1. Field of the Invention
The present invention, generally, relates to a method for forming metal wirings that can be used favorably in the creation of fine semiconductor elements. More specifically, the present invention relates to a method for forming a metal film by atomic layer deposition using a β-diketone metal complex.
2. Description of the Related Art
Next-generation fine semiconductor elements require formation of semiconductor elements having not only two-dimensional structures, but also three-dimensional structures. Accordingly, the formation of metal wirings for such fine semiconductor elements also requires the ratio of wiring height to wiring width to be improved to a range of 5 to 10, and the ratio of height to hole diameter to a range of approx. 5 to 10 for connection holes used to connect top-layer wirings and bottom-layer wirings. For this reason, it becomes necessary, when forming copper wirings for use as these metal wirings, to form a thin metal film that not only provides a copper diffusion barrier to prevent diffusion of copper, but also achieves good shielding property.
To this end, wiring structures having such high aspect ratios are creating a need to form metal films using the CVD method and ALD method known to achieve good shielding property, instead of forming metal films using the conventional PVD method. In particular, metal films that serve as Cu diffusion barriers must be thin, low in resistivity in order to prevent an increase of the wiring resistance, and formed in a manner ensuring good shielding property in areas of high aspect ratios, and these requirements necessitate use of the CVD method and ALD method to form these metal films. Among others, metal films that serve as Cu diffusion barriers for Cu wirings have traditionally used Ta/TaN films produced by PVD. With the PVD method, however, it is difficult to form barrier films having a uniform thickness over wirings of high aspect ratios or via holes and contact holes used for connecting wirings, and instead the PVD method tends to produce discontinuous films on side faces of trenches, via holes and contact holes, especially on side faces at the bottom of height gaps, as the film thickness decreases. As a result, Cu films formed by the PVD method on top of these barrier films also tend to become discontinuous. For this reason, voids are generated in electroplated copper layers where these discontinuous Cu films are used as seeds, which makes it difficult to form good wirings.
As a countermeasure, a method is currently reported in the area of Cu film forming using the PVD method, where a CVD-Co film is formed on top of a PVD-TaN film, instead of forming a PVD-Ta/TaN film under the traditional method, after which a Cu film is formed to form a continuous Cu film (U.S. Pat. No. 6,365,502). Since a smoother PVD-Cu film can be easily formed on a CVD-Ru film compared to on a PVD-Ta/TaN film, good burying property can be achieved at the time of Cu plating. Even when a film produced by the PVD-Cu process is used as a seed layer, therefore, good Cu plating can be achieved by forming a Co film or Ru film as the foundation. Among the film deposition methods using organic metal materials, the chemical vapor deposition (CVD) method produces films having higher resistivity than bulk films because of the effects of hydrocarbons, etc., breaking away from organic ligands and remaining in the film. In the case of the CVD method, high impurities and consequent low surface smoothness make it generally difficult to form a continuous film when the film thickness is reduced. Furthermore, it is difficult to achieve good adhesion when a Cu film is formed on top of the aforementioned film lacking in continuity. Although the CVD method normally achieves good shielding property under general conditions, when finer elements are needed and thus the aspect ratios of wiring trenches and connection holes must be increased substantially, it is difficult to shield the wirings effectively. Accordingly, the atomic layer deposition (ALD) method is desirable in situations where the film thickness must be reduced but the required shielding property must also be achieved. Under the ALD method, material molecules are adsorbed onto the surface in a uniform manner, after which the adsorbed molecules are caused to react with a different gas to break down and thereby eliminate the ligands, in order to form a desired metal film. With this method, however, finding a proper combination of a type of molecule that can be adsorbed to achieve good shielding property on one hand, and a type of reactant gas capable of easily breaking down the ligands of such molecule on the other, is difficult, and normally the resulting film tends to contain impurities such as residual carbon, oxygen and nitrogen and its resistivity is also likely much higher than the intended level. Under U.S. Pat. No. 6,527,855, a method to form a Co film using an organic metal material of Co and hydrogen gas is described, wherein oxygen gas is supplied after hydrogen gas is supplied. Under this method, however, the formed Co film tends to contain residual carbon and oxygen from the organic metal material and it is therefore difficult to obtain a quality Co film offering low resistivity.
Also, a Cu film required in electroplating as a seed layer must be formed thinly and continuously, just like a Co film. Particularly when a finer element is needed and thus an attempt is made to form a Cu film by the conventional PVD method inside a via hole of 20 to 30 nm in size, only a discontinuous Cu film is formed inside the via hole. If conditions are changed to form a continuous Cu film, on the other hand, the opening of the via hole is buried by the Cu film and voids generate inside the hole. These situations also present the need to form a thin, continuous Cu film.
An embodiment of the present invention provides a method for forming a film at low temperature and in a reducing atmosphere from a material that constitutes a metal element where β-diketone can be coordinated, such as any one of 8B, 1B and 2B family elements, or specifically Fe, Ni, Rh, Pd, Ir, Pt, Co, Ru and Cu in practical settings, wherein the resulting metal film exhibits low resistivity and high shielding property. The basic principles of the present invention are achieved by two processes. When any of the aforementioned metal complexes coordinated by β-diketone (hereinafter referred to as “β-diketone metal complexes”) is supplied to a substrate, such β-diketone metal complex has the property of easily adsorbing onto the substrate. Accordingly, the first principle of the present invention is that the β-diketone metal complex can be easily adsorbed onto the substrate surface in a uniform manner regardless of whether a metal film or oxide film is formed. The second principle is that by exposing the metal complex coordinated by β-diketone to a mixture gas of hydrogen and nitrogen that has been activated by plasma, β-diketone groups can be eliminated from the metal element in an extremely quick and reliable manner. By allowing the metal atoms to remain on the substrate surface this way, a metal film can be formed with ease. This quick and reliable elimination of β-diketone groups from the metal element dramatically increases the atomic layer deposition rate and also dramatically improves the purity of the metal element in the formed atomic layer.
