Patent Application
20180166290
This application claims priority under 35 U.S.C. § 119 to Japanese Patent Application No. 2016-241999 filed on Dec. 14, 2016, the entire content of which is hereby incorporated by reference.
The present invention relates to a method of manufacturing a semiconductor device, in particular, to a method of manufacturing a semiconductor device having a trench.
Silicon etching in which silicon as a constituent of a semiconductor substrate is etched is carried out in a manufacturing process of a semiconductor device to form a trench for isolating an element and a trench for a gate electrode in the semiconductor substrate. In the silicon etching, a plasma etching method has been proposed in which a silicon oxide film or a similar oxide film is used as a mask, the temperature of the semiconductor substrate is kept at −20° C., and oxygen or the like is added to sulfur hexafluoride serving as a main component of plasma etching gas (note, for example, Japanese Patent Application Laid-open No. 2003-37100).
However, in Japanese Patent Application Laid-open No. 2003-37100, since the substrate temperature (sample stage temperature) should be held at −20° C. which is far below 0° C., countermeasures against dew condensation needs to be taken in a cooling part in an etching machine and the flow path of a cooling medium. In addition, when the same etching machine has to operate under both the etching condition that the substrate is processed with the substrate temperature set around room temperature and the etching condition that the substrate is processed with the substrate temperature set at −20° C., a considerable time is needed until the temperature stabilizes. In another patent document, the substrate temperature is set even lower at −45° C. An example of the time required for the temperature to rise and fall between 15° C. and −45° C. is illustrated in
The present invention has been made in view of the above, and it is an object of the present invention therefore to provide a method of manufacturing a semiconductor device with which a desired trench shape can be obtained even at room temperature.
In order to achieve the purpose, the present invention uses the following measures.
First, according to one embodiment of the present invention, there is provided a method of manufacturing a semiconductor device in which a trench is formed in a semiconductor substrate, comprising:
forming a mask from inorganic substance on a front surface of the semiconductor substrate so that the mask has an opening in a portion in which the trench is to be formed;
controlling a temperature of a sample stage in a reaction container of an etching machine so as to keep the sample stage temperature constant;
putting the semiconductor substrate on the sample stage;
introducing etching gas including oxygen and sulfur hexafluoride to an interior of the reaction container while maintaining a flow rate ratio of oxygen to sulfur hexafluoride between 70% and 100%; and
performing plasma etching of the semiconductor substrate with the etching gas to for iii the trench.
According to another embodiment of the present invention, there is provided a method of manufacturing a semiconductor device in which a trench is formed in a semiconductor substrate, comprising:
forming a mask from inorganic substance on a front surface of the semiconductor substrate so that the mask has an opening in a portion where the trench is to be formed;
controlling a temperature of a sample stage in a reaction container of an etching machine so as to keep the sample stage temperature constant;
putting the semiconductor substrate on the sample stage;
introducing etching gas including oxygen and sulfur hexafluoride to an interior of the reaction container while setting a flow rate ratio of oxygen to sulfur hexafluoride to a first ratio;
a first etching step of performing plasma etching of the semiconductor substrate with the etching gas at the first ratio;
introducing, after the first etching step, the etching gas including oxygen and sulfur hexafluoride to the interior of the reaction container while setting the flow rate ratio of oxygen to sulfur hexafluoride to a second ratio which is lower than the first ratio; and
a second etching step of performing plasma etching of the semiconductor substrate with the etching gas at the second ratio.
According to another embodiment of the present invention, there is provided a method of manufacturing a semiconductor device in which a trench is formed in a semiconductor substrate, comprising:
forming a mask from inorganic substance on a front surface of the semiconductor substrate so that the mask has an opening in a portion in which the trench is to be formed;
controlling a temperature of a sample stage in a reaction container of an etching machine so as to keep the sample stage temperature constant;
putting the semiconductor substrate on the sample stage;
performing plasma etching by introducing etching gas including oxygen and sulfur hexafluoride to an interior of the reaction container while setting a flow rate ratio of oxygen to sulfur hexafluoride to a first ratio; and
continuing plasma etching by introducing the etching gas to the interior of the reaction container while changing the flow rate ratio of oxygen to sulfur hexafluoride to a second ratio which is lower than the first ratio, in a single step instead of in stages.
