This application claims priority to Taiwan Application Serial Number 108128361, filed Aug. 8, 2019, which is herein incorporated by reference.
The present disclosure relates to a temporary bonding composition, a temporary bonding film, a composite film, a method for temporary bonding workpiece and a semiconductor wafer packaging. More particularly, the present disclosure relates to a temporary bonding composition, a temporary bonding film, a composite film with the excellent thermal compression and the solvent resistance, and a method for temporary bonding workpiece and a semiconductor wafer packaging using thereof.
With the thinning of the semiconductor devices, the temporary bonding/debonding technology becomes one of the important technologies in the recent years. In general, the workpiece (i.e. wafer) should be bonded with the supported substrate by the temporary bonding adhesive, so as to perform the subsequent process to the workpiece. After the process is completed, the temporary bonding adhesive is removed to separate the workpiece from the supported substrate.
However, in the conventional temporary adhesion technique, the adhesive layer mainly relies on the adhesive property during the pressing process. Therefore, when a thick film is coated, such as by the spin coating, the bar coating, etc., a thick edge phenomenon is caused, so that it is impossible to achieve no overflow under the high deformation, and flatten the thickness difference of the thick side of 30 to 40 μm and take into account the chemical resistance at the same time. Furthermore, when the thick film is pressed, there will be an uncompressed area at the edge due to the deformation and the lack of flexibility of the press carrier.
Therefore, how to provide an improved temporary bonding composition having the excellent thermal compression and the solvent resistance with appropriate debonding method, is the goal of the relevant industry.
According to one aspect of the present disclosure, a temporary bonding composition is provided. The temporary bonding composition includes a polyfunctional crosslinker, a polymer and a solvent. The polyfunctional crosslinker includes a compound containing at least two functional groups selected from the group of blocked isocyanate groups, alkenyl ether groups, and alkoxyhydrocarbyl groups. Each of the blocked isocyanate groups is an isocyanate group protected by a blocking agent. The polymer has a functional group reacting to the polyfunctional crosslinker.
According to another aspect of the present disclosure, a temporary bonding film is provided. The temporary bonding film includes a polyfunctional crosslinker, a polymer and a light absorbing material. The polyfunctional crosslinker includes a compound containing at least two functional groups selected from the group of blocked isocyanate groups, alkenyl ether groups, and alkoxyhydrocarbyl groups. Each of the blocked isocyanate groups is an isocyanate group protected by a blocking agent. The polymer has a functional group reacting to the polyfunctional crosslinker.
According to further another aspect of the present disclosure, a composite film is provided. The composite film includes a detachable supported film and the temporary bonding film according to the aforementioned aspect. The temporary bonding film is disposed on a surface of the detachable supported film.
According to still another aspect of the present disclosure, a method for temporary bonding workpiece includes step as follows. A combining step is performed, wherein an adhesive layer is formed on a surface of at least one substrate and/or at least one workpiece. A bonding step is performed, wherein the substrate and the workpiece are bonded by the adhesive layer. A second heating step is performed, wherein the substrate and the workpiece are heated. A processing step is performed, wherein the workpiece is processed. A debonding step is performed, wherein the adhesive layer is irradiated with a laser so as to separate the workpiece from the substrate. The adhesive layer is formed by the temporary bonding composition according to the aforementioned aspect.
According to yet another aspect of the present disclosure, a semiconductor wafer package is provided. The semiconductor wafer package includes the temporary bonding composition according to the aforementioned aspect.
The present disclosure can be more fully understood by reading the following detailed description of the embodiment, with reference made to the accompanying drawings as follows:
The present disclosure will be further exemplified by the following specific embodiments. However, the embodiments can be applied to various inventive concepts and can be embodied in various specific ranges. The specific embodiments are only for the purposes of description, and are not limited to these practical details thereof.
A temporary bonding composition of the present disclosure includes a polyfunctional crosslinker, a polymer and a solvent. Preferably, the temporary bonding composition of the present disclosure can further include a light absorbing material. The aforementioned components will be described in detail hereafter.
