METHODS OF FORMING SINGLE CRYSTAL PIEZOELECTRIC LAYERS USING LOW TEMPERATURE EPITAXY AND RELATED SINGLE CRYSTALLINE PIEZOELECTRIC RESONATOR FILMS

Abstract

MOCVD systems can be used to form single crystal piezoelectric ScxAl1−xN layers having a concentration of Sc in a range between about 4% and about 18% at temperatures in a range, for example, between about 800 degrees Centigrade and about 950 degrees Centigrade. The single crystal piezoelectric ScxAl1−xN layers can have a crystalline structure characterized by an XRD ω-rocking curve FWHM value in a range between about less than 1.0 degrees to about 0.001 degrees as measured about the omega angle as of the ScxAl1−xN (0002) film reflection.

Description

BACKGROUND

The present invention relates generally to semiconductor devices. More particularly, the present invention provides methods of forming piezoelectric films for use in, for example, acoustic wave resonator devices and RF devices etc.

BRIEF DESCRIPTON OF THE DRAWINGS

FIG. 1A is a simplified diagram illustrating an acoustic resonator device having topside interconnections according to an example of the present invention.

FIG. 1B is a simplified diagram illustrating an acoustic resonator device having bottom-side interconnections according to an example of the present invention.

FIG. 1C is a simplified diagram illustrating an acoustic resonator device having interposer/cap-free structure interconnections according to an example of the present invention.

FIG. 1D is a simplified diagram illustrating an acoustic resonator device having interposer/cap-free structure interconnections with a shared backside trench according to an example of the present invention.

FIGS. 2 and 3 are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention.

FIG. 4A is a simplified diagram illustrating a step for a method creating a topside micro-trench according to an example of the present invention.

FIGS. 4B and 4C are simplified diagrams illustrating alternative methods for conducting the method step of forming a topside micro-trench as described in FIG. 4A.

FIGS. 4D and 4E are simplified diagrams illustrating an alternative method for conducting the method step of forming a topside micro-trench as described in FIG. 4A.

FIGS. 5 to 8 are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention.

FIG. 9A is a simplified diagram illustrating a method step for forming backside trenches according to an example of the present invention.

FIGS. 9B and 9C are simplified diagrams illustrating an alternative method for conducting the method step of forming backside trenches, as described in FIG. 9A, and simultaneously singulating a seed substrate according to an embodiment of the present invention.

FIG. 10 is a simplified diagram illustrating a method step forming backside metallization and electrical interconnections between top and bottom sides of a resonator according to an example of the present invention.

FIGS. 11A and 11B are simplified diagrams illustrating alternative steps for a method of manufacture for an acoustic resonator device according to an example of the present invention.

FIGS. 12A to 12E are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device using a blind via interposer according to an example of the present invention.

FIG. 13 is a simplified diagram illustrating a step for a method of manufacture for an acoustic resonator device according to an example of the present invention.

FIGS. 14A to 14G are simplified diagrams illustrating method steps for a cap wafer process for an acoustic resonator device according to an example of the present invention.

FIGS. 15A-15E are simplified diagrams illustrating method steps for making an acoustic resonator device with shared backside trench, which can be implemented in both interposer/cap and interposer free versions, according to examples of the present invention.

FIGS. 16A-16C through FIGS. 31A-31C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention.

FIGS. 32A-32C through FIGS. 46A-46C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a cavity bond transfer process for single crystal acoustic resonator devices according to an example of the present invention.

FIGS. 47A-47C though FIGS. 59A-59C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a solidly mounted transfer process for single crystal acoustic resonator devices according to an example of the present invention.

FIG. 60 is a schematic illustration of a piezoelectric Sc_xAl_1−xN layer formed using low-vapor pressure metalorganic precursors in CVD systems on a substrate in further embodiments according to the invention.

DETAILED DESCRIPTION OF EMBODIMENTS ACCORDING TO THE INVENTION

According to the present invention, techniques generally related to electronic devices are provided. More particularly, the present invention provides techniques related to a method of manufacture and structure for bulk acoustic wave resonator devices, single crystal resonator devices, single crystal filter and resonator devices, and the like. Merely by way of example, the invention has been applied to a single crystal resonator device for a communication device, mobile device, computing device, among others.

As appreciated by the present inventors, maintaining the growth temperature in the ranges described herein can avoid the segregation of the Sc which can result in the formation of undesired crystal structures such as compounds of Sc, such as rock-salt Sc_xAl_1−xN grains or the formation of metallic inclusions in the layer and thereby enable the formation of the single crystal piezoelectric Sc_xAl_1−xN layer. As further appreciated by the present inventors, the ratio of N to Sc in the precursors used for the growth of the single crystal piezoelectric Sc_xAl_1−xN layer may also be effective in promoting the single crystal piezoelectric Sc_xAl_1−xN layer.

In some embodiments according to the invention, MOCVD systems can be used to form single crystal piezoelectric Sc_xAl_1−xN layers having a concentration of Sc in a range between about 4% and about 18%. In some embodiments according to the invention, MOCVD systems can be used to form single crystal piezoelectric Sc_xAl_1−xN layers having a concentration of Sc in a range between about 4% and 41%. In particular, the single crystal piezoelectric Sc_xAl_1−xN layers can have a crystalline structure characterized by an XRD ω-rocking curve FWHM value in a range between about less than 1.0 degrees to about 0.001 degrees as measured about the omega angle as of the Sc_xAl_1−xN (0002) film reflection. In some embodiments according to the invention, the single crystal piezoelectric Sc_xAl_1−xN layer can have a thickness in a range between about 10 nm and about 2 um. In some embodiments according to the invention, the single crystal piezoelectric Sc_xAl_1−xN layer can be on a substrate of SiC, Al₂O₃, Si, or GaN. Other substrates can be used. The MOCVD system can be the system described in U.S. Provisional Patent Application Ser. No. 63/063,196, (Attorney Docket No. 181246-00037) entitled “Methods of Forming Single Crystal AlScN Piezoelectric Layers Using Low-Vapor Pressure Metalorganic Precursors in CVD Systems,” filed in the U.S.P.T.O. on Aug. 7, 2020, and as shown in FIGS. 1-8 therein. Accordingly, the piezoelectric films described herein, such as the piezoelectric layer 120, can be formed using the processes described in some embodiments according to the invention.

In further embodiments according to the invention, a low vapor pressure MO precursor, such as, tris(N,N′-di-i-propylformamidinato)scandium (i.e., (DIPA)₃Sc) can be heated to a temperature in a range between about 100 degrees Centigrade and about 250 degrees Centigrade and provided to the reaction chamber holding the substrate. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 150 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 175 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, (MeCp)₃Sc may be used as the Sc precursor. A Nitrogen precursor, such as NH₃ is also provided to the reaction chamber as described herein. It will be understood that the Sc source can be provided to form the single crystal piezoelectric Sc_xAl_1−xN layer to have a Sc content in a range between about 4% and about 18%.

In some embodiments according to the invention, the ratio of the N to Sc (and Al) maintained in the reactor during the growth of the single crystal piezoelectric Sc_xAl_1−xN layer can be controlled to increase the amount of N relative to the Sc to promote the pure formation of the single crystal piezoelectric Sc_xAl_1−xN layer and to reduce the formation of undesired crystal structures such as compounds of Sc other than Sc_xAl_1−xN. It will be understood that the temperature in the reaction chamber may also be controlled, either with or without changes to the N/Sc ratio described above) to promote the pure formation of the single crystal piezoelectric Sc_xAl_1−xN and to reduce the formation of undesired crystal structures such as compounds of Sc other than Sc_xAl_1−xN.

In some embodiments, a source vessel that holds the source of the low vapor pressure metalorganic (MO) precursors can be heated to a range between about 100 degrees Centigrade and about 250 degrees Centigrade and provided to the reaction chamber holding the substrate. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 150 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 175 degrees Centigrade and about 250 degrees Centigrade.

