Patent Application
20210066079
The present disclosure generally relates to methods and systems suitable for forming electronic devices. More particularly, the disclosure relates to methods and systems that can be used for selectively depositing a doped silicon germanium film on a surface of a substrate.
Because of their relatively high electron and/or hole mobility, high-mobility semiconductors, such as silicon germanium, may be desirable to use in the fabrication of electronic devices, such as semiconductor devices. Devices formed with high-mobility semiconductor materials may exhibit better performance, faster speeds, reduced power consumption, and have higher breakdown fields, compared to similar devices formed with lower-mobility semiconductor materials, such as silicon.
Monocrystalline silicon germanium (Si1-xGex) semiconductor materials may be deposited or grown using a variety of techniques. For example, gas-phase processes, including molecular beam epitaxy and chemical vapor deposition, may be used to epitaxially grow or deposit monocrystalline silicon germanium films on a substrate.
In some semiconductor device applications, the silicon germanium film may include one or more dopants to obtain a desired carrier concentration. For example, the silicon germanium film may include a p-type dopant, such as boron, to increase the carrier concentration of the material. While boron-doped silicon germanium films may work well in some applications, the contact resistance of the boron-doped silicon germanium films may be undesirably high, particularly for use as source/drain regions in field effect transistors (FET). Attempts to lower the contact resistance include the addition of another dopant and a high-temperature anneal process. Such techniques may be problematic because the use of the relatively high temperatures during the anneal process can lead to clustering of one or more of the dopants of the doped silicon germanium films.
In many applications, it may be desirable to selectively deposit the silicon germanium material on a first material relative to a second material. For example, it may be desirable to selectively deposit the silicon germanium material overlying semiconductor material relative to dielectric or insulating material. However, attempts to selectively deposit a p-type doped silicon germanium layer that has relatively low contact resistance have been challenging. Accordingly, improved methods and systems for selectively depositing layers of p-type doped silicon germanium with relatively low contact resistance are desired.
Any discussion, including discussion of problems and solutions, set forth in this section has been included in this disclosure solely for the purpose of providing a context for the present disclosure. Such discussion should not be taken as an admission that any or all of the information was known at the time the invention was made or otherwise constitutes prior art.
Various embodiments of the present disclosure relate to selective deposition methods, to structures and devices formed using such methods, and to apparatus for performing the methods and/or for forming the structure and/or devices. While the ways in which various embodiments of the present disclosure address drawbacks of prior methods and systems are discussed in more detail below, in general, various embodiments of the disclosure provide improved methods of selectively depositing a p-type doped silicon germanium layer. The p-type doped silicon germanium layer can exhibit relatively low contact resistance. Additionally or alternatively, the p-type doped silicon germanium layer can be formed at relatively low temperatures—e.g., 350° C. to 600° C., without the use of a step of annealing the p-type doped silicon germanium layer to improve the contact resistance of the p-type doped silicon germanium layer.
In accordance with exemplary embodiments of the disclosure, a selective deposition method is disclosed. The selective deposition method includes providing a substrate within a reaction chamber, depositing a p-type doped silicon germanium layer overlying a surface of the substrate, and depositing a cap layer overlying the p-type doped silicon germanium layer. The surface of the substrate can include a first area comprising a first material and a second area comprising a second material. The p-type doped silicon germanium layer can include gallium. The incorporation of gallium in the p-type doped silicon germanium layer can reduce contact resistance of the p-type doped silicon germanium layer comprising gallium. As discussed in more detail below, use of the cap layer facilitates selective deposition of the p-type doped silicon germanium layer comprising gallium over the first material relative to the deposition of the p-type doped silicon germanium layer comprising gallium over the second material. Exemplary methods further include a step of etching the cap layer and the p-type doped silicon germanium layer overlying the second material. The etching can be performed using a halide-containing gas, such as hydrogen chloride, chlorine or the like. The first material can include, for example, semiconductor material, such as silicon, silicon germanium, germanium tin, silicon germanium tin, germanium, or the like. The second material can include, for example, a dielectric material, such as an oxide, a nitride, an oxynitride and/or the like, such as silicon nitride, silicon oxide (SiO2), silicon carbide and mixtures thereof, such as SiOC, SiOCN, SiON. As set forth in more detail below, various steps of exemplary methods described herein can be performed in the same reaction chamber or in different reaction chambers of the same cluster tool.
