Patent Grant
7335611
High speed integrated circuits formed on a crystalline semiconductor wafer have ultra shallow semiconductor junctions formed by ion implanting dopant impurities into source and drain regions. The implanted dopant impurities are activated by a high temperature anneal step which causes a large proportion of the implanted atoms to become substitutional in the crystalline semiconductor lattice. Such a post-ion implantation anneal step are done by a rapid thermal process (RTP)-employing powerful lamps that heat the entire wafer volume to a very high temperature for a short time (e.g., a rate-of-rise of about 100-200 degrees C. per second and an initial rate-of-fall of 50-100 degrees C. per second). The heating duration must be short to avoid degrading the implanted junction definition by thermally induced diffusion of the dopant impurities from their implanted locations in the semiconductor wafer. This RTP approach is a great improvement over the older post-ion implant anneal technique of heating the wafer in a furnace for a long period of time. RTP using lamps is effective because the time response of the heat source (the lamp filament) is short in contrast to the furnace annealing step in which the heater response time is very slow. The high temperature, short duration heating of the RTP method favors the activation of implanted impurities while minimizing thermally induced diffusion.
An improved anneal is done by a flash lamp anneal process employing powerful flash lamps that heat the surface (only) of the entire wafer to a very high temperature for a very short time (e.g., a few milliseconds). The heating duration must be short to avoid degrading the implanted junction definition by thermally induced diffusion of the dopant impurities from their implanted locations in the semiconductor wafer. This flash approach is an improvement over the RTP approach, because the bulk of the wafer acts as a heat sink and permits rapid cooling of the hot wafer surface. High speed anneal using flashlamps is more effective because the heating is confined to the surface of the wafer, in contrast to the RTP annealing step in which the entire volume of the wafer is heated to approximately the same anneal temperature. The short duration at high temperature of the flash method minimizes thermally induced diffusion. However, it is difficult to achieve thermal uniformity over the entire wafer. Greater thermal non-uniformity within wafer creates significant amount of mechanical stress, resulting in wafer breakage and limits the highest operating temperature to approximately 1150° C. for anneal using flash lamps. The surface temperature during flashlamp annealing is determined by the intensity and pulse duration of flashlamps, which are difficult to control in a repeatable manner from one wafer to the next.
One problem with RTP is that as device size decreases to 65 nanometers (nm) and below, the minimal thermal diffusion caused by RTP or flash heating becomes significant relative to the device size, despite the short duration of the RTP or flash heating. Another problem is that the degree of activation of the implanted dopant impurities is limited by the maximum temperature of the RTP or flash process. Heating the entire wafer volume in the RTP process above the maximum temperature (e.g., 1100 degrees C.) can create mechanical stresses in the wafer that cause lattice defects and wafer breakage in extreme cases. Limiting the wafer temperature to a maximum level (e.g., 1100 degrees C.) prevents such breakage, but unfortunately limits the proportion of implanted (dopant) atoms that are activated (i.e., that become substitutional in the semiconductor crystalline lattice). Limiting the dopant activation limits sheet conductivity and limits device speed. This problem becomes more significant as device size is reduced below 65 nm (e.g., down to 45 nm).
In order to raise the level of dopant activation beyond that achieved by RTP or flash annealing, laser annealing has been introduced as a replacement for RTP. One type of laser that has been used is a C02 laser having an emission wavelength of 10.6 microns. This laser produces a narrow cylindrical beam, which must be raster-scanned across the entire wafer surface. In order to decrease the surface reflectivity at 10.6 microns, the beam is held at an acute angle relative to the wafer surface. Since the CO2 laser wavelength corresponds to a photon energy less than the bandgap of silicon, the silicon must be pre-heated to populate the conduction band with free carriers in order to facilitate the absorption of 10.6 micron photons through free carrier absorption. A fundamental problem is that the absorption at 10.6 microns is pattern-dependent because it is affected by the dopant impurities (which among other factors, determines the local free carrier concentration), so that the wafer surface is not heated uniformly. Also, conductive or metallic features on the wafer are highly reflective at the 10.6 micron laser wavelength, so that this process may not be useful in the presence of conductive thin film features.
The post-implant anneal step has been performed with short wavelength pulsed lasers (the short wavelength corresponding to a photon energy greater than the bandgap of silicon). While the surface heating is extremely rapid and shallow, such pulsed lasers bring the semiconductor crystal to its melting point, and therefore the heating must be restricted to an extremely shallow depth, which reduces the usefulness of this approach. Typically, the depth of the heated region does not extend below the depth of the ultra-shallow junctions (about 200 Angstroms).
The foregoing problems have been overcome by employing an array of diode lasers whose multiple parallel beams are focused along a narrow line (e.g., about 300 microns wide) having a length on the order of the wafer diameter or radius. The diode lasers have a wavelength of about 810 nm. This wavelength corresponds to a photon energy in excess of the bandgap energy of the semiconductor crystal (silicon), so that the laser energy excites electron transitions between the valence and conduction bands, which subsequently release the absorbed energy to the lattice and raises the lattice temperature. The narrow laser beam line is scanned transversely across the entire wafer surface (e.g., at a rate of about 300 mm/sec), so that each point on the wafer surface is exposed for a very short time (e.g., about 1 millisec). This type of annealing is disclosed in United States Patent Publication No. US 2003/0196996A1 (Oct. 23, 2003) by Dean C. Jennings et al. The wafer is scanned much more quickly by the wide thin beam line than by the pencil-like beam of a single laser spot, so that productivity is much greater, approaching that of RTP. But, unlike RTP, only a small portion of the wafer surface is heated, so that the stress is relieved in the remaining (bulk) portion of the wafer, allowing the peak temperature to be increased above the maximum RTP temperature (e.g., to about 1250-1300 degrees C). The entire wafer volume may also be preheated during the laser scanning anneal in order to improve the annealing characteristics. The maximum preheated temperature is dictated by the technology nodes, process requirements, compatibility with semiconductor materials, etc. As a result, dopant activation is much higher, so that sheet resistivity is lower and device speed is higher. Each region of the wafer surface reaches a temperature range of about 1250-1300 degrees C. for about 50 microsec. The depth of this region is about 10-20 microns. This extends well-below the ultra-shallow semiconductor junction depth of about 200 Angstroms.
The wafer surface must be heated above a minimum temperature (e.g., 1250 degrees C.) in order to achieve the desired degree of activation of the implanted (dopant) atoms. The elevated temperature is also required to anneal other lattice damage and defects caused by any preceeding implant or thermal steps, in order to improve the electrical characteristics of the junctions such as their electrical conductivity and leakage. The wafer surface must be kept below a maximum temperature (e.g., 1350 degrees C.) in order to avoid the melting temperature of the semiconductor crystal (e.g., crystalline or polycrystalline silicon). In order to uniformly heat the entire wafer surface within this desired temperature range, the optical absorption of the wafer surface must be uniform across the wafer, and the surface temperature in the illuminated portion of the wafer surface must be accurately monitored while the laser beam line is scanned across the wafer (to enable precise temperature control). This is accomplished by measuring the emission of light by the heated portion of the wafer surface (usually of a wavelength different from that of the laser light source), and the measurement must be uniformly accurate. As employed in this specification, the term “optical” is meant to refer to any wavelength of a light or electromagnetic radiation emitted from a light source (such as a laser) that is infrared or visible or ultraviolet or emitted from the heated wafer surface.
The problem is that the underlying thin film structures formed on the wafer surface present different optical absorption characteristics and different optical emissivities in different locations on the wafer surface. This makes it difficult if not impossible to attain uniform anneal temperatures across the wafer surface and uniformly accurate temperature measurements across the wafer surface. This problem can be solved by depositing a uniform optical absorption layer over the entire wafer surface that uniformly absorbs the laser radiation and then conducts the heat to the underlying semiconductor wafer. Such a film must withstand the stress of heating during the laser anneal step without damage or separation, and must be selectively removable after the laser anneal step with respect to underlayers and must not contaminate or damage the underlying semiconductor wafer or thin film features. Further, the absorber film must attain excellent step coverage (high degree of conformality) over the underlying thin film features. One advantage of such a film is that lateral heat conduction in the film can mask non-uniformities in the light beam. This approach has been attempted but has been plagued by problems. One type of absorber layer consists of alternating metal and dielectric layers that form an anti-reflective coating. The different layers in this type of absorber material tend to fuse together under the intense heat of the laser beam, and become difficult to remove following the laser anneal step or contaminate underlying layers with metal.
A better approach used in the present invention is to employ an absorber layer that can be deposited by plasma enhanced chemical vapor deposition (PECVD). As disclosed in U.S. patent application Ser. No. 10/679,189 filed Oct. 3, 2003 by Luc Van Autryve et al. entitled “Absorber Layer for DSA Processing” and assigned to the present assignee, the PECVD-deposited absorber layer may be amorphous carbon. One advantage of amorphous carbon is that it is readily and selectively (with respect to underlayers of other materials) removed by oxidation in a plasma process or a downstream oxidation process employing radicals, at a wafer temperature less than 400 C. Another advantage is that carbon is generally compatible with semiconductor plasma processes and therefore does not involve contamination, so long as excessive implantation does not occur. One problem is that the deposited layer is vulnerable to cracking or peeling under the high temperatures of the laser anneal step, unless the layer is deposited at a very high temperature (e.g., 550 degrees C.). (The tendency or resistance to such cracking, peeling or separation of the deposited layer from the underlying layer in response to high temperature or high temperature gradients is generally referred to in this specification as the thermal or thermal-mechanical properties of the deposited layer.) Also the thermal budget (time and temperature) associated with this PECVD deposition process caused dopants to form clusters which are difficult to dissolve with the subsequent laser anneal step, particularly for feature sizes below 65 nm (such as feature sizes of about 45 nm). Attempting to solve this problem by reducing the wafer temperature (e.g., to 400 degrees C.) during PECVD deposition of the absorber layer material creates two problems. First, the thermal properties of the deposited layer are such that it will fail (by cracking, peeling or separation from the wafer) during the laser annealing step. Secondly, the deposited layer that is produced is transparent or has insufficient optical absorption. Another problem encountered with this absorber layer is that it has poor step coverage. We have observed that the PECVD 550 degree absorber layer can have very large voids in the vicinity of pronounced steps in the underlying layer or thin film structures sizes below 65 nm.
