Semiconductor chip fabrication is a complicated process that involves a coordinated series of precise operations. It is well known that during the various steps in these operations, the surfaces of the semiconductor substrate (i.e., semiconductor wafers) become contaminated with a layer of residue comprised of particulates, organic materials, metallic impurities (e.g. copper, aluminum, titanium, tungsten, etc.), and native oxides (e.g., silicon dioxide).
An example of wafer contamination created as a result of a manufacturing operation can be seen in
After plasma etching, photoresist 104 is typically removed through a process called ashing to strip the photoresist material from the wafer surface.
Removal of these contaminants is a vital step in producing ICs because contaminants on a wafer surface cause defects in the IC which result in decreased reliability or even failure of the IC. Therefore, the removal of contaminants from the wafer surface is necessary to produce the highest yield of viable devices per wafer.
Proprietary chemical formulations are available to remove post etch residues. However, these formulations are expensive to purchase in sufficient quantities for large scale wafer manufacturing. Furthermore, these proprietary chemicals often take several minutes to effectively remove the contaminants on the wafer surface. This delay can result in lower wafer output which adds to the expense of employing these formulations in the context of large-scale wafer manufacturing. Non-proprietary cleaning chemicals have been utilized in the past for wafer cleaning. However, the amount of contamination that remains on the wafer surface remains unacceptably high unless long process times are provided to clean the wafer surface. This is equally counterproductive to the goal of achieving high throughput wafer manufacture. Therefore in view of the foregoing, there is a need for methods to remove post etch residue chemicals that can effectively clean the surface of a wafer in a timely fashion.
Broadly speaking, the present invention fills these needs by providing an improved cleaning method to removed contaminants from the surface of a wafer. It should be appreciated that the present invention can be implemented in numerous ways, including as a system, an apparatus and a method. Several inventive embodiments of the present invention are described below.
In one embodiment, a method for cleaning a semiconductor wafer is defined. A proximity head is provided which includes a plurality of source inlets and a plurality of source outlets. Next, the proximity head is defined in close proximity to a wafer surface. After the proximity head is defined in close proximity to the wafer surface, an oxidizer solution is applied through the plurality of source inlets to the wafer surface. The oxidizer solution forms an oxidized layer on one or more contaminant species on the wafer surface. The oxidizer solution is removed from the wafer surface through the plurality of source outlets. Then a cleaning solution is applied to the wafer surface through the plurality of source inlets. The cleaning solution is configured to substantially remove the oxidized layer along with the one or more contaminant species on the wafer surface. The cleaning solution is removed from the wafer surface through the plurality of source outlets.
In another embodiment, a method for cleaning a semiconductor wafer begins by applying to a wafer surface a first cleaning solution to remove one or more contaminant species on the wafer surface. The first cleaning solution is removed from the wafer surface along with at least some of the one or more contaminant species. Next, an oxidizer solution is applied to the wafer surface. The oxidizer solution forms an oxidized layer on remaining contaminant species. The oxidizer solution is removed from the wafer surface. Next, a second cleaning solution is applied to the wafer surface. The second cleaning solution is configured to substantially remove the oxidized layer along with the remaining contaminant species. The second cleaning solution is removed from the wafer surface.
In still another embodiment, a method for cleaning a semiconductor wafer is defined. A proximity head is provided which includes a plurality of source inlets and a plurality of source outlets. The proximity head is defined in close proximity to a wafer surface. Next, a first cleaning solution to remove one or more contaminant species on the wafer surface is applied through the plurality of source inlets to the wafer surface. The first cleaning solution is removed along with at least some of the one or more contaminant species from the wafer surface through the plurality of source outlets. Then, an oxidizer solution is applied through the plurality of source inlets to the wafer surface. The oxidizer solution forms an oxidized layer on remaining contaminant species. The oxidizer solution is removed through the plurality of source inlets. A second cleaning solution is applied through the plurality of source inlets to the wafer. The second cleaning solution is configured to substantially remove the oxidized layer along with the remaining contaminant species. The second cleaning solution is removed from the wafer surface through the plurality of source outlets.
The present invention will be readily understood by the following detailed description in conjunction with the accompanying drawings, and like reference numerals designate like structural elements.
An invention is described for apparatuses, systems, and methods for cleaning the surface of a semiconductor substrate. It will be obvious, however, to one skilled in the art, that the present invention may be practiced without some or all of these specific details. In other instances, well known process operations have not been described in detail in order not to unnecessarily obscure the present invention.
A semiconductor substrate can be made of any silicon-based material. In one exemplary embodiment, the substrate is a semiconductor wafer, which is a thin slice of semiconductor material, such as a silicon crystal, upon which microcircuits are constructed by diffusion and deposition of various materials. In this document, the terms semiconductor substrate and semiconductor wafer are used inter-changeably. What is disclosed by the embodiments herein is essentially a semiconductor substrate cleaning method that can be used with customized configurations of proximity heads or other apparatus to economically and efficiently remove contaminants from the surface of a substrate.
Generally speaking, the method applies an oxidizer solution to the wafer surface after the wafer has been contaminated by post etch or other manufacturing processes. The oxidizer solution is selected such that the oxidizer solution causes an oxide layer to form on the wafer surface to entrap contaminants both on the surface of the wafer and within patterned structures. Once the oxide layer forms, the oxide layer can be removed by applying a cleaning solution. In this manner the formation of the oxide layer provides a cooperative cleaning mechanism with the cleaning solution to remove contaminants from the wafer surface. Suitable oxidizers and cleaning solutions can then be chosen so that the combination of oxidizer and cleaning solution work cooperatively to remove contamination from the wafer surface. The selection of a particular oxidizer and cleaning solution can be readily identified if the contamination species on the wafer surface are known.