In accordance with further exemplary embodiments of the disclosure, a structure is formed using a method as described herein. The structure can include a substrate and a p-type doped silicon germanium layer. The p-type doped silicon germanium layer can include about 1×1017 at/cm3 to about 5×1021 at/cm3, or about 1×1017 at/cm3 to about 3×1021 at/cm3, or about 1×1018 at/cm3 to about 2×1021 at/cm3, or about 8×1018 at/cm3 to about 1×1021 at/cm3, or greater than 1×1019 at/cm3 boron. Additionally or alternatively, the p-type doped silicon germanium layer can include about 1×1017 at/cm3 to about 5×1021 at/cm3, or 1×1017 at/cm3 to about 3×1021 at/cm3, or about 1×1017 at/cm3 to about 1×1021 at/cm3, or about 1×1018 at/cm3 to about 8×1020 at/cm3, or about 1×1019 at/cm3 to about 1×1020 at/cm3gallium. Additionally or alternatively, the p-type doped silicon germanium layer can include about 30% to about 90%, or about 35% to about 70%, or about 40% to about 50% silicon and/or about 10% to about 70%, or about 65% to about 30%, or about 60% to about 50% germanium. A thickness of the p-type doped silicon germanium layer can be between about 1 nm and about 20 nm, between about 5 nm and 15 nm, or between about 7 nm and 10 nm. The structure can also include a cap layer. The cap layer can comprise silicon, such as p-type (e.g., boron) doped silicon. A concentration of the dopant in the silicon can be between 0 and about 1×1021 at/cm3, between about 8×1018 at/cm3 and about 5×1020 at/cm3, or between about 1×1019 at/cm3 and about 9×1019 at/cm3. A thickness of the cap layer can be between about 1 nm and about 10 nm, between about 2 nm and about 8 nm, or between about 4 nm and about 6 nm.
In accordance with yet additional embodiments of the disclosure, a device or portion thereof can be formed using a method as described herein. The device can include a substrate, a p-type doped silicon germanium layer, and a conducting layer overlying the p-type doped silicon germanium layer. The p-type doped silicon germanium layer can be used to form a source or drain region of the device, such as a field effect transistor (FET) (e.g., a FinFET).
In accordance with yet additional examples of the disclosure, a system to perform a method as described herein and/or to form a structure, device, or portion of either, is disclosed.
These and other embodiments will become readily apparent to those skilled in the art from the following detailed description of certain embodiments having reference to the attached figures. The invention is not being limited to any particular embodiments disclosed.
A more complete understanding of the embodiments of the present disclosure may be derived by referring to the detailed description and claims when considered in connection with the following illustrative figures.
It will be appreciated that elements in the figures are illustrated for simplicity and clarity and have not necessarily been drawn to scale. For example, the dimensions of some of the elements in the figures may be exaggerated relative to other elements to help improve understanding of illustrated embodiments of the present disclosure.
The description of exemplary embodiments of methods, structures, devices and systems provided below is merely exemplary and is intended for purposes of illustration only; the following description is not intended to limit the scope of the disclosure or the claims. Moreover, recitation of multiple embodiments having stated features is not intended to exclude other embodiments having additional features or other embodiments incorporating different combinations of the stated features.
As set forth in more detail below, various embodiments of the disclosure provide methods for selectively depositing a p-type doped silicon germanium layer including gallium. Exemplary methods can be used to, for example, form source or drain regions of semiconductor devices that exhibit relatively low contact resistance and that maintain the structure and composition of the p-type doped silicon germanium layer including gallium.
Typical solutions to deposit p-type doped silicon germanium layers with relatively low contact resistance include growing silicon germanium layers with relatively high concentrations of boron (e.g., higher than 1×1020 at/cm3). However, high concentrations of boron in the silicon germanium films can be difficult to achieve, particularly for silicon germanium films having a relatively high (e.g., greater than 40%) germanium concentration. This is thought to be due to the low solubility of boron in germanium. Therefore, increasing the boron concentration in the silicon germanium layers alone may not be suitable to obtain the desired contact resistance.
