray or the like. Further, as the semiconductor device has been reduced in size, contact area between a transistor and an interconnection or a contact area of a contact plug connecting interconnections with each other is reduced, so that contact resistance at the content portion is increased. This means that excessive voltage is required in a highly miniaturized semiconductor devices and that power consumption increases.
In order to address one of the aforementioned problems, that is, reduction of capacitor capacitance resulting from miniaturization of the semiconductor devices, various methods have been proposed to increase area of occupation in a capacitor using a polycrystalline silicon film or the like for the storage electrode. According to one of the proposed methods, the storage electrode is formed in a cylindrical shape, so as to increase contact area in a direction vertical to the main surface of the semiconductor substrate.
The structure of a conventional cylindrical capacitor and manufacturing method thereof will be described with reference to
FIGS. 22
to
28
. First, on a P type silicon substrate
102
, an isolating oxide film
105
a
is formed, resulting in separate element forming regions. On the element forming region formed separately by isolating oxide film
105
a
, a gate oxide film
104
c
and a gate electrode
104
(word line) of a two-layered structure including a high melting point metal silicide film
104
a
and a polycrystalline silicon film
104
b
are formed. Thereafter, using gate electrode
104
as a mask, source/drain regions
103
, which are n
−
diffusion layers, are formed by impurity implantation. In this manner, an MOSFET, that is, an MOS field effect transistor is formed. Thereafter, to cover gate electrode
104
and isolating oxide film
105
a
, an interlayer oxide film
105
b
is deposited on semiconductor substrate
102
. Thereafter, a contact hole
106
a
is formed to be connected to source/drain region
103
. Thereafter, a contact plug is filled in contact hole
106
a
, and etched to a prescribed shape. Thus, a bit line
106
connected to the MOS field effect transistor is formed as shown in FIG.
22
. Then, an interlayer oxide film
105
c
is deposited on interlayer oxide film
105
b
, and a contact hole
107
a
for forming a plug establishing electrical connection between source/drain region
103
and a storage electrode of the capacitor is formed. Thereafter, a conductive material is filled in contact hole
107
a
, so that a contact plug
107
is formed. Thereafter, an interlayer oxide film
105
j
is deposited on interlayer oxide film
105
c
and contact plug
107
. On interlayer oxide film
105
j
, a prescribed mask is formed, and thereafter, a contact hole
150
in which a capacitor is to be formed, is formed by etching as shown in FIG.
24
. Thereafter, a polycrystalline silicon film, which is to be storage electrodes
108
a
and
108
b
, is formed in contact hole
150
. Thereafter, a capacitor dielectric film
101
is formed to cover an upper surface of interlayer oxide film
105
j
and surfaces of storage electrodes
108
a
and
108
b
. Thereafter, a film which is to be a cell plate electrode
109
, is deposited to cover capacitor dielectric film
101
, and in this manner, the capacitor is completed.
As the two-dimensional area of semiconductor substrate
102
occupied by the semiconductor device decreases, the capacitor formed through the above described steps has come to be formed extending considerably large in the vertical direction with respect to semiconductor substrate
102
. In other words, contact hole
105
in which the capacitor is formed is large in the vertical direction with respect to the main surface of semiconductor substrate
102
.
Therefore, generally, contact hole
150
in which storage electrode
109
is formed has an upper portion of interlayer oxide film
105
j
etched by larger amount than the lower portion through dry etching as can be seen from
FIG. 25
, and therefore the contact hole come to have an inverted frusto-conical shape with inclined sidewalls, of which opening diameter gradually increases from the lower portion to the upper portion of interlayer oxide film
105
j
. Therefore, when a two-dimensionally small contact hole
150
is to be formed, the lower portion of contact hole
150
come to have too small an opening diameter relative to the upper portion. As a result, at the lower portion of contact hole
150
, the conductive material for forming the film to be the storage electrode
109
may not be sufficiently filled but clogged.
If the conductive material for forming the film to be cell plate electrode
109
is not properly filled in the lower portion of contact hole
150
, surface area of that portion which functions as an electrode of cell plate electrode
109
reduces, resulting in reduced electrostatic capacitance of the capacitor. Even when the conductive material for forming the film to be cell plate electrode
109
is properly filled, cell plate electrode
109
becomes very thin at the lower portion of contact hole
105
, and therefore it becomes difficult to store sufficient charges. Thus the function of the cell plate electrode cannot be ensured.
Further, the higher the height of the capacitor from the main surface of semiconductor substrate
102
, contact hole
150
come to have the higher aspect ratio.
Here, as the sidewalls of contact hole
150
are inclined, the opening diameter is small at the lower portion of contact hole
150
, and further, a phenomenon referred to as bowing, where the opening diameter at the upper portion of contact hole
150
come to be smaller than the middle portion of contact hole
150
, is observed. When the phenomenon of bowing occurs in contact hole
150
, a material
170
formed along contact hole
150
provided in interlayer oxide film
105
k
cannot be properly filled, resulting in undesirable void inside the material
170
.
Further, problems experienced in contact plug
107
will be described with reference to
FIGS. 27 and 28
.
FIG. 27
is a cross section taken along the line B—B of FIG.
23
. As can be seen from
FIG. 27
, contact plug
107
is required of a small opening diameter at an upper portion of contact hole
107
a
, considering short-circuit with bit line
106
. Therefore, when the contact hole is formed in the frusto-conical shape in a two dimensionally small semiconductor device as described above, the opening diameter at the lower portion becomes considerably small. Accordingly, the contact resistance at the contact between the lower surface of conductive contact plug filled in contact hole
107
a
and source/drain region
103
is high. Further, as can be seen from
FIG. 28
, when the opening diameter of contact hole
107
a
is enlarged by wet etching to reduce contact resistance to provide contact hole
107
b
, there will be an increased possibility of short-circuit between bit line
106
and the contact plug formed along contact hole
107
b.
SUMMARY OF THE INVENTION
Therefore, an object of the present invention is to provide a semiconductor device attaining larger capacitance of a capacitor and lower power consumption, and to provide manufacturing method thereof.
The semiconductor device in accordance with the present invention includes a semiconductor substrate, and an insulating film containing an impurity formed on the semiconductor substrate, of which impurity concentration distribution is set such that average isotropical etch rate from a lower surface to a prescribed portion near the lower surface is higher than average isotropic etch rate from an upper surface to a prescribed position near the upper surface under a prescribed etch condition.
