Method for contact-connecting a semiconductor component

Information

  • Patent Grant
  • 6773956
  • Patent Number
    6,773,956
  • Date Filed
    Tuesday, January 28, 2003
    21 years ago
  • Date Issued
    Tuesday, August 10, 2004
    19 years ago
Abstract
A solder metal made of a eutectic or stoichiometric composition including at least two metallic or semiconducting elements is applied to a contact (of the semiconductor component, brought into contact with the metal layer of a metallized film and alloyed by heating into the metal layer of the film, thereby producing an electrically conductive connection having a higher melting point. A solder metal that is particularly suitable for such a purpose is the Bi22In78 (melting point 73° C.), Bi43Sn57, or In52Sn48, or BiIn, or BiIn2.
Description




BACKGROUND OF THE INVENTION




Field of the Invention




The present invention relates to a method for contact-connecting a semiconductor component to a metallization on a film.




With electrically conductive adhesives, electrically conductive connections can be produced even at a low processing temperature. However, for curing, many adhesives of this type actually need higher temperatures, at which the plastics material of a film is damaged or a metallization applied thereto is detached. Moreover, the electrical conductivity is insufficient for many applications, and the connection produced is sensitive to moisture. Particularly if a contact of an electronic component (e.g., an Si-IC Chip) is intended to be electrically conductively connected to a metal layer (e.g., made of copper or nickel) of a metallized plastic film, in the case of which the limit of thermal loadability is about 120° C. and in the case of which the applied metal layer is very thin (typically about 100 nm), it is difficult, with conductive adhesive, to produce a sufficiently lasting and readily conductive connection that cannot be detached without destroying the film.




SUMMARY OF THE INVENTION




It is accordingly an object of the invention to provide a method for contact-connecting a semiconductor component to a metallized plastic film that overcomes the hereinafore-mentioned disadvantages of the heretofore-known devices and methods of this general type and that can be performed at a temperature at which the film is not damaged and which yields a permanent electrically conductive connection of sufficient conductivity.




With the foregoing and other objects in view, there is provided, in accordance with the invention, a method for contact-connecting a semiconductor component to a film provided with a metal layer, including the steps of disposing a solder material between a contact of the semiconductor component and the metal layer of the film, the solder material containing at least two different substances selected from a group consisting of elementary metals and semiconductor materials and having a melting point at a temperature at which the film is not damaged, and subsequently causing the solder material to melt and thereafter solidify and, thereby, produce a permanent electrically conducted connection of a material having a melting point higher than the melting point of the disposed solder material.




In accordance with another mode of the invention, a solder material, preferably, a metal, made of at least two metallic or semiconducting chemical elements is applied to a contact of the semiconducting component or to the metal layer of the film at the location provided for a contact connection. The solder material is configured such that it has a melting point that lies below a critical temperature for the resistivity of the film, and that it forms, after melting, a material that, after solidification, has a higher melting point than the original solder material. The molten solder material is, preferably, configured such that it forms an alloy or intermetallic compound or phase with the metal of the metal layer of the film or with the metal of the contact of the semiconductor component. The melting point is, preferably, so high that, in the event of an attempt to melt the solder connection, the film would inevitably be damaged or at the very least the metal layer would be detached from the film and the entire configuration would, thus, become unusable.




A solder material that is particularly suitable for such a purpose is a composition—i.e., a blend of at least and, preferably, two components that form a mixture, an alloy, or a stoichiometric compound—whose proportions are chosen such that the composition lies at a eutectic point or at least in the vicinity of a eutectic point. Specifically, it holds true for such a choice of the composition that the melting point of the composition increases in the event of any change in the proportions of the components. When the solder material melts, an alloy or an intermetallic compound is produced that contains a proportion of the metal of the metal layer of the film or of the contact of the semiconductor component so that the composition of the material forming the electrically conductive connection differs from the eutectic of the original composition of the solder material to such a significant extent, that the melting point is considerably higher, in particular, above the temperatures that are safe for the film. In such a case, an approximately eutectic composition shall be defined as a composition having a melting point that differs from the eutectic temperature by at most 10° C.




In accordance with a further mode of the invention, a solder material is selected with which, in the melting and solidification step, one of an alloy and an intermetallic compound having a higher melting point is formed with a metal of the metal layer of the film.




In accordance with an added mode of the invention, the solder material, in the melting and solidification step, forms, with a metal of the metal layer of the film, one of an alloy and an intermetallic compound having a higher melting point than the melting point of the solder material.




In accordance with an additional mode of the invention, a solder material is utilized having a melting point at most 10° C. above a temperature of a eutectic composition of the substances contained in the solder material.




