Patent Application
20160319459
The present invention relates to a template for epitaxial growth as an underlying substrate where a GaN compound semiconductor layer (general formula: AlxGayIn1-x-yN) is epitaxially grown, and also relates to a method for producing the same.
GaN nitride semiconductor devices such as light-emitting diodes and semiconductor lasers are conventionally produced by growing a multi-layered GaN compound semiconductor layer on a template for epitaxial growth (for example, see Non-patent Document 1).
The crystal quality of the template surface directly affects the crystal quality of the GaN compound semiconductor layer formed thereon, providing significant effects on the characteristics of a light-emitting device or the like which is formed as a result. In providing a light-emitting diode or a semiconductor laser in the ultraviolet region, it is particularly desirable to use a template having a reduced threading dislocation density of 107/cm2 or less or preferably about 106/cm2. When the ELO-AlN layer 103 is epitaxially grown by an epitaxial lateral overgrowth (ELO) method on the AlN underlying layer 102 having a cyclic groove pattern as shown in
However, for the template including the sapphire substrate, the AlN underlying layer, and the ELO-AlN layer as shown in
On the other hand, in order to prevent the complication of the manufacturing process and the decrease in throughput by omitting etching between crystal growth processes, proposed are the methods of providing a template for epitaxial growth in which a cyclic groove pattern is directly formed on the surface of the sapphire substrate by photolithography and reactive ion etching or the like, and the ELO-AlN layer is formed directly on the sapphire substrate (for example, see Patent Document 1, and Non-patent Documents 2 and 3). In order to grow an ELO-AlN layer on the grooved surface of a substrate, it is preferable to form deeper grooves on the sapphire substrate surface since the AlN layer grown from the bottom of the grooves needs to be separate from the AlN layer laterally overgrown from the flat surfaces of the protrusions between the grooves. However, the sapphire substrate has a low etching rate and is difficult to process, so that an ELO-AlN layer having a low threading dislocation density needs to be grown on a shallow-grooved substrate.
Patent Document 1: Japanese Patent No. 3455512
Non-patent Document 1: Kentaro Nagamatsu, et al., “High-efficiency AlGaN-based UV light-emitting diode on laterally overgrown AlN”, Journal of Crystal Growth, 310, pp. 2326-2329, 2008
Non-patent Document 2: N. Nagano, et al., “Epitaxial lateral overgrowth of AlN layers on patterned sapphire substrates”, phys. stat. sol. (a) 203, No. 7, pp. 1632-1635, 2006
Non-patent Document 3: J. Mei, et al., “Dislocation generation at the coalescence of aluminum nitride lateral epitaxy on shallow-grooved sapphire substrates”, Applied Physics Letters 90, 221909, 2007
According to Non-patent Document 2, when the ELO-AlN layer is directly grown on the sapphire (0001) substrate surface having grooves in the (10-10) direction, the layer grows laterally and then covers over the grooves at 1,100° C., the general growth temperature of epitaxially overgrowing AlN on the sapphire (0001) substrate, but the grown ELO-AlN has an extremely rough surface. However, at 1,300° C., the surface of the grown ELO-AlN is flat at the atomic level. That is, when the ELO-AlN layer is directly grown on the grooved surface of the sapphire (0001) substrate, the layer needs to be grown under high temperature of 1,300° C. or above. Although Patent Document 1 mentioned above does not disclose a specific AlN growth temperature, the growth temperature is thought to be 1,350° C. or above, or 1,400° C. or above as the layer is grown at an extremely high growth speed (at 1 μm per minute).
As described above, a high temperature treatment of 1,300° C. or above is conventionally required so as to provide a fine and flat ELO-AlN layer surface when an ELO-AlN layer is directly grown on the surface of a sapphire (0001) substrate. However, a heater, used for the heating, wears out much faster at the growth temperature of 1,300° C. or above than at below 1,300° C., and it is also difficult to produce the products in a stable yield. Thus, it is preferable to grow an ELO-AlN layer on the grooved surface of a sapphire (0001) substrate with stability at the growth temperature below 1,300° C.
