Patent Application
20240141519
The disclosure relates generally to stabilization and activation of device surfaces during water splitting and other reactions, as well as during other types of device operation.
Photoelectrochemical (PEC) water splitting mimics plants to generate sustainable clean fuels using two most abundant resources on the earth—sunlight and water. One prevailing scheme to artificially attain this solar to chemical energy conversion is to monolithically integrate a semiconductor material with electrocatalysts in a photoelectrode. In this approach, the semiconductor efficiently harvests the solar energy, while the electrocatalyst, which sometimes also acts as a protection layer, lowers the overpotential, mediates the charge carrier transfer, and provides active sites for the chemical reaction at solid/liquid interface.
Unfortunately, efficient photo-absorbers are not durable (e.g., Si, III-V), whereas durable materials show poor efficiency (e.g., TiO2, SrTiO3). For instance, both Si and III-V compound semiconductors suffer from poor stability due to chemical and photochemical corrosion. Compared to photovoltaic electrolyser (PV-EL) devices, the light absorber of PEC devices is often in direct contact with electrolyte, leading to more rapid degradation. The corrosion of semiconductors is influenced by many factors, including intensity of light illumination, biasing conditions, catalyst, surface passivation, semiconductor electronic band structure, electrolyte composition, and the interfaces of semiconductor/electrolyte as well as catalyst/electrolyte. These factors can be potentially addressed by exploring thermodynamic and kinetic protection schemes.
Recent efforts have been directed to providing a stable coating to yield stable photoelectrodes. These coatings are usually a combination of a charge transport layer combined with a catalyst, thus promoting efficient charge collection and separation and preventing corrosion. Different oxides, nitrides, selenides, and sulfides materials have been explored for protection of Si-based photocathodes in the presence of catalysts for the hydrogen evolution reaction (HER). Among these, gallium nitride (GaN) is an interesting option due to the chemical stable nature of N-rich surfaces. GaN is suitable as an efficient protective layer for silicon photocathodes, due to the almost ideal band alignment of the two materials for providing optimal electron transport.
Other protection schemes have been developed to enhance the stability of photoelectrodes. Kinetic protection for a given photoelectrode is possible by using a synergetic combination of a stable surface protection layer and a highly active co-catalyst. To further improve device stability, other photoelectrodes have employed relatively thick metal oxides, such as TiO2, Al2O3, and IrOx, as passivation layers, in addition to the use of suitable co-catalysts. Although the stability of these devices has improved, one major issue is the loss of photocurrent, due to poor charge transfer and, in some cases, undesired light absorption by the protection layers.
In accordance with one aspect of the disclosure, a method of fabricating a device includes providing a substrate of the device, forming a structure of the device, the structure being supported by the substrate, having a semiconductor composition, and including a surface, where nitrogen is present at the surface, and incorporating oxygen into the surface to form a stabilizing layer on the surface. Incorporating the oxygen is implemented such that the stabilizing layer includes a uniform distribution of an oxynitride material.
In accordance with another aspect of the disclosure, a device includes a substrate, a structure having a semiconductor composition, the structure being supported by the substrate, the structure including a surface, where nitrogen is present at the surface, and a stabilizing layer disposed on the surface of the structure. The stabilizing layer includes a uniform distribution of an oxynitride material.
In accordance with another aspect of the disclosure, a device includes a substrate, a structure having a semiconductor composition, the structure being supported by the substrate, the structure including a surface, and a stabilizing layer disposed on the surface of the structure, the stabilizing layer including an oxynitride material. The oxynitride material of the stabilizing layer is continuously distributed across the surface of the structure.
In accordance with another aspect of the disclosure, a device includes a substrate, a structure having a semiconductor composition, the structure being supported by the substrate, the structure including a non-polar sidewall surface; a passivation structure disposed along the non-polar sidewall surface of the structure, and a stabilizing layer disposed between the structure and the passivation structure, the stabilizing layer including an oxynitride material.
In accordance with another aspect of the disclosure, a method of fabricating a device includes providing a substrate of the device, forming a structure of the device, the structure being supported by the substrate, having a semiconductor composition, and including a surface, forming a stabilizing layer on the surface, the stabilizing layer including an oxynitride material, and depositing an insulating structure adjacent to the structure such that the stabilizing layer is disposed between the surface of the structure and the insulating structure.
In connection with any one of the aforementioned aspects, the methods, devices, and/or systems described herein may alternatively or additionally include or involve any combination of one or more of the following aspects or features. The stabilizing layer is configured as an activation layer. The stabilizing layer is configured as a passivation layer. Incorporating the oxygen includes implementing an oxidation reaction to form the stabilizing layer. Incorporating the oxygen includes implementing an electrochemical procedure. The electrochemical procedure is implemented for a period of time on the order of minutes. The electrochemical procedure includes implementing a water splitting reaction in which the device is immersed in water. Incorporating the oxygen includes annealing the surface. Incorporating the oxygen includes depositing an oxygen-containing material on the surface. The oxygen-containing material includes an oxide. The oxide is aluminum oxide. The oxide is hafnium oxide. Incorporating the oxygen includes treating the surface before depositing the oxygen-containing material. Incorporating the oxygen further includes annealing the surface after depositing the oxygen-containing material. The oxygen-containing material includes a ferroelectric material. Forming the structure includes forming an array of conductive projections supported by the substrate and extending outwardly from the substrate, the array of conductive projections including the structure. Forming the array of conductive projections includes implementing a molecular beam epitaxy (MBE) growth procedure such that each conductive projection of the array of conductive projections includes a respective nanowire. The MBE growth procedure is implemented under nitrogen-rich conditions such that sidewalls of each conductive projection of the array of conductive projections are nitrogen-terminated. The substrate includes silicon. The semiconductor composition of the structure includes gallium nitride such that the oxynitride material is GaOxN1-x. The stabilizing layer has a thickness falling in a range from about one monolayer to a few monolayers. The surface is oriented along a non-polar plane of the semiconductor composition. The surface is oriented along a polar plane of the semiconductor composition. The semiconductor composition is configured such that implementing the oxidation reaction results in partial oxygen substitution of the nitrogen. The semiconductor composition has a Wurtzite crystal structure. The nitrogen of the surface is disposed in a compound semiconductor arrangement of the semiconductor composition. The stabilizing layer is configured as a passivation layer. The structure is configured as a transistor channel. The device further includes a gate oxide layer. The stabilizing layer is disposed between the transistor channel and the gate oxide layer to stabilize an interface between the transistor channel and the gate oxide layer. The transistor channel includes gallium nitride. The gate oxide layer includes aluminum oxide. The gate layer includes hafnium oxide. The structure includes a stack of semiconductor layers configured for light emission. The device further includes a metal contact layer adjacent the stack of semiconductor layers, wherein the stabilizing layer is disposed along an interface between the metal contact layer and the stack of semiconductor layers. The stack of semiconductor layers includes an active layer. The stabilizing layer is disposed along a sidewall of the active layer. The stabilizing layer is configured as an activation layer. The stabilizing layer is configured to define catalytic sites along the surface of the structure. The surface is oriented along a non-polar plane of the semiconductor composition. The surface is oriented along a polar plane of the semiconductor composition. The stabilizing layer is configured with partial oxygen substitution of the nitrogen. The semiconductor composition has a Wurtzite crystal structure. The nitrogen of the surface is disposed in a compound semiconductor arrangement of the semiconductor composition. The surface includes a sidewall. The stabilizing layer is disposed along the sidewall. The stabilizing layer has a thickness falling in a range from a sub-nanometer thickness to a thickness of a few nanometers. The substrate includes silicon. The semiconductor composition of the structure includes gallium nitride such that the oxynitride material is GaOxN1-x. The surface is free of catalyst nanoparticles. The device further includes an array of conductive projections supported by the substrate and extending outwardly from the substrate. The array of conductive projections includes the structure. Each conductive projection of the array of conductive projections has a surface protected by an oxynitride layer. An electrochemical system including a working electrode configured in accordance with a device as described herein. The surface is a non-polar surface of the structure. The non-polar surface is oriented along an m-plane of a lattice of the structure. The non-polar surface is a sidewall of the structure. The device further includes a passivation cap disposed on a polar surface of the structure. The polar surface is oriented along a c-plane of a lattice of the structure. The passivation cap includes a nitride material or an oxide material. The device further includes a passivation structure that partially covers the non-polar surface. The passivation structure includes parylene. The passivation structure includes a nitride material or an oxide material. The structure is configured as a nanowire. The device further includes an electrode supported by the structure. The stabilizing layer is disposed between the structure and the electrode. The semiconductor composition includes nitrogen such that nitrogen is present at the surface. The semiconductor composition includes oxygen such that oxygen is present at the surface. The surface is a polar surface of the structure. The structure is configured as a transistor channel. The device further includes a gate oxide layer. The stabilizing layer is disposed between the transistor channel and the gate oxide layer to stabilize an interface between the transistor channel and the gate oxide layer. The surface is oriented along a c-plane of a lattice of the structure. The semiconductor composition includes nitrogen such that nitrogen is present at the surface. The semiconductor composition includes oxygen such that oxygen is present at the surface. The device further includes a passivation structure disposed along a sidewall of the structure, the sidewall being oriented along an m-plane of a lattice of the structure, and a further stabilizing layer between the passivation structure and the sidewall of the structure. The non-polar sidewall surface is an m-plane of a lattice of the structure. The passivation structure partially covers the non-polar sidewall surface. The stabilizing layer covers an entirety of the non-polar sidewall surface, and the passivation layer passivates an entirety of the non-polar sidewall surface. The surface is a non-polar surface of the structure. The surface is a polar surface of the structure. Depositing the insulating structure includes covering a c-plane surface of the structure. Depositing the insulating structure includes partially covering an m-plane surface of the structure. Depositing the insulating structure is implemented after forming the stabilizing layer. Forming the stabilizing layer includes depositing an oxygen-containing material on the surface, and treating the surface before depositing the oxygen-containing material. Forming the stabilizing layer further includes implementing an anneal to form the oxynitride material from oxygen of the oxygen-containing material. Forming the stabilizing layer includes depositing a nitrogen-containing material on the surface, and implementing an anneal to form the oxynitride material from nitrogen of the nitrogen-containing material.
