The present invention generally relates to optical lithography and more particularly relates to improved photomasks and methods of making the same, including alternating aperture phase shift masks (“aaPSMs”), and methods of making the same. More particularly, the present invention relates to improved aaPSMs having an internal substantially transparent etch stop layer and a layer deposited thereon.
Photomasks are high precision plates containing microscopic images of electronic circuits. Photomasks are typically made from flat pieces of material that are substantially transparent, such as quartz or glass, with an opaque layer, such as chrome, on one side. Etched in the opaque layer (e.g., chrome) of the mask is a pattern corresponding to a portion of an electronic circuit design. A variety of different photomasks, including, for example, aaPSMs, embedded attenuated phase shift masks and binary photomasks (e.g., chrome-on-glass), are used in semiconductor processing to transfer these patterns onto a semiconductor wafer or other type of wafer.
As shown in
As circuit designs have become increasingly complex, semiconductor manufacturing processes have become more sophisticated to meet the requirements of these complexities. In this regard, devices on semiconductor wafers have continued to shrink while circuit densities have continued to increase. This has resulted in an increased use of devices packed with smaller feature sizes, narrower widths and decreased spacing between interconnecting lines. For photolithographic processes, resolution and depth of focus (DoF) are important parameters in obtaining high fidelity of pattern reproduction from a photomask to a wafer. However, as feature sizes continue to decrease, the devices' sensitivity to the varying exposure tool wavelengths (e.g., 248 nm, 193 nm, 157 nm, 13 nm, etc.) used to write images on a semiconductor wafer has increased, thereby making it more and more difficult to write to an accurate image on the semiconductor wafer. In this regard,. as feature sizes continue to decrease, light diffraction effects in the photomask are exacerbated, thereby increasing the likelihood that defects will manifest in a pattern written on a semiconductor wafer. Accordingly, it has become necessary to develop new methods to minimize the problems associated with these smaller feature sizes.
One known method for increasing resolution in smaller feature sizes involves the use of shorter exposure wavelengths (e.g., 248 nm, 193 nm, 157 nm, 13 nm, etc.). Shorter exposure wavelengths, however, typically result in a shallower DoF in conventional binary chrome-on-glass (COG) photomasks having smaller feature sizes. In this regard, when the feature size is smaller than the exposure tool wavelength, binary COG photomasks become diffraction limited, thereby making it difficult, if not impossible, to write an accurate image on the semiconductor wafer. Accordingly, phase shifting masks (“PSMs”) have been used to overcome this problem. In this regard, PSMs are known to have properties which permit high resolution while maintaining a sufficient DoF. More particularly, a PSM reduces the diffraction limitation ordinarily associated with a binary COG mask by passing light through substantially transparent areas (e.g., glass, quartz or fused silica) which have either different thickness and/or different refractive indices than an ordinary binary COG mask. As a result, destructive interference is created in regions on the target semiconductor wafer that are designed to see no exposure. Thus, by reducing the impact of diffraction through phase shifting, the overall printability of an image is vastly improved such that the minimum width of a pattern resolved by using a PSM is approximately half the width of a pattern resolved in using an ordinary binary COG mask.
Various types of PSMs have been developed and are known in the art, including aaPSMs as described in co-pending U.S. Patent Application Publication no. 2004/0086787 A1 and U.S. patent application Ser. No. 10/391,001, filed Mar. 18, 2003, both of which are incorporated by reference herein in their entirety.
d=λ/2(n−1) (1)
where d is film thickness, n is refractive index at exposure wavelength, k is exposure wavelength. Thus, it is possible to etch smaller features in a semiconductor wafer and use shorter exposure wavelengths. Since the photoresist layer on the semiconductor wafer (
In practice, however, it is difficult to insure as the size of aaPSM continue to get smaller that the etched trenches are formed accurately. Conventional processes used to make aaPSMs etch the photomask to blank a specific depth which is determined by the wavelength of radiation used, as discussed above. Since this depth is significantly less than the photomask substrate thickness, there is no known technique where an optical emission spectrum (OES) could be used to determine the exact and appropriate etch time needed. In addition, there is no additional etching step (referred to as “overetch”) that can be done to address the plasma non-uniformity. Thus, there has been a long felt need for end point detection methods using an OES technique which allows for additional overetch time to adjust for any non-uniformities associated with plasma loading effects due to pattern density on the photomask.
