This application claims benefit of priority to Korean Patent Application No. 10-2022-0147629, filed on Nov. 8, 2022, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference in its entirety.
Example embodiments of the present disclosure relate to a method of controlling a semiconductor process and a semiconductor processing apparatus.
A semiconductor process may include, e.g., a photolithography process, an etching process, a deposition process, and the like, for forming a plurality of layers on a substrate, and a plurality of patterns may be formed on each of the plurality of layers. As line widths of the plurality of patterns and a spacing between the patterns have been gradually refined, a photolithography process using a shorter wavelength, e.g., extreme ultraviolet (EUV) light, has been suggested.
According to an example embodiment of the present disclosure, a method of controlling a semiconductor process includes forming a plurality of sample overlay keys by irradiating a first dose of extreme ultraviolet (EUV) light to a first photoresist layer formed on at least one sample wafer; determining a sample correction parameter for correcting a sample overlay error measured from the plurality of sample overlay keys; updating the sample correction parameter based on a difference between the first dose and a second dose; forming a plurality of main overlay keys by irradiating a second dose of extreme ultraviolet light to a second photoresist layer formed on the sample wafer based on the updated sample correction parameter; determining the main correction parameter based on a main overlay error measured from the plurality of main overlay keys; and performing a photolithography process on a wafer different from the sample wafer based on the main correction parameter.
According to an example embodiment of the present disclosure, a method of controlling a semiconductor process includes forming a plurality of sample layers including a plurality of sample overlay keys on at least one sample wafer while a light source outputs a first dose of extreme ultraviolet (EUV) light; generating a sample correction parameter based on a sample overlay error measured from the plurality of sample overlay keys; forming a plurality of layers including a plurality of main overlay keys on the sample wafer while the light source outputs a second dose of EUV light different from the first dose; generating a main correction parameter using the sample correction parameter, and a difference between a main overlay error measured in the plurality of main overlay keys and the sample overlay error; and controlling a photolithography process performed on a wafer different from the sample wafer using the main correction parameter.
According to an example embodiment of the present disclosure, a semiconductor processing apparatus includes a light source configured to output EUV light; a mask stage on which a mask is seated; a wafer stage on which a wafer is seated; an optical system configured to reflect EUV light output by the light source and to allow EUV light reflected from the mask to be incident to the wafer; and a control unit configured to control the light source, the mask stage, the wafer stage, and the optical system, wherein, when a first lot arrives in a state in which no previous history is present, the control unit performs sets output of the light source to be a first dose and a second dose higher than the first dose sequentially, performs a sample photolithography process on at least one sample wafer included in the first lot and determines a main correction parameter for correcting an overlay error, and wherein, when a second lot arrives following the first lot, the control unit determines output of the light source to be the second dose and performs a photolithography process on a plurality of wafers included in the second lot based on the main correction parameter.
Features will become apparent to those of skill in the art by describing in detail exemplary embodiments with reference to the attached drawings, in which:
Hereinafter, embodiments of the present disclosure will be described as follows with reference to the accompanying drawings.
Referring to
The light source 110 may generate and emit EUV radiation (e.g., EUV light) having a high degree of energy density within a wavelength range of several nanometers to several tens of nanometers. In example embodiments, the light source 110 may generate and output EUV light having a high degree of energy density in a 13.5 nm wavelength band. The light source 110 may include, e.g., a plasma-based light source or a synchrotron radiation light source. A plasma-based light source may generate plasma and may use light emitted by the plasma, and may include, e.g., a laser-produced plasma (LPP) light source or a discharge-produced plasma (DPP) light source. For example, when the light source 110 includes a plasma-based light source, a condensing mirror, e.g., an elliptical mirror or a spherical mirror, for increasing energy density of EUV light incident on the first sub-optical system 120 may be further included in the light source 110.