By such a structure, it becomes possible when, for example, an opening diameter of a frusto-conical contact hole formed by dry etching through an insulating film is to be enlarged by isotropic wet etching, to set etch rate of the insulating film in a direction approximately parallel to the main surface of the semiconductor substrate to be gradually lowered as it goes away from the main surface of the semiconductor substrate, by providing an insulating film of which impurity concentration is gradually made lower as it goes away from the main surface of the semiconductor substrate. Accordingly, it becomes possible to gradually enlarge the opening diameter of the contact hole nearer to the semiconductor substrate. As a result, it becomes possible to form an approximately columnar contact hole.
Therefore, when a capacitor is formed in the contact hole which is opened in approximately columnar shape as described above, the unsatisfactory filling of the film for forming the capacitor due to the narrowed portion near the semiconductor substrate can be prevented. Accordingly, decrease in capacitor capacitance resulting from increased resistance at the capacitor lower portion caused by unsatisfactory filling can be avoided. Thus, capacitor capacitance is improved. Therefore, for the same two-dimensional occupational area parallel to the main surface of the semiconductor substrate, the capacitor capacitance can be increased, and hence malfunction of the capacitor such as a soft error is suppressed. This means that a capacitor which operates correctly with small occupation area is provided, enabling miniaturization of the semiconductor device.
Further, it is possible to avoid enlarging of the opening diameter at a portion where the contact plug contacts other conductive layer, when the contact plug is formed in the contact hole opened in the approximately columnar shape as mentioned above. The contact area between the contact plug and other conductive layer is increased so that increase in contact resistance of the contact plug is suppressed, and therefore power consumption of the semiconductor device can be reduced.
According to the present invention, the insulating film may include a first insulating film having a first impurity, and a second insulating film formed on the first insulating film and having a second impurity at a lower impurity concentration than the impurity concentration of the first insulating film.
In such a structure, the impurity concentration of the first insulating film is adapted to be higher than the impurity concentration of the second insulating film, and therefore during wet etching, the first insulating film is etched by larger amount than the second insulating film. Accordingly, when the opening diameter of the contact hole formed through the first and second insulating films is to be enlarged by wet etching, it is possible to make larger the opening in the first insulating film than in the second insulating film. As a result, from the same reason as described with respect to the semiconductor device according to the above described aspect of the present invention, a capacitor which operates correctly with small occupation area can be formed, and the contact resistance can be reduced. Thus, the semiconductor device can be miniaturized and power consumption thereof can be reduced.
According to another aspect, the semiconductor device may further include a third insulating film formed on the second insulating film and having a third impurity having still higher impurity concentration than the second insulating film.
In such a structure, as the impurity concentration of the third insulating film is adapted to be higher than the impurity concentration of the second insulating film, in the step of enlarging the opening diameter of the insulating film by wet etching, the etch rate of the third insulating film is higher than the etch rate of the second insulating film. Therefore, it is possible to prevent unsatisfactory filling of the conductive material filled in the contact hole when, for example, the opening of the contact hole formed in the insulating film becomes smaller near the upper portion of the contact hole because of the influence of heat treatment or the like. Thus, increase in contact resistance of the contact plug caused by unsatisfactory filling of the contact plug can be suppressed, and hence power consumption of the semiconductor device can be reduced.
According to a still further aspect, in the semiconductor device in accordance with the present invention, the impurity concentration of the insulating film may be adapted to be gradually lower away from the semiconductor substrate. In such a structure, the insulating film contains larger amount of impurity closer to the semiconductor substrate, and therefore during wet etching, the closer to the semiconductor substrate, by the greater amount the insulating film is etched. Therefore, from the same reasons as described with respect to the semiconductor device according to the first aspect described above, a capacitor which operates correctly with small occupation area can be formed, and the contact resistance can be reduced. Therefore, the semiconductor device can be miniaturized and power consumption thereof can be reduced.
According to still another aspect, in the semiconductor device in accordance with the present invention, the impurity may include at least one of boron and phosphorous.
Such a structure enables variation of etching rate when the insulating film is wet-etched, when a BPTEOS (Boro Phospho Tetra Etyle Ortho Silicate) film, a PSG (Phospho Silicate Glass) film or the like is formed as the insulating film.
Preferably, in the semiconductor device in accordance with the present invention, a hole penetrating the insulating film is formed in the insulating film.
In this structure, the contact hole is used as a space for forming a capacitor or a space for forming the contact plug, and hence the effects of miniaturization of the semiconductor device and reduction of power consumption thereof can be attained.
According to a still further aspect of the present invention, in the semiconductor device in accordance with the present invention, a capacitor may be formed along an inner peripheral surface of the hole.
In this structure, the contact hole is used as a space for forming the capacitor, and hence the effect of miniaturizing the semiconductor device as mentioned above can be attained.
Further, in the semiconductor device in accordance with the present invention, a contact plug may be formed to fill the hole.
In this structure, the contact hole is used as a space for forming the contact plug, and thus the aforementioned effect of reducing power consumption of the semiconductor device, mentioned above, can be attained.
According to a still another aspect of the present invention, the method of manufacturing a semiconductor device includes the step of forming an insulating film of which impurity concentration distribution is set such that average isotropic etch rate from a lower surface to a position near the lower surface is higher than average isotropic etch rate from an upper surface to a position close to the upper surface under a prescribed etching condition, on a semiconductor substrate.
By such a manufacturing method, it becomes possible when, for example, an opening diameter of a frusto-conical contact hole formed penetrating through an insulating film by dry etching is to be enlarged by isotropic wet etching, to provide an insulating film of which etch rate in a direction approximately parallel to the main surface of the semiconductor substrate is gradually decreased as it goes away from the main surface of the semiconductor substrate, by setting the impurity concentration gradually lower as it goes away from the main surface of the semiconductor substrate. Therefore, an insulating film of which opening diameter is gradually enlarged nearer to the semiconductor substrate can be formed. As a result, an insulating film having a contact hole opened in an approximately columnar shape can be formed.