There have been no reports to date regarding the exposure of a β-diketone metal complex to hydrogen/nitrogen plasma as mentioned above, and it has not been known to date that β-diketone ligands could be eliminated very easily this way. For example, U.S. Pat. No. 6,527,855 B2 describes a process for forming a metal film from an organic metal material containing β-diketone, wherein an organic metal material containing β-diketone ligands is supplied to a substrate to be adsorbed onto the substrate surface, which is followed by a hydrogen gas supply cycle and steps to purge the supplied hydrogen and then supply oxygen gas. This is because the step to supply oxygen gas breaks down the organic metal material containing β-diketone ligands. Based on an experiment conducted by the present inventors, only high-resistivity Co films could be achieved when hydrogen gas alone was supplied. When oxygen gas was supplied, the problem of oxidization of the TaN film at the foundation occurred. Accordingly, after the supply of hydrogen gas the present inventors applied high-frequency power to the hydrogen gas to excite the gas and then implemented the film forming process using the excited hydrogen. This lowered the resistivity levels, but they were still at least 20 times higher than the resistivity levels of bulk films. Next, the present inventors introduced a mixture gas of hydrogen and nitrogen by adjusting the nitrogen mixing ratio to a range of approx. 0.01 to 0.5 of the total gas flow rate, and then applied high-frequency power to this gas and implemented the film forming process using the excited mixture gas of hydrogen and nitrogen, and ultimately found that the resistivity levels were kept in a range of 1 to 5 times the resistivity levels of bulk films. It should be noted that the resistivity levels fluctuated somewhat depending on the plasma power output and plasma application time, where raising the power output and increasing the application time reduced the resistivity. Under practical conditions of high-frequency power and plasma application time, however, resistivity levels of not more than 5 times, or more desirably not more than twice, the resistivity levels of bulk films could be achieved. These results suggest that this production method can be used favorably in the formation of metal films using organic metal materials.
Accordingly, in an embodiment of the present invention metal films such as Co film, Ru film and Cu film having lower resistivity than those achievable under conventional methods can be formed by repeating the step to supply an organic metal material containing β-diketone ligands, step to purge the organic metal material, step to supply a mixture gas of hydrogen and nitrogen and then implementing the film forming process using the mixture gas excited through application of high-frequency power, and step to purge the mixture gas. This method also causes organic metal materials of Co, Ru and Cu containing β-diketone ligands to be adsorbed easily onto an oxide film or metal film, and therefore very good shielding property can be achieved even with wirings having high aspect ratios such as those used in fine semiconductor wirings. For a trench with an aspect ratio is 7, for example, shielding property of 90% or more can be achieved with ease. Likely reasons that explain this lower resistance include the presence of activated excited species such as —NH and —NH2 generated by the excitation of a mixture gas of hydrogen and nitrogen, because these excited species sever the bond between β-diketone and metal and themselves bond with β-diketone, with the β-diketone-bonded excited species eventually gasifying and being discharged. These phenomena have never been reported before, and according to an embodiment of the present invention a metal film can be easily formed from an organic metal material containing β-diketone ligands. These principles can be applied to all metals that form a β-diketone complex. All metals to which β-diketone can be coordinated are covered by the present invention, but specifically the present invention can be applied to the formation of metal films from such 8B, 1B and 2B family elements as Pt, Pd, Rh, Ru, Ir, Ni, Ag and Au, among others. The present invention can also be applied to other metals to which β-diketone coordinates, such as Ti, Ta, Hf, Nb, Mo, W, Mn, Mg, Sr, Ba and La, among others.
For purposes of summarizing the invention and the advantages achieved over the related art, certain objects and advantages of the invention are described in this disclosure. Of course, it is to be understood that not necessarily all such objects or advantages may be achieved in accordance with any particular embodiment of the invention. Thus, for example, those skilled in the art will recognize that the invention may be embodied or carried out in a manner that achieves or optimizes one advantage or group of advantages as taught herein without necessarily achieving other objects or advantages as may be taught or suggested herein.
Further aspects, features and advantages of this invention will become apparent from the detailed description which follows.
These and other features of this invention will now be described with reference to the drawings of preferred embodiments which are intended to illustrate and not to limit the invention. The drawings are oversimplified for illustrative purposes and are not to scale.
1000: Step to transfer substrate in
1001: Temperature stabilization step
1002: Process starting step
1003: Step to introduce organic metal complex containing β-diketone ligands
1004: Step to purge organic metal complex containing β-diketone ligands
1005: Step to introduce mixture gas of nitrogen and hydrogen
1006: Application of plasma (generation of nitrogen/hydrogen plasma)
1007: Purging of mixture gas of nitrogen and hydrogen
1008: Repeat of steps 1003 to 1007
1009: Process ending step
1010: Step to transfer substrate out
301: Reactor
302: Shower head
303: Substrate heating base
304: Evacuation
305: Pressure regulation valve
306: Substrate
307: Gas introduction pipe connected to shower head
308: Valve for argon gas used for purge
309: Cu material introduction valve
310: Orifice
311: Valve for argon gas used for purge
312: Co material introduction valve
313: Orifice
314: Gas introduction valve
315: Orifice
316: Gas introduction valve
317: Orifice
318: Gas introduction valve
319: APR
320: MFC
321: Bypass valve
322: Ar gas introduction valve
323: Cu material supply valve
324: Cu material bottle
325: Cu material
326: APR
327: MFC
328: Bypass valve
329: A carrier introduction valve
330: Co material supply valve
331: Co material bottle
332: Co material
333: APR
334: MFC
335: APR
336: MFC
337: APR
338: MFC
101: Bottom-layer copper wiring
102: SiCN Cu diffusion barrier—Insulation film
103: Inter-layer insulation film
104: Etching stopper film
105: Inter-layer insulation film
106: Etching stopper layer
107: Via hole in dual damascene structure
108: Trench in dual damascene structure
109: Cu diffusion barrier metal film
110: Co film
111: Cu film
112: Cu plating film
113: Cu wiring
501: Cassette loader
502: Transfer robot
503: Load lock chamber
504: Vacuum robot
505: Reaction chamber for Cu deposition
506: Reaction chamber for Co deposition
507: Reaction chamber for formation of Cu barrier metal film
508: Ar gas supply
509: Cu material supply
510: Co material supply
511: Hydrogen gas supply
512: Cu material supply line
513: Co material supply line
514: H2 gas supply line
515: Nitrogen gas supply
516: Nitrogen gas supply line
401: Bottom-layer copper wiring
402: SiCN Cu diffusion barrier—Insulation film
403: Inter-layer insulation film
404: Etching stopper film
405: Inter-layer insulation film
406: Etching stopper layer
407: Via hole in dual damascene structure
408: Trench in dual damascene structure
409: Cu diffusion barrier metal film
410: Ru film
411: Cu film
412: Cu plating film
413: Cu wiring
The present invention will be explained with reference to embodiments. However, the embodiments are not intended to limit the present invention.
