The present invention is related to plasma processing, particularly to cleaning and removal of photoresist and etch residues following an etch process in semiconductor microfabrication.
Plasma processing systems are used in the manufacture and processing of semiconductors, integrated circuits, displays, and other devices or materials to both remove material from or to deposit material on a substrate such as a semiconductor substrate. Plasma processing of semiconductor substrates to transfer a pattern of an integrated circuit from the photolithographic mask to the substrate, or to deposit dielectric or conductive films on the substrate, have become standard methods in the industry.
In semiconductor processing, where various types of films are etched, integration challenges and trade-offs still remain. Conventionally, a dielectric layer is patterned with openings for depositing conductive materials to form vertical contacts. During the patterning process, etch resistant photoresist layer and/or a hard mask layer is deposited over the dielectric layer, exposed to a selected pattern and developed. The layered structure is then etched in a plasma environment where the patterned photoresist layer defines openings in the dielectric layer.
Following the etch step, photoresist remnants and etch residues (e.g., polymer debris) are frequently observed on the etched features and chamber surfaces. One of the integration challenges in plasma cleaning (also known as in-situ ashing), is to successfully remove photoresist remnants and etch residues, while avoiding erosion of surrounding layers. Known systems have used a one-step ashing process in which the bias applied to the substrate is maintained constant throughout the ashing process.
Halocarbon gases are commonly used in the etching of dielectric layers, such as oxides and newer SiOC-containing low-k dielectric materials. These gases are known to generate fluoro-carbon polymer etch products, that can deposit on the internal surfaces of the processing chamber, as well as on the substrate surface, during the dielectric etch process.
During a conventional one-step ash process, photoresist can be removed in an oxygen-containing plasma. To avoid post-ash residue formation, some bias power is applied to the substrate holder. During this process, the fluoro-carbon deposits on the chamber walls from the preceding dielectric etch are also etched, releasing fluorine radicals in the plasma. As bias is applied to the substrate holder, these fluorine radicals can erode the underlying dielectric film and consume the cap layer. By reducing the bias or applying zero bias, dielectric film erosion and cap layer consumption can be reduced but post-ash residue can still be observed.
A conventional one-step ash process, that can result in the above chamber problems, can involve the following plasma process conditions: Chamber pressure=50 mTorr, RF bias=150 W, O2 flow rate=200 sccm.
In semiconductor manufacturing, the conventional one-step ash process is frequently carried out in a processing chamber where the internal chamber surfaces (and the substrate to be ashed) can contain fluoro-carbon-based polymer deposits from a preceding dielectric etch process. Alternatively, the one-step ash process can be carried out in a processing chamber that has been cleaned of polymer deposits from a prior etch process.
It is an object of the invention to provide a plasma processing method for removing photoresist remnants and etch residues from a substrate with reduced erosion of the surrounding substrate layers compared to one-step ashing.
The above and other objectives are accomplished using a two-step in-situ plasma ashing process utilizing a process gas comprising an oxygen-containing gas. During the first ashing step, a first low or zero bias level is applied to the substrate holder upon which a substrate resides, while a second bias level is applied during the second ashing step. The pressure in the plasma processing chamber in the second ashing step is less than 20 mTorr.
During the first ashing step, where low or zero bias is applied to the substrate, a significant amount of photoresist remnants and etch residues on the substrate and internal surfaces/walls of the processing chamber are etched and removed from the chamber, while erosion of the remaining substrate layers is minimized. During the second ashing step, an increased bias is applied and the ashing process is continued until the photoresist remnants and etch residues are removed.
A more complete appreciation of the invention and many of the attendant advantages thereof will become readily apparent with reference to the following detailed description, particularly when considered in conjunction with the accompanying drawings, in which:
The inventors of related U.S. patent application Ser. No. 10/259,768, entitled LOW-PRESSURE METHOD FOR REMOVING PHOTORESIST AND ETCH RESIDUE, which are the inventors of the present application, realized that a two-step plasma ashing process can be utilized to remove photoresist remnants and etch residues from a substrate. During the first ashing step, where zero or low bias is applied to a substrate holder upon which a substrate resides, a significant amount of photoresist remnants and etch residues, from preceding etch processes that can, for example, utilize CxFy etch gases, are etched and removed from the processing chamber with minimal erosion of the remaining substrate layers. During the second ashing step, an increased bias is applied to the substrate holder and the ashing process is continued until the photoresist and/or hard mask remnants, and post-ash residues are removed.
