Patent Grant
9790238
This application is the National Stage of International Application No. PCT/KR2013/003866, filed May 3, 2013, which claims the benefit of and priority to Korean application No. 10-2012-0047440, filed May 4, 2012 and Korean application No. 10-2012-0047439, filed May 4, 2012, the entireties of which applications are incorporated herein by reference for any and all purposes.
The present invention relates to a novel strontium precursor. More particularly, the present invention relates a strontium precursor that exhibits excellent thermal stability and volatility and thus can be applied in the formation of a quality strontium-containing thin film even at a low temperature, a preparing method thereof, and a method for forming a strontium-containing thin film, using the same.
Strontium compounds are used in oxygen-ionic and electronic conductive thin films when being in the form of SrTiO3, SrBi2Ta2O9, BaxSr1-xTiO3, LaSrCoFe, and are found in thin film electroluminescent displays when being in the form of SrGa2S4:Ce. Like this, strontium compounds are used as precursors for preparing strontium-containing heterogeneous metal thin films, nano-size strontium oxides, and strontium-containing heterogeneous metal particles.
In addition, strontium titanate (SrTiO3) and barium strontium titanate ((Ba, Sr)TiO3), both being alkaline earth metal-containing oxides with a Perovskite structure, find applications in various fields including nonvolatile ferroelectric memory, microwave devices, dynamic random access memory (DRAMs), multilayer capacitors, electro optical devices, actuators, transducers, high-k dielectrics, and micro-electromechanical systems (MEMs) (Zhao, J.; Wang, X.; Chen, R.; Li. L. Materials Letters 2005, 59, 2329; Mao, Y.; Baneriee, S.; Wong, S. S. J. Am. Chem. Soc. 2003, 125, 15718; Gong, D.; Grimes, C. A.; Varghese, O. K; Hu, W.; Singh, R. S.; Chen, Z.; Dickey, D. J. J. Mater. Res. 2001, 16, 3331; Padture, N. P. Wei, X. Z. J. Am. Ceram. Soc. 2003, 86, 2215; Phule, P. P.; Risbud, S. H. J. Mater. Sci. 1990, 25, 1169; Hill, N. A. J. Phys. Chem. B 2000, 104, 6694). Further, SrO is known to act as a buffer layer between Si and SrTiO3, and alkaline earth thiogallates such as SrGa2S4:Ce are studied for use in phosphor thin films of electroluminescent displays (Asaoka, H.; Saiki, K.; Koma, A.; Yamamoto, H. Thin Solid Films 2000, 369, 273; Okamoto, S.; Tanaka, K.; Inoue, Y. Appl. Phys. Lett. 2000, 76, 946; Tanaka, K.; Inoue, Y.; Okamoto, S.; Kobayashi, K. J. Cryst. Growth 1995, 150, 1211).
To prepare the above-mentioned materials, various methods such as sol-gel, MOD (metal-organic decomposition), PLD (pulsed laser ablation), CVD (chemical vapor deposition), MOCVD (metal-organic chemical vapor deposition), ALD (atomic layer deposition), etc. have been employed. For use in these methods, various precursors are known, including alkoxides, aryloxides, b-diketonates, metallocenes, bis(trimethylsilyl)amide, and alkylamide. However, most of these precursors are dimers or higher oligomers with high volatile temperatures. In order to improve their volatility, the precursors are fluorinated, which leads contamination of the thin films with fluorides (Paw, W.; Baum, T. H.; Lam, K.-C.; Rheingold, A. L. Inorg. Chem. 2000, 39, 2011; Mizushima, Y.; Hirabayashi, I. J. Mater. Res. 1996, 11, 2698; Shamlian, S. H.; Hitchman, M. L.; Cook, S. L.; Richards. B. C. J. Mater Chem. 1994, 4, 81; Gardiner, R. A.; Brown, D. W.; Kirlin, P. S.; Rheingold, A. L. Chem. mater. 1991, 3, 1053). Meanwhile, Korean Patent Application Unexamined Publication No. 2008-0113053 discloses a strontium precursor containing a ligand composed only of cyclopentadienyl, but this precursor cannot be a solution to the problems mentioned above.
Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and an object of the present invention is to provide a novel strontium precursor that exhibits high thermal stability and volatility and which can be readily applied at a low temperature for the formation of a quality thin film.
In order to accomplish the object, the present invention provides a strontium precursor represented by the following Chemical Formula 1:
wherein, R1, R2, R3, R4, and R5 are independently H, or linear or branched alkyl of C1-C10; and R6 and R7 are independently linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10.
