Laser-assisted fabrication of semiconductor structures and devices formed by utilizing a compliant substrate

Abstract
Semiconductor structures are provided with high quality epitaxial layers of monocrystalline materials grown over monocrystalline substrates such as large silicon wafers utilizing a compliant substrate. One way to achieve the formation of a compliant substrate includes first growing an accommodating buffer layer on a silicon wafer. The accommodating buffer layer is lattice matched to both the underlying silicon wafer and an overlying monocrystalline material layer. With laser assisted fabrication, a laser energy source is used to preclean the accommodating buffer layer, to excite the accommodating buffer layer to higher energy to promote two-dimensional growth, and to amorphize the accommodating buffer layer, without requiring transport of the semiconductor structure from one environment to another. When chemical vapor deposition is utilized, the laser radiation source can also be employed to crack volatile chemical precursors and to enable selective deposition.
Description


FIELD OF THE INVENTION

[0001] This invention relates generally to semiconductor structures (including devices and integrated circuits) and their fabrication, and more specifically to the fabrication of semiconductor structures that include a monocrystalline material layer comprised of semiconductor material, compound semiconductor material, and/or other types of material such as metals and non-metals formed by utilizing a compliant substrate.



BACKGROUND OF THE INVENTION

[0002] Semiconductor structures often include multiple layers of conductive, insulating, and semiconductive layers. Often, the desirable properties of such layers improve with the crystallinity of the layer. For example, the electron mobility and band gap of semiconductive layers improves as the crystallinity of the layer increases. Similarly, the free electron concentration of conductive layers and the electron charge displacement and electron energy recoverability of insulative or dielectric films improves as the crystallinity of these layers increases.


[0003] For many years, attempts have been made to grow various monolithic thin films on a foreign substrate such as silicon (Si). To achieve optimal characteristics of the various monolithic layers, however, a monocrystalline film of high crystalline quality is desired. Attempts have been made, for example, to grow various monocrystalline layers on a substrate such as germanium, silicon, and various insulators. These attempts have generally been unsuccessful because lattice mismatches between the host crystal and the grown crystal have caused the resulting layer of monocrystalline material to be of low crystalline quality.


[0004] If a large area thin film of high quality monocrystalline material was available at low cost, a variety of semiconductor devices could advantageously be fabricated in or using that film at a low cost compared to the cost of fabricating such devices beginning with a bulk wafer of semiconductor material or in an epitaxial film of such material on a bulk wafer of semiconductor material. In addition, if a thin film of high quality monocrystalline material could be realized beginning with a bulk wafer such as a silicon wafer, an integrated device structure could be achieved that took advantage of the best properties of both the silicon and the high quality monocrystalline material.


[0005] Accordingly, a need exists for a semiconductor structure that provides a high quality monocrystalline film or layer over another monocrystalline material and for a process for making such a structure. In other words, there is a need for providing the formation of a monocrystalline substrate that is compliant with a high quality monocrystalline material layer so that true two-dimensional growth can be achieved for the formation of quality semiconductor structures, devices and integrated circuits having grown monocrystalline film having the same crystal orientation as an underlying substrate. This monocrystalline material layer may be comprised of a semiconductor material, a compound semiconductor material, and other types of material such as metals and non-metals. However, advantages of such structures may be lost if impurity's, such as those which reduce electron mobility or photo activity are not satisfactorily controlled.







BRIEF DESCRIPTION OF THE DRAWINGS

[0006] The present invention is illustrated by way of example and not limitation in the accompanying figures, in which like references indicate similar elements, and in which:


[0007]
FIGS. 1, 2, and 3 illustrate schematically, in cross section several device structures;


[0008]
FIG. 4 illustrates graphically the relationship between maximum attainable film thickness and lattice mismatch between a host crystal and a grown crystalline overlayer;


[0009]
FIG. 5 illustrates a high resolution Transmission Electron Micrograph of a structure including a monocrystalline accommodating buffer layer;


[0010]
FIG. 6 illustrates an x-ray diffraction spectrum of a structure including a monocrystalline accommodating buffer layer;


[0011]
FIG. 7 illustrates a high resolution Transmission Electron Micrograph of a structure including an amorphous oxide layer;


[0012]
FIG. 8 illustrates an x-ray diffraction spectrum of a structure including an amorphous oxide layer;


[0013] FIGS. 9-12 illustrate schematically, in cross-section, the formation of a certain device structure;


[0014] FIGS. 13-16 illustrate a probable molecular bonding structure of the device structures illustrated in FIGS. 9-12;


[0015] FIGS. 17-20 illustrate schematically, in cross-section, the formation of still another device structure; and


[0016] FIGS. 21-23 illustrate schematically, in cross-section, the formation of yet another device structure.


[0017]
FIG. 24 illustrates a flow diagram of a fabrication process in accordance with the present invention.







[0018] Skilled artisans will appreciate that elements in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the elements in the figures may be exaggerated relative to other elements to help to improve understanding of embodiments of the present invention.


DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0019] The present invention is directed to the fabrication of high quality semiconductor structures having certain features described herein. As used herein, the term “structures” will be used to refer to semiconductor structures, devices, integrated circuits and other items useful to commerce and scientific inquiry. As will be explained in greater detail herein, fabrication of semiconductor structures according to principles of the present invention is assisted using laser energy, applied in a number of ways.


[0020] By way of introduction, the present invention is directed to semiconductor structures having certain features, which will be generally described with reference to two examples. In a first general example, semiconductor structures of interest have features which include a monocrystalline silicon substrate, an amorphous oxide material overlying the monocrystalline silicon substrate, and a monocrystalline perovskite oxide material overlying the amorphous oxide material. A monocrystalline compound semiconductor material overlies the monocrystalline perovskite oxide material. The semiconductor structure features may optionally include a template layer between the monocrystalline perovskite oxide layer and the monocrystalline compound a semiconductor material, as well as a buffer material of monocrystalline semiconductor material formed between the monocrystalline perovskite oxide material and the monocrystalline compound semiconductor material. An optional template layer may also be formed between the monocrystalline perovskite oxide material and the buffer material.


[0021] In a second general example, semiconductor structures of interest have features which include a monocrystalline substrate characterized by a first lattice constant; a monocrystalline insulator layer having a second lattice constant different than the first lattice constant overlying the monocrystalline substrate and an amorphous oxide layer between the monocrystalline substrate and the monocrystalline insulator layer. A monocrystalline compound semiconductor layer having a third lattice constant different than the first lattice constant overlies the monocrystalline insulator layer. The second lattice constant is selected to be one of either equal to the third lattice constant or intermediate the first and third lattice constant. The semiconductor structure features may optionally include a template layer between the monocrystalline insulator layer and the monocrystalline compound semiconductor layer. Another optional additional feature may include a buffer layer between the monocrystalline insulator layer and the monocrystalline compound semiconductor layer.


[0022] With laser-assisted fabrication techniques according to principles of the present invention, “high-quality” semiconductor structures can be constructed with conventional equipment, using cost efficient techniques. As used herein, the term “high-quality” refers to active regions of monocrystalline compound semiconductor material having very low densities of crystallographic defects such as dislocations, anti phase domains, and stacking faults as well as very low impurity defect density levels approaching, in some instances, levels of less than 1015 parts per cubic centimeter.


[0023] For purposes of illustration and not limitation, further examples and descriptions of semiconductor structures and devices, and their general method of fabrication, which benefit from the present invention, will now be given. Referring initially to FIG. 1, a schematic illustration of a semiconductor structure 20 is shown in cross section. Semiconductor structure 20 includes a monocrystalline substrate 22, accommodating buffer layer 24 comprising a monocrystalline material, and a monocrystalline material layer 26. In this context, the term “monocrystalline” shall have the meaning commonly used within the semiconductor industry. The term shall refer to materials that are a single crystal or that are substantially a single crystal and shall include those materials having a relatively small number of defects such as dislocations and the like as are commonly found in substrates of silicon or germanium or mixtures of silicon and germanium and epitaxial layers of such materials commonly found in the semiconductor industry.


[0024] In accordance with one embodiment of the invention, structure 20 also includes an amorphous intermediate layer 28 positioned between substrate 22 and accommodating buffer layer 24. Structure 20 may also include a template layer 30 between the accommodating buffer layer and monocrystalline material layer 26. As will be explained more fully below, the template layer helps to initiate the growth of the monocrystalline material layer on the accommodating buffer layer. The amorphous intermediate layer helps to relieve the strain in the accommodating buffer layer and by doing so, aids in the growth of a high crystalline quality accommodating buffer layer.