Through use of the measures described above, it is possible to manufacture a semiconductor device in which a trench is shaped so as to have flat and smooth side wall surfaces substantially perpendicular in a thickness direction of a semiconductor substrate even when the substrate temperature is at room temperature.
Now, embodiments of the present invention are described with reference to the drawings.
The plasma etching machine includes a cylindrical reaction container 1 made of aluminum, stainless steel, or other materials. A conductive sample stage 3 on which a semiconductor substrate (silicon substrate or SOI substrate) 2 is placed is provided inside the reaction container 1. The sample stage is controlled so as to have a desired temperature by an external temperature fixing unit 14.
A gas flow rate adjuster (mass flow controller: MFC) (not shown) or an air valve (not shown) controls a flow rate and timing at which a gas used in etching is supplied. The gas is supplied evenly to a front surface of the semiconductor substrate 2 from a gas inlet 4 via a shower head plate 5 which is a transparent window having a porous structure.
A vacuum exhauster (not shown) that includes a turbo-molecular pump (TMP) is provided below the reaction container 1, and the interior of the reaction container 1 is kept at a given pressure by an auto-pressure controller (APC) or other pressure governors (omitted from the drawing). Processed reaction gas is exhausted to the outside of the reaction container 1 via the vacuum exhauster.
A microwave power source 6 and a microwave generator 16 generate a microwave that is introduced through a waveguide 7 to the reaction container 1 via a dielectric window 8 which is transmissive of electromagnetic waves and via the shower head plate 5. An electromagnet 9 for generating a magnetic field is placed on an outer peripheral wall of the reaction container 1. The plasma etching machine is structured to cause electron cyclotron resonance (ECR) through interaction between the magnetic field generated by the electromagnet 9 and the incident microwave, thereby forming high density plasma.
An electrostatic chuck 10 is provided on a surface of the conductive sample stage 3. A direct current voltage is applied by an electrostatic adsorption power source 17 to generate an electrostatic adsorption force with which the semiconductor substrate 2 is fixed to a surface of the electrostatic chuck 10. An insulating cover 18 made of ceramic or quartz is placed around the semiconductor substrate 2. The pieces provided at the center of the etching machine to form a structure on which the semiconductor substrate 2 is placed are collectively referred to as “electrode”.
A groove is formed on the surface of the electrostatic chuck 10 as a structure through which He or a similar inert gas is supplied from a constant temperature gas supply port 15 to a constant temperature gas flow path 12 which is formed between a rear surface of the fixed semiconductor substrate 2 and the electrostatic chuck 10 so that the interior of the flow path 12 is maintained at a given pressure. A medium of which the temperature is controlled by the temperature fixing unit 14 (for example, chiller unit) is circulating in a constant temperature circulatory flow path 13 which is embedded in the sample stage 3, and the temperature of the semiconductor substrate 2 is kept constant by heat conduction through gas in the constant temperature gas flow path 12 and heat conduction through a contacting surface.
A high frequency power source 11 is connected to the conductive sample stage 3 so that a sine wave voltage having a frequency of 13.56 MHz can be applied.
In short, the etching machine includes the reaction container 1, the electrode (sample stage) 3 which is provided inside the reaction container 1 and on which a silicon substrate or an SIO substrate is placed, the microwave power source (magnetron) 6 for generating plasma, the electromagnet 9 provided on the outer peripheral wall of the reaction container 1 to generate a magnetic field, the process gas inlet 4 through which a mixture gas of fluorine-containing gas and oxygen gas is supplied to the interior of the reaction container 1, a unit configured to keep constant the temperature of the silicon or SOI substrate put on the electrode 3 (the unit is made up of the constant temperature gas flow path 12, the constant temperature circulatory flow path 13, and the temperature fixing unit 14), and the high frequency power source 11 configured to supply a high frequency bias to the electrode 3, and the etching machine is configured to form a groove and/or a hole in the silicon or SOI semiconductor substrate 2. The mixture gas of fluorine-containing gas and oxygen gas is supplied from the process gas inlet 4 while the temperature of the mixture gas is kept constant at the same temperature as the sample stage temperature. This helps to control the temperature of the sample stage 3 on which the semiconductor substrate 2 is placed.