We feel that failure of the absorber layer (e.g., by peeling or cracking) arises from a lack of high quality chemical bonds (between the underlying layer and the deposited material) capable of withstanding the stress of being rapidly heated to 1300 degrees C. during the laser anneal step. We feel that, in order to improve the thermal properties of the deposited layer, achieving such high quality bonds at low wafer temperature requires high ion energies during the PECVD process. Such high ion energies are not readily attainable in conventional PECVD reactors. We feel that poor step coverage by the absorber layer or amorphous carbon layer is the result of the inability of a conventional PECVD or HDPCVD reactor to provide an intermediate range of ionization (ion-to-radical ratio) with an adequate level of energetic ion bombardment. These inadequacies arise, in part, because such conventional PECVD and HDPCVD reactors cannot operate within a wide intermediate range of source power coupling (to generate plasma electrons), chamber pressure and wafer voltage. Indeed, the different types of conventional PECVD and HDPCVD reactors tend to operate at either very high or very low ranges of source power coupling (to generate plasma electrons), chamber pressure and wafer voltage. Conventional PECVD reactors employ capacitively-coupled RF source power at relatively high-pressure, resulting in a very low range of ionization (ion-to-radical ratio) with an inadequate level of energetic ion bombardment (and no separate control of voltage or energy). This is due to the inefficient source power coupling (to generate plasma electrons) and the damping of ion energies by collisions with neutrals at high pressure. Even if separate RF biasing of the wafer is added, the damping of ion energies by collisions with neutrals at high pressure limits the voltage and energy range to a low range. Conversely, conventional HDPCVD reactors typically employ inductively-coupled RF source power at very low pressure. This type of plasma source typically initiates the plasma capacitively, and then has a high power threshold to transition to inductively coupled power mode. Once the power coupled is above this threshold and the source is operating in an inductive mode, the source power coupling is highly efficient and the minimum possible plasma density and range of ionization (ion-to-radical ratio) is very high. The separate RF wafer bias is coupled to the relatively dense plasma, which presents a very low electrical impedance load. The resultant RF bias power required to produce energetic ion bombardment is very high (>>10 kW for >2 kV). High energies are not generally attainable due to practical RF delivery system limitations (RF generators, matching networks, and feed structures). Most of the bias power (e.g., ˜80%) is dissipated as heat on the wafer. It is very difficult to remove the heat at low pressure at an adequate rate to maintain low wafer temperature (<400 deg. C. or lower). Finally, both capacitively-coupled PECVD and inductively-coupled HDPCVD reactors may have power coupling drift (with on-time) issues when used with carbon chemistry when depositing absorbing or semiconducting films (on RF windows or insulators). The need (fulfilled by the toroidal plasma CVD reactor and process described in detail below) is for a reactor capable of providing ionization ratios in a wide intermediate range together with an adequate level of energetic ion bombardment in all cases, through an ability to operate in a wide intermediate range of source power coupling and level, wafer voltage and chamber pressure. The toroidal plasma CVD reactor does not exhibit power coupling drift when used with carbon chemistry when depositing absorbing or semiconducting films. This is because the toroidal plasma CVD reactor is already conducting (metal), having only very thin, isolated DC breaks, which do not accumulate much deposition and are easily in-situ plasma cleaned.
One type of conventional PECVD reactor is a capacitively coupled plasma reactor having a pair of closely-spaced parallel plate electrodes across which RF plasma source power is applied. Such a capacitively coupled reactor typically is operated at high chamber pressure (2-10 Torr). High pressure and close-spacing (relative to electrode radius) are employed to maximize deposition rate on the wafer, and to minimize deposition outside the process region. The plasma source power couples to both electrons in the bulk plasma and to ions in the plasma sheaths. The voltage across the electrodes is typically relatively low (less than 1 KVpp at source power of several kW for 300 mm wafer) and the plasma sheath is very collisional, so that the ion energy is typically low. This type of reactor produces a very low ion-to-neutral population ratio and ion-to-radical ratio, so that the ion flux is low, which probably increases the ion energy level or wafer temperature required to obtain the requisite high quality bonds between the deposited and underlying materials. However, because of the low inter-electrode voltage and the high loss of ion energy in the collisional sheath, it is very difficult to generate the ion energy distribution required for high quality bonds.
Another type of conventional PECVD reactor is an inductively coupled high plasma density CVD (HPDCVD) reactor in which RF source power is applied to an inductive antenna. The reactor must be operated at a low chamber pressure (e.g., 5-10 milliTorr) and high plasma source power level, because of the high minimum induced electric field required to maintain the inductively coupled plasma mode, which in turn produces a high plasma density. The degree of ionization (ratio of ion-to-neutral density) produced in this reactor is confined to a range of very high values (four or five orders of magnitude greater than that of the capacitive reactor discussed above), because a large amount of RF source power is required to sustain the inductively coupled mode and because the RF induced electric field couples directly to electrons in the bulk plasma. This contrasts with a capacitively coupled plasma in which the RF electric field less efficiently couples to electrons indirectly by displacement across the plasma sheath or through plasma sheath oscillations. As a result, plasma density and conductivity is very high, making it difficult to generate a high wafer voltage at practical bias power levels (since the wafer voltage is loaded down through the highly conductive plasma). As a result, high ion energies cannot be attained without applying excessive amounts of RF bias power to the wafer. This could overheat the wafer and perhaps destroy the ultra shallow junction definition in the underlying semiconductor crystal lattice (by thermal diffusion). Typically, for a 300 mm wafer, a wafer voltage of 1-2 kV peak-to-peak would require RF bias power of about 10 kWatts. Cooling the wafer to maintain ultra-shallow junction definition is difficult at high bias power, and even higher bias voltage (than 1-2 kV) and thus higher power is desired for best film properties. RF power delivery systems >10 kW are very expensive and have limited availability.
Another problem with the HDPCVD reactor is that a large non-conductive window must be provided in the chamber ceiling through which the plasma source power may be inductively coupled from the coil antenna. This prevents the use of a conductive showerhead directly overlying the wafer, which limits gas distribution uniformity at the wafer and RF bias ground reference uniformity over the wafer. Moreover, coupling of source power into the chamber may be effectively reduced or even blocked if the reactor is employed to deposit a non-insulating material on the wafer, since that same material will also accumulate on the dielectric window during processing, creating a conductive shield or semi-conductive attenuator to the RF power. The temperature of a non-conductive surface, such as the dielectric window of the HDPCVD reactor, cannot be effectively controlled, so that deposition during processing and post-process cleaning of the reactor interior is more difficult. A related problem in both types of reactors is that plasma source power seeks a ground return from any available conductive surface in the chamber, so that process control is hampered by electrical changes due to deposition of by-products on the chamber surfaces. With both dielectric and metallic materials constituting the chamber surfaces, removal of deposited plasma by-products after processing may be difficult or may involve undue wear of chamber parts. This may be circumvented by employing disposable shields or process kits to prevent deposition on chamber surfaces. However, such disposable shields cannot provide good RF ground reference nor be thermally controlled with any precision.
In summary, the conventional reactors are either confined to a narrow low chamber pressure window (in the case of the HDPCVD reactor) or a narrow high chamber pressure window (in the case of the capacitively coupled reactor). Neither chamber can achieve a high ion energy, either because the sheath is highly collisional (in the capacitively coupled reactor) or because the plasma is highly conductive (in the HDPCVD reactor). Also, they are confined to either a narrow high degree-of-ionization regime (the HDPCVD reactor) or a narrow low degree-of-ionization regime (the capacitively coupled reactor). Moreover, both types of reactors are susceptible to wide deviations in performance whenever they are used for deposition of non-insulating materials, since the accumulation of non-insulating materials across electrode boundaries in a capacitively coupled reactor or on the dielectric window of an inductively coupled reactor will distort or inhibit the coupling of RF source power into the chamber. What is needed is a deposition process carried out at a very low temperature (e.g., room temperature up to several hundred degrees C.) for forming an optical absorber layer having such high quality bonds with the underlying layers (including the semiconductor lattice) that it is impervious to mechanical failure or separation during the laser annealing step. The process should have a wide source power window, a wide degree-of-ionization window in an intermediate range, a wide wafer voltage (bias power) window with wide ion energy window, and a wide wafer temperature window.