In the present disclosure where conditions and/or structures are not specified, the skilled artisan in the art can readily provide such conditions and/or structures, in view of the present disclosure, as a matter of routine experimentation.
An embodiment of the present invention provides a method of forming a single-metal film on a substrate by plasma atomic layer deposition (ALD), comprising: (i) contacting a surface of a substrate with a β-diketone metal complex in a gas phase, whereby molecules of the β-diketone metal complex are attached to the surface of the substrate; (ii) exposing the molecule-attached surface to a nitrogen-hydrogen mixed plasma, thereby forming an atomic layer of the metal; and (iii) repeating steps (i) and (ii) for a next atomic layer on top of the atomic layer in step (ii), thereby accumulating the atomic layers to form the single-metal film on the substrate. In an embodiment, the β-diketone metal complex can easily be adsorbed onto any surface, and the nitrogen-hydrogen plasma can quickly and completely cleave the coordinate bonds between the metal and the β-diketone(s), thereby efficiently forming the single-metal film. In an embodiment, no other ligand-supplying compounds are used, or no other plasma is used.
Further, embodiments include, but are not limited to, the followings:
In an embodiment, the single-metal film is an elemental metal film.
In an embodiment, the nitrogen-hydrogen mixed plasma may be produced by supplying a gas containing nitrogen and hydrogen, followed by applying RF power to the gas. In an embodiment, the gas containing nitrogen and hydrogen may be a mixture of nitrogen gas and hydrogen gas. Further, in an embodiment, a volumetric ratio of nitrogen to the gas mixture maybe 1/100 to 50/100.
In any of the foregoing embodiments, the metal constituting the β-diketone metal complex may be selected from the group consisting of metals belonging to Group 8, 1B, and 2B in the periodic chart. In an embodiment, the metal may be selected from the group consisting of Ru, Co, Pd, Pt, and Ir. Alternatively, the metal may be Cu. In an embodiment, the β-diketone metal complex may be constituted by three β-diketones coordinated to a metal in its molecule. In an embodiment, the β-diketone metal complex may have only β-diketone(s) (optionally substituted) coordinated to a metal in its molecule.
In any of the foregoing embodiments, the method may further comprise forming a Cu film on the single-metal film. In an embodiment, the Cu film may be formed using the single-metal film formed by steps (i) to (iii) as a Cu seed layer.
In any of the foregoing embodiments, steps (i) and (ii) may be repeated at least 10 times.
In any of the foregoing embodiments, steps (i) and (ii) may be repeated until a thickness of the single-metal film reaches at least 0.4 to 0.5 nm.
In any of the foregoing embodiments, the surface of the substrate on which the single-metal film is formed may be constituted by a Cu barrier layer.
In any of the foregoing embodiments, steps (i) and (ii) may be conducted at a temperature of 300° C. or lower.
In any of the foregoing embodiments, the method may further comprise purging the β-diketone metal complex gas after step (i) and purging the gas containing nitrogen and hydrogen after step (ii).
In any of the foregoing embodiments, the nitrogen-hydrogen plasma may be the only plasma to which the molecule-attached surface is exposed in step (ii).
In any of the foregoing embodiments, the β-diketone metal complex may be the only metal compound contacting the surface of the substrate in step (i).
In any of the foregoing embodiments, the single-metal film may have a purity of 99% or higher.
In any of the foregoing embodiments, the surface of the substrate on which the single-metal film is formed may have trenches and the single-metal film covers the trenches as a conformal coating.
Embodiments of the present invention are explained further below.
By causing an organic metal complex containing β-diketone ligands to be adsorbed onto a substrate and then processing this substrate using a gas containing at least hydrogen atoms and nitrogen atoms that have been activated by high frequency, β-diketone ligands can be removed efficiently. These hydrogen atoms and nitrogen atoms can be supplied by the same molecule, or by different molecules. Unless a special circumstance exists, however, even a normal mixture gas of hydrogen gas and nitrogen gas can remove β-diketone ligands with sufficient effect.
As for metal elements that can be coordinated to β-diketone and usable in an embodiment of the present invention, desirable examples include 8B, 1B and 2B family elements, or typically Fe, Ni, Rh, Pd, Ir, Pt, Co, Ru and Cu, among others, where each of the foregoing metals can have least one, or even two, three or more β-diketone coordinated to it. Using the aforementioned metals, a metal film of high purity (such as 99% or more, or even 99.9% or more in which case the film virtually consists of the applicable metal only) can be formed that does not easily produce nitrides when exposed to hydrogen/nitrogen plasma. Typical metal complexes coordinated to β-diketone include tridipivaloylmathanatocobalt (DPM3CO), tridipivaloylmathanatoruthenium (DPM3Ru) and copper hexafluoroacetylacetonate trimethylvinylsilane (Cu(hfac)tmvs) (
Depending on the application, metal elements having one or more β-diketone coordinated to them, other than the metal elements mentioned above, such as Ti, Ta, Hf, Nb, Mo, W, Mn, Mg, Sr, Ba and La, can be used in an embodiment.
