System for preventing excess silicon consumption in ultra shallow junctions

Abstract

The present invention provides a system for preventing excess silicon consumption in a semiconductor wafer by depositing a metal layer (114) on top of a native oxide layer above a silicide layer (110) of the semiconductor wafer and then reducing the native oxide layer to form low resistance contacts. The native oxide layer is reduced using a rapid thermal annealing process within a temperature range to preserve the integrity of the silicide layer (110) and reduce excess silicon consumption. The temperature range can be greater than 350° C. and less than 615° C., but is optimal between 485° C. to 550° C.

Description

TECHNICAL FIELD OF THE INVENTION

[0002] The present invention relates generally to the field of semiconductor devices, and more particularly to a system for preventing excess silicon consumption in ultra shallow junctions.

BACKGROUND OF THE INVENTION

[0003] As CMOS devices scaled to the 0.1 um regime, the self-aligned silicide (SALICIDE) contact technology increasingly becomes an integrated part of the ultra-shallow junctions and Si consumption in shallow junctions due to silicide contacts becomes a critical issue. A lower Si consumption is desirable and essential to the formation of ultra-shallow source and drain junctions in deep sub-micron CMOS transistors. Although many efforts to minimize Si consumption during the silicidation process have been reported, little is know about the extra Si consumption induced by the post-silicide processes.

[0004] TiSi2, CoSi2 and NiSi are three most important silicide systems for CMOS fabrication. Although TiSi2 is widely used in 0.25 um technology node and above, the line width dependence of phase transformation limits its application for sub-0.25 um technology nodes. NiSi is independent of line width and consumes the least amount of Si for NiSi formation (the mono-silicide is a low resistivity phase as compared with low resistivity disilicide phase for Co and Ti). However, NiSi is also the least stable silicide. Temperatures of back end processing steps after NiSi formation needs to be kept below 600° C. to prevent NiSi silicide agglomeration and transformation into the high resistivity thermodynamically stable phase of NiSi2. CoSi2 does not suffer from the line width dependence effect and is stable for the thermal budget used in most CMOS devices. It is currently the dominant silicide used in SALICDE application. The main disadvantage of CoSi2 is that it consumes the most of Si during silicide formation among the three common silicides. For every 1 nm silicide formed, Si consumption for CoSi2 is 1.04 nm, which is more than TiSi2 (0.9 nm) and NiSi (0.82 nm). Si consumption is defined as the distance between the initial silicon interface and the base of the silicide. As the source/drain junctions are getting shallower, Si consumption becomes a limiting factor for the extendibility of CoSi2 process. As a result, there is a need for a system to prevent excess silicon consumption in ultra shallow junctions.

SUMMARY OF THE INVENTION

[0005] Ti deposition and its subsequent thermal process (rapid thermal annealing (RTA) at temperatures equal to or greater than 615° C.) induce excess Si consumption in addition to those consumed during the original silicidation process. Specifically, Ti atoms can destroy the integrity of the original CoSi2 layer by taking Si from Co to form TiSi2. The Si-poor Co atoms then diffuse to the junction to react with more Si to form CoSi2. In this process, more Si is consumed in addition to those consumed in the original silicidation process. The present invention provides a mechanism for reducing excess Si consumption using a process window where Ti layer can be used for reducing interfacial oxide to reduce contact resistance, while preventing the extra Si consumption. When optimal RTA temperature window is used between 485° C. and 550° C., the interfacial oxide is reduced to form low resistance contacts, while the RTA temperature is low enough to preserve the integrity of the original CoSi2 layer. This temperature window can be extended to as high as less than 615° C. and as low as 350° C. based on current processes or other temperature above the backend process steps with reduced effectiveness. This process may also be used in Ti/CoSi2/Si multilayer systems.

[0006] More specifically, the present invention provides a system for preventing excess silicon consumption in a semiconductor wafer by depositing a metal layer on top of a native oxide layer above a silicide layer of the semiconductor wafer and then reducing the native oxide layer to form low resistance contacts. The native oxide layer is reduced using a rapid thermal annealing process within a temperature range to preserve the integrity of the silicide layer and reduce excess silicon consumption. The temperature range can be greater than 350° C. and less than 615° C., but is optimal between 485° C. to 550° C.

