Low power semiconductor transistor structure and method of fabrication thereof

Abstract

A structure and method of fabrication thereof relate to a Deeply Depleted Channel (DDC) design, allowing CMOS based devices to have a reduced σVT compared to conventional bulk CMOS and can allow the threshold voltage VT of FETs having dopants in the channel region to be set much more precisely. The DDC design also can have a strong body effect compared to conventional bulk CMOS transistors, which can allow for significant dynamic control of power consumption in DDC transistors. The semiconductor structure includes an analog device and a digital device each having an epitaxial channel layer where a single gate oxidation layer is on the epitaxial channel layer of NMOS and PMOS transistor elements of the digital device and one of a double and triple gate oxidation layer is on the epitaxial channel layer of NMOS and PMOS transistor elements of the analog device.

Description

TECHNICAL FIELD

This application relates in general to semiconductor devices and fabrication processes and more particularly to a low power semiconductor transistor structure and method of fabrication thereof.

BACKGROUND

For some time the semiconductor industry has been using bulk CMOS technology to make circuits in chips. Bulk CMOS technology has proven to be particularly “scalable,” meaning that bulk CMOS transistors can be made smaller and smaller while optimizing and reusing existing manufacturing processes and equipment in order to maintain acceptable production costs. Historically, as the size of a bulk CMOS transistor decreased, so did its power consumption, helping the industry provide increased transistor density and lower operating power. Thus, the semiconductor industry has been able to scale the power consumption of bulk CMOS transistors with their size, reducing the cost of operating transistors and the systems in which they reside.

In recent years, however, decreasing the power consumption of bulk CMOS transistors while reducing their size has become increasingly more difficult. Transistor power consumption directly affects chip power consumption, which, in turn, affects the cost of operating a system and, in some cases, the utility of the system. For example, if the number of transistors in the same chip area doubles while the power consumption per transistor remains the same or increases, the power consumption of the chip will more than double. This is due in part by the need to cool the resulting chip, which also requires more energy. As a result, this would more than double the energy costs charged to the end user for operating the chip. Such increased power consumption could also significantly reduce the usefulness of consumer electronics, for example, by reducing the battery life of mobile devices. It could also have other effects such as increasing heat generation and the need for heat dissipation, potentially decreasing reliability of the system, and negatively impacting the environment.

There has arisen among semiconductor engineers a widespread perception that continued reduction of power consumption of bulk CMOS is not feasible, in part because it is believed that the operating voltage V_DD of the transistor can no longer be reduced as transistor size decreases. A CMOS transistor is either on or off. The CMOS transistor's state is determined by the value of a voltage applied to the gate of the transistor relative to a threshold voltage V_T of the transistor. While a transistor is switched on, it consumes dynamic power, which can be expressed by the equation:P_dynamic=CV_DD²fwhere V_DD is the operating voltage supplied to the transistor, C is the load capacitance of the transistor when it is switched on, and f is the frequency at which the transistor is operated. While a transistor is switched off, it consumes static power, which can be expressed by the equation:P_static=I_OFFV_DD where I_OFF is the leakage current when the transistor is switched off. Historically, the industry has reduced transistor power consumption primarily by reducing the operating voltage V_DD, which reduces both dynamic and static power.

The ability to reduce the operating voltage V_DD depends in part on being able to accurately set the threshold voltage V_T, but that has become increasingly difficult as transistor dimensions decrease. For transistors made using bulk CMOS processes, the primary parameter that sets the threshold voltage V_T is the amount of dopants in the channel. Other factors that affect V_T are halo implantation, source and drain low doped extensions, and channel thickness. In theory, matching transistor V_T can be done precisely, such that the same transistors on the same chip will have the same V_T, but in reality the process and statistical variations in dopant concentration and placement mean that threshold voltages can vary significantly. Such mismatched transistors will not all switch on at the same time in response to the same gate voltage, and in extreme cases some may never switch on. Of even more concern, mismatched transistors result in increased leakage losses that waste power even when a transistor is not actively switching.

For transistors having a channel length of 100 nm or less, as few as thirty to fifty dopant atoms may be positioned in a channel at nominal dopant concentration levels. This compares with the thousands, or tens of thousands of atoms that are in positioned in the channel for previous generation transistors that have channel lengths greater than 100 nanometers or so. For nanometer scale transistors, the inherent statistical variation in numbers and placement of such few dopant atoms results in a detectable variation in V_T known as random dopant fluctuations (RDF). Along with process and material variations, for nanometer scale bulk CMOS transistors with doped channel, RDF is a major determinant of variations in V_T (typically referred to as sigma V_T or σV_T) and the amount of σV_T caused by RDF only increases as channel length decreases.

Processes and designs for novel transistors having greatly reduced σV_T are sought by the industry. However, many proposed solutions such as undoped channel FINFET would require substantial changes in transistor process manufacture and layout. This has slowed adoption, since the industry prefers to avoid redesigns that require substantial change in conventional and widely used integrated circuit manufacturing processes and transistor layout. This is particularly true for systems on chip (SoC) or other highly integrated devices that include a wide variety of circuit types, such as analog input and output circuits (I/O), digital circuits, and other types of circuits. Moreover, given the different types of circuits on such highly integrated systems, if one or more types of circuits can be improved, and any necessary legacy circuits remain the same, the overall SoC should still be produced together to avoid extra steps in the manufacturing process. For example, if an improvement to the digital circuits can be accomplished, and the improvement did not apply to analog circuits, it would be desirable to have the circuits to be manufactured together simultaneously without adding further processing steps. The entire integrated circuit can be redesigned to accommodate operation at the reduced voltage power source. As referenced herein, the term “redesign” can include appropriate sizing of transistor gates prior to circuit fabrication. However, difficulties are encountered when redesign attempts are made. Extra process and masking steps, can be complex, costly and technically difficult.

Given the substantial costs and risks associated with transitioning to a new technology, manufacturers of semiconductors and electronic systems have long sought a way to extend the use of bulk CMOS. At least in part due to the inability to easily control σV_T variation in groups of transistors as V_DD is substantially reduced below one volt, the continued reduction of power consumption in bulk CMOS has increasingly become viewed in the semiconductor industry as an insurmountable problem.

