Abstract
A lithographic method using an ultra-fine probe needle in which a base end of a nanotube is fastened to a holder with the tip end of the nanotube protruded from the holder. The tip end of the thus obtained nanotube probe needle is brought to contact a sample surface, a voltage is applied across the probe needle and sample, and the probe needle is moved while the sample substance in the area of contact of the probe needle is removed by the application of the voltage, thus forming a groove-form pattern on the sample surface.
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to a lithographic method that forms ultra-fine groove-form patterns in samples of electrical functional films, optical functional films, resist films, mask-forming films, and the like and more particularly to lithographic method using an ultra-fine probe needle capable of ultra-fine working, which uses an AFM cantilever, nanotube, etc., with a nano-size tip end diameter as a probe needle and forms groove-form patterns with an extremely small groove width in samples.




2. Prior Art




Generally, a lithographic method utilizing a photoresist and a mask (also called an exposure image-drawing method) is used in order to form circuit patterns on semiconductor chips. In this lithographic method, as shown in

FIG. 16

, a wafer is cut from a single crystal in steps (a) and (b). This wafer is used as a substrate


100


, and in step (c) a photoresist is dropped onto this substrate


100


while the substrate is rotated on a spinner, thus forming a photoresist film


102


on the surface of a substrate


100


in step (d).




A mask


104


corresponding to a photographic negative is superimposed on the surface of this photoresist film


102


in step (e), and the photoresist film


102


is exposed from above. The mask


104


is formed by patterning opaque parts


108


in a substrate film


106


. These opaque parts


108


prevent the photoresist film


102


from sensing light. When developed, the exposed parts


110


are removed in step (f), while the unexposed parts


112


remain. Conversely, there may be cases in which the unexposed parts are removed. Next, a diffusion layer


114


is formed in the exposed parts


110


by means of a diffusion treatment in step (g), and the unexposed parts


112


are removed in step (h), so that the semiconductor chip


116


is completed. Complex semiconductor patterns are formed by repeating these steps.




Since light is utilized in such an exposure system, the light that passes through the mask is diffracted in the areas of the opaque parts, thus lowering the resolution of the pattern. As the pattern of the mask becomes finer, this diffraction is increased, so that the resolution drops even more abruptly. Techniques in which the exposure wavelength is shortened have been developed in order to increase the resolution. First, development moved from the near ultraviolet of ultra-high-pressure mercury lamps to the far ultraviolet of excimer lasers. However, even in the case of promising excimer laser exposure, the resolution is only about 300 to 400 nm. In semiconductors, there is a demand for further increases in density and speed, and ultra-fine working in the range of 1 nm to 100 nm is impossible using conventional methods.




Accordingly, X-ray exposure techniques utilizing X-rays with a wavelength of approximately 0.1 nm have come to the fore. Although there are no problems in terms of obtaining a high resolution, lenses cannot be used for the directional control of X-rays, and reflection control by means of concave surfaces or convex surfaces is also difficult. Furthermore, there are also problems in terms of the parallel orientation of X-rays. In cases where an ordinary electron beam excitation mode is used as an X-ray source, the intensity of the X-rays is weak. On the other hand, in the case of a plasma X-ray source or SOR light source, the scale of the apparatus is large, so that adaptation for practical use is difficult.




Electron beam exposure has been developed in order to solve such difficulties. Since electron beams have a short wavelength, the resolution is extremely high, and such systems have good operability, as in the case of electron microscopes. On the other hand, however, such systems are inconvenient in that the exposure treatment must be performed in a vacuum. Electron beams also suffer from a drawback in that such beams are scattered in a photoresist, so that the electron beam itself spreads. Furthermore, in the case of electron beams, the energy of the electrons is high; accordingly, such a technique also suffers from the drawback of creating defects in the semiconductor that is worked.




SUMMARY OF THE INVENTION




Accordingly, the object of the present invention is to provide a lithographic technique with a high resolution that is completely separate from the concept of conventional exposure treatments using electromagnetic waves or electron beams and makes it possible to draw ultra-fine groove patterns with a groove width of several nanometers to several hundred nanometers on samples such as high-function films, resist films and mask-forming films, etc.