To further decrease the contact resistance of the silicon germanium layers, gallium can be added to the p-type doped silicon germanium layers. Gallium has a higher solubility in germanium than does boron. Moreover, the heavier atomic mass of gallium, compared to boron, may be advantageous in the formation of shallow junctions by reducing the channeling effects, compared to films with only boron doping. And, materials at an interface of a film (e.g., between the p-type doped silicon germanium layer comprising gallium and an overlying conducting layer) can greatly affect the contact resistance of the film. Gallium is thought to reduce contact resistance in p-type doped silicon germanium layers that include gallium by reducing a barrier height with higher gallium concentration near the interface.
However, selective deposition of p-type doped silicon germanium layers including gallium has been challenging. Gallium tends to segregate to a surface of the p-type doped silicon germanium layers, and typical etchants used in selective deposition processes can react with the gallium at or near the surface to produce gallium byproducts, thereby reducing the gallium concentration in the p-type doped silicon germanium layers, particularly at or near the surface of the layers. The reduced gallium concentration generally leads to p-type doped silicon germanium layers having higher contact resistance.
Exemplary methods described herein use a cap layer during a selective deposition method to reduce an amount of gallium that would otherwise be lost from the p-type doped silicon germanium layer including gallium. The cap layer can act as a sacrificial layer that is removed during an etch step. Use of the cap layer can mitigate gallium segregation, and maintain desired gallium concentrations in the p-type doped silicon germanium layers, since the gallium solubility is higher in germanium (about 5×1020 cm−3) than in silicon (about 1×1019 cm−3). Thus, the p-type doped silicon germanium layer including gallium can remain substantially intact and maintain its original properties and characteristics.
In this disclosure, “gas” can include material that is a gas at normal temperature and pressure (NTP), a vaporized solid and/or a vaporized liquid, and can be constituted by a single gas or a mixture of gases, depending on the context. A gas other than the process gas, i.e., a gas introduced without passing through a gas distribution assembly, a multi-port injection system, other gas distribution device, or the like, can be used for, e.g., sealing the reaction space, and can include a seal gas, such as a rare gas. In some cases, the term “precursor” can refer to a compound that participates in the chemical reaction that produces another compound, and particularly to a compound that constitutes a film matrix or a main skeleton of a film; the term “reactant” can be used interchangeably with the term precursor. The term “inert gas” can refer to a gas that does not take part in a chemical reaction and/or does not become a part of a film matrix to an appreciable extent. Exemplary inert gases include He, Ar, N2, and any combination thereof.
As used herein, the term “substrate” can refer to any underlying material or materials that can be used to form, or upon which, a device, a circuit, or a film can be formed. A substrate can include a bulk material, such as silicon (e.g., single-crystal silicon), other Group IV materials, such as germanium, or compound semiconductor materials, such as a Group II-VI or Group III-V semiconductor, and can include one or more layers overlying or underlying the bulk material. Further, the substrate can include various features, such as recesses, protrusions, and the like formed within or on at least a portion of a layer of the substrate. As set forth in more detail below, a surface of a substrate can include two of more areas, wherein each of the two or more areas comprise different material.
As used herein, the term “epitaxial layer” can refer to a substantially single crystalline layer upon an underlying substantially single crystalline substrate or layer.
As used herein, the term “chemical vapor deposition” can refer to any process wherein a substrate is exposed to one or more volatile precursors, which react and/or decompose on a substrate surface to produce a desired deposition.
As used herein, the term “silicon germanium” can refer to a semiconductor material comprising silicon and/or germanium and can be represented as Si1-xGex wherein 1≥x≥0, or 0.2≥x≥0.8, or 0.4≥x≥0.6.