In addition, the present invention provides a method for preparing a strontium precursor represented by Chemical Formula 1, comprising: a) reacting a compound represented by the following Chemical Formula 2 with SrI2 to synthesize a compound represented by the following Chemical Formula 3; and b) reacting the compound of Chemical Formula 3 with a compound represented by the following Chemical Formula 4:
wherein, R1, R2, R3, R4, and R5 are independently H, or linear or branched alkyl of C1-C10.
wherein, R1, R2, R3, R4, and R5 are independently H, or linear or branched alkyl of C1-C10.
Wherein, R6 and R7 are independently H, or linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10.
Also, the present invention provides a strontium precursor represented by the following Chemical Formula 5:
wherein, R1, R2, and R3 are independently H, or linear or branched alkyl of C1-C10; R4, R5, R6, and R7 are independently H, or linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10; m and n are independently an integer of 1 to 3.
Further, the present invention provides a method for preparing a strontium precursor represented by Chemical Formula 5, comprising: a) reacting a compound represented by the following Chemical Formula 6 with Sr(NR8R9)2 to synthesize a compound represented by the following Chemical Formula 7; and b) reacting the compound of Chemical Formula 7 with a compound represented by the following Chemical Formula 8.
wherein, R1, R2, and R3 are independently H, or linear or branched alkyl of C1-C10; and R4 and R5 are independently H, or linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10; and m and n are independently an integer of 1 to 3.
wherein, R1, R2, and R3 are independently H, or linear or branched alkyl of C1-C10, R4 and R5 are independently H, or linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10, R8 and R9 are independently H, or linear or branched alkyl of C1-C10, or trialkylsilyl (—SiR3); and m and n are independently an integer of 1 to 3.
wherein, R6 and R7 are independently H, or linear or branched alkyl of C1-C10, or fluorinated alkyl of C1-C10.
Further, the present invention provides a method for growing a strontium-containing thin film using the strontium precursor of Chemical Formula 1 or 5.
Being superior in thermal stability and volatility, the strontium precursor represented by Chemical Formula 1 or 5 can be readily applied in the formation of quality strontium-containing thin films.
In accordance with an aspect thereof, the present invention addresses a strontium precursor represented by the following Chemical Formula 1:
wherein, R1, R2, R3, R4 and R5 are independently H, or linear or branched alkyl of C1-C10; and R6 and R7 are independently H, or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10.
The strontium precursor represented by Chemical Formula 1 in accordance with the present invention may be expressed as the general formula Sr(Cp′)(bdk). The preparation of this compound may start with the reaction of a cyclopentadiene compound represented by the following Chemical Formula 2 with SrI2 in an organic solvent, followed by allowing the resulting cyclopentadiene strontium represented by the following Chemical Formula 3 to undergo a substitution reaction with a beta-diketonate represented by the following Chemical Formula 4 in an organic solvent:
wherein, R1, R2, R3, R4 and R5 are independently H, or linear or branched alkyl of C1-C10.
wherein, R1, R2, R3, R4 and R5 are independently H, or linear or branched alkyl of C1-C10.
wherein, R6 and R7 are independently H, or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10.
Examples of the solvent useful for the reactions include toluene, tetrahydrofuran, hexane, and diethylether, with preference for toluene.
Reaction procedures of preparing the strontium precursor of the present invention may be as shown in the following Reaction Schemes 1 and 2.
wherein, R1, R2, R3, R4, and R5 are independently H, or linear or branched alkyl of C1-C10.
As shown in Reaction Scheme 1, a substitution reaction is carried out at room temperature for 12 hrs to 24 hrs in a solvent such as toluene, tetrahydrofuran, hexane, or diethylether to give Sr′CpI as a yellow solid.
wherein, R1, R2, R3, R4, and R5 are independently H, or linear or branched alkyl of C1-C10; and R6 and R7 are independently H, or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10.
Next, as illustrated in Reaction Scheme 2, the resulting compound Sr′CpI of Reaction Scheme 1 is allowed to undergo a substitution reaction with compound 3 in a solvent, such as toluene, tetrahydrofuran, hexane, or diethylether, at room temperature for 12 to 24 hrs. After filtration at a reduced pressure, the filtrate is dried in a vacuum to afford the novel strontium precursor as a dark yellow solid. During the procedures of Reaction Schemes 1 and 2, by-products may be produced. They may be removed by sublimation or recrystallization to give the novel strontium precursor of high purity.