In the present embodiments, the polyfunctional crosslinker includes a compound containing at least two functional groups selected from the group of blocked isocyanate groups, alkenyl ether groups, and alkoxyhydrocarbyl groups. Preferably, the polyfunctional crosslinker of the present disclosure can include at least one compound selected from the group of a compound containing at least two blocked isocyanate groups, a compound containing at least two alkenyl ether groups, and a compound containing at least two alkoxyhydrocarbyl groups. Each of the blocked isocyanate groups is an isocyanate group protected by a blocking agent. Based on the total weight of the temporary bonding composition, a content of the polyfunctional crosslinker can be in a range of 0.5 wt % to 20 wt %. Preferably, the content of the polyfunctional crosslinker can be in a range of 0.8 wt % to 15 wt %. More preferably, the content of the polyfunctional crosslinker can be in a range of 2 wt % to 10 wt %.
According to the foregoing compound containing at least two blocked isocyanate groups, which can include a structure represented by formula (I):
wherein n1 is an integer greater than 2, R1 is an organic group containing a substituted or an unsubstituted alkylene group, alicyclic ring, aromatic ring, dimer of isocyanate or trimer of isocyanate. The aforementioned “substituted” means that any atom on the organic group can be substituted by other hetero atoms. For example, the aforementioned substituted alkyl group can be any —CH2— substituted by oxygen atom, —CH═CH—, or —C≡C—, such as an organic group containing an ether group. Any carbon atom of the aforementioned substituted aromatic ring can be but not limited to be substituted by an N atom. Each R2 is independently a residue of the blocking agent.
The aforementioned blocking agent can be but not limited to alcohols, phenols, pyridines, oximes, mercaptans, thiophenols, amides, cyclic amides, imides, imidazolines, imidazoles, triazoles, amidines, hydroxamic acid esters, pyrazoles, amines, formates, active methylenes, ureas or diketones. Preferably, the blocking agent can be but not limited to butanol, ethanol, isopropanol, phenol, methylphenol, ethylphenol, cyclohexanol, butyl cellosolve, 2-butylphenol, 2-hydroxypyridine, butanone oxime, cyclohexanone oxime, acetone oxime, acetaldehyde oxime, 1-dodecanethiol, pentafluorothiophenol, thiophenol, acetanilide, methylacetanilide, caprolactam, butyrolactam, valerolactam, maleimide, succinimide, 2-phenylimidazole, imidazole, 2-methylimidazole, 2-phenylimidazole, triazole, benzotriazole, 3,5-dimethylpyrazole, 3-methylpyrazole, 2-methyl-4-ethyl-5-methylpyrazole, diisopropylamine, aniline, ethyl malonate, dimethyl malonate, ethyl acetoacetate, methyl acetoacetate, diethyl malonate, phenylurea or thiourea. Furthermore, depending on the process temperature of the semiconductor wafer package, the blocking agent is preferably selected the structure dissociated by heating at a temperature range from 90° C. to 200° C. For example, caprolactams, butanone oximes, ethyl malonates, etc.
Furthermore, after heating the aforementioned compound of formula (I), a crosslinkable structure having an isocyanate group can be formed, and can react to a resin. The structure can be but not limited to a functional group represented by any one of formula (i-1), formula (i-2), formula (i-3), formula (i-4), formula (i-5), formula (i-6), formula (i-7) and formula (i-8), wherein R3 is a divalent organic group containing a substituted or an unsubstituted alkyl group, alkenyl group, alkynyl group, alicyclic ring or aromatic ring:
According to the foregoing compound containing at least two alkenyl ether groups, which can include a structure represented by formula (II):
R4—(O—CH═CH2)n
wherein R4 is an organic group containing a substituted or an unsubstituted alkylene group, alicyclic ring or aromatic ring. The aforementioned “substituted” means that any atom on the organic group can be substituted by other hetero atoms. For example, the aforementioned substituted alkyl group can be any —CH2— substituted by oxygen atom, —CH═CH—, or —C≡C—, such as an organic group containing an ether group. Any carbon atom of the aforementioned substituted aromatic ring can be but not limited to be substituted by an N atom, and n2 is the integer greater than 2. Specifically, the compound of the formula (II) can be but not limited to a compound represented by any one of formula (II-1), formula (II-2), formula (II-3) and formula (II-4), wherein x is the integer greater than 1:
According to the foregoing compound containing at least two alkoxyhydrocarbyl groups, which can include a structure represented by formula (III), formula (IV) or formula (V):
wherein R5, R7, R8 and R19 are each independently an organic group containing an alkyl group, an alicyclic ring or an aromatic ring, or hydrogen, preferably the organic group containing the alkyl group. R6, R9 and R11 are organic groups containing an aromatic ring or a heterocyclic ring, n3, n4 and n5 are each independently an integer greater than 2. Specifically, the compound of the formula (III) can be but not limited to a compound represented by any one of formula (III-1), formula (III-2), formula (III-3), formula (III-4) and formula (III-5):
Specifically, the compound of the formula (IV) can be but not limited to a compound represented by any one of formula (IV-1), formula (IV-2) and formula (IV-3):
Specifically, the compound of the formula (V) can be but not limited to a compound represented by formula (V-1):
In the present embodiments, the polymer has a functional group reacting to the polyfunctional crosslinker. Specifically, the polymer can be a polyamic acid, a polyimide, a polybenzoxazole, a copolymer or a mixture thereof including at least one of a hydroxyl group, a carboxyl group or an amine group. Based on the total weight of the temporary bonding composition, a content of the polymer can be in a range of 5 wt % to 60 wt %. Preferably, the content of the polymer can be in a range of 10 wt % to 55 wt %. More preferably, the content of the polymer can be in a range of 10 wt % to 52 wt %.