As used herein, the term “film” and/or “layer” can refer to any continuous or non-continuous structures and material, such as material deposited by the methods disclosed herein. For example, film and/or layer can include two-dimensional materials, three-dimensional materials, nanoparticles or even partial or full molecular layers or partial or full atomic layers or clusters of atoms and/or molecules. A film or layer may comprise material or a layer with pinholes, which may be at least partially continuous.
As used herein, a “structure” can include a substrate as described herein. Structures can include one or more layers overlying the substrate, such as one or more layers formed according to a method as described herein.
Further, in this disclosure, any two numbers of a variable can constitute a workable range of the variable, and any ranges indicated may include or exclude the endpoints. Additionally, any values of variables indicated (regardless of whether they are indicated with “about” or not) may refer to precise values or approximate values and include equivalents, and may refer to average, median, representative, majority, or the like. Further, in this disclosure, the terms “including,” “constituted by” and “having” refer independently to “typically or broadly comprising,” “comprising,” “consisting essentially of,” or “consisting of” in some embodiments. In this disclosure, any defined meanings do not necessarily exclude ordinary and customary meanings in some embodiments.
Turning now to the figures,
Method 100 includes the steps of providing a substrate within a reaction chamber (step 102), depositing a p-type doped silicon germanium layer (step 104), depositing a cap layer (step 106), etching (step 108), optionally repeating steps 104-108 (loop 110), and ending (step 112).
With reference to
As a non-limiting example, the reaction chamber may comprise a reaction chamber of a chemical vapor deposition system. However, it is also contemplated that other reaction chambers and alternative chemical vapor deposition systems may also be utilized to perform the embodiments of the present disclosure. The reaction chamber can be a stand-alone reaction chamber or part of a cluster tool.
Step 102 can include heating the substrate to a desired deposition temperature within the reaction chamber. In some embodiments of the disclosure, step 102 includes heating the substrate to a temperature of less than approximately 700° C., or to a temperature of less than approximately 650° C., or to a temperature of less than approximately 600° C., or to a temperature of less than approximately 550° C., or to a temperature of less than approximately 500° C., or to a temperature of less than approximately 450° C., or even to a temperature of less than approximately 400° C. For example, in some embodiments of the disclosure, heating the substrate to a deposition temperature may comprise heating the substrate to a temperature between approximately 400° C. and approximately 700° C.
In addition to controlling the temperature of the substrate, a pressure within the reaction chamber may also be regulated. For example, in some embodiments of the disclosure, the pressure within the reaction chamber during step 102 may be less than 200 Torr, or less than 100 Torr, or less than 50 Torr, or less than 25 Torr, or even less than 10 Torr. In some embodiments, the pressure in the reaction chamber may be between 10 Torr and 100 Torr.
During step 104, a layer of p-type doped silicon germanium including gallium is deposited on a layer overlying the surface of the substrate. The layer of p-type doped silicon germanium may form as a (e.g., mono) crystalline material overlying the first area/surface (e.g., area 206/surface 210) and as a polycrystalline or amorphous material over the second, non-monocrystalline area/surface (e.g., area 208/surface 212). A nucleation delay of the deposited layer of p-type doped silicon germanium may be greater on the second/non-monocrystalline surface 212 relative to the first surface 210.
During step 104, a silicon precursor, a germanium precursor, a p-type dopant (e.g., boron), and a gallium precursor are flowed into the reaction chamber—e.g., through one or more gas injectors, such as multi-port injectors (MPIs) including a plurality of individual port injectors for providing a gas mixture into the reaction chamber. Various combinations of the precursors can be supplied to one or more of the individual port injectors to fine tune concentration profiles as desired. To mitigate reaction with the gallium in the film as the film deposits, the silicon precursor, germanium precursor, p-type dopant, and/or gallium precursor (e.g., all the precursors) may desirably be halide (e.g., chlorine) free. In other words, a chemical formula of a precursor, or component thereof, may not include Cl.
The gallium dopant precursor can comprise, for example, at least one of trimethylgallium (TMG) or triethylgallium (TEG), tritertiarybutylgallium (TTBGa), galliumtrichlorine (GaCl3), Ga(BH4)3, RGaCl2, GaR3, GaHx, wherein R can be, for example, an ethyl, butyl, or propyl, group.