It will be understood that in some embodiments according to the present invention, the lines that deliver the low vapor pressure MO precursor vapor to the CVD reactor chamber can also be heated to the temperatures described above in reference to the low vapor pressure metalorganic (MO) precursors. In some embodiments, the CVD reactor is a horizontal flow reactor that can generate a laminar flow of the low vapor pressure MO precursor vapor over the wafers in the reactor. In some embodiments according to the invention, the horizontal flow reactor can include a planetary type apparatus that rotates during the deposition process and that rotates the wafer stations that hold each of the wafers. In some embodiments according to the invention, the low vapor pressure MO precursor can be any metal organic material having a vapor pressure of 4.0 Pa or less at room temperature. In some embodiments according to the invention, the low vapor pressure MO precursor can be any metal organic material having a vapor pressure of between about 4.0 Pa to about 0.004 Pa at room temperature.

In still further embodiments according to the invention, the heated line that conducts the low vapor pressure MO precursor vapor to the CVD reactor chamber is thermally isolated from the other MO precursors and hydrides. For example, in some embodiments, the heated line that conducts the low vapor pressure MO precursor vapor to the CVD reactor chamber is provided to the central injector column via a different route than that used to provide the other precursors, such as through a flexible heated line that is connected to a portion of the CVD reactor that moves. In particular, the other precursors may be provided to the central injector column through a lower portion of the CVD reactor that remains stationary when CVD reactor is opened by, for example, lifting the upper portion of the CVD reactor to open the CVD reactor chamber. Accordingly, when the CVD reactor chamber is in the open position, the upper and lower portions of the CVD reactor separate from one another to expose, for example, the planetary arrangements described herein.

As appreciated by the present inventors, providing the low vapor pressure MO precursor vapor to the central injector column by a different path than the other precursors, can allow the low vapor pressure MO precursor vapor to be heated to the relatively high temperature without adversely affecting (e.g., heating) the other precursors above room temperature, for example. Accordingly, while the other precursors may be provided via other precursor lines routed though the lower portion that are configured to mate/unmate when the CVD reactor is closed/opened, the heated low vapor pressure MO precursor line to the central injector column can remain a unitary flexible piece that allows the upper portion to move when opened/closed yet still be thermally isolated from the other precursors/precursor lines.

In some embodiments, the molar flow of the low vapor pressure MO precursor vapor is provided by a high temperature mass flow controller (MFC) that is downstream of the heated low vapor pressure MO precursor source vessel. In some embodiments according to the invention, an MFC is located upstream of the heated low vapor pressure MO precursor source vessel and a high temperature pressure controller is located downstream of the heated low vapor pressure MO precursor source vessel in-line with the line that conducts the low vapor pressure MO precursor vapor to the CVD reactor chamber. Accordingly, in embodiments where a device, such as the high temperature MFC or the high temperature pressure controller, is located in-line with the line that conducts the low vapor pressure MO precursor vapor to the CVD reactor chamber downstream of the heated low vapor pressure MO precursor source vessel, the respective device is configured to operate at relatively high temperatures, such as greater than 150 degrees Centigrade.

It will be understood that embodiments according to the invention can operate under the control of a processor circuit so that the heating and delivery of the low vapor MO precursor vapor is provided at the temperatures, pressures, amounts and other operational parameters needed to form single crystal piezoelectric layers as described herein. Although the operations described herein may refer to the operations being carried out by a processor circuit it will be understood that in some embodiments separate operations (or separate portions of the same operation) may be carried out, entirely or partially by a plurality of processor circuits and/or processing systems that are operatively coupled together to carry of the methods of forming that are described herein, as shown for example in FIGS. 7 and 8 of U.S. Provisional Patent Application Ser. No. 63/063,196, (Attorney Docket No. 181246-00037) entitled “Methods of Forming Single Crystal AlScN Piezoelectric Layers Using Low-Vapor Pressure Metalorganic Precursors in CVD Systems,” filed in the U.S.P.T.O. on Aug. 7, 2020.

In still further embodiments according to the invention, the MOCVD systems described herein can be utilized to form the single crystal piezoelectric Sc_xAl_1−xN layers described herein. For example, a substrate of SiC, Al₂O₃, Si, or GaN can be placed in the reactor 305. In some embodiments according to the present invention, the precursor provided to the reactor can be a precursor characterized by the general formula (1):

Sc(MeCp)_x(iPr—N—CH═N—iPr)_y  (1),

wherein x is 0, 1, or 2, y is 1, 2, or 3, with the proviso that x+y=3, and wherein there is one N atom for each outer shell electron of the Sc when x=0. Accordingly, in some embodiments according to the present invention, the precursor can be a Scandium-containing precursor with diisopropylformamidinate ligands, without methyl cyclopentadienyl ligands. Alternatively, in some embodiments according to the invention, the precursor can be a Scandium-containing precursor with diisopropylforamidinate ligands and with methyl cyclopentadienyl ligands. Lanthanide-containing precursors, for example, with diisopropylforamidinate ligands and with methyl cyclopentadienyl ligands, are described in U.S. Pat. No. 8,283,201, the entirety of which is hereby incorporated herein by reference. Another example, of a Scandium-containing precursor with diisopropylforamidinate ligands and with methyl cyclopentadienyl ligands is marketed by Air Liquide S.A. headquartered in Paris France under the tradename Scarlet™.

In further embodiments according to the present invention, the precursor can be characterized by the general formula (2):

Sc(R¹Cp)_x(R²—NC—C(R³)═N—R²)_y  (2)

wherein R¹ is H or a C₁-C₅ alkyl chain, R² is H or a C₁-C₅ alkyl chain, R³ is H or Me, x is 0, 1, or 2, y is 1, 2, or 3, with the proviso that x+y=3, and wherein there is one N atom for each outer shell electron of the Sc when x=0. In some embodiments, R¹ of the precursor is Me, Et, or iPr. In some embodiments, R² of the precursor is iPr or tBu. Accordingly, in some embodiments according to the present invention, the precursor can be a Scandium-containing precursor with dialkylformamidinate ligands or dialkylacetamidinate ligands, and alkyl cyclopentadienyl ligands, and/or a Scandium-containing precursor with dialkylformamidinate ligands or acetamidinate ligands, without alkyl cyclopentadienyl ligands. Lanthanide-containing precursors, for example, with dialkylforamidinate ligands and with alkyl cyclopentadienyl ligands, are described in U.S. Pat. No. 8,283,201, the entirety of which is hereby incorporated herein by reference.

In still other embodiments according to the invention, a Sc precursor, such as (DIPA)₃Sc, is placed in the vessel and heated to a temperature in a range between about 100 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 150 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, the low vapor pressure MO precursor can be heated to a temperature in a range between about 175 degrees Centigrade and about 250 degrees Centigrade. In some embodiments according to the invention, (MeCp)₃Sc may be used as the Sc precursor. A Nitrogen precursor, such as NH₃ is also provided to the reaction chamber as described herein.

The heated lines that conduct the Sc precursor to the reactor are also heated to the temperature ranges described above and provided to the reactor chamber that hold the substrate. The temperature in the reactor chamber is maintained at a growth temperature in a range between about 800 degrees Centigrade to about 950 degrees Centigrade.

It will be understood that the temperature in the reactor chamber may be maintained adjusting a heater in conjunction with monitoring the growth temperature using for example, pyrometry to measure the temperature of the substrate during the growth of the single crystal piezoelectric Sc_xAl_1−xN layer.

As appreciated by the present inventors, maintaining the growth temperature in a range between about 800 degrees Centigrade and about 950 degrees Centigrade can avoid the segregation of the Sc which can result in the formation of undesired crystal structures such as compounds of Sc, such as rock-salt Sc_xAl₁₋N grains or the formation of metallic inclusions in the layer and thereby enable the formation of the single crystal piezoelectric Sc_xAl_1−xN layer. As further appreciated by the present inventors, the ratio of N to Sc in the precursors used for the growth of the single crystal piezoelectric Sc_xAl_1−xN layer may also be effective in promoting the single crystal piezoelectric Sc_xAl₁₋N layer.

