Claims
- 1. A blend of polymeric materials comprising
(A) of from about 1 to about 80 percent by weight (based on the combined weights of Components A and B) of at least one substantially random interpolymer; wherein said interpolymer;
(1) contains of from about 0.5 to about 50 mole percent of polymer units derived from;
a) at least one vinyl or vinylidene aromatic monomer, or b) at least one hindered aliphatic or cycloaliphatic vinyl or vinylidene monomer, or c) a combination of at least one vinyl or vinylidene aromatic monomer and at least one hindered aliphatic or cycloaliphatic vinyl or vinylidene monomer; (2) contains of from about 50 to about 99.5 mole percent of polymer units derived from at least one aliphatic α-olefin having from 2 to 20 carbon atoms; (3) has a melt index (I2) of from about 0.01 to about 100 g/10 min; and (4) has a molecular weight distribution (Mw/Mn) of from about 1.5 to about 20; (B) of from about 20 to about 99 weight percent based on the combined weights of Components A, and B of one or more engineering thermoplastics.
- 2. The blend of claim 1 wherein;
(1) Component A is present in an amount of from about 1 to about 65 percent by weight (based on the combined weights of Components A and B); (2) Component A contains of from about 20 to about 50 mole percent of polymer units derived from;
a) at least one of said vinyl or vinylidene aromatic monomers, Component A(1)(a), represented by the following general formula; 8 wherein R1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to about 4 carbon atoms, preferably hydrogen or methyl; each R2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to about 4 carbon atoms, preferably hydrogen or methyl; Ar is a phenyl group or a phenyl group substituted with from 1 to 5 substituents selected from the group consisting of halo, C1-4-alkyl, and C1-4-haloalkyl; and n has a value from zero to about 4; or b) at least one of said hindered aliphatic or cycloaliphatic vinyl or vinylidene monomers, Component A(1)(b), represented by the following general formula; 9 wherein A1 is a sterically bulky, aliphatic or cycloaliphatic substituent of up to 20 carbons, R1 is selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to about 4 carbon atoms, preferably hydrogen or methyl; each R2 is independently selected from the group of radicals consisting of hydrogen and alkyl radicals containing from 1 to about 4 carbon atoms, preferably hydrogen or methyl; or alternatively R1 and A1 together form a ring system; or (c) a combination of at least one of said vinyl or vinylidene aromatic monomer and at least one of said hindered aliphatic or cycloaliphatic vinyl or vinylidene monomer; (3) Component A contains of from about 50 to about 80 mole percent of polymer units derived from at least one of said aliphatic α-olefins selected from the group consisting of ethylene or a combination of ethylene and at least one of propylene, 4-methyl pentene, butene-1, hexene-1 or octene-1; (4) Component A has a melt index (I2) of from about 0.01 to about 10 g/10 min; (5) Component A has a molecular weight distribution (Mw/Mn) of from about 1.8 to about 10; and (6) Component B is present in an amount of from about 35 to about 99 weight percent based on the combined weights of components A, and B and comprises acetal resins, acrylic resins, polyamides,nylon-6, nylon 6,6, polyimides, polyetherimides, cellulosics, polyesters, poly(arylate), aromatic polyesters, poly(carbonate), poly(butylene) and polybutylene and polyethylene terephthalates, polyethers, polycyclopentanes, and its copolymers, polymethylpentane, poly(carbonate), polyethylene terephthalate or polybutylene terephthalate; (7) Component B has a molecular weight (Mw) of from about 10,000 to about 40,000; and (8) has a melt flow rate (MFR) of from about 2 to about 80 g/10 min.
