The present invention relates to a susceptor for epitaxial growth reactors according to the preamble of claim 1 and to an epitaxial reactor using the same. In the field of epitaxial reactors for the microelectronic industry, with the term “susceptor” it is meant the heated support that houses one or more substrates during the epitaxial growth process; such support is generally heated by availing of its susceptance; such support generally maintains the name of “susceptor” even in those reactors where heating takes place in other ways, for example through lamps. The present invention is independent from the heating method.
Epitaxial growth susceptors may be divided into two big groups: those where substrates lie in a substantially horizontal position during the epitaxial growth process and those where substrates lie in a substantially vertical position (often few degrees from the vertical direction) during the epitaxial growth process. The present invention applies to the second group of susceptors.
With reference to
As shown in
As it is well known, the susceptor is placed inside a bell jar usually made of quartz; in the bell jar reaction gases are injected; the flow of reaction gases along side faces 5 (where the substrates are located) allows and determines the growth on the exposed faces of the substrates; clearly, there are many parameters affecting the growth.
The quality and the regularity of the grown material are of the utmost importance for the use of the thus treated substrates by the microelectronic industry, and are highly affected by the regularity and uniformity of the flow of the reaction gases along side faces 5 of the susceptor and therefore along the substrates. Such flow must therefore be controlled carefully.
In the past, it has been proposed by the applicant of the present patent application, for example in Italian patents No.1,231,547 applied for in 1989 and No.1,261,886 applied for in 1992 and in Italian patent application No.MI99A000607 filed in 1999, the use of first ribs placed along the edge side regions and such as to control the flow of reaction gases along the side faces.
While initially (in 1989) it was proposed that such ribs extend from the top of the body to the base of the body, later (from 1992 till today), at the implementation stage of the idea into products, it was preferred to limit their extension to the upper part of the body; this was due to two reasons: the assumed uselessness of the lower part of the ribs and the deformations of the ribs caused by the environment conditions in the reaction chamber, these deformations being proportional to their length.
Recently, it is becoming widespread to use, for the fabrication of microelectronic devices, also areas of the substrate really next to its edge (few millimetres).
From effected measurements it has been found that, if these areas really next to the edge are also considered, the uniformity of the grown material becomes considerably worse, particularly, for those substrates being nearest to the lower base.
Anyway, it has been checked that the simple idea of making the ribs longer down to, for example, the lower base is not effective; in fact, the lengthening of the ribs leads to an improvement in the thickness of the material grown in the areas next to the edge and to the rib but to a worsening, for example, in the areas next to the edge but far from the rib.
The present invention is aimed at solving the problem of the uniformity of the thickness of epitaxially grown substrates better than it has been done in the past.
Such problem is solved through the susceptor having the features set out in independent claim 1.
The use of second ribs separated and spaced from the first ribs and located in the lower part of the susceptor body considerably improves the uniformity in the thickness of the epitaxially grown substrate especially in the area of the substrate edge.
If necessary, further ribs may be provided in the central part of the substrate body. According to another aspect the present invention relates also to an epitaxial reactor having the features set out in independent claim 10 and using such susceptor.
Further advantageous features of the present invention are set out in the dependent claims.
The present invention will become clearer from the following description to be considered in conjunction with the accompanying drawings, wherein:
With reference to the figures, particularly
Second ribs 9 are therefore separated and suitably spaced from first ribs 8 and placed in such a way as to improve the thickness of the material grown in the areas next to the edge and to the rib but, at the same time, not to substantially worsen the thickness of the material grown elsewhere.
If necessary, particularly if the number of substrates per face is big, it may be advantageous to provide that along edge side regions 7 in the central part of body 2 third (and, if the case, further) ribs be provided adapted to control the flow of reaction gases along side faces 5; these are therefore separated and suitably spaced from both first ribs 8 and second ribs 9.
The fact that the ribs are of limited length, in addition to allowing a better flow control, reduces the mentioned problem of the deformations of the ribs; in fact, if the ribs get deformed (mainly due to the very high temperatures in the reaction chamber) the effect on the flow of reaction gases changes with time and therefore it is difficult to predict contrary to what would be required.
Such ribs, according to their simplest but still effective embodiment, may consist of strips; each strip is placed centrally along an edge side region 7.
Alternatively, such ribs may consist of couples of strips; a first strip of the couple is placed along a first edge of a side region 7 and a second strip of the couple is placed along a second edge of the same side region 7.
The ribs are preferably made of the same material of the susceptor body, that is graphite covered by silicon carbide; the use of quartz covered by silicon carbide is not advisable as it makes problems when cleaning the strips; in fact, these need to be periodically cleaned from the material deposited on themselves during the repeated epitaxial growth reactions.
Although it is advantageous to use the same material for both the ribs and the susceptor body, it is preferable that these be distinct parts for limiting the heat flow from the body to the ribs; in fact, if the ribs would substantially contribute to the heating of the substrates, this would be inevitably uneven.
If the strips are attached to the susceptor body, the strip may be shaped in such a way as to have at a first end a hook 11 or a tooth 12, as it is clearly shown in
Clearly, on the susceptor body there must be provided suitable holes or suitable recesses for the hook, the tooth and the pin: these are clearly shown in cross-section on the left side of
In order to further limit the heat flow from the body to the strips, the strip may be provided with a groove 14 on the side leaning on the susceptor body; in this way, the surface of the strip in contact with the body is extremely limited.
As already highlighted, the placement of the ribs is extremely important for achieving the desired effect.
It has been experimentally found that a good result is obtained when first ribs 8 extend from a level corresponding to about top 4 of body 2, to a level corresponding to about the centre of one of substrate areas 6, particularly the area 6a nearest to top 4 of body 2.
As regards second ribs 9, it has been experimentally found that a good result is obtained when second ribs 9 extend from a level corresponding to about the upper end of one of substrate areas 6, particularly the area 6b nearest to base 3 of body 2, to a level corresponding to about base 3 of body 2.
As regards the third ribs, these may be placed on all side regions 7, for example, just aligned with one of substrate areas 6 (perhaps with its upper half); in this way, they contribute to the control of the flow of reaction gases selectively over certain parts of side faces 5.
Equally important, in addition to the placement, is the choice of the sizes of the ribs, particularly their projection from the susceptor body; by the way, there is a proportion between the projection and the thickness of the grown material.
In order to better control the flow of reaction gases it is advantageous that first ribs 8 project from body 2 by a first quantity and that second ribs 9 project from body 2 by a second quantity; naturally, the first and the second quantities may be different.
In order to have an idea of the sizes of the projections, it may be simply said that, for a susceptor about 500 mm high and having a base diameter of about 350 mm, there have been tested projections from 1 mm to 10 min.
In case that third ribs are used, these may project from body 2 by a third quantity that may also be different from both the first quantity and the second quantity.
According to a further aspect, the present invention relates also to an epitaxial reactor that comprises at least a reaction chamber wherein there is located at least a susceptor 1 having the features described above.
In
Number | Date | Country | Kind |
---|---|---|---|
MI2001A001881 | Sep 2001 | IT | national |