Accordingly, it is an object of the present invention to provide an improved aaPSM that allows for end point detection using an OES technique.
It is a further object of the present invention to provide an improved aaPSM that also allows for additional overetch time to adjust for any non-uniformities associated with plasma loading effects due to pattern density on the photomask.
It is another object of the present invention to solve the shortcomings of the prior art.
Other objects will become apparent from the foregoing description.
It has now been found that the above and related objects of the present invention are obtained in the form of an aaPSM having an internal substantially transparent etch stop layer and at least one deposited layer formed thereon. The deposited layer may be either a deposited substantially transparent layer, such as SiO2, a deposited partially transparent layer, such as MoSi, or a deposited opaque layer, such as Cr. The internal substantially transparent etch stop layer of the present invention remains on the blank although the additional layers will be removed to form a patterned photomask. The characteristics of the internal substantially transparent etch stop layer of the present invention may include: (1) imperviousness to dry etch attack; (2) imperviousness to wet etch attack; (3) offering high transmission at desired wavelengths; (4) imperviousness to degradation under exposed radiation conditions; (5) offering an improvement for defect repair integration; (6) capability of being deposited in sufficient thickness as to allow for intensity balancing without undercut for alternating aperture phase shifting applications; (7) imperviousness to absorption of significant radiation at the exposure wavelengths such as 157 nm, 193 nm, and/or 248 nm; (8) capability of being deposited with either evaporative or sputtered techniques; (9) film properties of excellent adhesion and proper stress balancing; (10) allowing for end point detection during plasma dry etch processing to remove the top layer(s). In a preferred embodiment, the internal substantially transparent etch stop layer of the present invention is comprised of MgFx and even more particularly is comprised of MgF2 deposited under evaporation. Other materials that may be used for the substantially transparent etch stop layer of the present invention include, but are not limited to, Al2O3 and AlxNy.
More particularly, the present invention relates to a blank photomask comprising: a photosensitive resist material layer; a hard mask layer underlying the photosensitive resist material layer, wherein the hard mask layer is made from materials which are selectively resistant to etching in the blank photomask; an opaque layer underlying the the hard mask layer; a deposited substantially transparent layer underlying the opaque layer, a substantially transparent etch stop layer underlying the deposited substantially transparent layer, and a substantially transparent substrate underlying the substantially transparent etch stop layer. The deposited substantially transparent layer is of a thickness equal to λ/2(n−1), so that when the blank photomask is processed into an aaPSM, patterned regions are formed to comprise at least one opening exposing the deposited substantially transparent layer, and at least one light transmitting opening in which the deposited substantially transparent layer has been removed.
The present invention is also directed to a method for creating an aaPSM from the blank photomask described above and comprises the step of providing a blank photomask comprising a photosensitive resist material layer; an opaque layer underlying the photosensitive resist material layer; a deposited substantially transparent layer underlying the opaque layer, a substantially transparent etch stop layer underlying the deposited substantially transparent layer, and a substantially transparent substrate underlying the substantially transparent etch stop layer. The method further comprises the steps of forming in the blank photomask at least one opening exposing the deposited substantially transparent layer; forming at least one light transmitting opening in which the deposited substantially transparent layer has been removed; and further applying an etch process to the exposed portion of the substantially transparent etch stop layer to undercut portions of the opaque layer to provide balanced intensities between etched and unetched regions of the aaPSM. The etch process may be an isotropic etch. It may be either a dry etch or wet etch.
