Patent Grant
8110919
The present invention relates to thermal interfaces for use in connection with a heat dissipation arrangement involving heat-generating electronic devices, and more particularly to a thermal interface member incorporating a substantially thermally transparent, conformable, and non-tacky surface layer that retains such characteristics above solder reflow temperatures.
Thermal interfaces are widely used in heat dissipating applications where excess thermal energy is desired to be transferred from one location to another. The thermal interface is commonly positioned between such locations in a manner to accommodate the desired heat transfer in an efficient and mechanically useful manner. Example applications of such thermal interfaces is in the electronics industry, wherein electronic devices must be cooled in some fashion in order to maintain minimum threshold performance characteristics. A common method of cooling such electronic devices is through heat dissipation away from the heat-generating electronic devices. Such heat dissipation may be accomplished, for example, by thermally coupling the electronic device to a heat sink, which typically possesses a relatively high thermal dissipation capacity. Common heat sinks exhibit high heat dissipation characteristics through features such as materials, surface area, and exposure to cooling media.
Thermal coupling of heat-generating elements, such as electronic devices, to heat sinks may be facilitated by thermal interface materials and structures. For example, direct physical coupling between a heat-generating element and a heat sink may be difficult due to relative external geometries, materials, and spatial restrictions in the vicinity of the heat-generating element. In this case, thermal interfaces can act as the physical connection mechanism between the heat-generating element and the heat sink without significant impedance to heat transfer. Moreover, because heat transfer can be significantly impeded at thermal barriers where thermal energy must pass through media of relatively low thermal conductivity, thermal interfaces can increase the efficiency of heat transfer to a heat sink by minimizing the presence of thermal barriers. For example, thermal interfaces having relatively low modulus values can “conform” to surface irregularities in the heat-generating element and the heat sink, thereby minimizing and/or eliminating voids between surfaces that can be filled with relatively low thermal conductivity media such as air. Consequently, thermal interfaces have been found to significantly enhance heat transfer away from a variety of heat-generating devices.
In some applications, thermal interfaces have utilized relatively low modulus materials such as microcrystalline waxes, and silicone greases, gels, and waxes, in order to provide a “conformability” characteristic to the thermally conductive interface. Conformability of the interface may be achieved through materials having low modulus values at room temperature, or may instead be achieved as a result of a “phase changing” material which significantly softens at temperatures at or below the operating temperatures of the heat-generating devices to which the interface is coupled. The relative softness of the interface material can result in a surface tackiness that hinders such handling of such interfaces, such as in assembly of the thermal interfaces to respective components.
To overcome this problem, it has been found that the provision of an “anti-blocking” or release layer formed on at least one outer surface of the thermal interface assists production, assembly, and handling of the thermal interface. Moreover, such an outer non-tacky release layer serves to provide significant protection against contamination to the remainder of the thermal interface. In some cases, the anti-blocking or release layer may comprise a liner film that must be removed prior to the point in time when the thermal interface is placed into contact with the heat-generating device. This removal operation has frequently proven to be bothersome, and is time consuming and labor intensive. In other cases, the anti-blocking or release layer may be integrally formed, or permanently secured to, the remainder of the thermal interface. In such cases, however, the anti-blocking layer significantly inhibits the overall conformability of the interface.
In addition to the above, thermal interfaces are routinely installed in heat dissipation arrangements in a specific order in which the thermal interface is first secured to the heat sink, with the resultant combination then secured to a previously constructed package, such as an integrated circuit board. This protocol has been followed primarily due to the fact that mounting the thermal interface to components of an electronic package in its construction process is difficult and messy to handle. Even for thermal interfaces with anti-blocking layers, temperatures reached in solder reflow processes to secure electronic components to the package compromise the effectiveness of the anti-blocking layer.
In view of the above, therefore, it is a principal object of the present invention to provide a thermal interface incorporating one or more highly thermally conductive surfaces which remain non-tacky at or above solder reflow temperatures, while also enabling good overall conformability to adjacent surfaces.
It is a further object of the present invention to provide a thermal interface member having a non-tacky surface layer that is highly thermally conductive, conformable, and remains non-tacky at or above solder reflow temperatures.