Next, with reference to
First, the temperature fixing unit 14 illustrated in
Meanwhile, the semiconductor substrate 2 illustrated in
The plasma etching procedure in the first embodiment is described below with reference to a flow chart of
First, the sample stage temperature in the reaction container 1 is brought to a desired predetermined temperature that is around room temperature (Step S0). Next, the semiconductor substrate 2 on which the mask 22 has been formed is carried into the reaction container 1 and put on the sample stage 3 of which the temperature has been controlled (Step S1). The reaction container 1 is next exhausted by the vacuum pump device to create a vacuum space (Step S2). The etching gas which is a mixture of SF6 and O2 is then introduced to the interior of the reaction container 1 (Step S3). While the interior of the reaction container 1 is kept at a given pressure, for example, 2.5 Pa, the microwave power source 6 and the electromagnet 9 are activated to generate plasma (Step S4).
A high frequency voltage is further applied to the sample stage 3 from the high frequency power source 11 (Step S5). Ions that have the plasma of the etching gas as an ion source are thus accelerated by a high frequency electric field, to enter the semiconductor substrate 2 at a high speed. Plasma etching of the semiconductor substrate 2 is started as a result and, with the progress of the etching processing, a trench is formed in the semiconductor substrate 2 (Step S6). After a given length of time elapses, the application of the high frequency voltage, the microwave introduction, and the magnetic field application are stopped to end the etching processing (Step S7).
The given length of time is the time required until the etching reaches a desired depth, and can be set in advance to a time figured out from calculation, test etching, or the like. A semiconductor device is made up of transistors, resistors, and various other elements, and a method of manufacturing the semiconductor device includes various semiconductor steps in addition to the plasma etching described above.
Thereafter, the reaction container 1 is exhausted of the etching gas and the semiconductor substrate 2 is then carried out of the reaction container 1 (Step S8). In the obtained semiconductor substrate 2, a trench having a substantially ideal shape and a desired depth is formed. An example of the ideally shaped trench is illustrated in
The etch selectivity means the etch selectivity of silicon with respect to an oxide film, and is the etching rate ratio of silicon that is the substrate material to the silicon oxide film that is the mask material.
The shape of the trench obtained under the conditions given above is as follows:
A trench width 23 and a trench depth 24 are defined as a width at an upper end of the trench and a depth to the lowest point in the trench, respectively, and are as illustrated in
In the first embodiment, the sample stage temperature is 15° C. and the etching gas is made up solely of O2 gas and SF6 gas. There is no fear that a component having a low vapor pressure, for example, SiCl or SiBr, may be generated, and a high etching rate is obtained with ease. Since the O2/SF6 gas ratio can be set properly, occurrence of bowing and side etching are suppressed, and results in appropriate anisotropic etching. A high etching rate, 2.6 μm/min at the lowest, is accordingly achieved without fail, and the achieved etch selectivity also has as high a value as 20.
In addition, since the substrate temperature is relatively high in this etching which is performed at room temperature as opposed to etching in the related art in which a low-temperature environment is used, physical adsorption of a reaction product to the semiconductor substrate is reduced, thereby improving the yield greatly without contaminating the semiconductor substrate. Through use of the first embodiment, a desired trench shape can be obtained as described above under easy-to-handle etching conditions that include setting of the substrate temperature at room temperature and using a single step for a binary etching gas system.
The sample stage temperature which is 15° C. in the first embodiment can be set to 10° C. to 20° C. in order to obtain the same result. A favorable result is obtained when the sample stage temperature is within a range of from 5° C. to 30° C.
A trench shape that is obtained when the etching gas flow rate ratio is changed is illustrated in
In the comparative example in which the O2/SF6 ratio is 2:3 (66.7%) to set the ratio of SF6 higher than in the etching condition of the embodiment a phenomenon in which a central part of the trench swells out (bowing) has occurred as illustrated in
While the SF6 gas acts to etch silicon, the O2 gas acts to check the etching rate of the silicon oxide film that is the mask material, acts to form a protective film on a surface of the silicon oxide film that is the mask material by oxidizing silicon and silicon fluoride that are reaction products, and acts to form protective films by oxidizing silicon surfaces on inner wall surfaces of the etched trench. In the comparative example in which the bowing has occurred, the ratio of O2 is lower than in the etching conditions of the first embodiment of the present invention, and it is surmised that a failure to form a protective film capable of withstanding etching due to the low O2 ratio has made the trench shape swollen in the central part of the trench.