Therefore, an insulating film can be formed, without enlarging the opening diameter at the upper portion of the insulating film, which can prevent unsatisfactory filling of the film for forming the capacitor caused by narrowed portion near the semiconductor substrate, when a capacitor is formed in the contact hole opened in the approximately columnar shape as described above. Therefore, a capacitor which is free from the problem of decreased capacitance caused by increased resistance at the capacitor lower portion resulting from the unsatisfactory filling, can be formed not in the two-dimensionally large structure as conventionally formed by significantly enlarging the opening diameter of the upper portion of the insulating film. Therefore, for the same occupation area in a plane parallel to the main surface of the semiconductor substrate, the capacitor capacitance can be increased, and malfunction such as a soft error can be suppressed though the capacitor is small. As a result, a capacitor which operates correctly with small area of occupation can be formed, enabling miniaturization of the semiconductor device.
Further, when a contact plug, for example, is formed in the contact hole opened in the approximately columnar shape as described above, it is possible to enlarge the opening diameter at a portion where the contact plug contacts other conductive layer. Thus, as the contact area between the contact plug and other conductive layer is enlarged, increase in contact resistance at a lower portion of the contact plug can be suppressed, and a semiconductor device having low power consumption can be provided.
According to another aspect, in the method of manufacturing a semiconductor device of the present invention, the step of forming the insulating film may include the step of forming a first insulating film having a first impurity on the semiconductor substrate, and the step of forming a second insulating film having a second impurity of higher impurity concentration than the first insulating film, on the first insulating film.
By such a method of manufacturing, it is possible to set the impurity concentration of the first insulating film higher than the impurity concentration of the second insulating film. Therefore, in the subsequent step of wet etching, the first insulating film is etched by larger amount than the second insulating film. Therefore, when the opening diameter of the contact hole formed in the first and second insulating films is to be enlarged by wet etching, an insulating film is provided in which the opening diameter of the first insulating film only is enlarged. As a result, from the same reasons as described with respect to the manufacturing method of the semiconductor device according to the above described aspect, a capacitor which operates correctly with small area of occupation can be formed, and in addition, as the contact resistance is reduced, a semiconductor device which is miniaturized and consumes less power can be obtained.
In the method of manufacturing a semiconductor device in accordance with the present invention, the step of forming an insulating film may further include the step of forming a third insulating film having a third impurity of higher impurity concentration than the second insulating film, on the second insulating film.
When the manufacturing method is used, as the concentration of the third impurity is set higher than the concentration of the second impurity, the etch rate of the third insulating film is higher than the etch rate of the second insulating film, when the opening diameter of the contact hole is to be enlarged by wet etching. Therefore, when the opening diameter of an upper portion of the contact hole formed in the insulating film is reduced in size by heat treatment or the like, for example, unsatisfactory filling of the conductive material filled in the contact hole can be prevented. Therefore, increase in contact plug resistance derived from the unsatisfactory filling is suppressed, and hence a semiconductor device which consumes less power can be obtained.
In the method of manufacturing a semiconductor device in accordance with the present invention, the method of forming an insulating film may include the step of adding an impurity such that impurity concentration gradually lowers as it goes away from the semiconductor substrate.
By using such a manufacturing method, it becomes possible to form an insulating film which is etched by larger amount nearer to the semiconductor substrate, during wet etching. Therefore, from the same reasons as described with respect to the semiconductor device above, a capacitor is formed which operates correctly while occupying a small area, and hence a miniaturized semiconductor device can be provided.
In the method of manufacturing a semiconductor device in accordance with the present invention, the impurity may include one or more materials selected from the group consisting of boron and phosphorus.
By using such a manufacturing method, it becomes possible to vary the rate of wet etching when a BPTEOS film, a PSG film or the like is formed as the insulating film, and therefore a semiconductor device realizing the above described effects can be provided.
Preferably, the method of manufacturing a semiconductor device in accordance with the present invention further includes the step of forming a hole penetrating the insulating film, in the insulating film.
By using such a manufacturing method, the contact hole is utilized as a space for forming a capacitor or a space for forming a contact plug, and thus the semiconductor device which is miniaturized and consumes less power as described above, can be provided.
The method of manufacturing a semiconductor device in accordance with the present invention may preferably include the step of forming a capacitor along a sidewall of the hole.
By using such a manufacturing method, the contact hole is utilized as a space for forming the capacitor, and hence the miniaturized semiconductor device as described above can be provided.
Further, the method of manufacturing a semiconductor device in accordance with the present invention may further include the step of forming a contact plug to fill the hole.
By using such a manufacturing method, the contact hole may be utilized as a space for forming a contact plug, and hence the semiconductor device which consumes less power as described above can be provided.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1
is a cross section view representing a structure of a semiconductor device in accordance with a first embodiment of the present invention.
FIG. 2
is a cross sectional view showing a state immediately after a contact plug to be connected to source/drain region filling a contact hole formed in an interlayer oxide film is formed, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 3
is a cross sectional view showing a state immediately after a lower interlayer oxide film is formed for forming a capacitor to cover the surface of the interlayer oxide film in which the contact plug is formed, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 4
is a cross sectional view showing a state immediately after an upper interlayer oxide film is formed on the lower interlayer oxide film, for forming the capacitor, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 5
is a cross sectional view showing a state immediately after a frusto-conical contact hole penetrating through the upper and lower interlayer oxide films is formed toward the contact plug by dry etching, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 6
is a cross sectional view showing a state immediately after a contact hole having two frusto-cones continued in vertical direction is formed by significantly enlarging opening diameter of a contact hole formed in the lower interlayer oxide film in a direction horizontal to the semiconductor substrate by wet etching, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 7
is a cross sectional view showing a state immediately after a conductive layer to be a storage electrode is formed on a sidewall of the contact hole formed in the interlayer oxide film to form a capacitor, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 8
is a cross sectional view showing a state immediately after an unnecessary conductive layer formed on the interlayer oxide film for forming a capacitor is removed, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 9
is a cross sectional view showing a state immediately after a dielectric layer is formed to cover the surface of the conductive layer to be the storage electrode and the upper surface of the interlayer oxide film, in the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention.
FIG. 10
is a cross sectional view representing a structure of a semiconductor device in accordance with a second embodiment of the present invention.