[0025] Substrate 22, is a monocrystalline semiconductor or compound semiconductor wafer, preferably of large diameter. The wafer can be of, for example, a material from Group IV of the periodic table. Examples of Group IV semiconductor materials include silicon, germanium, mixed silicon and germanium, mixed silicon and carbon, mixed silicon, germanium and carbon, and the like. Preferably substrate 22 is a wafer containing silicon or germanium, and most preferably is a high quality monocrystalline silicon wafer as used in the semiconductor industry. Accommodating buffer layer 24 is preferably a monocrystalline oxide or nitride material epitaxially grown on the underlying substrate. Amorphous intermediate layer 28 is grown on substrate 22 at the interface between substrate 22 and the growing accommodating buffer layer by the oxidation of substrate 22 during the growth of layer 24. The amorphous intermediate layer serves to relieve strain that might otherwise occur in the monocrystalline accommodating buffer layer as a result of differences in the lattice constants of the substrate and the buffer layer. As used herein, lattice constant refers to the distance between atoms of a cell measured in the plane of the surface. If such strain is not relieved by the amorphous intermediate layer, the strain may cause defects in the crystalline structure of the accommodating buffer layer. Defects in the crystalline structure of the accommodating buffer layer, in turn, would make it difficult to achieve a high quality crystalline structure in monocrystalline material layer 26 which may comprise a semiconductor material, a compound semiconductor material, or another type of material such as a metal or a non-metal.


[0026] Accommodating buffer layer 24 is preferably a monocrystalline oxide or nitride material selected for its crystalline compatibility with the underlying substrate and with the overlying material layer. For example, the material could be an oxide or nitride having a lattice structure closely matched to the substrate and to the subsequently applied monocrystalline material layer. Materials that are suitable for the accommodating buffer layer include metal oxides such as the alkaline earth metal titanates, alkaline earth metal zirconates, alkaline earth metal hafnates, alkaline earth metal tantalates, alkaline earth metal ruthenates, alkaline earth metal niobates, alkaline earth metal vanadates, alkaline earth metal tin-based perovskites, lanthanum aluminate, lanthanum scandium oxide, and gadolinium oxide. Additionally, various nitrides such as gallium nitride, aluminum nitride, and boron nitride may also be used for the accommodating buffer layer. Most of these materials are insulators, although strontium ruthenate, for example, is a conductor. Generally, these materials are metal oxides or metal nitrides, and more particularly, these metal oxide or nitrides typically include at least two different metallic elements. In some specific applications, the metal oxides or nitrides may include three or more different metallic elements.


[0027] Amorphous interface layer 28 is preferably an oxide formed by the oxidation of the surface of substrate 22, and more preferably is composed of a silicon oxide. The thickness of layer 28 is sufficient to relieve strain attributed to mismatches between the lattice constants of substrate 22 and accommodating buffer layer 24. Typically, layer 28 has a thickness in the range of approximately 0.5-5 nm.


[0028] The material for monocrystalline material layer 26 can be selected, as desired, for a particular structure or application. For example, the monocrystalline material of layer 26 may comprise a compound semiconductor which can be selected, as needed for a particular semiconductor structure, from any of the Group IIIA and VA elements (III-V semiconductor compounds), mixed III-V compounds, Group II(A or B) and VIA elements (II-VI semiconductor compounds), and mixed II-VI compounds. Examples include gallium arsenide (GaAs), gallium indium arsenide (GaInAs), gallium aluminum arsenide (GaAlAs), indium phosphide (InP), cadmium sulfide (CdS), cadmium mercury telluride (CdHgTe), zinc selenide (ZnSe), zinc sulfur selenide (ZnSSe), and the like. However, monocrystalline material layer 26 may also comprise other semiconductor materials, metals, or non-metal materials which are used in the formation of semiconductor structures, devices and/or integrated circuits.


[0029] Appropriate materials for template 30 are discussed below. Suitable template materials chemically bond to the surface of the accommodating buffer layer 24 at selected sites and provide sites for the nucleation of the epitaxial growth of monocrystalline material layer 26. When used, template layer 30 has a thickness ranging from about 1 to about 10 monolayers.


[0030]
FIG. 2 illustrates, in cross section, a portion of a semiconductor structure 40 which is similar to the previously described semiconductor structure 20, except that an additional buffer layer 32 is positioned between accommodating buffer layer 24 and monocrystalline material layer 26. Specifically, the additional buffer layer is positioned between template layer 30 and the overlying layer of monocrystalline material. The additional buffer layer, formed of a semiconductor or compound semiconductor material when the monocrystalline material layer 26 comprises a semiconductor or compound semiconductor material, serves to provide a lattice compensation when the lattice constant of the accommodating buffer layer cannot be adequately matched to the overlying monocrystalline semiconductor or compound semiconductor material layer.


[0031]
FIG. 3 schematically illustrates, in cross section, a portion of a semiconductor structure 34 which is similar to structure 20, except that structure 34 includes an amorphous layer 36, rather than accommodating buffer layer 24 and amorphous interface layer 28, and an additional monocrystalline layer 38.


[0032] As explained in greater detail below, amorphous layer 36 may be formed by first forming an accommodating buffer layer and an amorphous interface layer in a similar manner to that described above. Monocrystalline layer 38 is then formed (by epitaxial growth) overlying the monocrystalline accommodating buffer layer. The accommodating buffer layer is then exposed to an anneal process to convert the monocrystalline accommodating buffer layer to an amorphous layer. Amorphous layer 36 formed in this manner comprises materials from both the accommodating buffer and interface layers, which amorphous layers may or may not amalgamate. Thus, layer 36 may comprise one or two amorphous layers. Formation of amorphous layer 36 between substrate 22 and additional monocrystalline layer 26 (subsequent to layer 38 formation) relieves stresses between layers 22 and 38 and provides a true compliant substrate for subsequent processing—e.g., monocrystalline material layer 26 formation.


[0033] The processes previously described above in connection with FIGS. 1 and 2 are adequate for growing monocrystalline material layers over a monocrystalline substrate. However, the process described in connection with FIG. 3, which includes transforming a monocrystalline accommodating buffer layer to an amorphous oxide layer, may be better for growing monocrystalline material layers because it allows any strain in layer 26 to relax.


[0034] Additional monocrystalline layer 38 may include any of the materials described throughout this application in connection with either of monocrystalline material layer 26 or additional buffer layer 32. For example, when monocrystalline material layer 26 comprises a semiconductor or compound semiconductor material, layer 38 may include monocrystalline Group IV or monocrystalline compound semiconductor materials.


[0035] In accordance with one embodiment of the present invention, additional monocrystalline layer 38 serves as an anneal cap during layer 36 formation and as a template for subsequent monocrystalline layer 26 formation. Accordingly, layer 38 is preferably thick enough to provide a suitable template for layer 26 growth (at least one monolayer) and thin enough to allow layer 38 to form as a substantially defect free monocrystalline material.


[0036] In accordance with another embodiment of the invention, additional monocrystalline layer 38 comprises monocrystalline material (e.g., a material discussed above in connection with monocrystalline layer 26) that is thick enough to form devices within layer 38. In this case, a semiconductor structure in accordance with the present invention does not include monocrystalline material layer 26. In other words, the semiconductor structure in accordance with this embodiment only includes one monocrystalline layer disposed above amorphous oxide layer 36.


[0037] The following non-limiting, illustrative examples illustrate various combinations of materials useful in structures 20, 40, and 34 in accordance with various alternative embodiments of the invention. These examples are merely illustrative, and it is not intended that the invention be limited to these illustrative examples.



EXAMPLE 1

[0038] Monocrystalline substrate 22 is a silicon substrate oriented in the (100) direction. The silicon substrate can be, for example, a silicon substrate as is commonly used in making complementary metal oxide semiconductor (CMOS) integrated circuits having a diameter of about 200-300 mm. In accordance with this embodiment, accommodating buffer layer 24 is a monocrystalline layer of SrzBa1-zTiO3 where z ranges from 0 to 1 and the amorphous intermediate layer is a layer of silicon oxide (SiOx) formed at the interface between the silicon substrate and the accommodating buffer layer. The value of z is selected to obtain one or more lattice constants closely matched to corresponding lattice constants of the subsequently formed layer 26. The accommodating buffer layer can have a thickness of about 2 to about 100 nanometers (nm) and preferably has a thickness of about 5 nm. In general, it is desired to have an accommodating buffer layer thick enough to isolate the monocrystalline material layer 26 from the substrate to obtain the desired electrical and optical properties. Layers thicker than 100 nm usually provide little additional benefit while increasing cost unnecessarily; however, thicker layers may be fabricated if needed. The amorphous intermediate layer of silicon oxide can have a thickness of about 0.5-5 nm, and preferably a thickness of about 1 to 2 nm.