In an embodiment of the present invention, a metal layer (single metal layer) constituted by a β-diketone coordinated metal complex can be formed in combination with other metal layer, for example, by using a Cu barrier film as the foundation layer. In an embodiment, a metal layer constituted by a β-diketone coordinated copper complex can be formed as a Cu seed film provided before a Cu film is formed. For this Cu barrier film, any known Cu barrier film or other appropriate film can be used. For example, PVD-TaN and CVD-Ru, as well as other films produced by ALD such as WNC, WN, TaN, RuTaN, RuTa, TaNC, RuTaNC, TiN, RuTiN and RuTi, can be used. In addition to the above, films that can be combined in a favorable manner with a metal layer constituted by β-diketone coordinated metal complex (as the bottom layer or top layer) include, for example, the metal films and alloy films described in U.S. patent application Ser. Nos. 12/203,405 and Ser. No. 12/201,434 owned by the same assignee as in the present application (the disclosure of each of which is herein incorporated by reference in its entirety with regard to metal films). In particular, the aforementioned combinations with metal films by ADL method are desirable because they allow the films to be formed continuously in the same reaction chamber and also offer excellent adhesion. Take note that, in an embodiment, a single metal layer can be formed directly on the substrate surface. In other words, the present invention covers all surfaces without limitation, as long as a β-diketone coordinated metal complex can be adsorbed onto the surface.
After a single metal layer using, say, Ru or Co has been formed on top of a Cu barrier film, a Cu seed layer is formed, for example. This Cu seed layer can be formed by PVD, etc., or according to an embodiment of the present invention using a β-diketone coordinated Cu complex. Ru and Co offer excellent adhesion to Cu and therefore allow the single metal layer and Cu seed layer to be formed continuously on top of a Cu barrier film. In an embodiment, the single metal layer in the aforementioned structure consists of one layer.
In an embodiment of the present invention, the method described in U.S. patent Ser. No. 12/203,405 owned by the same assignee as in the present application (the disclosure of which is herein incorporated by reference in its entirety with regard to ALD process conditions), among others, can be used. In the aforementioned embodiment, no alloy film is formed, but a film constituted by one type of metal is formed. In an embodiment of the present invention, laminated layers can be formed where said layers consist of virtually only one type of metal because β-diketone ligands are severed by nitrogen/hydrogen plasma. Take note, however, that some metal elements other than those in the 8B, 1B and 2B families (such as Ta) form nitrides when exposed to nitrogen/hydrogen plasma, even when nitrogen/hydrogen plasma severs β-diketone ligands, in which case the resulting film does not have a metal purity of 99% or more even when only one type of metal is used.
The thickness of this single metal layer varies depending on the application, but in an embodiment it is in a range of 0.5 to 100 nm (or 1 nm or more but 20 nm or less, such as in a range of 1 to 10 nm or 5 to 20 nm, in an embodiment). If the film is too thin, the single metal layer cannot demonstrate its properties. Theoretically the film thickness can be increased infinitely. The severance of β-diketone ligands by nitrogen/hydrogen plasma occurs much more quickly and reliably compared to, say, when hydrogen plasma alone is used. As a result, while the cycle needs to be repeated around 10 times to form one atomic layer before (for example, one cycle forms only 0.02 nm of Ru film and thus formation of one atomic layer requires 10 cycles to be repeated to achieve a thickness of approx. 0.2 nm), in an embodiment of the present invention around 0.04 to 0.05 nm of film can be achieved in one cycle, which is twice the rate compared to before, and therefore a 10-cycle achieves 0.4 to 0.5 nm of film corresponding to two or three atomic layers. A thickness corresponding to two or three atomic layers can be definitely recognized as a metal layer.
In an embodiment, the resistivity is not more than 5 times, or not more than twice, the resistivity of a bulk film formed by the same metal. In typical examples, the resistivity is 50 μΩcm or less, or even 20 μΩcm or less. Incidentally, although the resistivity of a single metal layer is slightly higher than that of a bulk film (complete crystallization), this is because the single metal layer is thin and the film forming temperature is low, or 300° C. or below, and therefore complete crystallization cannot be achieved as in the case of a bulk film. In other words, the resistivity can be lowered by heat-treating the single metal layer at high temperature. The aforementioned resistivity values assume use of no high-temperature treatment.
Examples of H2/N2 plasma and H2 plasma conditions are listed below:
Pressure: 150 to 400 Pa
Temperature: 250 to 300° C.
H2 flow rate: 100 to 500 sccm
N2 flow rate: 10 to 200 sccm
N2/(N2+H2) ratio: 1/100 to 50/100
RF power: 200 to 500
RF frequency: 1 to 30 MHz
Application time: 1 to 20 (per cycle)
As for the N2/(N2+H2) ratio mentioned above, surprisingly even only a small amount of N2 causes significant changes in film quality, and in an embodiment, sufficient effects can be achieved as long as the N2/(N2+H2) ratio is 1/1000 or more.
NH3 plasma can also be used (such as at 10 to 200 sccm) instead of H2/N2 plasma.
Also note that the cycle conditions under which to introduce a β-diketone coordinated metal complex and to cause it to adsorb onto the substrate surface can be set as follows in an embodiment, although specific conditions vary depending on the type of β-diketone coordinated metal complex:
Pressure: 150 to 400 Pa
Substrate temperature: 250 to 300° C.
The purge conditions using an inert gas (such as He or Ar) can be set as follows, for example:
Inert gas flow rate: 500 to 2000 sccm
Time: 1 to 3 sec
In the above, normally evacuation is also performed along with purge.