The silicon precursor may comprise one or more hydrogenated silicon precursors selected from the group comprising: silane (SiH4), disilane (Si2H6), trisilane (Si3H8), or tetrasilane (Si4H10). The germanium precursor may comprise at least one of germane (GeH4), digermane (Ge2H6), trigermane (Ge3H8), or germylsilane (GeH6Si). The p-type (e.g., boron) dopant precursor can include, for example, at least one of diborane (B2H6) or deuterium-diborane (B2D6), or one or more borohydrides. Exemplary borohydrides include gallium borohydride (Ga(BH4)3), aluminum borohydride (Al(BH4)3), and indium borohydride (In(BH4)3). In alternative embodiments of the disclosure, the p-type dopant precursor may comprise a borohydride having the formula YxM(BH4)3-x, wherein Y is independently chosen from hydrogen, deuterium, chlorine, bromine, and iodine; M is a Group IIIA metal independently chosen from gallium, aluminum, and indium; and x is an integer from 0-2. In some embodiments of the disclosure, the p-type dopant precursor, e.g., the boron dopant precursor, may be replaced by an alternative p-type dopant precursor. For example, the p-type dopant precursor may comprise an aluminum (Al) containing dopant precursor, such as, for example, a borohydride (e.g., Al(BH4)3).
In some embodiments, the silicon precursor can be provided into the reaction chamber at a flow rate of less than 500 sccm, or less than 250 sccm, or even less than 50 sccm. For example, the silicon precursor may flow into the reaction chamber at a silicon precursor flow rate between approximately 1 sccm and approximately 500 sccm.
In some embodiments, the germanium precursor is provided into the reaction chamber at a flow rate of less than 1000 sccm, or less than 300 sccm, or even less than 10 sccm. For example, the germanium precursor may flow into the reaction chamber at a germanium precursor flow rate between approximately 1 sccm and approximately 1000 sccm. In some embodiments, the germanium precursor may be provided in diluted form and the diluted form may comprise approximately 5% germanium precursor, such as, GeH4, for example, in a carrier gas.
In some embodiments, the p-type (e.g., boron) dopant precursor is provided into the reaction chamber at a flow rate of less than 500 sccm, or less than 250 sccm, or even less than 50 sccm. For example, the boron dopant precursor may flow into the reaction chamber at a boron dopant precursor flow rate between approximately 1 sccm and approximately 500 sccm. In some embodiments, the boron dopant precursor may be provided in diluted form and the diluted form may comprise approximately 1% p-type dopant precursor, such as diborane, for example, in a carrier gas.
In some embodiments, the gallium precursor is provided into the reaction chamber at a flow rate of less than 500 sccm, or less than 250 sccm, or even less than 50 sccm. For example, the gallium precursor may flow into the reaction chamber at a flow rate between approximately 1 sccm and approximately 500 sccm. In some embodiments, the gallium precursor may be provided in diluted form and the diluted form may comprise approximately 1% gallium precursor, such as, triethylgallium, for example, in a carrier gas.
A thickness of the p-type doped silicon germanium layer formed during step 104 in area 206 and/or area 208 can be between about 1 nm and about 20 nm, between about 5 nm and about 15 nm, or between about 7 nm and about 10 nm. A concentration of p-type dopant (e.g., boron) in the p-type doped silicon germanium layer in area 206 and/or area 208 can range from about 1×1017 at/cm3 to about 5×1021 at/cm3, or from about 1×1017 at/cm3 to about 3×1021 at/cm3, or about 1×1018 at/cm3 to about 2×1021 at/cm3, or about 8×1018 at/cm3 to about 1×1021 at/cm3 or greater than 1×1019 at/cm3 boron. The p-type doped silicon germanium layer in area 206 and/or area 208 can include about 1×1017 at/cm3 to about 5×1021 at/cm3, or about 1×1017 at/cm3 to about 3×1021 at/cm3, or about 1×1017 at/cm3 to about 1×1021 at/cm3, or about 1×1018 at/cm3 to about 8×1020 at/cm3, or about 1×1019 at/cm3 to about 1×1020 at/cm3 gallium. Additionally or alternatively, the p-type doped silicon germanium layer in area 206 and/or area 208 can include about 30% to about 90%, or about 35% to about 70%, or about 40% to about 50% silicon and/or about 10% to about 70%, or about 65% to about 30%, or about 60% to about 50% germanium. In some embodiments, the germanium (and/or other component) content within the p-type doped silicon germanium layer in area 206 and/or area 208 may not be constant, but rather may be varied, such that the germanium content (and/or other component) may have a graded composition within the p-type doped silicon germanium layer.