A method of forming a conductor in a thin film structure on a semiconductor substrate includes forming high aspect ratio openings in a base layer having vertical side walls, depositing a dielectric barrier layer comprising a dielectric compound of a barrier metal on the surfaces of the high aspect ratio openings including the vertical side walls, depositing a metal barrier layer comprising the barrier metal on the first barrier layer, depositing a main conductor species seed layer on the metal barrier layer and depositing a main conductor layer. The method further includes annealing the main conductor layer by (a) directing light from an array of continuous wave lasers into a line of light extending at least partially across the thin film structure, and (b) translating the line of light relative to the thin film structure in a direction transverse to the line of light. The method of claim 1 further comprising, prior to the annealing step, depositing an amorphous carbon optical absorber layer on the main conductor layer. The step of depositing an amorphous carbon optical absorber layer includes introducing a carbon-containing process gas into a reactor chamber containing the substrate in a process zone of the reactor, applying RF source power to an external reentrant conduit of the reactor to generate a reentrant toroidal RF plasma current passing through the process zone and applying a bias voltage to the substrate.
Introduction:
All the problems mentioned above in the background discussion are solved by depositing the amorphous carbon optical absorber layer in a low temperature PECVD process employing a toroidal source plasma reactor. The toroidal source can be operated with a wide range of ion energy, unlike either the HDPCVD reactor or the capacitively coupled PECVD reactor. Thus, a moderate ion flux can be maintained along with a moderate (or high) ion energy, so that a high quality bond between the deposited layer and the underlying substrate or thin films is established without requiring elevated wafer temperatures. In fact, the wafer temperature may be as cool as room temperature (which minimizes any impact on the implanted ultra-shallow junctions such as recrystallization of an amorphous layer formed during the implant process, dopant cluster formation or thermal diffusion). As a result, the absorber layer formed by this process can withstand the laser beam exposure and extreme heating without separating from the wafer and without cracking. The wide bias power or bias voltage range over which the toroidal plasma source reactor may be operated enables the stress of the deposited layer to be selected within a very wide range, i.e., from tensile to compressive stress levels. The wide source power range over which toroidal plasma source reactor may be operated enables the conformality of the deposited layer to be precisely controlled, for example, to guarantee a high degree of conformality for excellent step coverage. The toroidal source plasma reactor may be operated over a much wider range of chamber pressure (e.g., 10-80 mT), so that ion density and plasma sheath collisionality may be controlled over a much wider range. Since a high ion density is not required, a high wafer voltage and high ion energy may be maintained with a relatively small amount of bias power (e.g., 7 kV wafer voltage with only 7 kW of bias power for a 300 mm wafer). The toroidal plasma source reactor does not require a dielectric window for coupling RF power from an inductive antenna into the chamber (and requires only a very thin dielectric “DC-break”), and therefore a conductive shower head may be placed at the ceiling. This feature provides the best uniformity of process gas distribution and a highly uniform low-impedance RF ground reference over the wafer. Because there is no requirement for a dielectric window for inductive coupling, virtually the entire chamber can be metal and therefore be thermally controlled to regulate deposition during processing and to expedite post-processing high temperature cleaning of the chamber surfaces. The toroidal plasma source generates a plasma with low potential and the toroidal plasma current requires no ground return through chamber surfaces, so the potential to cause a drift-current out of the process region is low and therefore there is little or no deposition on chamber surfaces outside of the processing zone. Another advantage of the lack of any need for a dielectric window in the toroidal plasma reactor is that the reactor may be employed to deposit non-insulating materials on the wafer without bad effects from accumulation of the non-insulating material on chamber interior surfaces.
The present invention concerns dynamic surface annealing of ultra-shallow junctions in a semiconductor wafer using an array of continuous wave (CW) diode lasers collimated and focused to a single knife-edge light beam. The knife-edge light beam is highly intense and is scanned across the wafer in a direction transverse to its length. The temperature is raised briefly (to nearly the melting point of silicon) in such a highly localized area about the beam, that its cooling is extremely rapid because of the small volume that is thus heated at any particular instant. This technology is described in United States Patent Application Publication No. US 2003/0196996 A1 by Dean C. Jennings et al., published Oct. 23, 2003 (hereinafter referred to as Publication A). At extremely small feature sizes (e.g., 45 nm), it is difficult to heat the wafer uniformly due to the presence of 3-dimensional topological features. These features may be comprised of different materials or have different optical properties. Such features render heat absorption non-uniform. They also render the surface emissivity non-uniform, so that it is impossible to monitor the surface temperature accurately.
These problems have been addressed in the past by depositing an optical absorber layer over the entire wafer (which is later removed). This absorber layer has a high imaginary component of the complex refractive index (the “k” value of the n+ik , where ‘n’ is the refractive index and ‘k’ is the extinction coefficient). A sufficiently thick absorber layer masks emissivity variations due to the underlying films on the wafer, as well as their dimensional topological features, promoting improved laser absorption and uniformity of the heat absorption across the wafer (as well as magnitude and uniformity of surface emissivity). The problem is that the optical absorber layer must withstand the near-melting point temperatures sustained during dynamic surface (laser) annealing, without peeling or separating from the underlying layers. In order to avoid such peeling or separation, a high quality bond between the absorber layer and the underlying wafer features is achieved by depositing the absorber layer at a high temperature. The high temperature also serves to provide good film structural, optical and electrical properties. The problem is that if the wafer temperature is sufficiently high to achieve a high quality absorber layer that is immune to cracking, peeling or separation, then the wafer temperature causes the undesirable effects of either recrystallizing a pre-existing amorphous silicon layer or causes the ultra-shallow junctions to diffuse and thereby become poorly defined, thereby degrading circuit features on the wafer. Lower temperature conventional CVD absorber layers also have significantly reduced “k” values, requiring much thicker films to achieve the same net absorption and immunity to underlayer absorption characteristics.
These problems are overcome in accordance with the invention by depositing the absorber layer in a low temperature chemical vapor deposition process using the toroidal plasma source low temperature CVD process of United States Patent Application Publication No. 2004/0200417 by Hiroji Hanawa et al., published Oct. 14, 2004 (hereinafter referred to as Publication B). This process employs a unique toroidal source plasma reactor that is described in detail in Publication B. The process is carried out at very low temperatures, such as under 300 degrees C. or even as low as room temperature. Thus, it has little or no bad effects (e.g., thermal diffusion or dopant migration, or re-crystallization) upon the ultra-shallow junction features already formed on the wafer. If the absorber layer is to be amorphous carbon, then a carbon-containing process gas is employed. In order to enhance absorption of heat from the laser beam in the absorber layer, the deposited amorphous carbon layer is rendered more opaque by doping it with an impurity such as boron, phosphorous, arsenic, silicon or germanium. This may be done by an ion implantation step using the toroidal source plasma immersion ion implantation (P3i) process also described in Publication B, or (alternatively) by incorporating boron into the process gas mixture during the CVD low temperature deposition process. Ion implantation of other impurities (such as nitrogen) into the deposited amorphous carbon absorber layer may be employed in order to adjust or control the dielectric constant or refractive index of the absorber layer, in order to obtain a high dielectric constant, for example. Alternatively, other impurities (such as nitrogen, hydrogen, oxygen, fluorine) may be incorporated by including them in the process gas mixture during the CVD low temperature deposition process.
The thermal properties, i.e., the immunity of the low temperature deposited absorber layer from peeling, cracking or separation during the dynamic surface laser annealing step, are enhanced by making the deposited layer a compressively stressed layer. This is accomplished by raising the RF plasma bias power or bias voltage to a relatively high level in the low temperature plasma CVD process, as described in Publication B. Excellent step coverage over all the 3-dimensional micro-circuit features previously formed on the wafer is obtained by depositing the absorber layer with relatively high conformality. This is accomplished by setting the plasma RF source power in the low temperature plasma CVD process to a relatively high level, as described in Publication B. The adhesion of the deposited film may be enhanced by pre-treating the wafer in a cleaning process to remove surface oxidation or other contamination. One pre-treatment process uses a hydrogen plasma generated by plasma source power or bias power. A bias voltage may be added to enhance the cleaning rate. It is believed that the hydrogen ions and/or radicals etch the thin oxide or contaminant film. Another pre-treatment process uses a nitrogen and/or oxygen plasma generated by plasma source power or bias power. A bias voltage may be added to enhance the cleaning rate. It is believed that the nitrogen and/or oxygen ions and/or radicals etch the thin organic contaminant film. This pre-treatment process may be followed by the hydrogen plasma pre-treatment process to remove oxidation. Another pre-treatment process uses an inert gas plasma such as helium, neon, argon or xenon to sputter clean the surface oxidation or contamination. Alternatively, a wet pre-treatment process may be used to clean the wafer surface (to enhance bonding) prior to depositing the film.
The absorber layer film optical properties may be tuned with process variables in order to have a high absorption or extinction coefficient or imaginary part of the complex refractive index at the wavelength of radiation of the laser light beam and the wavelength of the temperature measurement pyrometer. Such process variables may include impurity (e.g., nitrogen) concentration in the absorber layer, dopant (e.g., boron) concentration in the absorber layer, wafer temperature, process gas pressure, gas flow rates (of C-containing gas, impurity-containing-gas, dilution gas such as helium, hydrogen or argon), RF bias voltage or power, RF plasma source power, process time and layer thickness. Additional enhancement of the properties of the absorber layer may be obtained by grading the concentration of such impurities with depth in the layer. This may be accomplished by adjusting the implantation depth profile of impurities that are ion implanted by the P3i process referred to above, or by ramping the concentration of such impurities in the process gas or changing RF bias voltage or power or RF plasma source power or pressure during the low temperature CVD process described in Publication B. Additional enhancement of the properties of the absorber layer may be obtained by curing the wafer with deposited absorber layer. Curing may include thermal (time at temperature) or UV exposure or a combination. This may further increase or stabilize the absorption or extinction coefficient or imaginary part of the complex refractive index.