The present invention is also directed to a method for creating an aaPSM from the blank photomask described above and comprises the step of providing the blank photomask comprising a photosensitive resist material layer; a hard mask layer underlying the photosensitive resist material layer wherein the hard mask layer is made from materials which are selectively resistant to etching in the blank photomask; an opaque layer underlying the hard mask layer; a deposited substantially transparent layer underlying the opaque layer, a substantially transparent etch stop layer underlying the deposited substantially transparent layer, and a substantially transparent substrate underlying the substantially transparent etch stop layer. The method further comprises the steps of creating a patterned image in the photosensitive resist layer; removing portions of the photosensitive resist layer that do not correspond to the patterned image, thereby exposing portions of the hard mask layer not corresponding to the patterned image; removing the exposed portions of the hard mask layer that do not correspond to the patterned image, thereby exposing portions of the opaque layer not corresponding to the patterned image; forming in the blank photomask a first set of at least one light transmitting opening exposing the deposited substantially transparent layer; and forming in the blank photomask a second set of at least one light transmitting opening in which a portion of the deposited substantially transparent layer has been removed and a portion of the substantially transparent etch stop layer has been exposed.
Additionally, the present invention is directed to an aaPSM comprising: a patterned opaque layer with a first set of at least one light transmitting openings and a second set of at least one light transmitting openings; a deposited substantially transparent layer underlying the opaque layer wherein the deposited substantially transparent layer has corresponding light transmitting openings to each of the openings of the first set of at least one light transmitting openings, a substantially transparent etch stop layer underlying the deposited substantially transparent layer, and a substantially transparent substrate underlying the substantially transparent etch stop layer, wherein portions of the deposited substantially transparent layer exposed to the light transmitting openings of the deposited substantially transparent layer are etched to provide undercuts to portions of the patterned opaque layer so that the aaPSM provides balanced intensities between etched and unetched regions of the aaPSM.
Additionally, the present invention is directed to a method for manufacturing a semiconductor comprising the steps of: interposing an aaPSM between a semiconductor wafer and an energy source, wherein the aaPSM comprises an patterned opaque layer with a first set of at least one light transmitting openings and a second set of at least one light transmitting openings; a deposited substantially transparent layer underlying the opaque layer wherein the deposited substantially transparent layer has corresponding light transmitting openings to each of the openings of the first set of at least one light transmitting openings, a substantially transparent etch stop layer underlying the deposited substantially transparent layer, and a substantially transparent substrate underlying the substantially transparent etch stop layer, wherein portions of the deposited substantially transparent layer exposed to the light transmitting openings of the deposited substantially transparent layer are etched to provide undercuts to portions of the patterned opaque layer so that the aaPSM provides balanced intensities between etched and unetched regions of the aaPSM. The etch technique used can be either a dry etch or a wet etch. The method further comprises the steps of generating energy in the energy source; transmitting the generated energy through the first and second set of at least one light transmitting openings; and etching an image on the semiconductor wafer corresponding to a pattern formed by the first and second set of at least one light transmitting openings.
Furthermore, the present invention is also directed to a blank phase shift photomask comprising a photosensitive resist material layer; a hard mask layer underlying the photosensitive resist material layer, wherein the hard mask layer is made from materials which are selectively resistant to etching in the blank phase shift photomask; an opaque layer underlying the hard mask layer; a deposited partially transparent layer underlying the opaque layer; a substantially transparent etch stop layer underlying the deposited partially transparent layer; and a substantially transparent substrate underlying the substantially transparent etch stop layer.
The present invention is also directed to a blank phase shift photomask comprising a photosensitive resist material layer; an opaque layer underlying the photosensitive resist material layer; an intermediate layer underlying the opaque layer, wherein the intermediate layer is made from materials having a higher extinction coefficient at an inspection tools wavelength than at an exposure tool wavelength; a deposited partially transparent layer underlying the intermediate layer; a substantially transparent etch stop layer underlying the deposited partially transparent layer; and a substantially transparent substrate underlying the substantially transparent etch stop layer.