[0039] In accordance with this embodiment of the invention, monocrystalline material layer 26 is a compound semiconductor layer of gallium arsenide (GaAs) or aluminum gallium arsenide (AlGaAs) having a thickness of about 1 nm to about 100 micrometers (μm) and preferably a thickness of about 0.5 μm to 10 μm. The thickness generally depends on the application for which the layer is being prepared. To facilitate the epitaxial growth of the gallium arsenide or aluminum gallium arsenide on the monocrystalline oxide, a template layer is formed by capping the oxide layer. The template layer is preferably 1-10 monolayers of Ti—As, Sr—O—As, Sr—Ga—O, or Sr—Al—O. By way of a preferred example, 1-2 monolayers of Ti—As or Sr—Ga—O have been illustrated to successfully grow GaAs layers.



EXAMPLE 2

[0040] In accordance with a further embodiment, monocrystalline substrate 22 is a silicon substrate as described above. The accommodating buffer layer is a monocrystalline oxide of strontium or barium zirconate or hafnate in a cubic or orthorhombic phase with an amorphous intermediate layer of silicon oxide formed at the interface between the silicon substrate and the accommodating buffer layer. The accommodating buffer layer can have a thickness of about 2-100 nm and preferably has a thickness of at least 5 nm to ensure adequate crystalline and surface quality and is formed of a monocrystalline SrZrO3, BaZrO3, SrHfO3, BaSnO3 or BaHfO3. For example, a monocrystalline oxide layer of BaZrO3 can grow at a temperature of about 700° C. The lattice structure of the resulting crystalline oxide exhibits a 45° rotation with respect to the substrate silicon lattice structure.


[0041] An accommodating buffer layer formed of these zirconate or hafnate materials is suitable for the growth of a monocrystalline material layer which comprises compound semiconductor materials in the indium phosphide (InP) system. In this system, the compound semiconductor material can be, for example, indium phosphide (InP), indium gallium arsenide (InGaAs), aluminum indium arsenide, (AlInAs), or aluminum gallium indium arsenic phosphide (AlGaInAsP), having a thickness of about 1.0 nm to 10 μm. A suitable template for this structure is 1-10 monolayers of zirconium-arsenic (Zr—As), zirconium-phosphorus (Zr—P), hafnium-arsenic (Hf—As), hafnium-phosphorus (Hf—P), strontium-oxygen-arsenic (Sr—O—As), strontium-oxygen-phosphorus (Sr—O—P), barium-oxygen-arsenic (Ba—O—As), indium-strontium-oxygen (In—Sr—O), or barium-oxygen-phosphorus (Ba—O—P), and preferably 1-2 monolayers of one of these materials. By way of an example, for a barium zirconate accommodating buffer layer, the surface is terminated with 1-2 monolayers of zirconium followed by deposition of 1-2 monolayers of arsenic to form a Zr—As template. A monocrystalline layer of the compound semiconductor material from the indium phosphide system is then grown on the template layer. The resulting lattice structure of the compound semiconductor material exhibits a 45° rotation with respect to the accommodating buffer layer lattice structure and a lattice mismatch to (100) InP of less than 2.5%, and preferably less than about 1.0%.



EXAMPLE 3

[0042] In accordance with a further embodiment, a structure is provided that is suitable for the growth of an epitaxial film of a monocrystalline material comprising a II-VI material overlying a silicon substrate. The substrate is preferably a silicon wafer as described above. A suitable accommodating buffer layer material is SrxBa1-xTiO3, where x ranges from 0 to 1, having a thickness of about 2-100 nm and preferably a thickness of about 5-15 nm. Where the monocrystalline layer comprises a compound semiconductor material, the II-VI compound semiconductor material can be, for example, zinc selenide (ZnSe) or zinc sulfur selenide (ZnSSe). A suitable template for this material system includes 1-10 monolayers of zinc-oxygen (Zn—O) followed by 1-2 monolayers of an excess of zinc followed by the selenidation of zinc on the surface. Alternatively, a template can be, for example, 1-10 monolayers of strontium-sulfur (Sr—S) followed by the ZnSeS.



EXAMPLE 4

[0043] This embodiment is an example of structure 40 illustrated in FIG. 2. Substrate 22, accommodating buffer layer 24, and monocrystalline material layer 26 can be similar to those described in example 1. In addition, an additional buffer layer 32 serves to alleviate any strains that might result from a mismatch of the crystal lattice of the accommodating buffer layer and the lattice of the monocrystalline material. Buffer layer 32 can be a layer of germanium or a GaAs, an aluminum gallium arsenide (AlGaAs), an indium gallium phosphide (InGaP), an aluminum gallium phosphide (AlGaP), an indium gallium arsenide (InGaAs), an aluminum indium phosphide (AlInP), a gallium arsenide phosphide (GaAsP), or an indium gallium phosphide (InGaP) strain compensated superlattice. In accordance with one aspect of this embodiment, buffer layer 32 includes a GaAsxP1-x superlattice, wherein the value of x ranges from 0 to 1. In accordance with another aspect, buffer layer 32 includes an InyGa1-yP superlattice, wherein the value of y ranges from 0 to 1. By varying the value of x or y, as the case may be, the lattice constant is varied from bottom to top across the superlattice to create a match between lattice constants of the underlying oxide and the overlying monocrystalline material which in this example is a compound semiconductor material. The compositions of other compound semiconductor materials, such as those listed above, may also be similarly varied to manipulate the lattice constant of layer 32 in a like manner. The superlattice can have a thickness of about 50-500 nm and preferably has a thickness of about 100-200 nm. The template for this structure can be the same of that described in example 1. Alternatively, buffer layer 32 can be a layer of monocrystalline germanium having a thickness of 1-50 nm and preferably having a thickness of about 2-20 nm. In using a germanium buffer layer, a template layer of either germanium-strontium (Ge—Sr) or germanium-titanium (Ge—Ti) having a thickness of about one monolayer can be used as a nucleating site for the subsequent growth of the monocrystalline material layer which in this example is a compound semiconductor material. The formation of the oxide layer is capped with either a monolayer of strontium or a monolayer of titanium to act as a nucleating site for the subsequent deposition of the monocrystalline germanium. The monolayer of strontium or titanium provides a nucleating site to which the first monolayer of germanium can bond.



EXAMPLE 5

[0044] This example also illustrates materials useful in a structure 40 as 30 illustrated in FIG. 2. Substrate material 22, accommodating buffer layer 24, monocrystalline material layer 26 and template layer 30 can be the same as those described above in example 2. In addition, additional buffer layer 32 is inserted between the accommodating buffer layer and the overlying monocrystalline material layer. The additional buffer layer 32, a further monocrystalline material which in this instance comprises a semiconductor material, can be, for example, a graded layer of indium gallium arsenide (InGaAs) or indium aluminum arsenide (InAlAs). In accordance with one aspect of this embodiment, additional buffer layer 32 includes InGaAs, in which the indium composition varies from 0 to about 50%. The additional buffer layer 32 preferably has a thickness of about 10-30 nm. Varying the composition of the buffer layer from GaAs to InGaAs serves to provide a lattice match between the underlying monocrystalline oxide material and the overlying layer of monocrystalline material which in this example is a compound semiconductor material. Such a buffer layer is especially advantageous if there is a lattice mismatch between accommodating buffer layer 24 and monocrystalline material layer 26.



EXAMPLE 6

[0045] This example provides exemplary materials useful in structure 34, as illustrated in FIG. 3. Substrate material 22, template layer 30, and monocrystalline material layer 26 may be the same as those described above in connection with example 1.


[0046] Amorphous layer 36 is an amorphous oxide layer which is suitably formed of a combination of amorphous intermediate layer materials (e.g., layer 28 materials as described above) and accommodating buffer layer materials (e.g., layer 24 materials as described above). For example, amorphous layer 36 may include a combination of SiOx and SrzBa1-zTiO3 (where z ranges from 0 to 1),which combine or mix, at least partially, during an anneal process to form amorphous oxide layer 36.


[0047] The thickness of amorphous layer 36 may vary from application to application and may depend on such factors as desired insulating properties of layer 36, type of monocrystalline material comprising layer 26, and the like. In accordance with one exemplary aspect of the present embodiment, layer 36 thickness is about 2 nm to about 100 nm, preferably about 2-10 nm, and more preferably about 5-6 nm.


[0048] Layer 38 comprises a monocrystalline material that can be grown epitaxially over a monocrystalline oxide material such as material used to form accommodating buffer layer 24. In accordance with one embodiment, layer 38 includes the same materials as those comprising layer 26. For example, if layer 26 includes GaAs, layer 38 also includes GaAs. However, in accordance with other embodiments, layer 38 may include materials different from those used to form layer 26. In accordance with one exemplary embodiment, layer 38 is about 1 monolayer to about 100 nm thick.