SUMMARY

There is substantial advantage in having a low power digital transistor process and structure that permits on-die analog I/O transistors to remain unchanged even when low power transistors replace standard transistors. Thus, it is desirable to have a mix of circuits where some are changed and others are unchanged legacy circuits, but where the process to manufacture them is not substantially changed. And to reduce costs and increase yields, it would be best to not substantially increase the number of manufacturing steps in producing the overall integrated circuit.

Thus, there is a need in the art for improved structures and fabrication methods for complementary metal oxide semiconductor (CMOS) transistors and integrated circuits, and also a transistor fabrication process that is compatible with the fabrication of digital and analog transistors on a single integrated circuit die.

A suite of novel structures and methods is provided to reduce power consumption in a wide array of electronic devices and systems. Some of these structures and methods can be implemented largely by reusing existing bulk CMOS process flows and manufacturing technology, allowing the semiconductor industry as well as the broader electronics industry to avoid a costly and risky switch to alternative technologies. Some of the structures and methods relate to a Deeply Depleted Channel (DDC) design, allowing CMOS based devices to have a reduced σV_T compared to conventional bulk CMOS and can allow the threshold voltage V_T of FETs having dopants in the channel region to be set much more precisely. The DDC design also can have a strong body effect compared to conventional bulk CMOS transistors, which can allow for significant dynamic control of power consumption in DDC transistors. There are many ways to configure the DDC to achieve different benefits, and additional structures and methods presented herein can be used alone or in conjunction with the DDC to yield additional benefits.

The disclosure describes various technical advantages over conventional semiconductor fabrication processing. One technical advantage is to provide a semiconductor structure that includes an analog device and a digital device each having an epitaxial channel layer. Another technical advantage is to have a single gate oxidation layer on the epitaxial channel layer of NMOS and PMOS transistor elements of the digital device and one of a double and triple gate oxidation layer on the epitaxial channel layer of NMOS and PMOS transistor elements of the analog device. Yet another technical advantage includes the use of a body bias to provide significant dynamic control of power consumption in DDC transistors. The result is the ability to independently control V_T (with a low σV_T) and V_DD, so that the body bias can be tuned separately from V_T for a given device.

Certain embodiments of the present disclosure may enjoy some, all, or none of these advantages. Other technical advantages may be readily apparent to one skilled in the art from the following figures, description, and claims.

BRIEF DESCRIPTION OF THE DRAWINGS

For a more complete understanding of the present disclosure, reference is made to the following description taken in conjunction with the accompanying drawings, wherein like reference numerals represent like parts, in which:

FIG. 1 shows a representative SoC with outlined groupings of DDC digital transistors, digital legacy transistors, DDC analog transistors, and analog legacy transistors, along with a respective profile.

FIG. 2 is a general flow chart showing different process steps related to processing DDC analog and digital devices.

FIG. 3 is an example of a transistor dopant profile illustrating ranges of dopants according to different embodiments.

FIG. 4 is a flow chart showing one embodiment of an integrated circuit process flow.

FIG. 5 is a flow chart showing one embodiment of an integrated circuit process flow.

FIG. 6 is a flow chart showing one embodiment of an integrated circuit process flow.

FIGS. 7 through 30 show a series of steps in a process flow of an SoC having DDC digital transistors, digital legacy transistors, DDC analog transistors, and analog legacy transistors according to one embodiment.

DETAILED DESCRIPTION

Novel structures and methods are disclosed to reduce power consumption in a wide array of electronic devices and systems. Some of these structures and methods can be implemented largely by reusing existing bulk CMOS process flows and manufacturing technology, allowing the semiconductor industry as well as the broader electronics industry to avoid a costly and risky switch to alternative technologies. Different transistor designs, including both analog and digital transistors, can be incorporated into a single integrated circuit or system on a chip (SoC) for improved power saving benefits. Moreover, these new structures can be incorporated into the process flow together with legacy transistor and layout structures, reducing the risk to manufacturers of incorporating new structures in the process flow of an integrated circuit by avoiding extra process steps. As a result, there is little or no substantial increase in expense of production of integrated circuits, such as SoC, that incorporate the novel power saving transistor structures.

Also provided are methods and structures for incorporating and using the innovations described herein in systems, such as in electronic products, to provide substantial benefits over conventional devices as a result of lower power operation. Such benefits include lower power consumption at the system level, improved system performance, improved system cost, improved system manufacturability and/or improved system reliability as a result of cooler low power systems that may be designed and manufactured according to the embodiments described and illustrated herein. As will be demonstrated, the innovations can advantageously be employed in a wide range of electronic systems including consumer devices such as personal computers, mobile phones, televisions, digital music players, set top boxes, laptop and palmtop computing devices, e-book readers, digital cameras, GPS systems, flat panel displays, portable data storage devices and tablets, as well as in a variety of other electronic devices. In some implementations, the transistors and integrated circuits can materially enhance the operation and, accordingly, the commercial suitability, of the electronic system as a whole. In some embodiments, innovative transistors, integrated circuits and systems that contain them as described herein may also enable more environmentally friendly implementations than alternative approaches.

These and other benefits provide an advancement in digital circuits that fulfills many needs of designers, producers, and consumers. These benefits can provide systems composed of novel structures that enable continued and further advancement of integrated circuits, resulting in devices and systems with improved performance. The embodiments and examples will be described herein with reference to transistors, integrated circuits, electronic systems, and related methods, and will highlight the features and benefits that the novel structures and methods provide at various levels of the manufacturing process and the chain of commerce, including to end users of electronic products. The application of concepts inherent in these examples to structures and methods of producing integrated circuits and electronic systems will prove expansive. Accordingly, it will be understood that the spirit and scope of the inventions is not limited to these embodiments and examples, but is only limited by the claims appended herein and also in related and co-assigned applications.