FIG. 60 is a schematic illustration of a piezoelectric Sc_xAl_1−xN layer 6410 formed using an MOCVD system in some embodiments according to the invention. According to FIG. 60, the single crystal piezoelectric Sc_xAl_1−xN layer 6410 can be formed on a substrate 6610. In some embodiments according to the invention the substrate 6610 can be SiC, Al₂O₃, Si, or GaN. Other substrates can also be used. In some embodiments according to the present invention, the single crystal piezoelectric Sc_xAl_1−xN layer 6410 is formed using the MOCVD system to have a concentration of Sc in a range between about 4% (Sc_0.04Al_0.96N) and 18% (Sc_0.18Al_0.82N). In some embodiments according to the present invention, the single crystal piezoelectric Sc_xAl_1−xN layer 6410 is formed using the MOCVD system to have a concentration of Sc in a range between about 4% (Sc_0.04Al_0.96N) and 41% (Sc_0.41Al_0.59N). The single crystal piezoelectric Sc_xAl_1−xN layer 6410 can have a crystalline structure characterized by an XRD ω-rocking curve FWHM value in a range between about less than 1.0 degrees to about 0.001 degrees as measured about an omega scan angle as measured about the Sc_xAl_1−xN (0002) film reflection. In some embodiments according to the invention, the single crystal piezoelectric Sc_xAl_1−xN layer 6410 can have a thickness in a range between about 10 nm and about 2 um. Other thicknesses can also be formed. In some embodiments according to the present invention, a nucleation layer 6410A can be formed on the substrate 6610 in order to promote the growth of the single crystal piezoelectric Sc_xAl_1−xN layer 6410. In some embodiments according to the present invention, the nucleation layer 6410A can be AlN.

FIG. 1A is a simplified diagram illustrating an acoustic resonator device 101 having topside interconnections according to an example of the present invention. As shown, device 101 includes a thinned seed substrate 112 with an overlying single crystal piezoelectric layer 120, which has a micro-via 129. The micro-via 129 can include a topside micro-trench 121, a topside metal plug 146, a backside trench 114, and a backside metal plug 147. Although device 101 is depicted with a single micro-via 129, device 101 may have multiple micro-vias. A topside metal electrode 130 is formed overlying the piezoelectric layer 120. A top cap structure is bonded to the piezoelectric layer 120. This top cap structure includes an interposer substrate 119 with one or more through-vias 151 that are connected to one or more top bond pads 143, one or more bond pads 144, and topside metal 145 with topside metal plug 146. Solder balls 170 are electrically coupled to the one or more top bond pads 143.

The thinned substrate 112 has the first and second backside trenches 113, 114. A backside metal electrode 131 is formed underlying a portion of the thinned seed substrate 112, the first backside trench 113, and the topside metal electrode 130. The backside metal plug 147 is formed underlying a portion of the thinned seed substrate 112, the second backside trench 114, and the topside metal 145. This backside metal plug 147 is electrically coupled to the topside metal plug 146 and the backside metal electrode 131. A backside cap structure 161 is bonded to the thinned seed substrate 112, underlying the first and second backside trenches 113, 114. Further details relating to the method of manufacture of this device will be discussed starting from FIG. 2.

FIG. 1B is a simplified diagram illustrating an acoustic resonator device 102 having backside interconnections according to an example of the present invention. As shown, device 101 includes a thinned seed substrate 112 with an overlying piezoelectric layer 120, which has a micro-via 129. The micro-via 129 can include a topside micro-trench 121, a topside metal plug 146, a backside trench 114, and a backside metal plug 147. Although device 102 is depicted with a single micro-via 129, device 102 may have multiple micro-vias. A topside metal electrode 130 is formed overlying the piezoelectric layer 120. A top cap structure is bonded to the piezoelectric layer 120. This top cap structure 119 includes bond pads which are connected to one or more bond pads 144 and topside metal 145 on piezoelectric layer 120. The topside metal 145 includes a topside metal plug 146.

The thinned substrate 112 has the first and second backside trenches 113, 114. A backside metal electrode 131 is formed underlying a portion of the thinned seed substrate 112, the first backside trench 113, and the topside metal electrode 130. A backside metal plug 147 is formed underlying a portion of the thinned seed substrate 112, the second backside trench 114, and the topside metal plug 146. This backside metal plug 147 is electrically coupled to the topside metal plug 146. A backside cap structure 162 is bonded to the thinned seed substrate 112, underlying the first and second backside trenches. One or more backside bond pads (171, 172, 173) are formed within one or more portions of the backside cap structure 162. Solder balls 170 are electrically coupled to the one or more backside bond pads 171-173. Further details relating to the method of manufacture of this device will be discussed starting from FIG. 14A.

FIG. 1C is a simplified diagram illustrating an acoustic resonator device having interposer/cap-free structure interconnections according to an example of the present invention. As shown, device 103 includes a thinned seed substrate 112 with an overlying single crystal piezoelectric layer 120, which has a micro-via 129. The micro-via 129 can include a topside micro-trench 121, a topside metal plug 146, a backside trench 114, and a backside metal plug 147. Although device 103 is depicted with a single micro-via 129, device 103 may have multiple micro-vias. A topside metal electrode 130 is formed overlying the piezoelectric layer 120. The thinned substrate 112 has the first and second backside trenches 113, 114. A backside metal electrode 131 is formed underlying a portion of the thinned seed substrate 112, the first backside trench 113, and the topside metal electrode 130. A backside metal plug 147 is formed underlying a portion of the thinned seed substrate 112, the second backside trench 114, and the topside metal 145. This backside metal plug 147 is electrically coupled to the topside metal plug 146 and the backside metal electrode 131. Further details relating to the method of manufacture of this device will be discussed starting from FIG. 2.

FIG. 1D is a simplified diagram illustrating an acoustic resonator device having interposer/cap-free structure interconnections with a shared backside trench according to an example of the present invention. As shown, device 104 includes a thinned seed substrate 112 with an overlying single crystal piezoelectric layer 120, which has a micro-via 129. The micro-via 129 can include a topside micro-trench 121, a topside metal plug 146, and a backside metal 147. Although device 104 is depicted with a single micro-via 129, device 104 may have multiple micro-vias. A topside metal electrode 130 is formed overlying the piezoelectric layer 120. The thinned substrate 112 has a first backside trench 113. A backside metal electrode 131 is formed underlying a portion of the thinned seed substrate 112, the first backside trench 113, and the topside metal electrode 130. A backside metal 147 is formed underlying a portion of the thinned seed substrate 112, the second backside trench 114, and the topside metal 145. This backside metal 147 is electrically coupled to the topside metal plug 146 and the backside metal electrode 131. Further details relating to the method of manufacture of this device will be discussed starting from FIG. 2.

FIGS. 2 and 3 are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. This method illustrates the process for fabricating an acoustic resonator device similar to that shown in FIG. 1A. FIG. 2 can represent a method step of providing a partially processed piezoelectric substrate. As shown, device 102 includes a seed substrate 110 with a piezoelectric layer 120 formed overlying. In a specific example, the seed substrate can include silicon, silicon carbide, aluminum oxide, or single crystal aluminum gallium nitride materials, or the like. The piezoelectric layer 120 can include a piezoelectric single crystal layer.

FIG. 3 can represent a method step of forming a top side metallization or top resonator metal electrode 130. In a specific example, the topside metal electrode 130 can include a molybdenum, aluminum, ruthenium, or titanium material, or the like and combinations thereof. This layer can be deposited and patterned on top of the piezoelectric layer by a lift-off process, a wet etching process, a dry etching process, a metal printing process, a metal laminating process, or the like. The lift-off process can include a sequential process of lithographic patterning, metal deposition, and lift-off steps to produce the topside metal layer. The wet/dry etching processes can includes sequential processes of metal deposition, lithographic patterning, metal deposition, and metal etching steps to produce the topside metal layer. Those of ordinary skill in the art will recognize other variations, modifications, and alternatives.