The current inventors have realized that if the above-mentioned second ashing step is performed at a very low pressure (less than 20 mTorr) in the plasma processing chamber, the process can reduce or eliminate detrimental oxidation of underlying dielectric substrate layers, for example low dielectric constant (low-k) materials such as SiOC materials (k˜2.7). The reduced oxidation has been attributed to lower concentration of oxygen-containing radicals in the plasma environment at low processing chamber pressure.
Thus, according to an embodiment of the invention, a process pressure less than 20 mTorr is utilized in the processing chamber during the second ashing step of the two-step ashing process. According to another embodiment of the invention, a process pressure less than about 10 mTorr can be utilized in the processing chamber during the second ashing step.
A two-step in-situ ash process according to the current invention can alleviate many of the above shortcomings by satisfying at least one of: 1) minimizing cap layer consumption; 2) minimizing dielectric faceting/erosion at the top of features, and reducing post-etch/critical-dimension (CD) bias; 3) minimizing post-ash residues; 4) minimizing damage (increase in “k” value) induced to low-k dielectric films during in-situ ash; and 5) providing automatic chamber dry cleaning, thereby increasing mean-time-between-chamber-cleaning.
During the second ashing step 130, bias is applied, and the ashing is carried out for a time sufficient to remove any post-ash residue 110 and any remaining photoresist 106.
The current invention can, for example, be carried out using a plasma processing system containing a capacitively coupled plasma source having an upper electrode and a lower electrode. The upper electrode can, for example, further function as a showerhead for introducing a process gas into the processing chamber, and the lower electrode can be a substrate holder configured for supporting a substrate to be processed and for applying a bias to the substrate. Capacitively coupled plasma sources are well known to persons skilled in the art. The current invention can also be carried out using other types of plasma sources including, for example, an inductive coupling plasma source (ICP).
Exemplary process parameters for the first ashing step of the two-step ashing process according to embodiments of the current invention will now be described. In one embodiment of the invention, the chamber pressure can be between about 1 mTorr and about 1000 mTorr. According to another embodiment of the invention, the chamber pressure can be between about 5 mTorr and about 50 mTorr. A process gas flow rate of about 5 sccm to about 1500 sccm can be used in the processing chamber. A process gas containing an oxygen-containing gas (e.g., O2) can be used alone, but it may also be used in conjunction with an inert gas (e.g., a noble gas (He, Ar, etc.) or N2). The flow rate of the oxygen-containing gas can, for example, be between about 5 sccm and about 500 sccm and the flow rate of the inert gas can, for example, be between about 0 sccm and about 1000 sccm. A bias power (lower electrode power) can, for example, be between about 0 W and about 100 W, an upper electrode power, can for example, between about 500 W and about 2200 W, and the substrate temperature can be between about −10° C. and about 250° C.
In one example, the process parameters for the first ashing step includes a chamber pressure of 20 mTorr, an Ar flow rate of 550 sccm, an O2 flow rate of 200 sccm, an upper electrode power of 300 W, and a lower electrode power of 0 W. The time duration of the first ashing step can, for example, be about 35 sec.
In the second ashing step of the two-step ashing process, the process parameter space can include the same conditions described above for the first ashing step, except that the chamber pressure in the second ashing step is less than 20 mTorr. In an embodiment of the invention, the chamber pressure in the second ashing step can be less than about 10 mTorr. In another embodiment of the invention, the chamber pressure in the second ashing step can be less than about 5 mTorr. A bias between about 50 W and about 1000 W can be used, where the bias applied to the substrate holder in the second ashing step (second bias) is greater than the bias applied to the substrate holder in the first ashing step (first bias).