In one embodiment, a novel nanoscale Field Effect Transistor (FET) structure is provided that has precisely controlled threshold voltage in comparison to conventional doped channel devices of the same channel length. In this context, precisely controlled threshold voltage includes the ability to set and possibly tune a V_T value that provides significant improvement or reduction of σV_T. This structure and methods of making it can allow FET transistors that have a low operating voltage as compared to conventional devices. One embodiment includes a nanoscale FET structure operable to have a depletion zone or region (i.e. deeply depleted channel, DDC) that extends from a gate to a highly doped screening layer set at a depth below the gate greater than one-half the gate length. In one embodiment, a channel region near the gate is substantially undoped as compared to a high concentration screening region located at a distance of at least ½ the gate length below the gate. This provides a substantially undoped channel region or layer (concentration of less than 5×10¹⁷ atoms/cm³ and typically formed as an epitaxially grown silicon layer) paired with a highly doped screening region or layer. Together, in operation, these structures act to define a deeply depleted zone or region that terminates electric fields emanating from the gate when a voltage that is approximately equal to or greater than the threshold voltage is applied to the gate.

In certain embodiments the screening layer is positioned to avoid direct contact with the source and the drain. In certain other embodiments, it may be formed as a sheet extending under multiple source/drain/channel regions, while in other embodiments it may be a self aligned implant or layer coextensive with the channel region. The screening region thickness can typically range from 5 to 50 nanometers. The screening region is highly doped relative to the channel, the threshold voltage tuning region (if provided), and the P-well. In practice, the screening region is doped to have a concentration between 1×10¹⁸ and 1×10²⁰ atoms/cm³. In certain embodiments, dopant migration resistant layers of carbon, germanium, or the like can be applied above screening region to prevent dopant migration toward the undoped channel and gate.

While threshold voltage is primarily set by the combination of gate work function, body bias, channel thickness, and depth and dopant concentration of the screening layer, small adjustments to threshold voltage are possible by optional provision of a separate epitaxially grown silicon layer adjacent to the screening region. Such a threshold voltage tuning region has a dopant concentration less than the dopant concentration of the screening region. For typical applications the threshold voltage tuning region is doped to have average concentrations ranging from between 5×10¹⁷ and 2×10¹⁹ atoms/cm³. When present, the threshold tuning region thickness can typically range from 5 to 50 nanometers in thickness. In certain embodiments, dopant migration resistant layers of carbon, germanium, or the like can be applied above and/or below the threshold voltage tuning region to prevent dopant migration into the channel region, or alternatively, from the screening region into the threshold voltage tuning region.

As will be appreciated, DDC depth (X_d) is established by the depth of the screening layer below the gate, and is typically one half of the gate length (i.e. ½ Lg), possibly equal to gate length (i.e. Lg) or to intermediate fractions thereabout (e.g. ¾ Lg). In one example, DDC depth may be set greater than or about equal to one-half the channel length Lg, which in operation allows for precise setting of the threshold voltage even at low operating voltages below one volt. Depending on the requirements of a particular application, different depths may provide different beneficial results. Given this disclosure, it will be understood that different DDC depths are possible in different applications, different device geometries, and various parameters of particular designs. Depending on the parameters of a particular application, different region thicknesses, dopant concentrations, and operating conditions used in forming the DDC transistor may provide different beneficial results.

As will be discussed, some of the structures and methods relate to a DDC design that can be produced together with legacy transistor devices in a monolithic circuit laid out on the same wafer and die. The DDC can permit CMOS devices having reduced σV_T compared to conventional bulk CMOS with highly doped channels, allowing for increased variability of V_T. The DDC design also can have a strong body effect compared to conventional bulk CMOS transistors, which can allow for improved body bias assisted control of transistor voltage threshold setting. There are many ways to configure the DDC to achieve different benefits, and additional structures and methods presented herein can be used alone or in conjunction with the DDC to yield additional benefits.

These structures and the methods of making the structures allow for FET transistors having both a low operating voltage and a low threshold voltage as compared to conventional nanoscale devices. Furthermore, DDC transistors can be configured to allow for the threshold voltage to be statically set with the aid of a voltage body bias generator. In some embodiments the threshold voltage can even be dynamically controlled, allowing the transistor leakage currents to be greatly reduced (by setting the voltage bias to upwardly adjust the V_T for low leakage, low speed operation), or increased (by downwardly adjusting the V_T for high leakage, high speed operation). Ultimately, these structures and the methods of making structures provide for designing integrated circuits having FET devices that can be dynamically adjusted while the circuit is in operation. Thus, transistors in an integrated circuit can be designed with nominally identical structure, and can be controlled, modulated or programmed to operate at different operating voltages in response to different bias voltages, or to operate in different operating modes in response to different bias voltages and operating voltages. In addition, these can be configured post-fabrication for different applications within a circuit.

Certain embodiments and examples are described herein with reference to transistors and highlight the features and benefits that the novel structures and methods provide transistors. However, the applicability of concepts inherent in these examples to structures and methods of producing integrated circuits is expansive and not limited to transistors or bulk CMOS. Accordingly, it will be understood in the art that the spirit and scope of the inventions is not limited to these embodiments and examples or to the claims appended herein and also in related and co-assigned applications, but may be advantageously applied in other digital circuitry contexts.

In the following description, numerous specific details are given of some of the preferred ways in which the inventions may be implemented. It is readily apparent that the inventions can be practiced without these specific details. In other instances, well known circuits, components, algorithms, and processes have not been shown in detail or have been illustrated in schematic or block diagram form in order not to obscure the inventions in unnecessary detail. Additionally, for the most part, details concerning materials, tooling, process timing, circuit layout, and die design have been omitted inasmuch as such details are not necessary to obtain a complete understanding of the inventions as they are considered to be within the understanding of persons of ordinary skill in the relevant art. Certain terms are used throughout the following description and claims to refer to particular system components. Similarly, it will be appreciated that components may be referred to by different names and the descriptions herein are not intended to distinguish between components that differ in name but not function. In the following discussion and in the claims, the terms “including” and “comprising” are used in an open-ended fashion, and thus should be interpreted to mean “including, but not limited to,” for example.