The present invention has been made in consideration of these problems, and an object thereof is to provide a method for producing a template for epitaxial growth in which an AlN layer or an AlGaN layer having a fine and flat surface is epitaxially grown on a sapphire (0001) substrate surface formed with recesses and protrusions such as grooves by a lateral overgrowth method, even at the growth temperature below 1,300° C., and to provide a template for epitaxial growth that has a reduced threading dislocation density.
The present inventors discovered that an epitaxially grown AlN layer or AlGaN layer having a fine and flat surface is provided by a lateral overgrowth method even at a growth temperature below 1,300° C., by first epitaxially growing an initial-stage AlN layer that is oriented in the c+ axis direction, in other words, that is subjected to C axis orientation control (polarity control) so as to make Al atoms appear at the outermost surface of growth crystals in a wurtzite crystal structure, on the flat surface of protrusion tops of a sapphire (0001) substrate formed with recesses and protrusions as grooves, and then expitaxially growing an AlN layer or an AlGaN layer so as to cover over the recesses by a lateral overgrowth method; and that a template for epitaxial growth having a reduced threading dislocation density is provided accordingly. Group III nitride crystals having a wurtzite crystal structure generally grow in the polarity of either group III atoms or nitrogen atoms in respect to the C axis direction, depending on the type of substrates and the conditions of the initial growth stage. When AlN is grown on the surface of a sapphire (0001) substrate, the polarity of Al needs to be actively controlled. Otherwise, an N polar face often appears on the outermost surface of growth crystals.
In other words, in order to achieve the above object, the present invention provides a method for producing a template for epitaxial growth that includes: processing a surface of a sapphire (0001) substrate to form recesses and protrusions on the surface so that protrusion tops are made flat with a given plan-view pattern;
epitaxially growing an initial-stage AlN layer on the surface of the sapphire (0001) substrate having the recesses and protrusions by performing C axis orientation control so that a C+ axis oriented AlN layer grows on flat surfaces of the protrusion tops, excluding edges, and that the AlN layer deposited on the recesses obtained by the recesses and protrusions forming process forms new recesses over the existing recesses; and
epitaxially growing an AlxGayN(0001) layer (1≧x>0, x+y=1) on the initial-stage AlN layer by a lateral overgrowth method so as to cover the new recesses with the AlxGayN(0001) layer laterally overgrown from above the protrusion tops.
Moreover, according to a second characteristic of the method for producing a template for epitaxial growth, having the above characteristic, the recesses are formed on the sapphire (0001) substrate surface at a depth of 1.0 μm or less.
Furthermore, according to a third characteristic of the method for producing a template for epitaxial growth, having the above characteristic, an AlN layer that is not oriented in the C+ axis is grown near steps formed by recesses and protrusions during growth of the initial-stage AlN layer.
According to a fourth characteristic of the method for producing a template for epitaxial growth, having the above characteristic, the AlxGayN(0001) layer is an AlN(0001) layer.
Additionally, in order to achieve the above object, the present invention provides a template for epitaxial growth including a sapphire (0001) substrate processed to form recesses and protrusions on its surface so that protrusion tops are made flat with a given plan-view pattern; an initial-stage AlN layer epitaxially grown on the surface of the sapphire (0001) substrate having the recesses and protrusions; and an AlxGayN(0001) layer (1≧x>0, x+y=1) epitaxially grown on the initial-stage AlN layer by a lateral overgrowth method, wherein the initial-stage AlN layer is provided so that a C+ axis oriented AlN layer grows on flat surfaces of the protrusion tops, excluding the edges, and that the AlN layer deposited on the recesses obtained by the recesses and protrusions forming process forms new recesses over the existing recesses, and the new recesses are covered with the AlxGayN(0001) layer that is laterally overgrown from above the protrusion tops.
Additionally, according to a second characteristic of the template for epitaxial growth, having the above characteristic, the recesses are formed on the sapphire (0001) substrate surface at a depth of 1.0 μm or less.
Furthermore, according to a third characteristic of the template for epitaxial growth, having the above characteristic, the initial-stage AlN layer includes an AlN layer that is not oriented in the C+ axis near steps formed by the recesses and protrusions.
