The present invention relates to a laser processing method and, in particular, to a laser processing method for forming an object to be processed with a through hole.
Known as a conventional laser processing method is one comprising converging laser light at a sheet-like object to be processed so as to form a modified region within the object and then etching the object so as to remove the modified region, thereby forming the object with a through hole along a thickness direction (see, for example, Patent Literature 1).
Patent Literature 1: Japanese Patent Application Laid-Open No. 2004-351494
There is a case where the above-mentioned laser processing method patterns an etch resist film, which is resistant to etching, on an outer surface of the object before the etching. That is, the etch resist film is produced so as to cover the whole area of the outer surface of the object. There is a case where the etch resist film is thereafter exposed to light and so forth, so as to form an opening for infiltrating an etchant into the modified region in an area corresponding to a denatured layer in the etch resist film. This can restrain the opening side of the resulting through hole from widening in excess by etching, for example, whereby the through hole can be formed accurately. In this case, however, the processing may become complicated and cumbersome, since the step of patterning by exposure to light or the like is additionally necessary as mentioned above.
It is therefore an object of the present invention to provide a laser processing method which can accurately form a through hole and facilitate the processing.
One aspect of the present invention relates to a laser processing method. This laser processing method is a laser processing method of converging laser light into an object to be processed made of silicon so as to form a modified region and etching the object along the modified region so as to form the object with a through hole, the method comprising an etch resist film producing step of producing an etch resist film resistant to etching on an outer surface of the object; a laser light converging step of converging the laser light at the object after the etch resist film producing step so as to form the modified region along a part corresponding to the through hole in the object and converging the laser light at the etch resist film so as to form a defect region along a part corresponding to the through hole in the etch resist film; and an etching step of etching the object after the laser light converging step so as to advance the etching selectively along the modified region and form the through hole.
This laser processing method converges the laser light at the etch resist film, so as to ablate the etch resist film along a part corresponding to the through hole, thereby forming a defect region (damaged region) in this part. Therefore, in the subsequent etching step, an etchant infiltrates from the defect region of the etch resist film into the modified region, so as to advance the etching selectively along the modified region. Hence, when producing the etch resist film on the outer surface of the object, a patterning process by exposure to light or the like is unnecessary, thus making it possible to form the through hole accurately and facilitate the processing.
The object to be processed may be shaped like a sheet having a main face in a (100) plane, the through hole may tilt with respect to a thickness direction of the object, and the etching step may perform anisotropic etching as the etching. This can favorably form the object with the through hole tilted with respect to the thickness direction.
The method may further comprise a step of removing the defect region of the etch resist film by etching the etch resist film after the laser light converging step before the etching step. This can reliably infiltrate the etchant into the modified region in the etching step.
The method may be a laser processing method for forming the object with a plurality of through holes, further comprising an insulating film producing step of producing an insulating film on an inner face of the through holes in the object after the etching step. When forming a plurality of through-hole electrodes by embedding a conductor in each of a plurality of through holes, for example, this can secure insulation between the through-hole electrodes adjacent to each other.
The laser processing method in accordance with the present invention can accurately form a through hole and facilitate the processing.
[
[
[
[
[
[
[
[
[
[
[
[
In the following, preferred embodiments of the present invention will be explained in detail with reference to the drawings. In the following explanations, the same or equivalent constituents will be referred to with the same signs while omitting their overlapping descriptions.
The laser processing method in accordance with an embodiment converges laser light into an object to be processed, so as to form a modified region. Therefore, the forming of the modified region will firstly be explained in the following with reference to
As illustrated in
In the laser processing device 100, the laser light L emitted from the laser light source 101 changes the direction of its optical axis by 90° with the dichroic mirror 103 and then is converged by the condenser lens 105 into the object 1 mounted on the support table 107. At the same time, the stage 111 is shifted, so that the object 1 moves relative to the laser light L along a part to form a modified region 5. This forms a modified region in the object 1 along the part 5.
As illustrated in
The converging point P is a position at which the laser light L is converged. The part 5 may be curved instead of being straight, shaped into a three-dimensional curved or planar surface form, or specified in terms of coordinates. The modified region 7 may be formed either continuously or intermittently. The modified region 7 may be formed like lines or dots. It will be sufficient if the modified region 7 is formed at least within the object 1. There are cases where fractures are formed from the modified region 7 acting as a start point, and the fractures and modified region 7 may be exposed at outer surfaces (the front face, rear face, and outer peripheral face) of the object 1.
