The present invention relates to a precision apparatus that uses within the apparatus a part made of a low thermal expansion material that undergoes martensitic transformation at a low temperature.
In some precision apparatuses such as precision machining equipment and precision measuring instruments, a material called Super Invar (32% Ni-5% Co—Fe), for example, which has an extremely small coefficient of thermal expansion, is sometimes used in a component that requires temperature-stable performance in order to reduce deformation and errors due to changes in ambient temperature.
However, when exposed to extremely low temperatures, a Super Invar material undergoes martensitic transformation, which changes the coefficient of thermal expansion of the Super Invar material to impair its original performance. Therefore, care needs to be taken to keep the part made of the Super Invar material from being exposed to extremely low temperatures lower than or equal to the martensitic transformation temperature.
To address the problem of martensitic transformation of such Ni—Co—Fe low thermal expansion materials, Japanese Patent Application Laid-Open No. 2001-11580 (hereinafter referred to as Patent literature 1) proposes an adjustment of components of an alloy to improve the stability of the alloy at low temperatures.
On the other hand, in the event that martensitic transformation occurs in a Super Invar material or other low thermal expansion material that undergoes martensitic transformation used in a precision apparatus, performance degradation or functional failure can occur.
If performance degradation or functional failure occurs, a temperature history, for example, can be used to determine whether or not the degradation or failure has been caused by martensitic transformation. That is, if means for obtaining the temperature history is provided in the precision apparatus, one can determine from the temperature history whether or not martensitic transformation has occurred due to exposure to extremely low temperatures.
Japanese Patent Application Laid-Open No. 2001-124715 describes a transformation observation apparatus including temperature detecting means and high-frequency current detecting means as means for determining whether transformation of metal has occurred or not.
As has been described above, provision of transformation observation equipment or temperature history obtaining means in a precision apparatus allows to readily determine whether performance degradation or functional failure in the apparatus has been caused by martensitic transformation of a low thermal expansion material used in the apparatus.
However, the provision of such transformation observation equipment or temperature history obtaining means adds cost to the precision apparatus, thereby making the precision apparatus expensive. Therefore, such transformation observation equipment or temperature history obtaining means have not commonly been adopted. In addition, transformation cannot be observed and a temperature history cannot be maintained while power is off such as during storage or transportation of the apparatus.
Therefore, it is a common practice that a precision apparatus is disassembled to take out a part made of a low thermal expansion material that might have undergone martensitic transformation and the surface (structure) of the part is observed or the dimensions or the coefficient of thermal expansion of the parts are precisely measured in order to determine whether or not performance degradation or functional failure has been caused by martensitic transformation. Such operation is laborious and time consuming.
In light of the problem described above, an object of the present invention is to provide a precision apparatus in which it can be readily and inexpensively determined whether or not martensitic transformation of a low thermal expansion material used in the apparatus has occurred.
According to a first aspect of the present invention, a precision apparatus that uses within it a low thermal expansion material that undergoes martensitic transformation at low temperature includes, on its outer surface, a low temperature history indication plate made of the same material as the low thermal expansion material. A surface of the low temperature history indication plate is mirror-polished.
According to a second aspect of the present invention, a precision apparatus that uses within it a low thermal expansion material that undergoes martensitic transformation at low temperature includes, on its outer surface, a low temperature history indication plate made of a plurality of materials having different martensitic transformation temperatures. A surface of the low temperature history indication plate is mirror-polished.
According to the present invention, it can be determined whether or not martensitic transformation of a low thermal expansion material used in an apparatus has occurred, simply by observing a low temperature history indication plate provided on the outer surface of the apparatus. Thus, determination as to whether martensitic transformation has occurred or not can be made in a remarkably simple and inexpensive manner without having to performing disassembly operation, which was previously required.
A configuration of a servo accelerometer, which is an example of a precision apparatus to which the present invention is applied, will be described first.
The servo accelerometer includes a feedback loop that detects a displacement of the pendulum 25 due to acceleration input with the capacitance sensor 28 and feeds a current (feedback current) “i” to the torquer coils 26 to return the pendulum 25 to the original position. The servo accelerometer operates on the principle that the flowing current “i” is proportional to acceleration.
The servo accelerometer which operates on the principle described above uses quartz glass as the material of the pendulum 25, which is the heart of the accelerometer, and the hinge 24, which supports the pendulum 25, in order to reduce errors due to temperature changes and deterioration by aging. Since quartz glass has a coefficient of thermal expansion of as small as 0.5 ppm/° C. or so, the yokes 21 used in combination is made of an Invar or Super Invar material, which is a magnetic material having a low coefficient of thermal expansion.