The above object is accomplished by unique steps of the present invention for a lithographic method that forms groove-form patterns on a sample surface (or on a surface of an object), and the unique steps of the present invention comprises the steps of:




causing a tip end of a probe needle to contact a surface of a sample (or an object) either continuously or intermittently, the probe needle being an ultra-fine probe needle with a nano-size tip end diameter,




applying a voltage across the probe needle and sample, and




causing the probe needle to move while removing a substance that makes the sample at a probe needle contact area by an application of said voltage.




In this method, the ultra-fine probe needle is a nanotube probe; and this nanotube probe is obtained by fastening a base end portion of a nanotube to a holder with a tip end portion of the nanotube being caused to protrude from the holder.




In this nanotube probe, the holder is a pyramid portion of a cantilever for AFM use. The pyramid portion is a portion protruding from the cantilever and the shape of the pyramid is free and contains all desired protruding shapes.




Also, the sample or an object on which the groove-form patterns are made is a lithographable matter such as an organic film, other organic matter and an inorganic matter, and a voltage is applied across the probe needle and this organic film so that the probe needle is used as a cathode.




In the method of the present invention, the groove width and groove depth of the groove-form pattern are controlled by adjusting the scanning speed of the probe needle and the applied voltage.




Furthermore, the organic film can be an electrical or optical functional film, a mask-forming film, or a resist film formed on a substrate. Also, the organic film can be a polysilane film.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is a schematic perspective view of the formation of a groove pattern in an organic film according to the present invention;





FIG. 2

is a control diagram showing the control of the movement of the nanotube probe needle;





FIG. 3

is a perspective view of the essential portion of a cantilever for AFM use;





FIG. 4

is a perspective view of a nanotube;





FIG. 5

is a process diagram in which the nanotube is fastened to the holder;





FIG. 6

is a process diagram in which the nanotube is fastened to the holder;





FIG. 7

is a process diagram in which the nanotube is fastened to the holder;





FIG. 8

is a sectional view of the essential portion in

FIG. 7

;





FIG. 9

is a sectional view of another method of fastening the nanotube;





FIG. 10

is a photograph of a nanotube probe in which the nanotube is fastened in place by means of a coating film;





FIG. 11

is a sectional view of a sample;





FIG. 12

is a structural formula of an organic polysilane;





FIG. 13

is a structural formula of a PMPS (polymethylphenylsilane);





FIG. 14

is a photograph of a sample which has grooves formed by the lithographic method shown in

FIG. 1

;





FIG. 15

is a sectional view of one of the grooves shown in

FIG. 14

; and





FIG. 16

shows a conventional lithographic method using a photoresist and mask.











DETAILED DESCRIPTION OF THE INVENTION




In order to develop lithographic techniques with a resolution that allows a groove width of several nanometers to several hundred nanometers, attention has been focused on the utilization of nanotube probe needles, AFM probe needles and STM probe needles, etc., with an emphasis on carbon nanotubes, and nano-scale lithographic techniques (hereafter referred to as “nano-lithography”) have now been realized. In particular, it has now been concluded that nanotube probe needles have the highest resolution as a result of their extremely small tip end curvature radius.




The present inventors have already disclosed SPM (scanning probe microscopes) devices, e.g., AFM (atomic force microscopes) devices and STM (tunnel microscopes) devices in Japanese Patent Application Nos. H10-376642, H10-378548, H 11-116939 and H11-116940.




The reasons for the preeminence of nanotubes as lithographic probe needles are as follows: specifically, nanotubes were first discovered as carbon nanotubes. Carbon nanotubes (also called “CNT”) have diameters ranging from approximately one (1) nanometer to several tens of nanometers. Furthermore, the axial lengths of such nanotubes range from nano-size to micro-size. Accordingly, if nanotubes with such a high aspect ratio are used as SPM probe needles, the surface structures of samples can be detected with a high resolution on the atomic level.




Following the discovery of carbon nanotubes, BCN (Boron Carbon Nitride) type nanotubes were synthesized. For example, a mixed powder of amorphous boron and graphite is packed into a graphite rod, and is evaporated in nitrogen gas. Alternatively, a sintered BN (Boron Nitride) rod is packed into a graphite rod, and is evaporated in helium gas. As still another alternative, BC


4


N (Boron 4-Carbon Nitride) is formed into an anode, graphite is used as a cathode, and an arc discharge is performed in helium gas. BCN type nanotubes in which some of the C (Carbon) atoms in CNT are replaced by B atoms and N atoms have been synthesized by these methods.




