Patent Application
20240006235
Embodiments of the disclosure generally relate to methods of forming composite barrier layers. More particularly, embodiments of the disclosure are directed to methods of forming Ru:NbN barrier films.
Microelectronic devices, such as semiconductors or integrated circuits, can include millions of electronic circuit devices such as transistors, capacitors, etc. To further increase the density of devices found on integrated circuits, even smaller feature sizes are desired. To achieve these smaller feature sizes, the size of conductive lines, vias, and interconnects, gates, etc. must be reduced. Reliable formation of multilevel interconnect structures is also necessary to increase circuit density and quality. Advances in fabrication techniques have enabled use of copper for conductive lines, interconnects, vias, and other structures. However, electromigration in interconnect structures becomes a greater hurdle to overcome, with decreased feature size and the increased use of copper for interconnections. Such electromigration may adversely affect the electrical properties of various components of the integrated circuit.
Specifically, for 5 nm node and below, barrier and liner thickness for copper interconnects becomes even more challenging with respect to device reliability and adhesion of the barrier layer. Also, the baseline thickness of a barrier film and liner at 5 nm is ˜45 Å. Higher thicknesses provide less space for gapfill and can increase resistivity.
Tantalum nitride (TaN) is a copper barrier at film thicknesses greater than 10 Å, where the film is continuous. However, at nodes below 22 nm, TaN deposited by thermal atomic layer deposition (ALD) is not a good copper barrier layer. Therefore, there is a need for new methods for depositing films that are effective copper barriers.
Some embodiments of the disclosure are directed to a method of forming a ruthenium doped niobium nitride barrier layer. The method comprises forming a first niobium nitride (NbN) barrier film on a substrate by a first ALD process, doping the first barrier film with ruthenium by a flash chemical vapor deposition process, and forming a second niobium nitride barrier film on the doped first barrier film by a second ALD process to form a ruthenium doped niobium nitride barrier layer.
Additional embodiments of the disclosure are directed to a method of forming a ruthenium doped niobium nitride layer. The method comprises exposing a substrate to a niobium precursor and ammonia to form a first barrier film on the substrate. The substrate comprises a dielectric layer having at least one feature. The first barrier film is doped with ruthenium by exposing the first barrier film to a ruthenium precursor and hydrogen gas (H2) in a flash chemical vapor deposition process. The substrate is exposed to the niobium precursor and ammonia to form a second barrier film on the doped first barrier film. The flash chemical vapor deposition process or the flash chemical vapor deposition process and formation of the second barrier film are repeated to form a doped metal nitride layer.
So that the manner in which the above recited features of the present invention can be understood in detail, a more particular description of the invention, briefly summarized above, may be had by reference to embodiments, some of which are illustrated in the appended drawings. It is to be noted, however, that the appended drawings illustrate only typical embodiments of this invention and are therefore not to be considered limiting of its scope, for the invention may admit to other equally effective embodiments.
Before describing several exemplary embodiments of the disclosure, it is to be understood that the disclosure is not limited to the details of construction or process steps set forth in the following description. The disclosure is capable of other embodiments and of being practiced or being carried out in various ways.
As used in this specification and the appended claims, the term “substrate” and “wafer” are used interchangeably, both referring to a surface, or portion of a surface, upon which a process acts. It will also be understood by those skilled in the art that reference to a substrate can also refer to only a portion of the substrate, unless the context clearly indicates otherwise. Additionally, reference to depositing on a substrate can mean both a bare substrate and a substrate with one or more films or features deposited or formed thereon.
A “substrate” as used herein, refers to any substrate or material surface formed on a substrate upon which film processing is performed during a fabrication process. For example, a substrate surface on which processing can be performed include materials such as silicon, silicon oxide, strained silicon, silicon on insulator (SOI), carbon doped silicon oxides, silicon nitride, doped silicon, germanium, gallium arsenide, glass, sapphire, and any other materials such as metals, metal nitrides, metal alloys, and other conductive materials, depending on the application. Substrates include, without limitation, semiconductor wafers. Substrates may be exposed to a pretreatment process to polish, etch, reduce, oxidize, hydroxylate (or otherwise generate or graft target chemical moieties to impart chemical functionality), anneal and/or bake the substrate surface. In addition to film processing directly on the surface of the substrate itself, in the present disclosure, any of the film processing steps disclosed may also be performed on an underlayer formed on the substrate as disclosed in more detail below, and the term “substrate surface” is intended to include such underlayer as the context indicates. Thus for example, where a film/layer or partial film/layer has been deposited onto a substrate surface, the exposed surface of the newly deposited film/layer becomes the substrate surface. What a given substrate surface comprises will depend on what films are to be deposited, as well as the particular chemistry used.