For a more complete understanding of the disclosure, reference should be made to the following detailed description and accompanying drawing figures, in which like reference numerals identify like elements in the figures.
The embodiments of the disclosed devices, systems, and methods may assume various forms. Specific embodiments are illustrated in the drawing and hereafter described with the understanding that the disclosure is intended to be illustrative. The disclosure is not intended to limit the invention to the specific embodiments described and illustrated herein.
Photoelectrochemical, photocatalytic, electronic, and other systems and devices are described. In some cases, the disclosed systems and devices (e.g., photoelectrodes) may be configured for water splitting and other chemical reactions. Methods of fabricating the devices (e.g., photoelectrodes or photocatalytic devices) are also described. The photoelectrodes or other devices include a stabilizing layer (e.g., a stabilizing activation layer) disposed on one or more surfaces thereof.
The stabilizing layer includes an oxynitride material. As described herein, the disclosed methods include incorporating oxygen into a structure surface (e.g., oxidizing the structure surface) to form the oxynitride material (e.g., a continuous or other uniform distribution of the oxynitride material). For instance, an oxidation reaction configured to form the continuous or other uniform distribution of an oxynitride material may be implemented. In some cases, the uniformity of the oxynitride distribution may relate to the comprehensive formation of the oxynitride material at each nitrogen site at the surface. Alternative or additional ways in which the distribution is uniform are presented below.
The composition of the oxynitride material may vary. For instance, the ratio of nitrogen to oxygen may vary. Thus, in some cases, the oxygen composition, may vary (e.g., decrease) as the distance from the surface increases. The oxynitride material may have a varying oxygen concentration, such as OxN1-x For example, in devices having a GaN device structure, the oxynitride material may be or otherwise include GaOxN1-x. The stabilizing layer in such cases may accordingly include gallium oxynitride in combination with a very thin layer (e.g., 1 nm or less) of gallium and oxide (e.g., on top of the gallium oxynitride, and a region of Ga OxN1-x with the oxygen concentration decreasing as the distance from the surface increases. References to the oxynitride material of the stabilizing layer may thus include materials with varying levels of oxygen content. The oxygen content level may vary with a number of factors, including, for instance, surface orientation, surrounding environment (e.g., electrolyte, metal layer, passivation layer, etc.), and/or treatment conditions. In any case, the oxynitride material of the stabilizing layer provides surface stabilization and device performance enhancement, as described below. The oxynitride material may vary in alternative or additional ways. For instance, the nitrogen and oxygen may be disordered. In some cases, the positioning of the nitrogen and oxygen may be swapped or otherwise vary.
In some cases, the oxynitride layer is configured as an activation layer. For instance, the oxynitride layer may activate a device surface by establishing or otherwise defining catalytic sites along the device surface. Alternatively or additionally, the oxynitride layer may activate the device surface by establishing or otherwise defining sites along the device surface for efficient charge transfer. Resistance presented at an interface, such as a metal-semiconductor interface of a light emitting device, may thus be decreased. The activation aspect of the oxynitride layer may thus improve the efficiency or performance of the disclosed devices, as described in connection with a number of examples herein.
In addition to providing such activation functions, the stabilizing layer may provide protection or other stabilization of the device surface. A structure on which the stabilizing layer is disposed may thus be more durable. For instance, in electrochemical cases, the stabilizing layer may provide protection against corrosion or other degradation. Such protection or other stabilization is achieved without adverse effects on device performance. Indeed, to the contrary, the oxynitride layer unexpectedly improves device performance while providing such protection or other stabilization.
In some cases, the stabilizing layer is configured as a passivation layer rather than an activation layer. The stabilizing layer may be used to stabilize an interface between a device structure, such as a transistor channel, and an adjacent structure, such as a transistor gate oxide. The stabilizing layer may be disposed between such structures to stabilize an interface therebetween. In some cases, the stabilizing layer may reduce interfacial traps at an interface of an electronic device. Such reduction may be useful during operation of transistors and a wide variety of other electronic devices. The stabilizing layer may provide alternative or additional stabilization functions, including, for instance, rendering conventionally unstable interfaces (e.g., high dielectric constant interfaces, such as III-nitride interfaces) more chemically stable. Such increased stability may be useful in connection with a broad range of electronic devices, such as high electron mobility transistors (HEMTs), metal-oxide-semiconductor field-effect transistors (MOSFETs), fin field-effect transistors (FinFETs), and vertical transistors. Still further stabilization may be provided in connection with light emitting devices via a passivation layer configured to reduce current leakage and/or surface recombination.
The water splitting and other chemical reactions may be solar driven (e.g., solar water splitting). The disclosed devices, systems and methods may thus be considered to implement artificial photosynthesis in some cases. In some cases, the disclosed devices, systems and devices include an array of conductive projections, such as nanowires or other nanostructures. Each nanostructure or other conductive projection may establish a structure to support and otherwise provide catalysts for the water splitting or other chemical reaction. In other cases, the disclosed devices may be configured with other types of structures, including planar structures. For instance, the functionality of the devices may be provided instead by a number of planar structures supported by a substrate.
The disclosed methods, devices, and systems involve structures having a surface that includes nitrogen. For instance, in transistor cases, the structure may be a transistor channel composed of, or otherwise including, a compound semiconductor that establishes the nitrogen-based surface. In photoelectrode cases involving an array of nanostructures, each nanostructure may be composed of, or otherwise include, a compound semiconductor that establishes the nitrogen-based surface. Alternative or additional surface protection may be provided by the nitrogen-based aspect of the surface. For instance, the nanostructures may be composed of GaN in an arrangement in which the surface is nitrogen-terminated. Such nitrogen termination may support the protection or other stabilization of the structures. Alternatively or additionally, the disclosed photoelectrodes or other devices may have one or more surfaces on which a nitrogen or other nitrogen-based layer is disposed.
Although described in connection with nanowire arrays, the surface stabilization and activation schemes described herein may be applied to a variety of different device structures. Various planar catalytic surfaces may be modified to include nitrogen. For instance, a nitrogen layer (or other nitrogen-based layer) may be deposited or otherwise applied to a variety of different electrode surfaces.
Photoelectrochemical, photocatalytic, and other water splitting provided by the disclosed devices and systems may involve solar-to-hydrogen conversion. The disclosed devices and systems provide improvements in the efficiency of photoelectrochemical water splitting and/or other water splitting (e.g., photocatalytic water splitting). The disclosed devices and systems may include one or more other aspects directed to efficiency improvements. For instance, the structures may include a double junction configuration, such as in multi-band InGaN nanowire arrays configured to provide a second junction.
Although described in connection with photoelectrochemical water splitting, the disclosed devices and systems may be used in other chemical reaction contexts and applications. For instance, the disclosed devices and systems may be useful in connection with various types of photocatalytic and/or other systems, and/or in connection with other reactions, including, for instance, nitrogen reduction to ammonia, CO2 reduction to various fuels and other chemicals, and activation of C—H bonds for the production of various chemicals.
Although described herein in connection with electrodes having GaN-based nanowire arrays for water splitting, the disclosed devices and systems are not limited to GaN-based nanowire arrays. A wide variety of other types of nanostructures and other conductive projections may be used. In some cases, the electrodes of the disclosed systems do not include an array of projections, and are instead planar devices. Thus, the nature, construction, configuration, characteristics, shape, and other aspects of electrodes through which the water splitting is implemented may vary.
The surface stabilization and activation of the disclosed methods and devices are also not limited to electrochemical or other chemical contexts. Although described herein in connection with a field effect transistor, the surface stabilization may be applied in various electronic contexts. For instance, the disclosed devices may be any type of photoelectronic, optoelectronic, or other electronic device. In such cases, the structures formed by the disclosed methods may be or include other various types of device structures, including, for instance, structures other than transistor structures. The manner in which the surfaces of such structures are protected or otherwise stabilized by the oxynitride material of the stabilizing layer of the disclosed methods and devices may vary accordingly.
The electrochemical system 100 includes one or more electrochemical cells 102. A single electrochemical cell 102 is shown for ease in illustration and description. The electrochemical cell 102 and other components of the electrochemical system 100 are depicted schematically in
In the example of
The hydrogen evolution occurs at the working electrode 108 as follows:
Hydrogen evolution: 2H++2e−H2
To that end, electrons may flow from the counter electrode 110 through a circuit path external to the electrochemical cell 102 to reach the working electrode 108. The working and counter electrodes 108, 110 may thus be considered a cathode and an anode, respectively.
In the example of
In some cases, no bias voltage is applied—e.g., in unassisted systems. In the example of
In this example, the working electrode 108 is configured as a photocathode. Light 118, such as solar radiation, may be incident upon the working electrode 108 as shown. The electrochemical cell 102 may thus be considered and configured as a photoelectrochemical cell. In such cases, illumination of the working electrode 108 may cause charge carriers to be generated in the working electrode 108. Electrons that reach the surface of the working electrode 108 may then be used in the hydrogen evolution. The photogenerated electrons may augment electrons provided via the current path. Alternatively or additionally, the electrons provided via the current path may recombine with the photogenerated holes at a backside or other contact. Further details regarding examples of photocathodes are provided below.
The working electrode 108 includes a substrate 120. The substrate 120 of the working electrode 108 may constitute a part of an architecture, a scaffolding, or other support structure, of the working electrode 108. The substrate 120 may be uniform or composite. For example, the substrate 120 may include any number of layers or other components. The substrate 120 thus may or may not be monolithic. The shape of the substrate 120 may also vary. For instance, the substrate 120 may or may not be planar or flat.
In the example of
In active or functional cases, the substrate 120 may include a light absorbing material. The light absorbing material is configured to generate charge carriers upon solar or other illumination. The light absorbing material has a bandgap such that incident light generates charge carriers (electron-hole pairs) within the substrate. Some or all of the substrate 120 may be configured for photogeneration of electron-hole pairs. To that end, the substrate 120 may include a semiconductor material. In some cases, the substrate 120 is composed of, or otherwise includes, silicon. For instance, the substrate 120 may be provided as a silicon wafer.