Furthermore, BN (Boron Nitride) type nanotubes have also been synthesized. These are nanotubes that contain almost no C atoms. For example, CNT and powdered B


2


O


3


are placed in a crucible and heated in nitrogen gas. As a result, a BN type nanotube in which almost all of the C atoms in the CNT are replaced by B atoms and N atoms is synthesized.




Both BCN type nanotubes and BN type nanotubes have material structures that are more or less similar to that of CNT; as a result, the ratio of the axial length to the diameter, i.e., the aspect ratio, is extremely high. Accordingly, not only carbon nanotubes, but also nanotubes in general such as BCN type nanotubes and BN type nanotubes, etc., can be used as the nanotube of the present invention. However, surface coating and doping of the metal surface may be performed in order to ensure electrical conductivity.




Assuming that nanotubes can not only detect indented and projecting structures in sample surfaces, but also remove atoms from the sample surfaces, then it should be possible to form grooves by moving and removing atoms from the surfaces of samples by means of nanotubes, thus making it possible to draw patterns consisting of grooves. Furthermore, the groove width in this case depends on the diameter of the nanotube used; if a nanotube with a diameter of 1 nm is used, then it should be possible to reduce the groove width to an extremely small value of around a few nanometers at the smallest. The lithographic method using an ultra-fine probe needle provided by the present invention was realized on the basis of this idea.




Probe needles used for ultra-fine working are not limited to nanotubes; AFM cantilevers and STM probe needles can also be used. Since these probe needles are small enough to image the distribution of atoms on sample surfaces, these needles can also form groove patterns on the nano-scale when used as lithographic probe needles. The following description will use the most effective nanotube probe needles as an example; however, this description can also be applied to the other probe needles mentioned above.




Next, the inventors investigated methods for removing atoms by means of nanotubes.




Utilizing the AFM contact mode or tapping mode, a nanotube was caused to contact a sample surface, and the nanotube probe needle was moved while a voltage was applied across the nanotube and sample. When this surface was observed in AFM mode, grooves were confirmed on the surface of the sample or the object.




The sample on which the present invention is applied contains all substances that are lithgraphable by the present invention; and especially the sample includes inorganic matters and organic matters.




In cases where the sample consists of an organic substance such as an organic polysilane, grooves are formed on the sample surface when a voltage is applied across the nanotube and sample so that the nanotube is caused to act as a cathode. Furthermore, since grooves are formed when a current flows, it appears that the Si—Si bonds are broken by electron injection, and that atoms or groups of atoms that are thus cut are released into space.




If a resist film is used as the sample, any desired groove pattern can be cut in this resist film, and nano-lithography with a groove width of several nanometers to several tens of nanometers can be realized depending on the diameter of the nanotube. Furthermore, in cases where a mask is used as the sample, a mask can be realized by coating a substrate film with an opaque film, and then forming a groove pattern in this opaque film by means of a nanotube. Furthermore, in cases where an electrical functional film or optical functional film is used as the sample, any desired pattern can be formed, so that nano-scale devices can be manufactured. In addition, nano-lithography has been perfected in which any type of film may be used as a sample, and in which nano-scale groove patterns can be formed in this sample.




Next, embodiments of the lithographic method using an ultra-fine probe needle of the present invention will be described in detail with reference to the accompanying drawings.





FIG. 1

is a schematic perspective showing the formation of a groove pattern in an organic film. The reference numeral


2


is a substrate consisting of single-crystal silicon, and an organic film


4


consisting of an organic substance is formed on the surface of the substrate


2


. A sample


5


consists of the substrate


2


and organic film


4


. The reference numeral


6


is an AFM cantilever,


8


is a pyramid-form holder formed from silicon, and


10


is a metal film consisting of Au, etc., which is vacuum-evaporated on the surface of the holder


8


. A nanotube


12


is fastened to the surface of the holder


8


. The reference numeral


14


is a DC power supply.