FIG. 11
is a cross sectional view showing a state immediately after an interlayer oxide film for forming a capacitor is formed to cover an interlayer oxide film in which a contact plug is formed, in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 12
is a cross sectional view showing a state immediately after a frusto-conical contact hole is formed by dry etching in the interlayer oxide film for forming a capacitor to expose the contact plug, in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 13
is a cross sectional view showing a state immediately after the opening diameter of the contact hole is enlarged by wet etching in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 14
is a cross sectional view showing a state immediately after a conductive layer, to be a storage electrode is formed along an inner surface of the contact hole in which the capacitor is to be formed and an upper surface of the interlayer oxide film, in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 15
is a cross sectional view showing a state immediately after the conductive layer formed on the upper surface of the interlayer oxide film in which the capacitor is formed, is removed in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 16
is a cross sectional view showing a state immediately after a dielectric film is formed on a surface of the conductive layer to be a storage electrode and on the upper surface of the interlayer oxide film in which the capacitor is to be formed, in the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention.
FIG. 17
is a cross sectional view representing a structure of a semiconductor device in accordance with a third embodiment of the present invention.
FIG. 18
is a cross sectional view representing a structure of a semiconductor device in accordance with the fourth embodiment of the present invention.
FIG. 19
is a cross sectional view showing a state immediately after a bit line penetrating through the interlayer oxide film and reaching a source/drain region is formed, in the method of manufacturing a semiconductor device in accordance with the fourth embodiment of the present invention.
FIG. 20
is a cross sectional view showing a state immediately after a contact hole penetrating the interlayer oxide film and reaching source/drain region is formed by dry etching, in the method of manufacturing a semiconductor device in accordance with a fourth embodiment of the present invention.
FIG. 21
is a cross sectional view taken along the line A-A of
FIG. 20
showing the state immediately after the bit line penetrating through the interlayer oxide film and reaching a source/drain region is formed, in the method of manufacturing a semiconductor device in accordance with the fourth embodiment of the present invention.
FIG. 22
is a cross sectional view showing a state immediately after a contact plug to be connected to the source/drain region is filled in the contact hole formed in the interlayer oxide film by dry etching and a bit line is formed, in the conventional method of manufacturing a semiconductor device.
FIG. 23
is a cross sectional view showing a state immediately after a contact hole penetrating through the interlayer oxide film and reaching a source/drain region is formed by dry etching, in the conventional method of manufacturing a semiconductor device.
FIG. 24
is a cross sectional view showing a state immediately after a contact hole is formed in the interlayer oxide film in which a capacitor is to be formed, by dry etching, to expose a surface of the contact plug, in the conventional method of manufacturing a semiconductor device.
FIG. 25
is a cross sectional view representing a structure of a conventional semiconductor device having a capacitor.
FIG. 26
is a cross sectional view showing a state where a void is formed in the contact plug, when the contact plug is filled in a contact hole formed in a bowing shape, in the conventional method of manufacturing a semiconductor device.
FIG. 27
is a cross sectional view showing a state viewed along the line B-B of
FIG. 23
, immediately after the contact hole penetrating through the interlayer oxide film and reaching the source/drain region is formed by dry etching, in the conventional method of manufacturing a semiconductor device.
FIG. 28
is a cross sectional view showing a state immediately after an opening diameter of the contact hole formed in the interlayer oxide film and reaching the source/drain region is enlarged by wet etching, in the conventional method of manufacturing a semiconductor device.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
Embodiments of the present invention will be described in the following with reference to the figures.
First Embodiment
The structure and the method of manufacturing a semiconductor device in accordance with the first embodiment of the present invention will be described with reference to
FIGS. 1
to
9
. The structure of the semiconductor device in accordance with the present embodiment will be described first, with reference to FIG.
1
. In the semiconductor device in accordance with the present embodiment, an isolating oxide film
5
a
for isolating element forming regions is formed on a P type silicon substrate
2
. On each of the element forming regions separated by isolating oxide film
5
a
, a gate electrode
4
(word line) including a gate oxide film
4
c
and a two-layered structure of a high melting point metal silicide film
4
a
and a polycrystalline silicon film
4
b
is formed. On both sides of gate electrode
4
, source/drain regions
3
, which are n
−
diffusion layers, are formed, thus providing an MOSFET, that is, an MOS field effect transistor.
To cover gate electrode
4
, source/drain region
3
and isolating oxide film
5
a
, an interlayer oxide film
5
b
is formed on semiconductor substrate
2
. In interlayer oxide film
5
b
, a contact hole
6
a
is formed to reach the central source/drain region
3
. A contact plug is filled in contact hole
6
a
, and a bit line
6
connected to the MOS field effect transistor etched to a prescribed shape is formed.
An interlayer oxide film
5
c
is formed on interlayer oxide film
5
b
, and a contact hole
7
b
in which a contact plug to be electrically connected to a storage electrode of a capacitor is formed penetrating through the interlayer oxide films
5
b
and
5
c
. A conductive material is filled in contact hole
7
b
, thus providing a contact plug
7
. Further, interlayer oxide film
5
d
which is a BPTEOS film, is formed on interlayer oxide film
5
c
. On interlayer oxide film
5
d
, an interlayer oxide film
5
e
which is a TEOS film almost free of any impurity, is formed on interlayer oxide film
5
d
. A contact hole
51
having two inverted frusto-cones connected in vertical direction, in which the capacitor is to be formed, is formed penetrating through interlayer oxide films
5
d
and
5
e
, respectively.
Along the inner wall of contact hole
51
, a polycrystalline silicon film, which is to be storage electrodes
8
a
and
8
b
, is formed. To cover surfaces of storage electrodes
8
a
and
8
b
and an upper surface of interlayer oxide film
5
e
, a capacitor dielectric film
1
is formed. To cover the surface of capacitor dielectric film
1
, a cell plate electrode
9
is formed, and a capacitor in the shape of two inverted frusto-cones continued in vertical direction is formed.