Although a RF bias is disclosed as being used, a DC bias may also be used or may be used instead of a RF bias. Additionally, chamber pressure can be varied during the ashing process. For example, the chamber pressure can be varied from the first step to the second step. Furthermore, the composition of the process gas can be varied during the ashing process. For example, the process gas (and flow ratios of different gases in the process gas) can be varied from the first step to the second step.
In one example, 200 mm silicon wafers were processed. The process parameters during the second ashing step included a chamber pressure of 10 mTorr, an upper electrode power of 300 W, a lower electrode power of 300 W, an O2 gas flow rate of 300 sccm (without using an inert gas), and a substrate temperature of 50° C. The substrate was exposed to the plasma environment for 35 sec in the second ashing step.
In another example, 300 mm silicon wafers were processed. The process parameters during the second ashing step included a chamber pressure of 15 mTorr, an upper electrode power of 300 W, a lower electrode power of 400 W, an O2 gas flow rate of 400 sccm (without using an inert gas), and a substrate temperature of 50° C. The substrate was exposed to the plasma environment for 35 sec in the second ashing step.
Alternatively, during the two-step process, a bias can be applied when substantially all (but not all) of the polymer has been removed from the chamber in order to increase throughput, but at a cost of reintroducing some of the effects of the conventional one-step process.
Furthermore, although described above as using only a single bias, a varying bias can be used instead. For example, the bias may be increased (either continuously or stepwise) before, during, or after the second step.
As described above, the time duration for the first step should be sufficiently long to complete the removal of fluoro-carbon material from the chamber walls and wafer surface. For example, the time duration for the first step can range from 10 sec to 100 sec. In another example, the time duration for the first step ranges from 20 to 50 sec. Similarly, the time duration for the second step should be sufficiently long to remove any post-ash residue and any remaining photoresist. For example, the time duration for the second step can range from 10 sec to 100 sec. In another example, the time duration for the second step ranges from 20 to 50 sec.
Alternatively, in the two-step ashing process in
After the end of the first step, the second step preferably utilizes a 50-200% overash to remove any remaining post-ash residue (PAR). That is, if the first step is completed in 50 sec, the second step would be 25 sec for a 50% overash and 50 sec for a 100% overash. The actual amount of overash can be determined empirically by examining a series of substrates that are overashed to different degrees.
a) First ash step: Chamber pressure=50 mTorr, RF bias =0 W, O2 flow 200 sccm, Second ash step: Chamber pressure=20 mTorr, RF bias=150 W, O2 flow=20 sccm, Ar/O2 flows=200/20 sccm;
b) Chamber pressure=50 mTorr, RF bias=150 W, O2 flow 200 sccm; and
c) Chamber pressure=50 mTorr, RF bias=150 W, O2 flow 200 sccm.
A reduced cap layer loss 140 is observed in the above two-step ash process (a), when compared to the one-step ash processes (b) and c)). For example, the cap layer loss decreases in the order c)>b)>a), as shown in TABLE 1. As a result, the two-step process provides an ash method that minimizes cap layer loss. The two-step process a) utilized a chamber pressure of 20 mTorr. However, it is believed that a chamber pressure less than 20 mTorr in the current invention further reduces cap layer loss.
Importantly,
Damage to sidewalls of a dielectric layer that occurs during an ash process, is critical in semiconductor manufacturing. Following a plasma ash, the damage can be evaluated by measuring dielectric sidewall loss due to exposure to a HF etching solution.
The process conditions in ash process d) were: First ash step: Chamber pressure=20 mTorr, RF bias=0 W, O2 flow 500 sccm; Second ash step: Chamber pressure=20 mTorr, RF bias=150 W, O2 flow 20 sccm, Ar/O2 flows=200/20 sccm.
The plasma ashed substrates were exposed to a 0.5% HF solution for 5 sec to 30 sec. SEM analysis of sidewall loss for a 30 sec HF exposure is shown in TABLE 2 for ashing processes a)-d). In summary, the dielectric sidewall loss (and therefore sidewall damage during the ash process) is less for the two-step ash process d) (where a lower chamber pressure and higher O2 flow are utilized), than the two-step process a). In addition, the one-step process b), which was carried out in a clean chamber, shows less dielectric sidewall loss than one-step process c) and two-step process a), that were both carried out in chambers with polymer deposits.