It is another object of the present invention to provide a method for constructing a thermal interface, wherein the surface layer of such interface is deposited on a release substrate and subsequently placed in registration with a bulk layer of the interface.
It is a still further object of the present invention to provide a method for constructing a package by securing a thermal interface to a package component prior to solder reflow, and subsequently securing the combination to a heat sink.
By means of the present invention, excess thermal energy generated by an electronic component may be efficiency dissipated to a heat sink or other thermal dissipater. In particular, the present invention provides a thermal interface that is highly conformable, but yet remains non-tacky at or above solder reflow temperatures. Consequently, the thermal interface of the present invention facilitates handling and thermal package assembly operations while providing a highly thermally conductive pathway from a heat-generating electronic device to a heat dissipater.
In a particular embodiment, the thermal interface member of the present invention includes a bulk layer having a thermal conductivity of at least about 0.5 W/m·K, and a surface layer that is disposed on at least a portion of at least one surface of the bulk layer. The surface layer includes a maximum cross-sectional thickness of less than about 10 microns, a thermal conductivity along at least the thickness dimension of at least about 50 W/m·K, and a melting point exceeding a solder reflow temperature. In some cases, the melting point of the surface layer is at least about 300° C.
In another embodiment, the thermal interface member of the invention includes a thermally conductive polymer-based bulk layer and a metallic surface layer disposed on at least a portion of at least one of first and second surfaces of the bulk layer. The metallic surface layer has a maximum cross-sectional thickness dimension of less than about 10 microns.
An apparatus for use in a heat dissipating arrangement includes a heat-generating component and a thermal interface member thermally coupled to the heat-generating component and having a thermal conductivity of at least about 0.5 W/m·K. The thermal interface member includes a bulk layer and a surface layer disposed on at least a portion of a surface of the bulk layer. The surface layer has a maximum cross-sectional thickness dimension of less than about 10 microns, a melting point exceeding a solder reflow temperature, and a modulus that is greater than about 107 Pa.
In a further aspect of the invention, a method for constructing a thermal interface member is provided by depositing a thermally conductive material on a substrate to a thickness of less than about 10 microns so as to form a coated substrate, and placing the coated substrate in registration with a bulk layer surface of the thermal interface member, such that the thermally conductive material of the coated substrate is contacted with the bulk layer surface. Finally, the substrate is separated from the thermally conductive material, such that the thermally conductive material remains in contact with the bulk layer surface as a surface layer.
In a further aspect, a package includes a support structure having a first surface, an electronic component having a mounting portion and a heat dissipation surface, wherein the mounting portion is coupled to the first surface of the support structure, and a thermal interface member that is thermally coupled to the heat dissipation surface of the electronic component. The thermal interface member includes a bulk layer and a surface layer, wherein the bulk layer has a thermal conductivity of at least about 0.5 W/m·K, and the surface layer has a maximum cross-sectional thickness of less than about 10 microns. Moreover, the surface layer has a thermal conductivity of at least about 50 W/m·K and a melting point exceeding a solder reflow temperature.
A method for constructing an electronic component package includes providing a thermal interface member having a bulk layer with a thermal conductivity of at least about 0.5 W/m·K, and a surface layer disposed on at least a portion of a surface of the bulk layer, with the surface layer having a maximum cross-sectional thickness of less than about 10 microns, a melting point exceeding a solder reflow temperature, and a thermal conductivity of at least about 50 W/m·K. The method further includes providing a support structure having a first surface, and providing an electronic component having a mounting portion and a heat dissipation surface. The thermal interface member is thermally coupled to the electronic component by placing the bulk layer of the thermal interface member in contact with the heat dissipation surface of the electronic component. Prior to, or subsequent to, the thermal coupling, the mounting portion of the electronic component may be mounted to the first surface of the support structure. Subsequent to mounting the mounting portion of the electronic component to the first surface of the support structure, a heat sink is thermally coupled to the thermal interface member.