[0007] Other features and advantages of the present invention will be apparent to those of ordinary skill in the art upon reference to the following detailed description taken in conjunction with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0008] For a better understanding of the invention, and to show by way of example how the same may be carried into effect, reference is now made to the detailed description of the invention along with the accompanying figures in which corresponding numerals in the different figures refer to corresponding parts and in which:

[0009] FIG. 1 shows a cross section of a CMOS transistor prior to the application of dielectric and metalization layers in accordance with the present invention;

[0010] FIG. 2A is the XPS depth profile of an as-received CoSi2 film on Si substrate;

[0011] FIG. 2B is the XPS depth profile of the as-deposited wafer with 200 Å IMP Ti on CoSi2;

[0012] FIG. 3A is the XPS depth profile of the as-deposited wafer after rapid thermal annealing at 725° C. for 30 seconds in accordance with the PRIOR ART;

[0013] FIG. 3B is the XPS depth profile of the as-deposited wafer after rapid thermal annealing at 615° C. for 30 seconds in accordance with the PRIOR ART;

[0014] FIG. 4 is the XPS depth profiles of the as-deposited wafer after rapid thermal annealing at 485° C. for 30 seconds in accordance with the present invention;

[0015] FIG. 5 shows the TOP-SIMS depth profiles of the as-deposited with 200 Å IMP Ti on CoSi2;

[0016] FIG. 6A shows the TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. in accordance with the PRIOR ART;

[0017] FIG. 6B shows the TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 615° C. in accordance with the PRIOR ART;

[0018] FIG. 7 shows the TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer, and the wafers after rapid thermal annealing at 485° C. in accordance with the present invention;

[0019] FIG. 8 shows the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer;

[0020] FIG. 9A shows the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. in accordance with the PRIOR ART;

[0021] FIG. 9B shows the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 615° C. in accordance with the PRIOR ART;

[0022] FIG. 10 shows the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. in accordance with the present invention;

[0023] FIG. 11A shows high resolution XPS spectra of Si 2s region of the as-received CoSi2 wafer along with the ion sputtering cycle;

[0024] FIG. 11B shows high resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer along with the ion sputtering cycle;

[0025] FIG. 12 shows high resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. in accordance with the PRIOR ART;

[0026] FIG. 13 shows high resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. along with the ion sputtering cycle in accordance with the present invention;

[0027] FIG. 14 shows the high resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer;

[0028] FIG. 15 shows the high resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. along with ion sputtering in accordance with the PRIOR ART; and

[0029] FIG. 16 shows the high resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. along with ion sputtering in accordance with the present invention.

DETAILED DESCRIPTION OF THE INVENTION

[0030] While the making and using of various embodiments of the present invention are discussed in detail below, it should be appreciated that the present invention provides many applicable inventive concepts, which can be embodied in a wide variety of specific contexts. The invention will now be described in conjunction with a n-type transistor using a CMOS process. It will be apparent to those of ordinary skill in the art that the benefits of the invention may be applied to other CMOS processes (as well as nMOS and pMOS), and transistor sizes. It will also be apparent to those of ordinary skill in the art that the invention may be applied to p-type transistors by reversing the conductivity types. The specific embodiments discussed herein are merely illustrative of specific ways to make and use the invention and do not limit the scope of the invention.

[0031] A CoSi2 surface is frequently, if not always, covered with a native oxide layer, mainly SiO2, as soon as it is exposed to air. This makes the contact resistance high. The most commonly used method to reduce the contact resistance is to deposit a thin Ti layer followed by high temperature (>700° C.) rapid thermal annealing (RTA) to reduce contact resistance. Excess Si consumption happens during the high temperature RTA of Ti/CoSi2 stack. These backend processes can cause excess Si consumption of approximately 30% more than that of the original silicide formation. As will be illustrated below, the mechanism of the excess Si consumption during the high temperature RTA is elucidated by TOF-SIMS, XPS and TEM cross-section analyses.