Moreover, according to a fourth characteristic of the template for epitaxial growth, having the above characteristic, the AlxGayN(0001) layer is an AlN(0001) layer.
According to the method for producing a template for epitaxial growth or the template for epitaxial growth, an AlN layer or an AlGaN layer having a fine and flat surface and a reduced threading dislocation density is epitaxially grown on a sapphire (0001) substrate having recesses and protrusions on its surface by a lateral overgrowth method at a growth temperature below 1,300° C., lower than conventional growth temperature. Specifically, the initial-stage AlN layer, an underlying layer for epitaxially growing an AlN layer or an AlGaN layer thereon by a lateral overgrowth method, has portions that are epitaxially grown from the flat surface of the protrusion tops, and are oriented in the C+ axis. Specifically, the surface of the initial-stage AlN layer is an Al polar face uniformly. Thus, even at a growth temperature below 1,300° C., the AlN layer or AlGaN layer grown epitaxially from thereabove by a lateral overgrowth method has a fine and flat surface and has a reduced threading dislocation density. As a result, a GaN nitride semiconductor layer of high crystal quality is stably provided as a layer formed thereon without increasing manufacturing costs, and thus a semiconductor device having the GaN nitride semiconductor layer will have superior properties.
The following describes embodiments of a method for producing a template for epitaxial growth (hereinafter, sometimes referred to as the “present production process”) and a template for epitaxial growth (hereinafter, sometimes referred to as the “present template”) according to the present invention with reference to the drawings.
First, the sapphire (0001) substrate 2 is prepared, and an Ni mask 5 which is patterned in a stripe shape is formed on the substrate (see
The sapphire substrate 2 having recesses and protrusions on its surface is put inside a conventional metalorganic vapor phase epitaxy (MOVPE) reaction chamber (not shown), and the initial-stage AlN layer 3 is epitaxially grown on the sapphire substrate 2 by the MOVPE method (see
The growth temperature of the initial-stage AlN layer 3 is below 1,300° C., and is set higher (for example, at 1,250° C.) than the epitaxial growth temperature of a general AlGaN layer (1,100° C. to 1,200° C., the crystallization temperature or higher). The pressure is set about 50 Torr or less (for example, about 25 Torr). In the embodiment, the initial-stage AlN layer 3 is subjected to the C axis orientation control (polarity control) so as to orient the growth film from the protrusion tops 7 of the sapphire substrate 2 into the C+ axis; in other words, to provide an Al polar face at the surfaces (protrusion surfaces 9) of the growth film. The C axis orientation control mentioned above is carried out by adjusting the flow ratio (NH3/TMA) between TMA (trimethylaluminum) and NH3 (ammonia) as the materials (precursors) of Al and N under the above-noted temperature and pressure conditions. In this embodiment, as for the conditions of the C axis orientation control, as described above, the pressure is set relatively low (at about below 50 Torr) so as to grow an AlN layer for a template; the growth speed of the layer is set lower than the speed of the AlN layer 4 that is epitaxially grown by a lateral overgrowth method on the initial-stage AlN layer 3; and the flow ratio is, for example, 148.
As for the initial-stage AlN layer 3, it is sufficient that the surfaces (protrusion surfaces 9) of the growth film grown from the protrusion tops 7 are Al polar faces. It is unnecessary to orient the growth film grown from the bottom of the recesses in the grooves 6, into the C+ axis. Moreover, the AlN layer grown from the side walls of the recesses in the grooves 6 is not oriented in the C+ axis, and semi-polar faces or non-polar faces are grown there. Thus, since the edges of the protrusion surfaces 9 have the growth film grown from the side walls of the recesses in the grooves 6, the edges have no Al polar face. The reason only the protrusion surfaces 9 (except for the edges) need to be Al polar faces is because the AlN layer 4, which is epitaxially grown on the initial-stage AlN layer 3 by a lateral overgrowth method, laterally grows from the protrusion surfaces 9 and finally seals the recesses 8, so that the film grown from the recesses 8 stops growing, and consequently it is necessary to consider with respect only to the growth film grown from the protrusion surfaces 9.