As used in this specification and the appended claims, the terms “reactive gas”, “precursor”, “reactant”, and the like, are used interchangeably to mean a gas that includes a species which is reactive with a substrate surface. For example, a first “reactive gas” may simply adsorb onto the surface of a substrate and be available for further chemical reaction with a second reactive gas.
The term “about” as used herein means approximately or nearly and in the context of a numerical value or range set forth means a variation of ±15%, or less, of the numerical value. For example, a value differing by ±14%, ±10%, ±5%, ±2%, or ±1%, would satisfy the definition of about.
“Atomic layer deposition” or “cyclical deposition” as used herein refers to the sequential exposure of two or more reactive compounds to deposit a layer of material on a substrate surface. The substrate, or portion of the substrate, is exposed separately to the two or more reactive compounds which are introduced into a reaction zone of a processing chamber. In a time-domain ALD process, exposure to each reactive compound is separated by a time delay to allow each compound to adhere and/or react on the substrate surface and then be purged from the processing chamber. These reactive compounds are said to be exposed to the substrate sequentially. In a spatial ALD process, different portions of the substrate surface, or material on the substrate surface, are exposed simultaneously to the two or more reactive compounds so that any given point on the substrate is substantially not exposed to more than one reactive compound simultaneously. As used in this specification and the appended claims, the term “substantially” used in this respect means, as will be understood by those skilled in the art, that there is the possibility that a small portion of the substrate may be exposed to multiple reactive gases simultaneously due to diffusion, and that the simultaneous exposure is unintended.
In one aspect of a time-domain ALD process, a first reactive gas (i.e., a first precursor or compound A) is pulsed into the reaction zone followed by a first time delay. Next, a second precursor or compound B is pulsed into the reaction zone followed by a second delay. During each time delay, a purge gas, such as argon, is introduced into the processing chamber to purge the reaction zone or otherwise remove any residual reactive compound or reaction by-products from the reaction zone. Alternatively, the purge gas may flow continuously throughout the deposition process so that only the purge gas flows during the time delay between pulses of reactive compounds. The reactive compounds are alternatively pulsed until a desired film or film thickness is formed on the substrate surface. In either scenario, the ALD process of pulsing compound A, purge gas, compound B and purge gas is a cycle. A cycle can start with either compound A or compound B and continue the respective order of the cycle until achieving a film with the predetermined thickness.
In an embodiment of a spatial ALD process, a first reactive gas and second reactive gas (e.g., nitrogen gas) are delivered simultaneously to the reaction zone but are separated by an inert gas curtain and/or a vacuum curtain. The substrate is moved relative to the gas delivery apparatus so that any given point on the substrate is exposed to the first reactive gas and the second reactive gas.
It has been found that the Ru:NbN materials disclosed herein advantageously provide superior barrier properties. The improved barrier properties may comprise a lower nitrogen content, a higher Ru content, better coverage, thinner layers, or lower line resistance.
In one or more embodiments, the barrier layer may be deposited via ALD. In a typical ALD process, alternating pulses or flows of “A” precursor and “B” precursor can be used to deposit a film. The alternating exposure of the surface to reactants “A” and “B” is continued until the desired thickness film is reached. However, instead of pulsing the reactants, the gases can flow simultaneously from one or more gas delivery head or nozzle and the substrate and/or gas delivery head can be moved such that the substrate is sequentially exposed to each of the reactive gases. Of course, the aforementioned ALD cycles are merely exemplary of a wide variety of ALD process cycles in which a deposited layer is formed by alternating layers of precursors and co-reactants.
In one or more embodiments, the co-reactants are in vapor or gas form. The reactants may be delivered with a carrier gas. A carrier gas, a purge gas, a deposition gas, or other process gas may contain nitrogen, hydrogen, argon, neon, helium, or combinations thereof. The various plasmas described herein, such as the nitrogen plasma or the inert gas plasma, may be ignited from and/or contain a plasma co-reactant gas.