Such servo accelerometers are sometimes used for measurement and control in aircrafts that fly at high altitudes or measurement of slopes in oilfield near polar regions, where the servo accelerometers are required to withstand extreme conditions such as a lower limit storage temperature of −40° C. or −70° C. If a lower limit storage temperature of −70° C. is required of a servo accelerometer, the yokes 21 may be made of an Invar material, which has a low martensitic transformation temperature; if a lower limit storage temperature of −40° C. is required of a servo accelerometer, the yokes 21 may be made of a Super Invar material, which has a coefficient of thermal expansion close to that of quartz glass and can deliver high performance.
However, temperature monitoring during storage is often inadequate. In case the yokes 21 are exposed to a temperature lower than a specified lower limit temperature, martensitic transformation will occur in the yokes 21.
A configuration of an embodiment of a precision apparatus according to the present invention will be described below with respect to a servo accelerometer as an example. The assumption here is that the yokes 21 making up magnetic circuits of the servo accelerometer are made of a Super Invar material.
As illustrated in
According to the example, if the ambient temperature decreases to the temperature at which martensitic transformation occurs in the Super Invar material, a change in the structure (appearance of a acicular pattern) that is attributed to martensitic transformation appears in the surface 31a of the low temperature history indication plate 31. One can consider that martensitic transformation is likely to have also occurred in the Super Invar material used inside the servo accelerometer 10.
Conventionally, etching or other process is often performed before metallographic observation. However, since the surface 31a of the low temperature history indication plate 31 was polished to a mirror state beforehand, the acicular structure caused by martensitic transformation in the austenite structure can be observed without needing to perform a process such as etching. The observation can be performed with the naked eye or a low-power magnifier.
As has been described above, the low temperature history indication plate 31 is simply attached to the outer surface of the servo accelerometer 10 in the example. By observing the low temperature history indication plate 31, it can be determined whether martensitic transformation has occurred or not. Accordingly, if performance degradation or functional failure occurs in the servo accelerometer, determination can be made as to whether the degradation or failure has been caused by martensitic transformation of the Super Invar material used within the servo accelerator, without needing to disassemble the servo accelerator and without needing to use a special facility or power supply. Thus, according to the example, it can be remarkably simply and inexpensively determined whether or not martensitic transformation has occurred during storage or transportation.
Since occurrence of martensitic transformation can be known instantly in this way, actions such as a review of the conditions of storage and use, for example, can be taken quickly.
While the low temperature history indication plate 31 is bonded in the example described above, the low temperature history indication plate 31 may be attached by welding, for example.
In another example, a low temperature history indication plate 31 is flipped over so that its mirror-polished surface 31a faces the outer surface of a servo accelerometer, and then is attached as illustrated in
Both sides of the low temperature history indication plate 31 may be mirror-polished and the low temperature history indication plate 31 may be attached to the outer surface of the servo accelerometer with a pressure-sensitive adhesive. In that case, if one of the sides (surface 31a) becomes corroded, the other surface attached with the pressure-sensitive adhesive can be observed for determination because the surface is protected.
While the low temperature history indication plates 31 in the examples described above are made of the same Super Invar material as the yoke 21, a low temperature history indication plate may be made of multiple materials having different martensitic transformation temperatures because martensitic transformation temperature can be changed by adjusting the contents of Ni—Co—Fe as described in Patent literature 1, for example.
With this configuration, determination can be made as to whether martensitic transformation has occurred in the yokes 21 and, in addition, a change in ambient temperature (low temperature to which the yoke 21 has been exposed) can be estimated. Furthermore, determination as to whether or not an acicular structure resulting from the martensitic transformation has appeared can be readily made from comparison among the surfaces of the materials 41, 42 and 43. Here, Tm1 and Tm3 are in the following relationship, for example.
Tm1≈Tm2+30(° C.)
Tm3≈Tm2−30(° C.)
An embodiment in which the present invention has been applied to a servo accelerometer has been described above. An embodiment of another precision apparatus that uses a low thermal expansion component will be described below.
The metal pipe 63 is made of Invar or Super Invar, which is a low thermal expansion material, in order to increase the positional accuracy of the optical fiber core 64A with respect to the shaft axis. Such a ferrule is described in Japanese Patent Application Laid-Open No. 2000-160385, for example. According to the present invention, a low temperature history indication plate 65 is bonded to the surface of the rear part, for example, of the cylindrical body 61 that is close to the flange 61A. If martensitic transformation occurs in the Super Invar material of the metal pipe 63, the fact can be known by observing the low temperature history indication plate 65.