[0032] The present invention demonstrates that this excess Si consumption from ultra-shallow junctions can be prevented by optimizing the temperature window of the contact loop process, while at the same time reducing the interface oxide, which is contrary to conventional and well established practices of wafer fabrication. By annealing the Ti—CoSi2 interfacial system at a temperature between 485° C. and 550° C., Ti reacts with the interface oxide and eliminates the high resistivity layer at the interface. The anneal temperature is chosen to be low enough to prevent TiSi2 formation and maintain the integrity of the CoSi2 layer. In such a case, no excess Si consumption takes place. The present invention works in any situation involving SiOx. In some applications, it may be desirable to use an anneal temperature outside the optimal range in order to satisfy other fabrication parameters. As a result, some excess Si consumption would be acceptable. For example, this temperature window can be extended to as high as less than 615° C. and as low as 350° C. based on current processes or other temperature above the backend process steps.

[0033] Now referring to FIG. 1, a cross section of a CMOS transistor 100 prior to the application of dielectric and metalization layers in accordance with the present invention is shown. The substrate 102 is processed through the formation of isolation regions 106 and any well implants 110 and threshold adjust implants 104 as is well known in the art. A gate structure 108 is formed on the threshold adjust implant or gate isolation layer 104 above the substrate 102. Gate structure 108 may comprise a gate electrode and gate dielectric or a disposable gate structure as is known in the art. If the gate electrode and dielectric are formed at this point (as opposed to a disposable gate), the gate dielectric may be a remote-plasma nitrided oxide for smaller (about 0.1 micron) transistors. Other gate dielectric materials suitable include oxide or nitrided oxide by means other than remote-plasma nitridation. The gate pattern/etch may be accomplished with a deep UV surface-imaging lithography with linewidth reduction etch to achieve a short gate length.

[0034] Thin sidewall spacers 112 are then formed on the sidewalls of gate structure 108. Prior to formation of sidewall spacers 112, a thin thermal oxide of thickness 3-6 nanometers may be formed during a gate sidewall-reoxidation process to in part repair any gate etch damage to the underlying gate oxide. This thin thermal oxide from the sidewall re-oxidation process is not shown. Similarly, after formation of sidewall spacers 112, a thin thermal oxide of thickness about 2-3 nm may be formed if desired as a screen oxide before a subsequent implantation processes. Spacers 112 comprise a blocking material, preferably silicon nitride or silicon carbide. However, they may comprise any material having a smaller implant range than the substrate. The material is chosen to reduce the implant range of dopants thus preventing dopants from reaching the surface of substrate 102 under the spacer 118 during a subsequent implantations. The material may also reduce the lateral extension of dopants from the drain extension edge inwards to the channel at the surface of substrate 102 during subsequent implantation.

[0035] As previously mentioned, the silicide (CoSi2) surface is always covered with a native oxide layer, mainly SiO2, as soon as it is exposed to air. This makes the contact resistance high. A thin layer 114 of metal, such as Ti, Co, W, Ni, Pt or other acceptable material is deposited on these surfaces. The wafer is then subjected to RTA, which causes the Ti or other acceptable material to react with the interface oxide and eliminate the high resistivity layer at the interface, thus reducing the contact resistance. If the temperature of the RTA exceeds approximately 550° C., excess Si consumption will occur. The optimal temperature of the RTA to reduce excess Si consumption is between 485° C. and 550° C. The RTA temperature is chosen to be low enough to prevent TiSi2 formation and maintain the integrity of the CoSi2 layer. In such a case, little to no excess Si consumption takes place. The present invention will work in any situation involving SiOx. In some applications, it may be desirable to use an anneal temperature outside the optimal range in order to satisfy other fabrication parameters. As a result, some excess Si consumption would be acceptable. For example, this temperature window can be extended to as low as 350° C. based on current processes, or other temperature above the backend process steps. The remaining process steps to fabricate the device are well known in the art and will depend on the device being fabricated and the application for which it will be used.