The silicon may be doped. In the example of
The substrate 120 of the working electrode 108 establishes a surface at which a number of structures are provided. Each structure may be disposed on, or otherwise supported by, the substrate 120. In this example, the structures are configured to provide a catalyst arrangement. In this case, the structures are configured to provide catalytic functionality. In such cases, the structures are free of catalyst nanoparticles. In other cases, the structures are configured as support structures, or scaffolding, for catalysts (e.g., catalyst nanoparticles) of the electrode 108. As described below, the structures may include an array of conductive projections extending outward from a surface of the substrate 120. In other cases, the structures are not configured as, or otherwise include, conductive projections. For instance, the structure(s) may include one or more planar structures, such as one or more layers supported by the substrate 120.
In the example of
Each nanostructure 126 and/or other structure supported by the substrate 120 has a semiconductor composition. In some cases, the semiconductor composition is or otherwise includes a semiconductor core 128. For instance, the core 128 may be composed of, or otherwise include, a Group III-V nitride semiconductor material, such as gallium nitride (GaN). Additional or alternative semiconductor materials may be used, including, for instance, indium gallium nitride (InGaN) and/or other Group III-V nitride semiconductor materials.
The core 128 of each nanowire or other nanostructure 126 may be or include a columnar, post-shaped, or other elongated structure that extends outward (e.g., upward) from the plane of the substrate 120. The semiconductor nanowires or other nanostructures 126 may be grown or formed as described in U.S. Pat. No. 8,563,395, the entire disclosure of which is hereby incorporated by reference. The nanostructures 126 may be referred to herein as nanowires with the understanding that the dimensions, size, shape, composition, and other characteristics of the nanostructures 126 or other conductive projections may vary.
The semiconductor composition of each nanostructure 126 may or may not be configured to facilitate the reaction(s) supported by the electrochemical system 100. In some cases, the semiconductor composition may be configured for photo-generation of charge carriers. Alternatively or additionally, the semiconductor composition may be configured to act as a catalyst for the reaction(s). The semiconductor composition may provide other functions, including, for instance, protection of the substrate 120. As mentioned above, the semiconductor composition may include GaN and/or InGaN. Further details regarding a number of examples involving GaN are provided below. Additional or alternative semiconductor materials may be used, including, for instance, indium nitride, aluminum nitride, boron nitride, aluminum oxide, silicon, and/or their alloys.
The semiconductor composition of each nanostructure 126 may be configured to provide or support surface passivation and/or other protection of the photoelectrode 108. As described herein, nitrogen is present at one or more surfaces 130 of each nanostructure 126. The surface 130 may thus be considered to include nitrogen. For instance, in some cases, the semiconductor composition is terminated with nitrogen. The nitrogen termination or other nitrogen-based aspect of the nanostructures 126 may protect the nanostructures 126 and/or other components of the electrode 108 (e.g., the substrate 120) during operation from, e.g., corrosion. Alternative or additional nitrogen-based protection schemes may be used in other cases. For instance, a layer including nitrogen may be deposited or otherwise disposed along the surface 130 of each nanostructure 126 and/or other element of the electrode 108. As described herein, the nitrogen may be present at the surface in various ways. In some cases, the nitrogen may be disposed below the surface (e.g., about 1 nm below), but sufficiently near the surface to be functionally active (e.g., chemically active for formation of an oxynitride layer). Accordingly, the terms “at”, “present” and “presence” are used herein to include various instances in which the nitrogen is functionally present at the surface, thereby including situations in which nitrogen atoms are disposed along or sufficiently near the surface to be functional for activity at the surface (e.g., chemically functional in connection with an oxidation reaction at the surface), rather than being limited to instances in which the nitrogen disposed is disposed only on the surface.
The nanostructures 126 may facilitate the hydrogen evolution and/or another chemical reaction in one or more ways. For instance, each nanostructure 126 may be configured to extract the charge carriers (e.g., electrons) generated in the substrate 120. The extraction brings the electrons to external sites along the surface 130 of the nanostructures 126 for use in the hydrogen evolution and/or other chemical reaction. The composition of the nanostructures 122 may also form an interface well-suited for hydrogen evolution and/or another chemical reaction, as explained below.
Each nanostructure 126 may be or include a columnar, post-shaped, or other elongated structure that extends outward (e.g., upward) from the plane of the substrate 120. The dimensions, size, shape, composition, and other characteristics of the nanostructures 126 may vary. For instance, each nanostructure 126 may or may not be elongated like a nanowire. Thus, other types of nanostructures from the substrate 120, such as various shaped nanocrystals, may be used.
In some cases, the nanostructures 126 are configured to generate electron-hole pairs upon illumination. For instance, the nanostructures 122 may be configured to absorb light at frequencies different than other light absorbing components of the electrode 108. For example, one light absorbing component, such as the substrate 120, may be configured for absorption in the visible or infrared wavelength ranges, while another component may be configured to absorb light at ultraviolet wavelengths. In other cases, the nanostructures 126 are the only light absorbing component of the electrode 108. In still other cases, the substrate 120 is the only light absorbing component of the electrode 108.
Each nanostructure 126 may include a layered or segmented arrangement of semiconductor materials. For instance, in Group III-nitride examples, the layers or segments of the arrangement may have differing Group III (e.g., indium and gallium) compositions. One or more layers or segments in the arrangement may be configured for absorption of a respective range of wavelengths. Other layers or segments may be directed to establishing a tunnel junction. Each nanostructure 126 may also include additional or alternative segments.
In other cases, the layered arrangement of semiconductor materials is also used to establish a multi-band structure, such as a quadruple band structure. Each layer or segment of the arrangement may have a different semiconductor composition to establish a different bandgap. The different bandgaps may be useful in connection with absorbing light of differing wavelengths. Further details regarding the formation and configuration of multi-band structures, including, for instance, triple-band structures, are provided in U.S. Pat. No. 9,112,085 (“High efficiency broadband semiconductor nanowire devices”) and U.S. Pat. No. 9,240,516 (“High efficiency broadband semiconductor nanowire devices”), the entire disclosures of which are incorporated by reference. Other layered or non-layered arrangements may be used in the semiconductor composition of the structure(s) of the disclosed devices.
The semiconductor composition of each nanowire 126 may be configured to improve the efficiency of the water splitting in additional ways. For instance, in some cases, the semiconductor composition of each nanowire 126 may include doping to promote charge carrier separation and extraction, as well as facilitate the establishment of a photochemical diode. For example, a dopant concentration of the semiconductor composition may vary laterally.
In examples involving III-nitride compositions, the dopant may be or include magnesium. Further details regarding the manner in which magnesium doping promotes charge carrier separation and extraction are set forth in U.S. Pat. No. 10,576,447 (“Methods and systems relating to photochemical water splitting”), the entire disclosure of which is incorporated by reference. Additional or alternative dopant materials may be used, including, for instance, silicon, carbon, and beryllium, depending on the semiconductor light absorber of choice.
In some cases, the working electrode 108 may further include catalyst nanoparticles disposed over the array of nanostructures 126. For instance, the nanoparticles may be distributed across or along the outer surface 130 (e.g., sidewalls) of each nanowire 126. In some cases, the nanoparticles are configured to facilitate or promote the proton reduction reaction. For instance, each nanoparticle 136 includes a metal, such as platinum. Other metals or materials may be used, including alloys, oxides, and/or other metal or metallic combinations. Further details regarding the formation, configuration, functionality, and other characteristics of nanoparticles in conjunction with a nanowire array are set forth in one or more of the above-referenced U.S. patents. Further details regarding the distribution of the nanoparticles are provided below in connection with a number of examples.
The electrode 108 also includes a stabilizing layer 132 disposed on the surface 130 of each nanostructure 126. In this case, the stabilizing layer 132 is configured to provide both stabilization and activation functionality for the electrode 108. The stabilizing layer 132 is thus configured as an activation layer or a stabilizing activation layer. The term “activation” is used to differentiate the activation layer from layers configured to act solely as a passivation or other protective layer, as well as other non-active layers. In this electrode example, the stabilization functionality may involve protection against corrosion and/or other passivation or protection. The activation functionality may involve defining or otherwise establishing catalytic sites along the surface 130 for the electrode 108. The nature of the stabilization and activation functionality may vary in other device contexts.
The stabilizing layer 132 may be composed of, or otherwise, include a uniform distribution of an oxynitride material. For instance, in cases in which the nanostructures 126 have a GaN core, the stabilizing layer 132 includes gallium oxynitride. The composition of the oxynitride layer may thus vary in accordance with the semiconductor composition of the nanostructure 126. Alternative or additional oxynitride materials may thus be used, including, for instance, aluminum oxynitride, indium oxynitride, strontium gallium oxynitride, zinc oxynitride, titanium oxynitride, chromium oxynitride, and silicon oxynitride.
The distribution of the oxynitride material may be uniform in various ways. For instance, the uniformity may establish, or otherwise relate to, a thickness of the stabilizing layer 132. Alternatively or additionally, the uniformity may establish, or otherwise relate to, a conformal nature of the stabilizing layer 132. Alternatively or additionally, the uniformity may relate to the consistency, regularity or smoothness of the surface of the stabilizing layer 132. For instance, the roughness of the surface may be decreased as a result of the uniform distribution of the oxynitride material. In some cases, the oxynitride material of the stabilizing layer 132 may be continuously distributed across the surface 130 (e.g., continuously cover the entirety of the surface 130).
Alternatively or additionally, the uniformity may relate to the presence of nitrogen atoms at the surface 130. For example, if the nitrogen atoms are randomly distributed on or otherwise at the surface, then the uniformity refers to the essentially universal or comprehensive (as opposed to local or restricted) formation of oxynitride sites around those nitrogen atoms. The phrase “uniform distribution” is thus used herein to include both continuous and discontinuous instances of the stabilizing layer 132. For instance, in some cases, adjacent nitrogen atoms may be spaced sufficiently apart so as to establish a discontinuity in the stabilizing layer 132. Thus, the stabilizing layer 132 (and accordingly the oxynitride material) may not be continuous at the surface 130 in some cases, but nonetheless still has a uniform distribution of oxynitride material in relation to the nitrogen sites at the surface 130. Alternatively or additionally, the surfaces 130 (or sections of a single surface 130) of the nanostructures 126 on which the stabilizing layer 132 is disposed may be spaced apart from one another, thereby establishing discrete sections of the stabilizing layer 132. As shown in these examples, the stabilizing layer 132 may be continuous or discontinuous, notwithstanding the uniform nature of the distribution of the oxynitride material.