The first sub-optical system 120 may include a plurality of mirrors. For example, in the semiconductor processing apparatus 100 according to an example embodiment, the first sub-optical system 120 may include two or three mirrors. The first sub-optical system 120 may transfer EUV light emitted from the light source 110 to the mask 145. EUV light emitted from the light source 110 may be reflected by mirrors included in the first sub-optical system 120 and may be incident on the mask 145 mounted on the mask stage 140. In an example embodiment, the first sub-optical system 120 may curve EUV light in the form of a curved slit and may allow light to be incident on the mask 145.
The mask 145 may be a reflective mask including a reflective region, a non-reflective region, and/or an intermediate reflective region. The mask 145 may include a reflective multilayer film for reflecting EUV light from a substrate formed of a low thermal expansion coefficient material (LTEM), e.g., quartz, and an absorption layer pattern formed on the reflective multilayer film. The reflective multilayer film may have a structure in which a molybdenum film (Mo layer) and a silicon film (Si layer) are alternately stacked. The absorption layer may be formed of, e.g., TaN, TaNO, TaBO, Ni, Au, Ag, C, Te, Pt, Pd, Cr, or the like. For example, the absorption layer portion may correspond to the above-described non-reflective region and/or intermediate reflective region.
The mask 145 may reflect EUV light from the first sub-optical system 120 toward the second sub-optical system 130. For example, EUV light passing through the first sub-optical system 120 may be structured according to a pattern shape including a reflective multilayer film and an absorption layer on a substrate, and may be incident on the second sub-optical system 130. EUV light may be structured to include at least second-order diffracted light based on the pattern on the mask 145. The structured EUV light may be incident on the second sub-optical system 130 while retaining the pattern shape information included in the mask 145, and may be irradiated toward the wafer W through the second sub-optical system 130 such that an image corresponding to the pattern shape included in the mask 145 is formed. For example, the structured EUV light may be irradiated toward the photoresist layer applied on the wafer W and may form a predetermined pattern on the photoresist layer.
The second sub-optical system 130 may include a plurality of mirrors. For example, as illustrated in
The second sub-optical system 130 may be controlled such that the EUV light reflected from the mask 145 is incident while forming a predetermined slope with respect to the upper surface of the wafer W. For example, the second sub-optical system 130 may adjust a travel path of the EUV light such that the EUV light may be incident while forming an angle of about 6 degrees with the upper surface of the wafer W.
The mask 145 may be seated on the mask stage 140, and the wafer W may be seated on the wafer stage 150. For example, the mask stage 140 and the wafer stage 150 may be controlled by the control unit 160 (e.g., a controller). In the initial state, in which the mask 145 and the wafer W are seated on the mask stage 140 and the wafer stage 150, respectively, when the upper surface of the mask 145 and the wafer W is defined as an X-Y plane, each of the mask stage 140 and the wafer stage 150 may be moved by the control unit 160. In an example embodiment, the control unit 160 may rotate each of the mask stage 140 and the wafer stage 150 on the X-Y plane with respect to the Z-axis, or on the Y-Z plane or the X-Z plane with respect to one axis of the X-Y plane. By the movement of the mask stage 140 and/or the wafer stage 150, as described above, the mask 145 and/or the wafer W may move or rotate along at least one of the X-axis, Y-axis, and Z-axis.
The measurement unit 170 may measure a critical dimension (CD) and/or overlay error of a plurality of patterns formed on the wafer W. For example, the measurement unit 170 may include an electron microscope or an optical microscope, e.g., a scanning electron microscope (SEM) or a transmission electron microscope (TEM). Also, the measurement unit 170 may measure a critical dimension or an overlay error using an image ellipsoidal polarization method or a spectroscopic image ellipsoidal polarization method. In example embodiments, the measurement unit 170 may be provided as a device different from the semiconductor processing apparatus 100.
For example, when a first layer and a second layer are stacked in order on the wafer W, the measurement unit 170 may measure overlay errors of a plurality of first overlay keys included in the first layer and a plurality of second overlay keys included in the second layer. The control unit 160 may generate a correction parameter for adjusting at least one of the light source 110, the optical systems 120 and 130, the mask stage 140, and the wafer stage 150 based on the overlay error measured by the measurement unit 170. As the control unit 160 performs the photolithography process based on the correction parameter, an overlay error may be reduced.