In this structure, on interlayer oxide film d containing boron and phosphorus as impurities, interlayer oxide film
5
e
almost free of any impurity such as phosphorus or boron is formed. Therefore, isotropic wet etch rate of interlayer oxide film
5
d
is higher than isotropic wet etch rate of interlayer oxide film
5
e
. Therefore, when contact hole
50
formed to penetrate interlayer oxide films
5
d
and
5
e
is to be enlarged in its opening diameter by wet etching, for example, it is possible to enlarge the opening diameter of interlayer oxide film
5
d
by larger amount than interlayer oxide film
5
e
. The contact hole formed penetrating through interlayer oxide films
5
d
and
5
e
by dry etching generally has an inverted frusto-conical shape with the opening diameter of interlayer oxide film
5
d
being smaller than the opening diameter of interlayer oxide film
5
e
. In the semiconductor device in accordance with the present embodiment, however, the opening diameter of interlayer oxide film
5
d
is enlarged to be larger than the opening diameter of interlayer oxide film
5
e
, as described above. Therefore, it is possible to form contact hole
51
in which the capacitor is formed in a shape having approximately identical two inverted frusto-cones continued in the vertical direction.
Therefore, in the semiconductor device in accordance with the present embodiment in which the capacitor is formed in the contact hole
51
opened in such a shape in that two inverted frusto-cones are continued in the vertical direction as described above, unsatisfactory filling of film constituting the capacitor, caused by the narrowing of the portion of contact hole closer to the semiconductor substrate
1
, that is, narrowing of the lower portion of interlayer oxide film
5
d
, can be prevented. Accordingly, lowering in capacitor capacitance resulting from the unsatisfactory filling can be suppressed, and hence the capacitor capacitance can be improved. Therefore, it becomes possible to increase the capacitor capacitance with the same occupation area in a plane parallel to the main surface of the semiconductor substrate, and therefore malfunction of the capacitor such as a soft error can be suppressed. As a result, a capacitor operating correctly with small occupation area is formed, and thus it becomes possible to miniaturize the semiconductor device.
The method of manufacturing a semiconductor device in accordance with the present embodiment will be described with reference to
FIGS. 2
to
9
. In
FIG. 2
, the steps until contact plug
7
is formed are approximately the same as those of the method of manufacturing a semiconductor device described with reference to the prior art, except that the contact hole
7
b
is formed in an approximately vertical columnar shape with respect to the main surface of semiconductor substrate
2
. Thereafter, referring to
FIG. 3
, contact plug
7
and interlayer oxide film
5
d
having the thickness of about 500 nm of BPTEOS are deposited. Thereafter, referring to
FIG. 4
, on interlayer oxide film
5
d
, interlayer oxide film
5
e
having the thickness of about 300 nm of TEOS is deposited. Thereafter, by photolithography and etching, a photoresist film having a hole shape is formed by patterning, to provide a storage electrode. Using the photoresist film as a mask, contact hole
50
is formed by reactive ion etching, to expose the surface of contact plug
7
, as shown in FIG.
5
.
Thereafter, in order to enlarge contact hole
50
, the sidewall of contact hole
50
is isotropically wet-etched, using buffered hydrofluoric acid. At this time, the wet etch rate of BPTEOS, that is, interlayer oxide film
5
d
is about 35 nm/min, while wet etch rate of TEOS, that is, interlayer oxide film
5
e
, is about 16 nm/min. Therefore, interlayer oxide film
5
d
is etched by larger amount than interlayer oxide film
5
e
, so that contact hole
51
comes to have such a shape that has two inverted frusto-cones continued in the vertical direction, as shown in FIG.
6
.
Then, referring to
FIG. 7
, after the enlarge contact hole
50
is formed, a polycrystalline silicon film
8
doped with phosphorus, which will be the storage electrode, is deposited to cover the surface of contact hole
51
and upper surface of interlayer oxide film
5
e
. Thereafter, a resist film or the like is filled in the hole formed by polycrystalline silicon film
8
, which will be the storage electrode in advance, to prevent damage to the bottom portion of the storage electrode by reactive ion etching. Thereafter, polycrystalline silicon film
8
deposited on the upper surface of interlayer oxide film
5
e
is removed by reactive ion etching as shown in
FIG. 8
, the resist film in the hole is removed, and storage electrodes
8
a
and
8
b
are formed. Thereafter, referring to
FIG. 9
, a capacitor dielectric film
1
is deposited to cover storage electrodes
8
a
and
8
b
and interlayer oxide film
5
e
. Thereafter, referring to
FIG. 1
, a cell plate electrode
9
formed of polycrystalline silicon film doped with phosphorus is deposited to cover the surface of capacitor dielectric film
1
. In this manner, a semiconductor device having a capacitor is completed.
As interlayer oxide film
5
e
not including any impurity is formed on interlayer oxide film
5
d
containing phosphorus and boron as impurities by such a manufacturing method, it is possible to set the etch rate of interlayer oxide film
5
d
higher than the etch rate of interlayer oxide film
5
e
. Accordingly, in the method of manufacturing a semiconductor device in accordance with the present embodiment in which opening diameter of contact hole
50
formed to penetrate interlayer oxide films
5
d
and
5
e
continuously in the shape of inverted frusto-cones by dry etching is further enlarged by wet etching, it is possible to enlarge the opening diameter of interlayer oxide film
5
d
larger than the opening diameter of interlayer oxide film
5
e
. Therefore, a contact hole
51
having two inverted frusto-cones continued in the vertical direction with the opening diameter of interlayer oxide film
5
d
only is enlarged wide can be formed.
Therefore, when the capacitor is formed in contact hole
51
which has two inverted frusto-cones continued in the vertical direction, a capacitor is formed in which unsatisfactory filling caused by narrower opening diameter of interlayer oxide film
5
d closer to the semiconductor substrate
2
as compared with the opening diameter of interlayer oxide film
5
e
, can be prevented.
Therefore, a capacitor can be formed in which lowering of electrostatic capacity derived from the unsatisfactory filling is suppressed. Therefore, it becomes possible to improve capacitor capacitance by enlarging the capacitor in the vertical direction with respect to the semiconductor substrate. Therefore, the capacitor capacitance can be increased with the same occupation area in a plane parallel to the main surface of the semiconductor substrate. Therefore, even when the area occupied by the capacitor is made small, a capacitor can be formed in which malfunction such as a soft error is suppressed. As a capacitor operating correctly with small occupation area is provided, it becomes possible to provide a miniaturized semiconductor device.
Second Embodiment
The structure and the method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention will be described with reference to
FIGS. 10
to
16
. First, the structure of the semiconductor device in accordance with the present embodiment will be described with reference to FIG.