Practical experience has shown however, that there may be situations where the formation of the initial oxide layer is inhibited by contaminant species. When encountered, this situation necessitates the use high concentrations of oxidizer as much as 5% by weight with process times as high as several minutes. Since oxidizer solutions are relatively expensive, this problem is equally unacceptable as the initial problem of using proprietary cleaning formulations or using cleaning solvents alone. An improvement over the two operation cleaning process is now discussed.
An improvement over the two operation cleaning process is obtained by employing an initial cleaning operation prior to application of the oxidizer solution. After a first cleaning solution is applied to the wafer surface, the first cleaning solution is removed with contaminants that inhibit oxide layer growth. The oxidizer solution can then be applied to the wafer surface so that an oxide layer forms. In general, the initial cleaning process removes contaminants which otherwise would inhibit the formation of the oxide layer. The cleaning method then employs the same oxidizer and cleaning solution treatment that was discussed above. A benefit which makes this process suitable for large scale wafer manufacture is that dilute chemical solutions can be utilized with process times that are below that experienced by previous cleaning methods.
An exemplary list of typical oxidizers employed in accordance with one embodiment of the present invention is listed in Table 1. Hydrogen peroxide, ozone dissolved in water, and nitric acid are listed as examples of typical oxidizers which may be utilized in the present invention. Additional oxidizers can be readily selected and tailored to form an oxide layer over an identified contamination species on a wafer surface.
It should be pointed out that these chemicals are readily available in bulk quantities and in suitable purity levels to employ in large scale wafer manufacture. Additionally the oxidizers listed in Table 1 can be employed in aqueous solutions using existing manufacturing equipment technologies as will be discussed later.
An exemplary list of acidic cleaning solutions employed in accordance with one embodiment of the present invention is listed in Table 2. Hydrofluoric acid, acetic acid, nitric acid, and sulfuric acid, an oxalic acid are listed as only examples of typical acidic, cleaning solutions which may be utilized in the present invention. Additional cleaning solutions may also be selected depending on the oxidizer to be dissolved and the nature of the contaminant species on the wafer surface. Example acidic solution should have a pH less than about 7.
Although the examples of Table 2 are acidic cleaning solutions, suitable base cleaning solutions can be employed in the present invention either as the only cleaning solution to be used with the oxidizer solution or in combination with a prior or subsequent cleaning operation employing an acidic cleaning solution. Examples of base cleaning solutions include ST250 and ST255 which are commercial cleaning formulations made by ATMI, Inc. and Rezi-38 which is a commercial cleaning formulation made by the J. T. Baker of Mallinckrodt Baker, Inc. A basic solution should therefore be one that has a pH greater than about 7 or a pH neutral solution. It should be pointed out that these particular formulations are ammonia-based and react well in cleaning copper-based contaminants which may be on a wafer surface. The concentration strength recommended by the manufacturer is used with process times in the range of about 1 s to 120 s for effective cleaning to be achieved.
Referring back to Table 2, the cleaning solutions listed benefit from being readily available in bulk quantities and in suitable purity levels to employ in large scale wafer manufacture. These cleaning solutions also are capable of being delivered in an aqueous solution using existing wafer cleaning technologies.
An illustration of a wafer cleaning technology which can used to employ the cleaning solutions and oxidizers listed above is the proximity head developed by Lam Research which is the assignee of the present invention.
Likewise,
For additional information with respect to the proximity head, reference can be made to an exemplary proximity head, as described in the U.S. Pat. No. 6,616,772, issued on Sep. 9, 2003 and entitled “M
For additional information about top and bottom menisci, reference can be made to the exemplary meniscus, as disclosed in U.S. patent application Ser. No. 10/330,843, filed on Dec. 24, 2002 and entitled “M
Although a few embodiments of the present invention have been described in detail herein, it should be understood, by those of ordinary skill, that the present invention may be embodied in many other specific forms without departing from the spirit or scope of the invention. Therefore, the present examples and embodiments are to be considered as illustrative and not restrictive, and the invention is not to be limited to the details provided therein, but may be modified and practiced within the scope of the appended claims. Additionally, the operational steps disclosed in the method claims herein do not follow any predetermined order and may be practiced in any order appropriate to the specific application.
This is a continuation-in-part application claiming priority from U.S. patent application Ser. No. 10/261,839, filed Sep. 30, 2002, now Pat. No. 7,234,477, issued on Jun. 26, 2007, entitled “Method And Apparatus For Drying Semiconductor Wafer Surfaces Using A Plurality Of Inlets And Outlets Held In Close Proximity To The Wafer Surfaces” by John M. de Larios et al. The aforementioned patent is incorporated by reference in its entirety for all purposes.
Number | Name | Date | Kind |
---|---|---|---|
6230720 | Yalamanchili et al. | May 2001 | B1 |
6230722 | Mitsumori et al. | May 2001 | B1 |
6247479 | Taniyama et al. | Jun 2001 | B1 |
6446358 | Mitsumori et al. | Sep 2002 | B1 |
6517635 | Mitsumori et al. | Feb 2003 | B2 |
6616772 | de Larios et al. | Sep 2003 | B2 |
6629540 | Mitsumori et al. | Oct 2003 | B2 |
20030168089 | Katakabe et al. | Sep 2003 | A1 |
20050139230 | Miyata et al. | Jun 2005 | A1 |
Number | Date | Country | |
---|---|---|---|
20070240737 A1 | Oct 2007 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 10261839 | Sep 2002 | US |
Child | 11477299 | US |