In addition, the present invention addresses a strontium precursor represented by the following Chemical Formula 5:
wherein, R1, R2 and R3 are independently H, or linear or branched alkyl of C1-C10; R4, R5, R6, and R7 are independently H, or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10; and m and n are independently an integer of 1 to 3.
Also, the present invention is concerned with a strontium precursor represented by the following Chemical Formula 7.
wherein, R1, R2 and R3 are independently H, or linear or branched alkyl of C1-C10; R4 and R5 are independently H, or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10; R8 and R9 are independently H, or linear or branched alkyl of C1-C10, or trialkylsilyl (—SiR3); and m and n are independently an integer of 1 to 3.
The strontium precursor, represented by Chemical Formula 5, according to the present invention can be prepared by reacting a compound represented by the following Chemical Formula 6 as a starting material with Sr(NR8R9)2 in an organic solvent to synthesize a strontium compound represented by Chemical Formula 7, and then subjecting the strontium compound of Chemical Formula 7 to substitution reaction with a beta-diketonate represented by the following Chemical Formula 8.
wherein, R1, R2 and R3 are independently H, or linear or branched alkyl of C1-C10; R4 and R5 are independently H or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10; and m and n are independently an integer of 1 to 3.
(R6 and R7 are independently H or linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10.)
Examples of the solvent useful in the reactions include toluene, tetrahydrofuran, hexane, and diethylether, with preference for toluene.
Preparation of a strontium precursor according to the present invention may be as illustrated in the following Reaction Scheme 3.
wherein, R1, R2 and R3 are independently H, or linear or branched alkyl of C1-C10; R4 and R5 are independently H, linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10; and R8 and R9 are independently H, linear or branched alkyl of C1-C10, or trialkylsilyl (—SiR3); and m and n are independently an integer of 1 to 3.
As shown in Reaction Scheme 3, a substitution reaction is carried out at room temperature for 12 to 24 hrs in a solvent such as tetrahydrofuran, hexane, or diethylether to give an intermediate [Sr(aminoalkoxide)(amide)]2 (1) as a white solid.
Another reaction procedure of preparing a strontium precursor according to the present invention may be as illustrated in the following Reaction Scheme 4.
wherein, R1, R2 and R3 are independently H, or linear or branched alkyl of C1-C10; R4, R5, R6, and R7 are independently H, linear or branched alkyl of C1-C10, or linear or branched fluorinated alkyl of C1-C10; and R8 and R9 are independently H, linear or branched alkyl of C1-C10, or trialkylsilyl (—SiR3); and m and n are independently an integer of 1 to 3.
As illustrated in Reaction Scheme 4, the resulting compound Sr(aminoalkoxide)(amide) (1) of Reaction Scheme 3 is allowed to undergo a substitution reaction with tetramethyl heptane dione in a solvent, such as toluene, tetrahydrofuran, hexane, or diethylether, at room temperature for 12 to 24 hrs. After filtration at a reduced pressure, the filtrate is dried in a vacuum to afford the novel strontium precursor as a white crystalline solid. During the procedures of Reaction Schemes 3 and 4, by-products may be produced. They may be removed by sublimation or recrystallization to give the novel strontium precursor of high purity.
In these reactions, the reactants are used at stoichiometric ratios.
The novel strontium precursor represented by Chemical Formula 1 or 5 takes the form of a white solid at room temperature, and is thermally stable and highly volatile.
As a precursor for use in thin films, the novel strontium precursor of the present invention can be applied to chemical vapor deposition or atomic layer deposition both of which are widely used for the preparation of STO or BST.
A better understanding of the present invention may be obtained through the following examples that are set forth to illustrate, but are not to be construed as limiting the present invention.
In a 200 mL Schlenk flask, a solution of strontium iodide (0.4 g, 1.2 mmol, 1 eq) in THF (100 mL) was mixed with 2,3,5-triisopropyl cyclopentadiene potassium (0.27 g, 1.2 mmol, 1 eq) in THF (50 mL) while stirring for 24 hrs. After removing potassium iodide by filtration, the filtrate was reacted with 2,2,6,6-tetramethyl heptanedione sodium (0.25 g, 1.2 mmol) in THF (50 mL) while stirring for an additional 24 hrs. Distillation in a vacuum was carried out to dryness to afford the compound as a yellow solid: Yield 52%.
The compound Sr(3iPrCp)(tmhd) was analyzed for 1H-NMR (THF-d8), 1H-NMR (C6D6), and FT-IR, as follows.
NMR data: (1H, THF-d8) δ 1.07 (s, 18H), 1.03-1.1 (several singlets, 18H), 2.8 (m, 3H), 5.4 (s, 1H), 6.02 (s, 1H).