A substrate is introduced to an ALD apparatus that has been evacuated, and the substrate temperature is set to and stabilized at a specified level, after which the ALD process is started. Normally, first an organic metal complex containing β-diketone ligands is introduced onto the substrate, and then the organic metal complex coordinated by a β-diketone complex is discharged. This discharge is preferably be implemented in such a way that an inert gas is introduced under evacuation to discharge the gas of this organic metal complex from the reaction chamber. Once a specified vacuum level is achieved, high frequency is applied to the mixture gas using a high-frequency power supply to activate the mixture gas and thereby produce a so-called plasma gas, and this plasma gas is used to eliminate β-diketone groups from the organic metal complex containing β-diketone ligands and adsorbed onto the substrate surface. At this time, an elimination from the organic metal complex containing β-diketone ligands can be achieved very effectively by using as a plasma gas a mixture gas of hydrogen and nitrogen where the two constitutes are mixed at a specified ratio. As a result, a metal film at the atomic layer level is formed. Next, the mixture gas of hydrogen and nitrogen is discharged. This discharge can also be achieved by supplying an inert gas. Thereafter, steps 1003 to 1007 are repeated to achieve a specified film thickness (1008). Normally this method forms approx. 0.5 Å of metal film of per cycle, which means that a metal film having the required film thickness can be formed after 20 to 100 cycles or so. After the ALD cycle has been repeated for a specified number of times, normally the atmosphere is evacuated sufficiently and then the substrate is transferred out of the ALD apparatus, upon which the process ends. Needless to say, if the next process is performed in vacuum, then the substrate is also transferred in vacuum.
Next, the H2, N2 and Ar gas supply systems are explained using
Next, specific application examples are given. It should be noted, however, that these application examples are only a part of embodiments and the present invention is not limited to these examples in any way.
First, it should be mentioned that in connection with next-generation Cu wirings that require extremely thin Cu barrier films, Cu barrier metal films formed by the ALD method, such as TaN and TiN films, are being examined in the industry. However, these films do not have good adhesion to Cu film and therefore a Co, Ru or other film offering excellent adhesion to Cu is required between the Cu barrier film and Cu film.
First in
Also, the substrate is transferred to 506 via the cassette loader 501, and in 506 the surface of the bottom-layer Cu wiring 401 at the via hole 407 is reduced by hydrogen plasma, after which the substrate is transported to the processing chamber 505 and a copper diffusion barrier metal film is formed. This metal film can be formed by the PVD method, CVD method or ALD method. The specific film is a TaN, RuTaN, TiN, RuTiN or other metal film that serves as a Cu diffusion barrier. Thereafter, the substrate is transferred to the processing chamber 507, where a Ru material constituted by a metal complex containing β-diketone ligands is evaporated and supplied to form an extremely thin Ru film of 1 to 2 nm in thickness through the cycle shown in
Detailed examples are given below.
In this example, a process of forming a Co film is illustrated. Using the ALD apparatus shown in
In
Incidentally, after the aforementioned process the substrate was transferred from the reactor to the next process, or Cu forming process, where the steps in
In this example, an inter-layer connection structure was formed through the procedure shown in
A substrate was transferred to the reaction chamber, and first in
Thereafter, a Cu material 332, or Cu(hfac)tmvs (copper hexafluoroacetylacetonate trimethylvinylsilane), was heated to 80° C. and supplied to form a Cu film 411 according to the sequence shown in
Although a Cu film was formed after a Ru film in this example, a mixed layer structure constituted by multiple Ru and Cu layers can also be formed by alternating the Ru ALD cycle and Cu ALD cycle. In this case, it was possible to form a Ru layer for 10 cycles, form Ru and Cu layers alternately for 10 cycles each, and then form a Cu layer for 50 cycles. Here, too, the good Cu electroplating property allowed complete burying by Cu plating of via holes of 30 nm or less in diameter in a structure of 5 to 10 in aspect ratio.
This example illustrates a process of forming a RuTaN film as a Cu barrier layer and then forming Ru and Cu layers. In the ALD apparatus shown in
A substrate was transferred to the reaction chamber, and first in
Next, only the Ru material was supplied and the similar plasma processing step was implemented, and this was typically repeated for 20 to 40 times to form approx. 1 to 2 nm of Ru film. Whether the quality of the formed Ru film is acceptable or not can be determined from the film's resistivity. The Ru film obtained under the above conditions had a resistivity of 30 μΩcm or less. This suggests that impurities arising from the Ru material could be reduced and a Ru metal film 410 of low resistivity (
The RBS analysis results shown in
This Ru layer was typically formed by 1 to 2 nm, and approx. 5 to 20 nM of Cu layer to serve as a seed layer for Cu deposition was formed on top of this Ru layer via electroplating. It was confirmed that this Cu layer could be formed continuously without causing the Cu layer to agglomerate over the Ru layer at the bottom, regardless of whether the PVD method, CVD method or ALD method was used. In other words, the Ru layer demonstrated good adhesion to Cu and was suitable for the formation of a continuous Cu layer. It was also confirmed that, by forming a Cu film via electroplating on top of this Cu layer, sufficient burying property could be achieved using this Cu film via electroplating even with wiring structures having wiring widths of 20 to 50 nm and aspect ratios of approx. 5 to 10. Accordingly, it can be concluded that the Ru film achieved by the method explained in this example is very effective in the formation of Cu seed layers as mentioned above as well as in the formation of fine Cu wirings via electroplating. On the other hand, it was difficult to form a thin Cu layer continuously when the Ru layer was formed by H2 plasma, and this application also presented other problem such as generation of voids due to the fact that it is difficult to achieve complete burying even by Cu electroplating and. These are due to a large amount of impurities.
The present invention includes the above mentioned embodiments and other various embodiments including the following:
1) A method for forming metal film by plasma atomic layer deposition, wherein said method includes steps to cause an organic metal complex containing β-diketone ligands to be chemically adsorbed onto a substrate, after which the substrate is processed using a gas containing at least hydrogen atoms and nitrogen atoms that have been activated, to form a metal layer from metal atoms constituting the aforementioned organic metal complex.
2) A method for forming metal film by plasma atomic layer deposition according to 1) above, wherein said method is characterized in that the mixture gas containing at least hydrogen atoms and nitrogen atoms is a mixture gas of hydrogen gas and nitrogen gas.
3) A method for forming metal film by plasma atomic layer deposition according to 1) or 2) above, wherein said method is characterized in that the constituent metal element of the aforementioned organic metal complex containing β-diketone ligands belongs to the 8B, 1B or 2B family.
4) A method for forming metal film by plasma atomic layer deposition according to 3) above, wherein said method is characterized in that the constituent metal element of the aforementioned organic metal complex containing β-diketone ligands is Ru, Co, Pd, Pt or Ir.
