This application claims the priority benefit of French Application for Patent No. 1870591, filed on May 23, 2018, the content of which is hereby incorporated by reference in its entirety to the maximum extent allowable by law.
The present disclosure generally concerns the manufacturing of integrated circuits, and more particularly the forming of silicide in such integrated circuits.
During the manufacturing of integrated circuits, a step of siliciding regions comprising silicon, which are intended to form electric contact areas, is generally provided, in order to decrease their resistivity.
An embodiment overcomes all or part of the disadvantages of conventional siliciding methods.
An embodiment provides a siliciding method enabling obtainment of a Schottky barrier between the silicon and the formed silicide which is decreased as compared with the case where the silicide is formed by a conventional method.
An embodiment provides a method enabling forming of a silicide of low resistance in certain regions and a thin silicide in other regions.
An embodiment provides forming, in source and drain regions of a transistor, a thin silicide which causes no degradation of the transistor performance.
Thus, an embodiment provides an integrated circuit where first semiconductor regions each include a silicided portion having group-III, IV, and/or V atoms.
According to an embodiment, the atoms are carbon and/or germanium atoms.
According to an embodiment, in each first region, the concentration of the atoms is at a maximum level at the interface between the silicided portion and a non-silicided portion.
According to an embodiment, other semiconductor regions each include a silicided portion having group-III, IV, and/or V atoms, preferably carbon and/or germanium atoms.
According to an embodiment, the silicided portion of the first regions is thicker than the silicided portion of the other regions.
Another embodiment provides a method of manufacturing a circuit such as defined hereabove.
According to an embodiment, the method includes, from a wafer at least partially made of a semiconductor material having the first and second regions defined therein, the following steps: a first siliciding of the first regions; a simultaneous implantation in the first silicided regions and in the second regions; and a second siliciding of the second regions.
According to an embodiment, the first siliciding includes the masking of the second regions followed by the deposition of a first metal layer, preferably including nickel.
According to an embodiment, the second siliciding includes the deposition of a second metal layer, preferably including nickel, on the second regions.
According to an embodiment, the first metal layer is thicker than the second metal layer.
According to an embodiment, the second metal layer is also deposited on the first silicided regions.
According to an embodiment, the first siliciding includes a first anneal and the second siliciding includes a second anneal performed at a temperature lower than a temperature of the first anneal, the duration of the second anneal being preferably smaller than a duration of the first anneal.
According to an embodiment, the trench includes a stack of a semiconductor layer, an insulating layer, and a semiconductor substrate, the second regions forming part of components formed inside and/or on top of the semiconductor layer.
According to an embodiment, the thickness of the semiconductor layer is smaller than 20 nm.
According to an embodiment, the first regions form part of components formed inside and/or on top of the substrate.
According to an embodiment, the implantation is a carbon and/or germanium implantation.
According to an embodiment, the first and second regions include silicon.
According to an embodiment, the implantation is amorphizing.
The foregoing and other features and advantages will be discussed in detail in the following non-limiting description of specific embodiments in connection with the accompanying drawings, among which
The same elements have been designated with the same reference numerals in the various drawings and, further, the various drawings are not to scale. For clarity, only those steps and elements which are useful to the understanding of the described embodiments have been shown and are detailed. In particular, the various usual integrated components where it is provided to silicide regions comprising silicon have not been described, the described method being compatible with such usual components and their operations.
In the following description, when reference is made to terms qualifying absolute positions, such as terms “front”, “back”, “top”, “bottom”, “left”, “right”, etc., or relative positions, such as terms “above”, “under”, “upper”, “lower”, etc., or to terms qualifying directions, such as terms “horizontal”, “vertical”, etc., it is referred to the orientation of the drawings. The terms “approximately”, “substantially”, “about”, and “on the order of” are used herein to designate a tolerance of plus or minus 10%, preferably of plus or minus 5%, of the value in question.
In the following description, the case of a wafer or plate at least partially made of a semiconductor material comprising at least one integrated circuit comprising components of a first type and components of a second type is considered. The components of the first type are called “high voltage” components and are intended to withstand high voltages, for example, higher than approximately 5 V, preferably higher than 5 V, such voltages being, for example, in the range from approximately 5 V to approximately 11 V, preferably from 5 to 11 V. The components of the second type are called “low voltage” components and are intended to withstand lower voltages than high-voltage components, for example, voltages lower than approximately 2 V, preferably lower than 2 V, for example, voltages of approximately 1.2 V, or even approximately 0.8 V, preferably 1.2 V or even 0.8 V.