Here, the laser light L is absorbed in particular in the vicinity of the converging point within the object 1 while being transmitted therethrough, whereby the modified region 7 is formed in the object 1 (i.e., internal absorption type laser processing). In the case of forming a removing part such as a hole or groove by melting it away from the front face 3 (surface absorption type laser processing), the processing region gradually progresses from the front face 3 side to the rear face side in general.
The modified region 7 in accordance with this embodiment means regions whose physical characteristics such as density, refractive index, and mechanical strength have attained states different from those of their surroundings. Examples of the modified region 7 include molten processed regions, crack regions, dielectric breakdown regions, refractive index changed regions, and their mixed regions. Further examples of the modified region 7 include an area where the density has changed from that of an unmodified region in a material of the object 1 and an area formed with a lattice defect (which may collectively be referred to as a high-density transitional region).
The molten processed regions, refractive index changed regions, areas where the modified region has a density different from that of the unmodified region, or areas formed with a lattice defect may further incorporate a fracture (cut or microcrack) therewithin or at an interface between the modified region 7 and an unmodified region. The incorporated fracture may be formed over the whole surface of the modified region 7 or in only a part or a plurality of parts thereof. Examples of the object 1 include those containing or constituted by silicon.
Here, this embodiment forms the object 1 with the modified region 7 and then etches the object 1, so as to advance the etching selectively along fractures (also known as cracks, microcracks, cuts, and the like; hereinafter simply referred to as “fractures”) included in or extending from the modified region 7, thereby removing a part extending along the modified region 7 in the object 1.
In the etching in this embodiment, for example, a capillary action or the like is utilized so that fractures included in or extending from the modified region 7 are impregnated with an etchant, so as to advance the etching along fracture surfaces. This advances the etching selectively at a higher etching rate along the fractures in the object 1 and removes them. Also, by utilizing the characteristic feature that the etching rate of the modified region 7 itself is high, the etching is selectively advanced along the modified region 7, so as to remove it.
Examples of the etching include a case where the object 1 is immersed in the etchant (dipping) and a case where the object 1 is coated with the etchant while being rotated (spin etching). The etching herein encompasses isotropic etching and anisotropic etching.
The isotropic etching is applicable to relatively thin objects to be processed (having a thickness of 10 μm to 100 μm, for example), so that the etching can advance isotropically independent of the crystal orientation and the modified region. When a fracture is exposed to the front face in this case, the etchant travels through the fracture to wet the inside, so that the whole surface in the thickness direction becomes a start point for the modified region, whereby a chip etched such that its cut surface is depressed into a semicircular form can be taken out. On the other hand, the anisotropic etching is applicable not only to relatively thin objects to be processed but also to thick ones (having a thickness of 800 μm to 100 μm, for example). In this case, even when the surface to be formed with the modified region differs from its plane direction, the etching can be advanced along the modified region. That is, the anisotropic etching herein enables not only the etching of the plane direction in conformity to the crystal orientation, but also the etching independent of the crystal orientation.
The laser processing method in accordance with an embodiment of the present invention will now be explained in detail.
As illustrated in
As illustrated in
The following explanation will assume the thickness direction of the object 1 (irradiation direction of the laser light L) to be the Z direction, a direction to which the parts 5 (through holes 24) tilt with respect to the thickness direction to be the X direction, and a direction perpendicular to the X and Z directions to be the Y direction.
First, when processing the object 1 in this embodiment, the object 1 is put into a furnace having an internal temperature of 1000° C., for example, so as to oxidize its whole surface by wet oxidation. This produces an oxide film 22 as an etch resist film resistant to etching on outer surfaces (at least the front face 3 and rear face 21) of the object as illustrated in
Subsequently, the object 1 is mounted and held on the mount table with the front face 3 facing up. Then, as illustrated in
Next, the position of the converging point is moved toward the front face 3 in the Z direction, so as to shift the converging point at a position near the rear face 21 of the object 1 in the Z direction, and thereafter the above-mentioned X-direction scan is performed. As a consequence, the laser light L converges at the object 1 while passing through the oxide film 22 on the front face 3 side, whereby a modified region 7 joining with the existing defect region 22b is formed on the rear face 21 side of the object 1. Here, since spot irradiation is performed with pulsed laser light as the laser light L, the resulting modified region 7 is constituted by modified spots. Thus formed modified region 7 incorporates therein fractures generated from the modified region 7 (ditto in the following modified regions).
Subsequently, the above-mentioned X-direction scan is repeatedly performed while progressively changing the position of the converging point in the Z direction from the rear face 21 side to the front face 3 side in the object 1. This forms modified regions 7 joining with each other along the part corresponding to the through hole 24 within the object 1. That is, the modified regions 7 tilted with respect to the Z direction along the (111) plane of the object 1 are formed within the object 1.