The same toroidal source plasma chamber of Publication B may be employed to perform both the absorber layer deposition using low temperature CVD process of Publication B as well as any P3i ion implantation processes (as described in Publication B) of impurities into the absorber layer, so that the wafer need not be transported between different chambers. Moreover, the process chamber of Publication A (that performs the laser beam dynamic surface anneal (DSA) process) is preferably integrated into the same tool or platform with the toroidal source plasma reactor of Publication B, so that the wafer can be coated with the absorber layer (e.g., of amorphous carbon), the absorber layer may be enhanced by P3i ion implantation of selected impurities and/or dopants, and the wafer then laser annealed using the DSA laser light source of Publication A, all in the same tool. This reduces risk of contamination of the wafer. Moreover the same toroidal plasma source chamber or a second (dedicated) toroidal source plasma chamber (of the same type described in Publication B) or a different type of plasma chamber may be integrated onto the same tool or platform for removing the absorber layer upon completion of the laser anneal DSA process.
A fully integrated process requires the following chambers which are used on a given wafer in the following order: a plasma immersion ion implantation (P3i) chamber for implanting dopants to form ultra-shallow junction (USJ) source/drain structures; a resist strip chamber for removing the USJ structure-defining or patterned photoresist; a wet clean chamber for post resist-strip cleaning; a toroidal source or P3i plasma reactor for performing the low temperature CVD process by which the amorphous carbon absorber layer is formed; a chamber containing the DSA multiple laser light source and scanning apparatus; a carbon-strip chamber for removing the absorber layer; and a wet clean chamber for post-strip cleaning of the wafer. At least two or more of the foregoing chambers may be integrated onto a common platform to reduce wafer handling, reduce contamination and increase productivity.
The absorber layer is preferably amorphous carbon, although other suitable materials may be chosen instead. The product of the film thickness and the absorption or extinction coefficient or imaginary part of the complex refractive index at the wavelength of radiation of the laser light beam of the absorber layer must be sufficient to deposit over all the 3-dimensional topological features or micro-circuit structures on the wafer such that the optical properties of the underlying materials are masked to the degree required by the absorber layer. The absorber layer optical properties are selected to maximize heat absorption from the laser beam. The absorber layer thermal or thermal-mechanical properties are selected to render the absorber layer immune from peeling, cracking or separation from the underlying wafer during DSA laser annealing despite the near-melting point temperatures of the process.
The absorber layer maximizes uniform absorption from the laser beam even in the presence of pronounced 3-dimensional surface topological features on the wafer. The absorber layer is a good heat conductor and therefore provides uniform heat distribution across the locally radiated area of the wafer. The uniform surface of the absorber layer renders the surface emissivity of the wafer uniform, so that accurate measurements of wafer temperature may be continuously made, for good process control.
The absorber layer as described above may also be advantageously used for more conventional annealing techniques, such as RTA (rapid thermal anneal) or “spike” anneal or flashlamp anneal, to improve the magnitude or uniformity of light absorption, and to reduce across wafer and wafer-to-wafer temperature variation. Such a layer may be used to mask the variation in the optical properties, including 3-D geometric effects, of underlayers. In this case, the absorber layer deposition/implantation is tuned for the desirable optical properties across the spectrum of wavelengths that the filament or arc/gas discharge light source produces. The heat absorber layer of the present invention may also be used in RTA annealing of semiconductor wafers having 3-dimensional micro-circuit topological features. In such a case, the absorber layer optical properties are adapted to the RTA light source. Such devices may include such highly reflective structures as silicon-on-insulator or polysilicon on dielectric structures.
Laser Thermal Flux Annealing Light Source:
The dynamic surface anneal light source referred to above uses CW diode lasers to produce very intense beams of light that strikes the wafer as a thin long line of radiation. The line is then scanned over the surface of the wafer in a direction perpendicular to the long dimension of the line beam. One embodiment of the light source is illustrated in the schematic orthographic representation of
In typical operation, the gantry beams 116, 118 are set at a particular position along the fixed rails 112, 114 and the beam source 120 is moved at a uniform speed along the gantry beams 116, 118 to scan the line beam 126 perpendicularly to its long dimension in a direction conveniently called the fast direction. The line beam 126 is thereby scanned from one side of the wafer 40 to the other to irradiate a 1 cm swath of the wafer 40. The line beam 126 is narrow enough and the scanning speed in the fast direction fast enough that a particular area of the wafer is only momentarily exposed to the optical radiation of the line beam 126 but the intensity at the peak of the line beam is enough to heat the surface region to very high temperatures. However, the deeper portions of the wafer 40 are not significantly heated and further act as a heat sink to quickly cool the surface region. Once the fast scan has been completed, the gantry beams 116, 118 are moved along the fixed rails 112, 114 to a new position such that the line beam 126 is moved along its long dimension extending along the slow axis. The fast scanning is then performed to irradiate a neighboring swath of the wafer 40. The alternating fast and slow scanning are repeated, perhaps in a serpentine path of the beam source 120, until the entire wafer 40 has been thermally processed. One example of optics beam source 120, orthographically illustrated in
Returning to
The source beam output by the light pipe 170 is generally uniform. As further illustrated in the schematic view of
In order to regulate or control the peak wafer temperature, the temperature of the illuminated portion of the wafer 40 is constantly monitored by a pyrometry system. The pyrometry system uses the same optics used to focus the laser source light on the wafer to direct thermal radiation emitted from the illuminated area of the wafer 40 in the neighborhood of the line beam 126 in the reverse direction to a pyrometer 161 schematically shown in
The features of the present invention described below may be employed with other laser types: CO2 gas-lasers; Neodymium YAG lasers (neodymium: yttrium-aluminum-garnet) which may optionally be frequency-doubled; Excimer lasers (a rare-gas halide or rare-gas metal vapor laser emitting in the ultraviolet (126 to 558 nm) that operates on electronic transitions of molecules, up to that point diatomic, whose ground state is essentially repulsive) with excitation by E-beam or electric discharge; diode lasers (light-emitting diode designed to use stimulated emission to form a coherent light output).
Low Temperature CVD Process of the Toroidal Source Plasma Reactor:
RF bias power or voltage is applied to the chuck 14 by an RF bias power generator 44 through an impedance match circuit 46. A D.C. chucking voltage is applied to the chuck 14 from a chucking voltage source 48 isolated from the RF bias power generator 44 by an isolation capacitor 50. The RF power delivered to the wafer 40 from the RF bias power generator 44 can heat the wafer 40 to temperatures beyond 400 degrees C., depending upon the level and duration of the applied RF plasma bias power from the generator 44 if no wafer cooling is employed. It is believed that about 80% or more of the RF power from the bias power generator 44 is dissipated as heat in the wafer 40. The wafer support pedestal 14 is an electrostatic chuck having an insulative or semi-insulative top layer or puck 60. A metal (molybdenum, for example) wire mesh or metal layer 62 inside of the puck 60 forms a cathode (or electrode) to which the D.C. chucking voltage and RF bias voltage is applied. The puck 60 is supported on a metal layer 64 that rests on a highly insulative layer 66. A metal base layer 68 may be connected to ground. The wafer 40 is electrostatically held on the chuck 14 by applying a D.C. voltage from the chucking voltage source 48 to the electrode 62. This induces an opposite (attractive) image charge in the bottom surface of the wafer 40. The effective gap between the two opposing charge layers is so minimal as a result of the upward charge migration in the semi-insulator layer 60 that the attractive force between the chuck and the wafer 40 is very large for a relatively small applied chucking voltage. The puck semi-insulator layer 60 therefore is formed of a material having a desired charge mobility, so that the material is not a perfect insulator. RF bias power or voltage from the RF bias power generator 44 may be applied to the electrode 62 or, alternatively, to the metal layer 64 for RF coupling through the semi-insulative puck layer 60. Heat is removed from the puck 60 by cooling the metal layer 64. For this reason, internal coolant passages 70 are provided within the metal layer 64 coupled to a coolant pump 72 and heat sink or cooling source 74. Heat sink 74 may optionally be a heat exchanger which can also furnish heat, if desired, to metal layer 64. A very high heat transfer coefficient between the wafer 40 and the puck 60 is realized by maintaining a very high chucking force. The force can be enhanced by providing a polished surface 60a.
A low-temperature chemical vapor deposition process preferably employs an electrostatic wafer chuck that both serves to couple RF bias power or voltage to the wafer and removes (or provides) heat to maintain the wafer temperature at the desired level or below a threshold. More preferably, the electrostatic chuck is the type described immediately above with reference to
The fact that the CVD reaction can be carried out in the toroidal source reactor at a low source power level, if desired, implies a large window in which source power can be varied, from the minimum level up to a maximum level (e.g., about 5 kW per toroidal source ). This window is sufficiently large to vary the conformality of the CVD deposited layer between non-conformal (0.1 conformality ratio) and conformal (>0.5 conformality ratio). At the same time, the stress level of the CVD deposited layer may be varied by varying the plasma bias power or voltage applied to the wafer between a low level for tensile stress in the deposited layer (e.g., 500 Watts) and a high level for compressive stress in the deposited layer (e.g., 3 kWatts or higher). As a result, the conformality and stress of each plasma CVD deposited layer are independently adjusted by adjusting the source and bias power levels, respectively, to different layers which are either conformal or non-conformal and having either tensile or compressive stress. Non-conformal films are useful for deep trench filling and for creating removable layers over photoresist. Conformal layers are useful for etch stop layers and passivation layers. Layers with compressive stress enhance carrier mobility in underlying or adjacent P-channel MOSFETs, while layers with tensile stress enhance carrier mobility in underlying or adjacent N-channel MOSFETs. The low minimum plasma source power of the toroidal source plasma reactor of
Post-CVD ion implantation processes can be carried out in the same toroidal source reactor that was used to perform the low temperature CVD process. The post CVD ion implantation processes include processes for enhancing adhesion between an amorphous or polycrystalline CVD deposited layer and its base layer, for raising the proportion of a species in the CVD layer beyond a stochiometric proportion, for implanting into the CVD layer a species not compatible with plasma CVD processes, or for implanting into the CVD layer a species that alters a particular material quality of the layer, such as dielectric constant or stress.