NMR data: (1H, C6D6) δ 1.05-1.4 (several singlets, 18H), 1.24 (s, 18H), 2.8 (m, 3H), 5.9 (s, 1H), 6.2 (s, 1H). (13C, C6D6) δ 22.9, 23.2, 26.3, 27.0, 28.9, 29.0, 30.2, 39.1, 41.6, 91.5, 124.02, 141.6, 143.9, 152.3, 201.6.
FT-IR (cm−1): 2960 (s), 2868 (m), 1580 (s), 1537 (w), 1500 (s), 1410 (s), 1357 (m), 1130 (w), 866 (w), 814 (w), 472 (w).
In a 200 mL Schlenk flask, a solution of strontium (0.4 g, 1.2 mmol, 1 eq) in THF (100 mL) was mixed with a solution of 1,3-di-t-butyl cyclopentadiene potassium (0.26 g, 1.2 mmol, 1 eq) in THF (50 mL) while stirring for 24 hrs. After removing potassium iodide by filtration, the filtrate was reacted with 2,2,6,6-tetramethyl heptanedione sodium (0.25 g, 1.2 mmol) in THF (50 mL) while stirring for an additional 24 hrs. Vaporization was carried out in a vacuum to dryness to afford the compound as a yellow solid: Yield 56%.
The compound Sr(2t-ButCp)(tmhd) was analyzed for 1H-NMR (C6D6), and FT-IR, as follows.
NMR data: (1H, C6D6) δ 1.13-1.32 (several singlets, 18H), 1.23 (s, 18H), 5.9 (s, 1H), 6.4 (singlets, 2H).
FT-IR (cm−1): 2960 (s), 2867 (m), 1598 (s), 1580 (s), 1500 (s), 1420 (s), 1360 (s), 1130 (w), 866 (w), 793 (w), 476 (w).
In a Schlenk flask, a solution of 1-((2-(dimethylamino)ethyl)(methyl)amino)-2-methylpropan-2-ol (demampH) (0.17 g, 1 mmol) in 15 mL of toluene was dropwise added to a solution of Sr(btsa)2.2DME (0.59 g, 1 mmol, 1 eq) in 15 mL of toluene. After stirring at room temperature for 15 hrs, the resulting reaction mixture was filtered, and the toluene was removed by distillation to dryness to afford the compound as a white solid (0.4 g, yield 95%). During quenching, X-ray crystals grew in the concentrated toluene.
The compound Sr(demamp)(btsa)(1) was analyzed for 1H-NMR and FT-IR, as follows.
1H NMR (C6D6, 300 MHz): δ 0.38 (s, 18H), 1.23 (s, 3H), 1.46 (s, 3H), 1.54 (m, 1H), 1.68 (m, 1H), 2.00 (m, 1H), 2.07 (s, br, 6H), 2.11 (d, 1H), 2.15 (s, 3H), 2.33 (d, 1H), 2.65 (m, 1H).
FTIR: (cm−1) 2945 (s), 2837 (w), 1484 (w), 1244 (w), 1059 (s), 961 (w), 883 (w), 817 (m), 659 (w).
Anal. Calcd for C30H78N6O2Si4Sr2: C, 42.76; H, 9.33; N, 9.97.
Found: C, 41.92; H, 9.15; N, 9.54.
In a Schlenk flask, a solution of tetramethylheptanedione (tmhd) (0.19 g, 1 mmol) in 5 mL of toluene was dropwise added to a solution of Sr(demamp)(btsa)(1) (0.84 g, 1 mmol) in 5 mL of toluene at room temperature, and then stirred for 12 hrs. After completion of the reaction, toluene was distilled, and the residue was dissolved in hexane, and filtered to give the compound as a white solid (0.41 g, Yield 93%). During quenching, X-ray crystals grew in the concentrated solution.
The resulting compound Sr(demamp)(tmhd)(2) was analyzed for 1H-NMR and FT-IR as follows.
1H NMR (C6D6, 300 MHz): δ 1.21 (s, br), 1.34 (s, 18H), 1.41 (s, br), 2.08 (s), 2.14 (s), 2.44 (s, br), 5.87 (s, 1H).
FTIR: (cm−1) 2950 (s), 2863 (m), 1589 (s), 1534 (w), 1504 (m), 1450 (s), 1423 (s), 1355 (m), 1225 (w), 1198 (w), 1185 (w), 864 (w), 470 (w).
Anal. Calcd for C40H80N4O6Sr2: C, 54.08; H, 9.08; N, 6.31.