The terms “presence” and “present at” are not limited to situations in which the nitrogen atoms, stabilizing layer, and/or oxynitride material are disposed on the surface. The terms are instead used to include situations in which the nitrogen atoms, the stabilizing layer, and/or the oxynitride material are below the surface, but still sufficiently near the surface to be functional for activity at the surface. The nitrogen atoms, the stabilizing layer, and/or the oxynitride material may thus be disposed slightly below the surface (e.g., about 1 nm below) in some cases, yet still sufficiently near the surface for purposes of formation of the oxynitride material and consequent stabilization of the surface.
The formation and/or presence of the oxynitride may be derived from the nitrogen at the surface 130. In some cases, the nitrogen of the surface 130 is disposed in a compound semiconductor arrangement of the semiconductor composition. For instance, in GaN and other examples, the semiconductor composition has a Wurtzite crystal structure. In some cases, a non-polar plane of the Wurtzite crystal structure may be nitrogen-terminated. The stabilizing layer 132 may be provided or otherwise configured with partial oxygen substitution of the nitrogen along the non-polar plane (and/or other planes in other cases). The surface(s) 130 may thus correspond with those surfaces of the nanostructures 126 that is/are oriented along a non-polar plane(s) of the semiconductor composition. In other cases (e.g., in transistor examples), the surface(s) 130 is/are oriented along a polar plane(s) of the semiconductor composition.
The semiconductor composition and/or the crystal orientation at the surface 130 of the nanostructure 126 may selectively determine where the stabilizing layer 132 is disposed on each nanostructure 126. Thus, the stabilizing layer 132 may or may not cover all of the surfaces of the nanostructure 126. In the example of
The stabilizing layer 132 may be sufficiently thin to avoid detrimental effects on charge transport or other activity along or otherwise at the surface 130. In some cases, the stabilizing layer 132 has a thickness of about 1 nm. In these and other cases, the stabilizing layer 132 may conformally cover the nanostructure 126, including any nanoparticles disposed thereon. The thickness may vary in other examples, including, for instance, thicknesses on the order of 1 nm (e.g., up to about 3 nm) or less than 1 nm. For example, the thickness may be one monolayer or on the order of one monolayer (e.g., a pair or a few monolayers). The thickness may thus vary from about 0.3 nm to about 3 nm. The thickness may not be exactly the same across the entirety of the stabilizing layer 132.
The thin nature of the stabilizing layer 132 allows the stabilization function to be provided without adversely affecting the transfer of charge carriers and other catalysis of the hydrogen evolution and/or other reaction occurring at the electrode 108. Further details regarding the functionality and other characteristics of the stabilizing layer 132 are provided below in connection with a number of examples.
In the example of
The nanostructures 126 and the stabilizing layer 132 are not shown to scale in the schematic depiction of
The nanowire arrangement may be fabricated on a substrate (e.g., a silicon substrate) via nanostructure-engineering. In one example, molecular beam epitaxial (MBE) growth of the nanowires is followed by photo-deposition of the nanoparticles. The photo-deposition of the nanoparticles may be configured to selectively deposit the nanoparticles on the respective sides of the nanowire. Further details regarding example fabrication procedures are provided below, e.g., in connection with
The nanostructures 126 may facilitate the water splitting in one or more ways. For instance, one or more aspects of each nanostructure 126 may be configured to extract charge carriers (e.g., electrons) generated in the substrate (e.g., as a result of light absorbed by the substrate 120). The extraction brings the charge carriers to external sites along the nanostructures 126 for use in the water splitting or other reactions. For instance, the nanostructures 126 may thus form an interface well-suited for evolution of hydrogen, the reduction of CO2, and/or other reactions.
The method 200 may begin with an act 202 in which a substrate is prepared or otherwise provided. The substrate may be or be formed from a silicon wafer. In one example, a 2-inch Si wafer was used, but other (e.g., larger) size wafers may be used. Other semiconductors and substrates may be used.
The substrate may have a planar or nonplanar surface. In some cases, the act 202 includes an act 204 in which a wet or other etch procedure is implemented to define the surface. For example, the etch procedure may be or include a crystallographic etch procedure. In silicon substrate examples, the crystallographic etch procedure may be a KOH etch procedure. In some cases, if the substrate has a <100> orientation, the wet etch procedure may establish that the surface includes a pyramidal textured surface with faces oriented along <111> planes. Other surface orientations and shapes may be used.
The act 202 may include fewer, additional, or alternative acts. For instance, in the example of
The act 202 may include still further acts. For instance, the act 202 may include one or more doping procedures to form doped regions or layers, and thereby establish a junction, as described herein. Alternatively, the substrate is provided at the outset with a desired dopant concentration profile.
The method 200 includes an act 210 in which a number of electrode or other device structures are grown or otherwise formed on the substrate. In some cases, a nanowire or other nanostructure array is grown or otherwise formed on the substrate. Each nanowire is formed on the surface of the substrate such that each nanowire extends outwardly from the surface of the substrate. Each nanostructure may have a semiconductor composition, as described herein. In some cases, the semiconductor composition is or otherwise includes a compound semiconductor material, such as a III-V semiconductor.
The nanostructure growth may be achieved in an act 212 in which a molecular beam epitaxy (MBE) procedure is implemented. The substrate may be rotated during the MBE procedure such that each nanostructure is shaped as a cylindrically shaped nanostructure. Each nanostructure may thus have a circular cross-sectional shape, as opposed to a plate-shaped or sheet-shaped nanostructure.
The MBE procedure may be implemented under nitrogen-rich conditions. The nitrogen-rich conditions may lead to nitrogen-terminated sidewalls and/or other surfaces, as described herein.
In some cases, the MBE procedure may be modified to fabricate the arrangement of layers or segments of each nanowire. Various parameters may be adjusted to achieve the different composition levels of the segments. For instance, the substrate temperature may be adjusted in an act 214. Beam equivalent pressures may alternatively or additionally be adjusted. In some cases, a dopant cell temperature is adjusted to control the doping (e.g., Mg doping) of the nanowires.
In one example, N-terminated thin GaN nanostructures were grown on Si for 30 minutes at a substrate temperature of about 735° C., with a Ga beam equivalent pressure (BEP) of about 2.2×10−7 torr, with a Ge cell (n-type dopant) temperature of about 1050° C., a nitrogen flow rate of 0.45 standard cubic centimeter per minute (sccm) and 350 W plasma power. The growth parameters may vary considerably in other cases.
In other cases (e.g., non-nanostructure cases), the act 210 may include forming other types of electrode or other device structures, such as one or more layers. The layer(s) may be configured to catalyze, participate in, or otherwise enable or facilitate the reaction. The layer(s) may accordingly be referred to as a reaction layer. For instance, the reaction layer(s) may be deposited on the substrate in an act 216. The layer(s) may establish a surface configured to catalyze or otherwise facilitate the water splitting and/or other reaction. The electrode layer(s) may be formed in alternative or additional ways, including, for instance, non-selective growth procedures.
One or more nitrogen-containing layers may be deposited or otherwise formed in an act 218. The nitrogen layer may be directed to protection of the reaction layer(s) and/or other aspects of the nanostructures. The nitrogen-containing layer(s) may alternatively or additionally be directed to supporting the formation of a stabilizing layer. In some cases, the act 218 may include implementing a reaction to form the nitrogen-containing layer(s) spontaneously. The layer(s) may be composed of, or otherwise include, a nitride or an oxynitride.
In some cases, the nitrogen-containing layer(s) may be formed on an electrode or other device structure that is planar (e.g., a structure that includes a number of planar layers or other planar components). The configuration of the planar structures may vary. Examples of planar structures are described in Cheng, et al., “Monolithic Photoelectrochemical Device for Direct Water Splitting with 19% Efficiency,” ACS Energ. Lett., 3, (8), 1795-1800 (2018), Young, et al., “Direct solar-to-hydrogen conversion via inverted metamorphic multi-junction semiconductor architectures,” Nat. Energ., 2, 17028 (2017), Khaselev et al., “A monolithic photovoltaic-photoelectrochemical device for hydrogen production via water splitting,” Sci., 280, (5362), 425-427 (1998), and Verlage et al., “A monolithically integrated, intrinsically safe, 10% efficient, solar-driven water-splitting system based on active, stable earth-abundant electrocatalysts in conjunction with tandem III-V light absorbers protected by amorphous TiO2 films,” Energ. Environ. Sci., 8, (11), 3166-3172 (2015), the entire disclosures of which are hereby incorporated by reference.
A wide variety of planar and other structures may be protected by the nitrogen-containing layer(s). For instance, the nitrogen-containing layer(s) may be deposited or otherwise formed on various surfaces not involving a c-plane surface or a nonpolar plane or surface.
In some cases, the act 218 may be integrated with, or implemented in conjunction with, the act 216, as described herein in conjunction with examples involving GaN or other nanostructures. In other cases involving GaN nanostructures, the acts 216 and 218 may be implemented separately.
The method 200 further includes an act 220 in which oxygen is incorporated into one or more surfaces of the nanostructures or other structures of the device to form a stabilizing layer on the one or more surfaces. In some cases, the surface(s) is/are oxidized. For instance, an oxidation reaction may be implemented to form the stabilizing layer. Alternatively or additionally, oxygen is deposited on the surface(s). The deposition may be followed by an annealing procedure in some cases to fully incorporate the oxygen atoms. The stabilizing layer may be configured as an activation layer or a passivation layer. The functionality of the stabilizing layer may vary with the nature of the device structure. As described herein, the oxidation of the surface(s) (or other incorporation of oxygen into the surface(s)) may be implemented such that the stabilizing layer is composed of, or otherwise includes, a uniform distribution of an oxynitride material. For instance, the oxidation reaction may be configured such that the stabilizing layer includes the uniform distribution. In some cases, the oxygen is incorporated into the surface such that the oxynitride material is continuously distributed across the surface (e.g., continuously covers the entirety of the surface).
In some cases, the oxynitride layer is formed in an act 222 in which an electrochemical procedure is implemented. The electrochemical procedure may be implemented for a period of time on the order of hours, e.g., about 5 to about 10 hours. The duration of the procedure may be sufficiently long to establish the uniform distribution of the oxynitride material. For instance, in other cases, the oxidation may be implemented for a period of time on the order of minutes. Further details are provided in connection with a number of examples below.