10
. The semiconductor device in accordance with the present embodiment will be described with reference to FIG.
10
. The semiconductor device in accordance with the present embodiment is approximately similar to the structure of the semiconductor device in accordance with the first embodiment in the overall structure, except that impurity concentration of the interlayer oxide film
5
f
in which the capacitor is formed gradually increases from an upper portion to the lower portion, and that a contact hole
53
penetrating through interlayer insulating film
5
f
is formed as a column approximately vertical to the main surface of the semiconductor substrate
2
.
Because of this structure, in the step of enlarging the opening diameter of the contact hole formed by dry etching penetrating through interlayer oxide film
5
f
by isotropic wet etching or the like, it becomes possible to set the etch rate of interlayer oxide film
5
f
in a direction approximately parallel to the main surface of semiconductor substrate
2
to be gradually smaller as it goes away from the main surface of semiconductor substrate
2
.
Therefore, it is possible to gradually enlarge the opening diameter of contact hole toward semiconductor substrate
2
, which contact hole is formed in the inverted frusto-conical shape in the common step of dry etching. Therefore, it becomes possible to form contact hole
53
with its opening diameter enlarged by wet etching in the shape of a column approximately vertical to the main surface of semiconductor substrate
2
.
Therefore, when the capacitor is formed in contact hole
52
opened approximately in the shape of a column, unsatisfactory filling of the film to be storage electrode
8
of the capacitor caused by narrowing of the portion nearer to the contact plug
7
can be prevented. Therefore, as in the first embodiment, the semiconductor device can be miniaturized.
The method of manufacturing a semiconductor device in accordance with the second embodiment of the present invention will be described with reference to
FIGS. 10
to
16
. In the method of manufacturing a semiconductor device in accordance with the present embodiment, the steps similar to those of the method of manufacturing a semiconductor device in accordance with the first embodiment are performed to attain the state of
FIG. 2
, in which the contact plug
7
is formed. Thereafter, referring to
FIG. 11
, interlayer insulating film
5
f
of BPTEOS is deposited with boron concentration being kept constant and phosphorus concentration varied continuously to be lower as it goes away from the semiconductor substrate
2
. More specifically, phosphorus concentration is gradually lowered from 8.4 mol % at the lowermost portion to 5 mol % at an uppermost portion. Thereafter, by photolithography and etching, a photoresist film of a hole shape for forming the storage electrode is formed by patterning. Using the photoresist film as a mask, contact hole
52
is formed by reactive ion etching, to expose the surface of contact plug
7
, as can be seen from FIG.
12
.
Thereafter, in order to enlarge the opening diameter of contact hole
52
, isotropic wet etching is performed on the sidewall of contact hole
52
, using buffered hydrofluoric acid. When buffered hydrofluoric acid is used, etch rate of the interlayer oxide film
5
f
is gradually increased from 8 nm/min at the uppermost portion to 12 nm/min at the lowermost portion. Therefore, the sidewall of contact hole
53
provided by enlarging the opening diameter of contact hole
52
becomes approximately vertical to the main surface of semiconductor substrate
2
, as can be seen from FIG.
13
. Thus, a contact hole
53
is provided in which the opening diameter at an upper portion and the opening diameter at a lower portion of interlayer oxide film
5
f
are approximately equal to each other.
After the opening diameter of contact hole
53
is enlarged, a polycrystalline silicon film
8
doped with phosphorus, which will be the storage electrode, is deposited along the upper surface of interlayer oxide film
5
f
and the surface of contact hole
53
. Thereafter, a resist film or the like is filled in the hole formed by polycrystalline silicone film
8
, which is to be the storage electrode, of a cylindrical shape in advance, so as to prevent any possible damage at the bottom portion of storage electrode caused by reactive ion etching. Thereafter, referring to
FIG. 15
, polycrystalline silicon film
8
deposited on the upper surface of interlayer oxide film
5
f
is removed by reactive ion etching, the resist film in the cylindrical hole is removed, and storage electrodes
8
a
and
8
b
are formed.
Thereafter, referring to
FIG. 16
, a capacitor dielectric film
1
is deposited to cover storage electrodes
8
a
,
8
b
and interlayer oxide film
5
f
. Thereafter, as shown in
FIG. 10
, a cell plate electrode
9
of polycrystalline silicon film doped with phosphorus is deposited to cover the surface of capacitor dielectric film
1
. In this manner, a semiconductor device having a capacitor is completed.
By such a manufacturing method, when contact hole
52
shown in
FIG. 12
formed by dry etching to penetrate through interlayer oxide film
5
f
is to be enlarged by wet etching or the like, it becomes possible to set etch rate of interlayer oxide film
5
f
in a direction approximately parallel to the main surface of semiconductor substrate
2
to be gradually decreased as it goes away from the main surface of semiconductor substrate
2
. Therefore, it is possible to gradually enlarge by wet etching the opening diameter toward the semiconductor substrate
2
. As a result, it becomes possible to deposit such an interlayer oxide film
5
f
that allows formation of a contact hole
53
in an approximately columnar shape, as shown in FIG.
13
.
Therefore, in the present embodiment in which the capacitor is formed in the contact hole
53
opened in the approximately columnar shape as mentioned above, unsatisfactory filling of the film for forming the capacitor caused by the narrowing of a portion nearer to the semiconductor substrate can be prevented. Therefore, as in the semiconductor device in accordance with the first embodiment, a miniaturized semiconductor device can be provided.
Third Embodiment
The structure and the manufacturing method of the semiconductor device in accordance with the third embodiment of the present invention will be described with reference to FIG.
17
. First, the structure of the semiconductor device in accordance with the present embodiment will be described with reference to FIG.
17
. As can be seen from
FIG. 17
, for the interlayer oxide film
5
i
deposited at an upper portion and interlayer insulating film
5
g
deposited at a lower portion, opening diameters formed by dry etching of which layers are expected to be smaller, BPTEOS film having phosphorus concentration of 8.4 mol % providing high isotropic wet etch rate are used, and for the interlayer oxide film
53
deposited at a middle portion of which opening diameter formed by dry etching is large, a BPTEOS film having phosphorus concentration of 5.0 mol % providing lower isotropic wet etch rate is used.