The present invention is also directed to a blank phase shift photomask comprising a photosensitive resist material layer; an opaque layer underlying the photosensitive resist material layer; a deposited partially transparent layer underlying the opaque layer; an intermediate layer underlying the deposited partially transparent layer, wherein the intermediate layer is made from materials having a higher extinction coefficient at an inspection tools wavelength than at an exposure tool wavelength; a substantially transparent etch stop layer underlying the intermediate layer; and a substantially transparent substrate underlying the substantially transparent etch stop layer.
The present invention is also directed to a blank phase shift photomask comprising a photosensitive resist material layer; an opaque layer underlying the photosensitive resist material layer; a first intermediate layer underlying the opaque layer, wherein the first intermediate layer is made from materials having a higher extinction coefficient at an inspection tools wavelength than at an exposure tool wavelength; a deposited partially transparent layer underlying the first intermediate layer; a second intermediate layer underlying the deposited partially transparent layer, wherein the second intermediate layer is made from materials having a higher extinction coefficient at an inspection tools wavelength than at an exposure tool wavelength; a substantially transparent etch stop layer underlying the second intermediate layer; and a substantially transparent substrate underlying the substantially transparent etch stop layer.
In addition, the present invention is also directed to a blank photomask comprising a photosensitive resist material layer; a hard mask layer underlying the photosensitive resist material layer, wherein the hard mask layer is made from materials which are selectively resistant to etching in the blank photomask; an opaque layer underlying the hard mask layer; a substantially transparent etch stop layer underlying the opaque layer; and a substantially transparent substrate underlying the substantially transparent etch stop layer.
Furthermore, the present invention is also directed to a method for forming isotropic regions in an alternating aperture phase shift mask having a substantially transparent etch stop layer, comprising the steps of defining the opaque region of the alternating aperture phase shift mask; forming an alternating anisotropic phase shift feature to a specific predetermined depth up to the substantially transparent etch stop layer, using etching techniques, which may be a dry etch or a wet etch; and forming an isotropic feature in the anisotropic phase feature using etch techniques, which may be a dry etch or a wet etch, in conjunction with the substantially transparent etch stop layer.
The present invention is also directed to an alternating aperture phase shift mask having an isotropic region and a substantially transparent etch stop layer made by the steps of defining the opaque region of the mask; forming an alternating anisotropic phase shift feature to a specific predetermined depth up to the substantially transparent etch stop layer, using etching techniques, which may be a dry etch or a wet etch; and forming an isotropic feature in the anisotropic phase feature using etch techniques, which may be a dry etch or a wet etch, in conjunction with the substantially transparent etch stop layer.
In addition, the present invention is also directed to a method for manufacturing a semiconductor comprising the steps of interposing a finished alternating aperture phase shift mask, having substantially transparent areas and a substantially transparent etch stop layer, between a semiconductor wafer and an energy source; transmitting energy generated by the energy source through the substantially transparent areas of the finished mask to the semiconductor wafer; and etching an image, corresponding to the substantially transparent areas of the finished photomask, on the semiconductor wafer, wherein the finished mask is made by defining the opaque region of the mask; forming an alternating anisotropic phase shift feature to a specific predetermined depth up to the substantially transparent etch stop layer using an etching technique, which may be a dry etch or a wet etch; and forming an isotropic feature in said anisotropic phase feature using an etching technique, which may be a dry etch or a wet etch, in conjunction with said substantially transparent etch stop layer.