In some cases, the electrochemical procedure involves or otherwise includes the electrochemical reaction that the device is configured to implement. In such cases, the act 222 may be configured as an initialization step or procedure for the device. For instance, the device may be configured or directed to implementing a water splitting or other hydrogen evolution reaction. The electrochemical procedure may then include implementing the water splitting reaction in which the device is immersed in water. The hydrogen evolution reaction may be implemented for a predetermined period of time to form an oxynitride layer of a desired thickness. In other cases, the electrochemical procedure differs from the electrochemical reaction that the device is configured to implement. For instance, the electrochemical procedure may be or include a water splitting reaction, while the device is directed to implementing another reaction, such as CO2 reduction.
Alternatively or additionally, the act 220 includes exposing the surface to oxygen in an act 224. In some cases, the exposure to oxygen occurs in an oxygen-containing reaction chamber, such as a plasma asher. Alternatively or additionally, the exposure involves the ambient environment. The exposure may last for a predetermined period of time, e.g., for a period of time on the order of minutes or on the order of hours, but other time periods may be used. The duration of the exposure may be selected to produce an oxynitride layer of a desired thickness. The duration of the exposure may be otherwise selected to establish the uniform distribution of the oxynitride material.
The incorporation of oxygen in the act 220 may alternatively or additionally include an act 226 in which an oxygen-containing material is deposited on the surface(s). For example, the oxygen-containing material may be composed of, or otherwise include, an oxide material, such as aluminum oxide, hafnium oxide, or an oxygen-containing ferroelectric layer (e.g., HfZrO2), but other materials may be used.
The act 220 may include additional acts in combination with any one or more of the above-described techniques for exposing the surface to oxygen (or otherwise incorporating oxygen into the surface). In the example of
The act 220 may alternatively or additionally include an act 227 in which the implementation of an anneal procedure. In some cases, the anneal may be implemented in an oxygen environment to provide a source of the oxygen. Alternatively, the anneal may follow the deposition of the oxygen-containing layer in the act 226 or other provision of oxygen to the surface(s). The anneal may be configured to incorporate the oxygen into the surface (e.g., via substitution in the lattice of the structure, etc.). The temperature of the annealing procedure may vary. For instance, the temperature may fall in a range from about 100° C. to about 500° C., but other temperatures may be used. The time period of the anneal may vary accordingly. The temperature, duration, and/or other characteristics of the procedure may be selected to establish the uniform distribution of the oxynitride material. In some cases, the anneal procedure may not involve an oxygen environment, e.g., when the oxygen is made available in another way, such as via deposition (e.g., deposition of an oxide material).
The oxidation of the surface may be enabled, enhanced or otherwise possible due to one or more aspects of the surface. For instance, the surface may be oriented along a non-polar plane of the semiconductor composition. In other cases, the surface is oriented along a polar plane. Alternatively or additionally, the semiconductor composition may be configured such that the oxidation reaction results in partial oxygen substitution of the nitrogen. In such cases, the nitrogen of the surface may be disposed in a compound semiconductor arrangement of the semiconductor composition. The semiconductor composition may have a Wurtzite crystal structure.
The method 200 may include an act 228 in which catalyst nanoparticles are deposited across the array of nanowires. For instance, catalyst nanoparticles may be deposited in photoelectrochemical examples, and may not be deposited in other applications, such as transistors and other electronic devices. The deposition of the nanoparticles may be achieved via implementation of a photo-deposition procedure in an act 230. The nanoparticles may be composed of, or otherwise include, a metal, such as platinum, or other metallic material. A drying act 232 may then be implemented. Further details regarding the photo-deposition procedures are set forth in one or more of the above-referenced U.S. patents. Alternatively or additionally, the act 228 includes the implementation of an electro-deposition procedure.
The amount of catalyst nanoparticles deposited in the act 228 may be reduced as a result of the formation of the oxynitride layer. As described below, The presence of the oxynitride layer allows a similar beneficial impact to be achieved with a lower amount of catalyst nanoparticles.
In some cases, the act 228 is implemented after the formation of the stabilizing layer in the act 220. In other cases, the act 228 is implemented before the formation of the stabilizing layer. Depositing the nanoparticles before the formation of the stabilizing layer may be useful in promoting the formation of the oxynitride material.
In some cases, the method 200 includes an act 234 in which one or more other device structures are formed. For instance, the structures may involve an interface stabilized by the stabilizing layer of the disclosed methods and devices. In one example, a passivation layer is deposited or otherwise formed. The stabilizing layer may thus be disposed between the passivation layer and the structure surface to be stabilized. In another example, a contact is formed in the act 234. The stabilizing layer may be disposed between the contact and structure surface to reduce contact resistance. The act 234 may alternatively or additionally be directed to the formation of any number of additional or alternative device structures, including, for instance, a backside contact.
The method 200 may include one or more additional acts directed to forming the photocatalytic structures of the device. For instance, one or more acts may be implemented to deposit catalyst nanoparticles across the array of nanowires. The deposition of the nanoparticles may be achieved via implementation of a photo-deposition procedure. The nanoparticles may be composed of, or otherwise include, a metal, such as platinum, or other metallic material. A drying act may then be implemented. Further details regarding the photo-deposition procedures are set forth in one or more of the above-referenced U.S. patents. Still other acts may include a procedure in which the photocatalytic structures of the device are annealed. The parameters of the anneal process may vary.
The device 300 includes a substrate 302, and a transistor body 304 supported by the substrate 302. In this example, the transistor body 304 is a region (e.g., a doped region) of the device 300. Alternatively or additionally, the transistor body 304 is a structure formed or otherwise disposed on the substrate 302. The transistor body 304 may thus be integrated with the substrate 302 to any desired extent. The manner in which the transistor body 304 is supported by the substrate 302 may vary accordingly.
The transistor body 304 includes a channel 306 or channel region having a semiconductor composition. The channel 306 may extend between source and drain regions of the device 300 as shown. The channel 306 may be formed during operation when a voltage G is applied to a gate 308 of the device 300. In some cases, the channel 306 is doped and/or otherwise configured differently relative to the remainder of the transistor body 304. The gate 308 is spaced from the channel 306 by a gate oxide layer 310. In some cases, the gate oxide layer 310 includes aluminum oxide, but additional or alternative oxide materials may be used, including, for instance, hafnium oxide, zirconium dioxide, strontium oxide, scandium oxide, lithium oxide, titanium oxide, tantalum oxide, tungsten oxide, and silicon oxide.
The channel 306 may be composed of, or otherwise include, additional or alternative semiconductor materials, including, for instance, AlGaN, GaN, InN, AlN, BN, and their alloys. The remainder of the transistor body 304 may or may not be composed of, or otherwise include, the same semiconductor material.
The device 300 includes a stabilizing layer 312 on a surface 314 of the channel 306. As described herein, the surface 314 includes nitrogen. For instance, the semiconductor composition of the channel 306 may be or include GaN. In some cases, the channel 306 is configured such that the surface 314 is nitrogen-terminated. In this example, the stabilizing layer 312 is configured as a protection or other passivation layer for the surface 314.
The stabilizing layer 312 may be or otherwise include a uniform distribution of an oxynitride material. In some cases, the oxynitride material is GaON. The uniform nature of the distribution may stabilize the interface between the channel 306 and the gate oxide layer 310. Such stability may be useful in connection with high voltage operation or other operational conditions in which the interface is subjected to high energy charge carriers and/or other damaging circumstances. In some cases, the oxynitride material is continuously distributed across the surface 314 (e.g., completely cover the entirety of the surface 314).
The stabilizing layer 312 may have a thickness that does not adversely affect the operation of the device 300. For instance, the stabilizing layer 312 may be thinner than the gate oxide layer 310. As described herein, the thickness of the stabilizing layer 312 may fall in a range from about one monolayer to a few monolayers in some cases. Other thicknesses may be used, including, for instance, various sub-nanometer thicknesses and thicknesses of about a few nanometers.
The components of the device 300 are schematically depicted in
Details regarding examples of the above-described devices, systems, and methods are now provided in connection with
The examples demonstrate that Si/GaN photocathodes are capable of generating sustained hydrogen production with approximate 100% Faradaic efficiency (FE) without the use of any electrocatalyst. Accelerated testing of the examples also demonstrates that the Si/GaN photocathodes are capable of sustaining high current density under intensified 3.5 suns illumination for more than 150 hours. As shown in the examples, under operating conditions, the photocurrent density and onset potential of Si/GaN photocathodes self-improve. A suite of advanced characterization techniques and first-principles calculations are used to elucidate the origins of this self-improving behavior. Under operating conditions, the Si/GaN photocathodes are subjected to a chemical transformation at the GaN surface that provides protection and enhances the PEC performance by adding active catalytic sites for hydrogen evolution reactions. In this way, these examples of Si protected photocathodes exhibit useful levels of stability and FE performance without the use of any electrocatalysts, as the result of a beneficial chemical transformation. The self-improving behavior and chemical transformation of the Si/GaN photocathodes provides useful devices and systems for hydrogen production in PEC water splitting.
To set a baseline for understanding the stability mechanism of the GaN overlayer, Si/GaN photocathodes were investigated under water reduction conditions. Iridium oxide (IrOx) is used as the counter electrode and graphite colloidal adhesive is used to connect the Si/GaN electrode to copper tape. This testing configuration prevents any metal contamination. Chronoamperometric (CA) tests were conducted on different samples under 1 sun intensity illumination. In all of the cases, the measured photocurrent undergoes an increase before it achieves a steady state. Interestingly, the calculated corresponding Faradaic efficiency (FE) also follows a similar enhancement, i.e., the FE starts from about 85 then achieves 100% once the photocurrent reaches its maximum, as shown in Part (a) of
To provide further insight into the PEC performance enhancement, an intermittent 10 hour CA test was performed with linear sweep voltammetry (LSV) collected after each hour to track the changes in PEC performance, i.e. photocurrent density and onset potential. As shown in part (c) of
To look into the underlying mechanism of this self-improving behavior, the changes of the surface resistance were analyzed by carrying out electrochemical impedance spectroscopy (EIS) at AM 1.5G 1 sun illumination. By evaluating the simulated equivalent circuit and the corresponding calculated results, the surface resistance (Rct,surf) decreases from 600Ω to 100Ω. The dramatic variation of Rct,surf evidences that the charge transfer at the solid/liquid interface improves over time. In addition, Mott-Schottky analysis reveals that the flat band potential is similar after reaction, which suggests that the flat band position is determined by the n+p Si solar cell substrate in agreement with previous results. Given that the band alignment remains unchanged, while a significant change in Rct,surf and mild changes in other resistance (R) and constant phase element (CPE) values, the observed self-improving behavior is originated by an improvement of the surface kinetics of the GaN layer.