The low temperature plasma CVD process is useful for CVD formation of silicon films, silicon nitride films, silicon-hydrogen films, silicon-nitrogen-hydrogen films, and versions of the foregoing films further containing oxygen or fluorine. The films exhibit excellent quality and excellent thermal properties, being free of cracking, peeling, flaking, etc., despite the very low temperature at which the CVD process is carried out. For application to CMOS devices, passivation layers are deposited over P- and N-channel devices with compressive and tensile stresses, respectively, using high non-conformality to enable selective etching and photoresist masking and removal, and etch stop layers with zero (neutral) stress can be deposited over all devices with high conformality. Low temperature plasma CVD process is also useful for CVD formation of carbon films.
A low temperature plasma CVD process employing the toroidal reactor of
Another feature of the toroidal plasma reactor of
Deposition of a Carbon Film by the Toroidal Source CVD Process:
The present invention is useful for depositing films such as carbon-based films of particular optical properties (at UV, infrared and visible wavelengths, i.e., “optical” wavelengths) or of particular electrical properties (e.g., in applications where optical properties are not of particular interest) such as conductivity or complex permittivity. Both electrical and optical properties of such films are adjusted to meet the particular need. The present invention is also useful for depositing films such as carbon-based films where subsequent strippability of the deposited carbon-based film layers is required with selectivity with respect to silicon or other underlying layer. The present invention is also useful for depositing films such as carbon-based films where conformality control is required, for void-free gap fill applications. The present invention is also useful for depositing films such as carbon-based films where stress control is required.
Hydrogen-Carbon films:
Carbon films of different electrical and optical properties may be deposited on wafers using the toroidal plasma source reactor of
Adjustment of the ion bombardment energy at the wafer surface may be done by adjusting RF bias power, RF bias voltage or wafer voltage, and/or chamber pressure, while adjustment of the flux of energetic ions at the wafer surface may be done by adjusting RF plasma source power and/or chamber pressure and/or dilution gas flow.
Energetic ion flux adjustment: at constant bias voltage and constant pressure, increasing the RF plasma source power increases the flux of energetic ions at the wafer surface. Radical flux at the wafer surface also increases with source power. However, at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), the ratio of energetic ion flux relative to radical flux at the wafer still typically increases (but is still much less than unity). Increasing RF plasma source power at constant bias voltage, while decreasing pressure, further increases the ratio of energetic ion flux relative to radical flux at the wafer. At constant source power and bias voltage, diluting the process gas with argon or xenon tends to increase the flux of energetic ions at the wafer surface, while diluting with helium or neon tends to decrease the flux of energetic ions at the wafer surface. The effect is intensified as ratio of dilution gas flow rate with respect to process gas flow rate is increased. At lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing pressure at constant RF plasma source power and bias voltage increases the flux of energetic ions at the wafer surface.
Ion energy adjustment: at constant RF plasma source power, increasing RF bias power or voltage increases ion bombardment energy at the wafer surface. At constant RF plasma source power and RF bias voltage and at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing the pressure decreases ion energy, though the effect is not necessarily large. At constant RF plasma source power and RF bias power and at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing the pressure decreases ion energy with larger effect, as the bias voltage (at constant bias power) is reduced due to the loading effect of the higher plasma ion and electron density.
Selecting the hydrogen-carbon gas species of the process gas (selecting the hydrogen-carbon ratio of the gas) affects the optical and electrical properties of the deposited material. Decreasing the hydrogen-carbon ratio of the gas typically decreases the C:H bonding and increases the C:C bonding, which increases the optical absorption (decreases transparency) and increases electrical conductivity. It also tends to increase the “imaginary” component of permittivity relative to “real” component. For example, C3H6 may produce a deposited layer with greater optical absorption and/or electrical conductivity than CH4, and C4H6 may provide a deposited layer with greater optical absorption and/or electrical conductivity than C3H6. Diluting the process gas(es) with hydrogen affects the optical and electrical properties of the deposited material. Decreasing the hydrogen dilution typically decreases the C:H bonding and increases the C:C bonding, which increases the optical absorption (decreases transparency) and increases electrical conductivity. It also tends to increase the “imaginary” component of permittivity relative to “real” component. In addition to the foregoing steps for adjusting the optical absorption of the deposited carbon material, optical absorption may be enhanced by including certain additive materials in the deposited material such as boron, nitrogen or sulfur. Any of these materials may be added by including precursor gases such as B2H6, N2 or H2S, respectively, in the process gases. Adding material such as boron, nitrogen or sulfur to the process gases also substantially improves the thermal stability of the deposited carbon material, allowing it to be rapidly heated to high temperature (>1400 degree C.) without failure.
Material additions can enhance optical absorption, thermal stability, and/or electrical conductivity and/or permittivity of the deposited material. The ratio of hydrogen to boron, nitrogen or sulfur in the additive gas affects the properties of the deposited layer. Typically decreasing the hydrogen-to-other-element ratio of the gas typically decreases the C:H bonding and increases the C:C bonding, which increases the optical absorption (decreases transparency) and increases electrical conductivity. It also tends to increase the “imaginary” component of permittivity relative to “real” component. For higher optical absorption or electrical conductivity, BSH9 (as compared to B2H6) or N2 (as compared to NH3) may increase absorption or conductivity to a greater degree. B2H6 typically must be diluted (in the gas bottle) due to its higher reactivity for safety reasons, and is commercially available diluted with helium, argon, hydrogen or nitrogen. Hydrogen-diluted-B2H6 typically provides greater enhancement of optical absorption and electrical conductivity than does helium-diluted-B2H6. Argon-diluted-B2H6 may provide even greater enhancement of optical absorption and electrical conductivity than does helium- or hydrogen-diluted B2H6. Nitrogen-diluted-B2H6 can also provide greater enhancement of optical absorption and electrical conductivity than does helium- or hydrogen-diluted-B2H6, and can provide a synergistic benefit as described below. B5H9 does not require dilution, and has a higher B-to-H ratio than B2H6, so may provide a greater enhancement of optical absorption and electrical conductivity than does helium- or hydrogen-diluted-B2H6. The factors mentioned above which increase conductivity also tend to increase the “imaginary” component of permittivity relative to “real” component. Alternatively, the post-CVD ion implantation step described above may be performed with one of the absorption-enhancement species (B, N or S) by implanting that species into the deposited carbon layer. If this post-CVD implantation step is carried out by plasma immersion ion implantation using the toroidal plasma source reactor of
There is a synergistic benefit of adding (a) boron (i.e., B2H6) plus (b) N2 or other form of nitrogen to the basic amorphous carbon precursor hydrocarbon gas (i.e., C3H6). Thermal stability (i.e., the thermal properties) of the deposited carbon layer is improved at 450 degrees C. and especially higher temperatures. Specifically, the deposited amorphous carbon layer may be laser heated at least to the melting point of silicon without delamination of the deposited layer, or peeling, etc. This feature (of adding boron and nitrogen) actually reduces the threshold wafer voltage or threshold ion energy typically required to avoid delamination or peeling. The foregoing feature, for improving the deposited layer thermal properties, of combining boron and nitrogen additives in the hydrocarbon gas may be employed when depositing an amorphous carbon layer having particular electrical properties controlled in the manner described above. It may also be employed for depositing a carbon layer that is not an optical absorber. It is believed that adjustment of the properties of the deposited carbon layer is based upon: (1) adjustment of the proportion of bound hydrogen atoms in the carbon layer, that is, proportion of C:H bonds out of the total atomic bonds in the deposited carbon layer and (2) the length of the C:C chains and (3) the bonding hybridization of the carbon atoms and the relative concentration of the different bonds, i.e., sp3:s2p:sp1. It is further believed that increasing the ion energy at the wafer surface and increasing the energetic ion flux at the wafer surface and increasing the wafer temperature can have the effect of (1) breaking more C:C chains (to produce shorter ones) and (2) breaking more C:H bonds (to reduce their presence) and forming more C:C bonds and (3) changing the bonding hybridization of the carbon atoms and the relative concentration of the different bonds, i.e., sp3:sp2:sp1. By reducing the hydrogen content in the process gases in the reactor chamber, the number of C:H bonds formed in the deposited carbon layer is reduced.
Reduction in the length of the C:C chains changes the state of the deposited material from a soft polymer to a hard amorphous carbon. With a reduction in the number of C:H bonds in the deposited carbon layer, the electrical conductivity changes from relatively insulative to semiconductive, while the optical properties change from relatively transparent to relatively opaque. Thus, the electrical conductivity of the deposited carbon layer may be set anywhere within a range between insulative and semiconductive, while its optical properties may be set anywhere within a range between transparent and opaque, in the toroidal plasma CVD process.