Various embodiments and examples of the methods and structures mentioned above are described herein. It will be realized that this detailed description is illustrative only and is not intended to be in any way limiting. Other embodiments will readily suggest themselves to persons of ordinary skill in the art having the benefit of this disclosure. Reference will be made in detail to embodiments illustrated in the accompanying drawings. The same reference indicators will be used throughout the drawings and the following detailed description to refer to the same or like parts.

In the interest of clarity, not all of the routine features of the implementations and embodiments described herein are shown and described. It will, of course, be appreciated that in the development of any such actual implementation of the inventions herein, numerous implementation-specific decisions will typically be made in order to achieve the developer's specific goals. Moreover, it will be appreciated that such a development effort might be complex and time-consuming, but would nevertheless be a routine undertaking of engineering for those of ordinary skill in the art having the benefit of this disclosure.

Also, concentrations of atoms implanted or otherwise present in a substrate or crystalline layers of a semiconductor to modify physical and electrical characteristics of a semiconductor will be described in terms of physical and functional regions or layers. These may be understood by those skilled in the art as three-dimensional masses of material that have particular averages of concentrations. Or, they may be understood as sub-regions or sub-layers with different or spatially varying concentrations. They may also exist as small groups of dopant atoms, regions of substantially similar dopant atoms or the like, or other physical embodiments. Descriptions of the regions based on these properties are not intended to limit the shape, exact location or orientation. They are also not intended to limit these regions or layers to any particular type or number of process Steps, type or numbers of layers (e.g., composite or unitary), semiconductor deposition, etch techniques, or growth techniques utilized. These processes may include epitaxially formed regions or atomic layer deposition, dopant implant methodologies or particular vertical or lateral dopant profiles, including linear, monotonically increasing, retrograde, or other suitable spatially varying dopant concentration. The embodiments and examples included herein may show specific processing techniques or materials used, such as epitaxial and other processes described below and illustrated in FIGS. 7-30. These examples are only intended as illustrative examples, and are not nor should they be construed as limiting. The dopant profile may have one or more regions or layers with different dopant concentrations, and the variations in concentrations and how the regions or layers are defined, regardless of process, may or may not be detectable via techniques including infrared spectroscopy, Rutherford Back Scattering (RBS), Secondary Ion Mass Spectroscopy (SIMS), or other dopant analysis tools using different qualitative or quantitative dopant concentration determination methodologies.

In one embodiment, a building block for low power circuits can be configured with low power transistors, such as for example a low power field effect transistor as provided herein that is operable at a voltage V_dd of less than 0.9 volts. In one example, the transistor may include a polysilicon gate with a gate length less than 100 nanometers, where the gate includes a polysilicon layer and a dielectric layer. The device further includes a low doped epitaxial channel contacting the dielectric layer of the polysilicon gate. A highly doped screening layer may be positioned in a manner to extend below low doped epitaxial channel and above a transistor body. The screening layer may be treated to reduce dopant diffusion into the low doped epitaxial channel, as discussed in more detail below. The device includes a source and a drain, with a low doped epitaxial channel extending between the source and drain.

In certain embodiments, a body tap may also be included to permit application of a body bias voltage to the transistor body. Body biasing relies on the body effect phenomenon to modulate the V_T of a MOSFET, and is commonly quantified as a body effect coefficient. As will be appreciated, forward biasing (FBB) the body with respect to the source reduces V_T, increasing transistor speed. However, because of the exponential dependence of leakage on V_T, it also leads to a large increase in power usage. Similarly, reverse body bias (RBB) reduces leakage at the cost of reduced speed and increased delay. In certain embodiments, application of a body bias permits increase of threshold voltage V_T to a value greater than 0.3 volts for example.

Body taps, schematically illustrated as a connection between a body bias generator and a transistor body, may be applied to individual devices, groups of devices, or entire circuits or sub-circuits on a given integrated circuit depending on the application. According to these embodiments, improved σV_T allows for a stronger body bias coefficient, that in turn allows for improved changes in V_T. In prior art systems, body bias coefficient was improved by highly doping the channel, which resulted in a wide and undesirable range of σV_T. Thus, a high threshold voltage was required for such devices to operate with body bias mediated control. According to the embodiments described herein, devices, systems and methods are provided that allow for greatly improved σV_T, and also provide improved and strong body bias coefficient. Thus, a wide range of adjustable V_T is possible with a strong body bias, resulting in a better performing device and system that operates at lower power.

FIG. 1 shows an exemplary SoC 100 configured with several diverse digital and analog transistor configurations that can be incorporated into a device using the methods described herein. According to the methods and processes discussed herein, a system having a variety of combinations of novel and legacy transistor devices and structures can be produced on silicon using bulk CMOS. The SoC 100 includes DDC digital logic devices 102, legacy digital logic devices 104, DDC analog devices 106, legacy analog devices 108, and legacy input and output (I/O) analog circuits and systems 110, and possibly other devices, which may be interconnected to each other within the circuit via a common bus 114, wire traces (not shown), or other interconnections. The devices are formed or otherwise processed as bulk CMOS on a common substrate 115, typically silicon or other similar substrate.

The SoC 100 includes at least one or more devices 106 that have DDC cross-section profiles, an example of which is shown here as a variety of both analog and digital transistors 120, 130, 140, 150, all of which can be formed together on substrate 115. The first device 120 is a digital transistor having a gate stack 122 and spacers, source and drain 124/126, a shallow well 127 (or body of the transistor) underneath a deeply depleted channel 128 and screening layer 129 that extends between the shallow trench isolated (STI) structures 117. The significance of this profile is the low power characteristic possible by this and other devices by virtue of the deeply depleted channel and screening layer. Another digital device 130 has a gate stack 132 and spacers, source and drain 134/136 and a shallow well 137 underneath a deeply depleted channel 138. Unlike device 120, this digital device 130 has a screening layer 139 that, along with DDC 138, extends between the source and drain 134/136. Like device 120, the significance of this profile is the low power characteristic possible by this and other devices by virtue of the deeply depleted channel and screening layer.

