Patent Application
20150187718
The present disclosure relates to electrodes. More particularly, it relates to three-dimensional high surface area electrodes.
One of the many aspects to consider when fabricating an implantable sensor is minimizing the foreign body reaction to the implantable sensor. In particular, an aim would be minimizing the complexity of the process for implanting the sensor and the resultant damage which may occur during the implantation.
High surface area electrodes with very small geometrical areas can help achieve the above goal while retaining sensitivity for sensing applications. Additionally, the use of the high surface area electrodes can also decrease the system cost, for example, when used with existing CMOS (complementary metal-oxide-semiconductor) technology.
Micro-scale and nano-scale structuring of electrodes have been used in sensing and energy storage. Such structuring of electrodes can also provide advantages in terms of high output signal and enhanced selectivity using different sensing techniques.
The most common fabrication methods for making such high surface area electrodes include direct Physical Vapor Deposition (PVD) or Chemical Vapor Deposition (CVD) for the electrode materials. However, the resulting structures for the electrodes fabricated using either PVD or CVD are not suitable for long-term use. For example, such electrodes can experience deformation in when subjected to liquid environments because of existing capillary forces in the environments.
Alternative bottom-up fabrication techniques which could be used to make high surface area electrodes include vapor-liquid-solid (VLS) growth, porous templates or complex electrochemical plating. Although the devices fabricated using bottom-up fabrication techniques function better in liquids than the electrodes fabricated using PVD or CVD, there are a number of different complications which arise. First, VLS uses high temperatures, high pressures and phase transitions which cannot be easily controlled. Additionally, porous templates require fabrication of porous templates and filing templates. Furthermore, electrochemical plating requires the use of liquids. In view of such requirements, these bottom-up fabrication techniques may not be compatible with current CMOS processes or other standard fabrication processes used in making implantable systems. Therefore, these bottom-up fabrication techniques can be pretty complex, expensive and difficult to replicate.
According to a first aspect of the present disclosure, a three dimensional high surface electrode is described. The electrode comprises at least one pillar between 1 micron and 50 nm tall with a core of silicon or silicon alloy, a complete and uniform layer of insulator between 50 nm and 250 nm, and a complete and uniform layer of conductive metal between 50 nm and 250 nm.
According to a second aspect of the present disclosure, a three dimensional high surface area electrode is described. The electrode comprises at least one pillar between 1 micron and 50 nm tall with a core of a CMOS layer and a complete and uniform layer of conductive metal between 50 nm and 250 nm.
The accompanying drawings, which are incorporated into and constitute a part of this specification, illustrate one or more embodiments of the present disclosure and, together with the description of example embodiments, serve to explain the principles and implementations of the disclosure.
Methods for designing and fabricating high surface area electrodes are described with embodiments in this present disclosure. In particular, the present disclosure describes methods of designing and fabricating pillars which are then used as an electrode for sensing applications. It should be noted that a plurality of pillars, etched or grown from a substrate (e.g. silicon), correspond to one or more electrodes based on the insulation provided to electrically isolate a group of pillars from other pillars (discussed later).
As referenced in this present disclosure, the term “nanopillar” or “micropillar” refers to pillars being formed using the method of the present disclosure in terms of nano-scale or micro-scale, respectively.
With reference to
1) designing the pillars to be fabricated based on a selected application,
2) lithographic patterning of a substrate where the pillars will be formed,
3) pattern transferring to form the pillars,
4) insulation of the pillars to define the electrodes, and
5) metal deposition for increased conductivity for the electrodes.
Further details concerning the above steps are provided below. It should be noted that the methods for the above steps are performed at room temperature. The use of room temperature is important because it allows the method to be applicable for use with a variety of materials when forming the pillars without concern for potentially damaging other structures or elements which may be found near the fabrication site (e.g. in the substrate) arising from use of extreme temperatures.
Additionally, the present disclosure also describes alternative embodiments for the discussed methods of fabrications of the electrode. In particular, details will be provided for adapting the method described above for use with CMOS technology as opposed to a substrate (e.g. silicon). Furthermore, an alternative hybrid fabrication method for fabricating the pillars for increased surface area will also be described.