Then, as illustrated in
Here, as illustrated in
Next, as illustrated in
Anisotropic etching is performed as the etching in this embodiment, while the (111) plane of the object 1 is harder to etch (exhibits a lower etching rate). Therefore, when the modified regions 7 extend along the (111) plane as in this embodiment, the etching favorably advances along the modified regions 7. Also, the inner face of the through hole 24 becomes a smooth surface with less irregularities, while the cross section of the through hole 24 attains a rectangular (diamond) form.
Next, as illustrated in
As in the foregoing, this embodiment forms the oxide film 22 on the front face 3 and rear face 21 by oxidizing the whole surface of the object 1. Then, it performs laser processing for forming the defect region 22b in the oxide film 22 on the rear face 21 side, the modified regions 7 within the object 1, and the defect region 22b in the oxide film 22 on the front face 3 side. Hence, in the subsequent etching, while the etchant reliably enters from the defect regions 22b of the oxide film 22 as base points, the etching advances selectively along the modified regions 7.
Therefore, a conventional step of patterning by exposure to light or the like is unnecessary in this embodiment for forming the oxide film 22 on the front face 3 and rear face 21 of the object 1, whereby the through hole 24 can be formed accurately, while the processing can be facilitated. This can further restrain the opening side of the through hole 24 from widening and the modified region 7 from being etched in excess and thereby increasing the cross-sectional area of the through hole 24 and so forth, whereby the form and size of the through hole 24 can be controlled favorably. The oxide film 22 can also inhibit the object 1 from reducing the thickness upon etching and keep the surface accuracy in the front face 3 and rear face 21.
In this embodiment, as mentioned above, the object 1 is shaped like a sheet having the front face 3 and rear face 21 in (100) planes and thus is easier to etch in the tilted direction of the through hole 24 (i.e., a direction along the (111) plane) by anisotropic etching. Therefore, this embodiment can favorably form the object 1 with the tilted through hole 24.
As mentioned above, this embodiment produces the oxide film 26 as an insulating film on the inner face of the through hole 24. This can fully secure insulation between the through-hole electrodes 30 adjacent to each other.
This embodiment converges the laser light L at the oxide film 22 so as to generate the defect regions 22b, which are entrances for the etchant into the modified regions 7, in the oxide film 22 and perform patterning as mentioned above and thus can also be applied easily for forming the oxide film 22 thicker.
Recently, as integration has been becoming higher, there have been stronger demands for developing interposers having fine wiring pitches. In this regard, this embodiment, which can form the through-hole electrodes 30 tilted with respect to the Z direction, exhibits the following operations and effects. That is, when attaining a fine wiring pitch, the electrode pad 29 on the front face 3 side and the electrode pad 29 on the rear face 21 side can be connected directly to each other, so as to secure a wiring width sufficiently, thereby preventing the electric resistance from increasing.
This embodiment can repeatedly perform the X-direction scan while changing the converging point position in the Y direction (laser processing on the XY plane) and repeatedly perform the same while changing the converging point position in the Z direction, so as to form modified regions 7 corresponding to a plurality of through holes 24. The method may repeatedly perform the X-direction scan while changing the converging point position in the Z direction (laser processing on the XZ plane) and repeatedly perform the same while changing the converging point position in the Y direction. The method may form a modified region 7 corresponding to one through hole 24 by irradiation with the laser light L while appropriately moving the converging point in the X, Y, and Z directions and repeatedly perform the same by the number corresponding to that of through holes 24.
Though a preferred embodiment of the present invention has been explained in the foregoing, the present invention is not limited thereto but may be modified or applied to others within the scope not changing the gist recited in each claim.
For example, the laser light entrance surface for forming the modified regions is not limited to the front face 3 of the object 1, but may be the rear face 21 of the object 1. Though the above-mentioned embodiment produces the oxide film 22 as an etch resist film, a nitride film may be formed. The etch resist film may be anything as long as it is resistant to the etchant used in the etching.
After producing the oxide film 22 before etching, the oxide film 22 may be etched separately, so as to remove the defect regions 22b. This allows the etchant to infiltrate reliably into the modified regions 7 in the etching for the object 1 in a later stage, whereby the through holes 24 can be formed accurately. Though the above-mentioned embodiment forms the defect region 22b by one scan of the oxide film 22, the scan may be performed a plurality of times depending on the thickness of the oxide film 22.
The on/off irradiation with the laser light L in the above-mentioned embodiment may be performed not only by controlling the on/off of the emission of the laser light L, but also by opening/closing a shutter disposed on the optical path of the laser light L or by masking on/off the front face 3 of the object 1, for example. Further, the intensity of the laser light L may be controlled between an intensity at a threshold for forming the modified regions 7 (processing threshold) or higher and an intensity lower than the processing threshold.