The third and fourth devices from the left are analog devices that share some of the physical characteristics of the digital devices in their channel regions, providing power saving features for these and other similar analog devices. Analog device 140 is a digital transistor having a gate stack 142 and spacers, source and drain 144/146, a shallow well 147 underneath a deeply depleted channel 148 and screening layer 149 that extends between the STI Structures 117. Like the digital devices described above, the significance of this analog device profile is that the low power characteristic possible by this and other analog devices by virtue of the deeply depleted channel and screening layer. Another analog device 150 has a gate stack 152 and spacers, source and drain 154/156 and a shallow well 157 underneath a deeply depleted channel 158. Unlike device 140, this digital device 150 has a screening layer 159 that, along with DDC 158, extends between the source and drain 154/156. Like device 140, the significance of this profile is the low power characteristic possible by this and other devices by virtue of the deeply depleted channel and screening layer.

In some applications, there may be the desire to apply a bias voltage to the body 127 of the transistor, such as bias voltage source 160 shown in FIG. 1. According to one embodiment, the V_T of a given device or multiple devices may be dynamically set by applying a bias voltage to the body. Thus, and again, body taps, schematically illustrated as a connection between bias voltage source 160 and a transistor, may be applied to individual devices, groups of devices, or entire circuits or sub-circuits on a given integrated circuit depending on the application. According to these embodiments, improved σV_T allows for a stronger body bias coefficient that allows for improved changes in V_T.

Referring to FIG. 2, a brief process flow chart 200 for producing DDC structures for analog and digital device is illustrated. These along with other process Steps allow for the processing and manufacture of integrated circuits that include DDC structured devices together with legacy devices, allowing for designs to cover a full range of analog and digital devices with improved performance and lower power. And, the novel structures can be formed together with legacy devices using well known processing techniques and design rules. In the first Step 202, if digital DDC devices are included in a process, a digital screen is implanted for both P-type and N-type devices. In the next Step, 204, if analog DDC type devices are included, analog screening is performed for both P-type and N-type analog DDC devices.

In practice, amorphizing silicon is performed to assisting in the activation and substitutionality of dopants. Since amorphous silicon cannot grow epitaxial layers, it must be returned to a crystalline state. So, in Step 206, low temperature re-crystallization is performed.

In Step 208, an optional Step of diffusion prevention may be performed. It is noted here that steps for preventing diffusion of dopants can be used along with different steps while manufacturing integrated circuits. Since undesired diffusion of dopants may occur at one or a number of steps in a given process flow, a designer may find it useful to perform diffusion prevention steps before, during or after any number of steps during circuit processing.

Epitaxial (EPI) deposition is then performed in Step 210. These Steps together with other Steps that are known in the art of semiconductor processing provide a novel and useful means to produce improved integrated circuits and SoC with improved and low power structures.

Referring to FIG. 3, a graph is shown with a range of different dopant profiles according to one embodiment. These ranges illustrated and the parameters set out are intended as examples, and those skilled in the art will understand that the benefits of the embodiments described and illustrated herein are attainable generally about or within those ranges.

In practice, designers and manufacturers gather statistical data from mathematical models and sample measurements from actual circuits to determine the variance of threshold voltages of a circuit design. The voltage differential mismatch between transistors, whether derived from manufacturing variations or RDFs, is determined as σV_T. In order for the circuit as a whole to operate, the operating voltage V_DD must be chosen in view of σV_T. Generally the larger the variance, the higher the σV_T, such that the operating voltage V_DD must be set higher for the transistor to operate properly. With multiple device implemented across a circuit, V_DD may need to be set at the highest overall value in order for the circuit to operate properly.

A structure and method of its production are provided that reduces σV_T, reducing the range of variance of the threshold voltage of the transistors across the integrated circuit. With reduced σV_T, the static value of V_T can be set more precisely and can even be varied in response to a changing bias voltage. The threshold voltage for nominally identical devices across a circuit may be more accurately set with decreased σV_T, thus allowing the device to operate using a lower operating voltage V_DD and, therefore, consume less power. Moreover, with more headroom to vary V_T for a given transistor or group of transistors, devices can be operated at different modes corresponding to different bias voltages for particular modes. This may add functionality to many devices and systems and may particularly benefit devices where fine control of device power modes is useful.

Referring to FIG. 4, one example of a production process for an integrated circuit, such as a SoC, is illustrated in a process flow chart 400. In the first Step 402, a P-type screening layer is formed, possibly by implant, which may act as a screening or V_T setting layer for a device in the integrated circuit. Next in Step 404, an N-type screening layer is formed, possibly by implant, which may act as a screening or V_T setting layer for another device in the integrated circuit. In Step 406, a low temperature re-crystallization is performed.

In Step 408, a diffusion prevention treatment is performed. While dopants can be implanted or co-deposited during epitaxial growth, further high temperature processing can promote dopant diffusion through the silicon lattice. High temperature process steps required to form transistor structures can result in dopant atoms moving from a screening layer into the previously undoped channel, or even migrate into a gate oxide. There are several methods provided herein to address the prevention of dopant diffusion in different process flows, such as for example when thermal annealing procedures are performed in a process.

In one method, carbon can be introduced into the screening via implant or the growth of a silicon carbide (SiC) epitaxial layer. During annealing for example, substitutional carbon traps (via a kick-out mechanism) any mobile carriers such as boron or phosphorus. The addition of carbon helps to prevent diffusion during the high thermal cycles a polysilicon gate transistor typically experiences.

Indium is known to form a cluster with boron which is not mobile. However, this also leads to low dopant activation of boron. Thus, methods to achieve both high activation and low diffusion include the co-implantation of indium and boron. Several examples are included herein, and others are possible given this disclosure, including these examples and other processes used together in different combinations. In one exemplary process, co-implantation of indium and boron can be performed such that their peaks align. Different ratios between the peaks of indium and boron along with anneal options such as Flash and Laser will result in high concentration and sharp profiles. In another example, co-implantation of indium and boron can be performed such that the peak of indium is closer to the surface then boron. Boron diffusing to the surface will be slowed by the indium while the screening and V_T layer will achieve high activation. In yet another example, co-implantation of indium and born can be performed such that the peak of the indium is closer to the substrate then the boron. This will prevent indium from diffusing into the substrate allowing high concentration to exist in the screening layer.