A material that is appropriate as a possible solder material, preferably, in conjunction with a metal layer of the film made of copper or nickel, is primarily a material containing bismuth (chemical symbol Bi). Eutectic or approximately eutectic (difference in temperature from the eutectic at most 10° C.) compositions that achieve what is desired are materials from the group of a composition including bismuth and indium, a composition including bismuth and tin, and a composition including indium and tin. The eutectic compositions of these materials in relative atomic masses are Bi


22


In


78


, Bi


43


Sn


57


, or In


52


Sn


48


. The material Bi


22


In


78


forms a eutectic composition having the melting point of 72.7° C. A solder connection can, thus, be produced at approximately 80° C. The solder material Bi


22


In


78


is applied, e.g., to the contact of the semiconductor component, which can be done by sputtering. The solder material, then, forms a thin layer on the contact. The layer is brought into contact with the metal layer of the film and, as required, kept under slight pressure. Through heating to a temperature above the melting point of the solder material, the solder material is melted and alloys with the metal of the metal layer of the film to form a material that forms an electrically conductive connection between the contact of the semiconductor component and the metal layer of the film that can be subjected to loading up to at least 270° C. With the use of a film whose thermal loadability extends up to a maximum of about 120° C., the connection can, therefore, be produced without difficulty at about 80° C. Afterwards, the connection can no longer be melted without destroying the film.




In accordance with yet another mode of the invention, a solder material is utilized including one of an intermetallic compound of one of BiIn and BiIn


2


and a phase of one of BiIn and BiIn


2


.




In accordance with yet a further mode of the invention, the solder material is applied in the disposing step by electron beam vaporization onto one of the contact of the semiconductor component and the metal layer of the film.




In accordance with yet an added mode of the invention, electron beam vaporization is used to apply the solder material onto one of the contact of the semiconductor component and the metal layer of the film.




In accordance with yet an additional mode of the invention, the solder material is applied in the disposing step with a layer thickness limited in comparison with a thickness of the metal layer of the film to permit at least a portion of the metal layer of the film to remain unchanged after the melting and solidification step.




In accordance with a concomitant mode of the invention, there is provided the step of insuring that at least a portion of the metal layer of the film remains unchanged after the melting and solidification step by applying the solder material with a layer thickness limited in comparison with a thickness of the metal layer of the film.




Other features that are considered as characteristic for the invention are set forth in the appended claims.




Although the invention is illustrated and described herein as embodied in a method for contact-connecting a semiconductor component, it is, nevertheless, not intended to be limited to the details shown because various modifications and structural changes may be made therein without departing from the spirit of the invention and within the scope and range of equivalents of the claims.




The construction and method of operation of the invention, however, together with additional objects and advantages thereof, will be best understood from the following description of specific embodiments when read in connection with the accompanying drawings.











BRIEF DESCRIPTION OF THE DRAWINGS




The FIGURE of the drawing is a partially hidden perspective view of a semiconductor component configuration according to the invention.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




Referring now to the single FIGURE of the drawing, it is seen that a semiconductor component


1


with a contact


2


and with a metal layer


3


of a film


4


that is provided on the contact. The dimensions of the film and of the component, the number and the dimensions of the contacts connected to the metallized film, and the number of layers that form the film and the metal layer are arbitrary.




To prevent the situation wherein, in the event of an excess of solder material a) the metal layer of the film alloys with the solder material in its entire thickness and, under certain circumstances, detaches from the film and b) non-alloyed solder material remains that still melts at a low temperature, at 72.7° C. in the example, the thickness of the applied solder layer is, preferably, limited. The solder material is applied, then, only with a layer thickness that ensures that the entire solder material forms an alloy or a stoichiometric intermetallic compound with the metal of the contact or the metal layer of the film and at least a layer portion of the original metal of the metal layer of the film that adheres to the film remains unchanged. When the solder material melts, the supply of solder material present between the contact of the semiconductor component and the metal layer of the film is, consequently, used up more rapidly than the metal of the metal layer. What is thereby achieved is that the metal layer does not alloy through to the film itself nor does unalloyed solder material remain. The melting point of the material of the connection produced is determined by the lowest melting point of the thermodynamic phases present in the connection zone.




In an exemplary embodiment in which a component is contact-connected to a film with a nickel metal layer having a thickness of 100 nm, a layer of Bi


22


In


78


having a thickness of 100 nm can be sputtered onto the contact of the component. The electrically conductive connection is produced within a few seconds in the event of heating to 80° C. and can be subjected to loading up to 650° C.




The further eutectic compositions specified above have the melting points 139° C. (Bi


43


Sn


57


) and 117° C. (In


52


Sn


48


). These compositions can be used in each case if the film used can be safely heated a few degrees Celsius above the relevant temperature value. The intermetallic phases BiIn and BiIn


2


, which are metallic compounds including bismuth and indium in stoichiometric ratios, melt at 109.5° C. and at 89° C., respectively. These are, likewise, temperatures that are still innocuous for customary plastic films. An intermetallic phase affords the advantage that it vaporizes as sole phase at a specific temperature and does not vaporize like a mixture of substances with different vapor pressures of the components contained therein. Therefore, if such an intermetallic phase or stoichiometric composition is used as solder material, it is possible to apply the solder material by electron beam vaporization.



