Patent Application
20130334469
This invention relates to a phase change thin film used in the microelectronics field and fabrication method thereof, and more particularly to a phase change thin film composed of a mixture of aluminum-antimony-tellurium and fabrication method thereof.
Memory enjoys a significant position in the semiconductor market, 10% of which is occupied by dynamic random access memory (DRAM) and flash alone. With the gradual popularity of portable electronic devices, a growing market for non-volatile memory can be expected, coupled with increasingly high requirements of consumers for the capacity, speed and etc. of memory. As a mainstream non-volatile memory, flash technology has encountered the bottleneck. The technical weakness becomes more highlighted with the development of integrated circuits. Limitations such as low speed, high write voltage and limited number of cycles have directly restricted further application of flash technology. Therefore, it is urgent to develop a novel memory technology to replace it so as to maintain the direction of development toward scaling down to small sizes for memory technology.
Phase change memory (PCM) technology, emerging in recent years and enjoying extensive application prospect, is a new kind of memory technology where phase change material is used as the storage medium; recently it is a hot point in memory research and is regarded as the most promising one to become the mainstream memory of the next generation. Since most of the phase change materials comprise chalcogen elements, they are also know as chalcogenide random access memory, considered as the semiconductor memory characterized by high speed, high density, low power consumption, high reliability, low cost and etc. Data storage of chalcogenide random access memory is realized by the reversible phase change between amorphous and polycrystalline states when phase change material is activated by applying energy, wherein the chalcogenide has high resistance in amorphous state and low resistance in polycrystalline state, thus PCM utilizes the resistance difference between the high and low resistance states to store “0” and “1”.
Ge2Sb2Te2 is a typical phase change material used for PCM, but it is found in actual applications that, due to great change of density and poor crystallization speed (about hundreds of ns generally) of Ge2Sb2Te2 material during phase change, the erase and write speed and the device reliability are influenced; furthermore, low crystallization temperature of about 160° C. makes it difficult to be used under high temperature conditions. Therefore, Ge2Sb2Te2 is not a prefect phase change material, especially for applications in certain special conditions.
To sum up, it is an urgent issue at present to develop novel phase change materials that can help devices simultaneously possess multiple advantages such as high speed, high reliability, high density, good thermal stability and low cost, or that demonstrate outstanding performance in certain aspects.
The main technical problem to be solved in the present invention is to provide an Al—Sb—Te phase change material used for PCM and fabrication method thereof. Said material is characterized by good thermal stability, high crystallization speed, low power consumption and nice compatibility with complementary metal-oxide semiconductor (CMOS) process.
In order to solve the foregoing technical problem, the present invention adopts the following technical scheme:
An Al—Sb—Te phase change material used for PCM, which is a mixture of three elements aluminum, antimony and tellurium.
Preferably, said phase change material has a general formula of Alx(SbyTe1)1-x, where 0<x≦0.85, 0.67≦y≦7.
Preferably, any two elements of aluminum, antimony and tellurium of said phase change material are bonded to each other to form a ternary system.
Preferably, elements aluminum and antimony of said phase change material are bonded to each other to form AlSb semiconductor.
Preferably, reversible change in resistivity of said phase change material is achieved by employing electrical pulse.
The present invention further provides a fabrication method of the foregoing Al—Sb—Te phase change material used for PCM: preparing phase change material of Alx(SbyTe1)1-x by magnetron sputtering, where 0<x≦0.85, 0.67≦y≦7.
Preferably, multi-target co-sputtering is used in magnetron sputtering; for example, co-sputtering with Al and Sb—Te alloy targets, or co-sputtering with Al, Sb and Te targets; in addition, sputtering with prepared single Al—Sb—Te alloy target can be used obviously.
The present invention has the advantages as the following:
The Al—Sb—Te phase change material provided by the present invention can realize reversible phase change between the high and low resistance states by employing electrical pulse from outside and perform the data storage by the resistance difference before and after phase change, wherein the phase change material, which serves as storage material, shows great difference between the high and low resistance states before and after reversible phase change under electrical pulse, facilitating peripheral circuits to easily discern between “0” and “1”, thereby functioning as a relatively ideal PCM material.
Said Al—Sb—Te phase change material does not fix the ratio of any two elements, showing high adjustability and benefits in finding out the proper composition for excellent performance in all aspects. By adjusting the content of three elements, storage materials with different crystallization temperatures, melting temperatures, and activation energies of crystallization can be achieved; the resistance difference before and after phase change can be noticeably increased, wherein any two elements of aluminum, antimony and tellurium of said material can be bonded to each other to form a ternary system with a uniform crystallization temperature, and wherein elements aluminum and antimony can be bonded to each other to form AlSb semiconductor such that the thermal stability of the material can be enhanced to improve the activation energy and data retention. It can be found that this material not only shows small volume difference before and after phase change and high crystallization speed during phase change, but also has good data retention for stable operation under high temperature conditions.
Moreover, as a common element used in microelectronics, aluminum (Al) features mature technology, so Al—Sb—Te phase change material is well compatible with CMOS.
a and 2b are XRD patterns of phase change thin films of Al0.58(Sb0.83Te1)0.42 and Sb0.83Te1 under different annealing temperatures.
The substantial characteristics and outstanding improvements of the present invention are further detailed below with reference to specific embodiment, however the present invention is not only restricted to the embodiment.
The present invention provides an aluminum-antimony-tellurium phase change material used for PCM, which has a general formula of Alx(SbyTe1)1-x, wherein the content of Al can not be over 85%, i.e., x shall be preferably in the range of 0<x≦0.85, and the ratio of Sb to Te shall also be controlled within a certain range, preferably in the range of 0.67≦y≦7. This phase change material is a mixture thin film of three elements aluminum, antimony and tellurium, which can be prepared by various methods, such as magnetron sputtering, pulsed laser deposition (PLD) and electron beam evaporation. Among the foregoing methods, magnetron sputtering is a more flexible one of preparing thin film, wherein the thin film can be prepared by co-sputtering with three targets of Al, Sb and Te with the composition adjusted by controlling the source power of three targets, by co-sputtering with Al and Sb—Te alloy targets, or by sputtering with prepared single Al—Sb—Te alloy target; Al—Sb—Te phase change materials of various compositions can be prepared by these methods.
The technical scheme of the present invention is further detailed by the preparation of Alx(SbyTe1)1-x phase change material and the test thereof in this embodiment. Detailed preparation method is described as follow:
To sum up, said Al—Sb—Te phase change material used for PCM described in the present invention is characterized by small volume difference before and after phase change, high crystallization speed during phase change and good data retention for stable operation under high temperature conditions. Moreover, said phase change material can realize reversible phase change under electrical pulse, showing great difference between the high and low resistance states before and after phase change, facilitating peripheral circuits to easily discern between “0” and “1”, thereby functioning as a relatively ideal PCM material.
The description and application of the present invention is only an illustration and is not to limit the present invention to the foregoing embodiment. Further modification and variation can be made to the embodiment disclosed herein and the substitutionally equivalent components of the embodiment are well known to ordinary one skilled in the art. It shall be understood to those skilled in the art that the present invention can be realized in other form, structure, layout, and ratio with other substrate, material and component without deviating from the spirit or substantial characteristics of the present invention. Modification and variation can be made to the embodiment disclosed herein without deviating from the spirit and scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201010619496.2 | Dec 2010 | CN | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN11/76300 | 6/24/2011 | WO | 00 | 8/23/2011 |