5) A method for forming metal film by plasma atomic layer deposition according to 4) above, wherein said method is characterized in that a copper film is formed on top of the aforementioned metal film.
6) A method for forming metal film by plasma atomic layer deposition according to 3) above, wherein said method is characterized in that the metal element constituting the organic metal complex containing β-diketone ligands is copper (Cu).
It will be understood by those of skill in the art that numerous and various modifications can be made without departing from the spirit of the present invention. Therefore, it should be clearly understood that the forms of the present invention are illustrative only and are not intended to limit the scope of the present invention.
Number | Name | Date | Kind |
---|---|---|---|
4058430 | Suntola et al. | Nov 1977 | A |
4210608 | Pinke | Jul 1980 | A |
4477296 | Nair | Oct 1984 | A |
4604118 | Bocko et al. | Aug 1986 | A |
4670110 | Withers et al. | Jun 1987 | A |
4860687 | Frijlink | Aug 1989 | A |
4891050 | Bowers et al. | Jan 1990 | A |
4902551 | Nakaso et al. | Feb 1990 | A |
4965656 | Koubuchi et al. | Oct 1990 | A |
5106454 | Allardyce et al. | Apr 1992 | A |
5382333 | Ando et al. | Jan 1995 | A |
5391517 | Gelatos et al. | Feb 1995 | A |
5453494 | Kirlin et al. | Sep 1995 | A |
5470661 | Bailey et al. | Nov 1995 | A |
5637533 | Choi | Jun 1997 | A |
5695810 | Dubin et al. | Dec 1997 | A |
5711811 | Suntola et al. | Jan 1998 | A |
5731634 | Matsuo et al. | Mar 1998 | A |
5820664 | Gardiner et al. | Oct 1998 | A |
5865365 | Nishikawa et al. | Feb 1999 | A |
5884009 | Okase | Mar 1999 | A |
5916365 | Sherman et al. | Jun 1999 | A |
5923056 | Lee et al. | Jul 1999 | A |
5939334 | Nguyen et al. | Aug 1999 | A |
5989672 | Hayashi | Nov 1999 | A |
5998048 | Jin et al. | Dec 1999 | A |
6006763 | Mori et al. | Dec 1999 | A |
6015986 | Schuegraf | Jan 2000 | A |
6033584 | Ngo et al. | Mar 2000 | A |
6040243 | Li et al. | Mar 2000 | A |
6063705 | Vaartstra | May 2000 | A |
6066892 | Ding et al. | May 2000 | A |
6074945 | Vaartstra et al. | Jun 2000 | A |
6108937 | Raaijmakers | Aug 2000 | A |
6124189 | Watanabe et al. | Sep 2000 | A |
6130123 | Liang et al. | Oct 2000 | A |
6133159 | Vaartstra et al. | Oct 2000 | A |
6136163 | Cheung et al. | Oct 2000 | A |
6139700 | Knag et al. | Oct 2000 | A |
6143658 | Donnelly et al. | Nov 2000 | A |
6144060 | Park et al. | Nov 2000 | A |
6171910 | Hobbs et al. | Jan 2001 | B1 |
6187691 | Fukuda et al. | Feb 2001 | B1 |
6203613 | Gates et al. | Mar 2001 | B1 |
6268291 | Andricacos et al. | Jul 2001 | B1 |
6217148 | Kato et al. | Aug 2001 | B1 |
6270572 | Kim et al. | Aug 2001 | B1 |
6281125 | Vaartstra et al. | Aug 2001 | B1 |
6294467 | Yokoyama et al. | Sep 2001 | B1 |
6297539 | Ma et al. | Oct 2001 | B1 |
6303500 | Jiang et al. | Oct 2001 | B1 |
6305314 | Sneh et al. | Oct 2001 | B1 |
6306756 | Hasunuma et al. | Oct 2001 | B1 |
6320213 | Kirlin et al. | Nov 2001 | B1 |
6323131 | Obeng et al. | Nov 2001 | B1 |
6329297 | Balish et al. | Dec 2001 | B1 |
6335280 | Van der Jeugd | Jan 2002 | B1 |
6342277 | Sherman et al. | Jan 2002 | B1 |
6346151 | Jiang et al. | Feb 2002 | B1 |
6347636 | Xia et al. | Feb 2002 | B1 |
6352945 | Matsuki et al. | Mar 2002 | B1 |
6359159 | Welch et al. | Mar 2002 | B1 |
6374831 | Chandran et al. | Apr 2002 | B1 |
6380080 | Visokay | Apr 2002 | B2 |
6383955 | Matsuki et al. | May 2002 | B1 |
6387207 | Janakiraman et al. | May 2002 | B1 |
6391785 | Satta et al. | May 2002 | B1 |
6395650 | Callegari et al. | May 2002 | B1 |
6403414 | Marsh | Jun 2002 | B2 |
6404191 | Daughton et al. | Jun 2002 | B2 |
6420189 | Lopatin | Jul 2002 | B1 |
6428859 | Chiang et al. | Aug 2002 | B1 |
6428894 | Babich et al. | Aug 2002 | B1 |
6433432 | Shimizu | Aug 2002 | B2 |
6444568 | Sundararajan et al. | Sep 2002 | B1 |
6444868 | Vaughn et al. | Sep 2002 | B1 |
6455424 | McTeer et al. | Sep 2002 | B1 |
6464779 | Powell et al. | Oct 2002 | B1 |
6475276 | Elers et al. | Nov 2002 | B1 |
6478931 | Wadley et al. | Nov 2002 | B1 |
6482733 | Raaijmakers et al. | Nov 2002 | B2 |