While carbon is useful in preventing migration of boron or other dopants, carbon itself may migrate into the undoped channel, increasing scattering and reducing channel mobility. To prevent carbon diffusion, the following procedure can be useful. If carbon and boron are co-implanted into amorphous silicon, a low temperature anneal may be used to re-grow the silicon layer. During this low temperature anneal, carbon re-grows substitutionally. This is because, when a process begins with crystal on silicon, it needs to be made amorphous, or amorphized, for processing so that is no longer in a crystalline state. It must then after be annealed to place it back in the crystalline state, or re-crystallized. Re-growth of crystal on silicon from the amorphous state can then be achieved. With carbon located in interstitial locations in the crystal lattice, carbon will substitute silicon atoms in the lattice. Thus, carbon re-grows substitutionally.

This re-growth results in a large concentration of silicon interstitials. With subsequent anneals, these interstitials diffuse rapidly towards the surface and pull boron from the screening region into the channel region. Additionally, the substitutional Carbon becomes interstitial via a kick-out mechanism which retards the boron diffusion. This interstitial carbon also diffuses towards the surface and would normally cause mobility degradation of the channel and create undesired surface states.

However, in this process embodiment, as the boron, excess interstitials and carbon move to the surface, a high temperature anneal followed by oxidation or a high temperature oxidation acts to consume boron, carbon and interstitial concentration that have moved to the surface. The oxidation process will create additional interstitials, so this oxidation needs to be thin (˜2 nm). The oxide is then stripped and the undoped silicon channel is epitaxially grown on the contamination free surface. The undoped epi has reduced exposure to the mobile carbon and boron which has been removed from the system via the oxide growth and strip. Additionally, a similar oxidation can be used after the EPI growth before the gate oxidation. This additional oxidation can be in addition to the first oxidation or instead of the first oxidation.

During implantation, significant damage is introduced into the silicon. The resulting interstitials assist the Boron in diffusing quickly. According to one embodiment, by removing the implant damage, the interstitials can be eliminated allowing for less diffusion and more abrupt junctions. Two methods of achieving this are plasma implantation and doped spin on glass. In a spin on glass process, a high dose of silicon dioxide is placed on the surface of the silicon. For plasma implantation, a high dose of highly doped plasma is deposited on the surface. Here, there is no penetration or deposition into the substrate, no implantation occurs. When annealed, dopants are drawn in at the solid solubility, where the higher temperature causes a higher solid solubility. Dopants can then be affected by thermally annealing to draw in more dopants without damaging the silicon structure. The result is a higher doping achieved with abrupt junctions, and damage to the silicon is greatly reduced.

In one embodiment, SiGe can be used to slow the diffusion of boron from the screening layer into the channel. SiGe can be deposited on top of the substrate. Dopants can be implanted in the substrate or directly co-deposited during epitaxial growth of the SiGe layer. A Si layer is still deposited as the channel. The SiGe prevents diffusion from these doped layers into the Si channel.

Delta doping of C/N/Ge/Cl/F can be used at the interface between the screening layer and the EPI layer. This layer serves to prevent dopant diffusion across the layer. This layer also minimizes the amount of dopant in the system that could diffuse into the channel of the device or segregate into the gate.

Source/drain and source/drain extensions may incur damage from the formation of the DDC channel area. Due to polysilicon requiring both deep implants and high thermal anneals to prevent poly depletion, damage and dopants introduced to the channel area via lateral straggle can create large diffusion from the DDC channel stack into the channel (via interstitials or co-diffusion effects). As poly depletion effects cannot be sacrificed, there is no way to lower the implant energy/dose or the anneal criteria. Two methods to keep channel doping from getting to the DDC channel stack is the use of RSD and secondary spacers.

A second spacer can be used to increase the lateral distance from the SD implant and the DDC channel dose to prevent damage to silicon when implanting dopants. This spacer may or may not be removed after the SD implant and before salicidation. With increased lateral Si between the Si and the DDC channel, there is a decrease in the effect of lateral straggle.

Referring again to FIG. 4, the next Step after diffusion prevention treatment is EPI deposition in Step 410. Next, in Steps 412 and 414 respectively, P-wells and N-wells are implanted. Next, in Steps 416 and 418 respectively, analog P-type and N-type V_T layers are implanted. STIs are then formed in Step 420 to separate the different devices from each other down to the shallow wells.

Next—depending on the type of device—single, double or triple gate oxidation is performed in Step 422. In practice, digital devices require only a thin single gate oxide layer, where analog devices have thicker double or triple gate oxide layers.

In Step 424, a polysilicon (polygate) layer is formed, followed by P-type Lightly Doped Drain (LDD) formed in Step 426, and N-type LDD formed in Step 428. These LDD, or tips, extend under the gate spacers.

Spacers are formed in Step 430. P+ and N+ implants are then performed in Steps 432 and 434. Silicide is then processed in Step 436, followed by contacts formed in Step 438.

Referring to FIG. 5, one example of a production process for an integrated circuit, such as a SoC, is illustrated in a process flow chart 500. In the first Step 502, a P-type screening layer is formed, possibly by implant, which may act as a screening or V_T setting layer for a device in the integrated circuit. Next in Step 504, an N-type screening layer is formed, possibly by implant. In Step 506, a P-type analog screening layer is implanted, followed by an N-type analog screening layer implanted in Step 508. A low temperature re-crystallization is then performed in Step 510.

Next, in Step 512, EPI deposition is performed. In Steps 514 and 516 respectively, P-wells and N-wells are implanted. In Steps 518 and 520 respectively, P-type and N-type V_T layers are implanted. In steps 522 and 524, analog P-type and N-type V_T layers are implanted. STIs are then formed in Step 526 to separate the different devices from each other down to the shallow wells.

Next—depending on the type of device—single, double or triple gate oxidation is performed in Step 528. In practice, digital devices require only a thin single gate oxide layer, where analog devices have thicker double or triple gate oxide layers. In Step 530, a polygate layer is formed, followed by P-type LDD formed in Step 532, and N-type LDD formed in Step 534. Spacers are formed in Step 536. P+ and N+ implants are then performed in Steps 538 and 540. Silicide is then processed in Step 542, followed by contacts formed in Step 544.