The objects and advantages enumerated above together with other objects, features, and advances represented by the present invention will now be presented in terms of detailed embodiments described with reference to the attached drawing figures which are intended to be representative of various possible configurations of the invention. Other embodiments and aspects of the invention are recognized as being within the grasp of those having ordinary skill in the art.
With reference now to the drawing figures, and first to
Bulk layer 12 is preferably thermally conductive at least along axis “z”, and may be a conformable material. In some embodiments, bulk layer 12 may be a phase-changing material. For example, bulk layer 12 may comprise a microcrystalline wax or a silicone-based polymer including silicone waxes, silicone greases, and silicone gels. Further examples of formulations useful in bulk layer 12 include those described in U.S. Pat. Nos. 5,950,066 and 6,197,859, which are incorporated herein by reference. In embodiments wherein bulk layer 12 is a phase-changing material, bulk layer 12 may have a melting point in the range of between about 40° C. and about 80° C. As such, bulk layer 12 may become at least partially liquid at temperatures encountered during normal operation of the heat-generating device or devices in connection with which thermal interface member 10 is being used. The phase changing characteristic provides a highly conformable interface for making good thermal contact with respective heat dissipation surfaces, such as surfaces of the heat-generating device. As is known in the art, phase-changing thermal interface materials enable relative ease of handling at room temperature while being highly conformable at operating temperatures.
In some embodiments, bulk layer 12 may further include thermally conductive particulate matter dispersed therein to enhance the thermal conductivity of bulk layer 12. A variety of thermally conductive particulate matter may be utilized to aid in the thermal conductivity of bulk layer 12, including, for example, alumina, aluminum nitride, boron nitride, graphite, silicon carbine, diamond, metallic powders and combinations thereof, with an average particle size of up to about 200 microns. In typical embodiments, the particulate filler material may be provided in bulk layer 12 at a concentration of between about 10 and 95 percent by weight. The loading levels of the particulate filler can affect the overall modulus of bulk layer 12. Accordingly, it is desired to maintain an operating temperature modulus of bulk layer 12 of no greater than about 106 Pa. In some applications, however, modulus values greater than 106 Pa for bulk layer 12 are permissible.
Bulk layer 12 may be formed with a thickness dimension “a” of between about 50 and 500 microns, with thicknesses in the range of between about 100 and 150 microns being most commonly employed.
Surface layer 14 is preferably a highly thermally conductive body comprised of one or more thermally conductive materials. Surface layer 14 may be disposed at, for example, all or a portion of first and/or second surfaces 16, 20 of bulk layer 12. Surface layer 14 is disposed along a substantially entire area of first surface 16 of bulk layer 12 in the embodiment illustrated in
An additional aspect in the enablement of ease of handling of thermal interface member 10 in production and assembly operations is the provision of surface layer 14 that exhibits a “non-tacky” surface. Such a characteristic may be accomplished through a variety of mechanisms, such as material type and material phase. Therefore, it is one aspect of the invention to provide surface layer 14 with a non-tacky upper surface 18. For some applications, it is desired that surface layer 14 be non-tacky both at room temperature and at elevated temperatures, such as above a solder reflow temperature. For example, thermal interface member 10 may be utilized in connection with a package assembly process which involves elevated temperatures, including temperatures at which solder reflow occurs to secure various package components to one another. Consequently, it is desired that surface layer 14 remain substantially intact at such elevated temperatures, as well as retain a non-tacky surface characteristic.
In order to accomplish the goals stated above, surface layer 14 may be in solid form, and have a melting point which exceeds a respective solder reflow temperature. For typical applications, solder reflow temperatures range between about 200 and about 260° C., depending upon the type of solder utilized. Accordingly, it is desired that surface layer 14 have a melting point temperature which is greater than the solder reflow temperature of the respective solder being utilized. In some cases, the melting point of surface layer 14 is greater than about 300° C. The following Table 1 demonstrates example solder alloy compositions, and their respective phase-change temperatures:
In order to maximize the effectiveness of thermal interface member 10, surface layer 14 is preferably thermally conductive, and may be substantially “thermally transparent”, in that the thermal conductivity of surface layer 14 may be significantly greater than the thermal conductivity of bulk layer 12. In some embodiments, surface layer 14 may have a thermal conductivity of at least about 50 W/m·K, and may typically have a thermal conductivity of between about 200 and 800 W/m·K. The thermal conductivities identified above refer to the thermal conductivity at least along axis “z”, but may also hold true along all directional axes.