FIG. 4A is a simplified diagram illustrating a step for a method of manufacture for an acoustic resonator device 401 according to an example of the present invention. This figure can represent a method step of forming one or more topside micro-trenches 121 within a portion of the piezoelectric layer 120. This topside micro-trench 121 can serve as the main interconnect junction between the top and bottom sides of the acoustic membrane, which will be developed in later method steps. In an example, the topside micro-trench 121 is extends all the way through the piezoelectric layer 120 and stops in the seed substrate 110. This topside micro-trench 121 can be formed through a dry etching process, a laser drilling process, or the like. FIGS. 4B and 4C describe these options in more detail.

FIGS. 4B and 4C are simplified diagrams illustrating alternative methods for conducting the method step as described in FIG. 4A. As shown, FIG. 4B represents a method step of using a laser drill, which can quickly and accurately form the topside micro-trench 121 in the piezoelectric layer 120. In an example, the laser drill can be used to form nominal 50 um holes, or holes between 10 um and 500 um in diameter, through the piezoelectric layer 120 and stop in the seed substrate 110 below the interface between layers 120 and 110. A protective layer 122 can be formed overlying the piezoelectric layer 120 and the topside metal electrode 130. This protective layer 122 can serve to protect the device from laser debris and to provide a mask for the etching of the topside micro-via 121. In a specific example, the laser drill can be an 11 W high power diode-pumped UV laser, or the like. This mask 122 can be subsequently removed before proceeding to other steps. The mask may also be omitted from the laser drilling process, and air flow can be used to remove laser debris.

FIG. 4C can represent a method step of using a dry etching process to form the topside micro-trench 121 in the piezoelectric layer 120. As shown, a lithographic masking layer 123 can be forming overlying the piezoelectric layer 120 and the topside metal electrode 130. The topside micro-trench 121 can be formed by exposure to plasma, or the like.

FIGS. 4D and 4E are simplified diagrams illustrating an alternative method for conducting the method step as described in FIG. 4A. These figures can represent the method step of manufacturing multiple acoustic resonator devices simultaneously. In FIG. 4D, two devices are shown on Die #1 and Die #2, respectively. FIG. 4E shows the process of forming a micro-via 121 on each of these dies while also etching a scribe line 124 or dicing line. In an example, the etching of the scribe line 124 singulates and relieves stress in the piezoelectric single crystal layer 120.

FIGS. 5 to 8 are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. FIG. 5 can represent the method step of forming one or more bond pads 140 and forming a topside metal 141 electrically coupled to at least one of the bond pads 140. The topside metal 141 can include a topside metal plug 146 formed within the topside micro-trench 121. In a specific example, the topside metal plug 146 fills the topside micro-trench 121 to form a topside portion of a micro-via.

In an example, the bond pads 140 and the topside metal 141 can include a gold material or other interconnect metal material depending upon the application of the device. These metal materials can be formed by a lift-off process, a wet etching process, a dry etching process, a screen-printing process, an electroplating process, a metal printing process, or the like. In a specific example, the deposited metal materials can also serve as bond pads for a cap structure, which will be described below.

FIG. 6 can represent a method step for preparing the acoustic resonator device for bonding, which can be a hermetic bonding. As shown, a top cap structure is positioned above the partially processed acoustic resonator device as described in the previous figures. The top cap structure can be formed using an interposer substrate 119 in two configurations: fully processed interposer version 601 (through glass via) and partially processed interposer version 602 (blind via version). In the 601 version, the interposer substrate 119 includes through-via structures 151 that extend through the interposer substrate 119 and are electrically coupled to bottom bond pads 142 and top bond pads 143. In the 602 version, the interposer substrate 119 includes blind via structures 152 that only extend through a portion of the interposer substrate 119 from the bottom side. These blind via structures 152 are also electrically coupled to bottom bond pads 142. In a specific example, the interposer substrate can include a silicon, glass, smart-glass, or other like material.

FIG. 7 can represent a method step of bonding the top cap structure to the partially processed acoustic resonator device. As shown, the interposer substrate 119 is bonded to the piezoelectric layer by the bond pads (140, 142) and the topside metal 141, which are now denoted as bond pad 144 and topside metal 145. This bonding process can be done using a compression bond method or the like. FIG. 8 can represent a method step of thinning the seed substrate 110, which is now denoted as thinned seed substrate 111. This substrate thinning process can include grinding and etching processes or the like. In a specific example, this process can include a wafer backgrinding process followed by stress removal, which can involve dry etching, CMP polishing, or annealing processes.

FIG. 9A is a simplified diagram illustrating a step for a method of manufacture for an acoustic resonator device 901 according to an example of the present invention. FIG. 9A can represent a method step for forming backside trenches 113 and 114 to allow access to the piezoelectric layer from the backside of the thinned seed substrate 111. In an example, the first backside trench 113 can be formed within the thinned seed substrate 111 and underlying the topside metal electrode 130. The second backside trench 114 can be formed within the thinned seed substrate 111 and underlying the topside micro-trench 121 and topside metal plug 146. This substrate is now denoted thinned substrate 112. In a specific example, these trenches 113 and 114 can be formed using deep reactive ion etching (DRIE) processes, Bosch processes, or the like. The size, shape, and number of the trenches may vary with the design of the acoustic resonator device. In various examples, the first backside trench may be formed with a trench shape similar to a shape of the topside metal electrode or a shape of the backside metal electrode. The first backside trench may also be formed with a trench shape that is different from both a shape of the topside metal electrode and the backside metal electrode.

FIGS. 9B and 9C are simplified diagrams illustrating an alternative method for conducting the method step as described in FIG. 9A. Like FIGS. 4D and 4E, these figures can represent the method step of manufacturing multiple acoustic resonator devices simultaneously. In FIG. 9B, two devices with cap structures are shown on Die #1 and Die #2, respectively. FIG. 9C shows the process of forming backside trenches (113, 114) on each of these dies while also etching a scribe line 115 or dicing line. In an example, the etching of the scribe line 115 provides an optional way to singulate the backside wafer 112.

FIG. 10 is a simplified diagram illustrating a step for a method of manufacture for an acoustic resonator device 1000 according to an example of the present invention. This figure can represent a method step of forming a backside metal electrode 131 and a backside metal plug 147 within the backside trenches of the thinned seed substrate 112. In an example, the backside metal electrode 131 can be formed underlying one or more portions of the thinned substrate 112, within the first backside trench 113, and underlying the topside metal electrode 130. This process completes the resonator structure within the acoustic resonator device. The backside metal plug 147 can be formed underlying one or more portions of the thinned substrate 112, within the second backside trench 114, and underlying the topside micro-trench 121. The backside metal plug 147 can be electrically coupled to the topside metal plug 146 and the backside metal electrode 131. In a specific example, the backside metal electrode 130 can include a molybdenum, aluminum, ruthenium, or titanium material, or the like and combinations thereof. The backside metal plug can include a gold material, low resistivity interconnect metals, electrode metals, or the like. These layers can be deposited using the deposition methods described previously.

FIGS. 11A and 11B are simplified diagrams illustrating alternative steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. These figures show methods of bonding a backside cap structure underlying the thinned seed substrate 112. In FIG. 11A, the backside cap structure is a dry film cap 161, which can include a permanent photo-imageable dry film such as a solder mask, polyimide, or the like. Bonding this cap structure can be cost-effective and reliable, but may not produce a hermetic seal. In FIG. 11B, the backside cap structure is a substrate 162, which can include a silicon, glass, or other like material. Bonding this substrate can provide a hermetic seal, but may cost more and require additional processes. Depending upon application, either of these backside cap structures can be bonded underlying the first and second backside vias.