During step 106, a cap layer is formed overlying the p-type doped silicon germanium layer. The cap layer can comprise or consist essentially of silicon. In some cases, the cap layer can include doped silicon, such as a p-type (e.g., boron and/or gallium) doped silicon. A concentration of the p-type dopant in the silicon layer can be up to 5×1×1021 at/cm3, or up to 3×1021 at/cm3, e.g., it can range from 0 and about 1×1021 at/cm3, between about 8×1018 at/cm3 and about 5×1020 at/cm3, or between about 1×1019 at/cm3 and about 9×1019 at/cm3.
In some embodiments, the cap layer comprises or essentially consists of a silicon germanium alloy. In other words, in some embodiments, the silicon germanium is For example, the cap layer may comprise 10 mol % silicon, or 20 mol % silicon, or 30 mol % silicon, or 40 mol % silicon, or 50 mol % silicon, or 60 mol % silicon, or 70 mol % silicon, or 80 mol % silicon, or 90 mol % silicon. For example, the cap layer may comprise 10 mol % germanium, or 20 mol % germanium, or 30 mol % germanium, or 40 mol % germanium, or 50 mol % germanium, or 60 mol % germanium, or 70 mol % germanium, or 80 mol % germanium, or 90 mol % germanium. In some embodiments, the silicon germanium-containing cap layer is doped with a p-type dopant, e.g., boron and/or gallium. A concentration of the p-type dopant in the silicon germanium cap layer can range from 0 and about 1×1021 at/cm3, between about 8×1018 at/cm3 and about 5×1020 at/cm3, or between about 1×1019 at/cm3 and about 9×1019 at/cm3.
In some embodiments, the cap layer is grown by means of precursors that do not contain a halogen. In some embodiments, the cap layer is grown by means of precursors that do not contain chlorine. The cap layer may be grown, for example, using one or more of the following precursors. As a silicon precursor, silane or disilane may be used. As a germanium precursor, germane or digermane may be used. As a boron precursor, diborane may be used. As a gallium precursor, triethylgallium may be used.
A thickness of cap layer 406 over area 206 and/or 208 formed during step 106 can be between about 1 nm and about 10 nm, between about 2 nm and about 8 nm, or between about 4 nm and about 6 nm. A concentration of p-type dopant (e.g., boron) in the p-type doped silicon germanium layer over area 206 and/or 208 can range from about 1×1017 at/cm3 to about 5×1021 at/cm3, or from about 1×1017 at/cm3 to about 3×1021 at/cm3, or about 1×1018 at/cm3 to about 2×1021 at/cm3, or about 8×1018 at/cm3 to about 1×1021 at/cm3 or greater than 1×1019 at/cm3 boron. Including a dopant, such as boron, in the cap layer may be desirable to increase an etch rate of cap layer 406 (portion 402 and/or portion 404) during step 108.
Returning to
The cap layer can be formed by flowing silicon and optionally a dopant precursor to a reaction chamber. The silicon precursor and the dopant precursor (e.g., p-type dopant precursor) can be the same or similar to those described above. Further, the flowrates of the precursors, the reaction chamber pressures, and/or the temperatures can be the same or similar to those described above in connection with step 104.
SIMS analysis of structures including a cap layer overlying a p-type doped silicon germanium layer including gallium showed no gallium segregation towards the cap layer.
During step 108, an etch is performed to at least partially remove the cap layer over the first area and remove the cap layer over the second area. Additionally, the p-type doped silicon germanium layer overlying the second area/material is removed, to thereby form a selectively deposited p-type doped silicon germanium layer overlying the first material/area relative to the second material/area.