Subsequently, an AlN layer 4 is grown by a conventional epitaxial lateral overgrowth method on the initial-stage AlN layer 3 having, on the surface, a recessed and protruded structure (the recesses 8 and the protrusion surfaces 9) formed along the grooves 6 on the sapphire substrate 2 (see
Recesses and protrusions are formed on the sapphire substrate 2, and the initial-stage AlN layer 3 and the AlN layer 4 are sequentially grown as described above, thus providing a template for epitaxial growth having a fine and flat surface and a reduced threading dislocation density (the present template 1).
The following describes examples (Examples 1 to 8) of the present template 1 produced by the present production method, and comparative examples (Comparative Examples 1 to 3) of templates not produced by the present production method with reference to the drawings. In the SEM images shown in the description below, a direction perpendicular to the image (cross section) is the extending direction of the grooves 6 that is the <11-20> direction; and a direction parallel to the image (cross section) and the surface of the sapphire substrate 2 is the <1-100> direction of the sapphire substrate 2. In the examples and comparative examples below, the growth temperatures of the initial-stage AlN layer 3 and the AlN layer 4 are both 1,250° C., and the growth conditions of the AlN layer 4 are the same. The growth conditions of the initial-stage AlN layer 3 are the same in the examples below. For the description below, the same reference numerals as in Examples 1 to 8 are used for the initial-stage AlN layer (in Comparative Examples 1 and 2) and the AlN layer that is epitaxially grown by a lateral overgrowth method in Comparative Examples 1 to 3, making clear that each one of the initial-stage AlN layer 3 and the AlN layer 4 corresponds to each other. The gradation of the SEM and TEM images shown below is binarized for international application, so that the images are less clear than actual photographic images.
In Comparative Example 1, a C− axis oriented initial-stage AlN layers 3 instead of the C+ axis oriented initial-stage AlN layers 3, was formed, and the AlN layer 4 was epitaxially grown by a lateral overgrowth method under the same growth conditions as in Examples 1 and 2. Specifically, Comparative Example 1 has the polarity of the C axis orientation control for the initial-stage AlN layer 3 that is different from the polarity in Examples 1 and 2. In Comparative Example 1, the width of the grooves 6 on the surface of the sapphire substrate 2 and the gaps between the grooves 6 are 2 μm respectively, and the depth thereof is 0.5 μm. The thicknesses of the initial-stage AlN layer 3 and the AlN layer 4 are 0.5 μm and 4 μm respectively. Additionally, the growth conditions of the C− axis oriented initial-stage AlN layers 3 in Comparative Example 1 are the same as the growth temperature and the pressure in Examples 1 and 2, but the flow ratio between TMA and NH3 (NH3/TMA) is different from the rate in Examples 1 and 2. While the flow ratio between TMA and NH3 (NH3/TMA) is 148 in Examples 1 and 2, the ratio in Comparative Example 1 is relatively high at 1,154.
When
When
In Comparative Example 3, without forming the C+ oriented initial-stage AlN layer 3, an AlN layer 4 was directly epitaxially grown on the sapphire substrate 2 having the grooves 6 on its surface by a lateral overgrowth method under the same conditions as in Examples 1 and 2. Specifically, Comparative Example 3 is different from Examples 1 and 2 in respect to whether or not the initial-stage AlN layer 3 was formed. In Comparative Example 3, the width of the grooves 6 on the surface of the sapphire substrate 2 and the gaps between the grooves 6 are 3 μm respectively, and the depth thereof is 0.5 μm. The thickness of the AlN layer 4 is 10 μm.