However, when the photolithography process is started in the absence of a previous history, a correction parameter for reducing an overlay error by the control unit 160 by adjusting the light source 110, the optical systems 120 and 130, the mask stage 140, and the wafer stage 150 may not be present. Accordingly, the control unit 160 may form a photoresist layer on a sample wafer, may perform a sample photolithography process, may measure the overlay error, and may generate a main correction parameter required to control the photolithography process for forming an actual semiconductor device based on the measured error.
In an example embodiment, the sample photolithography process for generating a main correction parameter may be executed under conditions different from those of a general photolithography process. For example, a sample photolithography process is performed with a first dose (dose) of EUV light, whereas a photolithography process for actually forming a semiconductor device may be performed with a second dose of EUV light, higher than the first dose. Also, in an example embodiment, a photoresist layer having relatively low quality may be used in the sample photolithography process. Accordingly, time and costs required for the sample photolithography process may be reduced, and efficiency of the semiconductor process may be improved.
The K3 correction parameter may be for an overlay error proportional to coordinates on both sides in the X-axis direction, and the K4 correction parameter may be for an overlay error proportional to coordinates on both sides in the Y-axis direction. Accordingly, the K3 correction parameter may be represented in the form of dx=k3*x, and the K4 correction parameter may be represented in the form of dy=k4*y. Also, in example embodiments, other linear correction parameters may be further generated in addition to the K1 to K4 correction parameters.
The K13 correction parameter may be defined as dx=k3*x3, and the K14 correction parameter may be defined as dy=k14*y3. Also, in example embodiments, other correction parameters may be further defined as the third order correction parameters other than the K13 correction parameter and the K14 correction parameter. For example, a K15 correction parameter proportional to the product of the square of the X-axis coordinate and the Y-axis coordinate in the X-axis direction may be represented as dx=k15*x2*y.
Correction parameters for reducing an overlay error in an example embodiment may be determined in a sample process. The sample process may be a process for forming only overlay keys on a wafer (e.g., without other than semiconductor elements involved in an actual operation of the semiconductor device). The overlay keys may have a relatively larger critical dimension than structures included in the semiconductor elements, and accordingly, the sample process may be performed with relatively low accuracy as compared to the main process of forming the semiconductor elements.
In an example embodiment, a sample photolithography process of irradiating EUV light to a photoresist layer to form overlay keys in a sample process may be performed with relatively weak intensity EUV light. Also, when desired, a photoresist layer for forming overlay keys may be used as a product of relatively lower quality than the photoresist layer used for forming the semiconductor elements. Accordingly, the costs and time required for the sample process may be reduced, and overall efficiency of the semiconductor process may be improved.
However, as compared to the photolithography process for forming semiconductor elements, by differently controlling or adopting the EUV light and/or the photoresist layer in the sample photolithography process, the accuracy of the correction parameter for correcting the overlay error may be reduced. In other words, when the correction parameter is determined only with the overlay error measured in the sample photolithography process, the overlay error may not be sufficiently corrected.
In an example embodiment, a first photolithography process may be performed to generate a first correction parameter, and a second photolithography process may be performed under the same conditions as the photolithography process for forming semiconductor elements. For example, semiconductor elements may be formed by the second photolithography process and subsequent processes. Also, an overlay error may be re-measured from overlay keys formed by the second photolithography process, and a main correction parameter necessary for controlling the photolithography process forming semiconductor elements may be determined based on the overlay error. Accordingly, a main correction parameter to reduce an overlay error may be generated while reducing the costs and time required for the sample process.