A selective deposition process can involve a greater amount of material remaining on a first surface relative to a second surface. For example, the selective process may result in a greater amount of the p-type doped silicon germanium layer remaining in the first area formed over monocrystalline material relative to any p-type doped silicon germanium layer remaining in the second area over non-monocrystalline material. In some embodiments of the disclosure, the selectivity of the deposition process can be expressed as the ratio of material formed on the first surface (or in the first area) relative to the amount of material formed on the first and second surfaces (or areas) combined. For example, if 10 nm of p-type doped silicon germanium layer remains in the first area and 1 nm of the p-type doped silicon germanium layer remains in the second area, the selective deposition process will be considered to have 91% selectivity. In some embodiments, the selectivity of the methods disclosed herein may be above about 80%, above about 90%, above about 95%, 99.5%, 98%, 99%, or even about 100%. Additionally or alternatively, a ratio of the p-type doped silicon germanium layer remaining in the first area relative to p-type doped silicon germanium layer remaining in the second area can be greater than, for example, 10, 5, or 2.
The cap layer and/or the p-type doped silicon germanium layer over the second area may have a higher etch rate—e.g., due to the amorphous or polycrystalline structure, than the respective layers over the first area—which can include monocrystalline materials. Thus, the non-crystalline material can be easily removed, while maintaining portion 302 substantially intact. In some cases, a small portion of cap layer 406 can remain over portion 302 after one or more etch steps 108.
Step 108 can be performed in the same reaction chamber used during step 104 and/or step 106. Alternatively, step 108 can be performed in another reaction chamber, such as another reaction chamber of the same cluster tool.
In some embodiments, a halide gas is used as an etchant during step 108. The halide gas can include, for example, one or more of hydrogen chloride, chlorine, or the like. During step 108, the halide gas can be flowed into the reaction chamber at a flow rate of less than 500 sccm, or less than 250 sccm, or even less than 100 sccm. For example, the halide gas may flow into the reaction chamber at a halide gas flow rate between approximately 1 sccm and approximately 500 sccm.
As illustrated, steps 104-108 can be repeated (loop 110) as desired until a desired thickness of the p-type doped silicon germanium is formed overlying the first area/material on the substrate. For example, steps 104-108 can be repeated about 1 to about 500 times, about 2 to about 100 times, about 2 to about 50 times, about 2 to about 30 times, or about 2 to about 20 times. Further, one or more (e.g., each) of steps 104-108 can be repeated one or more times prior to proceeding to the next step. Once a desired layer thickness of the p-type doped silicon germanium layer is obtained, method 100 can end (step 112).
Methods described herein can enlarge a selectivity window of p-type doped silicon germanium layer deposition that might otherwise arise, for example, where the deposition has a longer nucleation delay on surface 212, compared to surface 210. A thickness of the cap layer 406 can thus be less in cases where the nucleation delay is greater for p-type doped silicon germanium layer deposition over surface 212, compared to surface 210.
Substrate 602 can be or include any of the substrate material described herein. For example, substrate 602 can be the same as substrate 202 and/or structure 200.
P-type doped silicon germanium layer 604 can be the same or similar to first portion 302 of the p-type doped silicon germanium layer described above. P-type doped silicon germanium layer 604 can be used to form or be a source or drain region of a field effect transistor (FET), such as a source or drain region of a FinFET or other FET device.
Conducting layer 606 can include, for example, metal, such as titanium, nickel, cobalt, nickel platinum alloy, or the like. A contact resistance of p-type doped silicon germanium layer 604 can be lower than 10−9 Ω·cm2 to about 5×10−19 Ω·cm2, about 5×10−10 Ω·cm2 to about 2×10−19 Ω·cm2, or about 2×10−19 Ω·cm2 to about 1×10−19 Ω·cm2 without annealing.
In the illustrated example, system 700 includes an optional substrate handling system 702, one or more reaction chambers 704, a gas injection system 706, and optionally a wall 708 disposed between reaction chamber(s) 704 and substrate handling system 702. System 700 can also include a first gas source 710, a second gas source 712, a third gas source 714, a fourth gas source 716, an exhaust source 726, and a controller 728.