By the similar method as the methods of manufacturing semiconductor devices in accordance with the first and second embodiments described above in which anisotropic dry etching and isotropic wet etching are both used, with interlayer oxide films
5
i
,
5
h
and
5
g
provided as described above, it becomes possible to form a contact hole
54
penetrating through interlayer oxide films
5
i
,
5
h
and
5
g
to have approximately constant opening diameter with the sidewall being approximately vertical to the main surface of the semiconductor substrate. Therefore, if contact hole
54
is used as a contact hole for forming a capacitor, unsatisfactory filling of the contact hole, experienced in the bowing contact hole as described with respect to the prior art can be suppressed. When the contact hole
54
is used as a contact hole for forming the contact plug
70
, sufficient opening diameter is ensured at the contact portion, and therefore it is possible to form a contact plug with low contact resistance. Further, as the portion of the interlayer oxide film
5
i
of contact hole
54
is made large, filling of the conductive material to form contact plug
70
is facilitated. When contact hole
54
is used as a contact hole for forming a capacitor, a capacitor having large electrostatic capacitance can be provided, as in the first and second embodiments described above.
The method of manufacturing the semiconductor device in accordance with the third embodiment of the present invention will be described with reference to FIG.
17
. First, as the interlayer oxide film
5
i
deposited at an upper portion and interlayer insulating film
5
g
deposited at a lower portion, where the hole diameter is expected to be smaller, BPTEOS films having high wet etch rate and having phosphorus concentration of 8.4 mol % are deposited, and as the interlayer oxide film
5
h
deposited at an intermediate portion where the opening diameter of the contact hole formed by anisotropic dry etching is expected to be large, a BPTEOS film having low isotropic wet etch rate and a phosphorus concentration of 5.0 mol % is deposited. Thereafter, using a photoresist film patterned by lithography and etching as a mask, a contact hole penetrating through interlayer oxide films
5
i
,
5
h
and
5
g
, similar to the contact hole shown in
FIG. 26
, is formed in the conventional manner by reactive etching. More specifically, a contact hole in the so-called bowing shape with the wide middle portion and narrowed upper and lower portions is formed, as shown in FIG.
26
. Thereafter, referring to
FIG. 17
, opening diameters of interlayer oxide films
5
i
,
5
h
and
5
g
are enlarged by isotropic wet etching at respective etch rates, so that the sidewall of contact hole
54
is made approximately vertical to the main surface of the semiconductor substrate.
By such a manufacturing method, increase in contact resistance caused by reduced contact area can be prevented, as the opening diameter of interlayer oxide film
5
g
reaching other conductive layer is large at the portion of interlayer oxide film
5
g
of the interlayer oxide films
5
i
,
5
h
and
5
g
of contact hole
54
. Further, as the opening diameter of interlayer oxide film
5
i
of contact hole
54
is also large, filling of the conductive material for forming contact plug
70
is facilitated.
When the method of manufacturing contact hole
54
described above is used for forming a hole in which the capacitor is to be formed, a capacitor having large electrostatic capacitance can be formed, as in the first and second embodiments described above.
Fourth Embodiment
The structure and the manufacturing method of the semiconductor device in accordance with the fourth embodiment of the present invention will be described with reference to FIG.
18
. First, referring to
FIG. 18
, the structure of the semiconductor device in accordance with the present embodiment will be described. As can be seen from
FIG. 18
, an isolating oxide film
5
a
is formed on a P type silicon substrate. In each of the element forming regions separated by isolating oxide film
5
a
, a gate electrode
4
(word line) of a two-layered structure including a polycrystalline silicon film
4
b
and a high melting point metal silicide film
4
a
is formed, with a gate oxide film
4
c
interposed. In semiconductor substrate
2
, source/drain regions
3
as n
−
diffusion layers are formed, and thus an MOSFET, that is, an MOS field effect transistor is formed. To cover gate electrode
4
, source/drain region
3
and isolating oxide film
5
a
, an interlayer oxide film
5
b
which is a BPTEOS film having phosphorus concentration of 8.4 mol % is deposited on semiconductor substrate
2
. A contact hole
6
a
reaching source/drain region
3
is formed. A contact plug is filled in contact hole
6
a
, thus providing a bit line
6
connected to the MOS field effect transistor. On interlayer oxide film
5
b
, an interlayer oxide film
5
c
having phosphorus concentration of 5.0 mol % is formed, and a contact hole
7
b
of a shape having two inverted frusto-cones continued in the vertical direction, is formed, reaching the storage electrode of the capacitor. A contact plug
7
is formed by filling a conductive material in contact hole
7
b.
Because of this structure, the contact area between contact plug
7
and source/drain region
3
is enlarged, as the bottom portion of contact hole
7
b
in which contact plug
7
is formed is much enlarged by isotropic wet etching. Further, at the upper portion of contact hole
7
b
, opening diameter is not excessively enlarged, and therefore the contact hole is not so close as to electrically affect the bit line
6
. As a result, short circuit between contact plug
7
and bit line
6
at the side surface of contact plug
7
can be prevented, while contact resistance between contact plug
7
and source/drain region
3
can be reduced.
The method of manufacturing the semiconductor device in accordance with the fourth embodiment of the present invention will be described with reference to
FIGS. 19
to
21
. First, the isolating oxide film
5
a
is formed on P type silicon substrate
2
. Then, in the element forming region separated by isolating oxide film
5
a
, gate oxide film
4
c
and gate electrode
4
(word line) including two-layered structure including high melting point metal silicide film
4
a
and polycrystalline silicon film
4
b
are formed. Thereafter, from the main surface to a prescribed depth of semiconductor substrate
2
, source/drain regions
3
, which are n
−
diffusion layers, are formed by impurity implantation, and in this manner, an MOSFET, that is, an MOS field effect transistor is formed.
Thereafter, interlayer oxide film
5
b
of BPTEOS having phosphorus concentration of 8.4 mol % is deposited to cover source/drain region
3
, gate electrode
4
and isolating oxide film
5
a
. Thereafter, a contact hole
6
a
connected to source/drain region
3
is formed. Thereafter, a contact plug is filled in contact hole
6
a
and etched to a prescribed shape. Thus, as shown in
FIG. 19
, a bit line
6
is formed. Thereafter, interlayer oxide film
5
c
of BPTEOS having phosphorus concentration of 5.0 mol % is deposited to cover interlayer oxide film
5
b
and bit line
6
.