Referring to
In each of the plurality of chip regions 210, a plurality of elements included in an integrated circuit (e.g., transistors, capacitors, and resistors) may be formed. Overlay keys may be formed in the key regions 230 of the isolation region 220. As described above with reference to
In an example embodiment, a sample process of forming only overlay keys in key regions 230 may be executed to determine a correction parameter. For example, the sample process may be executed prior to a process for forming devices in the plurality of chip regions 210, and may be executed when a previously created correction parameter is not present or when a new correction parameter needs to be determined after a long time has elapsed since the previous correction parameter was created.
The sample process may include sample photolithography processes. However, overlay keys may have relatively large critical dimensions and spacing between structures (e.g., as compared to elements formed in the plurality of chip regions 210), and accordingly, the process may not need to be performed under the same conditions as a photolithography process for actually forming elements in the plurality of chip regions 210. In an example embodiment, by performing at least a portion of the sample photolithography processes using EUV light having relatively low intensity (as compared to the photolithography process for forming actual semiconductor elements), time and costs required to create a correction parameter to reduce the overlay error may be reduced. In example embodiments, the photoresist layer applied to the wafer 201 in the sample photolithography process may be a relatively inexpensive product (as compared to the photoresist used in the main photolithography process).
Referring first to
Prior to performing the first photolithography process with a first dose of EUV light in operation S10, a wafer may be seated on a wafer stage of a semiconductor processing apparatus, and a mask may be seated on a mask stage. Also, a first photoresist layer may be formed on the wafer. A first dose of EUV light may be emitted from a light source able to emit light in an extreme ultraviolet wavelength band, and may be reflected from a mask to be incident on a first photoresist layer.
By performing the first photolithography process of operation S10, sample overlay keys may be formed on the wafer. The sample overlay keys may include a plurality of structures formed on two or more layers stacked on a wafer. For example, by performing the first photolithography process using the first dose of EUV light at least twice as in operation S10, sample overlay keys may be formed on two or more stacked layers. The sample overlay keys may be formed in an isolation region defined between a plurality of chip regions on a wafer by the first photolithography process, and elements for implementing actual integrated circuits may not be formed in the plurality of chip regions. For example, referring to
The control unit of the semiconductor processing apparatus may generate a sample correction parameter by referring to the sample overlay keys formed using the first dose of EUV light (S11). The sample correction parameter may be determined according to a sample overlay error measured in the sample overlay keys formed by the first photolithography process.
When a sample correction parameter is generated, a second photolithography process may be performed with a second dose of EUV light (S12). For example, the second dose may be higher than the first dose, and the second photolithography process of operation S12 may be performed using EUV light having a relatively higher degree of intensity than the first photolithography process of operation S10. For example, the second photolithography process of operation S12 may be performed under the same conditions as a photolithography process for forming semiconductor elements included in an integrated circuit. Also, in the second photolithography process, images for forming semiconductor elements in the chip regions of the wafer may be generated.
The second photolithography process of operation S12, which is performed using EUV light of higher degree of intensity, may require a longer time than the first photolithography process in operation S10. However, since higher intensity of EUV light is used, an image formed on a second photoresist layer in the second photolithography process may have a higher quality than an image formed on the first photoresist layer in the first photolithography process.
Accordingly, an overlay error measured in a main overlay keys formed by the second photolithography process may be different from the overlay error measured in the sample overlay keys formed by the first photolithography process. The control unit of the semiconductor processing apparatus may generate a main correction parameter by modifying the sample correction parameter by referring to the overlay error measured in the main overlay keys formed by the second photolithography process (S13). In an example embodiment, the control unit may correct the sample correction parameter based on the difference between the overlay error measured in the main overlay keys and the overlay error measured in the sample overlay keys, and may generate the main correction parameter.
When the main correction parameter is generated, the control unit of the semiconductor processing apparatus (e.g., the control unit 160 of the semiconductor processing apparatus 100) may perform a photolithography process with the second dose of EUV light based on the main correction parameter (S14). The photolithography process of operation S14, which is performed using the main correction parameter, may be another wafer put into the process following the sample wafer to which the operations of operations S10 to S13 are applied.