In the present embodiments, the solvent can be an organic solvent. The organic solvent can be included but not limited to N-methylpyrrolidone, N, N-dimethylformamide, N, N-dimethylacetamide, N, N-diethylformamide, N-methylcaprolactam, dimethyl sulfoxide, γ-butyrolactone, γ-butyrolactam, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol mono-n-propyl ether and ethylene glycol monobutyl ether, etc. The aforementioned solvent can be used for mixing two or more. In addition, the solvent that can dissolve the polymer or the solvent that mixing two or more can be used as the solvent of the present disclosure. Based on the total weight of the temporary bonding composition, a content of the solvent can be in a range of 5 wt % to 95 wt %. Preferably, the content of the solvent can be in a range of 20 wt % to 80 wt %.
In the present embodiments, the light absorbing material being added as appropriate depends on the wavelength range of the light source applied during the debonding process. The light absorbing material added in the material of the present disclosure can expand the wavelength range of the light source when debonding. The aforementioned light absorbing material can be an organic pigment, an inorganic pigment or a dye. Preferably, the inorganic pigment can be carbon black, titanium black, titanium oxide, iron oxide, titanium nitride or silica fume. Based on the total weight of the temporary bonding composition, a content of the light absorbing material can be in a range of 0 wt % to 30 wt %. Preferably, the content of the light absorbing material can be in a range of 0.5 wt % to 25 wt %.
A temporary bonding film according to one embodiment of the present disclosure includes a polyfunctional crosslinker, a polymer and a light absorbing material. The polyfunctional crosslinker, the polymer and the light absorbing material can refer to the aforementioned paragraph, and will not be described herein. Furthermore, a glass transition temperature (Tg) of the temporary bonding film can be less than 200° C.
A composite film according to one embodiment of the present disclosure includes a detachable supported film and the temporary bonding film. The temporary bonding film is disposed on a surface of the detachable supported film. Specifically, the temporary bonding film is obtained by mixing the polyfunctional crosslinker, the polymer, the light absorbing and the solvent, then coated on the surface of the detachable supported film and heated to remove the some or all solvents. The temporary bonding film of the composite film can be peeled.
The aforementioned detachable supported film can include but not limited to a synthetic resin film with the film thickness of 15 μm to 200 μm, such as polyethylene terephthalate (PET), polyethylene, polypropylene, polycarbonate or polyvinyl chloride. Furthermore, the aforementioned method of coating can include but not limited to the spin coating, the slit coating, the bar coating, the screen printing, etc.
Please refer to
In the step 110, a combining step is performed, wherein an adhesive layer is formed on a surface of at least one substrate and/or at least one workpiece. Specifically, the adhesive layer can be disposed on a surface of the substrate only, the adhesive layer can be disposed on a surface of the workpiece only, or the adhesive layer can be disposed on a surface of the substrate and a surface of the workpiece simultaneously. In addition, the number of the substrate and the number of the workpiece can be in a one-to-one relationship, a many-to-one relationship or a one-to-many relationship. In other words, the method for temporary bonding workpiece 100 according to the present disclosure, one substrate can be used to bear one workpiece, a plurality of substrates can be used to jointly bear one workpiece, or one substrate can be used to bear a plurality of workpieces simultaneously.