FIGS. 12A to 12E are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. More specifically, these figures describe additional steps for processing the blind via interposer “602” version of the top cap structure. FIG. 12A shows an acoustic resonator device 1201 with blind vias 152 in the top cap structure. In FIG. 12B, the interposer substrate 119 is thinned, which forms a thinned interposer substrate 118, to expose the blind vias 152. This thinning process can be a combination of a grinding process and etching process as described for the thinning of the seed substrate. In FIG. 12C, a redistribution layer (RDL) process and metallization process can be applied to create top cap bond pads 160 that are formed overlying the blind vias 152 and are electrically coupled to the blind vias 152. As shown in FIG. 12D, a ball grid array (BGA) process can be applied to form solder balls 170 overlying and electrically coupled to the top cap bond pads 160. This process leaves the acoustic resonator device ready for wire bonding 171, as shown in FIG. 12E.

FIG. 13 is a simplified diagram illustrating a step for a method of manufacture for an acoustic resonator device according to an example of the present invention. As shown, device 1300 includes two fully processed acoustic resonator devices that are ready to singulation to create separate devices. In an example, the die singulation process can be done using a wafer dicing saw process, a laser cut singulation process, or other processes and combinations thereof.

FIGS. 14A to 14G are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. This method illustrates the process for fabricating an acoustic resonator device similar to that shown in FIG. 1B. The method for this example of an acoustic resonator can go through similar steps as described in FIGS. 1-5. FIG. 14A shows where this method differs from that described previously. Here, the top cap structure substrate 119 and only includes one layer of metallization with one or more bottom bond pads 142. Compared to FIG. 6, there are no via structures in the top cap structure because the interconnections will be formed on the bottom side of the acoustic resonator device.

FIGS. 14B to 14F depict method steps similar to those described in the first process flow. FIG. 14B can represent a method step of bonding the top cap structure to the piezoelectric layer 120 through the bond pads (140, 142) and the topside metal 141, now denoted as bond pads 144 and topside metal 145 with topside metal plug 146. FIG. 14C can represent a method step of thinning the seed substrate 110, which forms a thinned seed substrate 111, similar to that described in FIG. 8. FIG. 14D can represent a method step of forming first and second backside trenches, similar to that described in FIG. 9A. FIG. 14E can represent a method step of forming a backside metal electrode 131 and a backside metal plug 147, similar to that described in FIG. 10. FIG. 14F can represent a method step of bonding a backside cap structure 162, similar to that described in FIGS. 11A and 11B.

FIG. 14G shows another step that differs from the previously described process flow. Here, the backside bond pads 171, 172, and 173 are formed within the backside cap structure 162. In an example, these backside bond pads 171-173 can be formed through a masking, etching, and metal deposition processes similar to those used to form the other metal materials. A BGA process can be applied to form solder balls 170 in contact with these backside bond pads 171-173, which prepares the acoustic resonator device 1407 for wire bonding.

FIGS. 15A to 15E are simplified diagrams illustrating steps for a method of manufacture for an acoustic resonator device according to an example of the present invention. This method illustrates the process for fabricating an acoustic resonator device similar to that shown in FIG. 1B. The method for this example can go through similar steps as described in FIG. 1-5. FIG. 15A shows where this method differs from that described previously. A temporary carrier 218 with a layer of temporary adhesive 217 is attached to the substrate. In a specific example, the temporary carrier 218 can include a glass wafer, a silicon wafer, or other wafer and the like.

FIGS. 15B to 15F depict method steps similar to those described in the first process flow. FIG. 15B can represent a method step of thinning the seed substrate 110, which forms a thinned substrate 111, similar to that described in FIG. 8. In a specific example, the thinning of the seed substrate 110 can include a back side grinding process followed by a stress removal process. The stress removal process can include a dry etch, a Chemical Mechanical Planarization (CMP), and annealing processes.

FIG. 15C can represent a method step of forming a shared backside trench 113, similar to the techniques described in FIG. 9A. The main difference is that the shared backside trench is configured underlying both topside metal electrode 130, topside micro-trench 121, and topside metal plug 146. In an example, the shared backside trench 113 is a backside resonator cavity that can vary in size, shape (all possible geometric shapes), and side wall profile (tapered convex, tapered concave, or right angle). In a specific example, the forming of the shared backside trench 113 can include a litho-etch process, which can include a back-to-front alignment and dry etch of the backside substrate 111. The piezoelectric layer 120 can serve as an etch stop layer for the forming of the shared backside trench 113.

FIG. 15D can represent a method step of forming a backside metal electrode 131 and a backside metal 147, similar to that described in FIG. 10. In an example, the forming of the backside metal electrode 131 can include a deposition and patterning of metal materials within the shared backside trench 113. Here, the backside metal 131 serves as an electrode and the backside plug/connect metal 147 within the micro-via 121. The thickness, shape, and type of metal can vary as a function of the resonator/filter design. As an example, the backside electrode 131 and via plug metal 147 can be different metals. In a specific example, these backside metals 131, 147 can either be deposited and patterned on the surface of the piezoelectric layer 120 or rerouted to the backside of the substrate 112. In an example, the backside metal electrode may be patterned such that it is configured within the boundaries of the shared backside trench such that the backside metal electrode does not come in contact with one or more side-walls of the seed substrate created during the forming of the shared backside trench.

FIG. 15E can represent a method step of bonding a backside cap structure 162, similar to that described in FIGS. 11A and 11B, following a de-bonding of the temporary carrier 218 and cleaning of the topside of the device to remove the temporary adhesive 217. Those of ordinary skill in the art will recognize other variations, modifications, and alternatives of the methods steps described previously.

As used herein, the term “substrate” can mean the bulk substrate or can include overlying growth structures such as an aluminum, gallium, or ternary compound of aluminum and gallium and nitrogen containing epitaxial region, or functional regions, combinations, and the like.

One or more benefits are achieved over pre-existing techniques using the invention. In particular, the present device can be manufactured in a relatively simple and cost effective manner while using conventional materials and/or methods according to one of ordinary skill in the art. Using the present method, one can create a reliable single crystal based acoustic resonator using multiple ways of three-dimensional stacking through a wafer level process. Such filters or resonators can be implemented in an RF filter device, an RF filter system, or the like. Depending upon the embodiment, one or more of these benefits may be achieved. Of course, there can be other variations, modifications, and alternatives.

Wireless data communication demands high performance RF filters with frequencies around 5 GHz and higher. Bulk acoustic wave resonators (BAWR), widely used in such filters operating at frequencies around 3 GHz and lower, are leading candidates for meeting such demands. Current bulk acoustic wave resonators use polycrystalline piezoelectric AlN layers where each grain's c-axis is aligned perpendicular to the film's surface to allow high piezoelectric performance whereas the grains' a- or b-axis are randomly distributed. This peculiar grain distribution works well when the piezoelectric film's thickness is around 1 um and above, which is the perfect thickness for bulk acoustic wave (BAW) filters operating at frequencies ranging from 1 to 3 GHz. However, the quality of the polycrystalline piezoelectric films degrades quickly as the thicknesses decrease below around 0.5 um, which is required for resonators and filters operating at frequencies around 5 GHz and above.

Single crystalline or epitaxial piezoelectric layers grown on compatible crystalline substrates exhibit good crystalline quality and high piezoelectric performance even down to very thin thicknesses, e.g., 0.4 um. The present invention provides manufacturing processes and structures for high quality bulk acoustic wave resonators with single crystalline or epitaxial piezoelectric thn films for high frequency BAW filter applications.

BAWRs can use a piezoelectric material, e.g., AlN, in crystalline form, i.e., polycrystalline or single crystalline. The quality of the film heavy depends on the chemical, crystalline, or topographical quality of the layer on which the film is grown. In conventional BAWR processes (including film bulk acoustic resonator (FBAR) or solidly mounted resonator (SMR) geometry), the piezoelectric film is grown on a patterned bottom electrode, which is usually made of molybdenum (Mo), tungsten (W), or ruthenium (Ru). The surface geometry of the patterned bottom electrode significantly influences the crystalline orientation and crystalline quality of the piezoelectric film, requiring complicated modification of the structure.