Meanwhile, the photolithography process of operation S14 may be a portion of a semiconductor process for forming elements in a plurality of chip regions included in a wafer using the second dose of EUV light. In other words, by performing operations S10 to S13 on the sample wafer to generate the main correction parameter, which may reduce the overlay error, and performing a photolithography process for forming elements in the plurality of chip regions of different wafers based on the main correction parameter, overlay error may be reduced.
Referring to
The light source 110 included in the semiconductor processing apparatus 100 may irradiate a first dose of EUV light toward the first photoresist layer formed in operation S20 (S21). EUV light may be reflected from the mask 145 and may be irradiated toward the first photoresist layer, and accordingly, an image corresponding to a pattern formed on the mask 145 may be created on the first photoresist layer.
When an image including a pattern is created in the first photoresist layer, a plurality of sample overlay keys may be formed by on the sample wafer (S22). For example, a plurality of sample overlay keys may be formed by the first photolithography process in operations S20 and S21, and an etching process and/or a deposition process subsequent to the first photolithography process. The plurality of sample overlay keys may include a plurality of structures formed on a plurality of sample layers stacked in a direction perpendicular to the upper surface of the sample wafer.
The control unit 160 of the semiconductor processing apparatus 100 may measure sample overlay errors in the plurality of sample overlay keys, and may determine a sample correction parameter based on the measurement (S23). The sample correction parameter may include data necessary to control, e.g., adjust position of, the wafer stage 150, the mask stage 144, and an optical system (e.g., the first and second sub-optical systems 120 and 130) in the semiconductor processing apparatus 100 such that a sample overlay error occurring during the process of forming a plurality of sample overlay keys may be reduced.
When the sample correction parameter is determined, rework may be performed (S24). The rework may include a process of removing the plurality of sample overlay keys, and may include, e.g., an etching process, polishing process, and cleaning process for removing sample layers in which the plurality of sample overlay keys are formed. By the rework, the sample wafer may be restored to a state before the first photoresist is applied, e.g., the reworked sample wafer may be thinner than the sample wafer in operation S20.
The semiconductor processing apparatus 100 may form a second photoresist layer by applying a second photoresist on the restored sample wafer (S25). For example, the second photoresist layer may have the same quality as that of the first photoresist layer, or may have a higher quality than that of the first photoresist layer in example embodiments. For example, as compared to the first photoresist layer, the second photoresist layer may have further improved critical dimension uniformity (CDU) and/or line edge roughness (LER).
When the second photoresist layer is formed, the semiconductor processing apparatus 100 may irradiate a second dose of EUV light to the second photoresist layer (S26). The second dose of EUV light may be reflected from the mask 145 and may be irradiated to the second photoresist layer, and the mask 145 reflecting the second dose of EUV light may be the same as the mask reflecting the first dose of EUV light in operation S21. Meanwhile, the second dose is greater than the first dose (e.g., in terms of intensity and application time), and EUV light having a higher degree of intensity than in operation S21 may be irradiated toward the second photoresist layer. When an image is formed on the second photoresist layer by irradiating the second dose of EUV light, a plurality of main overlay keys may be formed by performing a subsequent process (S27).
For example, a plurality of main overlay keys may be formed by a second photolithography process including operations S25 and S26 and an etching process and/or a deposition process performed thereafter. The plurality of main overlay keys may include a plurality of structures formed on a plurality of layers stacked in a direction perpendicular to the upper surface of the sample wafer.
The control unit 160 of the semiconductor processing apparatus 100 may measure the main overlay error in the plurality of main overlay keys, and may calculate the difference between the sample overlay error (i.e., the sample correction parameter determined in operation S23) and the main overlay error (S28).
As described above, since EUV light is irradiated on the same mask (i.e., mask 145) to form both the sample overlay keys and the main overlay keys, the sample overlay keys and the main overlay keys may include similar structures. However, due to the difference in quality between the first photoresist layer and the second photoresist layer applied to the sample wafer in operations S20 and S25, and/or the difference in intensity of EUV light irradiated in each of operations S21 and S26, the sample overlay error and the main overlay error may appear differently.