[0049] Referring again to FIGS. 1-3, substrate 22 is a monocrystalline substrate such as a monocrystalline silicon or gallium arsenide substrate. The crystalline structure of the monocrystalline substrate is characterized by a lattice constant and by a lattice orientation. In a similar manner, accommodating buffer layer 24 is also a monocrystalline material and the lattice of that monocrystalline material is characterized by a lattice constant and a crystal orientation. The lattice constants of the accommodating buffer layer and the monocrystalline substrate must be closely matched or, alternatively, must be such that upon rotation of one crystal orientation with respect to the other crystal orientation, a substantial match in lattice constants is achieved. In this context the terms “substantially equal” and “substantially matched” mean that there is sufficient similarity between the lattice constants to permit the growth of a high quality crystalline layer on the underlying layer.


[0050]
FIG. 4 illustrates graphically the relationship of the achievable thickness of a grown crystal layer of high crystalline quality as a function of the mismatch between the lattice constants of the host crystal and the grown crystal. Curve 42 illustrates the boundary of high crystalline quality material. The area to the right of curve 42 represents layers that have a large number of defects. With no lattice mismatch, it is theoretically possible to grow an infinitely thick, high quality epitaxial layer on the host crystal. As the mismatch in lattice constants increases, the thickness of achievable, high quality crystalline layer decreases rapidly. As a reference point, for example, if the lattice constants between the host crystal and the grown layer are mismatched by more than about 2%, monocrystalline epitaxial layers in excess of about 20 nm cannot be achieved.


[0051] In accordance with one embodiment, substrate 22 is a (100) or (111) oriented monocrystalline silicon wafer and accommodating buffer layer 24 is a layer of strontium barium titanate. Substantial matching of lattice constants between these two materials is achieved by rotating the crystal orientation of the titanate material by 45° with respect to the crystal orientation of the silicon substrate wafer. The inclusion in the structure of amorphous interface layer 28, a silicon oxide layer in this example, if it is of sufficient thickness, serves to reduce strain in the titanate monocrystalline layer that might result from any mismatch in the lattice constants of the host silicon wafer and the grown titanate layer. As a result, in accordance with an embodiment of the invention, a high quality, thick, monocrystalline titanate layer is achievable.


[0052] Still referring to FIGS. 1-3, layer 26 is a layer of epitaxially grown monocrystalline material and that crystalline material is also characterized by a crystal lattice constant and a crystal orientation. In accordance with one embodiment of the invention, the lattice constant of layer 26 differs from the lattice constant of substrate 22. To achieve high crystalline quality in this epitaxially grown monocrystalline layer, the accommodating buffer layer must be of high crystalline quality. In addition, in order to achieve high crystalline quality in layer 26, substantial matching between the crystal lattice constant of the host crystal, in this case, the monocrystalline accommodating buffer layer, and the grown crystal is desired. With properly selected materials this substantial matching of lattice constants is achieved as a result of rotation of the crystal orientation of the grown crystal with respect to the orientation of the host crystal. For example, if the grown crystal is gallium arsenide, aluminum gallium arsenide, zinc selenide, or zinc sulfur selenide and the accommodating buffer layer is monocrystalline SrxBa1-xTiO3, substantial matching of crystal lattice constants of the two materials is achieved, wherein the crystal orientation of the grown layer is rotated by 45° with respect to the orientation of the host monocrystalline oxide. Similarly, if the host material is a strontium or barium zirconate or a strontium or barium hafnate or barium tin oxide and the compound semiconductor layer is indium phosphide or gallium indium arsenide or aluminum indium arsenide, substantial matching of crystal lattice constants can be achieved by rotating the orientation of the grown crystal layer by 45° with respect to the host oxide crystal. In some instances, a crystalline semiconductor buffer layer between the host oxide and the grown monocrystalline material layer can be used to reduce strain in the grown monocrystalline material layer that might result from small differences in lattice constants. Better crystalline quality in the grown monocrystalline material layer can thereby be achieved.


[0053] The following example illustrates a process for fabricating a semiconductor structure such as the structures depicted in FIGS. 1-3. The process starts by providing a monocrystalline semiconductor substrate comprising silicon or germanium. In accordance with a preferred embodiment of the invention, the semiconductor substrate is a silicon wafer having a (100) orientation. The substrate is preferably oriented on axis or, at most, about 4° off axis. At least a portion of the semiconductor substrate has a bare surface, although other portions of the substrate, as described below, may encompass other structures. The term “bare” in this context means that the surface in the portion of the substrate has been cleaned to remove any oxides, contaminants, or other foreign material. As is well known, bare silicon is highly reactive and readily forms a native oxide. The term “bare” is intended to encompass such a native oxide. A thin silicon oxide may also be intentionally grown on the semiconductor substrate, as an optional process step. In order to epitaxially grow a monocrystalline oxide layer overlying the monocrystalline substrate, the native oxide layer must first be removed to expose the crystalline structure of the underlying substrate. The following process is preferably carried out by molecular beam epitaxy (MBE), although other epitaxial processes may also be used in accordance with the present invention. The native oxide can be removed by first thermally depositing a thin layer of strontium, barium, a combination of strontium and barium, or other alkaline earth metals or combinations of alkaline earth metals in an MBE apparatus. In the case where strontium is used, the substrate is then heated to a temperature of about 750° C. to cause the strontium to react with the native silicon oxide layer. The strontium serves to reduce the silicon oxide to leave a silicon oxide-free surface. The resultant surface, which exhibits an ordered 2×1 structure, includes strontium, oxygen, and silicon. The ordered 2×1 structure forms a template for the ordered growth of an overlying layer of a monocrystalline oxide. The template provides the necessary chemical and physical properties to nucleate the crystalline growth of an overlying layer.


[0054] In accordance with an alternate embodiment of the invention, the native silicon oxide can be converted and the substrate surface can be prepared for the growth of a monocrystalline oxide layer by depositing an alkaline earth metal oxide, such as strontium oxide, strontium barium oxide, or barium oxide, onto the substrate surface by MBE at a low temperature and by subsequently heating the structure to a temperature of about 750° C. At this temperature a solid state reaction takes place between the strontium oxide and the native silicon oxide causing the reduction of the native silicon oxide and leaving an ordered 2×1 structure with strontium, oxygen, and silicon remaining on the substrate surface. Again, this forms a template for the subsequent growth of an ordered monocrystalline oxide layer.


[0055] Following the removal of the silicon oxide from the surface of the substrate, the substrate is cooled to a temperature in the range of about 200-800° C. and a layer of strontium titanate is grown on the template layer by molecular beam epitaxy. The MBE process is initiated by opening shutters in the MBE apparatus to expose strontium, titanium and oxygen sources. The ratio of strontium and titanium is approximately 1:1. The partial pressure of oxygen is initially set at a minimum value to grow stoichiometric strontium titanate at a growth rate of about 0.3-0.5 nm per minute. After initiating growth of the strontium titanate, the partial pressure of oxygen is increased above the initial minimum value. The overpressure of oxygen causes the growth of an amorphous silicon oxide layer at the interface between the underlying substrate and the growing strontium titanate layer. The growth of the silicon oxide layer results from the diffusion of oxygen through the growing strontium titanate layer to the interface where the oxygen reacts with silicon at the surface of the underlying substrate. The strontium titanate grows as an ordered (100) monocrystal with the (100) crystalline orientation rotated by 45° with respect to the underlying substrate. Strain that otherwise might exist in the strontium titanate layer because of the small mismatch in lattice constant between the silicon substrate and the growing crystal is relieved in the amorphous silicon oxide intermediate layer.


[0056] After the strontium titanate layer has been grown to the desired thickness, the monocrystalline strontium titanate is capped by a template layer that is conducive to the subsequent growth of an epitaxial layer of a desired monocrystalline material. For example, for the subsequent growth of a monocrystalline compound semiconductor material layer of gallium arsenide, the MBE growth of the strontium titanate monocrystalline layer can be capped by terminating the growth with 1-2 monolayers of titanium, 1-2 monolayers of titanium-oxygen or with 1-2 monolayers of strontium-oxygen. Following the formation of this capping layer, arsenic is deposited to form a Ti—As bond, a Ti—O—As bond or a Sr—O—As. Any of these form an appropriate template for deposition and formation of a gallium arsenide monocrystalline layer. Following the formation of the template, gallium is subsequently introduced to the reaction with the arsenic and gallium arsenide forms. Alternatively, gallium can be deposited on the capping layer to form a Sr—O—Ga bond, and arsenic is subsequently introduced with the gallium to form the GaAs.


[0057]
FIG. 5 is a high resolution Transmission Electron Micrograph (TEM) of semiconductor material manufactured so as to epitaxially grow single crystal SrTiO3 accommodating buffer layer 24 on silicon substrate 22. During this growth process, amorphous interfacial layer 28 is formed which relieves strain due to lattice mismatch. GaAs compound semiconductor layer 26 was then grown epitaxially using template layer 30.