The observed self-improving anodic shift of the onset potential and charge transfer improvement indicate an enhanced catalytic activity of the PEC tested GaN surface, which usually is obtained through the integration of a catalyst layer. Therefore, with the unique opportunity to improve device performance while decreasing (noble metal) catalyst loading, the direct integration of a platinum (Pt) catalyst onto the modified Si/GaN photocathode is investigated. A comparison between the as-prepared Si/GaN photocathode and the CA tested surface was conducted. The initial PEC performance of the as-prepared device was recorded by LSV scans. Then the CA testing was carried out for four hours to guarantee that the maximum current is achieved (see, e.g., parts (a)-(c) of
Surface roughness change and formation of new chemical species are factors associated with PEC performance improvement. Thus, atomic force microscopy (AFM) analysis was performed, as well as scanning transmission electron microscopy combined with electron energy loss spectroscopy (STEM/EELS) and X-ray photoelectron spectroscopy to trace the origin of the observed PEC performance enhancement. Specifically, by performing photoconductive (pc-) AFM on both as-prepared (“CA-0h”) and 10 hours CA tested (“CA-10h”) examples, the surface topography was compared, as well as probe the nanoscale origin of the macroscopic photocurrent enhancement. The surface morphology remains similar for CA-0h and CA-10h surfaces with similar surface roughness of about 12 nm (as shown in Parts (a) and (c) of
In order to understand how the tested example changed under operating conditions and the reason underlying the increased photocurrent at the sidewall of the GaN grains, aberration correction STEM/EELS was used to analyze crystal orientation combined with chemical information with less than 1 nm spatial resolution (as shown in Parts (a) and (b) of
By connecting the STEM/EELS results to the increased photocurrent and anodic shift of the onset potential, an oxygen-containing GaN phase is found to have formed. This finding was readily confirmed by XPS. In addition to the as-prepared example, three different Si/GaN photocathodes were analyzed after 1 h, 4 h and 10 h of chronoamperometric testing (CA-1h, CA-4h, and CA-10h). The XPS spectra of the as-prepared and tested examples show similar Ga 2p and N 1s core levels spectra and high signal-to-noise ratio, irrespectively of the length of the test. In contrast, more insights are gained from O 1s spectra (Parts (c)-(f) of
To better understand how the experimental observation of the self-improving PEC performance as well as the sustained operation of Si/GaN photocathodes correlate to the presence of gallium oxynitride, density functional theory (DFT) calculations for different GaN surfaces were performed. The top surface of the example is (000
The role of oxygens on the stability of GaN was explored with several representative surface models and the formation energy thereof. For the (0001) orientation, a full replacement of nitrogen atoms of either surface or subsurface bilayers by oxygens was found (red and green lines,
The calculations show that the effect of oxygen substitution is rather different for the non-polar (10
Catalytic activity was then assessed. The free energy of adsorption of hydrogen is the reaction intermediate for both HER and HOR. The absolute magnitude of the free energy of H adsorption (|ΔGads|≈0) is minimized to maximize the reaction. Here, examination of adsorption sites of the most stable surface of the non-polar plane (blue line, |ΔGads| of 0.31-0.39 eV. The results show that the surface with partial nitrogen substituted by oxygens is more active than the pristine one, indicating that transformation in the surface composition is likely responsible for the improved performance of the GaN-protected photocathode.
To advance the application of solar water splitting for renewable energy, work has been directed to the development of cutting-edge coatings for long-term stability and high efficiency. As described herein, Si/GaN photocathodes are capable of sustained hydrogen production with 150 h stability under 3.5 suns and a FE of about 100% without electrocatalysts. By employing pc-AFM, STEM/EELS and XPS characterization techniques, the presence of a thin oxynitride-like layer is shown, which forms over time on Si/GaN photocathodes within the first few hours of operation. Such gallium oxynitride, as well as many other widely reported oxynitrides (TaON, HfON, perovskite oxynitride, etc.), have the hybridization of N 2p and O 2p orbitals and possess good catalytic properties. The gallium oxynitride is capable of providing an electrocatalyst role by better mediation of charge transfer. The DFT simulation results were in line with the experiments that replacing the nitrogen atoms by oxygen to form oxynitride can passivate the surface for further stability, whereas the newly formed oxynitride can also provide more active sites for HER, leading to improved PEC performance. GaN is thus established as a stable and efficient protective layer via formation of oxynitride during hydrogen production.
In this case, the structure 1004 corresponds with, or otherwise includes, a stack of semiconductor layers configured for light emission. For example, one or more of the semiconductor layers in the stack may be composed of, or otherwise include, GaN, InGaN, and/or other III-V semiconductor materials.
The device 1000 further includes electrodes 1006, 1008 for applying a voltage across the stack of semiconductor layers. One of the electrodes 1006 may be configured as an n-metal contact, while the other electrode 1008 may be configured as an p-metal contact. The positions of the p-metal and n-metal contacts may be switched and otherwise vary.
In this example, the stack includes an n-type layer 1010, an active layer 1012, and a p-type layer 1014. The active layer 1012 is disposed between the n-type and p-type layers 1010, 1014. Each of the n-type and p-type layers 1010, 1014 may be configured as current conduction layers of the device 1000. The stack of semiconductor layers may include any number of semiconductor layers. For instance, additional layers may include one or more buffer layers, and/or one or more additional active layers.
The stack of semiconductor layers and, thus, the structure 1004 has a surface at which nitrogen is present. In this example, the surface corresponds with an upper surface of the p-type layer 1014. For instance, the p-type layer may be composed of, or otherwise include, GaN and/or another III-nitride semiconductor, although nitrogen may be present at the surface for additional or alternative reasons.
The device 1000 includes a stabilizing layer 1016 disposed on the surface of the p-type layer 1014. The stabilizing layer 1016 may be configured as described herein. For instance, the stabilizing layer may include a uniform distribution of an oxynitride material. In this case, the stabilizing layer 1016 is disposed adjacent to, and in contact with, the metal contact layer 1008 (e.g., the p-metal contact layer). The stabilizing layer 1016 is disposed along an interface between the metal contact layer 1008 and the stack of semiconductor layers to reduce contact resistance at the interface. In some cases, the oxynitride material of the stabilizing layer 1016 is continuously distributed across the surface of the p-type layer 1014 (e.g., continuously covers the entirety of the p-type layer 1014).
Alternatively or additionally, the stabilizing layer 1016 (or a section thereof) is disposed along an interface between the metal contact layer 1006 and the n-type layer 1010. The contact resistance may thus be reduced at the other contact of the device 1000 and/or both contacts.
The device 1100 further includes electrodes 1106, 1108 for applying a voltage across the stack of semiconductor layers. One of the electrodes 1106 may be configured as an n-metal contact, while the other electrode 1108 may be configured as an p-metal contact. The positions of the p-metal and n-metal contacts may be switched and otherwise vary.
As described above, the stack includes an n-type layer 1110, an active layer 1112, and a p-type layer 1114. The active layer 1112 is disposed between the n-type and p-type layers 1110, 1114. Each of the n-type and p-type layers 1110, 1114 may be configured as current conduction layers of the device 1100. The stack of semiconductor layers may include any number of semiconductor layers. For instance, additional layers may include one or more buffer layers, and/or one or more additional active layers.
The stack of semiconductor layers and, thus, the structure 1104 has a surface at which nitrogen is present. In this example, the surface corresponds with sidewalls of one or more of the semiconductor layers of the stack. For instance, each one of the n-type layer 1110, the active layer 1112, and the p-type layer 1114 may be composed of, or otherwise include, GaN and/or another III-nitride semiconductor, although nitrogen may be present at the surface for additional or alternative reasons. In this light emitting device example, the sidewall surface(s) may be a polar surface. In other examples (e.g., transistor devices), the sidewall surface(s) may be a non-polar surface.
The device 1100 includes a passivation layer 1116 disposed along the sidewalls of one or more of the layers of the stack. For example, the passivation layer 1116 may be or include a dielectric material, such as an oxide material. Additional or alternative non-conductive materials may be used. In this example, the passivation layer 1116 is disposed along each sidewall of the stack such that the entirety of each layer is passivated by the passivation layer 1116.
The device 1100 includes a stabilizing layer 1118 disposed between the passivation layer 1116 and the sidewall surfaces of the stack. The stabilizing layer 1118 may be configured as described herein. For instance, the stabilizing layer 1118 includes a uniform distribution of an oxynitride material. In this example, the stabilizing layer 1118 is disposed adjacent to, and in contact with, each sidewall of the stack. The stabilizing layer 1118 is thus disposed along an interface between the stack and the passivation layer 1116 to stabilize the interface between the active layer (and/or other layers of the stack) and the passivation layer and/or to reduce surface recombination. In some cases, the oxynitride material of the stabilizing layer 1118 is continuously distributed across the sidewall surfaces of the stack (e.g., continuously covering the entirety of each sidewall surface of the stack). The stabilizing layer may thus suppress surface traps and/or address other imperfections along the interface.
In this example, the stabilizing layer is disposed along the sidewalls of each layer in the semiconductor stack. In other cases, the stabilizing layer 1118 (or a section thereof) is disposed along the interface between a subset of the layers in the stack. For example, the stabilizing layer 1118 may be disposed along the sidewall(s) of only the active layer of the stack.
The devices 1000 and 1100 of
As described above, efficient yet durable photoelectrodes and other devices are fabricated. In solar-fuel production examples involving silicon/gallium nitride photocathodes active for hydrogen production, a thin layer of gallium oxynitride forms on the sidewalls of the gallium nitride grains, via a partial oxygen substitution at nitrogen sites. The thin layer establishes a higher density of catalytic sites for the hydrogen evolving reaction. The chemical transformation of gallium nitride into gallium oxynitride leads to sustained operation and enhanced catalytic activity, thus showing the promise for oxynitride layers as protective catalytic coatings for hydrogen evolution and other reactions.
