Claims
- 1. A method for the manufacture of printed circuit boards of plastic construction, which comprises:
- drilling a plurality of holes through a circuit board comprising a plastic substrate having adhered thereto a metal foil forming a circuit pattern in the foil by the image/print/etch procedure;
- applying a polymeric resist to the entire surface of the board but not onto the pads or into the holes thereof;
- treating the imaged board with a charge extender to create a higher differential of charge between the resist image and the surfaces of the hole walls;
- selectively catalyzing the surfaces of the hole walls with a catalyst having a charge higher than the charge on the surfaces of the hole walls and sufficiently lower than the charge of the resist image to cause the catalyst to be repelled therefrom, but sufficiently close to the charge on the surface of the hole walls to cause the catalyst to be absorbed thereon; and
- plating the catalyzed surfaces of the hole walls with a first metal by electroless deposition to form the completed circuit of the circuit board.
- 2. The method of claim 1 wherein the desired circuit pattern is obtained by etching a laminate of a metal foil adhered to a plastic substrate.
- 3. The method of claim 1 which further comprises subsequently plating the board with a second metal by electroless deposition.
- 4. The method of claim 3 wherein said first metal is copper or nickel and wherein said second metal is tin, a tin-lead alloy, or gold.
- 5. The method of claim 1 wherein the catalyst comprises colloidal particles.
- 6. The method of claim 5 wherein the colloidal catalyst has a zeta potential between about 3 and 20 (plus or minus) millivolts.
- 7. The method of claim 1 wherein the catalyst comprises metal ions.
- 8. The method of claim 7 wherein the metal ions are reduced by a reducing agent.
- 9. The method of claim 1 wherein the charge extender is an oxidizing agent, a strong base, strong acid, or a surfactant that alters the surface charge of the board.
- 10. The method of claim 9 wherein the charge extender is a fatty acid sulfate, an alkyl aryl sulfonate, sulfuric acid, chromic acid, potassium permanganate, hydrogen peroxide or sodium hydroxide.
- 11. The method of claim 1 wherein the metal foil is copper.
- 12. A method for the manufacture of printed circuit boards of plastic construction, which comprises:
- microroughening the surfaces of a plastic substrate by chemical or mechanical methods;
- applying a polymeric resist to a portion of the microroughened substrate to form an imaged circuit board;
- treating the microroughened, imaged board with a charge extender to create a higher differential of charge between the resist image and non-imaged areas; selectively catalyzing those areas not covered by the resist image with a catalyst having a charge higher than the charge on the non-imaged areas and sufficiently lower than the charge of the resist image to cause the catalyst to be repelled therefrom, but sufficiently close to the charge on the non-imaged areas to cause the catalyst to be absorbed thereon; and
- plating the catalyzed areas of the boards with a first metal by electroless deposition to form the completed circuit of the circuit board.
- 13. The method of claim 12 which further comprises providing said molded board with one or a plurality of holes prior to applying the resist.
- 14. The method of claim 12 wherein the plastic substrate is of a molded construction.
- 15. The method of claim 12 wherein further comprises subsequently plating the board with a second metal by electroless deposition.
- 16. The method of claim 15 wherein said first metal is copper or nickel, and wherein said second metal is tin, a tin-lead alloy, or gold.
- 17. The method of claim 12 wherein the catalyst comprises colloidal particles.
- 18. The method of claim 17 wherein the colloidal catalyst has a zeta potential between about 3 and 20 (plus or minus) millivolts.
- 19. The method of claim 12 wherein the catalyst comprises metal ions.
- 20. The method of claim 19 wherein the metal ions are reduced by a reducing agent.
- 21. The method of claim 12 wherein the charge extender is an oxidizing agent, a strong base, strong acid, or a surfactant that alters the surface charge of the board.
- 22. The method of claim 21 wherein the charge extender is a fatty acid sulfate, an alkyl aryl sulfonate, sulfuric acid, chromic acid, potassium permanganate, hydrogen peroxide or sodium hydroxide.
- 23. The method of claim 12 wherein the microroughening step comprises treating the board with an adhesion promotion system.
- 24. A method for the manufacture of printed circuited boards of plastic construction, which comprises:
- drilling a plurality of holes through a circuit board comprising a laminate of a metal foil adhered to a molded plastic substrate;
- etching the board to completely remove the metal foil and expose said plastic surface;
- applying a polymeric resist to the substrate to form the circuit;
- treating the imaged board with a charge extender to create a higher differential of charge between the resist image and non-imaged areas;
- selectively catalyzing those areas not covered by the resist image with a catalyst having a charge higher than the charge on the non-imaged areas and sufficiently lower than the charge of the resist image to cause the catalyst to be repelled therefrom, but sufficiently close to the charge on the non-imaged areas to cause the catalyst to be absorbed thereon; and
- plating the catalyzed areas of the boards with a first metal by electroless deposition to form the completed circuit of the circuit board.
- 25. The method of claim 24 which further comprises subsequently plating the board with a second metal by electroless deposition.
- 26. The method of claim 25 wherein said first metal is copper or nickel and wherein said second metal is tin, a tin-lead alloy, or gold.
- 27. The method of claim 24 wherein the catalyst comprises colloidal particles.
- 28. The method of claim 27 wherein the colloidal catalyst has a zeta potential between about 3 and 20 (plus or minus) millivolts.
- 29. The method of claim 24 wherein the catalyst comprises metal ions.
- 30. The method of claim 29 wherein the metal ions are reduced by a reducing agent.
- 31. The method of claim 24 wherein the charge extender is an oxidizing agent, a strong base, strong acid, or a surfactant that alters the surface charge of the boards.
- 32. The method of claim 31 wherein the charge extender is a fatty acid sulfate, an alkyl aryl sulfonate, sulfuric acid, chromic acid, potassium permanganate, hydrogen peroxide or sodium hydroxide.
- 33. The method of claim 24 which further comprises treating the exposed plastic surfaces with an adhesion promotion system after the foil is removed to impart additional microroughening to said surface.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is a continuation-in-part of each of application Ser. No. 574,086, filed Jan. 26, 1984, application Ser. No. 898,073 filed Aug. 20, 1986, now U.S. Pat. No. 4,759,952 and application Ser. No. 17,413, filed Feb. 24, 1987, now U.S. Pat. No. 4,761,304.
US Referenced Citations (24)
Foreign Referenced Citations (7)
Number |
Date |
Country |
44878 |
Feb 1982 |
EPX |
1814055 |
Jun 1970 |
DEX |
52-32829 |
Mar 1977 |
JPX |
55-9459 |
Jan 1980 |
JPX |
55-50690 |
Apr 1980 |
JPX |
57-4116 |
Jan 1982 |
JPX |
2066582 |
Jul 1981 |
GBX |
Non-Patent Literature Citations (3)
Entry |
McFayden & Matijevic, Journal of Colloid and Interface Science, vol. 44, No. 1, Jul. 1975, pp. 95-106. |
Weiser, Inorganic Colloid Chemistry, vol. I, John Wiley & Sons, Inc., 1933, pp. 137-138. |
Encyclopedia of Chemical Technology, Kirk-Othman, 3rd Edition, vol 17, pp. 680-708 (1982). |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
574086 |
Jan 1984 |
|