Wafer 1 comprises a LV (“low voltage”) portion, to the left of
Transistor 3 is formed inside and/or on top of layer 7. Transistor 3 comprises source and drain regions 13 separated from each other by a channel-forming region 15. Source and drain regions 13 each comprise a portion 17 of silicon epitaxially grown from layer 7. Channel-forming region 15 is topped with a gate stack 19 having at least its top made of silicon, for example, of polysilicon. Spacers 21 cover the sides of gate stack 19. Spacers 21 separate and electrically insulate gate stack 19 from epitaxial portions 17. As an example, the thickness of epitaxial portions 17, for example, measured from the upper surface of layer 7, is in the range from approximately 10 nm to approximately 20 nm, preferably in the range from 10 to 20 nm, for example, in the range from approximately 14 to 16 nm, preferably in the range from 14 to 16 nm.
Wafer 1 also comprises a HV (“high voltage”) portion, to the right in
Transistor 5 is formed inside and/or on top of substrate 11. Transistor 5 comprises source and drain regions 23 separated from each other by a channel-forming region 25. Region 25 is topped with a gate stack 27 having at least its top made of silicon, for example, of polysilicon. Spacers 29 cover the sides of gate stack 27. As an example, the thickness or width of spacers 29 is greater than that of spacers 21.
In the shown example, transistors 3 and 5 are separated and electrically insulated from each other by insulating walls 31, for example, formed by trench isolation structures.
As an example, mask 33 is deposited all over wafer 1, after which the portion of mask 33 covering the HV portion of wafer 1 is removed by etching. Mask 33 is, for example, formed of a stack of two layers, a lower silicon oxide layer having a thickness for example on the order of 3 nm, and an upper silicon nitride layer having a thickness, for example, on the order of 30 nm.
A metal layer 35 is deposited on the HV portion, preferably all over wafer 1. Thus, in the HV portion of wafer 1, layer 35 covers and is in contact with the regions to be silicided. Preferably, layer 35 comprises nickel in contact with these regions to be silicided.
As an example, metal layer 35 comprises a stack of two metal layers, a lower nickel and platinum metal layer and an upper titanium nitride layer enabling to avoid for the nickel of the lower layer to oxidize. The thickness of the nickel and platinum layer is, for example, in the range from approximately 15 nm to approximately 20 nm, preferably from 15 to 20 nm, for example, equal to approximately 16 nm, preferably equal to 16 nm. The thickness of the titanium nitride layer is, for example, in the range from approximately 10 nm to approximately 20 nm, preferably from 10 to 20 nm, for example, equal to approximately 10 nm, preferably equal to 10 nm.
An anneal is then performed so that metal layer 35 reacts with the silicon of the regions to be silicided with which layer 35 is in contact. As an example, the anneal is performed at a temperature in the range from 250 to 300° C., for example, on the order of 270° C., preferably 270° C. As an example, the duration of the anneal is in the range from 45 to 75 seconds, for example, approximately equal to 60 seconds, preferably equal to 60 seconds.
This results, in the HV portion of wafer 1, in a siliciding of the regions which comprise silicon and which are in contact with layer 35, in other words the forming of silicide in each of these regions, it being understood that the region comprising silicon is not entirely turned into silicide. In this example, after the anneal, each of regions 23 comprises a silicided portion 23a and the top of gate stack 27 comprises a silicided portion 27a. As an example, the thickness of silicided portions 23a, 27a is approximately 24 nm, preferably equal to 24 nm.
The removal of metal layer 35 enables to remove the excess material which has not reacted with silicon to form silicide. As an example, the removal of layer 35 is performed by wet etching.
The removal of mask 33 enables to expose, in the LV portion of wafer 1, regions to be silicided, that is, here, regions 13 and the top of gate stack 19. As an example, the removal of mask 33 is performed by wet etching.
During the implantation (schematically shown by vertical arrows in
As an example, germanium is implanted with an implantation energy in the range from approximately 1 keV to approximately 5 keV and/or carbon is implanted with an implantation energy in the range from approximately 1 keV to approximately 2 keV.
An advantage of carbon and germanium atoms is that they are not electrically active towards silicon, that is, they are not N- or P-type dopant atoms. This enables to not modify the N and/or P-type dopant concentrations in the silicon regions already doped when the implantation is performed, particularly at the level of the PN junctions of the transistors.
A metal layer 37 is deposited all over wafer 1. Layer 37 covers and is in contact with silicide 27a, 23a already formed in the HV portion, layer 37 covering and being in contact also with the regions to be silicided of the LV portion. Preferably, layer 37 comprises nickel in contact with the silicon of the regions to be silicided of the LV portion. Preferably, the thickness of layer 37 is smaller than that of layer 35.