6482740 | Soininen et al. | Nov 2002 | B2 |
6511539 | Raaijmakers | Jan 2003 | B1 |
6527855 | De La Rosa et al. | Mar 2003 | B2 |
6534395 | Werkhoven et al. | Mar 2003 | B2 |
6541067 | Marsh et al. | Apr 2003 | B1 |
6551399 | Sneh et al. | Apr 2003 | B1 |
6576053 | Kim et al. | Jun 2003 | B1 |
6586330 | Ludviksson et al. | Jul 2003 | B1 |
6593656 | Ahn et al. | Jul 2003 | B2 |
6617173 | Sneh | Sep 2003 | B1 |
6649091 | Ryan et al. | Nov 2003 | B2 |
6656748 | Hall et al. | Dec 2003 | B2 |
6664192 | Satta et al. | Dec 2003 | B2 |
6679951 | Soininen et al. | Jan 2004 | B2 |
6680540 | Nakano et al. | Jan 2004 | B2 |
6703708 | Werkhoven et al. | Mar 2004 | B2 |
6713381 | Barr et al. | Mar 2004 | B2 |
6720262 | Koh et al. | Apr 2004 | B2 |
6759325 | Raaijmakers et al. | Jul 2004 | B2 |
6777331 | Nguyen | Aug 2004 | B2 |
6784101 | Yu et al. | Aug 2004 | B1 |
6784504 | Derderian et al. | Aug 2004 | B2 |
6800542 | Kim | Oct 2004 | B2 |
6800567 | Cho et al. | Oct 2004 | B2 |
6824816 | Aaltonen et al. | Nov 2004 | B2 |
6842740 | Jeran et al. | Jan 2005 | B1 |
6849122 | Fair | Feb 2005 | B1 |
6852635 | Satta et al. | Feb 2005 | B2 |
6878628 | Sophie et al. | Apr 2005 | B2 |
6881260 | Marsh et al. | Apr 2005 | B2 |
6881437 | Ivanov et al. | Apr 2005 | B2 |
6887795 | Soininen et al. | May 2005 | B2 |
6921712 | Soininen et al. | Jul 2005 | B2 |
6933225 | Werkhoven et al. | Aug 2005 | B2 |
6936535 | Kim et al. | Aug 2005 | B2 |
6955986 | Li | Oct 2005 | B2 |
6984591 | Buchanan et al. | Jan 2006 | B1 |
7011981 | Kim et al. | Mar 2006 | B2 |
7067407 | Kostamo et al. | Jun 2006 | B2 |
7105054 | Lindfors | Sep 2006 | B2 |
7107998 | Greet et al. | Sep 2006 | B2 |
7118779 | Verghese et al. | Oct 2006 | B2 |
7135207 | Min et al. | Nov 2006 | B2 |
7183604 | Cartier | Feb 2007 | B2 |
7220451 | Aaltonen et al. | May 2007 | B2 |
7220669 | Hujanen et al. | May 2007 | B2 |
7241677 | Soininen et al. | Jul 2007 | B2 |
7256144 | Koyanagi et al. | Aug 2007 | B2 |
7273526 | Shinriki et al. | Sep 2007 | B2 |
7273814 | Matsuda | Sep 2007 | B2 |
7300873 | Millward | Nov 2007 | B2 |
7404985 | Chang et al. | Jul 2008 | B2 |
7419903 | Haukka et al. | Sep 2008 | B2 |
7435484 | Shinriki et al. | Oct 2008 | B2 |
7438949 | Weidman | Oct 2008 | B2 |
7476618 | Kilpela et al. | Jan 2009 | B2 |
7494927 | Kostamo et al. | Feb 2009 | B2 |
7541284 | Park | Jun 2009 | B2 |
7566661 | Lavoie | Jul 2009 | B2 |
7601223 | Lindfors et al. | Oct 2009 | B2 |
7615480 | Boyd | Nov 2009 | B2 |
7655564 | Shinriki | Feb 2010 | B2 |
7666773 | Huotari et al. | Feb 2010 | B2 |
20010003064 | Ohto | Jun 2001 | A1 |
20010013617 | Toyoda et al. | Aug 2001 | A1 |
20010018266 | Jiang et al. | Aug 2001 | A1 |
20010030366 | Nakano et al. | Oct 2001 | A1 |
20010041250 | Werkhoven et al. | Nov 2001 | A1 |
20010052318 | Jiang et al. | Dec 2001 | A1 |
20020004293 | Soininen et al. | Jan 2002 | A1 |
20020006711 | Yamazaki et al. | Jan 2002 | A1 |
20020011210 | Satoh et al. | Jan 2002 | A1 |
20020013487 | Norman et al. | Jan 2002 | A1 |
20020027286 | Sundararajan et al. | Mar 2002 | A1 |
20020173054 | Kim | Nov 2002 | A1 |
20030013302 | Nguyen et al. | Jan 2003 | A1 |
20030059535 | Luo et al. | Mar 2003 | A1 |
20030080363 | Maruyama et al. | May 2003 | A1 |
20030091938 | Fairbairn et al. | May 2003 | A1 |
20030100162 | Joo | May 2003 | A1 |
20030121608 | Chen et al. | Jul 2003 | A1 |
20030135061 | Norman et al. | Jul 2003 | A1 |
20030165615 | Aaltonen et al. | Sep 2003 | A1 |
20030214043 | Saitoh et al. | Nov 2003 | A1 |
20030219991 | Geusic et al. | Nov 2003 | A1 |
20030233976 | Marsh et al. | Dec 2003 | A1 |
20040005753 | Kostamo et al. | Jan 2004 | A1 |
20040028952 | Cartier et al. | Feb 2004 | A1 |
20040038529 | Soininen et al. | Feb 2004 | A1 |
20040041194 | Marsh | Mar 2004 | A1 |
20040053496 | Choi | Mar 2004 | A1 |
20040082125 | Hou et al. | Apr 2004 | A1 |
20040087143 | Norman et al. | May 2004 | A1 |
20040105934 | Chang et al. | Jun 2004 | A1 |
20040118697 | Wen et al. | Jun 2004 | A1 |
20040126944 | Rotondaro et al. | Jul 2004 | A1 |
20040142558 | Granneman | Jul 2004 | A1 |