The above and related objects, features and advantages of the present invention will be more fully understood by reference to the following, detailed description of the preferred, albeit illustrative, embodiment of the present invention when taken in conjunction with the accompanying figures, wherein:
a shows the equipment which can be used to make a semiconductor device from the aaPSM of the present invention;
b is flow diagram showing an example of the process for making a semiconductor device;
a shows a plan view of a conventional aaPSM;
b shows a cross-sectional view of conventional aaPSM;
c shows the light intensity transmitted through the aaPSM of
d is a semiconductor wafer exposed to light transmitted through the aaPSM of
The present invention is directed to improved aaPSMs and other types of PSMs and method for making the same. More particularly, the present invention utilizes a substantially transparent etch stop layer between a substantially transparent substrate and a deposited substantially transparent layer to insure that a proper opening depth is obtained in the formation of an aaPSM and other photomasks which require etching of substantially transparent substrates. Even more particularly, the internal substantially transparent etch stop layer of the present invention can have additional layers deposited thereon, such as a hard mask layer to prevent macroloading effects as disclosed in U.S. Pat. Nos. 6,472,107, 6,682,861 and 6,749,974, all of which are hereby incorporated by reference in their entirety, or an intermediate inspection layer as described in U.S. Patent Application Publication No. 2004/0043303 A1, which is also hereby incorporated by reference in its entirety. The internal substantially transparent etch stop layer of the present invention remains on the blank although the additional layers will be removed to form a patterned photomask. The characteristics of the internal substantially transparent etch stop layer of the present invention may include: (1) imperviousness to dry etch attack; (2) imperviousness to wet etch attack; (3) offering high transmission at desired wavelengths; (4) imperviousness to degradation under exposed radiation conditions; (5) offering an improvement for defect repair integration; (6) capability of being deposited in sufficient thickness as to allow for intensity balancing without undercut for alternating aperture phase shifting applications; (7) imperviousness to absorption of significant radiation at the exposure wavelengths of 157 nm, 193 nm, and or 248 nm; (8) capability of being deposited with either evaporative or sputtered techniques; (9) film properties of excellent adhesion and proper stress balancing; (10) allowing for end point detection during plasma dry etch processing to remove the top layer(s). In a preferred embodiment, the internal substantially transparent etch stop layer of the present invention is comprised of MgF2 deposited under evaporation. Alternatively, other suitable materials such as Al2O3 or AlxNy may also be used as the substantially transparent etch stop layer.
More particularly, referring to
The blank photomask 31 preferably includes five layers, but may include additional layers as needed or desired by the photomask manufacturer. For example, it may include a hard mask layer such as described in U.S. Patent Application Publication No. 2004/0137335 A1, which is incorporated by reference herein. The inclusion of a hard mask layer improves the uniformity of critical dimensions of the photomask by minimizing the effect of macro and micro-loading. In the blank phase shift photomask 31, the hard mask layer is underlying the photoresist material layer 41.
To form the aaPSM of the present invention, a pattern defined by an electronic file is transferred to the blank photomask using conventional lithography tools, including, for example, E-beam and/or laser beam writing tools. In one embodiment, the laser source which is used operates at 365 nm. However, the present invention is not limited to this particular wavelength laser source and will work with a variety of different image sources as discussed herein. As described in detail below, the blank photomask 31 is etched to form an aaPSM 51 having types of transmissive regions: (1) an unetched, film recess 40 covering a corresponding unetched portion of the deposited substantially transparent layer 37; and (2) a subtractively etched trench 42 etched in the deposited substantially transparent layer 37 up to the substantially transparent etch stop layer 35. In a preferred embodiment, these transmissive regions alternate between opaque regions on the photomask, as shown in
In one embodiment of the present invention to make the aaPSM of
Next, alternating phase-shift features are formed in the deposited substantially transparent layer 37. This is also accomplished in several steps in this embodiment of the present invention. In particular, after Step 5 has been completed, the remaining portions of the opaque layer 39 and the uncovered portions of the deposited substantially transparent layer are re-coated with photosensitive resist 43, Step 6. Predefined areas 36 in the photosensitive resist layer 43 of the partially processed photomask are exposed to an energy source, Step 7. In this regard, these predefined areas preferably alternate with the recesses 40 wherein a portion of chrome separates each alternating recess 40 (see Step 10 below) and predefined area. However, the present invention is not limited to PSMs which have alternating etched regions. It may also be used in any PSM which has etched regions of different depths, whether alternating or not. Next, the exposed areas 36 of the photosensitive resist layer 39 are developed (e.g., removed), Step 8. Thereafter, the portions of the deposited substantially transparent layer 39 that are no longer covered by photosensitive resist material 43 (or opaque material 39) are etched (e.g., vertical or anisotropic etching) to the substantially transparent etch stop layer 35, Step 9. The thickness of the deposited substantially transparent layer is chosen to satisfy equation (1). As a result, a phase shifted, transmissive vertical trench 45 is formed in the deposited substantially transparent layer 37. Thereafter, the remaining photoresist 43 is removed, Step 10. The result is an aaPSM having a vertical trench 45 alternating with unetched recess 40 in the deposited substantially transparent layer.