[0036] Specific embodiments and applications of the present invention are hereafter described in greater detail. 200 Å IMP (ion metal plasma) Ti was deposited on as-received blanket CoSi2 wafers in an AMAT Endura 5500 system with a background pressure of 1×10−9 torr. The wafers were then processed through rapid thermal annealing (RTA) at different temperatures for 30 seconds. The samples were then characterized by X-ray photoelectron spectroscopy (XPS), time of flight secondary ion mass spectrometry (TOF-SISM) and transmission electron microscope (TEM). TOF-SIMS has better depth resolution than XPS, while XPS has advantage in quantifying relative atomic concentrations. The combination of XPS and TOF-SIMS results provides more complete chemical information on the interfacial systems, which is complemented by structural information obtained from TEM. XPS analysis was carried out in a Physical Electronic/5700 system using monochromated Al Ka radiation. Binding energies were calibrated by setting Co 2p3/2 binding energy of CoSi2 as 779.0 eV. TOF-SIMS analysis was carried out in a Physical Electronic/TRIFT I system using Cs+ ion for both sputtering and data acquisition. To minimize matrix effect, CsX+ ion was monitored, where X is the species of interest. For TEM analysis, an FEI CM200 system was used.

[0037] Referring now to FIG. 2A, the XPS depth profile of an as-received CoSi2 film on Si substrate is shown. N 200, O 202, Co 204 and Si 206 signals are shown. Flat distributions of Co 204 and Si 206 signals indicate uniform concentrations across CoSi2 layer. At the top surface of CoSi2 layer, a significant oxygen peak exists in the state of SiO2 (see FIG. 11A).

[0038] Now referring to FIG. 2B, the XPS depth profile of the as-deposited wafer with 200 Å IMP Ti on CoSi2 is shown. N 210, O 212, Si 214, Ti 216 and Co 218 signals are shown. The CoSi2 layer is present between the Si substrate and Ti layer. Co 218 and Si 214 distributions are relatively the same as those of the as-received sample. This indicates the Ti-deposition does not affect the stoichiometry of CoSi2 layer. An oxygen pile-up at the Ti/CoSi2 interface is observed. The oxygen is originated from the surface oxide on top of the as-received CoSi2, and it causes high contact resistance.

[0039] Referring now to FIG. 3A, the XPS depth profile of the as-deposited wafer after rapid thermal annealing at 725° C. for 30 seconds in accordance with the PRIOR ART is shown. N 300, O 302, Si 304, Ti 306 and Co 308 signals are shown. With RTA at 725° C. for 30 seconds, oxygen pile-up is still present in between the top Ti and TiSi2 layers, and significant amount of nitrogen is incorporated into the top Ti layer due to the RTA ambient. The oxygen pile-up is preserved because, at the RTA temperature of 725° C., Ti quickly diffuses through the interface oxide layer and reacts with CoSi2, while the interface oxygen diffuses slowly within Ti. In addition, Ti reacts with underlying CoSi2 to form TiSi2, in which CoSi2 is broken and resulted in CoSi2−x. In this process, Si-poor Co atoms diffuse into the junctions to react with more Si to form CoSi2. This is clearly evident by the XPS depth profile that shows the relatively thick TiSi2 layer in between the top Ti and CoSi2 layers. Excess Si from source/drain junctions is consumed during the above RTA process, in addition to those consumed during the original CoSi2 formation process. As junctions become shallower, this excess Si consumption may be a significant limiting factor for the extendibility of CoSi2.

[0040] Now referring to FIG. 3B, the XPS depth profile of the as-deposited wafer after rapid thermal annealing at 615° C. for 30 seconds in accordance with the PRIOR ART is shown. N 310, O 312, Si 314, Ti 316 and Co 318 signals are shown. It is seen that the inter layer consists of Ti 216 and Si 314 is significantly narrowed, with oxygen pile-up becoming slightly flatter.