The reduction or breaking of C:C bonds and/or C:H bonds by ion bombardment may require very high ion energies (e.g., on the order of 100 eV to 1 keV). Polymer carbon (with long polymer chains) tends to be formed at low (less than 100 degrees C.) wafer temperatures. The length of the polymer chains is reduced by ion bombardment, even at the low wafer temperature. Alternatively, the wafer temperature may be increased during the toroidal plasma CVD process (e.g., to 400 degrees C.) to keep the C:C chain length short. The very high ion energy required to modify the optical and electrical properties of the deposited carbon layer (requiring high RF bias power) has the effect of enhancing adhesion of the carbon layer to the underlying wafer or thin film structures previously formed on the wafer, by forming high quality atomic bonds between the deposited carbon layer and the underlying material. It also enhances the resistance of the deposited film to mechanical failure or separation induced by thermal stress (e.g., very high temperatures), by generating compressive stress in the deposited carbon layer. It also increases the mechanical hardness of the film. Applying high bias voltage (i.e., >1 kV) substantially improves the thermal stability of the deposited carbon material, allowing it to be rapidly heated to high temperature (>1400 degrees C.) without failure. In addition to heating the wafer during the toroidal plasma CVD process, an additional method for enhancing the optical absorption of the deposited carbon layer is to heat the wafer to about 400 degrees C. after completion of the CVD process. It is believed that this step enhances optical absorption by the same mechanism of breaking up C:H bonds and forming more C:C bonds in the deposited carbon layer and changing the bonding hybridization of the carbon atoms and the relative concentration of the different bonds, i.e., sp3:sp2:sp1.
Adding an inert dilution gas to the hydrogen-carbon precursor gas may modify the electrical and optical properties of the film. Adding helium or neon, for example, makes the film more transparent (and more insulating), while adding argon or xenon makes the film more opaque (and more semiconducting). It is believed, for a constant RF source power and RF bias voltage, that the helium addition decreases the ion flux while adding argon or xenon increases the ion flux. Increasing the energetic ion flux tends to decrease the optical transparency and electrical resistivity of the film. The factors mentioned above which increase conductivity also tend to increase the “imaginary” component of permittivity relative to “real” component. Increasing the RF bias voltage at constant RF source power increases the ion energy of ions impinging on the wafer surface, which tends to decrease the optical transparency and electrical resistivity of the film. It also tends to increase the “imaginary” component of permittivity relative to “real” component. Increasing the RF source power at constant RF bias voltage increases the energetic ion flux to the wafer surface, which tends to decrease the optical transparency and electrical resistivity of the film. It also tends to increase the “imaginary” component of permittivity relative to “real” component. Increasing the gas pressure at constant RF source power and RF bias voltage increases the energetic ion flux to the wafer surface, which tends to decrease the optical transparency and electrical resistivity of the film. It also tends to increase the “imaginary” component of permittivity relative to “real” component.
The conformality of the deposited carbon layer is adjusted by adjusting the RF plasma source power. Adjusting deposited layer conformality by adjusting source power is described above in this specification. The stress of the deposited carbon layer is adjusted by adjusting the RF plasma bias power. Adjusting deposited layer stress by adjusting bias power is described above in this specification.
Fluoro-Carbon Films:
A fluoro-carbon process gas, selected from one of the fluoro-carbon gases listed earlier in this specification, may be employed as the CVD process gas, instead of a hydrogen-carbon gas, to deposit a fluorine-containing carbon layer on the wafer. Such a layer tends to be transparent across a wide band of wavelengths. A fluorine-containing carbon layer is useful where a very low-dielectric constant is desired in the deposited carbon layer. It is also useful where a transparent carbon layer is desired. It is also useful where a highly insulating carbon film is desired. It is also useful where a lower permittivity, having a small “imaginary” component relative to “real” component, is desired. For fluorocarbon film, preferred fluorcarbon gases are C4F6 or C3F6. Other fluorocarbon gases include C2F4, C2F6, C3F8, C4F8 and C5F8. The process may be used to deposit fluoro-hydrocarbon films. For fluoro-hydrocarbon films, fluoro-hydrocarbon gases such as CH2F2 may be used. Alternatively, the process may be used to deposit a film which is a combination of hydrocarbon and fluorocarbon materials, in which case combinations of suitable hydrocarbon and fluorocarbon gases may be employed as the process gas. Such fluorine-containing films may be amorphous or polymer. Such fluorine-containing films tend to be transparent, depending upon the fluorine content. Such films may have a very low dielectric constant, depending upon fluorine content. Films containing both fluorocarbons (or fluoro-hydrocarbons) and hydrocarbons may vary between transparent and absorbing depending upon the relative hydrogen and fluorine content.
The properties of the fluorine-containing carbon layer may be controlled in a manner similar to that described above for hydrogen-containing carbon layers, by controlling the length of carbon-carbon chains and by controlling the proportion and type of F:C bonds in the carbon film. The properties may be controlled by any one or a combination of some or all of the following actions:
Adjustment of the ion bombardment energy at the wafer surface may be done by adjusting RF bias power, wafer voltage and/or chamber pressure, while adjustment of the flux of energetic ions at the wafer surface may be done by adjusting RF plasma source power and/or chamber pressure and/or dilution gas flow.
Energetic ion flux adjustment: at constant bias voltage and constant pressure, increasing the RF plasma source power increases the flux of energetic ions at the wafer surface. Radical flux at the wafer surface also increases with source power. However, at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), the ratio of energetic ion flux relative to radical flux at the wafer still typically increases (but is still much less than unity). Increasing RF plasma source power at constant bias voltage, while decreasing pressure, further increases the ratio of energetic ion flux relative to radical flux at the wafer. At constant source power and bias voltage, diluting the process gas with argon or xenon tends to increase the flux of energetic ions at the wafer surface, while diluting with helium or neon tends to decrease the flux of energetic ions at the wafer surface. The effect is intensified as ratio of dilution gas flow rate with respect to process gas flow rate is increased. At lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing pressure at constant RF plasma source power and bias voltage increases the flux of energetic ions at the wafer surface.
Ion energy adjustment: at constant RF plasma source power, increasing RF bias power or voltage increases ion bombardment energy at the wafer surface. At constant RF plasma source power and RF bias voltage and at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing pressure decreases ion energy, though the effect is not necessarily large. At constant RF plasma source power and RF bias power and at lower to moderate pressure (i.e., mtorr pressure to several hundred mtorr), increasing pressure decreases ion energy with larger effect, as the bias voltage (at constant bias power) is reduced due to the loading effect of the higher plasma ion and electron density. The conformality of the deposited fluoro-carbon layer is adjusted by adjusting the RF plasma source power. Adjusting deposited layer conformality by adjusting source power is described above in this specification. The stress of the deposited fluoro-carbon layer is adjusted by adjusting the RF plasma bias power. Adjusting deposited layer stress by adjusting bias power is described above in this specification.
A combination of a fluoro-carbon gas and a hydrogen-carbon gas may be used as the process gas to form a carbon layer containing both fluorine and hydrogen in a desired proportion. This proportion may be used to realize a desired conductivity or absorption in the deposited carbon layer. The same methods described immediately above for regulating the proportion of C:H and C:F bonds in the individual C:F and C:H deposited materials may be used to control the proportion of C:H and C:F bonds in the combination C:F+C:H deposited carbon material. A carbon layer containing both hydrogen and fluorine may also be formed by adding a non-fluorocarbon gas containing fluorine to a hydrocarbon gas in a plasma process using the toroidal source. For example, F2 or BF3 or SiF4 or NF3 may be added to a hydrocarbon gas. Conversely, a carbon layer containing both hydrogen and fluorine may also be formed by adding a non-hydrocarbon gas that contains hydrogen to a fluorocarbon gas in a plasma process using the toroidal source. For example, H2 or B2H6 or SiH4 or NH3 may be added to a fluorocarbon gas.
Low Temperature Deposition of an Optical Absorber Layer:
An optical absorber layer (OAL), which may be an amorphous carbon layer (ACL), is deposited using the toroidal plasma source low temperature CVD process described above. The process gas that is introduced into the chamber is a carbon-precursor gas if the OAL is an ACL. We have discovered that absorption in the amorphous carbon material at the wavelength of interest (e.g., 810 nm) can be enhanced by adding impurity materials to the carbon. One example of such an impurity material that renders amorphous carbon opaque at 810 nm is boron. In such a case, the process gas consists of a carbon precursor gas such as propylene (for example) and a boron precursor gas (such as B2H6) and a diluent gas for the B2H6, such as hydrogen. Although helium could be used as the diluent gas, we have found that optical qualities of the amorphous carbon layer are enhanced best in the presence of hydrogen.