Referring to FIG. 6, one example of a production process for an integrated circuit, such as a SoC, is illustrated in a process flow chart 600. In the first Step 602, P-type shallow wells are formed, possibly by implant. Next in Step 604, P-type shallow wells are formed, possibly by implant. In Steps 606 and 608, P-type and N-type screening layers are formed, possibly by implant. Next, in steps 610 and 612, P-type and N-type analog screening layers are formed, possibly by implant. In Step 614, a low temperature re-crystallization is performed. Epitaxial (epi) deposition is performed in Step 616. STIs are then formed in Step 618 to separate the different devices from each other down to the shallow wells.

Next—depending on the type of device—single, double or triple gate oxidation is performed in Step 620. In practice, digital devices require only a thin single gate oxide layer, where analog devices have thicker double or triple gate oxide layers.

In Step 622, a polysilicon gate (polygate) layer is formed, followed by P-type LDD formed in Step 624, and N-type LDD formed in Step 626. Spacers are formed in Step 628. P+ and N+ implants are then performed in Steps 630 and 632. Silicide is then processed in Step 634, followed by contacts formed in Step 636.

Referring to FIGS. 7-30 collectively, one example of a process configured for improved power savings is shown in a process profile diagram. The process starts with a silicon wafer 700, which is typically used to form multiple integrated circuits thereon. FIGS. 7-30 will show one example of the processing of several different circuit components by way of a progressive series of cross-sections of a silicon wafer. There is cross-over and removal of different structures as the process progresses, where some of the structures are substituted or otherwise eliminated. Accordingly, labels in the progressive figures will necessarily be eliminated, thus not all numbering labels will not be shown in all figures through to the end. This example will illustrate component devices including a PMOS DDC logic transistor, an NMOS DDC logic transistor, a PMOS DDC analog transistor, an NMOS DDC analog transistor, a PMOS legacy logic transistor, an NMOS legacy logic transistor, a PMOS legacy analog transistor and an NMOS legacy logic transistor. Those skilled in the art will understand that different combinations and permutations of these and other devices are possible given the examples described herein, and also that the following example is merely for illustrative purposes.

FIG. 7 a substrate 700, such as silicon. This process will illustrate exemplary process steps for forming eight different devices in this order beginning from the left and ordered to the right of this series of figures:

• • a PMOS DDC digital logic device 702;
  • an NMOS DDC digital logic device 704;
  • a PMOS DDC analog device 706;
  • an NMOS DDC analog device 708;
  • a PMOS legacy digital logic device 710;
  • an NMOS legacy digital logic device 712;
  • a PMOS legacy analog device 714; and
  • an NMOS legacy analog device 716.

FIG. 8 shows an implanted P-type doping screening layer 800 formed for a PMOS DDC logic device on the substrate 700.

FIG. 9 shows a N-type doping screening layer formed for a NMOS DDC logic device on substrate 700 for another device.

FIG. 10 shows an implanted Analog P-type screening layer for a PMOS DDC analog device.

FIG. 11 shows an implanted Analog N-type screening layer for an NMOS DDC analog device.

FIG. 12 shows an EPI deposition. Though an undoped epitaxial channel is contemplated, selective masking may be implemented in order to provide certain transistor elements with a doped channel layer.

FIG. 13 shows implanted P-wells for various P-type devices, such as the PMOS DDC digital logic device, PMOS DDC analog device, PMOS legacy digital logic device, and PMOS legacy analog device to be formed in this example.

FIG. 14 shows implanted N-Wells 1402, 1404, 1406, 1408, for various N-type devices, such as the NMOS DDC digital logic device, NMOS DDC analog device, NMOS legacy digital logic device and NMOS legacy analog device to be formed in this example.

FIG. 15 shows an implanted P-type threshold voltage layer (V_T) 1500 for use in a PMOS legacy digital logic device of this example.

FIG. 16 shows an implanted N-type V_T layer 1600 for use in the PMOS legacy digital logic device of this example.

FIG. 17 shows an implanted analog P-type V_T layer 1700 for the PMOS legacy analog device in this example.

FIG. 18 shows an implanted analog N-type V_T layer 1800 for the NMOS legacy analog device in this example.

FIG. 19 shows STI formations 1902-1918 located between, down through the shallow wells of each device.

FIG. 20 shows gate oxidation layers 2002 CON1-2016 performed on each device, including single, double and triple gate oxidation layers for different devices. In this example, thin single oxidation layers are formed for digital devices, and relatively thicker double or triple oxidation for analog devices.

FIG. 21 shows a polygate layer 2100 formed over all devices.

FIG. 22 shows the selective removal of the polygate and oxidation layers to form separate gates and corresponding gate oxide layers 2202-2232.

FIG. 23 shows the forming of P-type LDD 2302-2308 on two digital devices, the NMOS DDC digital logic device and NMOS legacy digital logic device in this example.

FIG. 24 shows the formation of N-type LDD 2402-2408 on two other digital devices, the PMOS DDC digital logic device and PMOS legacy digital logic device in this example.

FIG. 25 shows the formation of P-type LDD 2502-2508 on two analog devices, the PMOS DDC analog device and PMOS legacy analog device in this example.

FIG. 26 shows the formation of N-type LDD 2602-2604 on two other analog devices, the NMOS DDC analog device and NMOS legacy analog device in this example.

FIG. 27 shows the formation of spacers 2702-2732 for each gate stack.

FIG. 28 shows the implantation of P-type material 2802-2824 in P-type digital and analog devices, including the PMOS DDC logic device, the PMOS DDC analog device, the PMOS legacy logic device and PMOS legacy analog device in this example.

FIG. 29 shows the implantation of N-type material 2902-2924 in N-type digital and analog devices, including the NMOS DDC digital logic device, NMOS DDC analog device, the NMOS legacy digital logic device, and the NMOS legacy analog device in this example.