In one or more embodiments, the various gases for the process may be pulsed into an inlet, through a gas channel, from various holes or outlets, and into a central channel. In one or more embodiments, the deposition gases may be sequentially pulsed to and through a showerhead. Alternatively, as described above, the gases can flow simultaneously through gas supply nozzle or head and the substrate and/or the gas supply head can be moved so that the substrate is sequentially exposed to the gases.
In one or more embodiments, the barrier layer material and the dopant metal are deposited using a multi-chamber process with separation of the barrier layer material (e.g. niobium nitride (NbN)) and the dopant metal (e.g., Ru). In other embodiments, a single chamber approach is used, with all processes occurring within one chamber and the different layers separated in processing by gas purges.
Some embodiments of the invention are directed to barrier applications, e.g. copper barrier applications. The barrier layer formed by one or more embodiments may be used as a copper barrier. In some embodiments, the barrier films for copper barrier applications include, but are not limited to, NbN. In some embodiments, the dopant metal includes, but is not limited to, Ru.
A plasma treatment can be used after doping to promote the intermetallic compound formation between the nitride matrix and the dopant metal, as well as removing film impurities and improving the barrier layer density. In other embodiments, post treatment can include, but is not limited to, physical vapor deposition (PVD) treatment, thermal anneal, chemical enhancement, or the like.
In some copper barrier applications, a high frequency plasma (defined as greater than about 14 MHz, e.g., about 40 MHz or greater) can be used with any inert gas, including, but not limited to, one or more of neon (Ne), hydrogen (H2), and argon (Ar) gas. In one or more embodiments, to prevent low-k damage, a higher plasma frequency can be used (higher than 13.56 MHz).
Suitable reactants for depositing a barrier film include metal-containing precursors and nitrogen-containing precursors. In some embodiments, the metal-containing precursor comprises niobium (Nb). In some embodiments, the niobium-containing precursor comprises substantially no halide atoms. As used in this regard, a precursor which “comprises substantially no halide atoms” contains less than 5%, less than 2% or less than 1% halide atoms on an atomic basis. In some embodiments, the niobium-containing precursor may be tris(diethylamido)(tert-butylimido)niobium (TBTDEN). In some embodiments, the metal-containing reactant is reacted with ammonia or hydrazine. Other suitable reactants are known to those skilled in the art.
Some embodiments of the disclosure are advantageously able to deposit the barrier film at a relatively low substrate temperature. In some embodiments, the temperature of the substrate is maintained at a temperature of less than or equal to 300° C. In some embodiments, after depositing the barrier film, the barrier film is treated with a conductively coupled plasma (CCP) or an inductively coupled plasma (ICP).
In some embodiments, the barrier film is deposited using an atomic layer deposition process which utilizes a plasma reactant. In some embodiments, the barrier film is deposited by an atomic layer deposition process which forms the barrier film without plasma (“thermal ALD”).
In one or more embodiments, the dopant metal may be incorporated into the barrier layer by any suitable method known to the skilled artisan. For example, in one or more embodiments, the dopant metal may be incorporated into the barrier layer by one or more of alternating and/or co-flowing of precursors in atomic layer deposition (ALD), chemical vapor deposition (CVD), and plasma enhanced atomic layer deposition (PEALD); precursors with multi-metal ligands; and dopant implanting/thermal diffusion. In one or more embodiments, when the dopant metal is incorporated into the barrier layer by alternating and/or co-flowing of precursors in atomic layer deposition (ALD), chemical vapor deposition (CVD), or plasma enhanced atomic layer deposition (PEALD), an appropriate metal-containing precursor may be used. Examples of suitable precursors include metal complexes containing the desired dopant, such as dopant metals coordinated with organic or carbonyl ligands. In one or more embodiments, a dopant precursor may comprise a multi-metal ligand. A suitable dopant precursor should have sufficient vapor pressure to be deposited in the appropriate process, such as ALD, plasma enhance atomic layer deposition (PEALD), or chemical vapor deposition (CVD). In one or more embodiments, the dopant is deposited using a chemical vapor deposition (CVD) process.
As used herein, “chemical vapor deposition” refers to a process in which a substrate surface is exposed to precursors and/or co-reagents simultaneous or substantially simultaneously. As used herein, “substantially simultaneously” refers to either co-flow or where there is an intentional overlap of precursors in the gas phase.
Depending on the dopant precursor used, a co-reactant may be used to deposit the dopant. For example, reducing gases such as hydrogen (H2) and ammonia can be used as co-reactants for depositing some dopants. Metal dopant precursors and co-reactants may be either co-flowed or flowed sequentially.