Claims
  • 1. A method for contact-connecting a semiconductor component to a film provided with a metal layer, which comprises:selecting a solder material: containing at least two different substances selected from a group consisting of elementary metals and semiconductor materials, having a melting point at a temperature at which the film is not damaged, and being combinable with a metal to form one of an alloy and an intermetallic compound having a higher melting point than the film; disposing the solder material between a contact of the semiconductor component and the metal layer of the film; and subsequently causing the solder material to melt, combine with one of a metal of the contact of the semiconductor component and a metal of the metal layer of the film to form one of an alloy and an intermetallic compound having a higher melting point than the film, thereafter solidify, and produce a permanent electrically conducted connection of a material having a melting point higher than the melting point of the disposed solder material.
  • 2. The method according to claim 1, which further comprises selecting a solder material with which, in the melting and solidification step, one of an alloy and an intermetallic compound having a higher melting point is formed with a metal of the metal layer of the film.
  • 3. The method according to claim 1, wherein the solder material, in the melting and solidification step, forms, with a metal of the metal layer of the film, one of an alloy and an intermetallic compound having a higher welting point than the melting point of the solder material.
  • 4. The method according to claim 1, which further comprises utilizing a solder material having a melting point at most 10° C. above a temperature of a eutectic composition of the substances contained in the solder material.
  • 5. The method according to claim 1, which further comprises utilizing a solder material containing bismuth.
  • 6. The method according to claim 1, which further comprises utilizing a solder material of a material selected from a group consisting of:a composition including bismuth and indium, a composition including bismuth and tin; and a composition including indium and tin.
  • 7. The method according to claim 6, which further comprises utilizing a solder material of a material selected from a group consisting of Bi22In78, Bi43Sn57, and In52Sn48.
  • 8. The method according to claim 1, which further comprises utilizing a solder material of a material selected from a group consisting of Bi22In78, Bi43S57, and In52Sn48.
  • 9. The method according to claim 6, which further comprises utilizing a solder material of a material including one of:an intermetallic compound of one of BiIn and BiIn2; and a phase of one of BiIn and BiIn2.
  • 10. The method according to claim 5, which further comprises applying the solder material in the disposing step by sputtering the solder material onto one of the contact of the semiconductor component and the metal layer of the film.
  • 11. The method according to claim 6, which further comprises sputtering the solder material onto one of the contact of the semiconductor component and the metal layer of the film.
  • 12. The method according to claim 9, which further comprises applying the solder material in the disposing step by electron beam vaporization onto one of the contact of the semiconductor component and the metal layer of the film.
  • 13. The method according to claim 9, which further comprises utilizing electron beam vaporization to apply the solder material onto one of the contact of the semiconductor component and the metal layer of the film.
  • 14. The method according to claim 1, which further comprises applying the solder material in the disposing step with a layer thickness limited in comparison with a thickness of the metal layer of the film to permit at least a portion of the metal layer of the film to remain unchanged after the melting and solidification step.
  • 15. The method according to claim 1, which further comprises insuring that at least a portion of the metal layer of the film remains unchanged after the melting and solidification step by applying the solder material with a layer thickness limited in comparison with a thickness of the metal layer of the film.
  • 16. The method according to claim 1, wherein the forming of the one of the alloy and the intermetallic compound occurs at a lower temperature than the melting point of the one of the alloy and the intermetallic compound.
Priority Claims (1)
Number Date Country Kind
00116427 Jul 2000 EP
CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of copending International Application No. PCT/EP01/08610, filed Jul. 25, 2001, which designated the United States and was not published in English.

US Referenced Citations (19)
Number Name Date Kind
3839727 Hedzik et al. Oct 1974 A
4811170 Pammer Mar 1989 A
4834794 Yagi et al. May 1989 A
5291371 Gruber et al. Mar 1994 A
5320272 Melton et al. Jun 1994 A
5391514 Gall et al. Feb 1995 A
5415944 Kazem-Goudarzi et al. May 1995 A
5442145 Imai et al. Aug 1995 A
5540379 Kazem-Goudarzi et al. Jul 1996 A
5729896 Dalal et al. Mar 1998 A
5888841 Zynder Mar 1999 A
5907187 Koiwa et al. May 1999 A
5928404 Paruchuri et al. Jul 1999 A
5972246 Nikaidoh et al. Oct 1999 A
6130476 LaFontaine, Jr. et al. Oct 2000 A
6196443 DiGiacomo Mar 2001 B1
6250541 Shangguan et al. Jun 2001 B1
6388185 Fleurial et al. May 2002 B1
6524888 Cokely et al. Feb 2003 B2
Foreign Referenced Citations (4)
Number Date Country
195 31 158 Feb 1997 DE
0 426 303 May 1991 EP
0 426 303 May 1991 EP
0 530 780 Mar 1993 EP
Non-Patent Literature Citations (2)
Entry
Morris, J. W. et al.: “Microstructure and Mechanical Properties of Sn-ln and Sn-Bi Solders”, JOM, US, Minerals, Metals and Materials Society, Warrendale, vol. 45, No. 7, Jul. 1993, pp. 25-27.
Rai, R.S. et al.: “Interfacial Reactions with Lead (Pb)-Free Solders”, IEEE, 1995 Proceedings, 45th Electronic Components and Technology Conference, May 24, 1995, pp. 1197-1202.