Found: C, 53.71; H, 9.35; N, 6.01.
Analysis of Strontium Precursors
Sr(3iPrCp)(tmhd) of Example 1 and Sr(2t-ButCp)(tmhd) of Example 2 were measured for thermal stability, volatility, and degradation temperature by a thermogravimetric analysis (TGA) method. In the TGA method, the products were heated at a rate of 10° C./min to 900° C. while argon gas was introduced at a pressure of 1.5 bar/min. TGA graphs of the strontium precursor compounds synthesized in Examples 1 and 2 are given in
Structural examination was made on the strontium precursor compounds synthesized in Examples 3 and 4, using Bruker SMART APEX II X-ray Diffractometer, and their X-ray structures are depicted in
Also, a Thermo Gravimetric Analysis (TGA) method was used to examine the thermal stability, volatility, and degradation temperature of Sr(demamp)(tmhd)(2). In the TGA method, the product was heated at a rate of 10° C./min to 900° C. while argon gas was introduced at a pressure of 1.5 bar/min.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2012-0047439 | May 2012 | KR | national |
| 10-2012-0047440 | May 2012 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2013/003866 | 5/3/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2013/165212 | 11/7/2013 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20020034586 | Leedham | Mar 2002 | A1 |
| 20060178006 | Xu et al. | Aug 2006 | A1 |
| 20080085365 | Yamada | Apr 2008 | A1 |
| 20080171890 | Kim | Jul 2008 | A1 |
| 20080194088 | Srinivasan et al. | Aug 2008 | A1 |
| 20100034719 | Dussarrat et al. | Feb 2010 | A1 |
| 20100095865 | Xu et al. | Apr 2010 | A1 |
| 20100291299 | Cameron et al. | Nov 2010 | A1 |
| 20110212629 | Ivanov | Sep 2011 | A1 |
| Number | Date | Country |
|---|---|---|
| 10-2008-0113053 | Dec 2008 | KR |
| Entry |
|---|
| Zhao et al. “Synthesis of thin films of barium titanate and barium strontium titanate nanotubes on titanium substrates,” Materials Letters, 4 pages, Feb. 2005. |
| Mao et al., “Large-Scale Synthesis of Single-Crystalline Perovskite Nanostructures,” J. Am. Chem. Soc, 2 pages Aug. 2003. |
| Gong et al., “Titanium oxide nanotube arrays prepared by anodic oxidation,” J. Matter Res., 4 pages, Sep. 2001. |
| Padture et al., Hydrothermal Synthesis of Thin Films of Barium Titanate Ceramic Nano-Tubes at 200° C., J. Am. Ceram. Soc., 3 pages, Jul. 2003. |
| Phule et al., “review Low-temperature synthesis and processing of electronic materials in the BaO—Ti02 system,” Journal of Materials Science, 15 pages, 1990. |
| Hill et al., “Why are there so Few Magnetic Ferroelectrics?,” J. Phys. Chem. B, 16 Pages, Apr. 2000. |
| Asaoka et al., “Heteroepitaxial growth of SrO on hydrogen-terminated Si(100) surface,” Thin Solid Films, 4 pages, 2000. |
| Okamoto et al. “Blue emitting Sr 2 Ga 2 S 5: Ce phosphor thin films grown by multisource deposition,” Applied Physics Letters, 4 pages, Feb. 2000. |
| Tanaka et al., “Blue luminescent SrGa,S, : Ce thin films grown by molecular beam epitaxy,” Journal of Crystal Growth, 4 pages, 1995. |
| Paw et al., Low-Melting, mononuclear Tetahydrofuran Complexes of M (2,2,6,6-teramethyleheptane-3,5-dionate)2 (M=Ba,Sr) and Related Analogues, Inorg. Chem., 4 pages, Apr. 2000. |
| Mizushima et al., “Preparation of YBa2CU07-d thin film by laser-assisted metal-organic chemical vapor deposition using highly volatile fluorocarbon-based Ba source,” Journal of Materials Research, 5 pages, Apr. 1996. |
| Shamlian et al., “Metal-Organic Chemical Vapour Deposition of YBCO using a New, Stable and Volatile Barium Precursor,” J. Mater. Chem. 5 pages, Jan. 1994. |
| Gardiner et al. “Volatile Barium B-Diketonate Polyether Adducts. Synthesis, Characterization, and Metalloorganic Chemical Vapor Deposition”, 7 pages, Aug. 1991. |
| Number | Date | Country | |
|---|---|---|---|
| 20150175629 A1 | Jun 2015 | US |