Based on a desired application for the electrode, parameters of the pillars (corresponding to one or more electrodes) are optimized. For some embodiments of the present disclosure, a parameters to be optimized is sizing of the pillars. For example, an electrode can be sized based on the intended target to be detected. If cells are to be detected using the pillars, an embodiment may design the pillars using micro-scale. The exact size will depend on the size of the particular cells. However, if proteins are to be detected (which are of a smaller scale) by the pillars, the embodiment according to the present disclosure may design the pillars using nano-scale. Another design aspect is the top material of the pillars which will depend on the application. Further discussion about this aspect will be provided below in the discussion for metal deposition.
The detailed design of the electrodes with pillars is generally performed using commercially-available software adapted to perform simulations and modeling of the pillars.
In embodiments according to the present disclosure, design of other parameters for the pillars are as follows:
After the design of the pillars is confirmed, fabrication of the pillars begins. First, in the lithographic patterning step, a substrate (e.g. a silicon wafer) is selected (see,
Alternative, embodiments according to the present disclosure may choose a CMOS die as the substrate. Examples of commercially available CMOS dies include TSMC 250 nm and IBM 250 nm. A benefit for using a commercially available CMOS die may include the ability to use already existing circuitry CMOS for control therefore removing a need to provide separate circuitry to control the system. Furthermore, insulation is already provided. Lastly, fabrication of such dies are already available therefore reducing costs compared to situations where substrates may need to be designed for use for a sensor. Embodiments where the CMOS is used will be discussed later in this present disclosure.
Next in the lithographic patterning step, the method defines where the pillars will be formed on the chosen substrate through the use of a resist (e.g. a photoresist or electron resist) (see,
After the photo resist has been applied onto the substrate, patterning of the photo resist occurs. In an embodiment of the present disclosure, photo lithography (or optical lithography) is performed by using a mask aligner (e.g. Carl Suss MA6 or MJB3) (see,
After the baking or exposure above has occurred, development is performed whereby selective portions of the photo resist (in particular the parts of the photo resist which was left exposed through the mask aligner) on the substrate are removed. The resulting product is an exposed substrate with portions of the substrate still covered in a layer of photo resist (see,
Aside from optical lithography, e-beam lithography can be used where electron resists can be utilized (e.g. PMMA950A4, MA-N, and FOX). Electron resists can also be spun or sprayed onto the surface of the substrate using the spin-coating or spray-coating techniques described above with reference to photo resists. For e-beam lithography, an electron beam pattern generator is used (e.g. Vistec 5000+, Jeol, FEI) to produce the pattern directly onto the electron resist. In this way a mask aligner is not used. The electron resist is then baked or exposed. Furthermore, MA-D or a mixture of MIBK and IPA is used during development when removing the selective parts of the electron resist covering the areas of the substrate to be removed (e.g etching).
It should be noted that the type of lithography used can depend on the scaling for the pillars. For example, an embodiment of the present disclosure may use e-beam lithography if the design of the pillars is of a nano-scale design. Meanwhile, photolithography would be applicable for micro-scale designs. There are situations where photolithography could be applicable for nano-scale design of pillars. However, these situations may be expensive and time consuming to implement.
After the resist has been removed from the selective sections of the substrate, the next step for the fabrication of the electrode is to transfer the pattern from the resist into the substrate. In particular, embodiments of the present disclosure associate this step of pattern transfer with top-down etching (see,
According to embodiments of the present disclosure, the term “top-down etching” refers to the formation of pillars from a substrate caused by the removal of substrate (via the process of etching) surrounding the sections of the substrate which will become the pillars. The removal of the surrounding substrate is performed using an etching material. This generalization of “top-down” formation of pillars is in contrast to the formation of pillars using a “bottom-up” technique. In this “bottom-up” method, pillars are grown from a catalyst on a given substrate. Embodiments of the present disclosure choose to use the top-down method of forming pillars because such methods can be readily replicated in commercially available foundries. With respect to “bottom-up” fabrication, such methods may be expensive, time consuming and are not compatable with existing methods in existing foundries.
As stated above, the methods of fabrication are chosen to be performed at room temperature. In particular, it should be noted that the etching in embodiments of the present disclosure is performed at room temperatures in order to avoid providing stress and/or damage to underlying structures in the substrate (especially if the material being etched on is CMOS).
With respect to the “top-down” etching of the present disclosure, such room-temperature etching is performed using a silicon plasma etch. An example of the silicon plasma etch which is used is described in Henry (“Alumina Etch masks for Fabrication of High-Aspect-Ratio Silicon Micropillars and Nanopillars”) where such etch has been developed and optimized for use in the methods described in the present disclosure. The silicon plasma etch is optimized to achieve embodiments which have uniform etch depth for all pillar widths and uniform sidewall roughness.