Bowing is defined as indicated by the bowing width 25 in
Trench etching in the first embodiment is performed by introducing the etching gas to the reaction container 1 at an arbitrary O2/SF6 ratio within a range of from 70% to 100%. Trench etching in the second embodiment is performed by first conducting trench etching at a first arbitrary O2/SF6 ratio within a range of from 70% to 100%, and then conducting etching at a second arbitrary O2/SF6 ratio within a range of from 70% to 100%. The first ratio is set higher than the second ratio. For example, the semiconductor substrate is etched by conducting etching for a given length of time with the first O2/SF6 ratio set to 100% (Steps S3 to S6), and then changing the gas flow rate ratio to conduct etching with the second O2/SF6 ratio set to 70% (Steps S11 to S14). Only two types of gas, O2 and SF6, are used as etching gas in this embodiment.
To give a specific example, the gas flow rate at the first O2/SF6 ratio that is 100% is O2:SF6=1:1, and the gas flow rate at the second O2/SF6 ratio that is 75% is O2:SF6=3:4. The first O2/SF6 ratio and the second O2/SF6 ratio are also set so that the sum of the gas flow rates is the same. Through setting of the same gas flow rate sum for the first O2/SF6 ratio and for the second O2/SF6 ratio in this manner, the pressure in the reaction container 1 can be kept constant, which prevents the flapping of the auto-pressure controller (APC) or other pressure governors and leads to stable etching.
At the first O2/SF6 ratio, etching that is high in oxygen concentration and in anisotropy can be expected. At the second O2/SF6 ratio, the oxygen concentration is lower than at the first O2/SF6 ratio, and etching that has a high etching rate in the depth direction of the trench and that is small in residue is accordingly accomplished. Conducting etching at the first O2/SF6 ratio and then conducting etching at the second O2/SF6 ratio in this manner yields a trench that is shaped so as to have vertical, flat, and smooth side wall surfaces and a rounded bottom surface, and that is free of residue.
To give a detailed description, the etching is conducted by the following procedure.
First, the sample stage temperature in the reaction container 1 is brought to a desired predetermined temperature that is around room temperature (Step S0). Next, the semiconductor substrate 2 is carried into the reaction container 1 and put on the sample stage 3 of which the temperature has been controlled (Step S1). The reaction container 1 is next exhausted by the vacuum pump device to create a vacuum space (Step S2). The etching gas which is a mixture of SF6 and O2 is then introduced to the interior of the reaction container 1 at the first O2/SF6 ratio (Step S3). While the interior of the reaction container 1 is kept at a given pressure, for example, 2.5 Pa, the microwave power source 6 and the electromagnet 9 are activated to generate plasma (Step S4).
A high frequency voltage is further applied to the sample stage 3 from the high frequency power source 11 (Step S5). Ions that have the plasma of the etching gas as an ion source are thus accelerated by a high frequency electric field, to enter the semiconductor substrate 2 at a high speed. The semiconductor substrate 2 is etched by plasm etching as a result (Step S6). After a given length of time elapses, the application of the high frequency voltage is stopped (Step S7).
Next, the etching gas which is a mixture of SF6 and O2 is introduced to the interior of the reaction container 1 at the second O2/SF6 ratio (Step S11). While the interior of the reaction container 1 is kept at a given pressure, for example, 2.5 Pa, the microwave power source 6 and the electromagnet 9 are activated to generate plasma (Step S12). A high frequency voltage is further applied to the sample stage 3 from the high frequency power source 11 (Step S13). Ions that have the plasma of the etching gas as an ion source are thus accelerated by a high frequency electric field, to enter the semiconductor substrate 2 at a high speed. A trench is formed in the semiconductor substrate 2 as a result (Step S14).
After a given length of time elapses, the application of the high frequency voltage, the microwave introduction, and the magnetic field application are stopped to end the etching processing (Step S15). The semiconductor substrate 2 is then carried out of the reaction container 1 (Step S8).