Thus, embodiments according to the present invention can use single crystalline piezoelectric films and layer transfer processes to produce a BAWR with enhanced ultimate quality factor and electro-mechanical coupling for RF filters. Such methods and structures facilitate methods of manufacturing and structures for RF filters using single crystalline or epitaxial piezoelectric films to meet the growing demands of contemporary data communication.

In an example, the present invention provides transfer structures and processes for acoustic resonator devices, which provides a flat, high-quality, single-crystal piezoelectric film for superior acoustic wave control and high Q in high frequency. As described above, polycrystalline piezoelectric layers limit Q in high frequency. Also, growing epitaxial piezoelectric layers on patterned electrodes affects the crystalline orientation of the piezoelectric layer, which limits the ability to have tight boundary control of the resulting resonators. Embodiments of the present invention, as further described below, can overcome these limitations and exhibit improved performance and cost-efficiency.

FIGS. 16A-16C through FIGS. 31A-31C illustrate a method of fabrication for an acoustic resonator device using a transfer structure with a sacrificial layer. In these figure series described below, the “A” figures show simplified diagrams illustrating top cross-sectional views of single crystal resonator devices according to various embodiments of the present invention. The “B” figures show simplified diagrams illustrating lengthwise cross-sectional views of the same devices in the “A” figures. Similarly, the “C” figures show simplified diagrams illustrating widthwise cross-sectional views of the same devices in the “A” figures. In some cases, certain features are omitted to highlight other features and the relationships between such features. Those of ordinary skill in the art will recognize variations, modifications, and alternatives to the examples shown in these figure series.

FIGS. 16A-16C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a piezoelectric film 1620 overlying a growth substrate 1610. In an example, the growth substrate 1610 can include silicon (S), silicon carbide (SiC), or other like materials. The piezoelectric film 1620 can be an epitaxial film including aluminum nitride (AlN), gallium nitride (GaN), or other like materials. Additionally, this piezoelectric substrate can be subjected to a thickness trim.

FIGS. 17A-17C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first electrode 1710 overlying the surface region of the piezoelectric film 1620. In an example, the first electrode 1710 can include molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials. In a specific example, the first electrode 1710 can be subjected to a dry etch with a slope. As an example, the slope can be about 60 degrees.

FIGS. 18A-18C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first passivation layer 1810 overlying the first electrode 1710 and the piezoelectric film 1620. In an example, the first passivation layer 1810 can include silicon nitride (SiN), silicon oxide (SiOx), or other like materials. In a specific example, the first passivation layer 1810 can have a thickness ranging from about 50 nm to about 100 nm.

FIGS. 19A-19C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a sacrificial layer 1910 overlying a portion of the first electrode 1810 and a portion of the piezoelectric film 1620. In an example, the sacrificial layer 1910 can include polycrystalline silicon (poly-Si), amorphous silicon (a-Si), or other like materials. In a specific example, this sacrificial layer 1910 can be subjected to a dry etch with a slope and be deposited with a thickness of about 1 um. Further, phosphorous doped SiO.sub.2 (PSG) can be used as the sacrificial layer with different combinations of support layer (e.g., SiNx).

FIGS. 20A-20C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a support layer 2010 overlying the sacrificial layer 1910, the first electrode 1710, and the piezoelectric film 1620. In an example, the support layer 2010 can include silicon dioxide (SiO.sub.2), silicon nitride (SiN), or other like materials. In a specific example, this support layer 2010 can be deposited with a thickness of about 2-3 um. As described above, other support layers (e.g., SiNx) can be used in the case of a PSG sacrificial layer.

FIGS. 21A-21C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of polishing the support layer 2010 to form a polished support layer 2011. In an example, the polishing process can include a chemical-mechanical planarization process or the like.

FIGS. 22A-22C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate flipping the device and physically coupling overlying the support layer 2011 overlying a bond substrate 2210. In an example, the bond substrate 2210 can include a bonding support layer 2220 (SiO.sub.2 or like material) overlying a substrate having silicon (Si), sapphire (Al.sub.20.sub.3), silicon dioxide (SiO.sub.2), silicon carbide (SiC), or other like materials. In a specific embodiment, the bonding support layer 2220 of the bond substrate 2210 is physically coupled to the polished support layer 2011. Further, the physical coupling process can include a room temperature bonding process following by a 300 degree Celsius annealing process.

FIGS. 23A-23C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of removing the growth substrate 1610 or otherwise the transfer of the piezoelectric film 1620. In an example, the removal process can include a grinding process, a blanket etching process, a film transfer process, an ion implantation transfer process, a laser crack transfer process, or the like and combinations thereof.

FIGS. 24A-24C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming an electrode contact via 2410 within the piezoelectric film 1620 (becoming piezoelectric film 1621) overlying the first electrode 1710 and forming one or more release holes 2420 within the piezoelectric film 1620 and the first passivation layer 1810 overlying the sacrificial layer 1910. The via forming processes can include various types of etching processes.

FIGS. 25A-25C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a second electrode 2510 overlying the piezoelectric film 1621. In an example, the formation of the second electrode 2510 includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching the second electrode 2510 to form an electrode cavity 2511 and to remove portion 2511 from the second electrode to form a top metal 2520. Further, the top metal 2520 is physically coupled to the first electrode 1720 through electrode contact via 2410.

FIGS. 26A-26C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first contact metal 2610 overlying a portion of the second electrode 2510 and a portion of the piezoelectric film 1621, and forming a second contact metal 2611 overlying a portion of the top metal 2520 and a portion of the piezoelectric film 1621. In an example, the first and second contact metals can include gold (Au), aluminum (Al), copper (Cu), nickel (Ni), aluminum bronze (AlCu), or related alloys of these materials or other like materials.

FIGS. 27A-27C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a second passivation layer 2710 overlying the second electrode 2510, the top metal 2520, and the piezoelectric film 1621. In an example, the second passivation layer 2710 can include silicon nitride (SiN), silicon oxide (SiOx), or other like materials. In a specific example, the second passivation layer 2710 can have a thickness ranging from about 50 nm to about 100 nm.

FIGS. 28A-28C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of removing the sacrificial layer 1910 to form an air cavity 2810. In an example, the removal process can include a poly-Si etch or an a-Si etch, or the like.

FIGS. 29A-29C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the second electrode 2510 and the top metal 2520 to form a processed second electrode 2910 and a processed top metal 2920. This step can follow the formation of second electrode 2510 and top metal 2520. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed second electrode 2910 with an electrode cavity 2912 and the processed top metal 2920. The processed top metal 2920 remains separated from the processed second electrode 2910 by the removal of portion 2911. In a specific example, the processed second electrode 2910 is characterized by the addition of an energy confinement structure configured on the processed second electrode 2910 to increase Q.

FIGS. 30A-30C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 1710 to form a processed first electrode 2310. This step can follow the formation of first electrode 1710. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed first electrode 3010 with an electrode cavity, similar to the processed second electrode 2910. Air cavity 2811 shows the change in cavity shape due to the processed first electrode 3010. In a specific example, the processed first electrode 3010 is characterized by the addition of an energy confinement structure configured on the processed second electrode 3010 to increase Q.

FIGS. 31A-31C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 1710, to form a processed first electrode 2310, and the second electrode 2510/top metal 2520 to form a processed second electrode 2910/processed top metal 2920. These steps can follow the formation of each respective electrode, as described for FIGS. 29A-29C and 30A-30C. Those of ordinary skill in the art will recognize other variations, modifications, and alternatives.

FIGS. 32A-32C through FIGS. 46A-46C illustrate a method of fabrication for an acoustic resonator device using a transfer structure without sacrificial layer. In these figure series described below, the “A” figures show simplified diagrams illustrating top cross-sectional views of single crystal resonator devices according to various embodiments of the present invention. The “B” figures show simplified diagrams illustrating lengthwise cross-sectional views of the same devices in the “A” figures. Similarly, the “C” figures show simplified diagrams illustrating widthwise cross-sectional views of the same devices in the “A” figures. In some cases, certain features are omitted to highlight other features and the relationships between such features. Those of ordinary skill in the art will recognize variations, modifications, and alternatives to the examples shown in these figure series.