In some embodiments, after depositing the dopant layer 216, the dopant layer and barrier layer are exposed to a hydrogen anneal treatment.
In some embodiments, instead of or in addition to using a reducing gas co-reactant, a post-plasma treatment step may be used after exposing the barrier film to the dopant metal precursor. According to one or more embodiments, the plasma comprises any suitable inert gas known to the skilled artisan. In one or more embodiments, the plasma comprises one or more of helium (He), argon (Ar), ammonia (NH3), hydrogen (H2), and nitrogen (N2). In some embodiments, the plasma may comprise a mixture of Ar and H2, such as a mixture having an Ar:H2 molar ratio in the range from 1:1 to 1:10. The plasma power may be in the range from about 200 to about 1000 Watts. The plasma frequency may be in the range from 350 kHz to 40 MHz. The plasma treatment time may vary from 5 second to 60 seconds, such as in the range from 10 seconds to 30 seconds. In some embodiments, the pressure during plasma treatment may be in the range from 0.5 to 50 Torr, such as from 1 to 10 Torr. In some embodiments, the wafer spacing may be in the range from 100 mils to 600 mils.
In one or more embodiments, the barrier film may be exposed to the dopant metal precursor during deposition, i.e. the dopant metal precursor may be used sequentially in the ALD cycle to provide a doped barrier film. For example, 1-10 cycles of metal-containing precursors and nitrogen-containing precursors can be used to form an initial metal nitride barrier layer, followed by exposure to 1-10 cycles of the dopant metal precursor, then resuming cycles of the metal-containing precursors and nitrogen-containing precursors, then optionally more doping, etc., until the desired doped barrier film thickness is reached. Alternatively, in other embodiments, the barrier film may be completely deposited to the desired thickness before exposing to the dopant metal precursors.
In various embodiments, the duration of the exposure to the dopant metal-containing precursor may range from 1 to 60 seconds, such as in the range from 3 to 30 seconds or from 5 to 10 seconds. Longer exposures to the dopant metal precursor will increase the amount of doping of the barrier film, as long as the barrier film has not reached the maximum doping for the density of the barrier film.
The Figures show substrates having a single feature for illustrative purposes; however, those skilled in the art will understand that there can be more than one feature. As used in this regard, the term “feature” means any intentional surface irregularity. Suitable examples of features include, but are not limited to, trenches which have a top, two sidewalls and a bottom, peaks which have a top and two sidewalls. Features can have any suitable aspect ratio (ratio of the depth of the feature to the average width of the feature). In some embodiments, the aspect ratio is greater than or equal to about 5:1, 10:1, 15:1, 20:1, 25:1, 30:1, 35:1 or 40:1.
In one or more embodiments, the dielectric layer 204 is a low-k dielectric layer. In certain embodiments, the dielectric layer 204 comprises silicon oxide (SiOx). Further embodiments provide that the dielectric layer 204 comprises porous or carbon-doped SiOx. In some embodiments, the dielectric layer 204 is a porous or carbon-doped SiOx layer with a k value less than about 5. In other embodiments, the dielectric layer 204 is a multilayer structure. For example, in one or more embodiments, the dielectric layer 204 comprises a multilayer structure having one or more of a dielectric layer, an etch stop layer, and a hard mask layer.
With reference to
In one or more embodiments, the barrier film 214 is substantially conformal. As used herein, a layer which is “substantially conformal” refers to a layer where the thickness is about the same throughout (e.g., on the top, middle and bottom of sidewalls and on the bottom 212 of the feature 206). A layer which is substantially conformal varies in thickness by less than or equal to about 5%, 2%, 1% or 0.5%.
In one or more embodiments, the barrier film 214 is deposited by atomic layer deposition (ALD), and has a thickness in a range of from about 2 Å to about 10 Å. In some embodiments, the barrier film 214 is deposited in a single ALD cycle. In other embodiments, the barrier film 214 is deposited in from 1 to 15 ALD cycles.
With reference to
Without intending to be bound by theory, it is thought that the metal dopant can selectively diffuse through the barrier layer 214 to the dielectric layer and form a complex with the dielectric material that will be resistant to electromigration. One proposed mechanism is that the exposed precursor can preferentially migrate to the dielectric/barrier layer interface via grain boundaries or other weak paths.