The cathode of the DC power supply


14


with a voltage of E is connected to the cantilever


6


, so that the metal film


10


of the holder


8


is formed into a cathode via a conductive film. Furthermore, the anode of the DC power supply


14


is connected to the substrate


2


and grounded. Accordingly, a negative voltage −E (V) is applied to the holder


8


relative to the substrate


2


which is at 0 (V). This E (V) is called “bias voltage”. When the cantilever


6


is moved in this state, i.e., in the contact mode, the atoms forming the organic film at the tip end of the nanotube probe needle


12


are released into space, so that a groove


16


with a groove depth of D and a groove width of W is formed in the organic film


4


.





FIG. 2

is a diagram showing the control of the movement of the nanotube probe needle. The nanotube probe needle


12


is fastened to a pyramid-form holder


8


, and this holder


8


is disposed on the tip end of the cantilever


6


. A substrate


18


is disposed behind the cantilever


6


. The cantilever


6


, holder


8


, nanotube probe needle


12


and substrate


18


are integrated to form a nanotube probe


20


.




A sample


5


is placed on a sample stand


21


. The sample


5


is driven in the X, Y and Z directions by an XYZ scanning circuit


30


. In

FIG. 2

, the reference numeral


24


is a semiconductor laser apparatus,


26


is a reflective mirror,


28


is a two-section light detector,


32


is an AFM display device, and


34


is a Z-axis detection circuit.




The nanotube probe needle


12


is moved in the Z direction until the needle


12


contacts the surface of the sample


5


. The laser beam LB from the semiconductor laser apparatus


24


is directed onto the back surface of the cantilever


6


, and the reflected light of this laser beam is again reflected by the reflective mirror


26


, so that the light is caused to be incident on the two-section light detector


28


. To describe

FIG. 2

in terms of an AFM device, the cantilever


6


is displaced upward and downward as the nanotube probe needle


12


is scanned in the X and Y directions, and the amount of displacement of the cantilever


6


in the Z direction is detected from the difference in the quantities of light detected by the detectors


28




a


and


28




b


. The amount of Z axis displacement is calculated by a Z axis detection circuit


34


, and this amount of Z axis displacement is displayed by an AFM display device


32


.




In the present invention, the sample


5


is moved in the X and Y directions while the nanotube probe needle


12


is caused to contact the surface of the organic film


4


either continuously or intermittently, thus forming the groove


16


shown in FIG.


1


. The voltage E applied to the nanotube and the movement speed in the X and Y directions may be adjusted in order to obtain the desired groove width W and groove depth D.





FIG. 3

is a perspective view of the essential portion of the AFM cantilever. An electrode


7


is formed on the side surface of the cantilever


6


, and a metal film


10


consisting of Au, etc., is formed on the surface of the pyramid-form holder


8


. The electrode


7


and metal film


10


are in an electrically continuous state. Since silicon is highly insulating, a metal film is formed on the surface of the holder


8


so that a voltage can be applied.




As seen from

FIG. 4

, a perspective view of the nanotube, the diameter d of a nanotube ranges from approximately one (1) nanometer to several tens of nanometers, and the axial length L ranges from several hundred nanometers to several microns. Accordingly, the aspect ratio L/d ranges from 10 to several thousand, so that a nanotube with any desired aspect ratio can be selected. Currently, no other comparable material exists.





FIGS. 5 through 7

are process diagrams illustrating the fastening of the nanotube


12


to the holder


8


.




Nanotubes


12


are attached to a knife edge


36


in a semi-protruding state by means of a non-uniform electric field. As shown in

FIG. 5

, this knife edge


36


and the AFM cantilever


6


on which a metal film


10


has been formed are positioned facing each other inside an electron microscope. The system is constructed so that the knife edge


36


and cantilever


6


can be independently moved and adjusted in three dimensions.




As shown in

FIG. 6

, the cantilever


6


is moved, and a fine adjustment is made so that one nanotube


12


contacts the surface of the holder


8


. More specifically, the base end portion


12




a


of the nanotube


12


contacts the holder


8


, while the tip end portion


12




b


of the nanotube


12


protrudes from the holder


8


. When the base end portion


12




a


is irradiated with an electron beam, organic impurities present in trace amounts inside the electron microscope are decomposed, thus causing a coating film


38


consisting of carbon to be formed so that this film covers the base end portion


12




a


. A cantilever


6


which has a nanotube probe needle


12


fastened in place by such a coating film


38


is shown in FIG.