[0041] Referring now to FIG. 4, the XPS depth profiles of the as-deposited wafer after rapid thermal annealing at 485° C. for 30 seconds in accordance with the present invention are shown. N 400, O 402, Si 404, Ti 406 and Co 408 signals are shown. By annealing the Ti—CoSi2 interfacial system at temperature around 485° C., Ti reacts with interface oxygen and the oxygen evenly diffuses through the Ti layer. The high resistivity layer at the interface is eliminated. The RTA temperature of 485° C. is low enough to prevent from the formation of TiSi2, therefore the integrity of the CoSi2 layer is maintained and no excess Si consumption takes place during this RTA process.

[0042] TOF-SIMS depth profiles with high depth resolution confirm the results of XPS depth profiles. The TOP-SIMS depth profiles of the as-deposited with 200 Å IMP Ti on CoSi2 are shown in FIG. 5. O 500, Si 502, N 504, Ti 506 and Co 508 signals are shown.

[0043] The TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. in accordance with the PRIOR ART are shown in FIG. 6A. O 600, Si 602, N 604, Ti 606 and Co 608 signals are shown. The TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 615° C. in accordance with the PRIOR ART are shown in FIG. 6B. O 610, Si 612, N 614, Ti 616 and Co 618 signals are shown.

[0044] The TOP-SIMS depth profiles of the as-deposited 200 Å IMP Ti—CoSi2 wafer, and the wafers after rapid thermal annealing at 485° C. in accordance with the present invention are shown in FIG. 7. O 700, Si 702, N 704, Ti 706 and Co 708 signals are shown.

[0045] In addition, TOF-SIMS depth profiling indicates that Ti diffuses deeply through the entire CoSi2 layer to Si substrate after RTA at 725° C. (FIG. 6A). Meanwhile, Si signal intensity increases along the depth profiling through the CoSi2 layer, which indicates a degradation of CoSi2 integrity. For the wafer after 485° C. RTA, Ti signal intensity reaches the detection limit of TOF-SIMS shortly after reaching into CoSi2 layer, and a flat distribution of Si signal through CoSi2 layer indicates the integrity of CoSi2 is preserved (comparing with FIGS. 5, 6A, 6B and 7). N signal variation is not clearly detected in all TOF-SIMS depth profiles due to the very low secondary ion yield of CsN+.

[0046] Now referring to FIG. 8, the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer are shown. After the 200 Å IMP Ti deposition, two separate layers of Ti 804 and CoSi2 802 are shown above the substrate 800. The Ti layer 804 measured ˜196 Å and the CoSi2 layer 802 measured ˜142 Å. An interfacial oxide layer can be clearly seen in the TEM cross-section image.

[0047] Referring now to FIG. 9A, the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. n accordance with the PRIOR ART are shown. The three layers, CoSi2 layer 902, Ti layer 904 and TiSi2 interlayer 906, are clearly present above the substrate 900. The top Ti layer 904 thickness is reduced to ˜135 Å and the TiSi2 interlayer 906 is measured ˜144 Å. In addition, the thickness of the CoSi2 layer 902 increases to ˜161 Å as well.

[0048] Now referring to FIG. 9B, the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 615° C. in accordance with the PRIOR ART are shown. Three layers are again present, but with a much thinner interlayer than that of FIG. 9A. The thickness of the top Ti layer 904, the TiSi2 interlayer 906 and the CoSi2 layer 902 are measured ˜149, ˜70 and ˜161 Å, respectively.

[0049] Referring now to FIG. 10, the TEM cross-section images of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. in accordance with the present invention are shown. It is seen that the two layers of Ti 1004 and CoSi2 1002 are very well preserved above substrate 1000. Assuming both TiSi2 interlayer and CoSi2 layer 1002 are stoiciometric, and utilizing Si consumption data of 1.04 for CoSi2 and 0.9 for TiSi2 for calculation, the Si consumptions of the wafers after RTA at 725, 615 and 485° C. are 297, 230, and 172 Å, respectively. This result is in good agreement with the XPS and TOF-SIMS depth profiling analyses that excess Si consumption takes place when the IMP Ti—CoSi2 system is processed at a RTA temperature higher than 615° C. There exists an optimal RTA temperature process window where the interfacial oxide is reduced to improve contact resistance. Meanwhile, the RTA temperature is low enough so that no TiSi2 is formed and CoSi2 integrity is preserved. In this way, no excess Si is consumed. Results from the wafer after RTA at 485° C. is an example of processing with the optimal RTA process window.