It is noted, however, that the method for processing the aaPSM of the present invention is not limited to the particular processing steps. In this regard, the processing method could be modified so long as the same results are achieved. Additionally, it is noted that the aaPSM of the present invention can be modified to be etched to different depths, in which case more than one substantially transparent etch stop layer and a corresponding number of deposited substantially transparent layers can be used.
In one embodiment of the present invention, the specified depth and the thickness of substantially transparent layer 33 can be selected so that the light that passes through the unetched recess 40 is approximately 180° out of phase from light that passes through the vertical trench 45, in accordance with the teachings of co-pending U.S. patent application Ser. No. 10/391,001, filed Mar. 18, 2003 to the same assignee, which is hereby incorporated by reference herein in its entirety. By making and using an aaPSM in this manner, there is zero asymmetry between the critical dimensions of the trench 45 and the unetched recess 40 of the deposited substantially transparent layer 37. As a result, the light intensity transmitted through these regions is balanced. Thus, it is possible to write an accurate image on a semiconductor wafer in a more efficient manner than was possible by prior art methods. In this regard, since the method of the present invention requires fewer etching steps (e.g., it does not require the step of undercutting the opaque layer), the overall output of aaPSMs over a given time period increases.
Alternatively, known and unknown techniques of balancing aerial intensities in aaPSMs can be used with the present invention, such as those disclosed in U.S. Patent Application Publication No. 2001/0044056 A1 and U.S. Patent Application Publication No. 2004/0086787 A1, assigned to the same assignee, without departing from the spirit of the present invention. For example, U.S. Patent Application Publication No. 2004/0086787 A1, which is incorporated by reference herein in its entirety, describes a method for modifying anisotropically etched features on conventional aaPSMs using an isotropic plasma quartz etch process, which involves three processing stages: (1) defining the opaque region (e.g., chrome) using a chlorine-based decoupled plasma process; (2) forming an alternating anisotropic phase shift feature to a specific predetermined depth through the use of a decoupled plasma source with a fluorine etchant; and (3) changing the plasma conditions by interrupting the bias power applied across the mask and etching strictly in the inductively coupled plasma mode. In lieu of the third step, it was also known that a wet etch may be used, as described in U.S. Patent Application Publication No. 2001/0044056 A1 which is hereby incorporated by reference in its entirety. These three processing stages achieve an isotropic undercutting of opaque layers which define the aaPSM and thereby achieve aerial intensity balancing.