7


.





FIG. 8

is a sectional view of the essential portion shown in FIG.


7


. It is seen that a metal film


10


is formed on the surface of the pyramid-form holder


8


, and that the base end portion


12




a


of the nanotube


12


is fastened in place by means of a coating film


38


. The tip end portion


12




b


of the nanotube


12


functions as a probe needle.





FIG. 9

is a sectional view of essential portion that illustrates another method for fastening the nanotube. When a current is caused to flow between the knife edge


36


and the holder


8


in the state shown in

FIG. 6

, the base end portion


12




a


of the nanotube


12


is converted into an amorphous state and fused to the holder


8


. Such fusion can also be accomplished by direct irradiation with an electron beam. Accordingly, the base end portion


12




a


becomes a fused portion


40


consisting of an amorphous structure. The nanotube


12


is firmly fastened to the holder by this fused portion.





FIG. 10

is a photograph of a nanotube probe in which the nanotube is fastened in place by means of a coating film. Since the nanotube


12


is thus fastened, the nanotube


12


does not easily come loose from the holder


8


. Since the nanotube


12


consists of an extremely pliable material, this nanotube is capable of extreme bending without breaking. Here, the nanotube is bent and fastened so that the tip end of the nanotube contacts the sample surface more or less perpendicularly. Accordingly, a nanotube probe


20


manufactured in this manner is highly durable, and has a long useful life.





FIG. 11

is a sectional view of a sample. Here, an organic film


4


produced by forming an organic substance into a film is disposed on a single-crystal silicon substrate


2


. In this embodiment, the thickness of the organic film


4


is designed as 11 nm. Various types of organic substances can be utilized for the organic film; one example is an organic polysilane. Organic polysilanes are one type of self-functionalizing material, and have properties based on one-dimensional excitons. For example, these properties include photoconductivity with a high hole mobility, high light-emitting characteristics, and a large non-linear optical effect, etc. In view of these properties, organic polysilanes appear to be a promising material for nano-opto-electronic elements.

FIG. 12

is a structural formula of an organic polysilane; R1 and R2 indicate hydrocarbon groups.




PMPS (polymethylphenylsilanes) are one type of organic polysilane;

FIG. 13

shows the structural formula of PMPS. This is a polysilane in which R1 is a methyl group, and R2 is a benzene ring. The molecular weight varies according to the degree of polymerization, and it is generally around 30,000. An organic film


4


is formed by spin-coating the single-crystal silicon substrate


2


(heat-treated for 30 minutes at 150° C.) with a toluene solution of this PMPS.





FIG. 14

is a photograph of a sample of a substrate


2


with an organic film


4


which has grooves


16


formed by a lithographic method using the contact mode shown in FIG.


1


. It is seen that grooves


16


are formed in the surface of the organic film


4


.

FIG. 15

is a sectional view of one of the grooves shown in FIG.


14


. As a result of measurement by means of an AFM, it was formed that the groove width W was 70 nm, and the groove depth D was 11 nm. Furthermore, it was found that grooves


16


corresponding to the diameter of the nanotube could also be formed by means of a lithogrpahic method using the tapping mode.




In this lithographic method, the groove width W can be freely adjusted by using a nanotube with a small cross-sectional diameter d, i.e., a small tip end curvature radius. Since nanotubes have cross-sectional diameters d ranging from approximately one (1) nanometer to several tens of nanometers, the groove width W can also be adjusted from several nanometers to several hundred nanometers. Such ultra-fine nano-scale working (nano-lithography) is in a region that was completely unattainable in the past.




For purposes of comparison, an investigation was made in order to ascertain what kinds of grooves can be formed in cases where a carbon nanotube is not attached. An experiment was performed in which grooves were formed by means of the pyramid-form holder


8


of the AFM cantilever shown in FIG.


3


. In the case of this silicon probe, a groove width W of approximately 850 nm was formed in the contact mode at a scanning speed of 0.05 (μm/s) and a bias voltage of −10 (V). Accordingly, the advantageous nature of nanotube tips was confirmed even in comparison with silicon probes. Furthermore, it was also confirmed that nanotubes have a long useful life.