Although illustrated with four gas sources 710-716, system 700 can include any suitable number of gas sources. Gas sources 710-716 can each include, for example, a precursor gas, such as a precursor (e.g., silicon precursor, germanium precursor, p-type dopant precursor, and/or gallium precursor) as described above, including mixtures of such precursors and/or mixtures of one or more precursors with a carrier gas, such as hydrogen, nitrogen, argon, helium or the like. Additionally or alternatively, one of gas sources 710-716 or another gas source can include an etchant, such as a halide—e.g., a chlorine-containing gas, such as hydrogen chloride and/or chlorine. Gas sources 710-716 can be coupled to reaction chamber 704 via lines 718-724, which can each include flow controllers, valves, heaters, and the like.
System 700 can include any suitable number of reaction chambers 704 and substrate handling systems 702. Further, one or more reaction chambers 704 can be or include a cross-flow, cold wall epitaxial reaction chamber.
Vacuum source 720 can include one or more vacuum pumps.
Controller 728 can be configured to perform various functions and/or steps as described herein. Controller 728 can include one or more microprocessors, memory elements, and/or switching elements to perform the various functions. Although illustrated as a single unit, controller 728 can alternatively comprise multiple devices. By way of examples, controller 728 can be used to control gas flow (e.g., by monitoring flow rates of precursors and/or other gases from sources 710-716 and/or controlling valves, motors, heaters, and the like). Further, when system 700 includes two or more reaction chambers, the two or more reaction chambers can be coupled to the same/shared controller.
During operation of reactor system 700, substrates, such as semiconductor wafers (not illustrated), are transferred from, e.g., substrate handling system 702, to reaction chamber 704. Once substrate(s) are transferred to reaction chamber 704, one or more gases from gas sources 710-716, such as precursors, dopants, carrier gases, and/or purge gases, are introduced into reaction chamber 704 via gas injection system 706. Gas injection system 706 can be used to meter and control gas flow of one or more gases (e.g., from one or more gas sources 710-716) during substrate processing and to provide desired flows of such gas(es) to multiple sites within reaction chamber 704.
Without the present invention being bound to a particular theory or mode of operation, it is believed that gallium segregates at the surface of boron- and gallium-doped silicon germanium layers. Also, it is believed that the capping layer effectively prevents or at least reduces gallium segregation at an exposed surface. When a thusly capped surface is then exposed to a chemical that preferentially etches gallium, the capping layer may prevent, or at least reduce, gallium removal from the SiGe:B:Ga layer. Exemplary chemicals which can preferentially remove gallium, and that the capping layer protects against, include aqueous HF and halogen-containing gasses such as HCl. Thus, a high surface concentration of p-type dopants such as Ga and B can be maintained. When a contact is then formed on the SiGe:B:Ga layer, a low contact resistance can be obtained. Note that even the presence of a few nanometers of cap layer on top of the SiGe:B:Ga layer does not have to be detrimental because of silicide formation on the one hand, and because the SIMS profiles show that any drop in boron concentration near the surface may be compensated for by an increase in gallium concentration near the surface. Thus, the present methods allow the formation of contacts having a very low contact resistance on p-type silicon germanium.
The example embodiments of the disclosure described above do not limit the scope of the invention, since these embodiments are merely examples of the embodiments of the invention, which is defined by the appended claims and their legal equivalents. Any equivalent embodiments are intended to be within the scope of this invention. Indeed, various modifications of the disclosure, in addition to those shown and described herein, such as alternative useful combinations of the elements described, may become apparent to those skilled in the art from the description. Such modifications and embodiments are also intended to fall within the scope of the appended claims.
This application claims priority to U.S. Provisional Patent Application Ser. No. 62/895,819 filed Sep. 4, 2019 titled METHODS FOR SELECTIVE DEPOSITION USING A SACRIFICIAL CAPPING LAYER, the disclosures of which are hereby incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62895819 | Sep 2019 | US |