The aforementioned adhesive layer is formed by a temporary bonding composition. The temporary bonding composition can refer to the aforementioned paragraph, and will not be described herein. The aforementioned workpiece can be but not limited to a chip, a wafer or a micro device for semiconductor manufacturing. The micro device for semiconductor manufacturing can be but not limited to the micro device obtained by a metallurgical treatment, such as depositing a multilayer structure on the wafer, wiring, and then cutting. The specific examples of the micro device can include but not limited to a field-effect transistor, an optical sensor, a logic chip, a Known Good Die (KGD), and the size of the micro device ranges from 1 micrometer to several millimeters. The aforementioned substrate can be made of a glass, a silicon wafer, or other materials that can be penetrated by a laser.
In the step 120, a bonding step is performed, wherein the substrate and the workpiece are bonded by the adhesive layer. For convenience of explanation, the structure in which the substrate and the workpiece bonded by the adhesive layer is a joint structure hereafter. Specifically, the step 120 can be achieved by thermal compression bonding, that is, the workpiece, the adhesive layer and the substrate are bonded by applying the temperature and the pressure. The temperature can range from the room temperature to 250° C., and the pressure can range from 0.5 kgf/cm2 to 5 kgf/cm2.
In the step 130, a second heating step is performed, wherein the substrate and the workpiece are heated. The temperature of the second heating step can range from 90° C. to 200° C., so as to perform the crosslinking curing reaction. Furthermore, the temperature and time of the second heating step can be appropriately adjusted depending on the actual demands, such as the selection of the type of functional groups of the polyfunctional crosslinker.
In the step 140, a processing step is performed, wherein the workpiece is processed. The processing method can be include but not limited to copper plating, etching, polishing, applique or printing.
In the step 150, a debonding step is performed, wherein the adhesive layer is irradiated with a laser so as to separate the workpiece from the substrate. The aforementioned laser can be a solid laser, such as a YAG laser, a ruby laser, a YVO4 laser and an optical fiber laser, a liquid laser, such as a pigment laser, a gas laser, such as a CO2 laser, an excimer laser, an Ar laser and a He-Ne laser, a semiconductor laser, a diode pump solid state laser (DPSSL), a free electron laser, etc.
Therefore, the method for temporary bonding workpiece 100 of the present disclosure is favorable for fixing the workpiece on the substrate temporarily by the temporary bonding composition of the present disclosure. That is, during the processing, the workpiece can be fixed stably on the substrate. After the processing, the workpiece can be separated from the substrate easily, and the temporary bonding composition can be removed from the workpiece easily. Furthermore, the method for temporary bonding workpiece 100 of the present disclosure is favorable for the high-temperature processes, thus the method for temporary bonding workpiece 100 of the present disclosure can be used as the temporary bonding/debonding technology of the semiconductor. For example, the workpiece can be the wafer, and the substrate can be the support substrate. The required supporting force during the processing of the wafer is provided by the support substrate, the wafer can be prevented from being broken during the processing. Then, after the process, the wafer is separated from the substrate.
Please refer to
In the step 111, a coating step is performed, wherein the temporary bonding composition is coated on a surface of the substrate and/or the workpiece. The method of coating can be include but not limited to the spin coating, the slit coating, the bar coating, the screen printing, etc.
In the step 112, a first heating step is performed, wherein the temporary bonding composition is heated, so as to convert the temporary bonding composition into the adhesive layer. The step 112 can be performed at the temperature of 50° C. to 200° C. for 0.5 hours to 2 hours, and the main purpose of the step 112 is removing some or all solvents of the temporary bonding composition. Furthermore, the temperature and the time of the step 112 can be adjusted appropriately according to the actual demands, such as the type of solvent or the amount of solvent.
Please refer to
Please refer to
In the step 113, a composite film is provided. The composite film can refer to the aforementioned paragraph, and will not be described herein.
In the step 114, a transferring step is performed, wherein the surface of the substrate and/or the workpiece is contacted with the temporary bonding film of the composite film and heated so as to transfer the temporary bonding film to the surface of the substrate and/or the workpiece and convert into the adhesive layer. Specifically, the step 114 can be heated at the temperature of 50° C. to 200° C. with rolling or vacuum thermal compression bonding, so that the temporary bonding film is transferred to the surface of the substrate and/or the workpiece. After the detachable supported film is removed, the step 114 is heated continuously at the temperature of 50° C. to 200° C. for 0.5 hours to 2 hours, so that the temporary bonding film is converted into the adhesive layer, and then performed the bonding step. The main purpose of heating in the step 114 is softening the temporary bonding film to favorable for transferring. Therefore, the subsequent transfer effect can be increased by adjusting the glass transition temperature.