20040152255 | Seidl et al. | Aug 2004 | A1 |
20040192021 | Li | Sep 2004 | A1 |
20040192036 | Koyanagi et al. | Sep 2004 | A1 |
20040214354 | Marsh et al. | Oct 2004 | A1 |
20040216668 | Lindfors et al. | Nov 2004 | A1 |
20040224475 | Lee et al. | Nov 2004 | A1 |
20050009325 | Chung et al. | Jan 2005 | A1 |
20050020060 | Aaltonen et al. | Jan 2005 | A1 |
20050048794 | Brask et al. | Mar 2005 | A1 |
20050082587 | Marsh | Apr 2005 | A1 |
20050085031 | Lopatin et al. | Apr 2005 | A1 |
20050087879 | Won et al. | Apr 2005 | A1 |
20050089632 | Vehkamaki et al. | Apr 2005 | A1 |
20050092247 | Schmidt et al. | May 2005 | A1 |
20050098440 | Kailasan et al. | May 2005 | A1 |
20050112509 | Fairbairn et al. | May 2005 | A1 |
20050118807 | Kim et al. | Jun 2005 | A1 |
20050124154 | Park et al. | Jun 2005 | A1 |
20050181555 | Haukka et al. | Aug 2005 | A1 |
20050208754 | Kostamo et al. | Sep 2005 | A1 |
20050229848 | Shinriki et al. | Oct 2005 | A1 |
20050238808 | Gatineau et al. | Oct 2005 | A1 |
20050266700 | Jursich et al. | Dec 2005 | A1 |
20050271812 | Myo et al. | Dec 2005 | A1 |
20060013955 | Senzaki | Jan 2006 | A1 |
20060035462 | Millward | Feb 2006 | A1 |
20060073276 | Antonissen | Apr 2006 | A1 |
20060084280 | Matsuki et al. | Apr 2006 | A1 |
20060093848 | Senkevich et al. | May 2006 | A1 |
20060118968 | Johnston et al. | Jun 2006 | A1 |
20060121733 | Kilpela et al. | Jun 2006 | A1 |
20060128150 | Gandikota et al. | Jun 2006 | A1 |
20060137608 | Choi et al. | Jun 2006 | A1 |
20060165892 | Weidman | Jul 2006 | A1 |
20060177601 | Park et al. | Aug 2006 | A1 |
20060211228 | Matsuda | Sep 2006 | A1 |
20060216932 | Kumar et al. | Sep 2006 | A1 |
20060223300 | Simka et al. | Oct 2006 | A1 |
20060263977 | Kim et al. | Nov 2006 | A1 |
20070014919 | Hamalainen et al. | Jan 2007 | A1 |
20070026654 | Huotari et al. | Feb 2007 | A1 |
20070036892 | Haukka et al. | Feb 2007 | A1 |
20070059502 | Wang et al. | Mar 2007 | A1 |
20070082132 | Shinriki et al. | Apr 2007 | A1 |
20070128864 | Ma et al. | Jun 2007 | A1 |
20070190782 | Park et al. | Aug 2007 | A1 |
20070218705 | Matsuki et al. | Sep 2007 | A1 |
20070248767 | Okura et al. | Oct 2007 | A1 |
20070254488 | Huotari et al. | Nov 2007 | A1 |
20080038465 | Dussurrat | Feb 2008 | A1 |
20080054472 | Shinriki et al. | Mar 2008 | A1 |
20080102613 | Elers | May 2008 | A1 |
20080124484 | Shinriki et al. | May 2008 | A1 |
20080146042 | Kostamo et al. | Jun 2008 | A1 |
20080171436 | Koh et al. | Jul 2008 | A1 |
20080200019 | Huotari et al. | Aug 2008 | A9 |
20080206982 | Suzuki | Aug 2008 | A1 |
20080206985 | Kim et al. | Aug 2008 | A1 |
20080214003 | Xia | Sep 2008 | A1 |
20080296768 | Chebiam | Dec 2008 | A1 |
20080315418 | Boyd | Dec 2008 | A1 |
20080318417 | Shinriki et al. | Dec 2008 | A1 |
20090068832 | Haukka et al. | Mar 2009 | A1 |
20090087339 | Shinriki | Apr 2009 | A1 |
20090104777 | Kim | Apr 2009 | A1 |
20090155997 | Shinriki | Jun 2009 | A1 |
20090163024 | Kim et al. | Jun 2009 | A1 |
20090209101 | Shinriki et al. | Aug 2009 | A1 |
20100055433 | Shinriki et al. | Mar 2010 | A1 |
Number | Date | Country |
---|---|---|
41 08 73 | Mar 1925 | DE |
0 469 456 | Jul 1991 | EP |
0 469 470 | Feb 1992 | EP |
0 880 168 | Nov 1998 | EP |
1 688 923 | Aug 2006 | EP |
368850 | Dec 1930 | GB |
1518243 | Jul 1978 | GB |
2340508 | Feb 2000 | GB |
1998-340994 | Dec 1998 | JP |
2003-168738 | Jun 2003 | JP |
10-2001-004717 | Jan 2001 | KR |
10-2001-004718 | Jan 2001 | KR |
10-2001-004719 | Jan 2001 | KR |
10-2001-96408 | Nov 2001 | KR |
10-2001-112889 | Dec 2001 | KR |
10-2003-0011399 | Feb 2003 | KR |
1020050103373 | Oct 2005 | KR |
WO 9310652 | May 1993 | WO |
WO 9801890 | Jan 1998 | WO |
WO 9917343 | Apr 1999 | WO |
WO 0003420 | Jan 2000 | WO |
WO 0038191 | Jun 2000 | WO |
WO 0188972 | May 2001 | WO |
WO 0150502 | Jul 2001 | WO |
WO 0209126 | Jul 2001 | WO |
WO 0209158 | Jul 2001 | WO |
WO 03023835 | Mar 2003 | WO |
WO 03040150 | May 2003 | WO |
WO 03056612 | Jul 2003 | WO |
WO 2004035858 | Apr 2004 | WO |
WO 2006035281 | Apr 2006 | WO |
Number | Date | Country | |
---|---|---|---|
20100092696 A1 | Apr 2010 | US |