An ionizable process gas 42 is introduced via the gas injection system 40 and the process pressure is adjusted. The flow rate of the process gas can be between about 10 sccm and about 5000 sccm, alternately between about 20 sccm and about 1000 sccm, and still alternately between about 50 sccm and about 500 sccm. The chamber pressure can, for example, be between about 1 mTorr and about 200 mTorr, alternately between about 5 mTorr and about 100 mTorr, still alternately between about 10 mTorr and about 50 mTorr. The controller 55 can be used to control the vacuum pumping system 50 and gas injection system 40. Substrate 25 is transferred into process chamber 10 through a slot valve (not shown) and chamber feed-through (not shown) via a (robotic) substrate transfer system where it is received by substrate lift pins (not shown) housed within substrate holder 20 and mechanically translated by devices housed therein. Once the substrate 25 is received from the substrate transfer system, it is lowered to an upper surface of the substrate holder 20.
In an alternate embodiment, the substrate 25 is affixed to the substrate holder 20 via an electrostatic clamp (not shown). Furthermore, the substrate holder 20 further includes a cooling system including a re-circulating coolant flow that receives heat from the substrate holder 20 and transfers heat to a heat exchanger system (not shown), or when heating, transfers heat from the heat exchanger system. Moreover, gas may be delivered to the backside of the substrate to improve the gas-gap thermal conductance between the substrate 25 and the substrate holder 20. Such a system is utilized when temperature control of the substrate is required at elevated or reduced temperatures. For example, temperature control of the substrate may be useful at temperatures in excess of the steady-state temperature achieved due to a balance of the heat flux delivered to the substrate 25 from the plasma and the heat flux removed from substrate 25 by conduction to the substrate holder 20. In other embodiments, heating elements, such as resistive heating elements, or thermoelectric heaters/coolers are included in the substrate holder 20.
The plasma processing system 1 of
With continuing reference to
Vacuum pump system 50 can include a turbo-molecular vacuum pump (TMP) capable of a pumping speed up to 5000 liters per second (and greater), and a gate valve for throttling the chamber pressure. In conventional plasma processing devices utilized for dry plasma etch, a 1000 to 3000 liter per second TMP is employed. TMPs are useful for low pressure processing, typically less than 50 mTorr. For high pressure processing (i.e. greater than 100 mTorr), a mechanical booster pump and dry roughing pump are used.
A controller 55 includes a microprocessor, a memory, and a digital I/O port capable of generating control voltages sufficient to communicate and activate inputs to the plasma processing system 1 as well as monitor outputs from the plasma processing system 1. Moreover, the controller 55 is coupled to and exchanges information with the RF generator 30, the impedance match network 32, the RF generator 72, the impedance match network 74, the gas injection system 40, plasma monitor system 57, and the vacuum pump system 50. A program stored in the memory is utilized to control the aforementioned components of a plasma processing system 1 according to a stored process recipe. One example of controller 55 is a digital signal processor (DSP); model number TMS320, available from Texas Instruments, Dallas, Tex.
The plasma monitor system 57 can comprise, for example, an optical emission spectroscopy (OES) system to measure excited particles in the plasma environment and/or a plasma diagnostic system, such as a Langmuir probe, for measuring plasma density. The plasma monitor system 57 can be used with controller 55 to determine the status of the etching process and provide feedback to ensure process compliance. Alternately, plasma monitor system 57 can comprise a microwave and/or a RF diagnostic system.
In addition, it is to be understood that the plasma processing systems depicted in
Numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that, within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.
The present application is related to co-pending U.S. patent application Ser. No. 10/259,768, filed on Sep. 30, 2002, the entire contents of which is herein incorporated by reference. The present application is related to copending United States patent application entitled “LOW-PRESSURE REMOVAL OF PHOTORESIST AND ETCH RESIDUE”, Attorney docket no. 227618US-6YA, filed on Sep. 30, 2002, the entire contents of which is herein incorporated by reference.