The present invention relates to a method of manufacturing a printed circuit board, and more particular to a method of manufacturing a polymer printed circuit board.
Methods of manufacturing printed circuit board (PCB) contain a subtractive method and a semi-additive method, etc. However, the subtractive method pollutes environment and increases production cost. As using the semi-additive method, cooper is etched decreasingly in deposition process.
As using the subtractive method to manufacture a printed circuit board which includes a copper clad laminate (CCL), and the CCL has a polymer substrate, a glass fiber, and a copper foil, wherein the copper foil is fixed on the polymer substrate and a main part of the copper foil is etched or eliminated. However, water consumption increases greatly as etching the copper foil in photolithography process and in rinsing process. Furthermore, chemical waste and heavy metals produce and pollute the environment.
As applying the semi-additive method to manufacture the printed circuit board, a copper layer is plated on the substrate in chemical deposition process (i.e., electroless deposition), and photoresist (PR) is fixed to expose circuit pattern, then the copper layer is plated on the circuit pattern. Thereafter, the PR is removed and the circuit pattern is etched so as to eliminate a part of the copper layer on the non-circuit pattern. However, copper consumption increases.
A photosintering method is disclosed in US Publication No. 2015/0147486 A1 and US 1008/0286488 A1 so as to manufacture metal pattern on the printed circuit board.
A laser method is disclosed in US Publication No. 2014/0120453 and is employed to manufacture micro-super capacitor. Laser induced graphene (LIG) materials and their use in electronic devices is disclosed in WO 2015175060 A3, but electric conductivity of the LIG is not high.
The present invention has arisen to mitigate and/or obviate the afore-described disadvantages.
The primary objective of the present invention is to provide a method of manufacturing a polymer printed circuit board which adheres the circuit pattern on the material layer securely and obtains outstanding electric conductivity on the circuit pattern after the circuit pattern is pressed.
To obtain above-mentioned objectives, a method of manufacturing a polymer printed circuit board provided by a first embodiment of the present invention contains steps of:
A. providing a material layer consisting of polymer;
B. forming circuit pattern on the material layer, wherein the circuit pattern is comprised of laser induced graphene, and the laser induced graphene is porous;
C. depositing metal nanoparticles on the LIG of the circuit pattern so as to use as a metal seed;
D. pressing the circuit pattern; and
E. forming a metal layer on the LIG of the circuit pattern.
In a second embodiment, a method of manufacturing a polymer printed circuit board contains steps of:
A. providing a material layer consisting of polymer;
B. forming circuit pattern on the material layer, wherein the circuit pattern is comprised of laser induced graphene, and the laser induced graphene is porous;
C. depositing metal nanoparticles on the LIG of the circuit pattern so as to use as a metal seed;
D. forming a metal layer on the LIG of the circuit pattern; and
E. pressing the circuit pattern.
Preferably, the material layer is a polymer film or a substrate on which the polymer is coated.
Preferably, the polymer is selected from the group of polyimide (PI) and polyetherimide (PEI).
Preferably, the LIG is formed on the material layer in a laser induction reacting process which is controlled by a computer.
Preferably, a predetermined area of the material layer is irradiated by laser beams in the laser induction reacting process, and a temperature of the predetermined area of the material layer rises up to at least 1500° C.
Preferably, the metal seed is selected from the group of platinum, gold, palladium, silver, copper, nickel, and zinc.
Preferably, in the step D, the circuit pattern is pressed in a rolling manner or in a laminating manner.
Preferably, the circuit pattern is pressed and is heated within a room temperature to a temperature of 500° C.
Preferably, the metal layer is formed on the LIG of the circuit pattern in any one of electroplating, electroless plating, and sputtering manners.
With reference to
A. providing a material layer 10 consisting of polymer;
B. forming circuit pattern on the material layer 10, wherein the circuit pattern is comprised of laser induced graphene (LIG) 20, as shown in
C. depositing metal nanoparticles on the LIG 20 of the circuit pattern so as to use as a metal seed;
D. pressing the circuit pattern; and
E. forming a metal layer 30 on the LIG 20 of the circuit pattern, as illustrated in FIG. 3.
The material layer 10 is a polymer film or a substrate on which the polymer is coated. Preferably, the polymer is selected from the group of polyimide (PI) and polyetherimide (PEI).
The LIG 20 is formed on the material layer 10 in a laser induction reacting process which is controlled by a computer.
Preferably, the material layer 10 is a smooth surface, and the computer controls laser beams to heat a predetermined area of the material layer 10 on which the circuit pattern is formed, and the laser beams burn the polymer of the material layer 10 so as to carbonize or graphitize the polymer, thus producing conductive carbon or porous graphene on the circuit pattern 10, as shown in
Preferably, the metal seed is selected from the group of platinum, gold, palladium, silver, copper, nickel, and zinc. And nanoparticles are used as the metal seed in the step E, hence the metal layer 30 connects with the LIG 20 quickly and has electric conductivity, as shown in
In the step D, the circuit pattern is pressed in a rolling manner or in a laminating manner by using a machine so that the circuit pattern is adhered on the material layer 10 securely and has outstanding electric conductivity. Preferably, the circuit pattern is pressed in a hot pressing manner in the step D and is heated within a room temperature to a temperature of 500° C.
Referring to
A. providing a material layer 10 consisting of polymer;
B. forming circuit pattern on the material layer 10, wherein the circuit pattern is comprised of laser induced graphene (LIG) 20;
C. depositing metal nanoparticles on the LIG 20 of the circuit pattern so as to use as a metal seed;
D. forming a metal layer 30 on the LIG 20 of the circuit pattern; and
E. pressing the circuit pattern on which the metal layer 30 is formed.
Thereby, the circuit pattern is adhered on the material layer 10 securely and has outstanding electric conductivity after being pressed in the step E.
While the preferred embodiments of the invention have been set forth for the purpose of disclosure, modifications of the disclosed embodiments of the invention as well as other embodiments thereof may occur to those skilled in the art. Accordingly, the appended claims are intended to cover all embodiments which do not depart from the spirit and scope of the invention.
The present application is a divisional application of U.S. patent application Ser. No. 15/402,881, entitled “Method of manufacturing polymer printed circuit board” fled on 10 Jan. 2017, which is incorporated herein by reference.