As shown in
When
It is generally considered preferable to form deeper grooves on the surface of a sapphire substrate when an AlN layer or the like is directly epitaxially grown on a sapphire substrate having recesses and protrusions thereon by a lateral overgrowth method (see for example, Non-patent Document 3 above). Specifically, when the grooves are shallow, a layer grown from the protrusions between the grooves and a layer grown from the inside of the grooves cannot be separated effectively, so that the effects from the lateral overgrowth cannot be obtained. However, it is confirmed that in the present production method, preferable results are obtained even when the grooves on the sapphire substrate surface are relatively shallow at 0.3 μm to 1 μm. Although the dependency on groove depths is unclear in the analysis result of XRC method, it is preferable that the groove depth is shallow at about 0.3 μm to 0.5 μm according to the pit observation of the surface. When the groove depth is about below 0.5 μm in the present production method, the sapphire substrate 2 receives less damage from the etching process of forming grooves, so that an initial-stage AlN layer 3 of a higher quality is provided and also the costs of forming grooves may be cut, which is thus more preferable.
It is clearly seen, based on the description of the present template 1 of the examples (Examples 1 to 8) and of the comparative examples (Comparative Examples 1 and 2) which were produced without depending on the present production method, that an AlN layer 4 having a fine and flat surface and a reduced threading dislocation density is obtained by subjecting an initial-stage AlN layer 3 to C+ axis orientation. It is also found that a GaN nitride semiconductor layer of high crystal quality is obtained by forming a GaN nitride semiconductor layer (AlGaNIn layer) that is included in a GaN nitride semiconductor device such as a light-emitting diode and a semiconductor laser, on the AlN layer 4 of the present template 1. Accordingly, a GaN nitride semiconductor device of higher properties is provided by using the present template 1.
The present production method and present template were described above in detail. However, the characteristic of the present invention lies in the provision of a C+ axis oriented initial-stage AlN layer 3. The above-noted process and conditions are simply an example for description, and these conditions and the like may be appropriately modified without departing from the present invention including the above characteristic.
For description, although the AlN layer 4 is epitaxially grown on the initial-stage AlN layer 3 by a lateral overgrowth method in the above-noted embodiments, an AlGaN layer, instead of an AlN layer, may be used as a semiconductor layer that is epitaxially grown on the initial-stage AlN layer 3 by a lateral overgrowth method. In the embodiments, although not discussed in the examples, it is conventionally known that it is easier to laterally overgrow an AlGaN layer than an AlN layer since Ga can be easily dissolved and that, as disclosed in e.g., Patent Document 1, an AlGaN layer or a GaN layer, instead of an AlN layer, is directly epitaxially grown by a lateral overgrowth method on a sapphire substrate having recesses and protrusions on its surface, so that it is obvious that the present invention is also applicable to the lateral overgrowth of an AlGaN layer.
In the embodiments mentioned above, as the C axis orientation control method by which it is possible to obtaine the C+ axis oriented initial-stage AlN layer 3, which is the characteristic of the present invention, it has been described that flow ratios (NH3/TMA) were adjusted so as to orient the layer to C axis; however the C axis orientation control method may be accomplished by controlling with reaction gas, supplying TMA earlier at the initial-growth stage or the like, instead of adjusting the flow ratios. Moreover, for the above-noted description, the metalorganic vapor phase epitaxy (MOVPE) is applied as the method of growing the initial-stage AlN layer 3 and the AlN layer 4, but the hydride VPE (vapor phase epitaxy) method may be applied as the growth method instead of MOVPE. Furthermore, in the embodiments, although the surface of the sapphire (0001) substrate 2 is processed to form recesses and protrusions by photolithography and anisotropic etching, as the recesses and protrusions forming process, processing methods other than anisotropic etching may be applied as long as flat protrusion tops are provided.
The template for epitaxial growth and the method for producing the same according to the present invention are applicable to produce a GaN nitride semiconductor device such as a light-emitting diode and a semiconductor laser.
1: Template for epitaxial growth according to the present invention
2: Sapphire (0001) substrate
3: Initial-stage AlN layer
4: AlxGayN(0001) layer
5: Ni mask
6: Grooves formed on the surface of the sapphire substrate
7: Protrusion top
8: Recess of initial-stage AlN layer
9: Protrusion surface of initial-stage AlN layer
10: Cavity (void)
This application is a divisional of co-pending U.S. patent application Ser. No. 13/517,970 filed on 20 Jun. 2012; which application is a National Phase filing under 35 U.S.C. §371 of International Application No. PCT/JP2009/071541 filed on Dec. 25, 2009.