The absorption-enhancing step of block 216 may consist of heating the wafer very briefly (for a matter of seconds or fraction of a minute) to a moderately hot temperature (e.g., 450 degrees C.) (block 216a). This heating step, which may be carried out in a separate reactor after deposition of the OAL, may increase the optical k value (extinction coefficient) from about 0.3 to 0.36 in some process examples. The OAL may be deposited to a thickness between about 0.25 micron and about 1 micron. Upon completion of the OAL deposition process of block 210, the dynamic surface annealing (DSA) process is performed (block 230 of
The optical absorption-enhancing species may be put into the OAL by post-CVD ion implantation step, as distinguished from the step of block 216 in which they are put into the OAL during the CVD deposition process by including them in the process gas. In such a case, the process of
The extinction coefficient or imaginary part of the index of refraction may be ramped without resorting to ion implantation of the absorption-enhancing species. For example, the concentration depth profile of the absorber-enhancing species added to the OAL during the CVD deposition step may be ramped. This is done by modifying the process of
The process of
An OAL including an anti-reflection section formed by any of the foregoing steps is depicted in
While the foregoing examples concern an OAL in which the optical absorption is maximized, the low-temperature CVD process described above may be used to form an OAL or amorphous carbon layer having low optical absorption at the wavelength of the light source. This may be accomplished, for example, by refraining from including or adding boron or other absorption-enhancing impurities in the OAL. In the case of a pure amorphous carbon OAL, the low-temperature CVD process forms a relatively transparent layer at the wavelength (810 nm) of the GaAs diode laser array 32 of
The pre-implant wafer cleaning reactor 360 may be a conventional cleaning reactor, but may be another toroidal source plasma reactor of the type illustrated in
The following is a partial list of carbon precursors for the optical absorber layer deposition:
Other precursors such as fluorocarbons may be used but tend to have poorer absorption (i.e., extinction coefficient or imaginary part of the complex refractive index) at the wavelength of radiation of the laser light beam as compared with hydrocarbons. Fluorocarbons may therefore be useful where it is desired to deposit a layer, or a portion of a layer, that is more transparent or less absorbing/opaque. Preferred fluorocarbon gases are C4F6 or C3F6. Other fluorocarbon gases include C2F4, C2F6, C3F8, C4F8 and C5F8. Impurity examples to further enhance optical properties are B2H6, BF3, B5H9, PH3, PF3, AsH3, AsF5, SiH4, SiF4, GeH4, GeF4, with the hydrides generally providing better absorption than the dopant-fluorides. In one example, on a 300 mm silicon wafer, C3H6 is used as a C-precursor gas at a flow rate of 600 sccm, with B-precursor B2H6 at a flow rate of 20 sccm, H2 at 180 sccm, and dilution gas Ar 200 sccm at a process chamber pressure of 15 mtorr. RF toroidal source power of 2 KW (at frequency of approximately 12-14 MHz) for each of two reentrant tubes in a crossed-toroidal configuration is applied. RF bias voltage (at frequency of 1-3 MHz) is ramped up to 7 KV peak-to-peak from zero after several seconds, requiring about 8 KW RF bias power. The electrostatic wafer chuck is maintained in a range −20 to +40 C, and the wafer temperature is about 80 degrees to 140 degrees C.). For a 1-minute process time, film thickness is about 0.25 micron and “k” value is about 0.36 at laser wavelength of about 800 nm. Film thickness is linear with deposition time, yielding about 0.75 micron in 3 minutes. B-precursor B2H6 (max 10-20%) is commonly available diluted with H2, He, Ar or N2, as its high reactivity precludes availability at 100%. While the H2 or He dilution is most preferred, Ar or N2 dilution may also be used. Other boron precursors may also be used. Without boron, the above example conditions yield a film with a “k” value of about 0.18 at laser wavelength of about 800 nm. N2 may be added instead of boron: With N2 and without boron, the above example conditions yield a film with a “k” value of about 0.25 at laser wavelength of about 800 nm. If lower “k” value films are desired for some other applications, H2 may be added. With 200-400 sccm added H2 and without boron or N2, the above example conditions yield a film with a “k” value of about 0.04 at laser wavelength of about 800 nm. Alternatively or additionally, fluorine-containing gas may be added to yield a low “k” film.
Amorphous carbon films may be deposited with control of the “k” value (absorption or extinction coefficient or imaginary part of the complex refractive index) over a wide range, while providing good step coverage over topography, free of voids, and control of film stress to improve thermal properties and avoid cracking or peeling, even when subjected to laser annealing or conventional annealing. Chuck or wafer temperature may be lower to increase deposition rate without sacrificing “k” value or other film properties. Curing at 450 C for several seconds increases “k” value to about 0.36. The layer allows efficient absorption of the laser, allowing the doped-silicon to be activated while the integrity of the absorber layer is maintained. The wafer surface may be taken to the melting temperature without failure of the absorber layer. Then after anneal, the absorber layer may be stripped and cleaned in a conventional manner (as photoresist strip/clean process). Alternatively, the strip process may also be carried out back in the same or a different plasma chamber having the above-described toroidal plasma source, using oxygen or oxygen/nitrogen mixtures.
The deposition process may be multi-step (as discussed above with reference to
Copper Annealing:
The invention may be employed to solve problems in copper conductor deposition in high aspect ratio openings. Such problems include poor vertical sidewall coverage within the high aspect ratio opening.
A first problem can arise in the deposition of the TaN/Ta barrier layer prior to copper deposition, in which the barrier layer coverage inside the high aspect ratio opening sidewall is uneven. The top corner edge of the metal (Ta) portion of the barrier layer is susceptible to being sputtered during its plasma deposition, taking material away from the top corner edge and depositing it on a facing surface of the sidewall, forming a neck protrusion on the sidewall which can restrict deposition below the neck protrusion in the bottom of the opening to very thin coverage. This first problem is solved by annealing the metal (Ta) portion of the barrier layer using the dynamic surface anneal (DSA) laser light source of
A second problem, similar to the first problem, arises during deposition of the copper seed layer over the barrier layer in the high aspect ratio opening, in which the copper seed layer coverage inside the high aspect ratio opening sidewall is uneven. The top corner edge of the copper seed layer is susceptible to being sputtered during its plasma deposition, taking copper material away from the top corner edge and depositing it on a facing surface of the sidewall, forming a copper neck protrusion on the sidewall which can restrict copper deposition below the neck protrusion in the bottom of the opening to very thin coverage. This second problem is solved by annealing the copper seed layer using the dynamic surface anneal (DSA) laser light source of
A third problem is that the electroplated copper conductor layer that fills the remainder of the high aspect ratio opening tends to have an extremely wide variation in copper crystal grain size throughout its bulk, which can grain sizes as small as 5 nm and as large as 200 nm. Such a large variation in grain size within the copper conductor layer gives rise to a number of problems including agglomeration of voids and additives collecting at grain boundaries. Such problems can cause copper electromigration during current flow through the copper conductor, which tends to break down the copper conductor. This problem is solved by annealing the electroplated copper conductor layer using an amorphous carbon absorber layer deposited by the toroidal source CVD process including features described above with reference to
In an alternative embodiment, the optical anneal step of block 410 includes a preliminary step of first depositing an amorphous carbon-containing optical absorber layer. For this purpose, an amorphous carbon absorber layer is first deposited over the Ta metal layer 406. This is accomplished by carrying out the toroidal source chemical vapor deposition process of
The next step (block 412 of