In one or more embodiments, the complex formed may be a metal oxide (MOx) or a metal silicate (MSixO). Thus, in embodiments where the dopant is ruthenium (Ru) and the dielectric layer comprises silicon oxide (SiOx), the ruthenium (Ru) can diffuse from the dopant layer 216 through the barrier layer 214 to form ruthenium oxide (RuOx) or ruthenium silicon oxide (RuSiOx). This boundary layer of ruthenium silicon oxide can prevent copper electromigration from a later deposited conductive material 222 into the dielectric layer 204.
In other embodiments, the metal dopant may form intermetallic compounds (e.g., Ru:NbN) with the barrier layer matrix, resulting in a high density, low resistivity phase, which presents superior barrier performance against copper (Cu), oxygen (O), and/or carbon (C) diffusion.
In addition to being a barrier against the conductive material 222, doped barrier layer 220 may also be a barrier to oxygen diffusing from the dielectric layer 204 to the conductive material 222. Oxygen diffusion from the dielectric layer 204 to the conductive material 222 can result in oxygen reacting with components in the conductive material 222.
In one or more embodiments, it is believed that oxygen diffusing from the dielectric layer 204 into the barrier layer 214 will react with the dopant and will be prevented from diffusing into the conductive material 222. As a result, oxygen will not be available to react with any seed layer or the conductive material 222.
In one or more embodiments, the dopant layer 216 is deposited by chemical vapor deposition and has a thickness in a range of from about 1 Å to about 3 Å or in a range of about 2 Å to about 10 Å.
In one or more embodiments, the barrier layer 220 comprises in a range of from about 0.01 to about 50 wt. % dopant, based on the total weight of the barrier layer 220. In certain embodiments, the barrier layer 220 comprises a range of from about 5% to about 70% dopant, such as a range of from about 10 to about 30 wt. % dopant, such as a range of from about 8 to about 25 wt. % dopant, or a range of from about 10 to about 20 wt. % dopant. In some embodiments, the barrier film 220 comprises a range of from about 5 to about 30 wt. % dopant, such as about 5 wt. %, about 6 wt. %, about 7 wt. %, about 8 wt. %, about 9 wt. %, about 10 wt. %, about 11 wt. %, about 12 wt. %, about 13 wt. %, about 14 wt. %, 15 wt. %, about 16 wt. %, about 17 wt. %, about 18 wt. %, about 19 wt. %, about 20 wt. %, about 21 wt. %, about 22 wt. %, about 23 wt. %, about 24 wt. %, 25 wt. %, about 26 wt. %, about 27 wt. %, about 28 wt. %, about 29 wt. %, or about 30 wt. % dopant. In some embodiments, the barrier layer comprises dopant in a range of 30 wt. % to 40 wt. %.
With reference to
In one or more embodiments, the second barrier film 218 is deposited by atomic layer deposition (ALD), and has a thickness in a range from about 2 Å to about 10 Å, or in a range of from about 2 Å to about 6 Å. In some embodiments, the second barrier film 218 is deposited in a single ALD cycle. In other embodiments, the second barrier film 218 is deposited in from 1 to 15 ALD cycles.
In some embodiments, one or more additional layers of the dopant layer or the barrier film are deposited. In these embodiments, each layer of the barrier film is separated by a layer of the dopant layer. In some embodiments, the doped barrier layer may be formed by 3, 4, 5, 6, 7 or more deposited layers.
In one or more embodiments, a doped barrier layer 220, which comprises the barrier film 214, doped layer 216, and second barrier film 218, has a combined thickness in a range of from about 5 Å to about 15 Å, or from about 8 Å to about 10 Å. In further embodiments, the combined thickness is less than about 15 Å.
In one or more embodiments, the doped barrier layer 220 has a high metal content and an amorphous crystallinity. Without intending to be bound by theory, it is thought that doping a barrier layer reduces the ALD crystallinity of the deposited barrier layer, which could reduce diffusion shortcut on grain boundary. Doping within the barrier layer instead of on top of the barrier may mitigate integration and corrosion risks due to minimal dopant diffusion.
In one or more embodiments, the doped barrier layer 220 comprises a dopant metal in a barrier film, where the dopant metal is an amorphous matrix of nanocrystallites. In specific embodiments, the doped niobium nitride (NbN) barrier film comprises ruthenium (Ru) in a niobium nitride film, where the ruthenium (Ru) is an amorphous matrix of nanocrystallites. The doped barrier film of one or more embodiments shows better diffusion barrier properties than barrier films of different compositions (e.g., TaN). Additionally, the doped barrier film of one or more embodiments, demonstrates superior adhesion to copper and oxide.
