Patent Application
20140113439
This is invention relates to methods for the deposition of amorphous silicon films and in particular such films with a thickness of 3 μm or above thicknesses.
It has been found that when seeking to deposit the thicker amorphous silicon films, such as those with a thickness of 3 μm or above, there can be significant problems with adhesion of the film to the substrate surface. Currently this is limiting the use of amorphous silicon film, especially in the MEMS industry.
Amorphous silicon is the non-crystalline allotropic form of silicon. It can be deposited in thin films onto a variety of substrates, offering some unique capabilities for a variety of electronics applications. Amorphous silicon is used in Microelectromechanical systems (MEMS) and Nanoelectromechanical systems (NEMS), Solar cells, Microcrystalline and micromorphous silicon, Large-scale production, and even available for roll-to-roll processing technique on various substrates. Specific MEMS applications for amorphous silicon films are:
1. thin film devices, including photodiodes or thin film transistors for colour or infrared sensing or piezoresistors for pressure sensors.;
2. masking layers for glass etching in micro-fluidic applications, or even as thin electrodes in a dielectrophoretic chip, because of its good resistance in highly concentrated HF solutions;
3. sacrificial layers in the micro-fabrication of capacitive ultrasonic transducers because of its simple removal in an alkaline solution (TMAH or KOH);
4. definion of a nano-gap in piezoelectric resonators for mechanical RF magnetic field modulation by dry-release removal of a-Si:H films by XeF2 etching.;
5. providing an interlayer for anodic bonding in order to improve bonding quality or in the fabrication of nano-fluidic channels.
The Applicants have developed a method for improving adhesion of a-Si:H thin films and, with additional features in particular embodiments, to lowering stress and improving uniformity.
The invention includes a method of depositing, in a chamber, an amorphous silicon layer on a surface of a substrate when the surface is pretreated with a NH3 plasma prior to deposition of the amorphous silicon layer.
In embodiments of the invention the NH3 plasma may have at least one of the following process conditions:
(a) an RF power supplied in the range of 150-250 W;
(b) the NH3 flow rate is between 80 and 110 sccm;
(c) the chamber pressure is between 800-1000 m Torr;
(d) the NH3 plasma is run for about 5 minutes.
The substrate may be made of silicon or a silicon containing material. The substrate may be silicon or glass (SiO2). The substrate may be coated with an intermediate layer of silicon dioxide or silicon nitride. However, the invention is not limited to such embodiments.
It is preferred that the substrate is heated to a constant temperature across its width by a flow of inert gas so as to improve the uniformity of the subsequent process steps. Conveniently the inert gas is N2.
The amorphous silicon film may be deposited using SiH4 as a process gas and this may be carried in a carrier gas, for example argon.
Typically, the chamber includes a platen. The platen temperature during the deposition of the amorphous silicon film may be between 200° C. and 350° C., for example 200° C. Preferably the chamber walls are at ˜75° C. and, where a showerhead is used for delivering the process gas, the showerhead, if used, may have a temperature in the region of 200° C.
When deposited in the above manner, the stress of the amorphous film may be low, for example less than or equal to 50 MPa.
Although the invention has been defined above, it is to be understood that it includes any invention combination of the features set out above or in the following description, drawings or claims.
The invention may be performed in various ways and a specific example will now be described in connection with the accompanying Figures in which:
a and 1b contrast the adhesion test results for a 3.2 μm silicon film deposition when deposited (a) using normal deposition techniques and (b) when using an embodiment of the present invention;
In order to improve adhesion, lower stress, and improve uniformity during the amorphous silicon deposition step a novel NH3 plasma substrate treatment step has been developed.
As an example, a low stress amorphous silicon film that does not show any signs of delamination has been successfully achieved with the following process steps. The process parameters are shown in Table 1.
Wafers are loaded into the process module which can comprise a vacuum processing chamber as shown in
Wafers are loaded into the process module at reduced pressure (<0.1 Torr) and brought to process temperature with the aid of N2 (>2Torr and ˜2000 sccm). At temperature a NH3 plasma treatment step was carried out using a RF (14) driven showerhead (5, 6) as can be seen in
The NH3 plasma substrate treatment step is a key process step for increasing the adhesion property between the deposited amorphous silicon film and the substrate. For example, an NH3 plasma substrate treatment step of 200 W high frequency power (13.56 MHz), 900 mTorr pressure and 95 sccm NH3 gas flow for 5 min. The film stress could be further tuned by running at low temperature deposition process (as low as 200° C.) for extra low stress film deposition (50 MPa);
Experimentally it was found that an amorphous silicon film deposited at low temperature, coupled with optimised process parameters of RF frequencies, power, pressure and gas flows, could produce a very low stress (≦50 MPa) amorphous silicon film. For example, at 200° C. for showerhead and platen temperatures, 75° C. for chamber side wall temperature, deposition with 120 W high frequency power (13.56 MHz), 700 mTorr process chamber pressure, 120 sccm for SiH4 and 500 sccm for Ar gas flows would offer the extra low tensile stress amorphous silicon film deposition (+48.1 MPa) with a deposition rate about 109 nm/min.
In
It will be seen that it is the NH3 plasma substrate treatment step which has significantly increased the amorphous silicon film adhesion property.
The traditional methods for enhancing the deposited film adhesion property may include increasing the amorphous silicon film deposition temperature and introducing an intermediate layer, such as silicon nitride and silicon dioxide, but both of the methods have shortcomings. Elevated temperature >350° C. will not be acceptable in many applications due to stress and thermal budget considerations while the introduction of additional layers results in cost, complication and potentially unwanted films to be subsequently removed.
The following experiments were carried out for comparison of the film adhesion enhancement.
The results in Table 2 show that a higher platen temperature (350° C.) may enhance the adhesion property, but it also introduced a high compressive stress for the deposited amorphous silicon film. With the above example, the higher temperature deposition resulted in 10% fail of the standard adhesion test with film in −332.9 MPa high compressive stress.
The results in Table 3 & 4 (both for films ˜3.3 μm) have show the poor adhesion of the deposited amorphous silicon film, with either SiN or SiO2 interlayer, and without NH3 plasma step.
Table 5 summarizes the key findings from Tables 1-4. Namely that for Si, SiO2 and SiN surfaces that have experienced a vacuum break all a-Si:H films show signs of delamination with the exception of the NH3 plasma treated substrate. Raising the process temperature to 350° C. substantially reduces the amount of delamination; however even this aggressive process is not as productive as the low stress 200° C. a-Si:H deposition onto Si that has been treated with NH3 plasma step.
A possible mechanism to understand the improvement in adhesion of the a-Si:H films is described as follows. A silicon surface that has been exposed to atmosphere will have native oxide layer. At the wafer surface the silicon atoms are joined via oxygen atoms in a giant covalent structure. However, at the surface of the silicon dioxide, the silicon-oxygen bonds are hydrolysed in air with time and form —OH groups. Therefore, at the surface, there are Si—OH bonds instead of Si—O—Si bonds as shown in
Thus, with the use of the NH3 plasma substrate treatment step to remove the Si—OH bonds on the top surface of the substrate, the adhesion of the deposited amorphous silicon film is improved significantly.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1218697.9 | Oct 2012 | GB | national |
| Number | Date | Country | |
|---|---|---|---|
| 61715411 | Oct 2012 | US |