Industrial Applicability
The laser processing method of the present invention can form through holes accurately and facilitate the processing.
Reference Signs List
1 . . . object to be processed; 3 . . . front face (outer surface; main face); 7 . . . modified region; 21 . . . rear face (outer surface; main face); 22 . . . oxide film (etch resist film); 22b . . . defect region; 24 . . . through hole; 26 . . . oxide film (insulating film); L . . . laser light; P . . . converging point
Number | Date | Country | Kind |
---|---|---|---|
2010-167410 | Jul 2010 | JP | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/JP2011/066323 | 7/19/2011 | WO | 00 | 2/6/2012 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2012/014712 | 2/2/2012 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
4325182 | Tefft et al. | Apr 1982 | A |
6424048 | Umetsu et al. | Jul 2002 | B1 |
6992026 | Fukuyo et al. | Jan 2006 | B2 |
7033519 | Taylor et al. | Apr 2006 | B2 |
7132054 | Kravitz et al. | Nov 2006 | B1 |
8257603 | Logunov et al. | Sep 2012 | B2 |
8541319 | Shimoi et al. | Sep 2013 | B2 |
20020151169 | Umetsu et al. | Oct 2002 | A1 |
20030235385 | Taylor et al. | Dec 2003 | A1 |
20050272223 | Fujii et al. | Dec 2005 | A1 |
20060219676 | Taylor et al. | Oct 2006 | A1 |
20070023851 | Hartzell et al. | Feb 2007 | A1 |
20090013724 | Koyo et al. | Jan 2009 | A1 |
20100136766 | Sakamoto et al. | Jun 2010 | A1 |
20120103679 | Yamamoto et al. | May 2012 | A1 |
20120107994 | Taya et al. | May 2012 | A1 |
20120125893 | Shimoi et al. | May 2012 | A1 |
20120261177 | Yamamoto et al. | Oct 2012 | A1 |
20120308765 | Nukaga et al. | Dec 2012 | A1 |
20120322232 | Holden | Dec 2012 | A1 |
20120322242 | Lei et al. | Dec 2012 | A1 |
20130029092 | Wakioka | Jan 2013 | A1 |
20130029093 | Wakioka | Jan 2013 | A1 |
20130143381 | Kikukawa | Jun 2013 | A1 |
20130309445 | Nukaga et al. | Nov 2013 | A1 |
Number | Date | Country |
---|---|---|
1294540 | May 2001 | CN |
1473087 | Feb 2004 | CN |
1538195 | Oct 2004 | CN |
4-150212 | May 1992 | JP |
7-40482 | May 1995 | JP |
10-202878 | Aug 1998 | JP |
2873937 | Jan 1999 | JP |
2000-246475 | Sep 2000 | JP |
2002-210730 | Jul 2002 | JP |
2004-128445 | Apr 2004 | JP |
2004-136358 | May 2004 | JP |
2004-160618 | Jun 2004 | JP |
2004-223586 | Aug 2004 | JP |
2004-304130 | Oct 2004 | JP |
2004-351494 | Dec 2004 | JP |
2004-359475 | Dec 2004 | JP |
2005-1211 | Jan 2005 | JP |
2005-74663 | Mar 2005 | JP |
2005-121915 | May 2005 | JP |
2005-121916 | May 2005 | JP |
2005-144586 | Jun 2005 | JP |
2005-144622 | Jun 2005 | JP |
2005-152693 | Jun 2005 | JP |
2005-169993 | Jun 2005 | JP |
2005-206401 | Aug 2005 | JP |
2005-208175 | Aug 2005 | JP |
2005-306702 | Nov 2005 | JP |
2005-351774 | Dec 2005 | JP |
2006-176355 | Jul 2006 | JP |
2006-290630 | Oct 2006 | JP |
2006-352171 | Dec 2006 | JP |
2007-36758 | Feb 2007 | JP |
2007-101833 | Apr 2007 | JP |
2009-267247 | Nov 2009 | JP |
2010-142837 | Jul 2010 | JP |
0050198 | Aug 2000 | WO |
Entry |
---|
Andrius Marcinkevi{hacek over (c)}ius, et al., “Femtosecond laser-assisted three-dimensional microfabrication in silica”, Mar. 1, 2001, Optics Letters, vol. 26, No. 5, p. 277-279. |
U.S. Office Action dated Mar. 13, 2013 that issue in U.S. Appl. No. 13/388,717 including Double Patenting Rejections on pp. 4-5. |
Number | Date | Country | |
---|---|---|---|
20120135606 A1 | May 2012 | US |