At operation 110, the device is optionally post-processing. The optional post-processing operation 110 can be, for example, a process to modify film properties (e.g., annealing) or a further film deposition process (e.g., additional ALD or CVD processes) to grow additional films. In some embodiments, the optional post-processing operation 110 can be a process that modifies a property of the deposited film. In some embodiments, the optional post-processing operation 110 comprises annealing the as-deposited film. In some embodiments, annealing is done at temperatures in the range of about 300° C., 400° C., 500° C., 600° C., 700° C., 800° C., 900° C. or 1000° C. The annealing environment of some embodiments comprises one or more of an inert gas (e.g., molecular nitrogen (N2), argon (Ar)) or a reducing gas (e.g., molecular hydrogen (H2) or ammonia (NH3)) or an oxidant, such as, but not limited to, oxygen (O2), ozone (O3), or peroxides. Annealing can be performed for any suitable length of time. In some embodiments, the film is annealed for a predetermined time in the range of about 15 seconds to about 90 minutes, or in the range of about 1 minute to about 60 minutes. In some embodiments, annealing the as-deposited film increases the density, decreases the resistivity and/or increases the purity of the film.
With reference to
Although the conductive fill material 220 in
In certain embodiments, a seeding layer (not illustrated) may be deposited on top of the doped barrier layer 220. According to one or more embodiments, the seeding layer can comprise an alloy of copper, such as a Cu—Mn alloy.
In addition to being a copper barrier, the doped barrier layer 220 may also be a barrier to oxygen diffusing from the dielectric layer 204 to the conductive fill material 222. Oxygen diffusion from the dielectric layer 204 to the conductive fill material 222 can result in oxygen reacting with components in the conductive fill material 222 and/or seed layer.
In some embodiments, the substrate is moved from a first chamber to a separate, next chamber for further processing. The substrate can be moved directly from the first chamber to the separate processing chamber, or the substrate can be moved from the first chamber to one or more transfer chambers, and then moved to the separate processing chamber. In some embodiments, the deposition of the barrier film and the dopant film can be done in a single chamber, and then the post-processing can be performed in a separate chamber. Accordingly, the processing apparatus may comprise multiple chambers in communication with a transfer station. An apparatus of this sort may be referred to as a “cluster tool” or “clustered system”, and the like.
Generally, a cluster tool is a modular system comprising multiple chambers which perform various functions including substrate center-finding and orientation, degassing, annealing, deposition and/or etching. According to one or more embodiments, a cluster tool includes at least a first chamber and a central transfer chamber. The central transfer chamber may house a robot that can shuttle substrates between and among processing chambers and load lock chambers. The transfer chamber is typically maintained at a vacuum condition and provides an intermediate stage for shuttling substrates from one chamber to another and/or to a load lock chamber positioned at a front end of the cluster tool. Two well-known cluster tools which may be adapted for the present disclosure are the Centura® and the Endura®, both available from Applied Materials, Inc., of Santa Clara, Calif. However, the exact arrangement and combination of chambers may be altered for purposes of performing specific steps of a process as described herein. Other processing chambers which may be used include, but are not limited to, cyclical layer deposition (CLD), atomic layer deposition (ALD), chemical vapor deposition (CVD), physical vapor deposition (PVD), etch, pre-clean, chemical clean, plasma nitridation, degas, orientation, hydroxylation and other substrate processes. By carrying out processes in a chamber on a cluster tool, surface contamination of the substrate with atmospheric impurities can be avoided without oxidation prior to depositing a subsequent film.
According to one or more embodiments, the substrate is continuously under vacuum or “load lock” conditions, and is not exposed to ambient air when being moved from one chamber to the next. The transfer chambers are thus under vacuum and are “pumped down” under vacuum pressure. Inert gases may be present in the processing chambers or the transfer chambers. In some embodiments, an inert gas is used as a purge gas to remove some or all of the reactants (e.g., reactant). According to one or more embodiments, a purge gas is injected at the exit of the deposition chamber to prevent reactants (e.g., reactant) from moving from the deposition chamber to the transfer chamber and/or additional processing chamber. Thus, the flow of inert gas forms a curtain at the exit of the chamber.