The control unit 160 of the semiconductor processing apparatus 100 may determine a main correction parameter based on the difference (S29), i.e., in view of the difference between the sample overlay error and the main overlay in operation S28. In an example embodiment, the control unit 160 of the semiconductor processing apparatus 100 may determine the main correction parameter by updating the sample correction parameter based on the difference between the sample overlay error and the main overlay error.
As described with reference to
In an example embodiment, the sample wafer may include a plurality of sample wafers included in a lot, and the method according to the example embodiment described with reference to
For example, a portion of a plurality of wafers included in one lot may be selected as sample wafers. A main correction parameter may be determined by selecting a portion of a plurality of wafers included in a lot as sample wafers and applying the control method described with reference to
In another example, the entirety of wafers included in a lot may be selected as sample wafers, the control method described with reference to
Referring to
Referring to
When the etching process is completed, first sample structures 315 may be formed on the first sample layer 310, as illustrated in
Referring to
As illustrated in
When the sample overlay error OE1 is measured, the control unit of the semiconductor processing apparatus may generate a sample correction parameter based on the sample overlay error OE1. For example, the sample correction parameter may include data for controlling a wafer stage, a mask stage, and an optical system of a semiconductor processing apparatus to reduce the sample overlay error OE1. A sample correction parameter may be generated to reduce the sample overlay error OE1 generated in a first photolithography process of irradiating the first dose of EUV light.
However, process conditions applied to the first photolithography process may be different from process conditions applied to a photolithography process for forming semiconductor elements in chip regions of a wafer. For example, differently from a photolithography process for forming semiconductor elements, EUV light may be irradiated to the first photoresist layer 301 with a relatively weak intensity in the first photolithography process. Also, in example embodiments, the first photoresist layer 301 may have a relatively low quality as compared to a photoresist layer applied on a wafer in a photolithography process for forming semiconductor elements. By limiting the intensity of EUV light and the quality of the first photoresist layer 301, as described above, costs and time required for the first photolithography process may be reduced and the sample correction parameters may be rapidly generated.
However, when the photolithography process for forming semiconductor elements is controlled with reference to only the sample correction parameter, as described above, overlay errors generated in the photolithography process may not be sufficiently corrected due to different process conditions. Accordingly, in an example embodiment, after determining the sample correction parameter, the plurality of sample layers 310, 320, and 330 may be removed, a second photolithography process may be performed under the same conditions as the photolithography process for forming semiconductor elements, and the correction parameter may be modified. For example, a plurality of layers including a plurality of main overlay keys may be formed on the sample wafer 300 by the second photolithography process. The control unit of the semiconductor processing apparatus may measure the main overlay error in a plurality of main overlay keys and may update the sample correction parameter based on the main overlay error and may generate the main correction parameter, which will be described in greater detail with reference to
The process described with reference to
Referring to
The second dose of EUV light may be greater than the first dose of EUV light. Also, in example embodiments, the second photoresist layer 303 may have further improved quality than the first photoresist layer 301.
Referring to
Referring to
As illustrated in
When the main correction parameter is determined, the control unit 160 may control the photolithography process performing to form semiconductor elements in other wafers put into the process after the sample wafer 300 by referring to the main correction parameter. Accordingly, overlay errors which may occur in a photolithography process for forming semiconductor elements included in an integrated circuit may be reduced.
In an example embodiment, the control unit 160 of the semiconductor processing apparatus 100 may measure a sample overlay error and may generate a sample correction parameter, and may generate a main correction parameter. For example, after generating the sample correction parameter, the control unit 160 may generate the main correction parameter based on the difference between the sample overlay error and the main overlay error.