FIG. 30 illustrates deposition of silicide 3002 CON1-3048 on each device's exposed source, gate and drain. Body bias 3050 communicating with the well or body of device 702 is included to illustrate the possibility of biasing the body of any one of the transistors in order to control the V_T of one or more devices. Thus, the devices formed in FIG. 30 include:

• • a PMOS DDC digital logic device 702;
  • an NMOS DDC digital logic device 704;
  • a PMOS DDC analog device 706;
  • an NMOS DDC analog device 708;
  • a PMOS legacy digital logic device 710;
  • an NMOS legacy digital logic device 712;
  • a PMOS legacy analog device 714; and
  • an NMOS legacy analog device 716.

There are many different approaches to processing these novel features and structures. Those skilled in the art will understand that, given this disclosure, there are numerous variations on the particular manufacturing process steps and parameters for making such circuits. The following are examples.

In one exemplary process, and oxide layer is formed in a temperature range of 700 to 900° C. over a period of 0 to 60 seconds.

For the PMOS well implants, the P+ implant may be implanted within a range from 10 to 80 keV, and at concentrations from 1×10¹³ to 8×10¹³/cm². As+ may be implanted within a range of 5 to 60 keV, and at concentrations from from 1×10¹³ to 8×10¹³/cm².

For NMOS well implants, the boron implant B+ implant may be within a range of 0.5 to 5 keV, and within a concentration range of 1×10¹³ to 8×10¹³/cm². A germanium implant Ge+, may be performed within a range of 10 to 60 keV, and at a concentration of 1×10¹⁴ to 5×10¹⁴/cm². A carbon implant, C+, may be performed at a range of 0.5 to 5 keV, and at a concentration of 1×10¹³ to 8×10¹³/cm².

A low temperature recrystallization anneal may be performed at a range of 550-600° C., over a period of 30 to 150 seconds.

A high temperature defect elimination anneal may be performed within a range of 900 to 1025° C. over a period of 0 to 10 seconds.

An EPI deposition of intrinsic Si may be performed within a range of 500 to 700° C., and at a thickness of 10 to 75 nm.

A shallow trench isolation, trench patterning, trench etch, sacrificial oxidation, trench fill, trench polish may be performed also.

Standard CMOS processing beyond this point including all standard thermal cycles, such as for example poly-Si deposition/etch, SPCR deposition/etch, multiple spike anneals, and other processes may be performed within a range of 900 to 1025° C.

In another process, where some devices on the wafer are DDC type devices and others are non-DDC type devices, a process may include the same process flow as that described immediately above, where some implants may be selectively masked over certain devices that do not need DDC process.

In yet another process, a process may include the same process flow as that described immediately above, where some implants are selectively performed after an EPI deposition instead of before an EPI deposition in order to form non-DDC configured devices in those regions.

While certain exemplary embodiments have been described and shown in the accompanying drawings, it is to be understood that such embodiments are merely illustrative of and not restrictive on the broad invention, and that this invention not be limited to the specific constructions and arrangements shown and described, since various other modifications may occur to those ordinarily skilled in the art. Accordingly, the specification and drawings are to be regarded in an illustrative rather than a restrictive sense.

Claims

1. An integrated circuit having transistor devices of a plurality of device types formed on a substrate, comprising: a first screening layer for a first device type, the first screening layer being positioned below a first gate insulator of the first device type, the first screening layer haying a first dopant concentration;a second screening layer for a second device type, the second screening layer being positioned below a second gate insulator of the second device type, the second screening layer having a second dopant concentration;a threshold voltage layer for a third device type, the threshold voltage layer being positioned below a third gate insulator of the third device type, the threshold voltage layer having a third dopant concentration;a first substantially undoped layer for the first device type being positioned above and adjacent to the first screening layer;a second substantially undoped layer for the second device type being positioned above and adjacent to the second screening layer,a shallow trench isolation isolating the first device type, the second device type and the third device type;a first source and drain region for the first device type penetrating the first substantially undoped layer and the first screening layer;a second source and drain region for the second device type penetrating the second substantially undoped layer and the second screening layer,wherein a thickness of the first gate insulator is different from a thickness of the second gate insulator and a depth position of the threshold voltage layer is different from each of a depth of position of the first screening layer and the second screening layer.

2. The integrated circuit of claim 1, wherein the first screening layer for the first device type further includes a first P-type screening layer for a first transistor element of the first device type, and a first N-type screening layer for a second transistor element of the first device type.

3. The integrated circuit of claim 1, further comprising: a body tap operable to apply a body bias voltage to a body of the first transistor element of the first device type.

4. The integrated circuit of claim 1, wherein the second screening layer for the second device type further includes a second P-type screening layer for a first transistor element of the second device type, and a second N-type screening layer for a second transistor element of the second device type.

5. The integrated circuit of claim 1, further comprising: a body tap operable to apply a bias voltage to a body of the first transistor element of the second device type.

6. The integrated circuit of claim 1, further comprising: one of a single, double, or triple gate oxidation layers for each device.

7. The integrated circuit of claim 1, wherein a thickness of the first substantially undoped layer is same to a thickness of the second substantially undoped layer.

8. The integrated circuit of claim 1, further comprising: a first Lightly Doped Drain (LDD) for the first device type and a second LDD for the second device type, a depth position of the first LDD is different from a depth position of the second LDD.

9. The integrated circuit of claim 8, further comprising: a third Lightly Doped Drain for the third device type, a depth position of the third LDD is same to the depth position of the second LDD.

10. The integrated circuit of claim 1, wherein a thickness of the second gate insulator is same to a thickness of the third gate insulator.

11. The integrated circuit of claim 1, wherein the first device type is a Deeply Depleted Channel (DDC) logic device, the second device type is a DDC analog device, the third device type is a legacy analog device.

12. The integrated circuit of claim 1, further comprising a dopant migration resistant layer between the first screening layer and the first substantially undoped layer.

13. The integrated circuit of claim 12, wherein the dopant migration resistant layer includes carbon.

14. The integrated circuit of claim 12, wherein the dopant migration resistant layer further includes SiGe deposited before forming the substantially undoped layer.