[0058]
FIG. 6 illustrates an x-ray diffraction spectrum taken on a structure including GaAs monocrystalline layer 26 comprising GaAs grown on silicon substrate 22 using accommodating buffer layer 24. The peaks in the spectrum indicate that both the accommodating buffer layer 24 and GaAs compound semiconductor layer 26 are single crystal and (100) orientated.


[0059] The structure illustrated in FIG. 2 can be formed by the process discussed above with the addition of an additional buffer layer deposition step. The additional buffer layer 32 is formed overlying the template layer before the deposition of the monocrystalline material layer. If the buffer layer is a monocrystalline material comprising a compound semiconductor superlattice, such a superlattice can be deposited, by MBE for example, on the template described above. If instead the buffer layer is a monocrystalline material layer comprising a layer of germanium, the process above is modified to cap the strontium titanate monocrystalline layer with a final layer of either strontium or titanium and then by depositing germanium to react with the strontium or titanium. The germanium buffer layer can then be deposited directly on this template.


[0060] Structure 34, illustrated in FIG. 3, may be formed by growing an accommodating buffer layer, forming an amorphous oxide layer over substrate 22, and growing semiconductor layer 38 over the accommodating buffer layer, as described above. The accommodating buffer layer and the amorphous oxide layer are then exposed to an anneal process sufficient to change the crystalline structure of the accommodating buffer layer from monocrystalline to amorphous, thereby forming an amorphous layer such that the combination of the amorphous oxide layer and the now amorphous accommodating buffer layer form a single amorphous oxide layer 36. Layer 26 is then subsequently grown over layer 38. Alternatively, the anneal process may be carried out subsequent to growth of layer 26.


[0061] In accordance with one aspect of this embodiment, layer 36 is formed by exposing substrate 22, the accommodating buffer layer, the amorphous oxide layer, and monocrystalline layer 38 to a rapid thermal anneal process with a peak temperature of about 700° C. to about 1000° C. and a process time of about 5 seconds to about 10 minutes. However, other suitable anneal processes may be employed to convert the accommodating buffer layer to an amorphous layer in accordance with the present invention. For example, laser annealing, electron beam annealing, or “conventional” thermal annealing processes (in the proper environment) may be used to form layer 36. When conventional thermal annealing is employed to form layer 36, an overpressure of one or more constituents of layer 30 may be required to prevent degradation of layer 38 during the anneal process. For example, when layer 38 includes GaAs, the anneal environment preferably includes an overpressure of arsenic to mitigate degradation of layer 38.


[0062] As noted above, layer 38 of structure 34 may include any materials suitable for either of layers 32 or 26. Accordingly, any deposition or growth methods described in connection with either layer 32 or 26, may be employed to deposit layer 38.


[0063]
FIG. 7 is a high resolution TEM of semiconductor material manufactured to epitaxially grow a single crystal SrTiO3 accommodating buffer layer on silicon substrate 22. During this growth process, an amorphous interfacial layer forms as described above. Next, additional monocrystalline layer 38 comprising a compound semiconductor layer of GaAs is formed above the accommodating buffer layer and the accommodating buffer layer is exposed to an anneal process to form amorphous oxide layer 36.


[0064]
FIG. 8 illustrates an x-ray diffraction spectrum taken on a structure including additional monocrystalline layer 38 comprising a GaAs compound semiconductor layer and amorphous oxide layer 36 formed on silicon substrate 22. The peaks in the spectrum indicate that GaAs compound semiconductor layer 38 is single crystal and (100) orientated and the lack of peaks around 40° to 50° indicates that layer 36 is amorphous.


[0065] The process described above illustrates a process for forming a semiconductor structure including a silicon substrate, an overlying oxide layer, and a monocrystalline material layer comprising a gallium arsenide compound semiconductor layer by the process of molecular beam epitaxy. The process can also be carried out by the process of chemical vapor deposition (CVD), metal organic chemical vapor deposition (MOCVD), migration enhanced epitaxy (MEE), atomic layer epitaxy (ALE), physical vapor deposition (PVD), chemical solution deposition (CSD), pulsed laser deposition (PLD), or the like. Further, by a similar process, other monocrystalline accommodating buffer layers such as alkaline earth metal titanates, zirconates, hafnates, tantalates, vanadates, ruthenates, and niobates, alkaline earth metal tin-based perovskites, lanthanum aluminate, lanthanum scandium oxide, and gadolinium oxide can also be grown. Further, by a similar process such as MBE, other monocrystalline material layers comprising other III-V and II-VI monocrystalline compound semiconductors, semiconductors, metals and non-metals can be deposited overlying the monocrystalline oxide accommodating buffer layer.


[0066] Each of the variations of monocrystalline material layer and monocrystalline oxide accommodating buffer layer preferably uses an appropriate template for initiating the growth of the monocrystalline material layer. For example, if the accommodating buffer layer is an alkaline earth metal zirconate, the oxide can be capped by a thin layer of zirconium. The deposition of zirconium can be followed by the deposition of arsenic or phosphorus to react with the zirconium as a precursor to depositing indium gallium arsenide, indium aluminum arsenide, or indium phosphide respectively. Similarly, if the monocrystalline oxide accommodating buffer layer is an alkaline earth metal hafnate, the oxide layer can be capped by a thin layer of hafnium. The deposition of hafnium is followed by the deposition of arsenic or phosphorous to react with the hafnium as a precursor to the growth of an indium gallium arsenide, indium aluminum arsenide, or indium phosphide layer, respectively. In a similar manner, strontium titanate can be capped with a layer of strontium or strontium and oxygen and barium titanate can be capped with a layer of barium or barium and oxygen. Each of these depositions can be followed by the deposition of arsenic or phosphorus to react with the capping material to form a template for the deposition of a monocrystalline material layer comprising compound semiconductors such as indium gallium arsenide, indium aluminum arsenide, or indium phosphide.


[0067] The formation of a device structure in accordance with another embodiment is illustrated schematically in cross-section in FIGS. 9-12. Like the previously described embodiments referred to in FIGS. 1-3, this embodiment involves the process of forming a compliant substrate utilizing the epitaxial growth of single crystal oxides, such as the formation of accommodating buffer layer 24 previously described with reference to FIGS. 1 and 2 and amorphous layer 36 previously described with reference to FIG. 3, and the formation of a template layer 30. However, the embodiment illustrated in FIGS. 9-12 utilizes a template that includes a surfactant to facilitate layer-by-layer monocrystalline material growth.


[0068] Turning now to FIG. 9, an amorphous intermediate layer 58 is grown on substrate 52 at the interface between substrate 52 and a growing accommodating buffer layer 54, which is preferably a monocrystalline crystal oxide layer, by the oxidation of substrate 52 during the growth of layer 54. Layer 54 is preferably a monocrystalline oxide material such as a monocrystalline layer of SrzBa1-zTiO3 where z ranges from 0 to 1. However, layer 54 may also comprise any of those compounds previously described with reference layer 24 in FIGS. 1-2 and any of those compounds previously described with reference to layer 36 in FIG. 3 which is formed from layers 24 and 28 referenced in FIGS. 1 and 2.


[0069] Layer 54 is grown with a strontium (Sr) terminated surface represented in FIG. 9 by hatched line 55 which is followed by the addition of a template layer 60 which includes a surfactant layer 61 and capping layer 63 as illustrated in FIGS. 10 and 11. Surfactant layer 61 may comprise, but is not limited to, elements such as Al, In and Ga, but will be dependent upon the composition of layer 54 and the overlying layer of monocrystalline material for optimal results. In one exemplary embodiment, aluminum (Al) is used for surfactant layer 61 and functions to modify the surface and surface energy of layer 54. Preferably, surfactant layer 61 is epitaxially grown, to a thickness of one to two monolayers, over layer 54 as illustrated in FIG. 10 by way of molecular beam epitaxy (MBE), although other epitaxial processes may also be performed including chemical vapor deposition (CVD), metal organic chemical vapor deposition (MOCVD), migration enhanced epitaxy (MEE), atomic layer epitaxy (ALE), physical vapor deposition (PVD), chemical solution deposition (CSD), pulsed laser deposition (PLD), or the like.


[0070] Surfactant layer 61 is then exposed to a Group V element such as arsenic, for example, to form capping layer 63 as illustrated in FIG. 11. Surfactant layer 61 may be exposed to a number of materials to create capping layer 63 such as elements which include, but are not limited to, As, P, Sb and N. Surfactant layer 61 and capping layer 63 combine to form template layer 60.


[0071] Monocrystalline material layer 66, which in this example is a compound semiconductor such as GaAs, is then deposited via MBE, C VD, MOCVD, MEE, ALE, PVD, CSD, PLD, and the like to form the final structure illustrated in FIG. 12.