For example, the control unit 160 of the semiconductor processing apparatus 100 may reflect an overlay delta value (i.e., the difference between the overlay sample error and the main overlay error) to the sample correction parameter in advance, based on the difference between the first dose and the second dose, before measuring the main overlay error. For example, the overlay delta value may be determined in advance by performing a photolithography process multiple times while changing the dose of EUV light for a separate test wafer different from the sample wafer. The control unit 160 may update a sample correction parameter based on the overlay delta value, and may perform a second photolithography process based on the updated sample correction parameter.
The control unit 160 may measure the main overlay error generated in the second photolithography process and may calculate an overlay error difference between the sample overlay error and the main overlay error. Also, the control unit 160 may update the overlay delta value using the difference between the sample overlay error and the main overlay, and may generate a main correction parameter by reflecting the updated overlay delta value to the sample correction parameter. The control unit 160 may perform the photolithography process on the main wafers of a subsequent lot put into the process subsequently to the lot including the sample wafers based on the main correction parameter.
When a photolithography process is performed with a first dose of EUV light, a temperature may increase in an optical system, a mask, and a wafer. Similarly, when the photolithography process is performed with the second dose of EUV light, the temperature of the optical system, a mask, and a wafer may increase. However, due to the difference in intensity of EUV light, a first temperature change when the photolithography process is performed with the first dose of EUV light may be different from a second temperature change when the photolithography process is performed with the second dose of EUV light. Due to the difference between the first temperature change and the second temperature change, a sample overlay error and a main overlay error may appear differently.
The difference between the first temperature change and the second temperature change may be due to the difference between the first dose and the second dose, and the difference between the sample overlay error and the main overlay error due to the difference between the first temperature change and the second temperature change may be a system dependent variable. Accordingly, the control unit 160 of the semiconductor processing apparatus 100 may perform the photolithography process on a test wafer, e.g., a non-product wafer (NPW), while changing the dose of EUV light, and may obtain an overlay delta value, which is a difference in overlay error according to the dose of EUV light, in advance.
The control unit 160b may update the sample correction parameter obtained after the first photolithography process using an overlay delta value according to a difference in dose of EUV light. Also, by updating the overlay delta value with the measured overlay difference, after performing the second photolithography process based on the updated sample correction parameter, an overlay error may be accurately corrected for main wafers of a subsequent lot other than the sample wafers.
For example, in the example embodiment illustrated in
The control unit 160 of the semiconductor processing apparatus 100 may obtain overlay delta values in advance according to a dose difference of EUV light irradiated on the test wafer using a test wafer, e.g., a non-product wafer, and may store the values in a memory. The overlay delta values stored in the memory may be applied to correct the sample correction parameter obtained by the control unit from the first photolithography process according to the difference in the dose of EUV light applied to each of the first photolithography process and the second photolithography process, performed in order on the sample wafer.
Referring to
When the semiconductor processing apparatus 100 receives wafers grouped into a lot, the control unit 160 of the semiconductor processing apparatus may determine whether a previous history is present (S101). The semiconductor processing apparatus receiving wafers may be configured to perform a photolithography process using EUV light. The control unit 160b may determine whether there is a previous history of performing the photolithography process by irradiating EUV light to the mask 145 disposed on the mask stage 144 in process S101.
In the case in which the result of the determination in operation S101 is that the previous history is not present, the control unit 160 may perform a task for generating a correction parameter necessary for reducing the overlay error. The control unit may first perform a first photolithography process with a first dose of EUV light (S102). The semiconductor processing apparatus may form a sample overlay key (S103) by performing the first photolithography process, and may generate a sample correction parameter for correcting a sample overlay error measured in the sample overlay key (S104).
When the sample correction parameter is determined, the sample layer on which the sample overlay key is formed may be removed by a rework process (S105). The sample layer formed on the sample wafer may be removed by the rework process, and the sample wafer may be restored to an original bare wafer state.
The control unit of the semiconductor processing apparatus may update the sample correction parameter based on the difference between the first dose and the second dose (S106). Operation S106 may not necessarily need to be performed after the rework process of operation S105, e.g., operation S106 may be started before the rework process or may be performed together with the rework process.