The substrate can be processed in single substrate deposition chambers, where a single substrate is loaded, processed and unloaded before another substrate is processed. The substrate can also be processed in a continuous manner, similar to a conveyer system, in which multiple substrate are individually loaded into a first part of the chamber, move through the chamber and are unloaded from a second part of the chamber. The shape of the chamber and associated conveyer system can form a straight path or curved path. Additionally, the processing chamber may be a carousel in which multiple substrates are moved about a central axis and are exposed to deposition, etch, annealing, cleaning, etc. processes throughout the carousel path.
During processing, the substrate can be heated or cooled. Such heating or cooling can be accomplished by any suitable means including, but not limited to, changing the temperature of the substrate support and flowing heated or cooled gases to the substrate surface. In some embodiments, the substrate support includes a heater/cooler which can be controlled to change the substrate temperature conductively. In one or more embodiments, the gases (either reactive gases or inert gases) being employed are heated or cooled to locally change the substrate temperature. In some embodiments, a heater/cooler is positioned within the chamber adjacent the substrate surface to convectively change the substrate temperature.
The substrate can also be stationary or rotated during processing. A rotating substrate can be rotated (about the substrate axis) continuously or in discrete steps. For example, a substrate may be rotated throughout the entire process, or the substrate can be rotated by a small amount between exposures to different reactive or purge gases. Rotating the substrate during processing (either continuously or in steps) may help produce a more uniform deposition or etch by minimizing the effect of, for example, local variability in gas flow geometries.
Additional embodiments of the disclosure are directed to processing tools 900 for the formation of the devices and practice of the methods described, as shown in
The cluster tool 900 comprises a plurality of processing chambers 902, 904, 906, 908, 910, 912, 914, 916, and 918, also referred to as process stations, connected to the central transfer station. The various processing chambers provide separate processing regions isolated from adjacent process stations. The processing chamber can be any suitable chamber including, but not limited to, an atomic layer deposition chamber, a chemical vapor deposition chamber, an annealing chamber, and the like. The particular arrangement of process chambers and components can be varied depending on the cluster tool and should not be taken as limiting the scope of the disclosure.
In the embodiment shown in
The size and shape of the loading chamber 954 and unloading chamber 956 can vary depending on, for example, the substrates being processed in the cluster tool 900. In the embodiment shown, the loading chamber 954 and unloading chamber 956 are sized to hold a wafer cassette with a plurality of wafers positioned within the cassette.
A robot 952 is within the factory interface 950 and can move between the loading chamber 954 and the unloading chamber 956. The robot 952 is capable of transferring a wafer from a cassette in the loading chamber 954 through the factory interface 950 to load lock chamber 960. The robot 952 is also capable of transferring a wafer from the load lock chamber 962 through the factory interface 950 to a cassette in the unloading chamber 956. As will be understood by those skilled in the art, the factory interface 950 can have more than one robot 952. For example, the factory interface 950 may have a first robot that transfers wafers between the loading chamber 954 and load lock chamber 960, and a second robot that transfers wafers between the load lock 962 and the unloading chamber 956.
The cluster tool 900 shown has a first section 920 and a second section 930. The first section 920 is connected to the factory interface 950 through load lock chambers 960, 962. The first section 920 includes a first transfer chamber 921 with at least one robot 925 positioned therein. The robot 925 is also referred to as a robotic wafer transport mechanism. The first transfer chamber 921 is centrally located with respect to the load lock chambers 960, 962, process chambers 902, 904, 916, 918, and buffer chambers 922, 924. The robot 925 of some embodiments is a multi-arm robot capable of independently moving more than one wafer at a time. In some embodiments, the first transfer chamber 921 comprises more than one robotic wafer transfer mechanism. The robot 925 in first transfer chamber 921 is configured to move wafers between the chambers around the first transfer chamber 921. Individual wafers are carried upon a wafer transport blade that is located at a distal end of the first robotic mechanism.
After processing a wafer in the first section 920, the wafer can be passed to the second section 930 through a pass-through chamber. For example, chambers 922, 924 can be uni-directional or bi-directional pass-through chambers. The pass-through chambers 922, 924 can be used, for example, to cryo cool the wafer before processing in the second section 930, or allow wafer cooling or post-processing before moving back to the first section 920.
A system controller 990 is in communication with the first robot 925, second robot 935, first plurality of processing chambers 902, 904, 916, 918 and second plurality of processing chambers 906, 908, 910, 912, 914. The system controller 990 can be any suitable component that can control the processing chambers and robots. For example, the system controller 990 can be a computer including a central processing unit (CPU) 992, memory 994, inputs/outputs (I/O) 996, and support circuits 998. The controller 990 may control the processing tool 900 directly, or via computers (or controllers) associated with particular process chamber and/or support system components.