In this example, layer 37 has a structure identical to that of layer 35 and thus comprises a lower nickel and platinum layer and an upper titanium nitride layer. The thickness of the nickel and platinum layer of layer 37 is, for example, in the range from approximately 5 nm to approximately 10 nm, preferably from 5 to 10 nm, for example equal to approximately 7 nm, preferably equal to 7 nm. The thickness of the titanium nitride layer of layer 37 is, for example, in the range from approximately 3 nm to approximately 8 nm, preferably from 3 to 8 nm, for example, equal to approximately 5 nm, preferably equal to 5 nm.
An anneal is then performed so that metal layer 37 reacts with the silicon that it covers. As an example, the anneal is performed at a temperature in the range from 200 to 250° C., for example, on the order of 230° C., preferably 230° C. As an example, the duration of the anneal is in the range from 10 to 30 seconds, for example, equal to approximately 20 seconds, preferably equal to 20 seconds.
This results, in the LV portion of wafer 1, in a siliciding of the regions which comprise silicon and which are in contact with layer 37, in other words the forming of silicide in each of these regions, it being understood that the region is not entirely turned into silicide. In this example, after the anneal, each of regions 13, and more particularly the epitaxial portion 17 of these regions 13, comprises a silicided portion 17a and the top of gate stack 19 comprises a silicided portion 19a. As an example, the thickness of silicided portions 17a, 19a is approximately 11 nm, preferably 11 nm.
In this embodiment, the first anneal described in relation with
At a next step, not shown, metal layer 37 is removed, for example, by wet etching, to remove the excess metal which has not reacted. An additional anneal step is, for example, carried out to favor, in the HV portion of wafer 1, the accumulation of the atoms implanted during the step of
The described method enables obtainment of a thick silicide, for example, having a thickness greater than 20 nm, for example, having a thickness in the range from 20 to 30 nm, in the HV portion of wafer 1 and a thin silicide, for example, having a thickness smaller than 20 nm, for example, having a thickness in the range from 11 to 20 nm in the LV portion of wafer 1.
The provision of a thin silicide in the LV portion enables avoiding the silicide 17a of source and drain regions 13 extending all the way to insulating layer 9 and/or to channel forming region 15, which would degrade the performance of transistor 3.
In the HV portion, the thick silicide, which is less resistive than a thin silicide, is adapted to the voltages applied to the high-voltage components. As an example, the resistivity of the silicide in the HV portion is on the order of 14 μΩ·cm when its thickness is on the order of 24 nm, preferably of 24 nm, while the resistivity of the silicide in the LV portion is in the range from 30 to 60 μΩ·cm when its thickness is approximately 11 nm, which is not adapted to high-voltage components.
Further, in the above-described method, the provision, after the siliciding performed in the HV portion, of an implantation step such as described in relation with
Conversely, due to the fact that the implantation described in relation with
Further, the described implantation being amorphizing, this causes a decrease, or even a suppression, of the penetration of silicide 13a of the drain and source regions 13 from transistor 3 to channel-forming region 15 of this transistor and/or to layer 9, which would degrade the performance of transistor 3.
Specific embodiments have been described. Various alterations, modifications, and improvements will occur to those skilled in the art. In particular, it may be provided for each of the source and drain regions of high-voltage transistor 5 to comprise a portion epitaxially grown from substrate 11.
More generally, the above-described method applies to regions to be silicided of other components than those described hereabove, for example, to those of a diode formed in the LV portion, of an ONO-type (Oxide-Nitride-Oxide) capacitance formed in the HV portion, of a flash memory cell formed in the HV portion, to those of a power transistor formed in the HV portion, etc.
The materials and/or the thicknesses of the various above-described layers as well as the temperatures and/or the durations of the above-described anneals may be adapted, for example, according to the targeted silicide thicknesses in the LV portion and/or in the HV portion.
Hard mask 33 may be made of a layer and/or of other materials than those indicated hereabove provided that it prevents the forming of silicide in the LV portion at the step described in relation with
Although an embodiment where metal layer 37 is deposited on the already silicided regions of the HV portion of wafer 1 has been described, it may be provided to mask the HV portion before the deposition of this layer.
Further, it may be provided for the wafer to comprise additional areas where no siliciding is performed. This would for example be true for an area where only optical components would be formed, for an area where components used for electrostatic discharges are formed, or for an area comprising precision resistors.
Such alterations, modifications, and improvements are intended to be part of this disclosure, and are intended to be within the spirit and the scope of this disclosure. Accordingly, the foregoing description is by way of example only and is not intended to be limiting.
Number | Date | Country | Kind |
---|---|---|---|
1870591 | May 2018 | FR | national |