[0050] The interface reaction of Ti—CoSi2 system with different RTA temperatures is further supported by the chemical state information obtained from the high-resolution XPS core spectra. The high resolution XPS spectra of Si 2s region of the as-received CoSi2 wafer, the as-deposited 200 Å IMP Ti—CoSi2 wafer, and the wafers after RTA at 725 and 485° C., along with the ion sputtering cycle, are shown in FIGS. 11A, 11B, 12 and 13. FIG. 11A shows high resolution XPS spectra of Si 2s region of the as-received CoSi2 wafer along with the ion sputtering cycle and FIG. 11B shows high resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer along with the ion sputtering cycle. Si 2s was chosen to calculate the elemental composition and to represent the chemical state information, because Si 2p and Co 3s peaks partially overlap to each other. At the top surface of the as-received CoSi2 wafer, the Si 2s peak has two resolved peaks corresponding to the Si chemical states in Co disilicide (151.5 eV) and SiO2 (154.9 eV) (FIG. 11A). The surface oxide thickness is estimated to be about 30-40 A from XPS peak ratio analysis. This is in agreement with XPS and TOF-SIMS depth profiling results that a thin SiO2 layer is present at the top surface of the as-received CoSi2. After IMP Ti deposition without RTA (FIG. 11B), only one peak is present at the Ti—CoSi2 interface with a binding energy of 150.7 eV. Sputtering into the CoSi2 layer, Si 2s peak shifts to 151.5 eV, corresponding to CoSi2. This suggests that IMP Ti deposition process dissociates SiO2 into free oxygen and metallic Si (or TiSix), though oxygen is still piled up at the Ti—CoSi2 interface.

[0051] Now referring to FIG. 12, high-resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. in accordance with the PRIOR ART is shown. It is clearly seen that Si 2s peak has a binding energy of 150.7 eV within the sputtering time window of 10-20 minutes (according to FIG. 3A), which corresponding to the chemical state of TiSi2. After 20 minutes sputtering, Si 2s binding energy shifts up to 151.5 eV, which corresponds to the chemical state of CoSi2.

[0052] Referring now to FIG. 13, high resolution XPS spectra of Si 2s region of the as-depositied 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. along with the ion sputtering cycle in accordance with the present invention is shown. Similar to that of FIG. 11B, only one peak is present at the Ti—CoSi2 interface with a binding energy of 150.7 eV and no SiO2 is present. Sputtering into the CoSi2 layer, Si 2s peak shifts to 151.5 eV, corresponding to CoSi2. This indicates that no significant amount of TiSi2 is formed from Ti—CoSi2 system with 485° C. RTA.

[0053] FIG. 14 shows the high-resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer.

[0054] FIG. 15 shows the high-resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 725° C. along with ion sputtering in accordance with the PRIOR ART.

[0055] FIG. 16 shows the high resolution XPS spectra of Ti 2p region of the as-deposited 200 Å IMP Ti—CoSi2 wafer after rapid thermal annealing at 485° C. along with ion sputtering in accordance with the present invention. The binding energy of the as-deposited IMP Ti 2p3/2 is 454.4 eV, corresponding to metallic Ti. After the RTA at 725° C., two trends of Ti 2p peaks are present. From the wafer surface to about 10 minutes sputtering, Ti 2p3/2 has a binding energy of 455.3 eV, corresponding to the chemical states of TiN/TiO.

[0056] This is confirmed by FIG. 3A, which shows that significant amounts of oxygen and nitrogen are present in the top Ti layer. Within the sputtering time window of 10-20 minutes, Ti 2p3/2 binding energy shifts down to 454.6 eV, which corresponds to the chemical state of TiSi2. Similar to FIG. 14, FIG. 16 shows no significant peak shift of Ti 2p3/2 after the Ti—CoSi2 wafer is rapid thermally annealed at 485° C. The Ti 2p3/2 binding energy of this bulk sample is 454.6 eV. Considering no silicide formation is observed from this sample (FIGS. 4 and 7), it can be concluded that Ti in Ti—CoSi2 system after the 485° C. RTA exits as TiO1−x.

