Claims
- 1. A heat resistant negative working photosensitive composition that comprises
(a) one or more polybenzoxazole precursor polymers (I): 20wherein x is an integer from about 10 to about 1000, y is an integer from 0 to about 900 and (x+y) is about less then 1000; Ar1 is selected from the group consisting of a tetravalent aromatic group, a tetravalent heterocyclic group, or mixtures thereof; Ar2 is selected from the group consisting a divalent aromatic, a divalent heterocyclic, a divalent alicyclic, a divalent aliphatic group that may contain silicon, or mixtures thereof; Ar3 is selected from the group consisting a divalent aromatic group, a divalent aliphatic group, a divalent heterocyclic group, or mixtures thereof; Ar4 is selected from the group consisting Ar1 (OH)2 or Ar2; G is an organic group selected from the group consisting of groups having a carbonyl, carbonyloxy or sulfonyl group attached directly to the terminal NH group of the polymer; (b) one or more photo-active compounds which release acid upon irradiation (PAGs); (c) a latent crosslinker which contains at least two ˜N-(CH2OR)n units wherein n=1 or 2 and R is a linear or branched C1-C8 alkyl group, with the proviso that when a glycoluril is employed as the latent crosslinker, the G group in the polybenzoxazole precursor polymer is produced from the reaction of a cyclic anhydride; and (d) at least one solvent that is not NMP.
- 2. A heat resistant negative working photoresist composition of claim 1, wherein Ar1 is selected from the group consisting of the following structures:
- 3. A heat resistant negative working photoresist composition of claim 1, wherein Ar1 is a moiety derived from a reactant selected from the group consisting of 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane, 3,3′-dihydroxy-4,4′-diaminodiphenylether, 3,3′-dihydroxybenzidine, 4,6-diaminoresorcinol, and 2,2-bis(3-amino-4-hydroxyphenyl)propane.
- 4. A heat resistant negative working photoresist composition of claim 3, wherein Ar1 is a moiety derived from the reactant 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane.
- 5. A heat resistant negative working photoresist composition of claim 1, wherein Ar3 is selected from the group consisting of the following structures:
- 6. A heat resistant negative working photoresist composition of claim 1, wherein Ar3 is a moiety derived from a reactant selected from the group consisting of: isophthaloyl dichloride, phthaloyl dichloride, terphthaloyl dichloride, 4,4′-diphenyletherdicarboxylic acid dichloride, 4,4′-diphenyletherdicarboxylic acid, terephthalic acid, isophthalic acid, dimethylisophthalate, dimethylphthalate, dimethylterphthalate, diethylisophthalate, diethylphthalate, diethylterphthalate, and mixtures thereof.
- 7. A heat resistant negative working photoresist composition of claim 1, wherein G is selected from the group consisting of the following structures:
- 8. A heat resistant negative working photoresist composition of claim 1, wherein G is an organic group having a carbonyl attached directly to the terminal NH group of the polymer.
- 9. A heat resistant negative working photoresist composition of claim 1, wherein G is an alkyl carbonyl group or a carbonyl group derived from a cyclic anhydride.
- 10. A heat resistant negative working photoresist composition of claim 1, wherein the PAG is selected from the group consisting of oxime sulfonates, halomethyl triazides, diazoquinone sulfonates, and sulfonium or idonium salts of sulfonic acids.
- 11. A heat resistant negative working photoresist composition of claim 1, wherein the PAG is selected from the group consisting of oxime sulfonates and sulfonium or idonium salts of sulfonic acids.
- 12. A heat resistant negative working photoresist composition of claim 1, wherein the latent crosslinker is selected from the group consisting of alkoxymethylmelamines, alkoxymethylglycolurils, alkoxymethylbenzoguanamines, alkoxymethyldiguanamines, and melamine or benzoguanamine polymers.
- 13. A heat resistant negative working photoresist composition of claim 1, wherein the latent crosslinker is selected from the group consisting of alkoxymethylmelamines and alkoxyamethylglycolurils.
- 14. A heat resistant negative working photoresist composition of claim 1, wherein the latent crosslinker is selected from the group consisting of
- 15. A heat resistant negative working photoresist composition of claim 1, wherein the solvent is selected from the group consisting of gamma-butyrolactone (GBL), propylene glycol methyl ether acetate, methoxy ethyl ether and mixtures thereof.
- 16. A heat resistant negative working photoresist composition of claim 15, wherein the solvent is gamma-butyrolactone.