[0072] FIGS. 13-16 illustrate possible molecular bond structures for a specific example of a compound semiconductor structure formed in accordance with the embodiment of the invention illustrated in FIGS. 9-12. More specifically, FIGS. 13-16 illustrate the growth of GaAs (layer 66) on the strontium terminated surface of a strontium titanate monocrystalline oxide (layer 54) using a surfactant containing template (layer 60).


[0073] The growth of a monocrystalline material layer 66 such as GaAs on an accommodating buffer layer 54 such as a strontium titanium oxide over amorphous interface layer 58 and substrate layer 52, both of which may comprise materials previously described with reference to layers 28 and 22, respectively in FIGS. 1 and 2, illustrates a critical thickness of about 1000 Angstroms where the two-dimensional (2D) and three-dimensional (3D) growth shifts because of the surface energies involved. In order to maintain a true layer by layer growth (Frank Van der Mere growth), the following relationship must be satisfied:


δSTO>(δINTGaAs)


[0074] where the surface energy of the monocrystalline oxide layer 54 must be greater than the surface energy of the amorphous interface layer 58 added to the surface energy of the GaAs layer 66. Since it is impracticable to satisfy this equation, a surfactant containing template was used, as described above with reference to FIGS. 10-12, to increase the surface energy of the monocrystalline oxide layer 54 and also to shift the crystalline structure of the template to a diamond-like structure that is in compliance with the original GaAs layer.


[0075]
FIG. 13 illustrates the molecular bond structure of a strontium terminated surface of a strontium titanate monocrystalline oxide layer. An aluminum surfactant layer is deposited on top of the strontium terminated surface and bonds with that surface as illustrated in FIG. 14, which reacts to form a capping layer comprising a monolayer of Al2Sr having the molecular bond structure illustrated in FIG. 14 which forms a diamond-like structure with an sp3 hybrid terminated surface that is compliant with compound semiconductors such as GaAs. The structure is then exposed to As to form a layer of AlAs as shown in FIG. 15. GaAs is then deposited to complete the molecular bond structure illustrated in FIG. 16 which has been obtained by 2D growth. The GaAs can be grown to any thickness for forming other semiconductor structures, devices, or integrated circuits. Alkaline earth metals such as those in Group IIA are those elements preferably used to form the capping surface of the monocrystalline oxide layer 54 because they are capable of forming a desired molecular structure with aluminum.


[0076] In this embodiment, a surfactant containing template layer aids in the formation of a compliant substrate for the monolithic integration of various material layers including those comprised of Group III-V compounds to form high quality semiconductor structures, devices and integrated circuits. For example, a surfactant containing template may be used for the monolithic integration of a monocrystalline material layer such as a layer comprising Germanium (Ge), for example, to form high efficiency photocells.


[0077] Turning now to FIGS. 17-20, the formation of a device structure in accordance with still another embodiment of the invention is illustrated in cross-section. This embodiment utilizes the formation of a compliant substrate which relies on the epitaxial growth of single crystal oxides on silicon followed by the epitaxial growth of single crystal silicon onto the oxide.


[0078] An accommodating buffer layer 74 such as a monocrystalline oxide layer is first grown on a substrate layer 72, such as silicon, with an amorphous interface layer 78 as illustrated in FIG. 17. Monocrystalline oxide layer 74 may be comprised of any of those materials previously discussed with reference to layer 24 in FIGS. 1 and 2, while amorphous interface layer 78 is preferably comprised of any of those materials previously described with reference to the layer 28 illustrated in FIGS. 1 and 2. Substrate 72, although preferably silicon, may also comprise any of those materials previously described with reference to substrate 22 in FIGS. 1-3.


[0079] Next, a silicon layer 81 is deposited over monocrystalline oxide layer 74 via MBE, CVD, MOCVD, MEE, ALE, PVD, CSD, PLD, and the like as illustrated in FIG. 18 with a thickness of a few hundred Angstroms but preferably with a thickness of about 50 Angstroms. Monocrystalline oxide layer 74 preferably has a thickness of about 20 to 100 Angstroms.


[0080] Rapid thermal annealing is then conducted in the presence of a carbon source such as acetylene or methane, for example at a temperature within a range of about 800° C. to 1000° C. to form capping layer 82 and silicate amorphous layer 86. However, other suitable carbon sources may be used as long as the rapid thermal annealing step functions to amorphous the monocrystalline oxide layer 74 into a silicate amorphous layer 86 and carbonize the top silicon layer 81 to form capping layer 82 which in this example would be a silicon carbide (SiC) layer as illustrated in FIG. 19. The formation of amorphous layer 86 is similar to the formation of layer 36 illustrated in FIG. 3 and may comprise any of those materials described with reference to layer 36 in FIG. 3 but the preferable material will be dependent upon the capping layer 82 used for silicon layer 81.


[0081] Finally, a compound semiconductor layer 96, such as gallium nitride (GaN) is grown over the SiC surface by way of MBE, CVD, MOCVD, MEE, ALE, PVD, CSD, PLD, or the like to form a high quality compound semiconductor material for device formation. More specifically, the deposition of GaN and GaN based systems such as GaInN and AlGaN will result in the formation of dislocation nets confined at the silicon/amorphous region. The resulting nitride containing compound semiconductor material may comprise elements from groups III, IV and V of the periodic table and is defect free.


[0082] Although GaN has been grown on SiC substrate in the past, this embodiment of the invention possesses a one step formation of the compliant substrate containing a SiC top surface and an amorphous layer on a Si surface. More specifically, this embodiment of the invention uses an intermediate single crystal oxide layer that is amorphosized to form a silicate layer which adsorbs the strain between the layers. Moreover, unlike past use of a SiC substrate, this embodiment of the invention is not limited by wafer size which is usually less than 50 mm in diameter for prior art SiC substrates.


[0083] The monolithic integration of nitride containing semiconductor compounds containing group III-V nitrides and silicon devices can be used for high temperature RF applications and optoelectronics. GaN systems have particular use in the photonic industry for the blue/green and UV light sources and detection. High brightness light emitting diodes (LEDs) and lasers may also be formed within the GaN system.


[0084] FIGS. 21-23 schematically illustrate, in cross-section, the formation of another embodiment of a device structure in accordance with the invention. This embodiment includes a compliant layer that functions as a transition layer that uses clathrate or Zintl type bonding. More specifically, this embodiment utilizes an intermetallic template layer to reduce the surface energy of the interface between material layers thereby allowing for two dimensional layer by layer growth.


[0085] The structure illustrated in FIG. 21 includes a monocrystalline substrate 102, an amorphous interface layer 108 and an accommodating buffer layer 104. Amorphous interface layer 108 is formed on substrate 102 at the interface between substrate 102 and accommodating buffer layer 104 as previously described with reference to FIGS. 1 and 2. Amorphous interface layer 108 may comprise any of those materials previously described with reference to amorphous interface layer 28 in FIGS. 1 and 2. Substrate 102 is preferably silicon but may also comprise any of those materials previously described with reference to substrate 22 in FIGS. 1-3.


[0086] A template layer 130 is deposited over accommodating buffer layer 104 as illustrated in FIG. 22 and preferably comprises a thin layer of Zintl type phase material composed of metals and metalloids having a great deal of ionic character. As in previously described embodiments, template layer 130 is deposited by way of MBE, CVD, MOCVD, MEE, ALE, PVD, CSD, PLD, or the like to achieve a thickness of one monolayer. Template layer 130 functions as a “soft” layer with non-directional bonding but high crystallinity which absorbs stress build up between layers having lattice mismatch. Materials for template 130 may include, but are not limited to, materials containing Si, Ga, In, and Sb such as, for example, AlSr2, (MgCaYb)Ga2, (Ca,Sr,Eu,Yb)In2, BaGe2As, and SrSn2As2.


[0087] A monocrystalline material layer 126 is epitaxially grown over template layer 130 to achieve the final structure illustrated in FIG. 23. As a specific example, an SrAl2 layer may be used as template layer 130 and an appropriate monocrystalline material layer 126 such as a compound semiconductor material GaAs is grown over the SrAl2. The Al—Ti (from the accommodating buffer layer of layer of SrzBa1-zTiO3 where z ranges from 0 to 1) bond is mostly metallic while the Al—As (from the GaAs layer) bond is weakly covalent. The Sr participates in two distinct types of bonding with part of its electric charge going to the oxygen atoms in the lower accommodating buffer layer 104 comprising SrzBa1-zTiO3 to participate in ionic bonding and the other part of its valence charge being donated to Al in a way that is typically carried out with Zintl phase materials. The amount of the charge transfer depends on the relative electronegativity of elements comprising the template layer 130 as well as on the interatomic distance. In this example, Al assumes an sp3 hybridization and can readily form bonds with monocrystalline material layer 126, which in this example, comprises compound semiconductor material GaAs.