Please refer to
Please refer to
As shown in
Please refer to
The step 710 is for performing a combining step, the step 720 is for performing a bonding step, the step 730 is for performing a second heating step, the step 740 is for performing a processing step, and the step 750 is for performing a debonding step. The step 710 to the step 750 can refer to the related descriptions of the step 110 to the step 150 in
In the step 760, a dissolving step is performed, wherein the residue of the adhesive layer on the workpiece is dissolved and removed by a cleaning solvent after the debonding step. The aforementioned cleaning solvent can be but not limited to N, N-diethyl formamide (DEF), cyclohexanone, N-methyl pyrrolidinone (NMP) or gamma-butyl lactone (GBL). However, in order to select the solvent which is less harmful to the environment or the human body, the cleaning solvent of the present disclosure is preferably N, N-diethyl formamide as the main solvent.
The polymer according to one embodiment of the present disclosure can be performed the polycondensation reaction in the organic solvent by using a diamine and a dianhydride as a reactant, and stirred at the temperature of 25° C. to 50° C. for 8 hours to 12 hours to obtain a reaction solution containing polyamic acid, wherein the polycondensation reaction is adjusted according to the amount of the reaction. The aforementioned reaction solution containing polyamic acid is refluxed in the dehydration ring-closure reaction process by adding toluene at the temperature of 120° C. to 150° C. for 3 hours to 6 hours to obtain a reaction solution containing polyimide or an amic acid/imide copolymer. The amic acid/imide copolymer is a partially cyclized polyamic acid, wherein the cyclization ratio of the amic acid/imide copolymer can be greater than 70%, preferably, the cyclization ratio of the amic acid/imide copolymer can be greater than 90%. Finally, toluene is distilled by the aforementioned reaction solution of polyimide or the amic acid/imide copolymer, and the solid content is adjusted by the level of reduced pressure distillation or adding the organic solvent to obtain the amic acid/imide copolymer solution or the polyimide solution.
The aforementioned organic solvent, used to dissolve reactants and products, includes the organic solvent having the better solubility and the organic solvent having the poor solubility. The organic solvent having the better solubility includes but not limited to N-methylpyrrolidone, N, N-dimethylformamide, N, N-dimethylacetamide, N-methylcaprolactam, dimethyl sulfoxide, tetramethylurea, hexamethyl phosphoramide, γ-butyrolactone, and pyridine. The organic solvent having the poor solubility includes but not limited to methanol, ethanol, isopropanol, n-butanol, cyclohexanol, ethylene glycol, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, diethyl ether, acetone, methyl ethyl ketone, cyclohexanone, methyl acetate, ethyl acetate, tetrahydrofuran, dichloromethane, chloroform, 1,2-dichloroethane, benzene, toluene, xylene, n-hexane, n-heptane and n-octane. The aforementioned organic solvents can be used singly or mixed two or more. Since the organic solvent is used to dissolve reactants and products, thus, any organic solvent that can dissolve reactants and products can be used, but is not limited to the above.
The semiconductor wafer package of the present disclosure includes the aforementioned temporary bonding composition. The temporary bonding composition can refer to the aforementioned paragraph, and will not be described herein. The structure and manufacturing method of the semiconductor wafer package are conventional and will not be further described herein.
The property of thermal compression: at 2 Kg/cm2, provided a laminate of the temporary bonding composition between two of the substrate and/or the workpiece and the laminate are thermal compressed, and determined the proportion of the area of the temporary bonding composition to the whole area of the substrate after thermal compression. The proportion of the area of the temporary bonding composition to the whole area of the substrate is greater than 95% indicated that excellent, between 95% and 75% indicated that great, between 75% and 50% indicated that good, less than 50% indicated that poor.
The property of solvent resistance after baking: the temporary bonding composition is formed into a film by baking, and then immersed in the solvent (AP7880T, purchased from Applichem Technology Corporation) at 70° C., and determined the degree of film damage. The degree of film damage is less than 10% indicated that excellent. The degree of film damage is between 10% and 20% indicated that great. The degree of film damage is between 20% and 40% indicated that good. The degree of film damage is greater than 40% indicated that poor.
The property of the laser releasing ability: irradiating the adhesive layer with the laser until the debond occurred, the cumulative laser power is greater than or equal to 2 W and less than 5 W indicated that great, the cumulative laser power is greater than or equal to 5 W and less than 8 W indicated that good, and the cumulative laser power is greater than 8 W indicated that poor.