- 3. The blend of claim 1 wherein;
(1) Component A is present in an amount of from about 1 to about 50 percent by weight (based on the combined weights of Components A and B); (2) Component A contains of from about 30 to about 45 mole percent of polymer units derived from;
a) said vinyl or vinylidene aromatic monomer which comprises styrene, α-methyl styrene, ortho-, meta-, and para-methylstyrene, and the ring halogenated styrenes, or b) said hindered aliphatic or cycloaliphatic vinyl or vinylidene monomers which comprises 5-ethylidene-2-norbornene or 1-vinylcyclo-hexene, 3-vinylcyclo-hexene, and 4-vinylcyclohexene; or c) a combination of at least one of a) and b); (3) Component A contains of from about 55 to about 70 mole percent of polymer units derived from said α-olefin, which comprises ethylene, or ethylene and at least one of propylene, 4-methyl-1-pentene, butene-1, hexene-1 or octene-1; or (4) Component A has a melt index (I2) of from about 0.01 to about 5 g/1 min; (5) Component A has a molecular weight distribution (Mw/Mn) of from about 2 to about 5; and (6) Component B is present in an amount of from about 50 to about 99 percent by weight (based on the combined weights of Components A and B) and comprises poly(carbonate), polyethylene terephthalate or polybutylene terephthalate; (7) Component B has a molecular weight (Mw) of from about 15,000 to about 38,000; and (8) has a melt flow rate (MFR) of from about 4 to about 30 g/10 min.
- 4. A blend of claim 3 wherein
i) said vinyl or vinylidene aromatic monomer, Component A1(a), is styrene; ii) said aliphatic α-olefin, Component A2, is ethylene; iii) said, Component B, is poly(carbonate).
- 5. A blend of claim 3 wherein
i) said vinyl or vinylidene aromatic monomer, Component A1(a), is styrene; ii) said aliphatic α-olefin, Component A2, is ethylene; iii) said Component B, is poly(carbonate).
- 6. The blend of claim 1 further comprising a filler.
- 7. The blend of claim 1 further comprising one or more ignition resistance additives selected from halogenated hydrocarbons, halogenated carbonate oligomers, halogenated diglycidyl ethers, organophosphorous compounds, fluorinated olefins, antimony oxide and metal salts of aromatic sulfur compounds.
- 8. A blend of claim 1 wherein Component A is produced by polymerization in the presence of a metallocene or constrained geometry catalyst and a co-catalyst.
- 9. A blend of claim 1 in the form of a molded or extruded article.
- 10. A blend of claim 2 in the form of a molded or extruded article.
- 11. A blend of claim 3 in the form of a molded or extruded article.
- 12. A blend of claim 4 in the form of a molded or extruded article.
- 13. A blend of claim 5 in the form of a molded or extruded article.
- 14. A blend of claim 6 in the form of a molded or extruded article.
- 15. A blend of claim 7 in the form of a molded or extruded article.
- 16. A blend of claim 8 in the form of a molded or extruded article.
- 17. The blend of claim 1 further comprising
(C) of from about 15 to about 30 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more polyolefin elastomers wherein said polyolefin elastomer;
(1) has a melt index (I2) of from about 0.01 to about 100 g/10 min; and (2) has a density of from about 0.860 to about 0.900 g/cm3; and (D) of from about 0.5 to about 20 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more functional polyolefins.
- 18. The blend of claim 1 further comprising
(C) of from about 10 to about 20 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more polyolefin elastomers wherein said polyolefin elastomer;
(1) has a melt index (I2) of from about 0.1 to about 10 g/10 min; and (2) has a density of from about 0.860 to about 0.895 g/cm3; and (D) of from about 0.5 to about 15 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more functional polyolefins.
- 19. The blend of claim 1 further comprising
(C) of from about 3 to about 15 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more polyolefin elastomers wherein said polyolefin elastomer;
(1) has a melt index (I2) of from about 0.25 to about 5.0 g/10 min; and (2) has a density of from about 0.860 to about 0.885 g/cm3; and (D) of from about 1.0 to about 10 percent by weight (based on the combined weights of Components A, B, C, and D) of one or more functional polyolefins.
- 20. A blend of claim 17 in the form of a molded or extruded article.
- 21. A blend of claim 18 in the form of a molded or extruded article.
- 22. A blend of claim 19 in the form of a molded or extruded article.
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application claims the benefit of US provisional application number 60/077,663 filed on Mar. 11, 1998.
Provisional Applications (1)
|
Number |
Date |
Country |
|
60077663 |
Mar 1998 |
US |
Continuations (1)
|
Number |
Date |
Country |
Parent |
09260450 |
Mar 1999 |
US |
Child |
09882619 |
Jul 2001 |
US |