- 17. A heat resistant negative working photoresist composition of claim 1, wherein the polybenzoxazole precursor polymer comprises from about 25 to about 35 wt % of the total composition, the PAG comprises from about 2 to about 15 wt % of the total composition, the latent crosslinker comprises from about 2 to about 35 wt % of the total composition, and the solvent comprises from about 45 to about 87 wt % of the total composition.
- 18. A heat resistant negative working photoresist composition of claim 1, wherein G is selected from the group consisting of an alkyl carbonyl and a carbonyl group derived from a cyclic anhydride, the latent crosslinker is selected from the group consisting of alkoxymethylmelamines and alkoxymethylglycolurils, and the PAG is selected from the group consisting of oxime sulfonates and sulfonium or idonium salts of sulfonic acids.
- 19. A heat resistant negative working photoresist composition of claim 1, wherein Ar1 is a moiety derived from the reactant 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane, the solvent is gamma-butyrolactone, and the latent crosslinker is selected from the group consisting of alkoxymethylmelamines and alkoxyamethylglycolurils.
- 20. A heat resistant negative working photoresist composition of claim 1, wherein the latent crosslinker is an alkoxyamethylglycoluril, G is a carbonyl moiety derived a cyclic anhydride, and the PAG is selected from the group consisting of oxime sulfonates and sulfonium salts of sulfonic acids
- 21. A heat resistant negative working photoresist composition of claim 1, additionally comprising an adhesion promoter.
- 22. A heat resistant negative working photoresist composition of claim 21, wherein the adhesion promoter is present in the composition in an amount of from about 0.1 to about 2 wt % of the total composition.
- 23. A heat resistant negative working photoresist composition of claim 21, wherein the adhesion promoter is an N-derivatized aminoalkyl alkoxysilane.
- 24. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 1;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 25. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 2;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 26. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 3;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 27. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 4;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 28. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 5;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 29. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 6;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 30. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 7;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 31. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 8;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 32. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 9;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 33. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 10(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 34. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 11;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 35. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 12;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 36. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 13;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 37. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 14;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 38. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 15;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 39. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 16;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 40. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 17;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 41. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 18;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 42. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 19;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 43. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 20;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 44. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 21;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 45. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 22;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 46. A process for forming a patterned image on a substrate, the process comprises the steps of:
(a) providing a substrate; (b) coating on said substrate a negative-working photosensitive composition of claim 23;(c) exposing the coated substrate to actinic radiation; (d) post exposure baking the coated substrate at an elevated temperature; (e) developing the coated substrate with an aqueous developer, thereby forming a relief image; and (f) baking the substrate at an elevated temperature, thereby curing the relief image.
- 47. A process according to claim 24, wherein the substrate to be coated with the negative-working photoresist composition in step (a) is a substrate that has been treated with an external adhesion promoter.
- 48. A process according to claim 47 wherein the external adhesion promoter is selected from the group consisting of vinylalkoxysilanes, methacryloxalkoxyysilanes, mercaptoalkoxysilanes, aminoalkoxysilanes, epoxyalkoxysilanes and glycidoxyalkoxysilanes.
- 49. A process according to claim 48 wherein the external adhesion promoter is selected from the group consisting of gamma-aminopropyltrimethoxysilane, gamma-glycidoxypropylmethyldimethoxysilane, gamma-glycidoxypropyl-methyldiethoxysilane, gamma-mercaptopropylmethyldimethoxysilane, 3-methacryl-oxypropyldimethoxymethylsilane, and 3-methacryloxypropyltrimethoxysilane.
- 50. A process according to claim 49 wherein the external adhesion promoter is gamma-aminopropyltrimethoxysilane.
- 51. A substrate having a patterned image produced by the process of claim 24.
- 52. A substrate having a patterned image produced by the process of claim 41.
- 53. A substrate having a patterned image produced by the process of claim 42.
- 54. A substrate having a patterned image produced by the process of claim 43.
- 55. A substrate having a patterned image produced by the process of claim 44.
- 56. A substrate having a patterned image produced by the process of claim 45.
- 57. A substrate having a patterned image produced by the process of claim 46.
- 58. A substrate having a patterned image produced by the process of claim 47.
- 59. A substrate having a patterned image produced by the process of claim 48.
- 60. A substrate having a patterned image produced by the process of claim 49.
- 61. A substrate having a patterned image produced by the process of claim 50.
RELATED APPLICATIONS
[0001] This application claims priority from United States Provisional Patent Application No. 60/453,869 filed Mar. 11, 2003.
Provisional Applications (1)
|
Number |
Date |
Country |
|
60453869 |
Mar 2003 |
US |