FIGS. 32A-32C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a piezoelectric film 3220 overlying a growth substrate 3210. In an example, the growth substrate 3210 can include silicon (S), silicon carbide (SiC), or other like materials. The piezoelectric film 3220 can be an epitaxial film including aluminum nitride (AlN), gallium nitride (GaN), or other like materials. Additionally, this piezoelectric substrate can be subjected to a thickness trim.

FIGS. 33A-33C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first electrode 3310 overlying the surface region of the piezoelectric film 3220. In an example, the first electrode 3310 can include molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials. In a specific example, the first electrode 3310 can be subjected to a dry etch with a slope. As an example, the slope can be about 60 degrees.

FIGS. 34A-34C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first passivation layer 3410 overlying the first electrode 3310 and the piezoelectric film 3220. In an example, the first passivation layer 3410 can include silicon nitride (SiN), silicon oxide (SiOx), or other like materials. In a specific example, the first passivation layer 3410 can have a thickness ranging from about 50 nm to about 100 nm.

FIGS. 35A-35C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a support layer 3510 overlying the first electrode 3310, and the piezoelectric film 3220. In an example, the support layer 3510 can include silicon dioxide (SiO.sub.2), silicon nitride (SiN), or other like materials. In a specific example, this support layer 3510 can be deposited with a thickness of about 2-3 um. As described above, other support layers (e.g., SiNx) can be used in the case of a PSG sacrificial layer.

FIGS. 36A-36C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the optional method step of processing the support layer 3510 (to form support layer 3511) in region 3610. In an example, the processing can include a partial etch of the support layer 3510 to create a flat bond surface. In a specific example, the processing can include a cavity region. In other examples, this step can be replaced with a polishing process such as a chemical-mechanical planarization process or the like.

FIGS. 37A-37C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming an air cavity 3710 within a portion of the support layer 3511 (to form support layer 3512). In an example, the cavity formation can include an etching process that stops at the first passivation layer 3410.

FIGS. 38A-38C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming one or more cavity vent holes 3810 within a portion of the piezoelectric film 3220 through the first passivation layer 3410. In an example, the cavity vent holes 3810 connect to the air cavity 3710.

FIGS. 39A-39C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate flipping the device and physically coupling overlying the support layer 3512 overlying a bond substrate 3910. In an example, the bond substrate 3910 can include a bonding support layer 3920 (SiO.sub.2 or like material) overlying a substrate having silicon (Si), sapphire (Al.sub.2O.sub.3), silicon dioxide (SiO.sub.2), silicon carbide (SiC), or other like materials. In a specific embodiment, the bonding support layer 3920 of the bond substrate 3910 is physically coupled to the polished support layer 3512. Further, the physical coupling process can include a room temperature bonding process following by a 300 degree Celsius annealing process.

FIGS. 40A-40C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of removing the growth substrate 3210 or otherwise the transfer of the piezoelectric film 3220. In an example, the removal process can include a grinding process, a blanket etching process, a film transfer process, an ion implantation transfer process, a laser crack transfer process, or the like and combinations thereof.

FIGS. 41A-41C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming an electrode contact via 4110 within the piezoelectric film 3220 overlying the first electrode 3310. The via forming processes can include various types of etching processes.

FIGS. 42A-42C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a second electrode 4210 overlying the piezoelectric film 3220. In an example, the formation of the second electrode 4210 includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching the second electrode 4210 to form an electrode cavity 4211 and to remove portion 4211 from the second electrode to form a top metal 4220. Further, the top metal 4220 is physically coupled to the first electrode 3310 through electrode contact via 4110.

FIGS. 43A-43C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first contact metal 4310 overlying a portion of the second electrode 4210 and a portion of the piezoelectric film 3220, and forming a second contact metal 4311 overlying a portion of the top metal 4220 and a portion of the piezoelectric film 3220. In an example, the first and second contact metals can include gold (Au), aluminum (Al), copper (Cu), nickel (Ni), aluminum bronze (AlCu), or other like materials. This figure also shows the method step of forming a second passivation layer 4320 overlying the second electrode 4210, the top metal 4220, and the piezoelectric film 3220. In an example, the second passivation layer 4320 can include silicon nitride (SiN), silicon oxide (SiOx), or other like materials. In a specific example, the second passivation layer 4320 can have a thickness ranging from about 50 nm to about 100 nm.

FIGS. 44A-44C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the second electrode 4210 and the top metal 4220 to form a processed second electrode 4410 and a processed top metal 4420. This step can follow the formation of second electrode 4210 and top metal 4220. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed second electrode 4410 with an electrode cavity 4412 and the processed top metal 4420. The processed top metal 4420 remains separated from the processed second electrode 4410 by the removal of portion 4411. In a specific example, the processed second electrode 4410 is characterized by the addition of an energy confinement structure configured on the processed second electrode 4410 to increase Q.

FIGS. 45A-45C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 3310 to form a processed first electrode 4510. This step can follow the formation of first electrode 3310. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed first electrode 4510 with an electrode cavity, similar to the processed second electrode 4410. Air cavity 3711 shows the change in cavity shape due to the processed first electrode 4510. In a specific example, the processed first electrode 4510 is characterized by the addition of an energy confinement structure configured on the processed second electrode 4510 to increase Q.

FIGS. 46A-46C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process using a sacrificial layer for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 3310, to form a processed first electrode 4510, and the second electrode 4210/top metal 4220 to form a processed second electrode 4410/processed top metal 4420. These steps can follow the formation of each respective electrode, as described for FIGS. 44A-44C and 45A-45C. Those of ordinary skill in the art will recognize other variations, modifications, and alternatives.

FIGS. 47A-47C through FIGS. 59A-59C illustrate a method of fabrication for an acoustic resonator device using a transfer structure with a multilayer mirror structure. In these figure series described below, the “A” figures show simplified diagrams illustrating top cross-sectional views of single crystal resonator devices according to various embodiments of the present invention. The “B” figures show simplified diagrams illustrating lengthwise cross-sectional views of the same devices in the “A” figures. Similarly, the “C” figures show simplified diagrams illustrating widthwise cross-sectional views of the same devices in the “A” figures. In some cases, certain features are omitted to highlight other features and the relationships between such features. Those of ordinary skill in the art will recognize variations, modifications, and alternatives to the examples shown in these figure series.

FIGS. 47A-47C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a piezoelectric film 4720 overlying a growth substrate 4710. In an example, the growth substrate 4710 can include silicon (S), silicon carbide (SiC), or other like materials. The piezoelectric film 4720 can be an epitaxial film including aluminum nitride (AlN), gallium nitride (GaN), or other like materials. Additionally, this piezoelectric substrate can be subjected to a thickness trim.

FIGS. 48A-48C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first electrode 4810 overlying the surface region of the piezoelectric film 4720. In an example, the first electrode 4810 can include molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials. In a specific example, the first electrode 4810 can be subjected to a dry etch with a slope. As an example, the slope can be about 60 degrees.

FIGS. 49A-49C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a multilayer mirror or reflector structure. In an example, the multilayer mirror includes at least one pair of layers with a low impedance layer 4910 and a high impedance layer 4920. In FIGS. 49A-49C, two pairs of low/high impedance layers are shown (low: 4910 and 4911; high: 4920 and 4921). In an example, the mirror/reflector area can be larger than the resonator area and can encompass the resonator area. In a specific embodiment, each layer thickness is about ¼ of the wavelength of an acoustic wave at a targeting frequency. The layers can be deposited in sequence and be etched afterwards, or each layer can be deposited and etched individually. In another example, the first electrode 4810 can be patterned after the mirror structure is patterned.

FIGS. 50A-50C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a support layer 5010 overlying the mirror structure (layers 4910, 4911, 4920, and 4921), the first electrode 4810, and the piezoelectric film 4720. In an example, the support layer 5010 can include silicon dioxide (SiO.sub.2), silicon nitride (SiN), or other like materials. In a specific example, this support layer 5010 can be deposited with a thickness of about 2-3 um. As described above, other support layers (e.g., SiNx) can be used.