In one or more embodiments, the controller 990 may be one of any form of general-purpose computer processor that can be used in an industrial setting for controlling various chambers and sub-processors. The memory 994 or computer readable medium of the controller 990 may be one or more of readily available memory such as non-transitory memory (e.g. random access memory (RAM)), read only memory (ROM), floppy disk, hard disk, optical storage media (e.g., compact disc or digital video disc), flash drive, or any other form of digital storage, local or remote. The memory 994 can retain an instruction set that is operable by the processor (CPU 992) to control parameters and components of the processing tool 900.
The support circuits 998 are coupled to the CPU 992 for supporting the processor in a conventional manner. These circuits include cache, power supplies, clock circuits, input/output circuitry and subsystems, and the like. One or more processes may be stored in the memory 994 as software routine that, when executed or invoked by the processor, causes the processor to control the operation of the processing tool 900 or individual processing units in the manner described herein. The software routine may also be stored and/or executed by a second CPU (not shown) that is remotely located from the hardware being controlled by the CPU 992.
Some or all of the processes and methods of the present disclosure may also be performed in hardware. As such, the process may be implemented in software and executed using a computer system, in hardware as, e.g., an application specific integrated circuit or other type of hardware implementation, or as a combination of software and hardware. The software routine, when executed by the processor, transforms the general purpose computer into a specific purpose computer (controller) that controls the chamber operation such that the processes are performed.
In some embodiments, the controller 990 has one or more configurations to execute individual processes or sub-processes to perform the method. The controller 990 can be connected to and configured to operate intermediate components to perform the functions of the methods. For example, the controller 990 can be connected to and configured to control a physical vapor deposition chamber.
Processes may generally be stored in the memory 994 of the system controller 990 as a software routine that, when executed by the processor, causes the process chamber to perform processes of the present disclosure. The software routine may also be stored and/or executed by a second processor (not shown) that is remotely located from the hardware being controlled by the processor. Some or all of the method of the present disclosure may also be performed in hardware. As such, the process may be implemented in software and executed using a computer system, in hardware as, e.g., an application specific integrated circuit or other type of hardware implementation, or as a combination of software and hardware. The software routine, when executed by the processor, transforms the general purpose computer into a specific purpose computer (controller) that controls the chamber operation such that the processes are performed.
In some embodiments, the system controller 990 has a configuration to control an atomic layer deposition chamber to deposition a barrier film on a substrate. The system controlled 990 has a second configuration to control a chemical vapor deposition chamber to deposit a metal film on the barrier film at a temperature in the range of about 20° C. to about 400° C.
In one or more embodiments, a processing tool comprises: a central transfer station comprising a robot configured to move a wafer; a plurality of process stations, each process station connected to the central transfer station and providing a processing region separated from processing regions of adjacent process stations, the plurality of process stations comprising a deposition chamber, a plasma treatment chamber, a remote plasma source, an annealing chamber, and a controller connected to the central transfer station and the plurality of process stations, the controller configured to activate the robot to move the wafer between process stations, and to control a process occurring in each of the process stations.
Reference throughout this specification to “one embodiment,” “certain embodiments,” “one or more embodiments” or “an embodiment” means that a particular feature, structure, material, or characteristic described in connection with the embodiment is included in at least one embodiment of the disclosure. Thus, the appearances of the phrases such as “in one or more embodiments,” “in certain embodiments,” “in one embodiment” or “in an embodiment” in various places throughout this specification are not necessarily referring to the same embodiment of the disclosure. Furthermore, the particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments.
Although the disclosure herein has been described with reference to particular embodiments, it is to be understood that these embodiments are merely illustrative of the principles and applications of the present disclosure. It will be apparent to those skilled in the art that various modifications and variations can be made to the method and apparatus of the present disclosure without departing from the spirit and scope of the disclosure. Thus, it is intended that the present disclosure include modifications and variations that are within the scope of the appended claims and their equivalents.
This application claims priority to U.S. Provisional Application No. 63/357,613, filed Jun. 30, 2022, the entire disclosure of which is hereby incorporated by reference herein.
| Number | Date | Country | |
|---|---|---|---|
| 63357613 | Jun 2022 | US |