The rounded bottom surface formed after the etching at the second O2/SF6 ratio has a relatively large curvature than in the etching at the first O2/SF6 ratio. The trench depth 31 in the etching at the first O2/SF6 ratio is desirably from 80% to 99% of the final trench depth 32, while the remaining 20% to 1% of the trench depth 32 is etched in the etching at the second O2/SF6 ratio. More desirably, the trench depth 31 in the etching at the first O2/SF6 ratio is from 90% to 99% of the final trench depth 32, while the remaining 10% to 1% of the trench depth 32 is etched in the etching at the second O2/SF6 ratio.
Etching at the first O2/SF6 ratio and etching at the second O2/SF6 ratio are used in the example described above. However, a third O2/SF6 ratio, a fourth O2/SF6 ratio, and more may be set. The O2/SF6 ratio in this case is set smaller in a step that follows than in a preceding step. The sum of gas flow rates is desirably constant, but different flow rate sums may be used.
First O2/SF6 ratio>second O2/SF6 ratio>third O2/SF6 ratio>fourth O2/SF6 ratio> . . . >Final O2/SF6 ratio
Trench etching in the second embodiment uses etching gas at the first O2/SF6 ratio and the second O2/SF6 ratio that are arbitrary ratios within a range of from 70% to 100%. The third embodiment is an etching method in which the gas ratio is changed during etching from the first O2/SF6 ratio to the second O2/SF6 ratio continuously in a single step, instead of in stages.
First, the sample stage temperature in the reaction container 1 is brought to a desired predetermined temperature that is around room temperature (Step S0). Next, the semiconductor substrate 2 is carried into the reaction container 1 and put on the sample stage 3 of which the temperature has been controlled (Step S1). The reaction container 1 is next exhausted by the vacuum pump device to create a vacuum space (Step S2). The etching gas which is a mixture of SF6 and O2 is then introduced to the interior of the reaction container 1 at the first O2/SF6 ratio (Step S3). While the interior of the reaction container 1 is kept at a given pressure, for example, 2.5 Pa, the microwave power source 6 and the electromagnet 9 are activated to generate plasma (Step S4).
A high frequency voltage is further applied to the sample stage 3 from the high frequency power source 11 (Step S5). Ions that have the plasma of the etching gas as an ion source are thus accelerated by a high frequency electric field, to enter the semiconductor substrate 2 at a high speed. As a result, the etching of the semiconductor substrate 2 by plasm etching is started (Step S6).
The etching processing is conducted while changing the etching gas mixing ratio to the second O2/SF6 ratio in a single step instead of in stages, without fixing the etching gas mixing ratio to any particular ratio (Step S21) to form a trench in the semiconductor substrate 2 (Step S6). After a given length of time elapses, the application of the high frequency voltage, the microwave introduction, and the magnetic field application are stopped to end the etching processing (Step S7). The semiconductor substrate 2 is then carried out of the reaction container 1 (Step S8).
According to the third embodiment, the stopping and starting of high frequency voltage application that accompanies the switch of the etching gas ratio is conducted less frequently than in the second embodiment. This shortens the etching time and also helps to form a trench stably.
Etching gas in the first to third embodiments of the present invention is not limited to the SF6+O2 gas described above and, as long as the main component of etching gas is the SF6+O2 gas, Cl2 (chlorine) can be added in order to use an SF6+O2+Cl2 gas, or HBr can be added in order to use an SF6+O2+HBr gas, or SiF4 can be added in order to use an SF6+O2+SiF4 gas, or NF3 can be added in order to use an SF6+O2+NF3 gas, or one or more rare gases out of He, Ne, Ar, Kr, and Xe may be mixed with the SF6+O2 gas.
The set conditions of the embodiments can be used not only in processing under a single etching condition, but also when processing under a different etching condition is inserted before or after the processing under a single etching condition.
The description given above on the present invention uses a few embodiments having plasma etching procedures. However, the present invention is applicable irrespective of how plasma is generated, and the same effects can therefore be obtained when the present invention is carried out in, for example, a parallel plate RIE device, a helicon etching machine, or an inductively coupled etching machine.