Following the formation of the pillars (see,
Insulation can be performed in a number of ways. In an embodiment of the present disclosure, thermal oxidation can be performed. In this method, oxides or nitrides are formed on the surface of the pillars through the use of extremely high temperatures (˜1000° C.). Although the method of creating the oxides or nitrides may be easy, if the substrate, where the pillars are being formed on, is sensitive to extreme temperatures (e.g. as in the case with using CMOS), then damage to the underlying structures of the substrate can occur.
Alternatively, embodiments using lower temperatures (or even room temperature) are possible. For example, plasma oxidation can be performed where the substrate is placed in a machine with oxygen plasma at ˜200° C. in order to grow an oxide layer to be used for insulation.
However, for a number of embodiments of the present disclosure, insulation is performed by depositing insulating material (oxides or nitrides) onto the pillars directly. The insulating materials are deposited onto the pillars in a manner similar to the metal deposition discussed below. The use of this insulating technique allows the embodiment to avoid high temperatures that may be present in thermal oxidation which can damage other elements in the overall system. However, as discussed below, the method of depositing the insulating materials in a similar manner as the metal deposition may be more complicated than the above two methods (e.g. thermal oxidation or plasma oxidation) described.
Lastly, the method of fabrication concludes with the deposition of a metal layer on the formed pillars (see,
Additionally, a variety of methods for metal deposition onto the pillars can be also used. It should be noted that to ensure the electrode operates as anticipated, a uniform and complete coverage of the pillars in the metal layer is provided.
Typically a metal layer can be provided onto the pillars using methods such as electron beam evaporation or ion beam induced deposition. However, it was found that the pillars were not completely and continuously covered. In particular, coverage of the sides of the pillars was not complete and uniform.
In this way, embodiments of the present disclosure utilize an optimized sputtering deposition of low impedance metals. Typically sputtering involves ejecting a material from a target (which is a source) to the substrate. However, as shown in
According to embodiments of the present disclosure, the sputtering used in the present disclosure is optimized through the use of special hardware (e.g. a tilting and rotating stage) and high pressure to ensure a complete and continuous coverage over the pillars. In particular, the stage, used to hold the substrate, is able to tilt with respect to the incoming metal being deposited at angles up to 90 degrees (see,
After the metal layer has been deposited, a last step of removing excess metals is performed called liftoff. Liftoff can be performed using image reversal bake and flood exposure methods that are already known in the art. As a result of the methods described above, an electrode is fabricated which can be used in electrode based sensors (e.g.
As described above, various substrates (e.g. silicon) can be used for the fabrication of the pillars. It should be noted that the methods for designing and fabricating electrodes are also applicable with CMOS. It should be noted that previous etching on CMOS dies had failed in part because of the challenges associated with etching metals such as difficulties concerning the charges thereof as well as damage to the die in ordinary processes. The invention of the present disclosure overcomes these problems by using masks resistant to degradation by the processes that etch the metal as well as using temperatures of less than 500° C. throughout the entire fabrication process.
As stated above, a benefit of using CMOS is that the CMOS die generally already has insulation present. Therefore, that fabrication step can be skipped.
A CMOS die that would be used for embodiments according to the present disclosure is generally a plurality of layers of metals and insulation on a silicon or silicon-on-insulator substrate. Furthermore, the CMOS includes existing elements within its structure. Unlike the fabrication methods described above using a substrate (e.g. silicon) where the entire substrate can be etched, with respect to CMOS, a top most metal layer of the CMOS is designated for the formation of the pillars to be patterned and etched. A flow chart depicting steps performed in the fabrication method of pillars using CMOS can be seen in
With fabrication of nanopatterned electrodes using CMOS, extreme temperatures are avoided so as to avoid damaging already existing elements in the CMOS. Such elements being referred to within the CMOS may be underlying structures and/or electronics already imbedded during the fabrication of the CMOS. Thus the use of the room-temperature etching facilitates the aim of avoiding the use of extreme hot or cold temperatures during the fabrication process.