The above comparative experiment indicates that an AFM cantilever can be used as an ultra-fine probe needle in a construction that is exactly the same as that of a nanotube tip. The polarity of the applied voltage is also the same. An experiment was also performed using an STM probe needle; in this case as well, a similar groove pattern was successfully formed. Accordingly, it was found that nano-size groove patterns can be formed if an ultra-fine probe needle with a nano-size tip end curvature radius is used.




The present invention is not limited to the above embodiment. Various modifications, design alterations, etc. within limits that involve no departure from the technical concept of the present invention are also included within the technical scope of the present invention.




As seen from the above, according to the present invention, nano-scale groove patterns, e.g., groove patterns ranging from several tens of nanometers to several hundred nanometers, can be formed in a sample surface by means of a nano-size ultra-fine probe needle. Accordingly, the increased density and increased speed of semiconductor chips can be achieved by the realization of nano-lithography.




Furthermore, the present invention makes it possible to realize conventionally unknown nano-lithography by using a nanotube with a tip end diameter of one (1) nanometer to several tens of nanometers. Furthermore, as a result of the high pliability of nanotubes, nano-lithography with a long useful life can be established.




In addition, since a cantilever commonly used in AFM can be used as an ultra-fine probe needle, inexpensive nano-lithography can be realized.




Furthermore, the present invention allows the reliable formation of a nano-scale groove pattern in an organic film by applying a voltage across the probe needle and organic film so that the probe needle acts as a cathode. Accordingly, nano-electronic devices can be realized.




In addition, the groove width and groove depth of the groove-form pattern can be freely adjusted merely by adjusting the scanning speed of the nanotube probe needle and the applied voltage. Thus, highly functional nano-lithography can be realized.




Furthermore, the present invention makes it possible to realize nano-lithography in electrical functional films, optical functional films, mask-forming films and resist films formed on substrates, so that nano-devices can be realized.




In addition, the present invention makes it possible to form a nano-scale groove pattern in a polysilane film. Accordingly, organic nano-opto-electronic devices that exhibit the physical properties of polysilanes can be realized.



Claims
  • 1. A lithographic method to form groove-form patterns on a sample surface comprising the steps of:preparing a nanotube probe that is formed by fastening a base end portion of a nanotube to a holder with a tip end portion of said nanotube being caused to protrude from said holder, causing a tip end of said tip end portion of said nanotube probe to contact a surface of a sample either continuously or intermittently, applying a voltage across said nenotube probe and said sample; and causing said nanotube probe to move while removing a substance that makes said sample at a tip end contact area by an application of said voltage, and wherein a groove width of and a groove depth of said groove of said groove-form pattern are controlled by adjusting a scanning speed of said nanotube probe and said applied voltage.
  • 2. A lithographic method to form groove-form patterns on a sample surface comprising the steps of:causing a tip end of a probe needle to contact a surface of a sample either continuously or intermittently, said probe needle being an ultra-line probe needle with a nano-size tip end diameter, applying a voltage across said probe needle and sample, and caushig said probe needle to move while removing a substance that makes said sample at a probe needle contact area by an application of said voltage, and wherein a groove width of and a groove depth of said groove of said groove-form pattern are controlled by adjusting a scanning speed of said probe needle and said applied voltage.
  • 3. The lithographic method according to claim 2 or 1, wherein said holder is a pyramid portion of a cantilever for AFM use.
  • 4. The lithographic method according to claim 2 or 1, wherein said sample is a lithographable matter including an organic film, other organic matter and an inorganic matter.
  • 5. The lithographic method according to claim 4, wherein said organic film is one selected from the group consisting of an electrical or optical functional film, a mask-fimning film and a resist film tbrmcd on a substrate.
  • 6. The lithographic method according to claim 4, wherein said organic film is a polysilane film.
US Referenced Citations (5)
Number Name Date Kind
4464460 Hiraoka et al. Aug 1984 A
6078055 Bridger et al. Jun 2000 A
6146227 Mancevski Nov 2000 A
6166386 Yano et al. Dec 2000 A
6306779 Muehl et al. Oct 2001 B1
Foreign Referenced Citations (4)
Number Date Country
2000405558 Nov 2000 JP
2000346788 Dec 2000 JP
2001198900 Jul 2001 JP
2002162335 Jun 2002 JP