[0088] The compliant substrate produced by use of the Zintl type template layer used in this embodiment can absorb a large strain without a significant energy cost. In the above example, the bond strength of the Al is adjusted by changing the volume of the SrAl2 layer thereby making the device tunable for specific applications which include the monolithic integration of III-V and Si devices and the monolithic integration of high-k dielectric materials for CMOS technology.


[0089] Clearly, those embodiments specifically describing structures having compound semiconductor portions and Group IV semiconductor portions, are meant to illustrate exemplary embodiments. There are a multiplicity of other combinations and other embodiments which are possible. For example, the present invention also contemplates structures and methods for fabricating material layers which form semiconductor structures, devices and integrated circuits including other layers such as metal and non-metal layers. More specifically, the invention includes structures and methods for forming a compliant substrate which is used in the fabrication of semiconductor structures, devices and integrated circuits and the material layers suitable for fabricating those structures, devices, and integrated circuits. By using embodiments of the type described herein, it is now simpler to integrate devices that include monocrystalline layers comprising semiconductor and compound semiconductor materials as well as other material layers that are used to form those devices with other components that work better or are easily and/or inexpensively formed within semiconductor or compound semiconductor materials. This allows a device to be shrunk, the manufacturing costs to decrease, and yield and reliability to increase.


[0090] In accordance with one embodiment, a monocrystalline semiconductor or compound semiconductor wafer can be used in forming monocrystalline material layers over the wafer. In this manner, the wafer is essentially a “handle” wafer used during the fabrication of semiconductor electrical components within a monocrystalline layer overlying the wafer. Therefore, electrical components can be formed within semiconductor materials over a wafer of at least approximately 200 millimeters in diameter and possibly at least approximately 300 millimeters.


[0091] By the use of this type of substrate, a relatively inexpensive “handle” wafer overcomes the fragile nature of compound semiconductor or other monocrystalline material wafers by placing them over a relatively more durable and easy to fabricate base material. Therefore, an integrated circuit can be formed such that all electrical components, and particularly all active electronic devices, can be formed within or using the monocrystalline material layer even though the substrate itself may include a monocrystalline semiconductor material. Fabrication costs for compound semiconductor devices and other devices employing non-silicon monocrystalline materials should decrease because larger substrates can be processed more economically and more readily compared to the relatively smaller and more fragile substrates (e.g., conventional compound semiconductor wafers).


[0092] As mentioned, with laser-assisted fabrication techniques according to principles of the present invention, “high-quality” semiconductor structures such as those described above can be fabricated by employing cost effective equipment and techniques. Heretofore, in order to achieve the low crystallographic defect density levels contemplated herein, the semiconductor structure was subjected to treatment of significant duration carried out at elevated temperatures. For example, low crystallographic defect density levels have been achieved by growing the device layers at elevated temperatures (e.g., above 700° C.) or by post growth rapid thermal annealing (e.g., 900° C. for 20 seconds).


[0093] Such heating, although beneficial for healing certain kinds of defects, gives rise to impurity control issues which, if not managed effectively, can lead to the degradation of operational performance. Further, as mentioned above, growth techniques carried out heretofore have employed the use of surfactants such as aluminum and other materials to facilitate nucleation during initial stages of growth. The use of surfactants, particularly when subjected to increased temperatures has been found to introduce levels of impurities that raise concerns about the eventual operational performance of the semiconductor structure. The use of laser-assisted fabrication techniques according to principles of the present invention can be employed in place of surfactants during the various stages of semiconductor structure fabrication. For example, according to principles of the present invention, laser energy is employed to modify the surface energy of the accommodating buffer layer in various semiconductor structures described above to assist in the nucleation of monocrystalline semiconductor material to the accommodating buffer layer surface, without use of surfactants. Thus, ex-situ elements are employed to facilitate monocrystalline material deposition without employing potential impurity sources to change the chemical structure and composition of underlying layers.


[0094] Referring to FIG. 24, there is shown a flow diagram 300 of a fabrication sequence for the structures provided by FIGS. 1-23 in which irradiation is provided by a laser source at step 302 for treating at least a portion of the surface of at least one of a monocrystalline silicon substrate 304, a monocrystalline perovskite oxide film 306, and amorphous interface layer 308, prior to forming the compound semiconductor layer at step 310. Laser-assisted techniques according to principles of the present invention provide further advantages in the practical fabrication of commercially significant semiconductor structures. For example, practical constraints have required that various components or layers of semiconductor structures be fabricated in different environments, and transported at certain times, from one environment to another. For example, molecular beam epitaxy is currently the preferred method of forming an STO accommodating buffer layer used with substrates of monocrystalline silicon. As those skilled in the art will appreciate, practical molecular beam epitaxy is carried out in a dedicated, special-purpose reactor chamber. Subsequent layer-by-layer growth on top of the STO accommodating buffer layer requires that the semiconductor structure in process be removed from the molecular beam epitaxy reactor chamber. This usually results in the partially formed semiconductor structure being exposed to ambient moisture, and other substances, for example. Prior to commencing growth of the monocrystalline material, a laser, such as a continuous wave, frequency doubled Ar+ laser (Argon high and laser) is employed to preclean the STO accommodating buffer layer surface. Other types of lasers (such as Ar—F, Ar—Cl and Xe—F) are contemplated by the present invention, although it is generally preferred that the lasers employed emit ultraviolet radiation. Preferably, the same laser treatment is also used to desorb any adsorbed H2O or OH groups that may have formed on the surface of the STO accommodating buffer layer since its removal from the molecular beam epitaxy reactor chamber.


[0095] Following the precleaning and desorbing steps, and without transport to another environment, the partially formed semiconductor structure is prepared for monocrystalline material growth. After formation of any desired template layer, the same continuous wave, frequency doubled Ar+ laser is employed to energize the surface of the partially formed semiconductor structure as growth of the monocrystalline material is initiated. Laser irradiation at this point in the fabrication process promotes the surface atoms into higher energy states, such that two-dimensional growth is realized without the need of surfactant materials. In this manner, three-dimensional or “island” growth can be readily eliminated.


[0096] As fabrication continues, the monocrystalline material layer increases in thickness at a controlled rate. At a thickness less than the critical thickness for stress relief by dislocation formation, the same laser as that used above in the precleaning and desorbing steps is employed to selectively heat the underlying (e.g., STO) accommodating buffer layer. It is preferred that the single crystal STO material formed by molecular beam epitaxy is left unaltered until this latter stage in the fabrication process. Rather than subjecting the partially formed or fully formed semiconductor structure to rapid thermal annealing or other gross heating step, the continuous wave, frequency doubled Ar+ laser is employed to selectively operate on a layer, more specifically, to completely amorphous the STO accommodating buffer layer. In carrying out this step in the fabrication process, it is preferred that the laser energy output be set to a level above the bandgap energy of silicon but below the bandgap energy of the monocrystalline material, so that the underlying monocrystalline substrate selectively absorbs most, if not all of a heat energy resulting from this amorphization step when the (STO) accommodating buffer layer is completely amorphized. Growth of the monocrystalline material continues until the desired thickness is achieved. Laser operation can also be employed to anneal the growth material as well as selectively activating organometallics present in the semiconductor structure, further eliminating the need for thermal gross activation.


[0097] As seen from the above description, the use of laser-assisted fabrication techniques according to principles of the present invention reduces overall heating of the semiconductor structure by eliminating rapid thermal annealing or other gross heating methods usually associated with amorphization. Further, the use of laser-assisted fabrication techniques according to principles of the present invention selectively directs the thermal effects of the amorphizing energization to a portion of the semiconductor structure which most efficiently tolerates heating. Thus, for example, heating can be directed to portions of the semiconductor structure where impurity controls are most readily implemented.


[0098] Further advantages of laser-assisted semiconductor structure fabrication are possible, as when chemical vapor deposition is employed for material growth. In addition to the precleaning and desorbing steps described above, a laser, preferably the same laser previously employed, is used to heat or otherwise activate the growth-supporting layer and/or to crack or decompose the precursors for layer growth (such as AsH3, Ga(C2H5)3 used for certain types of noncrystalline materials). With laser-assisted activation and cracking or decomposition, chemical vapor deposition can be carried out at lower substrate temperatures.


[0099] As a further advantage, the use of laser-assisted chemical vapor deposition according to principles of the present invention enables selective deposition of the monocrystalline material over preselected regions of the underlying semiconductor structure. Deposition can be controlled with the exacting precision associated with laser irradiation processes. As will be appreciated, laser radiation energy can be applied with precision with regard to depth, as well as the two-dimensional “footprint” or surface area of the material being treated. With the present invention, highly selective deposition of monocrystalline materials can be readily achieved by directly heating the precursor material(s). Further, laser-assisted fabrication according to principles of the present invention can be employed to heal highly localized regions without requiring gross thermal treatment. Those skilled in the art will appreciate practical advantages afforded by the present invention, for example, where the semiconductor structure already contains operational devices which cannot tolerate high temperatures.