In an alternative embodiment, the optical anneal step of block 418 includes a preliminary step of first depositing an amorphous carbon-containing optical absorber layer. For this purpose, an amorphous carbon absorber layer is first deposited over the copper seed layer 414. This is accomplished by carrying out the toroidal source chemical vapor deposition process of
In using the DSA laser light source of
The next step in the process for forming a copper conductor is illustrated in
A plurality (e.g., 14) parallel laser bars 134 each consisting of plural (e.g., 49) laser emitter arranged linearly (
Following the optical annealing of the copper layer 422, the amorphous carbon optical absorber layer 426 is stripped (block 430 of
Referring to
Laser-Writable Carbon Mask:
Features for controlling the optical characteristic of the amorphous carbon layer have been described earlier in this specification with reference to
An optical pattern is written into the carbon layer using, for example, a laser beam (block 446 of
A laser-writable amorphous carbon mask may be employed to define selective exposure of different regions of a thin film structure or semiconductor layer to light in an optical annealing process such as rapid thermal processing anneal. This facilitates selective annealing in which only selected areas of a semiconductor wafer or thin film layer are annealed at a particular time. The first step (block 460 of
Amorphous Carbon Hardmask for Trench or Gate Etch:
The toroidal plasma CVD processes of
A similar process illustrated in
While the invention has been described in detail by specific reference to preferred embodiments, it is understood that variations and modifications thereof may be made without departing from the true spirit and scope of the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2344138 | Drummond | Mar 1944 | A |
| 3109100 | Gecewicz | Oct 1963 | A |
| 3576685 | Swann et al. | Apr 1971 | A |
| 3907616 | Wiemer | Sep 1975 | A |
| 4116791 | Zega | Sep 1978 | A |
| 4382099 | Legge et al. | May 1983 | A |
| 4385946 | Finegan et al. | May 1983 | A |
| 4434036 | Hoerschelmann et al. | Feb 1984 | A |
| 4465529 | Arima et al. | Aug 1984 | A |
| 4481229 | Suzuki et al. | Nov 1984 | A |
| 4500563 | Ellenberger et al. | Feb 1985 | A |
| 4521441 | Flowers | Jun 1985 | A |
| 4539217 | Farley | Sep 1985 | A |
| 4565588 | Seki et al. | Jan 1986 | A |
| 4584026 | Wu et al. | Apr 1986 | A |
| 4698104 | Barker et al. | Oct 1987 | A |
| 4764394 | Conrad | Aug 1988 | A |
| 4778561 | Ghanbari | Oct 1988 | A |
| 4867859 | Harada et al. | Sep 1989 | A |
| 4871421 | Ogle et al. | Oct 1989 | A |
| 4892753 | Weng et al. | Jan 1990 | A |
| 4912065 | Mizuno et al. | Mar 1990 | A |
| 4937205 | Nakayama et al. | Jun 1990 | A |
| 4948458 | Ogle | Aug 1990 | A |
| 5040046 | Chhabra et al. | Aug 1991 | A |
| 5061838 | Lane et al. | Oct 1991 | A |
| 5074456 | Degner et al. | Dec 1991 | A |
| 5106827 | Borden et al. | Apr 1992 | A |
| 5107201 | Ogle | Apr 1992 | A |
| 5270250 | Murai et al. | Dec 1993 | A |
| 5277751 | Ogle | Jan 1994 | A |
| 5288650 | Sandow | Feb 1994 | A |
| 5290382 | Zarowin et al. | Mar 1994 | A |
| 5290731 | Sugano et al. | Mar 1994 | A |
| 5312778 | Collins et al. | May 1994 | A |
| 5354381 | Sheng | Oct 1994 | A |
| 5423945 | Marks et al. | Jun 1995 | A |
| 5435881 | Ogle | Jul 1995 | A |
| 5505780 | Dalvie et al. | Apr 1996 | A |
| 5510011 | Okamura et al. | Apr 1996 | A |
| 5514603 | Sato | May 1996 | A |
| 5520209 | Goins et al. | May 1996 | A |
| 5542559 | Kawakami et al. | Aug 1996 | A |
| 5561072 | Saito | Oct 1996 | A |
| 5569363 | Bayer et al. | Oct 1996 | A |
| 5572038 | Sheng et al. | Nov 1996 | A |
| 5587038 | Cecchi et al. | Dec 1996 | A |
| 5627435 | Jansen et al. | May 1997 | A |
| 5643838 | Dean et al. | Jul 1997 | A |
| 5646050 | Li et al. | Jul 1997 | A |
| 5648701 | Hooke et al. | Jul 1997 | A |
| 5653811 | Chan | Aug 1997 | A |
| 5654043 | Shao et al. | Aug 1997 | A |
| 5660895 | Lee et al. | Aug 1997 | A |
| 5665640 | Foster et al. | Sep 1997 | A |
| 5674321 | Pu et al. | Oct 1997 | A |
| 5683517 | Shan | Nov 1997 | A |
| 5711812 | Chapek et al. | Jan 1998 | A |
| 5718798 | Deregibus | Feb 1998 | A |
| 5723367 | Wada et al. | Mar 1998 | A |
| 5770982 | Moore | Jun 1998 | A |
| 5888413 | Okumura et al. | Mar 1999 | A |
| 5897752 | Hong et al. | Apr 1999 | A |
| 5911832 | Denholm et al. | Jun 1999 | A |
| 5935077 | Ogle | Aug 1999 | A |
| 5944942 | Ogle | Aug 1999 | A |
| 5948168 | Shan et al. | Sep 1999 | A |
| 5985742 | Henley et al. | Nov 1999 | A |
| 5994207 | Henley et al. | Nov 1999 | A |
| 5994236 | Ogle | Nov 1999 | A |
| 5998933 | Shun'Ko | Dec 1999 | A |
| 6000360 | Koshimuzu | Dec 1999 | A |
| 6013567 | Henley et al. | Jan 2000 | A |
| 6020592 | Liebert et al. | Feb 2000 | A |
| 6041735 | Murzin et al. | Mar 2000 | A |
| 6050218 | Chen et al. | Apr 2000 | A |
| 6076483 | Shintani et al. | Jun 2000 | A |
| 6096661 | Ngo et al. | Aug 2000 | A |
| 6101971 | Denholm et al. | Aug 2000 | A |
| 6103599 | Henley et al. | Aug 2000 | A |
| 6103624 | Nogami et al. | Aug 2000 | A |
| 6132552 | Donohoe et al. | Oct 2000 | A |
| 6139697 | Chen et al. | Oct 2000 | A |
| 6150628 | Smith et al. | Nov 2000 | A |
| 6153524 | Henley et al. | Nov 2000 | A |
| 6155090 | Rubenson | Dec 2000 | A |
| 6164241 | Chen et al. | Dec 2000 | A |
| 6165376 | Miyake et al. | Dec 2000 | A |
| 6174450 | Patrick et al. | Jan 2001 | B1 |
| 6174743 | Pangrle et al. | Jan 2001 | B1 |
| 6182604 | Goeckner et al. | Feb 2001 | B1 |
| 6187110 | Henley et al. | Feb 2001 | B1 |
| 6207005 | Henley et al. | Mar 2001 | B1 |
| 6237527 | Kellerman et al. | May 2001 | B1 |
| 6239553 | Barnes et al. | May 2001 | B1 |
| 6248642 | Donlan et al. | Jun 2001 | B1 |
| 6265328 | Henley et al. | Jul 2001 | B1 |
| 6291313 | Henley et al. | Sep 2001 | B1 |
| 6291939 | Dolan et al. | Sep 2001 | B1 |
| 6300643 | Fang et al. | Oct 2001 | B1 |
| 6303519 | Hsiao et al. | Oct 2001 | B1 |
| 6305316 | DiVergilio et al. | Oct 2001 | B1 |
| 6335536 | Goeckner et al. | Jan 2002 | B1 |
| 6339297 | Sugai et al. | Jan 2002 | B1 |
| 6341574 | Bailey, III et al. | Jan 2002 | B1 |
| 6348126 | Hanwa et al. | Feb 2002 | B1 |
| 6350697 | Richardson et al. | Feb 2002 | B1 |
| 6392351 | Shun'Ko | May 2002 | B1 |
| 6395150 | Can Cleemput et al. | May 2002 | B1 |
| 6403453 | Ono et al. | Jun 2002 | B1 |
| 6410449 | Hanawa et al. | Jun 2002 | B1 |
| 6413321 | Kim et al. | Jul 2002 | B1 |
| 6417078 | Dolan et al. | Jul 2002 | B1 |
| 6418874 | Cox et al. | Jul 2002 | B1 |
| 6426015 | Xia et al. | Jul 2002 | B1 |
| 6433553 | Goeckner et al. | Aug 2002 | B1 |
| 6453842 | Hanawa et al. | Sep 2002 | B1 |
| 6461972 | Kabansky | Oct 2002 | B1 |
| 6468388 | Hanawa et al. | Oct 2002 | B1 |
| 6475888 | Sohn | Nov 2002 | B1 |
| 6494986 | Hanawa et al. | Dec 2002 | B1 |
| 6511899 | Henley et al. | Jan 2003 | B1 |
| 6513538 | Chung et al. | Feb 2003 | B2 |
| 6514838 | Chan | Feb 2003 | B2 |
| 6528391 | Henley et al. | Mar 2003 | B1 |
| 6551446 | Hanwa et al. | Apr 2003 | B1 |
| 6559408 | Smith et al. | May 2003 | B2 |
| 6579805 | Bar-Gadda | Jun 2003 | B1 |
| 6582999 | Henley et al. | Jun 2003 | B2 |
| 6593173 | Anc et al. | Jul 2003 | B1 |
| 6664187 | Ngo et al. | Dec 2003 | B1 |
| 6679981 | Pan et al. | Jan 2004 | B1 |
| 6800559 | Bar-Gadda | Oct 2004 | B2 |
| 6811448 | Paton et al. | Nov 2004 | B1 |
| 6838695 | Doris et al. | Jan 2005 | B2 |
| 6841341 | Fairbairn et al. | Jan 2005 | B2 |
| 7097779 | Mosden et al. | Aug 2006 | B2 |
| 7109087 | Autryve et al. | Sep 2006 | B2 |
| 7115993 | Wetzel et al. | Oct 2006 | B2 |
| 20010042827 | Fang et al. | Nov 2001 | A1 |
| 20020047543 | Sugai et al. | Apr 2002 | A1 |
| 20030013260 | Gossman et al. | Jan 2003 | A1 |
| 20030013314 | Ying et al. | Jan 2003 | A1 |
| 20030085205 | Lai et al. | May 2003 | A1 |
| 20030186524 | Ryo | Oct 2003 | A1 |
| 20030196996 | Jennings et al. | Oct 2003 | A1 |
| 20040104481 | Ong | Jun 2004 | A1 |
| 20040200417 | Hanawa et al. | Oct 2004 | A1 |
| 20040229050 | Li et al. | Nov 2004 | A1 |
| 20040253839 | Shimizu et al. | Dec 2004 | A1 |
| 20050074956 | Autryve et al. | Apr 2005 | A1 |
| 20050167394 | Liu et al. | Aug 2005 | A1 |
| 20060019039 | Hanawa et al. | Jan 2006 | A1 |
| 20060019477 | Hanawa et al. | Jan 2006 | A1 |
| 20060234458 | Jennings et al. | Oct 2006 | A1 |
| Number | Date | Country |
|---|---|---|
| 0 546 852 | Jun 1993 | EP |
| 0 836 218 | Apr 1998 | EP |
| 0 964 074 | Dec 1999 | EP |
| 1 111 084 | Jun 2001 | EP |
| 1 158 071 | Nov 2001 | EP |
| 1154468 | Nov 2001 | EP |
| 1 191 121 | Mar 2002 | EP |
| 59-86214 | May 1984 | JP |
| 59-218728 | Dec 1984 | JP |
| 62-120041 | Jun 1987 | JP |
| 070455542 | Feb 1995 | JP |
| 63172158 | Jul 1998 | JP |
| 2000150908 | May 2000 | JP |
| WO 9900832 | Jan 1999 | WO |
| WO 0111650 | Feb 2001 | WO |
| WO 0173769 | Oct 2001 | WO |
| WO 0225694 | Mar 2002 | WO |
| WO 9318201 | Sep 2003 | WO |
| WO 03090257 | Oct 2003 | WO |
| WO 2004008520 | Jan 2004 | WO |
| WO 2005024922 | Mar 2005 | WO |
| WO 2005036627 | Apr 2005 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070032095 A1 | Feb 2007 | US |