Further, combinations of the techniques may also be used in conjunction with each other, such as forming an undercut region within the trenches of the aaPSM as well as selecting an appropriate light absorbing layers to work in conjunction to form an aaPSM having balanced aerial intensities. In accordance with the present invention, more specifically, the transparent etch stop layer may be utilized in conjunction with an isotropic etch step (either wet or dry etch) to achieve an intensity balancing without the manufacturing difficulties typically associated with isotropic etch processes, such as phase targeting difficulties and “wicking” defects. For example, upon completion of the anisotropic etching downward to the transparent etch stop layer 35 as shown in Step 9 of
In selecting the material and thickness of the substantially transparent etch stop layer and the deposited substantially transparent layer of the present invention, the following factors should be considered:
(1) Impervious to dry etch attack. The deposited material should have very low and perhaps no noticeable removal in dry plasma etch chemistry containing chlorine and/or fluorine species. Hence, it should as a barrier in the removal of the top layers of the photomask during pattern definition. Experiments have demonstrated that the use of a substantially transparent etch stop layer comprised of MgF2 deposited under evaporation are impervious to fluorine species using a decoupled plasma source system such as manufactured by Applied Materials, Inc. The substantially transparent etch stop layers should not be removed in sufficient quantity in Inductively Couple Plasma Source, Reactive Ion Etch Sources and similar sources that those skilled in the art may want to apply.
(2) Impervious to wet etch attack. The deposited material should have very low and perhaps no noticeable removal in wet chemistry containing NH4OH and acid based solutions, such as H2SO4 or HCL or other similar chemistries that those skilled in the art should apply.
(3) Offers High Transmission at the desired wavelength (e.g., 157 nm, 193 nm, and 248 nm). The etch stop layer should be made of a material which when deposited should improve the transmission of the photomask above the standard measured transmission by minimizing reflections off the photomask that would be lost from the system. For example, as
(4) Consistent Optical Properties At Actinic Exposures. The optical properties of the material should not significantly change under actinic exposures (e.g., 157 nm, 193 nm, and 248 nm). Hence, the transmission remains the same for the lifetime of the photomask during normal use, the optical properties do not change during normal use, the film does not change in any undesired way during normal usage.
(5) Defect Repair Improvement. The use of a substantially transparent etch stop layer allows for additional opportunities to repair defects detected in an unwanted area. One technique is to utilize a focused ion beam (FIB) with XeF2 chemistry to remove the defect over substantially transparent etch stop layer. The substantially transparent etch stop layer acts as protection layer for the underlying substrate so that a phase and or transmission error should not occur during the repair technique. One skilled in the art should be able to repair the substrate using an electron beam or laser beam in similar conditions. Without the substantially transparent etch stop layer, repair work of the defect by further etching would be more difficult since it is likely that there would be a significant change to the optical properties of the photomask rendering it sufficiently deficient or perhaps totally useless for the given application. Further, other repair techniques can be adapted to take advantage of the presence of the etch stop layer such as described in U.S. patent application Ser. No. __/______, filed on Sep. 8, 2004, entitled “Method of Repairing a Photomask Having an Internal Etch Stop Layer,” to the same assignee, which is hereby incorporated by reference herein in its entirety.
(6) Intensity balancing. By selecting an etch stop layer of the appropriate material and thickness in accordance with the teaching of co-pending U.S. patent application Ser. No. 10/391,001, filed on Mar. 18, 2003, to the same assignee, discussed above, the etch stop layer should be able to provide compensation for the intensity balance one would see in an alternating phase shift application. In such an embodiment, the etch stop layer can act as an attenuator if deposited in the correct thickness in the areas where a trench does not exist. Hence, this reduces or may even eliminate the need for an undercut process which enable very advanced applications such as at the 65 nm node and below that would normally have problems in designing around the undercut requirement and minimum feature width. The use of an etch stop layer allows for smaller geometries on the photomask and hence, smaller geometries on the wafer. However, as discussed above, the etch stop layer may also be used in conjunction with an undercut process (by isotropic etching on the etch stop layer to undercut the absorber layer) to achieve the desired intensity balancing.
(7) High Transmission. The material of the etch stop layer of the present invention should have a low extinction coefficient (k) at or near zero. Therefore, the transmission through the material is at close to 100% of the exposed wavelength.
(8) Easily Deposited. The material of the etch stop layer of the present invention should be able to be deposited with known deposition techniques such as sputter deposition, evaporative deposition, chemical vapor deposition, metal organic epitaxy, etc.