[0100] As will be appreciated, laser-assisted fabrication techniques according to the present invention can be used with processes other than chemical vapor deposition which require activation of precursor materials by incident energy. With the present invention, incident energy can be directly inputted to the precursor materials and/or the exposed surface by highly localized laser irradiation, rather than gross thermal activation using rapid thermal annealing or other techniques.


[0101] In the foregoing specification, the invention has been described with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the present invention as set forth in the claims below. Accordingly, the specification and figures are to be regarded in an illustrative rather than a restrictive sense, and all such modifications are intended to be included within the scope of present invention.


[0102] Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any element(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential features or elements of any or all the claims. As used herein, the terms “comprises,” “comprising,” or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus.


Claims
  • 1. A process for fabricating a semiconductor structure comprising: providing a monocrystalline silicon substrate having a first lattice constant; selecting a material that when properly oriented has a second lattice constant and crystalline structure such that the material can be deposited as a monocrystalline film overlying the monocrystalline silicon substrate, the second lattice constant being different than the first lattice constant; depositing a monocrystalline film of the material overlying the monocrystalline silicon substrate, the film having a thickness less than a thickness of the material that would result in strain-induced defects, the monocrystalline film being strained because the first lattice constant is different than the second lattice constant; forming an amorphous interface layer at an interface between the monocrystalline film and the monocrystalline silicon substrate, the amorphous interface layer having a thickness sufficient to relieve the strain in the monocrystalline film; selecting a compound semiconductor material having a third lattice constant that is different than the first lattice constant and that when properly oriented can be deposited on the monocrystalline film as a monocrystalline compound semiconductor layer; epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film; selecting the second lattice constant to be one of (a) intermediate to the first and third lattice constants and (b) equal to the third lattice constant; and treating at least a portion of the surface of at least one of (a) monocrystalline silicon substrate (b) monocrystalline film and (c) amorphous interface layer by irradiating with a laser radiation source.
  • 2. The process of claim 1 wherein the treating step comprises precleaning the monocrystalline film with a laser radiation source prior to deposition of the monocrystalline layer of the compound semiconductor material.
  • 3. The process of claim 2 wherein the precleaning step comprises precleaning with an ultraviolet laser radiation source.
  • 4. The process of claim 1 wherein the treating step comprises desorbing moisture from the surface irradiated.
  • 5. The process of claim 1 wherein the treating step comprises exciting an initial portion of the compound semiconductor material deposited on the monocrystalline film with the laser radiation source to promote nucleation and two-dimensional growth of the compound semiconductor material while maintaining the semiconductor structure free of surfactants.
  • 6. The process of claim 5 wherein the laser radiation source operates in the ultraviolet regime.
  • 7. The process of claim 1 wherein the treating step comprises the step of irradiating the monocrystalline film with a laser radiation source so as to convert the monocrystalline film to substantially completely amorphous material.
  • 8. The process of claim 7 wherein the step of irradiating the monocrystalline film is carried out before a thickness of the compound semiconductor material exceeds a critical thickness less than a thickness of the material that would result in strain-induced defects.
  • 9. The process of claim 1 wherein the treating step comprises the step of irradiating the monocrystalline layer so as to anneal the compound semiconductor material.
  • 10. The process of claim 1 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film is carried out utilizing chemical vapor deposition with a volatile chemical precursor to growth of the compound semiconductor material, with the treating step comprising the step of irradiating at least a portion of the precursor with a laser radiation source so as to decompose the precursor, thereby enabling growth of the compound semiconductor material at a lower temperature.
  • 11. The process of claim 1 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film includes the treating step of irradiating a preselected portion of the monocrystalline film with a laser radiation source to excite a preselected region of the monocrystalline film so as to selectively accelerate growth of the compound semiconductor material in the region of laser radiation.
  • 12. The process of claim 1 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film is carried out utilizing chemical vapor deposition with a precursor to growth of the compound semiconductor material, with the treating step comprising the step of irradiating a preselected portion of the precursor with a laser radiation source so as to selectively decompose the precursor irradiated, thereby initiating selective growth of the compound semiconductor material in the region of laser radiation.
  • 13. The process of claim 1 wherein the treating step comprises precleaning the monocrystalline film with a laser radiation source prior to deposition of the monocrystalline layer of the compound semiconductor material, the process further comprising: exciting at least a portion of the monocrystalline film with the laser radiation source, so as to render the excited portion more reactive; continuing irradiation with the laser radiation source so as to excite an initial portion of the compound semiconductor material deposited on the monocrystalline film to promote nucleation and two-dimensional growth of the compound semiconductor material while avoiding the use of surfactants; and after carrying out said continuing irradiation step, increasing the power of said laser radiation source so as to heal defects in an initial portion of the compound semiconductor material being deposited.
  • 14. The process of claim 1 further comprising forming a first template layer overlying the monocrystalline silicon substrate to nucleate the monocrystalline film.
  • 15. The process of claim 14 further comprising forming a second template layer overlying the monocrystalline film to nucleate epitaxial deposition of the monocrystalline layer.
  • 16. A process for fabricating a semiconductor structure comprising: providing a monocrystalline silicon substrate; depositing a monocrystalline perovskite oxide film overlying the monocrystalline silicon substrate, with a thickness less than a thickness of the material that would result in strain-induced defects; forming an amorphous oxide interface layer containing at least silicon and oxygen at an interface between the monocrystalline perovskite oxide film and the monocrystalline silicon substrate; epitaxially forming a monocrystalline compound semiconductor layer overlying the monocrystalline perovskite oxide film; and treating at least a portion of the surface of at least one of (a) monocrystalline silicon substrate (b) monocrystalline perovskite oxide film and (c) amorphous oxide interface layer by irradiating with a laser radiation source.
  • 17. The process of claim 16 wherein the treating step comprises precleaning the monocrystalline film with a laser radiation source prior to deposition of the monocrystalline layer of the compound semiconductor material.
  • 18. The process of claim 17 wherein the precleaning step comprises precleaning with an ultraviolet laser radiation source.
  • 19. The process of claim 16 wherein the treating step comprises desorbing moisture from the surface irradiated.
  • 20. The process of claim 16 wherein the treating step comprises the step of exciting an initial portion of the compound semiconductor material deposited on the monocrystalline film with the laser radiation source to promote nucleation and two-dimensional growth of the compound semiconductor material while avoiding the use of surfactants.
  • 21. The process of claim 20 wherein the laser radiation source operates in the ultraviolet regime.
  • 22. The process of claim 16 wherein the treating step comprises the step of irradiating the monocrystalline film with a laser radiation source so as to convert the monocrystalline film to substantially completely amorphous material.
  • 23. The process of claim 22 wherein the step of irradiating the monocrystalline film is carried out before a thickness of the compound semiconductor material exceeds a critical thickness less than a thickness of the material that would result in strain-induced defects.
  • 24. The process of claim 16 wherein the treating step comprises the step of irradiating the monocrystalline layer so as to anneal the compound semiconductor material.
  • 25. The process of claim 16 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film is carried out utilizing chemical vapor deposition with a volatile chemical precursor to growth of the compound semiconductor material, with the treating step comprising the step of irradiating at least a portion of the precursor with a laser radiation source so as to decompose the precursor, thereby enabling growth of the compound semiconductor material at a lower temperature.
  • 26. The process of claim 16 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film includes the treating step of irradiating a preselected portion of the monocrystalline film with a laser radiation source to excite a preselected region of the monocrystalline film so as to selectively accelerate growth of the compound semiconductor material in the region of laser radiation.
  • 27. The process of claim 16 wherein the step of epitaxially depositing a monocrystalline layer of the compound semiconductor material overlying the monocrystalline film is carried out utilizing chemical vapor deposition with a precursor to growth of the compound semiconductor material, with the treating step comprising irradiating a preselected portion of the precursor with a laser radiation source so as to selectively decompose the precursor portion irradiated, thereby initiating selective growth of the compound semiconductor material in the region of laser radiation.
  • 28. The process of claim 16 wherein the treating step comprises precleaning the monocrystalline film with a laser radiation source prior to deposition of the monocrystalline layer of the compound semiconductor material, the process further comprising: exciting with the laser radiation source, so as to render more reactive, at least a portion of the monocrystalline film; continuing irradiation with the laser radiation source so as to excite an initial portion of the compound semiconductor material deposited on the monocrystalline film to promote nucleation and two-dimensional growth of the compound semiconductor material while avoiding the use of surfactants; and after carrying out said continuing irradiation step, increasing the power of said laser radiation source so as to heal defects in an initial portion of the compound semiconductor material being deposited.
  • 29. The process of claim 16 further comprising forming a first template layer overlying the monocrystalline silicon substrate to nucleate the monocrystalline film.