Further details are set forth below regarding crystallographic-based aspects and effects of nanostructures, such as III-nitride nanostructures (e.g., GaN nanowires and other nanostructures). The crystallographic-based aspects and effects may be useful and/or provided in connection with PEC devices and systems for various types of reactions, as well as other types of devices.
The crystallographic aspects and effects of the disclosed devices may be useful in addressing the efficiency, stability, and product selectivity challenges for artificial photosynthesis. The disclosed devices may accordingly avoid the tradeoff between stability and efficiency. Past high efficiency solar water splitting devices generally exhibit very short lifetime, whereas devices with long-term stability have shown low efficiency. The disclosed devices may also be useful in supporting selective production of target products, which has remained difficult to achieve, with, for example, very low faradaic efficiency of light-driven chemical transformation of CO2 and CH4 to liquid chemicals and fuels to date. The crystallographic aspects and effects of the disclosed devices involve configuring the surface of the photoelectrode. Because the reactions are carried on the surface of the photoelectrode, tuning the surface structure of the photoelectrode provides one of the most effective means to address these fundamental challenges. The facet(s) exposed at the surface play a useful role in determining electronic and catalytic activity, including redox reaction sites, adsorption of chemical species, and desorption of product molecules. In addition, due to the diversity in the arrangement of atoms, facets strongly impact charge carrier separation, extraction and recombination, electrical conductivity, and resistance to photocorrosion and oxidation, all of which are useful factors for achieving efficient and stable artificial photosynthesis and other chemical reactions.
Although described in connection with water splitting examples, the crystallographic-based aspects and effects may be useful in connection with a broad range of artificial photosynthesis chemical reactions.
As described above, Ill-nitride semiconductor nanostructures, e.g., Ga(In)N nanowires, are useful for applications in artificial photosynthesis. Ga(In)N nanostructures are the only known group III-V compound semiconductors whose energy bandgap can be tuned across nearly the entire solar spectrum while straddling a broad range of redox potentials under visible and near-infrared light irradiation, which is useful for high efficiency artificial photosynthesis.
In some cases, the disclosed devices are configured as photoelectrodes made of III-nitride nanowires. III-nitride nanowires have demonstrated stable and efficient operation for 3,000 hours without any performance degradation. The III-nitride nanowire-based photoelectrodes may be used in various reactions, including, for instance, CO2 reduction to syngas, formic acid, and methane, each with relatively high Faradaic efficiency. Other chemical reactions may be supported, including, for instance, light driven conversion of CH4 into aromatic compounds using gallium nitride (GaN) nanowires.
As described below, the crystallographic aspects of III-nitride nanostructures may be used to improve catalytic and other performance measures. Previous studies have been largely focused on the effects of composition, size, and doping of GaN-based structures on their catalytic performance. Wurtzite III-nitride nanostructures, however, have different facets, e.g., polar vs. nonpolar vs. semipolar, and different polarities, e.g., metal-polar vs. nitrogen polar, which have very different structural, chemical, electrical, and polarization properties. To date, the role of crystal facet and polarity of III-nitride nanostructures on photoelectrochemical reactions has remained largely unknown. The relationship between the crystal facets and catalytic and electrical activity is accordingly addressed below. It is shown that significant activity (e.g., photoelectrochemical activity) is observed at the nonpolar surfaces (e.g., when the nonpolar surfaces are exposed to an electrolyte), whereas little to no activity is measured at the polar (e.g., c-plane) surfaces (e.g., when only the polar surfaces are exposed to the electrolyte), thereby enabling the rational design, synthesis, and practical application of next-generation metal-nitride semiconductor photoelectrodes and other devices.
Although described in connection with GaN nanostructures, the disclosed devices and methods may use a wide variety of semiconductor materials. The disclosed devices and methods are accordingly not limited to III-nitride semiconductors. For instance, the disclosed devices may include one or more layers, components or other elements composed of, or otherwise including, various nitrogen-containing semiconductors and/or various oxygen-containing semiconductors.
Described below are a number of examples that analyze the effect of facet and surface polarity of wurtzite III-nitrides on their photoelectrochemical (PEC) activities, e.g., solar water splitting. To identify unambiguously the impact of facets with different polarities, a number of example III-nitride nanostructures were fabricated by both top-down and bottom-up methods, thereby exposing selectively certain facets/surfaces to the electrolyte and compare their PEC activities. In addition, to rule out any variations in light absorption and alloy composition associated with nanostructure engineering, GaN layers were grown directly on a Si p-n wafer as a platform that serves as the primary light absorber. In these examples, the light absorption and photogenerated electron density in the GaN nanostructures remained nearly the same regardless of variations in their facet and surface polarity.
The examples show that the nonpolar GaN surfaces are significantly more active than the polar surfaces for the PEC reaction. The atomic origin of such behavior is further revealed through detailed density functional theory (DFT) calculations set forth below.
The examples show the unique formation of oxynitrides on the nonpolar plane, but not the c-plane, during the PEC reaction. The presence of oxynitride leads to a positive surface polarization and significant downward band bending, which can drastically enhance charge carrier (electron) extraction. The examples also provide useful insight and guidelines on crystal facet engineering of the emerging metal-nitride photocatalysts and photoelectrodes for a broad range of artificial photosynthesis chemical reactions.
In a first set of examples, GaN epilayers were grown on a Si p-n wafer using plasma-assisted molecular beam epitaxy (MBE). To date, the growth of GaN epilayers directly on Si wafer has remained extremely challenging due to the large lattice mismatch (about 17%) and the large difference in thermal expansion coefficients. Previously, various methods, including an AlN seed layer, an AlGaN/GaN defect filtering layer, a low temperature AlN interlayer, and a SiC intermediate layer, have been employed to improve GaN epilayer quality. These growth techniques, however, are not suitable for the present examples because large bandgap buffer layers would act as charge carrier transfer barriers between the Si wafer and the GaN epilayer, and thus degrade the PEC performance.
Moreover, previous studies have focused on GaN growth on Si (111) substrates, with few demonstrations of GaN epilayers on Si (100) wafers, which are required for direct integration with Si p-n junctions. To overcome these challenges, the examples used optimized growth conditions to realize GaN quasi-epilayer structures on the Si p-n wafers through controlled nanowire coalescence. The growth temperature was about 640° C. with a nitrogen flow rate of 0.4 sccm. The Ga beam equivalent pressure was about 1.6e-7 Torr, corresponding to a growth rate of about 120 nm/h.
The quasi-film structures preferentially grow along the c-plane direction. For such structures, the top GaN c-plane is thus the surface predominantly exposed to the electrolyte, whereas the non-polar planes are kept unexposed. To compare the effects of polar and non-polar planes, two samples were prepared, Sample A and Sample B. Sample A was an as-grown quasi-epilayer, while Sample B was patterned by photolithography and etching of the quasi-epilayer to expose the non-polar surfaces, in this case, sidewalls. With exposed sidewalls, photoexcited electrons can migrate to the GaN nonpolar surfaces and reduce protons to hydrogen. On the other hand, without such exposed sidewalls, electrons have to migrate to the top c-plane surfaces for proton reduction reaction. The photolithography and etching are schematically illustrated in part (a) of
Part (b) of
PEC characterizations were performed in a three-electrode setting consisting of the GaN/Si photocathode, an Ag/AgCl reference electrode, and an IrOx counter electrode in 0.5 M H2SO4 under AM1.5G one-sun illumination. Pt co-catalyst nanoparticles were deposited on the GaN/Si photocathodes via photodeposition. The linear scan voltammetry (LSV) measurements were performed from 0.6 to about 0.3 V vs. RHE with a scan rate of 100 mV/s. Although a high photocurrent density (up to about 40 mA/cm2) is expected from a Si p-n junction under AM1.5G one-sun illumination, Sample A exhibited no measurable photocurrent density, suggesting that the Ga-face c-plane GaN is not very photoelectrochemically active (see part (a) of
With reference now to
The as-grown GaN NW/Si photocathode exhibits an onset potential of 0.45 V vs. RHE and maximum photocurrent density of 28 mA/cm2 (see part (a) of
The photocurrent data of
Density Functional Theory (DFT) Analysis. As described above, during PEC water splitting reactions, oxygen adsorption and substitution can occur on GaN surfaces. Therefore, to understand the fundamental difference in the PEC activity between c-plane and nonpolar plane GaN surfaces, it has been taken into account the role of oxygen that can readily adsorb and be incorporated into the surfaces, e.g., during operation.
The DFT calculations were performed with the generalized gradient approximation, using the plane-wave pseudopotential quantum-ESPRESSO package. Ultrasoft pseudopotentials were used to describe the interaction between valence electrons and ionic cores, where Ga 3d electrons were explicitly treated as valence electrons. The wave functions and electronic density were expanded in a plane-wave basis set truncated at a cutoff energy of 30 Ry and 240 Ry, respectively. The surface was modeled with a repeated slab geometry using a (2×2) unit cell with a thickness of seven GaN bilayers, where the N-terminated bottom side was passivated by pseudo-hydrogen with charge of 0.75e. In addition, the (10
For the nonpolar (10
On the other hand, for the polar (0001) GaN surface, the most stable surface configuration in an oxygen-rich condition was found to be the one with a 0.25 ML coverage of oxygen adsorption (see part (b) of
Interestingly, the oxygen was found to have significant effects on the surface polarization and thereby the band bending at the surfaces. More specifically, the calculations showed that oxygen substitution and adsorption lead to a positive and negative surface polarization at the nonpolar (10
Quantitatively, these surface polarizations induce an upward band bending of 0.21 eV at the (0001) plane and a downward band bending of 0.25 eV at the non-polar surface, as shown in parts (c) and (d) of
The difference between Sample A and B in surface polarization induced by different surface oxygen interactions contributes to their difference in surface band bending shown in the MS measurements. Sample A, with essentially only its top c-plane exposed to the electrolyte, showed a negative flat-band potential (see part (b) of
Through the foregoing theoretical and experimental analyses, the significance of the non-polar GaN planes in promoting PEC hydrogen evolution reaction has been identified. During the PEC reaction, the formation of unique gallium oxynitride on the nonpolar GaN surfaces significantly enhances charge carrier (electron) transport and extraction, whereas oxygen adsorption on polar c-plane surfaces prevents the efficient charge carrier extraction. The analyses elucidate the atomic origin for the high efficiency photo(electro)catalytic activities of GaN nanowires, compared to conventional GaN film structures. Exposing the non-polar facets of wurtzite III-nitrides is a useful strategy for achieving breakthrough advances in PEC activity by enhancing the electron migration between the photocathode and the electrolyte. An understanding of the relationship between crystallographic orientation and photo(electro)chemical reactions will be useful in PEC water splitting and various other catalytic reactions such as carbon dioxide reduction and nitrogen fixation.