FIGS. 51A-51C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of polishing the support layer 5010 to form a polished support layer 5011. In an example, the polishing process can include a chemical-mechanical planarization process or the like.

FIGS. 52A-52C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate flipping the device and physically coupling overlying the support layer 5011 overlying a bond substrate 5210. In an example, the bond substrate 5210 can include a bonding support layer 5220 (SiO.sub.2 or like material) overlying a substrate having silicon (Si), sapphire (Al.sub.2O.sub.3), silicon dioxide (SiO.sub.2), silicon carbide (SiC), or other like materials. In a specific embodiment, the bonding support layer 5220 of the bond substrate 5210 is physically coupled to the polished support layer 5011. Further, the physical coupling process can include a room temperature bonding process following by a 300 degree Celsius annealing process.

FIGS. 53A-53C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of removing the growth substrate 4710 or otherwise the transfer of the piezoelectric film 4720. In an example, the removal process can include a grinding process, a blanket etching process, a film transfer process, an ion implantation transfer process, a laser crack transfer process, or the like and combinations thereof.

FIGS. 54A-54C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming an electrode contact via 5410 within the piezoelectric film 4720 overlying the first electrode 4810. The via forming processes can include various types of etching processes.

FIGS. 55A-55C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a second electrode 5510 overlying the piezoelectric film 4720. In an example, the formation of the second electrode 5510 includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching the second electrode 5510 to form an electrode cavity 5511 and to remove portion 5511 from the second electrode to form a top metal 5520. Further, the top metal 5520 is physically coupled to the first electrode 5520 through electrode contact via 5410.

FIGS. 56A-56C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to an example of the present invention. As shown, these figures illustrate the method step of forming a first contact metal 5610 overlying a portion of the second electrode 5510 and a portion of the piezoelectric film 4720, and forming a second contact metal 5611 overlying a portion of the top metal 5520 and a portion of the piezoelectric film 4720. In an example, the first and second contact metals can include gold (Au), aluminum (Al), copper (Cu), nickel (Ni), aluminum bronze (AlCu), or other like materials. This figure also shows the method step of forming a second passivation layer 5620 overlying the second electrode 5510, the top metal 5520, and the piezoelectric film 4720. In an example, the second passivation layer 5620 can include silicon nitride (SiN), silicon oxide (SiOx), or other like materials. In a specific example, the second passivation layer 5620 can have a thickness ranging from about 50 nm to about 100 nm.

FIGS. 57A-57C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the second electrode 5510 and the top metal 5520 to form a processed second electrode 5710 and a processed top metal 5720. This step can follow the formation of second electrode 5710 and top metal 5720. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed second electrode 5410 with an electrode cavity 5712 and the processed top metal 5720. The processed top metal 5720 remains separated from the processed second electrode 5710 by the removal of portion 5711. In a specific example, this processing gives the second electrode and the top metal greater thickness while creating the electrode cavity 5712. In a specific example, the processed second electrode 5710 is characterized by the addition of an energy confinement structure configured on the processed second electrode 5710 to increase Q.

FIGS. 58A-58C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 4810 to form a processed first electrode 5810. This step can follow the formation of first electrode 4810. In an example, the processing of these two components includes depositing molybdenum (Mo), ruthenium (Ru), tungsten (W), or other like materials; and then etching (e.g., dry etch or the like) this material to form the processed first electrode 5810 with an electrode cavity, similar to the processed second electrode 5710. Compared to the two previous examples, there is no air cavity. In a specific example, the processed first electrode 5810 is characterized by the addition of an energy confinement structure configured on the processed second electrode 5810 to increase Q.

FIGS. 59A-59C are simplified diagrams illustrating various cross-sectional views of a single crystal acoustic resonator device and of method steps for a transfer process with a multilayer mirror for single crystal acoustic resonator devices according to another example of the present invention. As shown, these figures illustrate the method step of processing the first electrode 4810, to form a processed first electrode 5810, and the second electrode 5510/top metal 5520 to form a processed second electrode 5710/processed top metal 5720. These steps can follow the formation of each respective electrode, as described for FIGS. 57A-57C and 58A-58C. Those of ordinary skill in the art will recognize other variations, modifications, and alternatives.

In each of the preceding examples relating to transfer processes, energy confinement structures can be formed on the first electrode, second electrode, or both. In an example, these energy confinement structures are mass loaded areas surrounding the resonator area. The resonator area is the area where the first electrode, the piezoelectric layer, and the second electrode overlap. The larger mass load in the energy confinement structures lowers a cut-off frequency of the resonator. The cut-off frequency is the lower or upper limit of the frequency at which the acoustic wave can propagate in a direction parallel to the surface of the piezoelectric film. Therefore, the cut-off frequency is the resonance frequency in which the wave is travelling along the thickness direction and thus is determined by the total stack structure of the resonator along the vertical direction. In piezoelectric films (e.g., AlN), acoustic waves with lower frequency than the cut-off frequency can propagate in a parallel direction along the surface of the film, i.e., the acoustic wave exhibits a high-band-cut-off type dispersion characteristic. In this case, the mass loaded area surrounding the resonator provides a barrier preventing the acoustic wave from propagating outside the resonator. By doing so, this feature increases the quality factor of the resonator and improves the performance of the resonator and, consequently, the filter.

Claims

1. A method of forming a piezoelectric acoustic resonator layer, the method comprising: loading a substrate into a MOCVD reactor chamber;forming an MOCVD single crystal piezoelectric ScxAl1−xN layer on the substrate, where x is in a range between about 0.04 and about 0.18.

2. The method of claim 1 wherein forming the MOCVD single crystal piezoelectric ScxAl1−xN layer on the substrate comprises: providing a heated Sc precursor material to the reactor chamber at a temperature in a range between about 100 degrees Centigrade and about 250 degrees Centigrade to grow the MOCVD single crystal piezoelectric ScxAl1−xN layer.

3. The method of claim 1 further comprising: maintaining a surface of the substrate at a growth temperature in a range between about 800 degrees Centigrade to about 950 degrees Centigrade while forming the MOCVD single crystal piezoelectric ScxAl1−xN layer, wherein the growth temperature is measured using pyrometry.

4. The method of claim 2 wherein the heated Sc precursor material comprises (DIPA)3Sc.

5. The method of claim 2 wherein the heated Sc precursor material comprises (MeCp)3Sc or Cp3Sc.

6. The method of claim 2 wherein the heated Sc precursor material is of general formula (2): Sc(R1Cp)x(R2—NC—C(R3)═N—R2)y  (2),

7. The method of claim 1 wherein the MOCVD formed single crystal piezoelectric ScxAl1−xN layer has a crystalline structure characterized by an XRD rocking curve FWHM value in a range between about less than 1.0 degrees to about 0.001 degrees as measured about an omega scan angle.

8. The method of claim 1 wherein the single crystal piezoelectric ScxAl1−xN layer has a thickness in a range between about 10 nm and about 2 um.

9. The method of claim 1 wherein the substrate comprises SiC, Al2O3, Si, or GaN.

10. A piezoelectric acoustic resonator comprising: a substrate;an MOCVD formed single crystal piezoelectric ScxAl1−xN layer on the substrate, where x is in a range between about 0.04 and about 0.18.

11. The piezoelectric acoustic resonator of claim 10 wherein the MOCVD formed single crystal piezoelectric ScxAl1−xN layer has a crystalline structure characterized by an XRD rocking curve FWHM value in a range between about less than 1.0 degrees to about 0.001 degrees as measured about an omega scan angle.

12. The piezoelectric acoustic resonator of claim 11 wherein the single crystal piezoelectric ScxAl1−xN layer has a thickness in a range between about 10 nm and about 2 um.

13. The piezoelectric acoustic resonator of claim 10 wherein the substrate comprises SiC, Al2O3, Si, or GaN.