An additional aspect of the present invention is the overall conformability of thermal interface member 10. As described above, it is an important feature of thermal interfaces to conform well to surfaces against which the interfaces are mounted so as to minimize thermal barriers and to thereby enhance thermal conductivity. Conventional thermal interfaces incorporating an “anti-blocking” or release layer typically either require that such layer be manually removed prior to installation, or such layers, when left in place in the interface, reduce thermal performance of the interface as a result of a lack of conformability of such layer and/or a relatively low thermal conductivity of the layer material itself. Accordingly, surface layer 14 may be both highly thermally conductive, as described above, and highly conformable. Surface layer 14 may therefore have a thickness of less than about 10 microns. Surface layer 14 is effective even in situations where its modulus is greater than 106 Pa due to its thinness.
Applicants have determined that one manner in which to accomplish the above-described conformability in surface layer 14 is through the provision of a very small thickness dimension “b” of surface layer 14. Depending upon the materials utilized for surface layer 14, thickness dimension “b” may be less than about 10 microns, and may typically be between about 2 and 6 microns. Thickness dimension “b” of surface layer 14 may refer to a maximum cross-sectional thickness of surface layer 14.
Surface layer 14 may comprise one or more of a variety of materials compatible with the aspects described above. A particular class of materials that Applicants have found to be useful in the surface layers of the present invention are metals and/or metal complexes which are capable of being deposited into a thin layer, such as less than about 6 microns in thickness. Example materials for surface layer 14 include aluminum, copper, silver, and copper-tungsten. Other materials and material combinations, however, are also contemplated as being useful in surface layer 14. An example of another useful material is graphite.
It is contemplated that first surface 14 may be provided at bulk layer 12 through one of a variety of processes, including, for example, vapor deposition, plasma polymerization, spray coating, sputtering, and the like. One method for applying surface layer 14 to bulk layer 12 that will be described herein for example purposes is vapor deposition of a metal material as surface layer 14.
As illustrated in
Release liner substrate 42 may be placed in a vacuum chamber and transferred between an unwind roll and a wind-up roll, both positioned in the vacuum chamber. Aluminum spools are then placed at receptacles within the vacuum chamber, wherein the aluminum spools are heated at the receptacles to an evaporative temperature of the aluminum, while the vacuum chamber is substantially evacuated. Vapor-state aluminum is then emitted from the aluminum spools, and is deposited on the moving substrate positioned about 12 inches from the aluminum receptacles.
The thickness “b” of surface layer 14 at release liner substrate 42 may be controlled by the speed of the substrate within the vapor deposition chamber. Typically, substrate 42 is operated between the unwind roll and wind-up roll at a speed of between about 400-1200 ft/min while vapor deposition is occurring. Once the substrate 42 has been exposed to this metal vapors, the chamber is restored to atmospheric pressure. In some embodiments, the vapor-deposited substrate may pass over a chill roll to bring the vapor-state metal to solid-state on the substrate prior to being rolled at the wind-up roll.
Once the deposited material reaches a predetermined minimal thickness, such as between about 2 and 6 microns, the coated substrate 44 is transferred to a calendaring operation as illustrated in
The coated substrate is then placed into a calendaring operation in an orientation with the release liner coming into contact with the calendaring rolls, and the surface layer material being exposed for registration with a bulk layer 12. The registration of the surface layer with the bulk layer causes the surface layer to adhere to the bulk layer with greater strength than the coupling between the surface layer and its respective release liner substrate. As a result, the substrate is then removed from the surface layer while the surface layer remains in contact with the bulk layer. Individual thermal interface members may then be die cut to desired size. In this form, the thermal interface members have opposing non-tacky surfaces so as to be easily handled in transport and package assembly steps. Typically, the release liner positioned at, for example, second surface 20 of bulk layer 12 is removed immediately prior to installation of thermal interface member at the heat-generating device.