(9) Proper Stress and Adhesion Characteristics. The material of the etch stop layer of the present invention should be made to exhibit the proper stress and adhesion to be used in this application.
(10) Proper End Point Detection. Most significantly, the etch stop layer allows for end point detection for dry plasma etch applications, or other etching procedures.
In another embodiment, as shown in
The blank phase shift photomask 60 may further include additional layers as needed or desired by the photomask manufacturer. For example, it may include a hard mask layer such as described in U.S. Pat. Nos. 6,472,107, 6,682,861 and 6,749,974, which are incorporated by reference herein. The inclusion of a hard mask layer improves the uniformity of critical dimensions of the photomask by minimizing the effect of macro and micro-loading. In the blank phase shift photomask 60, the hard mask layer is positioned between the photoresist material layer 61 and the opaque layer 63.
Similarly, the blank photomask 60 may also include, for example, one or more intermediate inspection layers such as described in U.S. Patent Application Publication No. US 2004/0043303 A1, assigned to the same assignee, which is also incorporated by reference herein. The intermediate inspection layers are made from materials which have properties that provide for mask at the inspection tool wavelength (e.g., 365 nm) while at the same time maintain a low transmission of light at the exposure tool wavelength (e.g., 248 nm, 193 nm or 157 nm). As explained in the above-cited incorporated reference, the intermediate inspection layers should have a higher extinction coefficient (e.g., absorptivity of light) at the 365 nm inspection tool wavelength than at the various exposure tool wavelengths (i.e., 157 nm, 193 nm and 248 nm). The intermediate inspection layer may be positioned either below, or above a phase shift layer (i.e., the partially transparent layer 65). Alternatively, an EAPSM may include two intermediate inspection layers, each of which is positioned either below or above the phase shift layer. EAPSMs having one or more intermediate inspection layers provide accurate results in both the process for writing an image onto a semiconductor wafer and the process for inspecting the EAPSM.
These two examples of other potential layers that can be included in the blank photomask 60 in accordance with the present invention are merely illustrative and by no means intended to limit the scope of the present invention.
In a preferred form of this embodiment, the substantially transparent etch stop layer may be comprised of MgFx. Alternatively, the substantially transparent etch stop layer may be comprised of Al2O3 or AlxOy, or other similar materials based on the selection criteria discussed above. In an embodiment where an exposure wavelength of 157 nm is to be used with the EAPSM, the deposited partially transparent layer 65 may be comprised of SiON and the substantially transparent layer (e.g., quartz or fused silica) may be doped with fluorine to facilitate a high transmission of light (e.g., about 85%). In these embodiments of the present invention, the blank phase shift photomask can be processed as discussed above such that during processing, the etch stop layer will act as an etch stop of the deposited partially transparent layer.
In another embodiment as shown in
Now that the preferred embodiments of the present invention have been shown and described in detail, various modifications and improvements thereon will become readily apparent to those skilled in the art. For example, the etch stop layer of the present invention may be used in a wide variety of photomasks. Further, the present invention is not limited to the precise processing steps described herein. In this regard, the aaPSM or other photomasks of the present invention may be made with fewer or more processing steps, depending upon the equipment used and needs of the photomask maker. Further, the method of the present invention may also, for example, form all the unetched regions 40 in a series of processing steps, and form the etched regions 45 in a second series of processing steps. Thus, the present embodiments are therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims, and all changes that come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
This application is a continuation-in-part of U.S. patent application Ser. No. 10/658,039, filed Sep. 9, 2003, and U.S. patent application Ser. No. 10/229,830, filed Aug. 27, 2002, both of which are hereby incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10658039 | Sep 2003 | US |
| Child | 10936026 | Sep 2004 | US |
| Parent | 10229830 | Aug 2002 | US |
| Child | 10936026 | Sep 2004 | US |