This disclosure relates generally to the field of self-assembled monolayers and, more specifically, to the application of a self-assembled monolayer to a substrate containing a contact metal, e.g., indium, to prevent oxide formation when peripheral electronic components are connected.
Self assembled monolayers (SAMs) are surfaces consisting of a single layer of molecules on a substrate. Rather than having to use a technique such as chemical vapor deposition or molecular beam epitaxy to add molecules to a surface (often with poor control over the thickness of the molecular layer), self assembled monolayers can be prepared simply by adding a solution of the desired molecule onto the substrate surface and washing off the excess.
Flip chip hybridization is a microelectronics packaging and assembly process which directly connects an individual chip (e.g., a sensor device) to a substrate, e.g., a readout integrated circuit (ROIC), eliminating the need for peripheral wirebonding. Electrical connections are made between the two parts using interconnect bumps consisting of a conductive material. One type of conductive interconnect bump that may be used for direct connection of certain active devices to the substrate is an indium bump. However, the use of indium poses a problem requiring special processing, since it readily oxides in air. Once formed, an oxide layer formed on indium is difficult to break.
Currently, one technique to remove this oxide layer is a mechanical scrubbing process where two indium bumps are rubbed against each other until the oxide layer breaks. Such conventional removal of indium oxide from the conductive interconnects often results in harmful mechanical stresses being imposed on the chip contacts that may have an adverse impact on manufacturing yields. Another technique to remove oxidation is by using a cleaning agent, such as a flux. Fluxes can be categorized as either corrosive and noncorrosive. For electrical devices, the fluxes should be noncorrosive. The use of fluxes also requires the application of a solvent to remove contaminants from the soldered connection. The solvents must be nonconductive and noncorrosive and used in a manner that keeps dissolved flux residue from “contact” surfaces. Any flux remaining in the joint corrodes the connection and creates a defective circuit.
In accordance with one embodiment of this disclosure, a method of forming a self assembled monolayer to reduce formation of an oxide is disclosed. The method includes applying an inhibitor to a substrate including conductive contacts and processing the substrate and inhibitor to form the self assembled monolayer.
In accordance with one embodiment of this disclosure, a device manufacturing method is disclosed. The method includes providing a first electronic circuit comprising a first plurality of metal contacts thereon; providing a second electronic circuit comprising a second plurality of metal contacts thereon; forming a self assembled monolayer between the first plurality of metal contacts and the second plurality of metal contacts; and conductively connecting the first plurality of metal contacts and the second plurality of metal contacts together.
These and other features and characteristics, as well as the methods of operation and functions of the related elements of structure and the combination of parts and economies of manufacture, will become more apparent upon consideration of the following description and the appended claims with reference to the accompanying drawings, all of which form a part of this specification, wherein like reference numerals designate corresponding parts in the various Figures. It is to be expressly understood, however, that the drawings are for the purpose of illustration and description only and are not intended as a definition of the limits of claims. As used in the specification and in the claims, the singular form of “a”, “an”, and “the” include plural referents unless the context clearly dictates otherwise.
a and 3b show experimental results of indium oxide formation growth without application of the self-assembled monolayer inhibitor and with the inhibitor.
a and 4b show results of imaging by a scanning electron microscope for both an untreated sample and a sample treated with an indium oxide inhibitor solution.
Any pre-existing oxide on the contact, e.g., indium oxide, may be removed from the substrate by an etch process. The substrate may be etched by immersion in an acid solution, e.g., a hydrochloric acid and water solution, for about 1 minute. The substrate may then be rinsed in deionized water and then rinsed with acetone. The substrate may be dried in an inert gas, e.g., nitrogen gas.
The self-assembled monolayer inhibitor is then applied to the substrate 120, which protects against oxide growth on the substrate. In one embodiment, the inhibitor may be a solution of 1 mM of benzotriazole (C6H5N3) or octadecanethiol (C18H38S) mixed with ethanol. The substrate is immersed in the inhibitor solution for about 60 minutes. Once the substrate has been applied with the inhibitor solution, the substrate may be rinsed with isopropanol and dried by the application of nitrogen gas.
The self-assembled monolayer may then be cured 130 to the substrate by heating the substrate at 200C for 5 minutes in air.
a and 3b show experimental results of indium oxide formation growth without application of the self-assembled monolayer inhibitor and with the inhibitor. In the experimental set-up, a sample including indium bumps with no inhibitor solution is compared with a sample having the inhibitor solution. Both inhibitor solutions, including benzotriazole and octadecanethiol mixed with ethanol, were tested.
a and 4b show results of imaging by a scanning electron microscope for both an untreated sample and a sample treated with an indium oxide inhibitor solution. In
Although the above disclosure discusses what is currently considered to be a variety of useful embodiments, it is to be understood that such detail is solely for that purpose, and that the appended claims are not limited to the disclosed embodiments, but, on the contrary, is intended to cover modifications and equivalent arrangements that are within the spirit and scope of the appended claims.