Thermal interface member 10 may be used in connection with heat dissipation from a heat-generating component package. As illustrated in
In the embodiment illustrated in
Electronic device 72 is used herein in a comprehensive sense, and is intended to include components incorporated in a variety of electronic systems, such as data processing, communications, power supply systems, and the like. Example devices contemplated as electronic component 72 include semiconductor devices such as transistors and diodes, as well as passive components.
Electronic component 72, in the embodiment illustrated in
As shown in
The arrangement illustrated in
The processes described above are contrasted with the conventional process for manufacturing an electronic component package, in that conventional techniques first mount the thermal interface member to the heat sink, and subsequently connect the electronic component/support structure combination to the heat sink/thermal interface member combination. Typically, this final assembly step is undertaken by original equipment manufacturers who sell complete electronic component packages. The final assembly step, however, requires a process step for removing the release liner from the thermal interface member (such as release liner 46 from bulk layer 12) prior to connection of the thermal interface member/heat sink combination to the electronic component. This process step is time consuming, and can sometimes result in damage to the thermal interface member, resulting in product loss and/or reduced product performance. The thermal interface member of the present invention enables coupling of the thermal interface member to the electronic component/support structure combination at the package manufacturer. Where the thermal interface member is mounted to the electronic component prior to electronic component to the support structure, the thermal interface member of the present invention is capable of withstanding solder reflow temperatures required in securing the electronic component to the support structure. Moreover, surface layer 14 acts to protect bulk layer 12 from contaminants during the solder reflow process. The electronic components may also be shipped in current surface mount technology (SMT) format without concern for the thermal interface member sticking to the SMT tapes and reels, because of the non-tacky surface presented by surface layer 14 prior to coupling to heat sink 92.
The invention has been described herein in considerable detail in order to comply with the patent statutes, and to provide those skilled in the art with the information needed to apply the novel principles and to construct and use embodiments of the invention as required. However, it is to be understood that the invention can be carried out by specifically different devices and that various modifications can be accomplished without departing from the scope of the invention itself.
This application is a divisional of U.S. Non-Provisional patent application Ser. No. 11/964,219, filed on Dec. 26, 2007 and entitled “Thermal Interface with Non-Tacky Surface”, the content of which being incorporated herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4819857 | Mizuishi et al. | Apr 1989 | A |
| 4938992 | Mears | Jul 1990 | A |
| 5300809 | Makamura et al. | Apr 1994 | A |
| 5679457 | Bergerson | Oct 1997 | A |
| 5738936 | Hanrahan | Apr 1998 | A |
| 5950066 | Hanson et al. | Sep 1999 | A |
| 6090484 | Bergerson | Jul 2000 | A |
| 6162663 | Schoenstein et al. | Dec 2000 | A |
| 6165612 | Misra | Dec 2000 | A |
| 6197859 | Green et al. | Mar 2001 | B1 |
| 6344104 | Sekiya et al. | Feb 2002 | B1 |
| 6359334 | Jiang | Mar 2002 | B1 |
| 6399209 | Misra et al. | Jun 2002 | B1 |
| 6657296 | Ho et al. | Dec 2003 | B2 |
| 6657297 | Jewram et al. | Dec 2003 | B1 |
| 6667548 | O'Connor et al. | Dec 2003 | B2 |
| 6974723 | Matayabas et al. | Dec 2005 | B2 |
| 20020034651 | Yamagata et al. | Mar 2002 | A1 |
| 20040009353 | Knowles et al. | Jan 2004 | A1 |
| 20050013119 | Misra | Jan 2005 | A1 |
| 20050077618 | McCutcheon et al. | Apr 2005 | A1 |
| 20060246276 | Chung | Nov 2006 | A1 |
| 20070164424 | Dean et al. | Jul 2007 | A1 |
| 20070235861 | Chien et al. | Oct 2007 | A1 |
| 20070241303 | Zhong et al. | Oct 2007 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20100309634 A1 | Dec 2010 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11964219 | Dec 2007 | US |
| Child | 12858849 | US |