The nanostructure(s) 1702 is/are supported by a substrate (not shown) as described herein. The nanostructures 1702 may be disposed in an array or other arrangement. In this case, each nanostructure 1702 is configured as a nanowire, but other shapes and structures may be used. The nanostructures may be grown (e.g., epitaxially grown) or formed via additional and/or alternative techniques, such as through etching. The device 1700 may include or have any one or more of the features or characteristics of the nanowire-based devices described herein.
The nanostructure 1702 has a semiconductor composition. In some cases, the nanostructure 1702 is composed of GaN and/or another III-nitride semiconductor material. Alternative or additional semiconductor materials (e.g., compound semiconductors). For instance, the semiconductor composition is not limited to nitrogen-containing semiconductors. Oxygen-containing semiconductors may be used in other cases.
The nanostructure 1702 has a surface at which either nitrogen or oxygen is present. The presence of nitrogen or oxygen may arise from the composition of the semiconductor material. In some cases, the surface may be nitrogen-terminated.
The device 1700 includes a stabilizing layer 1704. The stabilizing layer 1704 is disposed on the surface of the nanostructure 1702. In this case, the surface on which the stabilizing layer 1704 is disposed is a sidewall of the nanostructure 1702. The stabilizing layer 1704 includes an oxynitride material, as described herein. The oxynitride material may be continuously distributed across the surface of the nanostructure 1702. The stabilizing layer may thus continuously cover the surface. The oxynitride of the stabilizing layer 1704 may be established via the substitution of the nitrogen or oxygen at the surface with oxygen or nitrogen, respectively.
In the example of
The device 1700 further includes a passivation cover or cap 1706 disposed on a polar surface of the nanostructure 1702. In this example, the nanostructure 1702 has a top or upper polar surface, end, or facet. The passivation cap 1706 may be configured to completely cover or passivate the top surface of the nanostructure 1702. Such coverage or passivation may protect the nanostructure 1702 from corrosion or other degradation arising from, for instance, an electrolyte in which the device 1700 is immersed. In this wurtzite example, the polar surface is oriented along a c-plane of the lattice. In some cases, the passivation cap 1706 includes a nitride material or an oxide material. For example, the passivation cap 1706 may be composed of, or otherwise include, AlOx, HfO2, SixNy, and AlSiNx, but other materials may be used.
As with the example of
The example of
The device 1710 further includes a passivation cover or cap 1716 disposed on a polar surface of the nanostructure 1712. The passivation cap 1716 may be disposed on a polar surface, as well as configured and constructed, as described above in connection with the example of
The device 1710 includes further includes a passivation structure 1718 that partially covers the non-polar surface of the nanostructure 1712. In this example, the passivation structure 1718 surrounds or otherwise covers a lower portion of the sidewall surface of the nanostructure 1712.
The extent to which the sidewall surface is passivated by the passivation structure 1718 may vary. As described above, the current density of the device 1710 may not be significantly hampered by a decrease in exposed surface area of the nanostructure 1712. The passivation structure 1718 may thus cover a substantial amount of the sidewall surface without adversely affecting charge transfer and/or other device performance.
In some cases, the passivation structure 1718 is composed of, or otherwise includes, parylene, as described above. Other materials may be used, including various nitride materials and various oxide materials. For instance, AlOx, HfO2, SixNy, or AlSiNx may be used.
The passivation structure 1718 may be configured as, or otherwise include, a layer in which any number of nanostructures 1712 of the device 1710 are embedded or otherwise disposed. For instance, the device 1710 may be configured as described and shown in the example of part (c) of
In other examples, the device may include other types of nanostructures. For instance, the device may be configured as a light emitting device, such as a light emitting diode (LED) device. The device may thus include an active layer and an electrode supported by the active layer, as described above in connection with the example of 10. In such cases, the stabilizing layer is disposed between the active layer and the electrode. The active layer has a non-polar surface (e.g., an upper surface oriented along the m-plane of a wurtzite lattice) on which the stabilizing layer is disposed. The presence of the oxynitride of the stabilizing layer may thus promote charge transfer between the active layer and the electrode, as described above.
LED and other devices having a stabilizing layer on a non-polar surface may also include one or more passivation structures disposed along a sidewall of the active layer or other structure stabilized by the stabilizing layer. Please see, e.g., the example shown in
In still other cases, the device includes a stabilizing layer disposed along a polar surface to act as a passivation layer. For instance, the device may be configured as a transistor, such as a transistor device. In such cases, the stabilizing layer is disposed between a channel layer and a gate oxide layer, as described above in connection with the example of
The nanostructure 1724 has a semiconductor composition. The semiconductor composition may vary. For instance, any of the semiconductor compositions described herein may be used.
The nanostructure 1724 has a surface stabilized by a stabilizing layer 1726. The stabilizing layer 1726 is composed of, or otherwise includes, an oxynitride material, as described herein. In this example, the surface is an upper, planar surface of the nanostructure 1724. In some cases, the surface is a non-polar surface, in which case the stabilizing layer 1726 may be used to facilitate charge transfer between the nanostructure 1724 and another layer, such as a contact or electrode 1728. As described herein, the surface may correspond with the m-plane of a lattice of the nanostructure 1724. The stabilizing layer 1726 may thus establish an interface between the m-plane surface of the nanostructure 1724 and the electrode 1728. In other cases, the stabilizing layer 1726 is disposed between the nanostructure 1724 and another layer, component or element of the device 1700. In still other examples, the surface of the nanostructure 1724 is a polar surface, (e.g., corresponding with a c-plane of the lattice). In such cases and other cases, the stabilizing layer 1726 may be used to passivate the surface of the nanostructure 1724. For instance, the stabilizing layer 1726 may act to stabilize an interface between the nanostructure 1724 and the layer 1728, which may be configured as an oxide or other dielectric layer. In any of these cases, the oxynitride material of the stabilizing layer 1726 may be continuously distributed across the planar surface of the nanostructure 1724 (e.g., continuously cover the entirety of the surface).
The device 1700 may have one or more other aspects, features, components, or other characteristics in common with any one of the other examples described herein.
The method 1800 may be implemented in conjunction with one or more of the acts of the other fabrication methods described herein, including, for instance, those shown in connection with
The method 1800 includes an act 1802 in which a structure of the device is formed. The structure may be or include a nanostructure such as a nanowire or an active, channel, or other layer of a device. The structure is supported by the substrate, has a semiconductor composition, as described herein.
In the example of
On the charge transfer branch, the method 1800 may include an act 1804 in which one or more passivation structures is deposited. For instance, the passivation structure(s) may be disposed adjacent to the structure. As a result, a portion of the structure is covered by the passivation structure. Examples of such passivation structures include the cap layer on a c-plane of a nanowire, as described herein. The act 1804 may thus in some cases include covering a c-plane or other polar surface of the structure. In other examples, the passivation structure partially covers a sidewall (e.g., an m-plane) or other non-polar surface of the nanowire, as described herein.
The method 1800 includes an act 1806 in which a stabilizing layer is formed on a non-polar surface of the structure. The stabilizing layer includes an oxynitride material, as described herein. In some cases, the act 1806 may include depositing an oxygen-containing material (e.g., an oxide) on the non-polar surface, and implementing an anneal to form the oxynitride material from oxygen of the oxygen-containing material. The act 1806 may include any one or more of the acts described herein in connection with incorporating oxygen into the surface (see, e.g.,
The act 1806 may be implemented via an oxidation reaction, as described herein. The act 1806 may thus be implemented after depositing a passivation structure in the act 1804. In other cases, depositing the passivation structure is implemented after forming the stabilizing layer.
Turning to the passivation/insulation branch, the method 1800 includes an act 1808 in which a stabilizing layer is formed on a polar surface of the structure. The stabilizing layer is composed of, or otherwise includes, an oxynitride material, as described herein. In this case, the oxynitride of the stabilizing layer is used to passivate and/or insulate an interface of the device, such as the interface between a channel layer and a gate dielectric layer of a transistor device, as described herein. The polar surface of the structure may thus be a c-plane of a wurtzite lattice, as described herein. The act 1808 may include any one or more of the acts described herein in connection with incorporating oxygen into the surface (see, e.g.,
The method 1800 may include an act 1810 to address one or more surfaces of the structure, such as an polar (e.g., c-plane) surface on which the stabilizing layer is formed, or a non-polar (e.g., m-plane) surface, via the deposition of a passivation or other insulating structure. In examples of the former case, the act 1810 may include depositing an insulating layer, such as a gate oxide layer. In examples of the latter case, the act 1810 may include depositing a passivation structure along sidewalls. For instance, the non-polar sidewalls of an active layer may be passivated via the act 1810. The act 1810 may be directed to depositing a passivation structure along such non-polar surface(s) of the structure such that the m-plane or other non-polar surface is covered by the passivation structure. The passivation structure deposited in the act 1810 may thus be useful in cases in which use of the oxynitride of the stabilizing layer would not passivate the non-polar surface for the reasons set forth herein.
The present disclosure has been described with reference to specific examples that are intended to be illustrative only and not to be limiting of the disclosure. Changes, additions and/or deletions may be made to the examples without departing from the spirit and scope of the disclosure.
The foregoing description is given for clearness of understanding only, and no unnecessary limitations should be understood therefrom.
This application claims the benefit of U.S. provisional application entitled “Oxynitride-Based Surface Stabilization,” filed Feb. 26, 2021, and assigned Ser. No. 63/154,428, the entire disclosure of which is hereby expressly incorporated by reference.
This invention was made with government support under Contract No. DE-EE0008086 awarded by the Department of Energy and under Contract No. W911NF2110337 awarded by the U.S. Army Research Office. The government has certain rights in the invention.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2022/018126 | 2/28/2022 | WO |