[0057] The foregoing illustrates the impact of Ti deposition and its subsequent thermal treatment using XPS, TOF-SIMS and TEM. CoSi2 surface is covered with a native oxide upon exposure to air. This oxide layer may be reduced by depositing a Ti layer, followed by RTA. However, if the temperature is too high (greater than or equal to 615° C.), Ti atoms can destroy the integrity of the original CoSi2 layer by taking Si from Co to form TiSi2. The Si-poor Co atoms then diffuse to the junction to react with more Si to form CoSi2. In this process, more Si is consumed in addition to those consumed in the original silicidation process. When the Ti—CoSi2 interfacial system is processed in an optimal RTA temperature window, the interfacial oxide is reduced to form low resistance contacts, while the RTA temperature is low enough to preserve the integrity of the original CoSi2 layer. Therefore, the excess Si consumption is prevented.

[0058] The embodiments and examples set forth herein are presented to best explain the present invention and its practical application and to thereby enable those skilled in the art to make and utilize the invention. However, those skilled in the art will recognize that the foregoing description and examples have been presented for the purpose of illustration and example only. The description as set forth is not intended to be exhaustive or to limit the invention to the precise form disclosed. Many modifications and variations are possible in light of the above teaching without departing from the spirit and scope of the following claims.

Claims

1. A method for preventing excess silicon consumption in a semiconductor wafer, comprising the steps of: depositing a metal layer on top of a native oxide layer that resides upon a silicide layer; and reducing the native oxide layer to form low resistance contacts, using a rapid thermal annealing process within a selected temperature range.

2. The method as recited in claim 1, wherein the temperature range is greater than 350° C. and less than 615° C.

3. The method as recited in claim 1, wherein the temperature range is about 485° C. to 550° C.

4. The method as recited in claim 1, wherein the temperature range is approximately 485° C.

5. The method as recited in claim 1, wherein excess silicon consumption is substantially reduced.

6. The method as recited in claim 1, wherein excess silicon consumption is reduced to approximately zero.

7. The method as recited in claim 1, wherein the metal layer comprises a metal selected from the group consisting of Ti, Co, W, Ni and Pt.

8. The method as recited in claim 1, wherein the metal layer is Ti.

9. The method as recited in claim 1, wherein the silicide layer is CoSi2.

10. A method for preventing excess silicon consumption in a semiconductor wafer, comprising the steps of: depositing a metal layer on top of a native oxide layer that resides upon a CoSi2 layer; and reducing the native oxide layer to form low resistance contacts, using a rapid thermal annealing process at a temperature greater than 350° C. and less than 615° C.

11. The method as recited in claim 10, wherein the temperature is about 485° C. to 550° C.

12. The method as recited in claim 10, wherein the temperature is approximately 485° C.

13. The method as recited in claim 10, wherein excess silicon consumption is substantially reduced.

14. The method as recited in claim 10, wherein excess silicon consumption is reduced to approximately zero.

15. The method as recited in claim 10, wherein the metal layer comprises a metal selected from the group consisting of Ti, Co, W, Ni and Pt.

16. The method as recited in claim 10, wherein the metal layer is Ti.

17. A system for preventing excess silicon consumption in a semiconductor wafer, comprising: deposition of a metal layer atop a native oxide layer that resides upon a CoSi2 layer, wherein the metal layer comprises a metal selected from the group consisting of Ti, Co, W, Ni and Pt; and reduction of the native oxide layer to form low resistance contacts using a rapid thermal annealing process at a temperature of about 485° C. to 550° C.

18. The system as recited in claim 17, wherein excess silicon consumption is substantially reduced.

19. The system as recited in claim 17, wherein excess silicon consumption is reduced to approximately zero.

20. The system as recited in claim 17, wherein the metal layer is Ti.