The diamine used in Synthesis Example is shown in Table 1. In Table 1, the trade name of diamine (A-1) is BisAPAF, the trade name of diamine (A-2) is JEFFAMINE-D400, and y is in accordance with the product specifications.
The dianhydride used in Synthesis Example is shown in Table 2. In Table 2, the trade name of the dianhydride (B-1) is BPADA.
The diamine and the dianhydride are sequentially added to the solvent according to the ratio shown in Table 3, so as to prepare the amic acid/imide copolymer solution or the polyimide solution. The solid content of the amic acid/imide copolymer solution or the polyimide solution is 20 wt %. Specifically, the diamine and the dianhydride are performed the polycondensation reaction in the organic solvent according to the ratio shown in Table 3, and stirred at the temperature of 25° C. to 50° C. for 8 hours to 12 hours to obtain a reaction solution containing polyamic acid, wherein the polycondensation reaction is adjusted according to the amount of the reactants. The aforementioned reaction solution containing polyamic acid is refluxed in the dehydration ring-closure reaction process by adding toluene at the temperature of 120° C. to 150° C. for 3 hours to 6 hours to obtain a reaction solution containing polyimide or the amic acid/imide copolymer. The cyclization ratio of the amic acid/imide copolymer is greater than 90%. Finally, toluene is distilled from the aforementioned reaction solution of polyimide or the amic acid/imide copolymer, and the solid content is adjusted by the level of reduced pressure distillation or adding the organic solvent to obtain the polyimide solution or the amic acid/imide copolymer solution. The solid content of the polyimide solution or the amic acid/imide copolymer solution is 20 wt %.
The polyfunctional crosslinker used in Example/Comparative Example is shown in Table 4. In Table 4, the polyfunctional crosslinker (a-1), the polyfunctional crosslinker (a-2) and the polyfunctional crosslinker (a-3) are compounds containing at least two blocked isocyanate groups formed by isocyanate groups combined with different blocking agents. The polyfunctional crosslinker (b-1) and the polyfunctional crosslinker (b-2) are compounds containing at least two alkenyl ether groups. The polyfunctional crosslinker (c-1) and the polyfunctional crosslinker (c-2) are compounds containing at least two alkoxyhydrocarbyl groups. Furthermore, the polyfunctional crosslinker (d-1) is a thermal crosslinker of an epoxy compound, and the polyfunctional crosslinker (d-2) is a non-blocking isocyanate.
The light absorbing material used in Example/Comparative Example is carbon black, which is bought from Daxin Materials Co., Ltd. The trade name of carbon black is PK-127, and the average particle diameter of carbon black is 120 nm.
The type and the content of the polymer, the polyfunctional crosslinker, the solvent and the light absorbing material are according to Table 5 to prepare the temporary bonding composition of Example/Comparative Example.
The evaluation of the joint structure of Example/Comparative Example is performed, such as the properties of the thermal compression, the solvent resistance after baking, the laser releasing ability, etc. The laser wavelengths used in Example/Comparative Example and the evaluation results are shown in Table 6.
As shown in Table 5 and Table 6, the polymer of Comparative Example 1 does not contain an OH functional group, which causes the solvent resistance after baking of Comparative Example 1 poor. Furthermore, the polyfunctional crosslinkers of Comparative Example 2 to Comparative Example 4 are different from Example 1 to Example 10. Comparative Example 2 does not add the polyfunctional crosslinker of the present disclosure. The polyfunctional crosslinker of Comparative Example 3 has an epoxy group structure. The polyfunctional crosslinker of Comparative Example 4 is a non-blocking isocyanate. It can be indicated that without adding the polyfunctional crosslinker of the present disclosure and the use of polyfunctional crosslinker not of the present disclosure do not have excellent thermal compression and solvent resistance simultaneously. Therefore, the temporary bonding composition of Example 1 to Example 10 of the present disclosure, the thermal compression are excellent, great or good, the solvent resistance after baking are excellent or great, and the laser releasing ability are excellent or great. It is shown that the temporary bonding composition of the present disclosure has the excellent thermal compression and solvent resistance, which is favorable for the application of the temporary bonding/debonding technique.
Although the present disclosure has been described in considerable detail with reference to certain embodiments thereof, other embodiments are possible. Therefore, the spirit and scope of the appended claims should not be limited to the description of the embodiments contained herein.
It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the present disclosure without departing from the scope or spirit of the disclosure. In view of the foregoing, it is intended that the present disclosure cover modifications and variations of this disclosure provided they fall within the scope of the following claims.