The dither suspension 73 includes a cylindrical part 73A, a sleeve 73B surrounding the cylindrical part 73A, multiple arm plates 73C that extend radially between the cylindrical part 73A and the sleeve 73B and are coupled with each other, and limbs 73D radially protruding outward from the outer surface of the sleeve 73B. The limbs 73D are fit into grooves 72B formed in the inner wall of the housing hole 72A. Piezoelectric elements 74 are fixed on both sides of each arm plate 73C. The gyroscope main body 71 is housed in a housing space 77C in the casing 77. An annular protrusion 77A formed in the center of the bottom of the housing space 77C supports one end of the cylindrical part 73A of the dither suspension 73. A fixing pin 78 is fixed in a fixing hole 77B of the annular protrusion 77A through a shaft hole 73E formed in the cylindrical part 73A to fix the cylindrical part 73A to the annular protrusion 77A. Thus, the low-thermal-expansion glass body 72 of the gyroscope main body 71 is supported on the annular protrusion 77A of the casing 77 by the cylindrical part 73A through the limbs 73D, the sleeve 73B and the arm plates 73C of the dither suspension 73. In this state, the cover 76 covers the opening of the casing 77 and is fixed on the casing 77 with screws.
The space in the low-thermal-expansion glass body 72 including the light path is filled with a laser medium. Electrodes, not depicted, discharge high-voltage electricity in the space to generate plasma. Two laser beams traversing clockwise and counterclockwise are produced by reflection by the mirrors. When the casing 77 is rotated about its central axis (input angular velocity is applied to the casing 77), the angular velocity is provided to the gyroscope main body 71, an optical path difference results, and the optical path difference results in a difference in oscillating frequency between the two laser beams. The frequency difference can be detected as an optical interference pattern to detect the input angular velocity.
The ring laser gyroscope 70 enters a state (a dead band of the gyroscope) in which the ring laser gyroscope cannot detect input angular velocities lower than a certain value. The phenomenon is known as lock-in. To prevent the lock-in, the piezoelectric elements 74 are attached on the arm plates 73C to apply dither angular oscillation about the axis. Such a ring laser gyroscope is disclosed in U.S. Pat. No. 5,088,825, for example. Japanese Patent Application Laid-Open No. 2008-197066 discloses the use of a dither suspension 73 made of Inver or Super Inver that has a coefficient of thermal expansion close to that of the low-thermal-expansion glass body 72 of the gyroscope main body 71.
According to the present embodiment, a low temperature history indication plate 79 which indicates a possibility of transformation of the dither suspension 73 made of a low thermal expansion material to martensite is attached to the top surface of the cover 76.
While examples of precision apparatuses that use components made of Super Invar materials have been described above, the present invention is also applicable to various other precision apparatuses that use low thermal expansion materials that undergo martensitic transformation when being exposed to extremely low temperatures. Furthermore, a low temperature history indication plate that measures as small as several millimeters per side enables visual identification of martensitic transformation. Therefore, the low temperature history indication plate can be attached to a small apparatus as well.
If the low temperature history indication plate is made of a material having a martensitic transformation temperature somewhat higher than the martensitic transformation temperature of a low thermal expansion material used in a precision apparatus, for example occurrence of martensitic transformation can be identified well in advance.
Number | Date | Country | Kind |
---|---|---|---|
2010-040053 | Feb 2010 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
3182507 | Rogen | May 1965 | A |
4198679 | Fainzilberg | Apr 1980 | A |
5088825 | Derry et al. | Feb 1992 | A |
20090120106 | Chin | May 2009 | A1 |
20120033707 | Sloan | Feb 2012 | A1 |
20130008567 | Katsumata | Jan 2013 | A1 |
Number | Date | Country |
---|---|---|
2000-160385 | Jun 2000 | JP |
2001-011580 | Jan 2001 | JP |
2001-124715 | May 2001 | JP |
2006010527 | Jan 2006 | JP |
2008-197066 | Aug 2008 | JP |
409124 | Apr 1974 | SU |
1224615 | Apr 1986 | SU |
WO 8806728 | Sep 1988 | WO |
Number | Date | Country | |
---|---|---|---|
20110203511 A1 | Aug 2011 | US |