Although the use of CMOS would limit the conditions by which the pillars can be formed, as stated above, there are a number of benefits in adapting the fabrication methods for use with CMOS. First, the use of CMOS can be desired because the pillars formed on the substrate would already be isolated from other pillars. In fact, because of this benefit, the fabrication method described above would not require the use of an insulating material for the pillars (comparing
As discussed earlier, a number of embodiments according to the present disclosure can be fabricated using a hybrid fabrication method for increased electrode surface area. The hybrid fabrication method first utilizes the steps for top-down fabrication methods of the electrode according to the present disclosure (e.g. steps 1-5 as summarized above) and seen in
The particles used in the hybrid method are used based on the size of the target element to be detected. For example, if the target species to be detected is a protein, embodiments may use nanoparticles which may be more sensitive. On the other hand, microparticles can also be applied to the pillars for embodiments where the electrode is to be adapted for detecting larger species (e.g. cells).
Embodiments according to the present disclosure may use particles having a size of 10 nm or 1 μm. In various embodiments the particles may be made from platinum.
The following are descriptions of various embodiments which have been performed using the above methods described in the present disclosure in the fabrication of high surface area electrodes. The results of each of the various embodiments are reviewed under a high power optical microscope or scanning electrode microscope (SEM) in order to determine if such steps are performed properly. Additionally, tests (e.g. measuring impedance) may also be performed to confirm that such structures operate as intended (see,
With reference to
It was noted that the electrodes have impedance levels similar to an electrical circuit having a capacitor and resistor in parallel. Thus, by reviewing the impedances of other fabricated electrodes, determination of whether or not they were fabricated properly can be confirmed using this method.
In order to test micro-scale patterning for embodiments of the present disclosure, the following set up was used. First, a Carl-Suss MA6 mask aligner was used for optical lithography. For patterned electrodes, non-contact (proximity mode) lithography was used to avoid damage to small structures. AZ5214E photoresist was used for micro-scale patterning. An inward tapered profile was achieved for better lift-off performance by using image reversal processing. The resist was spun at 4000 rpm for 1 minute and baked at 95° C. for 4 minutes. UV exposure was done using the mask aligner for 2 seconds using an intensity of 15 mW/cm2. Following the UV exposure, an image reversal bake at 110° C. for 2 minutes and a flood exposure for 10 seconds was performed. The pattern was then developed using MF-319 for a minute. Successful patterning was confirmed by optical microscopy (not shown).
In order to test nano-scale patterning for embodiments of the present disclosure, the following set up was used. First, PMMA 950 A4 was used to achieve clean lift-off while still achieving a desired resolution. The resist was spun at 4000 rpm for 1 minute followed by a 180° C. bake for 5 minutes. Next, a dose of 1200 μc/cm2 was used to write the pattern in a Leica EBPG5000+ system. Patterns were developed in 1:3 solution of MIBK and IPA for 20 seconds followed by a deionized water rinse. Afterwards, a 50 nm alumina mask was sputter coated in a Temescal TES BJD-1800 DC reactive sputter system by depositing aluminum in oxygen plasma for 5 minutes. Lastly, mask liftoff was performed in dicholoromethane in an ultrasonic bath for 2 minutes. Successful patterning was confirmed by optical microscopy (not shown).
In order to test silicon etching for embodiments of the present disclosure, the following set up was used. In the embodiment shown, a room-temperature silicon plasma etch was used with the nano-scale features.
Aluminum oxide was deposited on the patterned silicon with a TES 1800 DC magnetron system, using a 99.995% aluminum target and a 5:1 mixture of argon to oxygen as the process gas. This ratio of gases allows for the aluminum to be sputtered without poisoning the target while still deposits a stoichiometric aluminum oxide. At 400 W DC power, this process deposited alumina at an approximate rate of 10 nm min−1. Liftoff is carried out in acetone for the micron scale and a mixture of acetone and dichloromethane for the nanoscale pattern.
Etching was performed using Oxford Instrument's PlasmaLab System 100 ICP-RIE 380s with a Pseudo-Bosch etch. Etching was performed at 15 degrees Celsius. An ICP power of 1300 Watts combined with a RIE power of 23 Watts in a Chamber Pressure of 10, SF6 flow rate of 32 SCCM, and C4F8 flow rate of 53 SCCM was found to provide control.
The silicon plasma etch is optimized to achieve uniform etch depth for all pillar widths and uniform sidewall roughness. A benefit of such uniformity allows reliable comparison between performances of electrodes with different sized pillars. A resulting embodiment according to the present disclosure using the above procedure can be seen in
In order to test silicon etching for embodiments of the present disclosure, the following set up was used. The patterning was performed with a MA-N 2403 resist. Pillars were fabricated using both dry plasma (Cl2:BCl3) as well as wet etchants (e.g. TMAH) to etch away parts of the metal pad using a UNAXIS RIE machine. For the dry plasma (Cl2:BCl3) etch the temperature was set to 25 degrees Celsius and RIE power to 120 watts. Flow rate for Cl2 was set to 4 SCCM and the flow rate of BCl3 was set to 20 SCCM.