The second dose of EUV light may be an output of a light source in a second photolithography process to be performed on a sample wafer restored to an original state after the rework process is completed. Since the second dose has a predetermined value, the control unit may update the sample correction parameter by referring to the overlay delta value determined according to the difference between the first dose and the second dose. As described above with reference to
The semiconductor processing apparatus may perform a second photolithography process with reference to the sample correction parameter updated by the overlay delta value (S107). The second photolithography process may be performed with a second dose of EUV light, and a main overlay key (S108) may be formed by the second photolithography process. The control unit may measure the main overlay error on the main overlay key.
The control unit may calculate the difference between the sample overlay error and the main overlay error, and may correct the overlay delta value applied to update the sample correction parameter in operation S106 using the difference in the overlay errors (S109). Also, by applying the overlay delta value corrected in operation S109 to the sample correction parameter obtained in operation S104, a main correction parameter to be applied to the photolithography process of wafers grouped into a subsequent lot may be generated (S110).
When the main correction parameter is generated, the semiconductor processing apparatus may correct the overlay error with the main correction parameter and may perform the photolithography process without performing a sample photolithography process on the wafers of a subsequent lot. For example, when wafers included in a new lot (i.e., operation S100) are determined to have a previous history present (i.e., operation S101), a photolithography process may be immediately performed with a second dose of EUV light (S111), i.e., without performing operations S102 to S110. The photolithography process in operation S111 may include a process of imaging a predetermined pattern by irradiating the second dose of EUV light to the photoresist layer formed on the wafer. Thereafter, by performing subsequent processes, e.g., a deposition process, an etching process, and a cleaning process (S112), semiconductor elements for implementing an integrated circuit may be formed in the chip regions of the wafer.
By way of summation and review, when a photolithography process for forming a pattern on a photoresist layer using EUV light is performed without previous history, a sample photolithography process for determining a correction parameter for correcting an overlay error may be performed. However, when the sample photolithography process is performed under the same conditions as the main photolithography process for forming actual patterns, costs and time may increase.
In contrast, example embodiments provide a method of controlling a semiconductor process and a semiconductor processing apparatus which may reduce the time and costs required for the sample exposure process using relatively weak intensity EUV light and/or a low quality photoresist layer in a sample photolithography process for determining correction parameters to reduce an overlay error. That is, when a sample photolithography process is performed in a state in which the correction parameter for reducing the overlay error has not been determined (i.e., in a state in which there is no previous history), a relatively low dose of EUV light may be used or a relatively low quality photoresist layer may be used. Accordingly, by swiftly completing the sample photolithography process at a low cost, the entire process of manufacturing a semiconductor may be efficiently controlled.
The methods, processes, and/or operations described herein may be performed by code or instructions to be executed by a computer, processor, controller, or other signal processing device. The computer, processor, controller, or other signal processing device may be those described herein or one in addition to the elements described herein. The algorithms, code or instructions for implementing the operations of the method embodiments herein may transform the computer, processor, controller, or other signal processing device into a special-purpose processor for performing the methods herein.
Also, another embodiment may include a computer-readable medium, e.g., a non-transitory computer-readable medium, for storing the code or instructions described above. The computer-readable medium may be a volatile or non-volatile memory or other storage device, which may be removably or fixedly coupled to the computer, processor, or controller which is to execute the code or instructions for performing the method embodiments described herein.
Example embodiments have been disclosed herein, and although specific terms are employed, they are used and are to be interpreted in a generic and descriptive sense only and not for purpose of limitation. In some instances, as would be apparent to one of ordinary skill in the art as of the filing of the present application, features, characteristics, and/or elements described in connection with a particular embodiment may be used singly or in combination with features, characteristics, and/or elements described in connection with other embodiments unless otherwise specifically indicated. Accordingly, it will be understood by those of skill in the art that various changes in form and details may be made without departing from the spirit and scope of the present invention as set forth in the following claims.
Number | Date | Country | Kind |
---|---|---|---|
10-2022-0147629 | Nov 2022 | KR | national |