Thereafter, using a photoresist formed by photolithography and etching as a mask, a contact hole
7
a
penetrating through interlayer oxide films
5
b
and
5
c
and reaching source/drain region
3
is formed, to attain the state of FIG.
20
and
FIG. 21
, which is a cross section taken along the line A—A of FIG.
20
. Thereafter, when isotropic wet etching is performed, the portion of interlayer oxide film
5
b
of contact hole
7
a
has its opening diameter enlarged by larger amount, as it has higher wet etch rate than interlayer oxide film
5
c
. Therefore, contact hole
7
a
shown in
FIG. 21
comes to have such a shape of contact hole
7
b
as shown in
FIG. 22
, in which only the opening diameter of interlayer oxide film
5
b
is enlarged, that is, a shape in which two inverted frusto-cones continue in the vertical direction.
In accordance with such a manufacturing method, the interlayer oxide film
5
c
at the upper portion of contact hole
7
b
has its opening diameter not excessively enlarged, and therefore short-circuit between bit line
6
and contact plug
7
is avoided. Further, as the opening diameter of interlayer oxide film
5
c
which is at the bottom portion of contact hole
7
b
where contact plug
7
is formed is enlarged, contact area between contact plug and source/drain region
3
can be enlarged. Therefore, the short-circuit between contact plug
7
and bit line
6
is prevented, while contact resistance between contact plug
7
and source/drain region
3
can be reduced.
Though BPTEOS film containing an impurity has been described in the first to fourth embodiments above, an interlayer oxide film formed of PTEOS film, BTEOS film or an interlayer oxide film containing impurities of an arbitrary combination of phosphorus or boron and other material may be used, provided that the interlayer oxide film contains an impurity allowing variation of etch rate. allowing variation of etch rate.
Though a TEOS film is used as an interlayer oxide film not containing impurity in the first to fourth embodiments above, an NSG (Non Doped Silicate Glass) film or the like not doped with any impurity may be used in place of the TEOS film.
Further, though wet etching has been described as an example of isotropic etching in the first to fourth embodiments above, the amount of enlargement of the opening diameter of the contact hole may be differentiated by dry etching, provided that the etching is isotropical.
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
Claims
- 1. A semiconductor device, comprising:a semiconductor substrate; and an insulating film having an upper portion and containing an impurity formed in said semiconductor substrate, with an impurity concentration distribution such that an average wet isotropic etch rate in the lower portion is higher than the average wet isotropic etch rate in the upper portion.
- 2. The semiconductor device according to claim 1, wherein said insulating film includes:a first insulating film constituting the lower portion and having a first impurity, and a second insulating film, constituting the upper portion, formed on said first insulating film and having a second impurity of lower impurity concentration than the impurity concentration of said first insulating film.
- 3. The semiconductor device according to claim 2, further comprisinga third insulating film formed on said second insulating film, and having a higher impurity concentration than the impurity concentration of said second insulating film, such that the wet isotropic etch rate of the third insulating film is greater than that of the second insulating film.
- 4. The semiconductor device according to claim 1, wherein impurity concentration distribution of said insulating film is set such that the impurity concentration gradually decreases from the upper portion to the lower portion.
- 5. The semiconductor device according to claim 1, wherein said impurity includes at least one of boron and phosphorus.
- 6. The semiconductor device according to claim 1, wherein a hole penetrating the insulating film is formed in said insulating film.
- 7. The semiconductor device according to claim 6, wherein a capacitor is formed along an internal peripheral surface of said hole.
- 8. The semiconductor device according to claim 6, wherein a contact plug is formed to fill said hole.
- 9. The semiconductor device according to claim 1, wherein said insulating film includes a silicon oxide film.
- 10. The semiconductor device according to claim 9, wherein said silicon oxide film is of a TEOS film.
- 11. A method of manufacturing a semiconductor device, comprising the step of forming, on a semiconductor substrate, an insulating film having an upper portion and a lower portion and containing an impurity with an impurity concentration distribution such that an average wet isotropic etch rate in the lower portion is higher than the average wet isotropic etch rate in the upper portion.
- 12. The method of manufacturing a semiconductor device according to claim 11, whereinsaid step of forming an insulating film includes the steps of forming a first insulating film constituting the lower portion and having a first impurity on said semiconductor substrate, and forming a second insulating film, consisting the upper portion having a second impurity of higher impurity concentration than the impurity concentration of said first insulating film, on said first insulating film.
- 13. The method of manufacturing a semiconductor device according to claim 12, whereinsaid step of forming said insulating film further includes the step of forming a third insulating film having a third impurity of higher impurity concentration than the impurity concentration of said second insulating film, on said second insulating film, such that the wet isotropic etch rate of the third insulating film is greater than that of the second insulating film.
- 14. The method of manufacturing a semiconductor device according to claim 11, wherein said step of forming said insulating film includes the step of adding an impurity such that the impurity concentration gradually decreases from the upper portion to the lower portion.
- 15. The method of manufacturing a semiconductor device according to claim 11, wherein said impurity includes at least one of boron and phosphorus.
- 16. The method of manufacturing a semiconductor device according to claim 11, further comprising the step of forming a hole penetrating through the insulating film, in said insulating film.
- 17. The method of manufacturing a semiconductor device according to claim 16, further comprising the step of forming a capacitor along a side surface of said hole.
- 18. The method of manufacturing a semiconductor device according to claim 16, further comprising the step of forming a contact plug to fill said hole.
- 19. The method of manufacturing a semiconductor device according to claim 11, wherein said insulating film is a silicon oxide film.
- 20. The method of manufacturing a semiconductor device according to claim 19, wherein said silicon oxide film is of a TEOS film.
- 21. The semiconductor device according to claim 4, wherein the average wet isotropic etch rate gradually increases from the upper portion to the lower portion.
- 22. The method according to claim 14, wherein the average wet isotropic etch rate gradually increases from the upper portion to the lower portion.
Priority Claims (1)
Number |
Date |
Country |
Kind |
11-165897 |
Jun 1999 |
JP |
|
US Referenced Citations (4)