For the wet TMAH etch the surface was submerged in a liquid for room temperature for 10 minutes.
A resulting embodiment according to the present disclosure using the above procedure can be seen in
In order to test silicon oxidation for embodiments of the present disclosure, the following set up was used. First, pillar structures were oxidized in a wafer furnace at 1000° C. for 90 minutes, followed by 15 minute nitrogen anneal and a gradual return to room temperature.
A resulting embodiment according to the present disclosure using the above procedure can be seen in
Success can be seen be checked by reference to a color chart, visual observation of surface, and SEM images of pillars.
In order to test low temperature silicon oxidization for embodiments of the present disclosure, the following set up was used. First, an Oxford HD ICP-CVD system was used to perform plasma enhanced chemical vapor deposition (PECVD) of silicon oxide layers. Operating parameters for the system were 350° C. table temperature and silicon oxide deposition rate of ˜70 nm/minute at high pressure (˜1000 mTorr). A resulting embodiment according to the present disclosure using the above procedure can be seen in
In order to test metal deposition electron beam evaporation deposition for embodiments of the present disclosure, the following set up was used. First, deposition was performed formed on a CHA electron beam deposition system at 2×10−6 torr. The sample substrate was placed on a rotating stage and various low impedance metals such as Au and Pt were used as metal sources. A 5 nm Ti adhesion layer was evaporated at 0.5 angstrom/s and subsequently an Au or Pt layer of 50 nm or 100 nm was evaporated at 1 angstrom/s. Results show that it may be difficult to realize conformal coating on these pillars using electron beam deposition because of the inherent straight line deposition mechanism in these systems. A resulting embodiment according to the present disclosure using the above procedure can be seen in
In order to test metal deposition sputter deposition of low impedance metals for embodiments of the present disclosure, the following set up was used. Metal deposition sputter deposition can be used to perform conformal coatings. First high density Argon plasma of 20 mTorr is used to increase the isotropy of the deposition. A 5 nm Ti adhesion layer is DC sputtered and then 50 nm or 100 nm Au or Pt films were DC sputtered. Resulting embodiments according to the present disclosure using the above procedure can be seen in
A special stage was used which could tilt the sample with respect to the incoming metal atoms at angles up to 90° C. Secondly, the stage could rotate at speeds up to 120 r.p.m. A combination of tilt and rotation along with optimization of plasma parameters (high pressure, around 20 mTorr) resulted in very uniformly controlled conformal sidewalls.
In order to test metal deposition ion beam induced deposition of Platinum for embodiments of the present disclosure, the following set up was used. First, deposition was performed using an FEI Nova 600 Nanolab ion beam source. 100 nm thick depositions was aligned directly over the pillar array electrodes. EDS analysis in an FEI Sition 200 SEM/EDAX machine was used to confirm the composition of the deposited layer. A resulting embodiment according to the present disclosure using the above procedure can be seen in
A number of embodiments of the disclosure have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the present disclosure. Accordingly, other embodiments are within the scope of the following claims.
The examples set forth above are provided to those of ordinary skill in the art as a complete disclosure and description of how to make and use the embodiments of the disclosure, and are not intended to limit the scope of what the inventor/inventors regard as their disclosure.
Modifications of the above-described modes for carrying out the methods and systems herein disclosed that are obvious to persons of skill in the art are intended to be within the scope of the following claims. All patents and publications mentioned in the specification are indicative of the levels of skill of those skilled in the art to which the disclosure pertains. All references cited in this disclosure are incorporated by reference to the same extent as if each reference had been incorporated by reference in its entirety individually.
It is to be understood that the disclosure is not limited to particular methods or systems, which can, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting. As used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the content clearly dictates otherwise. The term “plurality” includes two or more referents unless the content clearly dictates otherwise. Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the disclosure pertains.
The present application is a Divisional of U.S. application Ser. No. 14/106,701 filed on Dec. 13, 2013, which claims priority to U.S. Provisional application 61/736,944 filed on Dec. 13, 2012, both of which are incorporated herein by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 61736944 | Dec 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14106701 | Dec 2013 | US |
| Child | 14656650 | US |